WO2019188334A1 - Adhésif réactif, film stratifié et corps d'emballage - Google Patents

Adhésif réactif, film stratifié et corps d'emballage Download PDF

Info

Publication number
WO2019188334A1
WO2019188334A1 PCT/JP2019/010507 JP2019010507W WO2019188334A1 WO 2019188334 A1 WO2019188334 A1 WO 2019188334A1 JP 2019010507 W JP2019010507 W JP 2019010507W WO 2019188334 A1 WO2019188334 A1 WO 2019188334A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid
polyol
adhesive
film
reactive adhesive
Prior art date
Application number
PCT/JP2019/010507
Other languages
English (en)
Japanese (ja)
Inventor
千勇 徳永
ギョウン ジョン
英男 田邊
Original Assignee
Dic株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dic株式会社 filed Critical Dic株式会社
Priority to CN201980018507.0A priority Critical patent/CN111836866B/zh
Priority to JP2019556718A priority patent/JP6675595B2/ja
Publication of WO2019188334A1 publication Critical patent/WO2019188334A1/fr

Abstract

L'invention concerne : un adhésif réactif qui contient une composition de polyisocyanate (X), une composition de polyol (Y) et un anhydride pyromellitique, la teneur en anhydride pyromellitique étant de 0,2 à 2,0 % en poids par rapport à la teneur en matières solides totales de l'adhésif réactif ; et un film stratifié qui est obtenu par stratification d'une couche adhésive entre un premier film plastique et un second film plastique, ladite couche adhésive étant une couche de l'adhésif réactif susmentionné. L'adhésif réactif comprend en outre de préférence du 3a,4,5,7a-tétrahydro-7-méthyl-5-(tétrahydro-2,5-dioxo-3-furanyl)-1,3-iso-benzofurandione ou de l'acide gallique.
PCT/JP2019/010507 2018-03-27 2019-03-14 Adhésif réactif, film stratifié et corps d'emballage WO2019188334A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201980018507.0A CN111836866B (zh) 2018-03-27 2019-03-14 反应性粘接剂、层叠膜及包装物
JP2019556718A JP6675595B2 (ja) 2018-03-27 2019-03-14 反応性接着剤、積層フィルム、及び包装体

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018059793 2018-03-27
JP2018-059793 2018-03-27

Publications (1)

Publication Number Publication Date
WO2019188334A1 true WO2019188334A1 (fr) 2019-10-03

Family

ID=68061491

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/010507 WO2019188334A1 (fr) 2018-03-27 2019-03-14 Adhésif réactif, film stratifié et corps d'emballage

Country Status (4)

Country Link
JP (1) JP6675595B2 (fr)
CN (1) CN111836866B (fr)
TW (1) TW201942296A (fr)
WO (1) WO2019188334A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0346034B2 (fr) * 1984-08-14 1991-07-12 Dainippon Ink & Chemicals
US5157100A (en) * 1991-09-20 1992-10-20 The Sherwin-Williams Company Method for extending the pot-life of polyol-polyisocyanate mixtures
JPH10102028A (ja) * 1996-09-27 1998-04-21 Nippon Polyurethane Ind Co Ltd 熱可塑性ポリウレタン樹脂を用いたラミネートフィルム用接着剤組成物
JP2015113411A (ja) * 2013-12-12 2015-06-22 ヘンケルジャパン株式会社 食品包装フィルム用接着剤
JP2018199251A (ja) * 2017-05-26 2018-12-20 Dic株式会社 積層フィルム及び包装体

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001164229A (ja) * 1999-12-09 2001-06-19 Dainippon Ink & Chem Inc 無溶剤型接着剤組成物およびラミネート方法
US9676976B2 (en) * 2010-06-21 2017-06-13 Dic Corporation Oxygen-barrier film and adhesive

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0346034B2 (fr) * 1984-08-14 1991-07-12 Dainippon Ink & Chemicals
US5157100A (en) * 1991-09-20 1992-10-20 The Sherwin-Williams Company Method for extending the pot-life of polyol-polyisocyanate mixtures
JPH10102028A (ja) * 1996-09-27 1998-04-21 Nippon Polyurethane Ind Co Ltd 熱可塑性ポリウレタン樹脂を用いたラミネートフィルム用接着剤組成物
JP2015113411A (ja) * 2013-12-12 2015-06-22 ヘンケルジャパン株式会社 食品包装フィルム用接着剤
JP2018199251A (ja) * 2017-05-26 2018-12-20 Dic株式会社 積層フィルム及び包装体

Also Published As

Publication number Publication date
JP6675595B2 (ja) 2020-04-01
TW201942296A (zh) 2019-11-01
JPWO2019188334A1 (ja) 2020-05-28
CN111836866B (zh) 2022-04-01
CN111836866A (zh) 2020-10-27

Similar Documents

Publication Publication Date Title
JP6098914B2 (ja) 無溶剤型ラミネート接着剤、その硬化物、ラミネート接着剤用ポリオール組成物、及び積層フィルム
JP6451021B2 (ja) 反応型接着剤、積層フィルム及び包装体
JP6797352B2 (ja) 接着剤、積層フィルム、及び積層フィルムの製造方法
JP6620963B2 (ja) 反応型接着剤、積層フィルム及び包装体
JP7004090B2 (ja) 接着剤、積層フィルム、及び積層フィルムの製造方法
JP6452018B1 (ja) ２液型接着剤用の硬化剤、２液型接着剤、積層フィルム及び包装体
JP6481321B2 (ja) ウレタン化触媒、ポリオール混合物、接着剤、及び積層フィルム
JP6650134B1 (ja) 反応性接着剤、積層フィルム、及び包装体
JP2020094154A (ja) 反応性接着剤、積層フィルム、及び包装体
JP2018043771A (ja) 包装体
JP7183638B2 (ja) 反応性接着剤、積層フィルム、及び包装体
JP6675595B2 (ja) 反応性接着剤、積層フィルム、及び包装体
JP2019104874A (ja) ポリイソシアネート組成物、接着剤組成物、積層フィルム及び包装体
JP7206888B2 (ja) 反応性接着剤、積層フィルム、及び包装体
JP2017095550A (ja) 無溶剤接着剤用ポリオール組成物、無溶剤型接着剤、及び積層フィルム
JP2018100366A (ja) 反応性接着剤、積層フィルム、及び包装体
JP2022121908A (ja) 反応性接着剤、積層体及び包装体
JP2020041103A (ja) ２液型接着剤、積層フィルム及び包装体

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2019556718

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19775122

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19775122

Country of ref document: EP

Kind code of ref document: A1