WO2019155925A1 - Film adhésif de polyuréthane thermofusible et structure fibreuse en couches - Google Patents

Film adhésif de polyuréthane thermofusible et structure fibreuse en couches Download PDF

Info

Publication number
WO2019155925A1
WO2019155925A1 PCT/JP2019/002658 JP2019002658W WO2019155925A1 WO 2019155925 A1 WO2019155925 A1 WO 2019155925A1 JP 2019002658 W JP2019002658 W JP 2019002658W WO 2019155925 A1 WO2019155925 A1 WO 2019155925A1
Authority
WO
WIPO (PCT)
Prior art keywords
hot melt
polyurethane layer
melt polyurethane
hot
layer
Prior art date
Application number
PCT/JP2019/002658
Other languages
English (en)
Japanese (ja)
Inventor
真人 割田
道憲 藤澤
Original Assignee
株式会社クラレ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クラレ filed Critical 株式会社クラレ
Publication of WO2019155925A1 publication Critical patent/WO2019155925A1/fr

Abstract

L'utilisation est faite d'un film adhésif de polyuréthane thermofusible qui comprend une première couche de polyuréthane thermofusible, une deuxième couche de polyuréthane thermofusible et une troisième couche de polyuréthane, qui est interposée entre la première couche de polyuréthane thermofusible et la deuxième couche de polyuréthane thermofusible, la troisième couche de polyuréthane présentant une température de ramollissement supérieure à celle de la première couche de polyuréthane thermofusible et de la deuxième couche de polyuréthane thermofusible.
PCT/JP2019/002658 2018-02-08 2019-01-28 Film adhésif de polyuréthane thermofusible et structure fibreuse en couches WO2019155925A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018020760 2018-02-08
JP2018-020760 2018-02-08

Publications (1)

Publication Number Publication Date
WO2019155925A1 true WO2019155925A1 (fr) 2019-08-15

Family

ID=67549429

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/002658 WO2019155925A1 (fr) 2018-02-08 2019-01-28 Film adhésif de polyuréthane thermofusible et structure fibreuse en couches

Country Status (2)

Country Link
TW (1) TW201936837A (fr)
WO (1) WO2019155925A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021000806A (ja) * 2019-06-24 2021-01-07 昭和電工マテリアルズ株式会社 繊維製品及びその製造方法、並びに接着剤セット
KR102229750B1 (ko) * 2019-11-14 2021-03-18 엄기천 합성 피혁의 제조방법

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0820096A (ja) * 1994-07-08 1996-01-23 Okura Ind Co Ltd ウレタン系ホットメルトフィルム
JPH09235519A (ja) * 1996-03-01 1997-09-09 Daicel Chem Ind Ltd ホットメルト型接着フィルムと加工品
JPH10192004A (ja) * 1996-12-27 1998-07-28 Mizuno Corp 靴用接着シート及び、それを用いた靴の製造方法
JPH11172209A (ja) * 1997-12-09 1999-06-29 Unitika Ltd 目止めテープ
JP2002370333A (ja) * 2001-06-15 2002-12-24 Chiyoushirou Sakoguchi 被転写物である靴下、サポーター等の所望個所に二層構造の角質化防止膜として転写できる転写材
JP2016056243A (ja) * 2014-09-05 2016-04-21 株式会社アイセロ 熱接着フィルム

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0820096A (ja) * 1994-07-08 1996-01-23 Okura Ind Co Ltd ウレタン系ホットメルトフィルム
JPH09235519A (ja) * 1996-03-01 1997-09-09 Daicel Chem Ind Ltd ホットメルト型接着フィルムと加工品
JPH10192004A (ja) * 1996-12-27 1998-07-28 Mizuno Corp 靴用接着シート及び、それを用いた靴の製造方法
JPH11172209A (ja) * 1997-12-09 1999-06-29 Unitika Ltd 目止めテープ
JP2002370333A (ja) * 2001-06-15 2002-12-24 Chiyoushirou Sakoguchi 被転写物である靴下、サポーター等の所望個所に二層構造の角質化防止膜として転写できる転写材
JP2016056243A (ja) * 2014-09-05 2016-04-21 株式会社アイセロ 熱接着フィルム

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2021000806A (ja) * 2019-06-24 2021-01-07 昭和電工マテリアルズ株式会社 繊維製品及びその製造方法、並びに接着剤セット
JP7259588B2 (ja) 2019-06-24 2023-04-18 株式会社レゾナック 繊維製品及びその製造方法、並びに接着剤セット
KR102229750B1 (ko) * 2019-11-14 2021-03-18 엄기천 합성 피혁의 제조방법

Also Published As

Publication number Publication date
TW201936837A (zh) 2019-09-16

Similar Documents

Publication Publication Date Title
JP4875179B2 (ja) 車両内装材用合成皮革及びその製造方法
JP4782119B2 (ja) 耐傷性、耐擦過傷性に優れた銀面調皮革様シート
TW201540518A (zh) 雙面膠帶、其製造方法、其使用方法、及藉由其組合的物品
JP6357367B2 (ja) 表皮材とその製造方法
WO2019155925A1 (fr) Film adhésif de polyuréthane thermofusible et structure fibreuse en couches
JP5398451B2 (ja) 合成皮革の製造方法
WO2014132488A1 (fr) Feuille adhésive à usage médical et procédé de production de feuille adhésive à usage médical
JP7300384B2 (ja) ポリウレタンホットメルト接着剤、それを用いた積層体及び積層体の製造方法
JP2014129622A (ja) 合成皮革
TWI794284B (zh) 合成皮革之製造方法
JP2013208814A (ja) ポリウレタン積層体及びポリウレタン積層体の製造方法
WO2019176941A1 (fr) Adhésif thermofusible durcissant à l'humidité et corps adhésif
KR20110002321A (ko) 수성 폴리우레탄 접착액을 이용한 기능성 원단의 라미네이팅 방법
JP5779424B2 (ja) 銀付調皮革様シート
WO2022158507A1 (fr) Structure de couche poreuse et procédé de production de structure de couche poreuse
JP2004211262A (ja) 耐摩耗性の良好な皮革様シート
JP3400281B2 (ja) 皮革様シートおよびその製造方法
JP2018184000A (ja) 表皮材とその製造方法
JP4582944B2 (ja) 合成皮革及びその製造方法
JP2020002474A (ja) シート状物およびその製造方法
JPWO2019058804A1 (ja) 合成皮革の製造方法
TWI835056B (zh) 多孔層結構體及多孔層結構體之製造方法
JPH01111077A (ja) 皮革様シート状物の製造方法
JPS61225364A (ja) 伸縮性衣料用素材
JP2006233392A (ja) 銀付き調人工皮革およびその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19751528

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19751528

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP