WO2019111733A1 - Sac d'emballage destiné à chauffer - Google Patents

Sac d'emballage destiné à chauffer Download PDF

Info

Publication number
WO2019111733A1
WO2019111733A1 PCT/JP2018/043236 JP2018043236W WO2019111733A1 WO 2019111733 A1 WO2019111733 A1 WO 2019111733A1 JP 2018043236 W JP2018043236 W JP 2018043236W WO 2019111733 A1 WO2019111733 A1 WO 2019111733A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
packaging bag
film
multilayer film
heating
Prior art date
Application number
PCT/JP2018/043236
Other languages
English (en)
Japanese (ja)
Inventor
勝弘 本郷
三浦　崇
史絵 松永
Original Assignee
東洋製罐株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2018152903A external-priority patent/JP6551591B2/ja
Application filed by 東洋製罐株式会社 filed Critical 東洋製罐株式会社
Publication of WO2019111733A1 publication Critical patent/WO2019111733A1/fr

Abstract

La présente invention concerne un sac d'emballage qui est destiné à chauffer et qui comprend un film multicouche comportant au moins une couche de soudage et une couche de base formée à partir d'une résine de polyester. Pendant le test de traction (température ambiante 200 °C, largeur d'échantillon 10 mm, distance entre mandrins 20 mm, vitesse de traction 1 mm/min) d'un film de résine qui constitue la couche la plus à l'extérieur du film multicouche, au point où un échantillon a été étendu de 10 mm, la charge par unité d'épaisseur de l'échantillon était de 0,25 N/µm ou moins, et par conséquent, même si une pression interne est exercée sur le sac d'emballage et que le sac d'emballage se dilate, tel que lorsqu'il est chauffé dans un four à micro-ondes, non seulement l'invention empêche la formation de trous dans le sac d'emballage, mais elle empêche également tout endommagement de la surface externe.
PCT/JP2018/043236 2017-12-07 2018-11-22 Sac d'emballage destiné à chauffer WO2019111733A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2017235134 2017-12-07
JP2017-235134 2017-12-07
JP2018-152903 2018-08-15
JP2018152903A JP6551591B2 (ja) 2017-12-07 2018-08-15 加熱用包装袋

Publications (1)

Publication Number Publication Date
WO2019111733A1 true WO2019111733A1 (fr) 2019-06-13

Family

ID=66750164

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/043236 WO2019111733A1 (fr) 2017-12-07 2018-11-22 Sac d'emballage destiné à chauffer

Country Status (1)

Country Link
WO (1) WO2019111733A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021090791A1 (fr) * 2019-11-06 2021-05-14 東洋製罐株式会社 Poche destinée à un usage dans un four à micro-ondes

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005335336A (ja) * 2004-05-31 2005-12-08 Dainippon Printing Co Ltd 横柄エンボス化粧シート及び横柄エンボス化粧板
JP2006143223A (ja) * 2004-11-16 2006-06-08 Dainippon Printing Co Ltd 電子レンジ加熱用包装袋
JP2014151945A (ja) * 2013-02-08 2014-08-25 Toyo Seikan Kaisha Ltd 電子レンジ加熱用包装材、電子レンジ加熱用包装袋、及び電子レンジ加熱用包装食品

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005335336A (ja) * 2004-05-31 2005-12-08 Dainippon Printing Co Ltd 横柄エンボス化粧シート及び横柄エンボス化粧板
JP2006143223A (ja) * 2004-11-16 2006-06-08 Dainippon Printing Co Ltd 電子レンジ加熱用包装袋
JP2014151945A (ja) * 2013-02-08 2014-08-25 Toyo Seikan Kaisha Ltd 電子レンジ加熱用包装材、電子レンジ加熱用包装袋、及び電子レンジ加熱用包装食品

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021090791A1 (fr) * 2019-11-06 2021-05-14 東洋製罐株式会社 Poche destinée à un usage dans un four à micro-ondes
JP2021075289A (ja) * 2019-11-06 2021-05-20 東洋製罐株式会社 電子レンジ用パウチ
CN114599590A (zh) * 2019-11-06 2022-06-07 东洋制罐株式会社 微波炉用袋

Similar Documents

Publication Publication Date Title
KR102218933B1 (ko) 전자레인지 가열용 포장 주머니
JP5790497B2 (ja) 多層積層易開封包装体
US20180111359A1 (en) Multi-ply films for sterilization or pasteurization processes
JP6790471B2 (ja) 包装体
JP6728683B2 (ja) 多層フィルム
JP4450639B2 (ja) 電子レンジ調理用袋
WO2019111733A1 (fr) Sac d'emballage destiné à chauffer
JP6318737B2 (ja) ボイル処理用食品包装フィルム、深絞り包装体用底材、および深絞り包装体
JP6740837B2 (ja) 再封性およびデッドホールド性を有するシーラントフィルム
JP6551591B2 (ja) 加熱用包装袋
US20180079577A1 (en) Heat-Resistant Easy-Open Package
JP6805685B2 (ja) 再封性シーラントフィルム
JP2002104474A (ja) 蓋材および軟包装体
JP2005035574A (ja) レトルト殺菌処理可能な紙カップ容器
JP6657816B2 (ja) 包装体
JP3739677B2 (ja) 蓋材およびそれを用いた包装体
JP6859699B2 (ja) 再封性シーラントフィルム
JP7404754B2 (ja) 電子レンジ加熱用包装袋
JP2020164178A (ja) 包装材料および包装体
JPH1086296A (ja) 多層シート及び易開封容器
JP7077658B2 (ja) 電子レンジ加熱用の包装袋及び包装食品
JP6880966B2 (ja) 蒸気抜きパウチおよびパウチの製造方法
JP6900638B2 (ja) 包装体
JP2004216631A (ja) 複合フィルム
JP7106830B2 (ja) 包装材

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18885568

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18885568

Country of ref document: EP

Kind code of ref document: A1