WO2019017315A1 - 非水電解質二次電池電極用バインダー及びその用途 - Google Patents

非水電解質二次電池電極用バインダー及びその用途 Download PDF

Info

Publication number
WO2019017315A1
WO2019017315A1 PCT/JP2018/026640 JP2018026640W WO2019017315A1 WO 2019017315 A1 WO2019017315 A1 WO 2019017315A1 JP 2018026640 W JP2018026640 W JP 2018026640W WO 2019017315 A1 WO2019017315 A1 WO 2019017315A1
Authority
WO
WIPO (PCT)
Prior art keywords
mass
binder
secondary battery
electrolyte secondary
monomer
Prior art date
Application number
PCT/JP2018/026640
Other languages
English (en)
French (fr)
Inventor
朋子 仲野
直彦 斎藤
剛史 長谷川
松崎　英男
Original Assignee
東亞合成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東亞合成株式会社 filed Critical 東亞合成株式会社
Priority to JP2019531024A priority Critical patent/JP7078047B2/ja
Publication of WO2019017315A1 publication Critical patent/WO2019017315A1/ja

Abstract

本明細書は、非水電解質二次電池用水系バインダー、並びに、当該バインダーを用いて得られる非水電解質二次電池電極合剤層用組成物及び非水電解質二次電池電極を提供する。バインダーは、架橋重合体又はその塩を含有し、前記架橋重合体は、エチレン性不飽和カルボン酸単量体に由来する構造単位を含み、塩基化合物存在下、１３．０質量％以上の単量体濃度で重合して得られたものであり、かつ、中和度８０～１００モル％に中和された後、水媒体中で測定した粒子径が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下である。

Description

非水電解質二次電池電極用バインダー及びその用途
　本発明はリチウムイオン二次電池等に使用可能な非水電解質二次電池電極用バインダー及びその用途、並びに、該バインダーに用いられるカルボキシル基含有架橋重合体又はその塩の製造方法に関する。
　非水電解質二次電池としては、例えばリチウムイオン二次電池がよく知られている。非水電解質二次電池電極は、活物質及びバインダー等を含む電極合剤層を形成するための組成物を集電体上に塗布・乾燥等することにより作製される。負極合剤層組成物に用いられるバインダーとしては、スチレンブタジエンゴム（ＳＢＲ）ラテックス及びカルボキシメチルセルロース（ＣＭＣ）を含む水系のバインダーが使用されている。また、分散性及び結着性に優れるバインダーとして、アクリル酸系重合体水溶液又は水分散液を含むバインダーが知られている。一方、正極合剤層に用いられるバインダーとしては、ポリフッ化ビニリデン（ＰＶＤＦ）のＮ－メチル－２－ピロリドン（ＮＭＰ）溶液が広く使用されている。しかし、近年の環境意識の高まりを背景に、正極合剤層組成物に対しても有機溶剤を使用しない水系化の要求が高まっている。
　一方、リチウムイオン二次電池の用途が拡大するにつれて、エネルギー密度、信頼性及び耐久性向上への要求が強まる傾向にある。例えば、リチウムイオン二次電池の電気容量を高める目的で、負極用活物質としてシリコン系の活物質を用いる仕様が増えてきている。しかしながら、シリコン系活物質は充放電時の体積変化が大きいことが知られており、繰り返し使用するにつれて電極合剤層の剥離又は脱落等が生じ、その結果、電池の容量が低下し、サイクル特性（耐久性）が悪化するという問題があった。このような不具合を抑制するためには、一般的にはバインダーの結着性を高めることが有効であり、耐久性を改善する目的で、バインダーの結着性向上に関する検討が行われている。
　出願人は、これまでに、シリコン系活物質を含む電極にも適用可能な結着性に優れるバインダーとして、架橋型アクリル酸系重合体を含むバインダーを開示している。
　例えば、特許文献１では、エチレン性不飽和カルボン酸単量体を構成単量体とし、中和度９０モル％において特定の水分散液粘度を有する架橋重合体（塩）を含むバインダーを開示している。特許文献２では、カルボキシル基を有する架橋重合体又はその塩であって、中和後に塩水中に分散させた際の粒子径が十分小さい重合体を含むバインダーを開示している。
国際公開第２０１６／１５８９３９号 国際公開第２０１７／０７３５８９号
　特許文献１及び２に開示されるバインダーはいずれも優れた結着性を有するものであるが、リチウムイオン二次電池の性能向上に伴い、より結着力の高いバインダーを求める要求が高まりつつある。
　一般に、結着性を高めるためには、バインダーとなる重合体の分子量を高めることが効果的である。また、分子量の高い重合体を製造するためには、モノマー濃度の高い条件で重合反応を行うことが有効であることが知られている。さらに、得られる重合体は、分散安定性に優れ、電極組成物中において、合一等することなく小粒子の重合体粒子として存在するものの方が、電極合剤層における均一分散性に優れるとともに、活物質等との接着点が増えるため、結着性を向上する観点からも好ましいと考えられる。
　特許文献１に記載のバインダーは、実施例において、２０質量％を超える高い単量体濃度で重合して得られた架橋重合体が開示されているが、結着性には更なる向上の余地があった。架橋重合体の粒子径が十分小さいものでない点に起因するものと推定される。特許文献２に記載のバインダーも優れた結着性を示すことが開示されているが、実施例において開示されている各架橋重合体の重合時の単量体濃度は、約１０質量％程度である。特許文献２に記載の架橋重合体について、結着性の更なる改善を目的に重合時の単量体濃度を高めた場合には、重合安定性及び重合体の分散安定性が十分ではなく、結着性を大きく改善することは難しいことが分かった。
　本開示は、このような事情に鑑みてなされたものであり、従来よりも優れた結着性を備える非水電解質二次電池電極用水系バインダーを提供する。また、本開示は、上記バインダーを用いて得られる非水電解質二次電池電極合剤層用組成物及び非水電解質二次電池電極も提供する。
　本発明者らは、上記課題を解決するために鋭意検討した結果、塩基化合物存在下、エチレン性不飽和カルボン酸単量体を含む単量体成分を高い単量体濃度で重合して得られたものであって、粒子径が十分小さい架橋重合体又はその塩を含むバインダーが、電極活物質等によく結着し、当該バインダーを含む電極合剤層は、優れた結着性を示すという知見を得た。本発明はこれらの知見に基づいて完成されたものである。
　本発明は以下の通りである。
〔１〕架橋重合体又はその塩を含有する非水電解質二次電池電極用バインダーであって、
　前記架橋重合体は、エチレン性不飽和カルボン酸単量体に由来する構造単位を含み、塩基化合物存在下、１３．０質量％以上の単量体濃度で重合して得られたものであり、かつ、中和度８０～１００モル％に中和された後、水媒体中で測定した粒子径が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下である、非水電解質二次電池電極用バインダー。
〔２〕前記塩基化合物は、有機アミン化合物である前記〔１〕に記載の非水電解質二次電池電極用バインダー。
〔３〕前記有機アミン化合物は、当該有機アミン化合物に存在する窒素原子数に対する炭素原子数の比で表される値（Ｃ／Ｎ）が３以上である前記〔２〕に記載の非水電解質二次電池電極用バインダー。
〔４〕前記架橋重合体の重合に用いる単量体の総量に対する前記エチレン性不飽和カルボン酸単量体の濃度が、１０質量％以上、１００質量％以下である前記〔１〕～〔３〕のいずれか一に記載の非水電解質二次電池電極用バインダー。
〔５〕前記エチレン性不飽和カルボン酸単量体に対する前記塩基化合物の使用量が、０．００１モル％以上、４．０モル％以下である前記〔１〕～〔４〕のいずれか一に記載の非水電解質二次電池電極用バインダー。
〔６〕非水電解質二次電池電極用バインダーに用いられる架橋重合体又はその塩の製造方法であって、
　塩基化合物存在下、エチレン性不飽和カルボン酸単量体を含む単量体成分を１３．０質量％以上の単量体濃度で沈殿重合法により重合する重合工程を備え、
　前記架橋重合体又はその塩は、中和度８０～１００モル％に中和された後、水媒体中で測定した粒子径が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下である、方法。
〔７〕前記〔１〕～〔５〕のいずれか一に記載のバインダー、活物質及び水を含む非水電解質二次電池電極合剤層用組成物。
〔８〕負極活物質として炭素系材料またはケイ素系材料を含む前記〔７〕に記載の非水電解質二次電池電極合剤層用組成物。
〔９〕集電体表面に、前記〔７〕又は〔８〕に記載の非水電解質二次電池電極合剤層用組成物から形成される合剤層を備えた非水電解質二次電池電極。
　本発明の非水電解質二次電池電極用バインダーは、電極活物質等に対して優れた結着性を示す。また、上記バインダーは、集電体とも良好な接着性を発揮することができる。このため、上記バインダーを含む電極合剤層及びこれを備えた電極は、結着性に優れるとともにその一体性を維持することができる。このため、充放電に伴う活物質の体積変化、及び形状変化によって電極合剤層が劣化することが抑制され、耐久性（サイクル特性）の高い二次電池を得ることが可能となる。
　本発明の非水電解質二次電池電極合剤層用組成物は、電極材料に対する良好な結着性と集電体に対する良好な接着性とを有するため、一体性の良好な電極合剤層を形成でき、電極特性の良好な非水電解質二次電池電極を得ることが可能となる。
　本発明の非水電解質二次電池電極用バインダーは、架橋重合体又はその塩を含有するものであり、活物質及び水と混合することにより電極合剤層組成物とすることができる。上記の組成物は、集電体への塗工が可能なスラリー状態であってもよいし、湿粉状態として調製し、集電体表面へのプレス加工に対応できるようにしてもよい。銅箔又はアルミニウム箔等の集電体表面に上記組成物から形成される合剤層を形成することにより、本発明の非水電解質二次電池電極が得られる。
　以下に、本発明の非水電解質二次電池電極用バインダー及び当該バインダーに用いられる架橋重合体の製造方法、並びに、当該バインダーを用いて得られる非水電解質二次電池電極合剤層用組成物及び非水電解質二次電池電極の各々について詳細に説明する。
　尚、本明細書において、「（メタ）アクリル」とは、アクリル及び／又はメタクリルを意味し、「（メタ）アクリレート」とは、アクリレート及び／又はメタクリレートを意味する。また、「（メタ）アクリロイル基」とは、アクリロイル基及び／又はメタクリロイル基を意味する。
＜バインダー＞
　本発明のバインダーは、カルボキシル基を有する架橋重合体又はその塩を含む。カルボキシル基を有する架橋重合体又はその塩は、エチレン性不飽和カルボン酸に由来する構造単位を有していてもよい。
＜架橋重合体の構造単位＞
＜エチレン性不飽和カルボン酸単量体に由来する構造単位＞
　架橋重合体は、エチレン性不飽和カルボン酸単量体に由来する構造単位（以下、「（ａ）成分」ともいう）を有することができる。架橋重合体が、係る構造単位を有することによりカルボキシル基を有する場合、集電体への接着性が向上するとともに、リチウムイオンの脱溶媒和効果及びイオン伝導性に優れるため、抵抗が小さく、ハイレート特性に優れた電極が得られる。また、水膨潤性が付与されるため、合剤層組成物中における活物質等の分散安定性を高めることができる。
　上記（ａ）成分は、例えば、エチレン性不飽和カルボン酸単量体を含む単量体を重合することにより架橋重合体に導入することができる。その他にも、（メタ）アクリル酸エステル単量体を（共）重合した後、加水分解することによっても得られる。また、（メタ）アクリルアミド及び（メタ）アクリロニトリル等を重合した後、強アルカリで処理してもよいし、水酸基を有する重合体に酸無水物を反応させる方法であってもよい。
　エチレン性不飽和カルボン酸単量体としては、（メタ）アクリル酸、イタコン酸、クロトン酸、マレイン酸、フマル酸；（メタ）アクリルアミドヘキサン酸及び（メタ）アクリルアミドドデカン酸等の（メタ）アクリルアミドアルキルカルボン酸；コハク酸モノヒドロキシエチル（メタ）アクリレート、ω－カルボキシ－カプロラクトンモノ（メタ）アクリレート、β－カルボキシエチル（メタ）アクリレート等のカルボキシル基を有するエチレン性不飽和単量体またはそれらの（部分）アルカリ中和物が挙げられ、これらの内の１種を単独で使用してもよいし、２種以上を組み合わせて使用してもよい。上記の中でも、重合速度が大きいために一次鎖長の長い重合体が得られ、バインダーの結着力が良好となる点で重合性官能基としてアクリロイル基を有する化合物が好ましく、特に好ましくはアクリル酸である。エチレン性不飽和カルボン酸単量体としてアクリル酸を用いた場合、カルボキシル基含有量の高い重合体を得ることができる。
　架橋重合体における（ａ）成分の含有量は、特に限定するものではないが、例えば、架橋重合体の全構造単位に対して１０質量％以上、１００質量％以下含むことができる。かかる範囲で（ａ）成分を含有することで、集電体に対する優れた接着性を容易に確保することができる。下限は、例えば２０質量％以上であり、また例えば３０質量％以上であり、また例えば４０質量％以上である。下限は、５０質量％以上であってもよく、例えば、６０質量％以上であり、また例えば７０質量％以上であり、また例えば８０質量％以上である。また、上限は、例えば、９９質量％以下であり、また例えば９８質量％以下であり、また例えば９５質量％以下であり、また例えば９０質量％以下である。範囲としては、こうした下限及び上限を適宜組み合わせた範囲とすることができるが、例えば、１０質量％以上、１００質量％以下であり、また例えば２０質量％以上、１００質量％以下であり、また例えば３０質量％以上、１００質量％以下であり、また例えば５０質量％以上、９９質量％以下などとすることができる。全構造単位に対する（ａ）成分の割合が１０質量％未満の場合、分散安定性、結着性及び電池としての耐久性が不足する場合があり得る。
＜その他の構造単位＞
　本発明の架橋重合体は、（ａ）成分以外に、これらと共重合可能な他のエチレン性不飽和単量体に由来する構造単位（以下、「（ｂ）成分」ともいう。）を含むことができる。（ｂ）成分としては、例えば、スルホン酸基及びリン酸基等のカルボキシル基以外のアニオン性基を有するエチレン性不飽和単量体化合物、または非イオン性のエチレン性不飽和単量体等に由来する構造単位が挙げられる。これらの構造単位は、スルホン酸基及びリン酸基等のカルボキシル基以外のアニオン性基を有するエチレン性不飽和単量体化合物、または非イオン性のエチレン性不飽和単量体を含む単量体を共重合することにより導入することができる。これらの内でも、（ｂ）成分としては、耐屈曲性良好な電極が得られる観点から非イオン性のエチレン性不飽和単量体に由来する構造単位が好ましく、バインダーの結着性が優れる点で（メタ）アクリルアミド及びその誘導体等が好ましい。また、（ｂ）成分として水中への溶解性が１ｇ／１００ｍｌ以下の疎水性のエチレン性不飽和単量体に由来する構造単位を導入した場合、電極材料と強い相互作用を奏することができ、活物質に対して良好な結着性を発揮することができる。これにより、堅固で一体性の良好な電極合剤層を得ることができるため好ましい。特に脂環構造含有エチレン性不飽和単量体に由来する構造単位が好ましい。
　（ｂ）成分の割合は、架橋重合体の全構造単位に対し、０質量％以上、９０質量％以下とすることができる。（ｂ）成分の割合は、１質量％以上、６０質量％以下であってもよく、２質量％以上、５０質量％以下であってもよく、５質量％以上、４０質量％以下であってもよく、１０質量％以上、３０質量％以下であってもよい。また、架橋重合体の全構造単位に対して（ｂ）成分を１質量％以上含む場合、電解液への親和性が向上するため、リチウムイオン電導性が向上する効果も期待できる。
　（メタ）アクリルアミド誘導体としては、例えば、イソプロピル（メタ）アクリルアミド、ｔ－ブチル（メタ）アクリルアミド、Ｎ－ｎ－ブトキシメチル（メタ）アクリルアミド、Ｎ－イソブトキシメチル（メタ）アクリルアミド等のＮ－アルキル（メタ）アクリルアミド化合物；ジメチル（メタ）アクリルアミド、ジエチル（メタ）アクリルアミド等のＮ，Ｎ－ジアルキル（メタ）アクリルアミド化合物が挙げられ、これらの内の１種を単独で使用してもよいし、２種以上を組み合わせて使用してもよい。
　脂環構造含有エチレン性不飽和単量体としては、例えば、（メタ）アクリル酸シクロペンチル、（メタ）アクリル酸シクロヘキシル、（メタ）アクリル酸メチルシクロヘキシル、（メタ）アクリル酸ｔ－ブチルシクロヘキシル、（メタ）アクリル酸シクロデシル及び（メタ）アクリル酸シクロドデシル等の脂肪族置換基を有していてもよい（メタ）アクリル酸シクロアルキルエステル；（メタ）アクリル酸イソボルニル、（メタ）アクリル酸アダマンチル、（メタ）アクリル酸ジシクロペンテニル、（メタ）アクリル酸ジシクロペンテニルオキシエチル、（メタ）アクリル酸ジシクロペンタニル、並びに、シクロヘキサンジメタノールモノ（メタ）アクリレート及びシクロデカンジメタノールモノ（メタ）アクリレート等のシクロアルキルポリアルコールモノ（メタ）アクリレート等が挙げられ、これらの内の１種を単独で使用してもよいし、２種以上を組み合わせて使用してもよい。上記の中でも、重合速度が大きいために一次鎖長の長い重合体が得られ、バインダーの結着力が良好となる点で重合性官能基としてアクリロイル基を有する化合物が好ましい。
　その他の非イオン性のエチレン性不飽和単量体としては、例えば（メタ）アクリル酸エステルを用いてもよい。（メタ）アクリル酸エステルとしては、例えば、（メタ）アクリル酸メチル、（メタ）アクリル酸エチル、（メタ）アクリル酸ブチル、（メタ）アクリル酸イソブチル及び（メタ）アクリル酸２－エチルヘキシル等の（メタ）アクリル酸アルキルエステル化合物；
（メタ）アクリル酸フェニル、（メタ）アクリル酸フェニルメチル、（メタ）アクリル酸フェニルエチル等の（メタ）アクリル酸アラルキルエステル化合物；
（メタ）アクリル酸２－メトキシエチル、（メタ）アクリル酸エトキシエチル等の（メタ）アクリル酸アルコキシアルキルエステル化合物；
（メタ）アクリル酸ヒドロキシエチル、（メタ）アクリル酸ヒドロキシプロピル及び（メタ）アクリル酸ヒドロキシブチル等の（メタ）アクリル酸ヒドロキシアルキルエステル化合物等が挙げられ、これらの内の１種を単独で使用してもよいし、２種以上を組み合わせて使用してもよい。活物質との密着性及びサイクル特性の観点からは、（メタ）アクリル酸アラルキルエステル化合物を好ましく用いることができる。
　リチウムイオン伝導性及びハイレート特性がより向上する観点から、（メタ）アクリル酸２－メトキシエチル及び（メタ）アクリル酸エトキシエチルなどの（メタ）アクリル酸アルコキシアルキル類等、エーテル結合を有する化合物が好ましく、（メタ）アクリル酸２－メトキシエチルがより好ましい。
　非イオン性のエチレン性不飽和単量体の中でも、重合速度が速いために一次鎖長の長い重合体が得られ、バインダーの結着力が良好となる点でアクリロイル基を有する化合物が好ましい。また、非イオン性のエチレン性不飽和単量体としては、得られる電極の耐屈曲性が良好となる点でホモポリマーのガラス転移温度（Ｔｇ）が０℃以下の化合物が好ましい。
　架橋重合体は塩であってもよい。塩の種類としては特に限定しないが、リチウム、ナトリウム、カリウム等のアルカリ金属塩；カルシウム塩及びバリウム塩等のアルカリ土類金属塩；マグネシウム塩、アルミニウム塩等のその他の金属塩；アンモニウム塩及び有機アミン塩等が挙げられる。これらの中でも電池特性への悪影響が生じにくい点からアルカリ金属塩及びマグネシウム塩が好ましく、アルカリ金属塩がより好ましい。
＜架橋重合体の態様＞
　本発明の架橋重合体における架橋方法は特に制限されるものではなく、例えば以下の方法による態様が例示される。
１）架橋性単量体の共重合
２）ラジカル重合時のポリマー鎖への連鎖移動を利用
３）反応性官能基を有する重合体を合成後、必要に応じて架橋剤を添加して後架橋
　上記の内でも、操作が簡便であり、架橋の程度を制御し易い点から架橋性単量体の共重合による方法が好ましい。
＜架橋性単量体＞
　架橋性単量体としては、２個以上の重合性不飽和基を有する多官能重合性単量体、及び加水分解性シリル基等の自己架橋可能な架橋性官能基を有する単量体等が挙げられる。
　上記多官能重合性単量体は、（メタ）アクリロイル基、アルケニル基等の重合性官能基を分子内に２つ以上有する化合物であり、多官能（メタ）アクリレート化合物、多官能アルケニル化合物、（メタ）アクリロイル基及びアルケニル基の両方を有する化合物等が挙げられる。これらの化合物は、１種のみを単独で用いてもよいし、２種以上を組み合わせて用いてもよい。これらの内でも、均一な架橋構造を得やすい点で多官能アルケニル化合物が好ましく、分子内に複数のアリルエーテル基を有する多官能アリルエーテル化合物が特に好ましい。
　多官能（メタ）アクリレート化合物としては、エチレングリコールジ（メタ）アクリレート、プロピレングリコールジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレート、ポリプロピレングリコールジ（メタ）アクリレート等の２価アルコールのジ（メタ）アクリレート類；トリメチロールプロパントリ（メタ）アクリレート、トリメチロールプロパンエチレンオキサイド変性体のトリ（メタ）アクリレート、グリセリントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート等の３価以上の多価アルコールのトリ（メタ）アクリレート、テトラ（メタ）アクリレート等のポリ（メタ）アクリレート；メチレンビスアクリルアミド、ヒドロキシエチレンビスアクリルアミド等のビスアミド類等を挙げることができる。
　多官能アルケニル化合物としては、トリメチロールプロパンジアリルエーテル、トリメチロールプロパントリアリルエーテル、ペンタエリスリトールジアリルエーテル、ペンタエリスリトールトリアリルエーテル、テトラアリルオキシエタン、ポリアリルサッカロース等の多官能アリルエーテル化合物；ジアリルフタレート等の多官能アリル化合物；ジビニルベンゼン等の多官能ビニル化合物等を挙げることができる。
　（メタ）アクリロイル基及びアルケニル基の両方を有する化合物としては、（メタ）アクリル酸アリル、（メタ）アクリル酸イソプロペニル、（メタ）アクリル酸ブテニル、（メタ）アクリル酸ペンテニル、（メタ）アクリル酸２－（２－ビニロキシエトキシ）エチル等を挙げることができる。
　上記自己架橋可能な架橋性官能基を有する単量体の具体的な例としては、加水分解性シリル基含有ビニル単量体、Ｎ－メチロール（メタ）アクリルアミド、Ｎ－メトキシアルキル（メタ）アクリレート等が挙げられる。これらの化合物は、１種単独であるいは２種以上を組み合わせて用いることができる。
　加水分解性シリル基含有ビニル単量体としては、加水分解性シリル基を少なくとも１個有するビニル単量体であれば、特に限定されない。例えば、ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルメチルジメトキシシラン、ビニルジメチルメトキシシランン等のビニルシラン類；アクリル酸トリメトキシシリルプロピル、アクリル酸トリエトキシシリルプロピル、アクリル酸メチルジメトキシシリルプロピル等のシリル基含有アクリル酸エステル類；メタクリル酸トリメトキシシリルプロピル、メタクリル酸トリエトキシシリルプロピル、メタクリル酸メチルジメトキシシリルプロピル、メタクリル酸ジメチルメトキシシリルプロピル等のシリル基含有メタクリル酸エステル類；トリメトキシシリルプロピルビニルエーテル等のシリル基含有ビニルエーテル類；トリメトキシシリルウンデカン酸ビニル等のシリル基含有ビニルエステル類等を挙げることができる。
　架橋重合体が架橋性単量体により架橋されたものである場合、上記架橋性単量体の使用量は、架橋性単量体以外の単量体（非架橋性単量体）の総量に対して０．０２～０．７モル％であることが好ましく、０．０３～０．４モル％であることがより好ましい。架橋性単量体の使用量が０．０２モル％以上であれば結着性及び合剤層スラリーの安定性がより良好となる点で好ましい。０．７モル％以下であれば、架橋重合体の安定性が高くなる傾向がある。
＜架橋重合体の粒子径＞
　合剤層組成物において、架橋重合体が大粒径の塊（二次凝集体）として存在することなく、適度な粒径を有する水膨潤粒子として良好に分散している場合、当該架橋重合体を含むバインダーが良好な結着性能を発揮し得るため好ましい。
　本発明の架橋重合体又はその塩は、該架橋重合体が有するカルボキシル基に基づく中和度が８０～１００モル％であるものを水中に分散させた際の粒子径（水膨潤粒子径）が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下の範囲にあることが好ましい。上記粒子径のより好ましい範囲は０．２μｍ以上、５．０μｍ以下であり、さらに好ましい範囲は０．５μｍ以上、３．０μｍ以下である。粒子径が０．１μｍ以上、１０μｍ以下の範囲であれば、合剤層組成物中において好適な大きさで均一に存在するため、合剤層組成物の安定性が高く、優れた結着性を発揮することが可能となる。粒子径が１０μｍを超えると、上記の通り結着性が不十分となる虞がある。一方、粒子径が０．１μｍ未満の場合には、安定製造性の観点において懸念される。
　なお、上記水膨潤粒子径は、本明細書実施例に記載の方法により測定することができる。
　架橋重合体が未中和若しくは中和度８０モル％未満の場合は、アルカリ金属水酸化物等により中和度８０～１００モル％に中和し、水中に分散させた際の粒子径を測定すればよい。一般に、架橋重合体又はその塩は、粉末または溶液（分散液）の状態では一次粒子が会合、凝集した塊状粒子として存在する場合が多い。上記の水分散させた際の粒子径が上記範囲である場合、当該架橋重合体又はその塩は極めて優れた分散性を有するものであり、中和度８０～１００モル％に中和して水分散することにより塊状粒子が解れ、ほぼ一次粒子の分散体、若しくは２次凝集体であっても、その粒子径が０．１～１０μｍの範囲内にある、安定な分散状態を形成するものである。
　水膨潤粒子径の体積平均メジアン径を個数平均メジアン径で除した値である粒子径分布は、結着性の観点から好ましくは１０以下であり、より好ましくは３．０以下であり、さらに好ましくは１．５以下である。上記粒子径分布の下限値は、通常は１．０である。
　また、本発明の架橋重合体又はその塩の乾燥時における粒子径（乾燥粒子径）は、体積基準メジアン径で０．０３μｍ以上、３μｍ以下の範囲にあることが好ましい。上記粒子径のより好ましい範囲は０．１μｍ以上、１μｍ以下であり、さらに好ましい範囲は０．３μｍ以上、０．８μｍ以下である。
　なお、上記乾燥粒子径は、本明細書実施例に記載の方法により測定することができる。
　一般に、架橋重合体は、そのポリマー鎖の長さ（一次鎖長）が長いほど強靭さが増大し、高い結着性を得ることが可能となるとともに、その水分散液の粘度が上昇する。また、長い一次鎖長を有するポリマーに比較的少量の架橋を施して得られた架橋重合体（塩）は、水中では水に膨潤したミクロゲル体として存在する。本発明の電極合剤層用組成物においては、このミクロゲル体の相互作用により増粘効果や分散安定化効果が発現される。ミクロゲル体の相互作用はミクロゲル体の水膨潤度、およびミクロゲル体の強度によって変化するが、これらは架橋重合体の架橋度により影響を受ける。架橋度が低すぎる場合はミクロゲルの強度が不足して、分散安定化効果や結着性が不足する場合がある。一方架橋度が高すぎる場合は、ミクロゲルの膨潤度が不足して分散安定化効果や結着性が不足する場合がある。すなわち、架橋重合体としては、十分に長い一次鎖長を有する重合体に適度な架橋を施した微架橋重合体であることが望ましい。
　架橋重合体又はその塩は、合剤層組成物中において、中和度が２０～１００モル％となるように、エチレン性不飽和カルボン酸単量体由来のカルボキシル基等の酸基が中和され、塩の態様として用いることが好ましい。上記中和度は５０～１００モル％であることがより好ましく、６０～９５モル％であることがさらに好ましい。中和度が２０モル％以上の場合、水膨潤性が良好となり分散安定化効果が得やすいという点で好ましい。本明細書では、上記中和度は、カルボキシル基等の酸基を有する単量体及び中和に用いる中和剤の仕込み値から計算により算出することができる。なお、中和度は架橋重合体又はその塩を、減圧条件下、８０℃で３時間乾燥処理後の粉末をＩＲ測定し、カルボン酸のＣ＝Ｏ基由来のピークとカルボン酸塩のＣ＝Ｏ基由来のピークの強度比より確認することができる。
　本発明の架橋重合体又はその塩は、２質量％水溶液の粘度が５００ｍＰａ・ｓ以下であり、４質量％水溶液の粘度が５０００ｍＰａ・ｓ以上であることが好ましい。上記２質量％水溶液の粘度は、より好ましくは３００ｍＰａ・ｓ以下であり、さらに好ましくは１００ｍＰａ・ｓ以下である。また、上記４質量％水溶液の粘度は、より好ましくは１００００ｍＰａ・ｓ以上であり、さらに好ましくは３００００ｍＰａ・ｓ以上である。
　２質量％水溶液の粘度が５００ｍＰａ・ｓ以下であれば、後述する合剤層用組成物の粘度が十分低くなるため、塗工性が良好なものとなる。尚、結着性の観点から、２質量％水溶液の粘度は１ｍＰａ・ｓ以上であることが好ましい。
　４質量％水溶液の粘度が５０００ｍＰａ・ｓ以上であれば、合剤層用組成物の安定性が確保されるとともに、良好な結着性を示す。尚、塗工性の観点から、４質量％水溶液の粘度は１００００００ｍＰａ・ｓ以下であることが好ましい。
　本発明の架橋重合体又はその塩は、水中では水を吸収して膨潤した状態となる。よって、水溶液中の濃度が高くなり、架橋重合体同士のパッキングが十分な状態に至ると水溶液の粘度は急激に上昇する。
　一般に、架橋重合体が適度な架橋度を有する場合、当該架橋重合体が有する親水性基の量が多いほど、架橋重合体は水を吸収して膨潤し易くなる。また、架橋度についていえば、架橋度が低いほど、架橋重合体は膨潤し易くなる。ただし、架橋点の数が同じであっても、分子量（一次鎖長）が大きいほど三次元ネットワークの形成に寄与する架橋点が増えるため、架橋重合体は膨潤し難くなる。よって、架橋重合体の親水性基の量、架橋点の数及び一次鎖長等を調整することにより、上記２質量％水溶液及び４質量％水溶液の粘度を調節することができる。この際、上記架橋点の数は、例えば、架橋性単量体の使用量、ポリマー鎖への連鎖移動反応及び後架橋反応等により調整が可能である。また、重合体の一次鎖長は、開始剤及び重合温度等のラジカル発生量に関連する条件の設定、並びに、連鎖移動等を考慮した重合溶媒の選択等により調整することができる。
　水溶液粘度は、合剤層用組成物の粘度に大きく影響を及ぼすため、上記の粘度特性を満たす架橋重合体（塩）をバインダーとして使用することにより、高濃度であっても塗工性に優れる合剤層用組成物が得られる。さらに、上記の粘度特性を満たすように架橋度及び分子量等が調節された架橋重合体又はその塩は、バインダーとして優れた結着性を発揮するため、より高い合剤層剥離強度を得ることができる。
＜架橋重合体又はその塩の製造方法＞
　架橋重合体は、溶液重合、沈殿重合、懸濁重合、乳化重合等の公知の重合方法を使用することが可能であるが、生産性の点で沈殿重合及び懸濁重合（逆相懸濁重合）が好ましい。結着性等に関してより良好な性能が得られる点で、沈殿重合、懸濁重合、乳化重合等の不均一系の重合法が好ましく、中でも沈殿重合法がより好ましい。
　沈殿重合は、原料である不飽和単量体を溶解するが、生成する重合体を実質溶解しない溶媒中で重合反応を行うことにより重合体を製造する方法である。重合の進行とともにポリマー粒子は凝集及び成長により大きくなり、数十ｎｍ～数百ｎｍの一次粒子が数μｍ～数十μｍに二次凝集したポリマー粒子の分散液が得られる。ポリマーの粒子サイズを制御するために分散安定剤を使用することもできる。
　尚、分散安定剤や重合溶剤等を選定することにより上記二次凝集を抑制することもできる。一般に、二次凝集を抑制した沈殿重合は、分散重合とも呼ばれる。
　沈殿重合の場合、重合溶媒は、使用する単量体の種類等を考慮して水及び各種有機溶剤等から選択される溶媒を使用することができる。より一次鎖長の長い重合体を得るためには、連鎖移動定数の小さい溶媒を使用することが好ましい。
　具体的な重合溶媒としては、メタノール、ｔ－ブチルアルコール、アセトン、メチルエチルケトン、アセトニトリル及びテトラヒドロフラン等の水溶性溶剤の他、ベンゼン、酢酸エチル、ジクロロエタン、ｎ－ヘキサン、シクロヘキサン及びｎ－ヘプタン等が挙げられ、これらの１種を単独であるいは２種以上を組み合わせて用いることができる。又は、これらと水との混合溶媒として用いてもよい。本発明において水溶性溶剤とは、２０℃における水への溶解度が１０ｇ／１００ｍｌより大きいものを指す。
　上記の内、粗大粒子の生成や反応器への付着が小さく重合安定性が良好であること、析出した重合体微粒子が二次凝集しにくい（若しくは二次凝集が生じても水媒体中で解れやすい）こと、連鎖移動定数が小さく重合度（一次鎖長）の大きい重合体が得られること、及び後述する工程中和の際に操作が容易であること等の点で、メチルエチルケトン及びアセトニトリルが好ましい。
　また、同じく工程中和において中和反応を安定かつ速やかに進行させるため、重合溶媒中に高極性溶媒を少量加えておくことが好ましい。係る高極性溶媒としては、好ましくは水及びメタノールが挙げられる。高極性溶媒の使用量は、媒体の全質量に基づいて好ましくは０．０５～１０．０質量％であり、より好ましくは０．１～５．０質量％、さらに好ましくは０．１～１．０質量％である。高極性溶媒の割合が０．０５質量％以上であれば、上記中和反応への効果が認められ、１０．０質量％以下であれば重合反応への悪影響も見られない。また、アクリル酸等の親水性の高いエチレン性不飽和カルボン酸単量体の重合では、高極性溶媒を加えた場合には重合速度が向上し、一次鎖長の長い重合体を得やすくなる。高極性溶媒の中でも特に水は上記重合速度を向上させる効果が大きく好ましい。
　本発明では、架橋重合体は、塩基化合物の存在下、１３．０質量％以上の単量体濃度で重合して得られる。単量体濃度は好ましくは１５．０質量％以上であり、より好ましくは１７．０質量％以上であり、更に好ましくは１９．０質量％以上であり、一層好ましくは２０．０質量％以上である。単量体濃度はなお好ましくは２２．０質量％以上であり、より一層好ましくは２５．０質量％以上である。一般に、重合時の単量体濃度を高くするほど高分子量化が可能であり、一次鎖長の長い重合体を製造することができる。本発明の架橋重合体は、十分に長い一次鎖長を有する重合体に適度な架橋を施した微架橋重合体であるため、その一次鎖長を直接測定することは、分析的に困難である。一般的には、重合体の一次鎖長は溶液粘度と相関することが知られているが、架橋重合体の場合にはその架橋度によっても溶液粘度は変動する。
　よって、上記の方法で得られた架橋重合体を、当該重合体の構造又は特性で規定することは非常に困難である。
　なお、本明細書において「単量体濃度」とは、重合を開始する時点における反応液中の単量体濃度を示す。
　単量体濃度の上限値は、使用する単量体及び溶媒の種類、並びに、重合方法及び各種重合条件等により異なるが、重合反応熱の除熱が可能であれば、沈殿重合では概ね４０％程度、懸濁重合では概ね５０％程度、乳化重合では概ね７０％程度である。
　上記塩基化合物は、いわゆるアルカリ性化合物であり、無機塩基化合物及び有機塩基化合物の何れを用いてもよい。塩基化合物存在下において重合反応を行うことにより、例えば１３．０質量％を超えるような高い単量体濃度条件下であっても、重合反応を安定に実施することができる。また、このような高い単量体濃度で重合して得られた重合体は、分子量が高いため（一次鎖長が長いため）結着性にも優れる。
　無機塩基化合物としては、水酸化リチウム、水酸化ナトリウム、水酸化カリウム等のアルカリ金属水酸化物、水酸化カルシウム、水酸化マグネシウム等のアルカリ土類金属水酸化物等が挙げられ、これらの内の１種又は２種以上を用いることができる。
　有機塩基化合物としては、アンモニア及び有機アミン化合物が挙げられ、これらの内の１種又は２種以上を用いることができる。中でも、重合安定性及び得られる架橋重合体又はその塩を含むバインダーの結着性の観点から、有機アミン化合物が好ましい。
　有機アミン化合物としては、例えば、モノメチルアミン、ジメチルアミン、トリメチルアミン、モノエチルアミン、ジエチルアミン、トリエチルアミン、モノブチルアミン、ジブチルアミン、トリブチルアミン、モノヘキシルアミン、ジヘキシルアミン、トリヘキシルアミン、トリオクチルアミン及びトリドデシルアミン等のＮ－アルキル置換アミン；モノエタノールアミン、ジエタノールアミン、トリエタノールアミン、プロパノールアミン、ジメチルエタノールアミン及びＮ，Ｎ－ジメチルエタノールアミン等の（アルキル）アルカノールアミン；ピリジン、ピペリジン、ピペラジン、１，８－ビス（ジメチルアミノ）ナフタレン、モルホリン及びジアザビシクロウンデセン（ＤＢＵ）等の環状アミン；ジエチレントリアミン、Ｎ、Ｎ－ジメチルベンジルアミンが挙げられ、これらの内の１種又は２種以上を用いることができる。
　これらの内でも、長鎖アルキル基を有する疎水性アミンを用いた場合、より大きな静電反発及び立体反発が得られることから、単量体濃度の高い場合であっても重合安定性を確保しやすい点で好ましい。具体的には、有機アミン化合物に存在する窒素原子数に対する炭素原子数の比で表される値（Ｃ/Ｎ）が高い程、立体反発効果による重合安定化効果が高い。上記Ｃ／Ｎの値は、好ましくは３以上であり、より好ましくは５以上であり、さらに好ましくは１０以上であり、一層好ましくは２０以上である。
　Ｃ／Ｎ値の高いアミン化合物は、一般的には疎水性が高く、アミン価の低い化合物である。上記の通り、Ｃ／Ｎ値が高いアミン化合物は高い重合安定化効果を示す傾向があり、重合時の単量体濃度を高くすることが可能となるため、重合体が高分子量化（一次鎖長の増大）され、結着性が向上する傾向がある。また、Ｃ／Ｎ値の高いアミン化合物の存在下において重合を行った場合、粒子径の小さい架橋重合体又はその塩が得られる傾向がある。このため、活物質等との接着性が増加し、結着性が向上する。
　本製造方法では、エチレン性不飽和カルボン酸単量体を含む単量体成分を重合する重合工程を備えることが好ましい。例えば、（ａ）成分の由来となるエチレン性不飽和カルボン酸単量体を１０質量％以上、１００質量％以下、及び（ｂ）成分の由来となる他のエチレン性不飽和単量体０質量％以上、９０質量％以下を含む単量体成分を重合する重合工程を備えることが好ましい。
　上記重合工程により、架橋重合体には、エチレン性不飽和カルボン酸単量体に由来する構造単位（（ａ）成分）が１０質量％以上、１００質量％以下導入される。エチレン性不飽和カルボン酸単量体の使用量は、また例えば、２０質量％以上、１００質量％以下であり、また例えば、３０質量％以上、１００質量％以下であり、また例えば、５０質量％以上、９９質量％以下である。均一性に優れた小粒子径の重合体微粒子を得易い点で、上記重合工程は、沈殿重合法によることが好ましい。
　重合時には、上記エチレン性不飽和カルボン酸単量体に対し、０．００１モル％以上の塩基化合物を用いることが好ましい。０．００１モル％以上の塩基化合物存在下で重合反応を行うことにより、重合安定性を向上することができ、高い単量体濃度条件でも円滑に重合反応が進行する。エチレン性不飽和カルボン酸単量体に対する塩基化合物の使用量は、好ましくは０．０１モル％以上であり、より好ましくは０．０３モル％以上であり、さらに好ましくは０．０５モル％以上である。塩基化合物の使用量は、０．３モル％以上であってもよく、０．５モル％以上であってもよい。
　また、塩基化合物の使用量の上限は、４．０モル％以下であることが好ましい。４．０モル％以下の塩基化合物存在下で重合反応を行うことにより、重合安定性を向上することができ、高い単量体濃度条件でも円滑に重合反応が進行する。エチレン性不飽和カルボン酸単量体に対する塩基化合物の使用量は、好ましくは３．０モル％以下であり、より好ましくは２．０モル％以下であり、さらに好ましくは１．０モル％以下である。
　尚、本明細書では、塩基化合物の使用量は、エチレン性不飽和カルボン酸単量体に対して用いた塩基化合物のモル濃度を表したものであり、中和度を意味するものではない。すなわち、用いる塩基化合物の価数は考慮しない。
　本製造方法では、上記エチレン性不飽和カルボン酸単量体以外にも、これと共重合可能な他のエチレン性不飽和単量体を単量体成分として含んでよい。当該他のエチレン性不飽和単量体としては、例えば、スルホン酸基及びリン酸基等のカルボキシル基以外のアニオン性基を有するエチレン性不飽和単量体化合物、並びに、非イオン性のエチレン性不飽和単量体等が挙げられる。具体的な化合物としては、上述した（ｂ）成分を導入可能な単量体化合物が挙げられる。上記他のエチレン性不飽和単量体は、単量体成分の全量に対して０質量％以上、９０質量％以下含んでもよく、１質量％以上、６０質量％以下であってもよく、５質量％以上、５０質量％以下であってもよく、１０質量％以上、３０質量％以下であってもよい。また、同様に上記架橋性単量体を使用してもよい。
　重合開始剤は、アゾ系化合物、有機過酸化物、無機過酸化物等の公知の重合開始剤を用いることができるが、特に限定されるものではない。熱開始、還元剤を併用したレドックス開始、ＵＶ開始等、公知の方法で適切なラジカル発生量となるように使用条件を調整することができる。一次鎖長の長い架橋重合体を得るためには、製造時間が許容される範囲内で、ラジカル発生量がより少なくなるように条件を設定することが好ましい。
　上記アゾ系化合物としては、２，２’－アゾビス（２，４－ジメチルバレロニトリル）、２，２’－アゾビス（Ｎ－ブチル－２－メチルプロピオンアミド）、２－（ｔｅｒｔ－ブチルアゾ）－２－シアノプロパン、２，２’－アゾビス（２，４，４－トリメチルペンタン）、２，２’－アゾビス（２－メチルプロパン）等が挙げられ、これらの内の１種又は２種以上を用いることができる。
　上記有機過酸化物としては、２，２－ビス（４，４－ジ－ｔ－ブチルパーオキシシクロヘキシル）プロパン（日油社製、商品名「パーテトラＡ」）、１，１－ジ（ｔ－ヘキシルパーオキシ）シクロヘキサン（同「パーヘキサＨＣ」）、１，１－ジ（ｔ－ブチルパーオキシ）シクロヘキサン（同「パーヘキサＣ」）、ｎ－ブチル－４，４－ジ（ｔ－ブチルパーオキシ）バレレート（同「パーヘキサＶ」）、２，２－ジ（ｔ－ブチルパーオキシ）ブタン（同「パーヘキサ２２」）、ｔ－ブチルハイドロパーオキサイド（同「パーブチルＨ」）、クメンハイドロパーオキサイド（日油社製、商品名「パークミルＨ」）、１，１，３，３－テトラメチルブチルハイドロパーオキサイド（同「パーオクタＨ」）、ｔ－ブチルクミルパーオキサイド（同「パーブチルＣ」）、ジ－ｔ－ブチルパーオキサイド（同「パーブチルＤ」）、ジ－ｔ－ヘキシルパーオキサイド（同「パーヘキシルＤ」）、ジ（３，５，５－トリメチルヘキサノイル）パーオキサイド（同「パーロイル３５５」）、ジラウロイルパーオキサイド（同「パーロイルＬ」）、ビス（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート（同「パーロイルＴＣＰ」）、ジ－２－エチルヘキシルパーオキシジカーボネート（同「パーロイルＯＰＰ」）、ジ－ｓｅｃ－ブチルパーオキシジカーボネート（同「パーロイルＳＢＰ」）、クミルパーオキシネオデカノエート（同「パークミルＮＤ」）、１，１，３，３－テトラメチルブチルパーオキシネオデカノエート（同「パーオクタＮＤ」）、ｔ－ヘキシルパーオキシネオデカノエート（同「パーヘキシルＮＤ」）、ｔ－ブチルパーオキシネオデカノエート（同「パーブチルＮＤ」）、ｔ－ブチルパーオキシネオヘプタノエート（同「パーブチルＮＨＰ」）、ｔ－ヘキシルパーオキシピバレート（同「パーヘキシルＰＶ」）、ｔ－ブチルパーオキシピバレート（同「パーブチルＰＶ」）、２，５－ジメチル－２，５－ジ（２－エチルヘキサノイル）ヘキサン（同「パーヘキサ２５０」）、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート（同「パーオクタＯ」）、ｔ－ヘキシルパーオキシ－２－エチルヘキサノエート（同「パーヘキシルＯ」）、ｔ－ブチルパーオキシ－２－エチルヘキサノエート（同「パーブチルＯ」）、ｔ－ブチルパーオキシラウレート（同「パーブチルＬ」）、ｔ－ブチルパーオキシ－３，５，５－トリメチルヘキサノエート（同「パーブチル３５５」）、ｔ－ヘキシルパーオキシイソプロピルモノカーボネート（同「パーヘキシルＩ」）、ｔ－ブチルパーオキシイソプロピルモノカーボネート（同「パーブチルＩ」）、ｔ－ブチルパーオキシ－２－エチルヘキシルモノカーボネート（同「パーブチルＥ」）、ｔ－ブチルパーオキシアセテート（同「パーブチルＡ」）、ｔ－ヘキシルパーオキシベンゾエート（同「パーヘキシルＺ」）及びｔ－ブチルパーオキシベンゾエート（同「パーブチルＺ」）等が挙げられ、これらの内の１種又は２種以上を用いることができる。
　上記無機過酸化物としては、過硫酸カリウム、過硫酸ナトリウム、過硫酸アンモニウム等が挙げられる。
　また、レドックス開始の場合、亜硫酸ナトリウム、チオ硫酸ナトリウム、ナトリウムホルムアルデヒドスルホキシレート、アスコルビン酸、亜硫酸ガス（ＳＯ2）、硫酸第一鉄等を還元剤として用いることができる。
　重合開始剤の好ましい使用量は、用いる単量体成分の総量を１００質量部としたときに、例えば、０．００１～２質量部であり、また例えば、０．００５～１質量部であり、また例えば、０．０１～０．１質量部である。重合開始剤の使用量が０．００１質量部以上であれば重合反応を安定的に行うことができ、２質量部以下であれば一次鎖長の長い重合体を得やすい。
　重合時の単量体成分の濃度については、より一次鎖長の長い重合体を得る観点から高い方が好ましい。ただし、単量体成分の濃度が高すぎると、重合体粒子の凝集が進行し易い他、重合熱の制御が困難となり重合反応が暴走する虞がある。このため、例えば沈殿重合法の場合、重合開始時の単量体濃度は、２～４０質量％程度の範囲が一般的であり、好ましくは５～４０質量％の範囲である。本発明の架橋重合体は、重合開始時に１３．０質量％以上の単量体濃度で重合して得られたものである。単量体濃度は好ましくは１５．０質量％以上であり、より好ましくは１７．０質量％以上であり、更に好ましくは１９．０質量％以上であり、一層好ましくは２０．０質量％以上である。単量体濃度はなお好ましくは２２．０質量％以上であり、より一層好ましくは２５．０質量％以上である。
　重合温度は、使用する単量体の種類及び濃度等の条件にもよるが、０～１００℃が好ましく、２０～８０℃がより好ましい。重合温度は一定であってもよいし、重合反応の期間において変化するものであってもよい。また、重合時間は１分間～２０時間が好ましく、１時間～１０時間がより好ましい。
　重合工程を経て得られた架橋重合体分散液は、乾燥工程において減圧及び／又は加熱処理等を行い溶媒留去することにより、目的とする架橋重合体を粉末状態で得ることができる。この際、上記乾燥工程の前に、未反応単量体（及びその塩）、開始剤由来の不純物等を除去する目的で、重合工程に引き続き、遠心分離及び濾過等の固液分離工程、水、メタノール又は重合溶媒と同一の溶媒等を用いた洗浄工程を備えることが好ましい。上記洗浄工程を備えた場合、架橋重合体が二次凝集した場合であっても使用時に解れやすく、さらに残存する未反応単量体が除去されることにより結着性や電池特性の点でも良好な性能を示す。
　架橋重合体粉末中に含まれる残存溶剤及び未反応単量体は、臭気、電池性能及び安全性（ガス化による電池の膨れ等）への懸念等から少ない方が好ましい。具体的には、架橋重合体粉末中、好ましくは２．０質量％以下であり、より好ましくは１．０質量%以下であり、さらに好ましくは０．５質量％以下であり、一層好ましくは０．１質量％以下である。
　本製造方法では、塩基化合物存在下にエチレン性不飽和カルボン酸単量体を含む単量体組成物の重合反応を行うが、重合工程により得られた重合体分散液にアルカリ化合物を添加して重合体を中和（以下、「工程中和」ともいう）した後、乾燥工程で溶媒を除去してもよい。また、上記工程中和の処理を行わずに架橋重合体の粉末を得た後、電極合剤層スラリーを調製する際にアルカリ化合物を添加して、重合体を中和（以下、「後中和」ともいう）してもよい。上記の内、工程中和の方が、二次凝集体が解れやすい傾向にあり好ましい。
　本製造方法では、架橋重合体は重合工程後のスラリーの状態、または乾燥工程後の粉末の状態において、金属異物を除去する金属除去工程を設けてもよい。金属異物を除去する方法としては特段の制限はなく、格子型マグネット、マグネットストレーナー、マグネットフィルター、電磁分離機、マグネットプーリー、ドラム磁選機及び吊下磁選機等の公知の方法を用いることができる。
　金属除去工程では、数十～数百μｍ以上のサイズの磁性を有する金属異物が除去される。金属異物除去工程後の架橋重合体に含まれる金属異物は、該架橋重合体に対し、好ましくは１０ｐｐｍ以下であり、より好ましくは１ｐｐｍ以下であり、さらに好ましくは０．１ｐｐｍ以下であり、一層好ましくは０．０１ｐｐｍ以下である。
＜非水電解質二次電池電極合剤層用組成物＞
　本発明の非水電解質二次電池電極合剤層用組成物は、上記架橋重合体又はその塩を含有するバインダー、活物質及び水を含む。
　本発明の電極合剤層組成物における架橋重合体又はその塩の使用量は、活物質の全量に対して、例えば、０．１質量％以上２０質量％以下である。上記使用量は、また例えば、０．２質量％以上１０質量％以下であり、また例えば０．３質量％以上８質量％以下であり、また例えば０．４質量％以上５質量％以下である。架橋重合体及びその塩の使用量が０．１質量％未満の場合、十分な結着性が得られないことがある。また、活物質等の分散安定性が不十分となり、形成される合剤層の均一性が低下する場合がある。一方、架橋重合体及びその塩の使用量が２０質量％を超える場合、電極合剤層組成物が高粘度となり集電体への塗工性が低下することがある。その結果、得られた合剤層にブツや凹凸が生じて電極特性に悪影響を及ぼす虞がある。
　架橋重合体及びその塩の使用量が上記範囲内であれば、分散安定性に優れた組成物が得られるとともに、集電体への密着性が極めて高い合剤層を得ることができ、結果として電池の耐久性が向上する。さらに、上記架橋重合体及びその塩は、活物質に対して少量（例えば５質量％以下）でも十分高い結着性を示し、かつ、カルボキシアニオンを有することから、界面抵抗が小さく、ハイレート特性に優れた電極が得られる。
　上記活物質の内、正極活物質としては主に遷移金属酸化物のリチウム塩が用いられ、例えば、層状岩塩型及びスピネル型のリチウム含有金属酸化物を使用することができる。層状岩塩型の正極活物質の具体的な化合物としては、コバルト酸リチウム、ニッケル酸リチウム、並びに、三元系と呼ばれるＮＣＭ｛Ｌｉ（Ｎｉx，Ｃｏy，Ｍｎz）、ｘ＋ｙ＋ｚ＝１｝及びＮＣＡ｛Ｌｉ（Ｎｉ1-a-bＣｏaＡｌb）｝等が挙げられる。また、スピネル型の正極活物質としてはマンガン酸リチウム等が挙げられる。酸化物以外にもリン酸塩、ケイ酸塩及び硫黄等が使用され、リン酸塩としては、オリビン型のリン酸鉄リチウム等が挙げられる。正極活物質としては、上記のうちの１種を単独で使用してもよく、２種以上を組み合わせて混合物又は複合物として使用してもよい。
　尚、層状岩塩型のリチウム含有金属酸化物を含む正極活物質を水に分散させた場合、活物質表面のリチウムイオンと水中の水素イオンとが交換されることにより、分散液がアルカリ性を示す。このため、一般的な正極用集電体材料であるアルミ箔（Ａｌ）等が腐食される虞がある。このような場合には、バインダーとして未中和又は部分中和された架橋重合体を用いることにより、活物質から溶出するアルカリ分を中和することが好ましい。また、未中和又は部分中和された架橋重合体の使用量は、架橋重合体の中和されていないカルボキシル基量が活物質から溶出するアルカリ量に対して当量以上となるように用いることが好ましい。
　正極活物質はいずれも電気伝導性が低いため、導電助剤を添加して使用されるのが一般的である。導電助剤としては、カーボンブラック、カーボンナノチューブ、カーボンファイバー、黒鉛微粉、炭素繊維等の炭素系材料が挙げられ、これらの内、優れた導電性を得やすい点からカーボンブラック、カーボンナノチューブ及びカーボンファイバー、が好ましい。また、カーボンブラックとしては、ケッチェンブラック及びアセチレンブラックが好ましい。導電助剤は、上記の１種を単独で使用してもよく、２種以上を組み合わせて使用してもよい。導電助剤の使用量は、導電性とエネルギー密度を両立するという観点から活物質の全量に対して、例えば、０．２～２０質量％とすることができ、また例えば、０．２～１０質量％とすることができる。また正極活物質は導電性を有する炭素系材料で表面コーティングしたものを使用してもよい。
　一方、負極活物質としては、例えば炭素系材料、リチウム金属、リチウム合金及び金属酸化物等が挙げられ、これらの内の１種又は２種以上を組み合わせて用いることができる。これらの内でも、天然黒鉛、人造黒鉛、ハードカーボン及びソフトカーボン等の炭素系材料からなる活物質（以下、「炭素系活物質」ともいう）が好ましく、天然黒鉛及び人造黒鉛等の黒鉛、並びにハードカーボンがより好ましい。また、黒鉛の場合、電池性能の面から球形化黒鉛が好適に用いられ、その粒子サイズの好ましい範囲は、例えば、１～２０μｍであり、また例えば、５～１５μｍである。また、エネルギー密度を高くするために、ケイ素やスズなどのリチウムを吸蔵できる金属又は金属酸化物等を負極活物質として使用することもできる。その中でも、ケイ素は黒鉛に比べて高容量であり、ケイ素、ケイ素合金及び一酸化ケイ素（ＳｉＯ）等のケイ素酸化物のようなケイ素系材料からなる活物質（以下、「ケイ素系活物質」ともいう）を用いることができる。しかし、上記ケイ素系活物質は高容量である反面充放電に伴う体積変化が大きい。このため、上記炭素系活物質と併用するのが好ましい。この場合、ケイ素系活物質の配合量が多いと電極材料の崩壊を招き、サイクル特性（耐久性）が大きく低下する場合がある。このような観点から、ケイ素系活物質を併用する場合、その使用量は炭素系活物質に対して、例えば、６０質量％以下であり、また例えば、３０質量％以下である。
　本発明の架橋重合体を含むバインダーは、当該架橋重合体がエチレン性不飽和カルボン酸単量体に由来する構造単位（（ａ）成分）を有する。ここで、（ａ）成分はケイ素系活物質に対する親和性が高く、良好な結着性を示す。このため、本発明のバインダーはケイ素系活物質を含む高容量タイプの活物質を用いた場合にも優れた結着性を示すことから、得られる電極の耐久性向上に対しても有効であるものと考えられる。
　炭素系活物質は、それ自身が良好な電気伝導性を有するため、必ずしも導電助剤を添加する必要はない。抵抗をより低減する等の目的で導電助剤を添加する場合、エネルギー密度の観点からその使用量は活物質の総量に対して、例えば、１０質量％以下であり、また例えば、５重量％以下である。
　非水電解質二次電池電極合剤層用組成物がスラリー状態の場合、活物質の使用量は、組成物全量に対して、例えば、１０～７５質量％の範囲であり、また例えば、３０～６５質量％の範囲である。活物質の使用量が１０質量％以上であればバインダー等のマイグレーションが抑えられるとともに、媒体の乾燥コストの面でも有利となる。一方、７５質量％以下であれば組成物の流動性及び塗工性を確保することができ、均一な合剤層を形成することができる。
　また、湿粉状態で電極合剤層用組成物を調製する場合、活物質の使用量は、組成物全量に対して、例えば、６０～９７質量％の範囲であり、また例えば、７０～９０質量％の範囲である。また、エネルギー密度の観点から、バインダーや導電助剤等の活物質以外の不揮発成分は、必要な結着性や導電性が担保される範囲内で出来る限り少ない方がよい。
　非水電解質二次電池電極合剤層用組成物は、媒体として水を使用する。また、組成物の性状及び乾燥性等を調整する目的で、メタノール及びエタノール等の低級アルコール類、エチレンカーボネート等のカーボネート類、アセトン等のケトン類、テトラヒドロフラン、Ｎ－メチルピロリドン等の水溶性有機溶剤との混合溶媒としてもよい。混合媒体中の水の割合は、例えば、５０質量％以上であり、また例えば、７０質量％以上である。
　電極合剤層用組成物を塗工可能なスラリー状態とする場合、組成物全体に占める水を含む媒体の含有量は、スラリーの塗工性、および乾燥に必要なエネルギーコスト、生産性の観点から、例えば、２５～９０質量％の範囲とすることができ、また例えば、３５～７０質量％とすることができる。また、プレス可能な湿粉状態とする場合、上記媒体の含有量はプレス後の合剤層の均一性の観点から、例えば、３～４０質量％の範囲とすることができ、また例えば、１０～３０質量％の範囲とすることができる。
　本発明のバインダーは、上記架橋重合体又はその塩のみからなるものであってもよいが、これ以外にもスチレン／ブタジエン系ラテックス（ＳＢＲ）、アクリル系ラテックス及びポリフッ化ビニリデン系ラテックス等の他のバインダー成分を併用してもよい。他のバインダー成分を併用する場合、その使用量は、活物質に対して、例えば、０．１～５質量％以下とすることができ、また例えば、０．１～２質量％以下とすることができ、また例えば、０．１～１質量％以下とすることができる。他のバインダー成分の使用量が５質量％を超えると抵抗が増大し、ハイレート特性が不十分なものとなる場合がある。上記の中でも、結着性及び耐屈曲性のバランスに優れる点で、スチレン／ブタジエン系ラテックスが好ましい。
　上記スチレン／ブタジエン系ラテックスとは、スチレン等の芳香族ビニル単量体に由来する構造単位及び１，３－ブタジエン等の脂肪族共役ジエン系単量体に由来する構造単位を有する共重合体の水系分散体を示す。上記芳香族ビニル単量体としては、スチレンの他にα－メチルスチレン、ビニルトルエン、ジビニルベンゼン等が挙げられ、これらの内の１種又は２種以上を用いることができる。上記共重合体中における上記芳香族ビニル単量体に由来する構造単位は、主に結着性の観点から、例えば、２０～６０質量％の範囲とすることができ、また例えば、３０～５０質量％の範囲とすることができる。
　上記脂肪族共役ジエン系単量体としては、１，３－ブタジエンの他に２－メチル－１，３－ブタジエン、２，３－ジメチル－１，３－ブタジエン、２－クロロ－１，３－ブタジエン等が挙げられ、これらの内の１種又は２種以上を用いることができる。上記共重合体中における上記脂肪族共役ジエン系単量体に由来する構造単位は、バインダーの結着性及び得られる電極の柔軟性が良好なものとなる点で、例えば、３０～７０質量％の範囲とすることができ、また例えば、４０～６０質量％の範囲とすることができる。
　スチレン／ブタジエン系ラテックスは、上記の単量体以外にも、結着性等の性能をさらに向上させるために、その他の単量体として（メタ）アクリロニトリル等のニトリル基含有単量体、（メタ）アクリル酸、イタンコン酸、マレイン酸等のカルボキシル基含有単量体を共重合単量体として用いてもよい。
　上記共重合体中における上記その他の単量体に由来する構造単位は、例えば、０～３０質量％の範囲とすることができ、また例えば、０～２０質量％の範囲とすることができる。
　本発明の非水電解質二次電池電極合剤層用組成物は、上記の活物質、水及びバインダーを必須の構成成分とするものであり、公知の手段を用いて各成分を混合することにより得られる。各成分の混合方法は特段制限されるものではなく、公知の方法を採用することができるが、活物質、導電助剤及びバインダーである架橋重合体粒子等の粉末成分をドライブレンドした後、水等の分散媒と混合し、分散混練する方法が好ましい。電極合剤層用組成物をスラリー状態で得る場合、分散不良や凝集のないスラリーに仕上げることが好ましい。混合手段としては、プラネタリーミキサー、薄膜旋回式ミキサー及び自公転式ミキサー等の公知のミキサーを使用することができるが、短時間で良好な分散状態が得られる点で薄膜旋回式ミキサーを使用して行うことが好ましい。また、薄膜旋回式ミキサーを用いる場合は、予めディスパー等の攪拌機で予備分散を行うことが好ましい。また、上記スラリーの粘度は、６０ｒｐｍにおけるＢ型粘度として、例えば、５００～１００，０００ｍＰａ・ｓの範囲とすることができ、また例えば、１，０００～５０，０００ｍＰａ・ｓの範囲とすることができる。
　一方、電極合剤層用組成物を湿粉状態で得る場合、ヘンシェルミキサー、ブレンダ―、プラネタリーミキサー及び２軸混練機等を用いて、濃度ムラのない均一な状態まで混練することが好ましい。
　また、非水電解質二次電池電極合剤層用組成物中に多量の多価金属イオンが含まれると、架橋重合体のカルボキシル基と相互作用する結果、スラリーの安定性が低下し、電極合剤層の均一性及び結着性が低下する恐れがある。係る観点から、非水電解質二次電池電極合剤層用組成物中の多価金属イオン濃度は、架橋重合体に対して好ましくは１００ｐｐｍ以下であり、より好ましくは５０ｐｐｍ以下であり、さらに好ましくは１０ｐｐｍ以下である。多価金属としては特に限定されないが、例えば、Ｆｅ、Ａｌ、Ｃｒ、Ｃｕ、Ｃａ等が挙げられる。
＜非水電解質二次電池用電極＞
　本発明の非水電解質二次電池用電極は、銅又はアルミニウム等の集電体表面に上記電極合剤層用組成物から形成される合剤層を備えてなるものである。合剤層は、集電体の表面に本発明の電極合剤層用組成物を塗工した後、水等の媒体を乾燥除去することにより形成される。合剤層組成物を塗工する方法は特に限定されず、ドクターブレード法、ディップ法、ロールコート法、コンマコート法、カーテンコート法、グラビアコート法及びエクストルージョン法などの公知の方法を採用することができる。また、上記乾燥は、温風吹付け、減圧、（遠）赤外線、マイクロ波照射等の公知の方法により行うことができる。
　通常、乾燥後に得られた合剤層には、金型プレス及びロールプレス等による圧縮処理が施される。圧縮することにより活物質及びバインダーを密着させ、合剤層の強度及び集電体への密着性を向上させることができる。圧縮により合剤層の厚みを、例えば、圧縮前の３０～８０％程度に調整することができ、圧縮後の合剤層の厚みは４～２００μｍ程度が一般的である。
　本発明の非水電解質二次電池用電極にセパレータ及び非水電解液を備えることにより、非水電解質二次電池を作製することができる。
　セパレータは電池の正極及び負極間に配され、両極の接触による短絡の防止や電解液を保持してイオン導電性を確保する役割を担う。セパレータにはフィルム状の絶縁性微多孔膜であって、良好なイオン透過性及び機械的強度を有するものが好ましい。具体的な素材としては、ポリエチレン及びポリプロピレン等のポリオレフィン、ポリテトラフルオロエチレン等を使用することができる。
　非水電解液は、非水電解質二次電池に一般的に使用される公知のものを用いることができる。具体的な溶媒としては、プロピレンカーボネート及びエチレンカーボネート等の高誘電率で電解質の溶解能力の高い環状カーボネート、並びに、エチルメチルカーボネート、ジメチルカーボネート及びジエチルカーボネート等の粘性の低い鎖状カーボネート等が挙げられ、これらを単独で又は混合溶媒として使用することができる。非水電解液は、これらの溶媒にＬｉＰＦ6、ＬｉＳｂＦ6、ＬｉＢＦ4、ＬｉＣｌＯ4、ＬｉＡｌＯ4等のリチウム塩を溶解して使用される。非水電解質二次電池は、セパレータで仕切られた正極板及び負極板を渦巻き状又は積層構造にしてケース等に収納することにより得られる。
　以上説明したように、本明細書に開示される非水電解質二次電池電極用バインダーは、合剤層において電極材料との優れた結着性と集電体との優れた接着性とを示すこのため、上記バインダーを使用して得られた電極を備えた非水電解質二次電池は、良好な一体性を確保でき、充放電を繰り返しても良好な耐久性（サイクル特性）を示すと予想され、車載用二次電池等に好適である。
　以下、実施例に基づいて本発明を具体的に説明する。尚、本発明は、これらの実施例により限定されるものではない。尚、以下において「部」及び「％」は、特に断らない限り質量部及び質量％を意味する。
≪架橋重合体塩の製造≫
（製造例１：架橋重合体塩Ｒ－１の製造）
　重合には、攪拌翼、温度計、還流冷却器及び窒素導入管を備えた反応器を用いた。
　反応器内にアセトニトリル５６７部、イオン交換水２．２０部、アクリル酸（以下、「ＡＡ」という）１００部、ペンタエリスリトールトリアリルエーテル（ダイソー社製、商品名「ネオアリルＰ－３０」）０．６０部及び上記ＡＡに対して１．０モル％に相当するトリオクチルアミンを仕込んだ。反応器内を十分に窒素置換した後、加温して内温を５５℃まで昇温した。内温が５５℃で安定したことを確認した後、重合開始剤として２，２’－アゾビス（２，４－ジメチルバレロニトリル）（和光純薬工業社製、商品名「Ｖ－６５」）０．０４０部を添加したところ、反応液に白濁が認められたため、この点を重合開始点とした。単量体濃度は１５．０％と算出された。外温（水バス温度）を調整して内温を５５℃に維持しながら重合反応を継続し、重合開始点から６時間経過した時点で内温を６５℃まで昇温した。内温を６５℃で維持し、反応開始点から１２時間経過した時点で反応液の冷却を開始し、内温が２５℃まで低下した後、水酸化リチウム・一水和物（以下、「ＬｉＯＨ・Ｈ2Ｏ」という）の粉末５２．５部を添加した。添加後室温下１２時間撹拌を継続して、架橋重合体塩Ｒ－１（Ｌｉ塩、中和度９０モル％）の粒子が媒体に分散したスラリー状の重合反応液を得た。
（架橋重合体塩Ｒ－１（Ｌｉ中和物）の膨潤前平均粒子径測定）
　上記で得られた架橋重合体塩Ｒ－１を含む重合反応液を、アセトニトリルを分散媒とするレーザー回折/散乱式粒度分布計（マイクロトラックベル社製、マイクロトラックＭＴ－３３００ＥＸII）にて粒子径測定を行った。体積基準メジアン径は０．３５μｍであった。
　得られた重合反応液を遠心分離して重合体粒子を沈降させた後、上澄みを除去した。その後、重合反応液と同重量のアセトニトリルに沈降物を再分散させた後、遠心分離により重合体粒子を沈降させて上澄みを除去する洗浄操作を２回繰り返した。沈降物を回収し、減圧条件下、８０℃で３時間乾燥処理を行い、揮発分を除去することにより、架橋重合体塩Ｒ－１の粉末を得た。架橋重合体塩Ｒ－１は吸湿性を有するため、水蒸気バリア性を有する容器に密封保管した。なお、架橋重合体塩Ｒ－１の粉末をＩＲ測定し、カルボン酸のＣ＝Ｏ基由来のピークとカルボン酸ＬｉのＣ＝Ｏ由来のピークの強度比より中和度を求めたところ、仕込みからの計算値に等しく９０モル％であった。
（架橋重合体塩Ｒ－１（Ｌｉ中和物）の水媒体中での平均粒子径測定）
　上記で得られた架橋重合体塩Ｒ－１の粉末０．２５ｇ、及びイオン交換水４９．７５ｇを１００ｃｃの容器に量りとり、自転／公転式攪拌機（シンキー社製、あわとり錬太郎ＡＲ－２５０）にセットした。次いで、撹拌（自転速度２０００ｒｐｍ／公転速度８００ｒｐｍ、７分）、さらに脱泡（自転速度２２００ｒｐｍ／公転速度６０ｒｐｍ、１分）処理を行い架橋重合体塩Ｒ－１（中和度９０モル％）が水に膨潤した状態のハイドロゲルを作成した。
　次に、イオン交換水を分散媒とするレーザー回折/散乱式粒度分布計（マイクロトラックベル社製、マイクロトラックＭＴ－３３００ＥＸII）にて上記ハイドロゲルの粒度分布測定を行った。ハイドロゲルに対し、過剰量の分散媒を循環しているところに、適切な散乱光強度が得られる量のハイドロゲルを投入したところ、数分後に測定される粒度分布形状が安定した。安定を確認次第、体積基準の粒度分布測定を行い、平均粒子径としてメジアン径（Ｄ５０）を求めたところ、１．２μｍであった。また、以下の基準に従い単分散性を評価した結果、（体積基準メジアン径／個数基準メジアン径）で表される粒子径分布は１．２であり、単分散性は「◎」と判断された。
評価基準；
　◎：体積基準メジアン径／個数基準メジアン径が１．５未満
　○：体積基準メジアン径／個数基準メジアン径が１．５以上、３．０未満
　△：体積基準メジアン径／個数基準メジアン径が３．０以上、１０未満
　×：体積基準メジアン径／個数基準メジアン径が１０以上
（製造例２～２３：架橋重合体（塩）Ｒ－２～Ｒ－２３の製造）
　各原料の仕込み量を表１又は表２に記載の通りとした以外は製造例１と同様の操作を行い、架橋重合体（塩）Ｒ－２～Ｒ－２３を含む重合反応液を得た。各重合反応液について製造例１と同様の操作により膨潤前平均粒子径を測定し、表１及び表２に示した。
　各重合反応液について、製造例１と同様の操作を行い、粉末状の架橋重合体（塩）Ｒ－２～Ｒ－２３を得た。各架橋重合体（塩）は、水蒸気バリア性を有する容器に密封保管した。
　得られた各重合体（塩）について、製造例１と同様に、水媒体中での平均粒子径を測定した。結果を表１又は表２に示す。また、製造例２１で得られた架橋重合体塩について、後記する方法により２質量％水溶液粘度及び４質量％水溶液粘度を測定した。尚、製造例２０では、ＬｉＯＨ・Ｈ2Ｏの粉末５２．５部の代わりにＮａＯＨを用いることにより、架橋重合体Ｎａ塩（中和度９０モル％）を得た。
（２質量％水溶液粘度の測定）
　架橋重合体塩Ｒ－２１の粉末２．０部、及びイオン交換水９８部を容器に秤量し、自転／公転式撹拌機（シンキー社製、あわとり錬太郎ＡＲ－２５０）にセットした。次いで撹拌（自転速度２０００ｒｐｍ／公転速度８００ｒｐｍ、７分）、さらに脱泡（自転速度２２００ｒｐｍ／公転速度６０ｒｐｍ、１分）処理を未膨潤粉末状部がなくなるまで繰り返し、架橋重合体塩Ｒ－２１のリチウム塩が水に膨潤した状態のハイドロゲル微粒子分散液を調製した。得られたハイドロゲル微粒子分散液を２５℃±１℃に調整した後、Ｂ型粘度計（東機産業社製、ＴＶＢ－１０）を用いて、ローター速度１２ｒｐｍにおける粘度を測定した結果、６０ｍＰａ・ｓであった。
（４質量％水溶液粘度の測定）
　架橋重合体塩Ｒ－２１の粉末４．０部、及びイオン交換水９６部を容器に秤量した以外は、上記２質量％水溶液粘度の測定と同様の操作を行い、ハイドロゲル微粒子分散液を調製した。得られたハイドロゲル微粒子分散液を２５℃±１℃に調整した後、Ｂ型粘度計（東機産業社製、ＴＶＢ－１０）を用いて、ローター速度１２ｒｐｍにおける粘度を測定した結果、３５，０００ｍＰａ・ｓであった。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　表１及び表２において用いた化合物の詳細を以下に示す。
　ＡＡ：アクリル酸
　ＩＢＸＡ：アクリル酸イソボルニル
　ＤＭＡＡ：Ｎ，Ｎ－ジメチルアクリルアミド
　Ｐ－３０：ペンタエリスリトールトリアリルエーテル（ダイソー社製、商品名「ネオアリルＰ－３０」）
　Ｔ－２０：トリメチロールプロパンジアリルエーテル（ダイソー社製、商品名「ネオアリルＴ－２０」）
　ＴＭＡ：トリメチルアミン（Ｃ／Ｎ値：３）
　ＴＥＡ：トリエチルアミン（Ｃ／Ｎ値：６）
　ＴＯＡ：トリオクチルアミン（Ｃ／Ｎ値：２４）
　ＴＤＡ：トリドデシルアミン（Ｃ／Ｎ値：３６）
　ＴＳＡ：トリステアリルアミン（Ｃ／Ｎ値：５４）
　ピリジン：（Ｃ／Ｎ値：５）
　ジブチルアミン：（Ｃ／Ｎ値：８）
　ヘキシルアミン：（Ｃ／Ｎ値：６）
　ＤＭＡＮ：１，８－ビス（ジメチルアミノ）ナフタレン（Ｃ／Ｎ値：７）
　ＡｃＮ：アセトニトリル
　Ｖ－６５：２，２’－アゾビス（２，４－ジメチルバレロニトリル）（和光純薬工業社製）
（負極電極の評価）
　負極活物質として、黒鉛、又は、ケイ素粒子及び黒鉛を用い、各架橋重合体をバインダーとして用いた合剤層用組成物について、その塗工性及び形成された合剤層／集電体間の剥離強度（すなわちバインダーの結着性）を測定した。黒鉛としては天然黒鉛（日本黒鉛社製、商品名「ＣＧＢ－１０」）、ケイ素粒子としては（Ｓｉｇｍａ－Ａｌｄｒｉｃｈ、Ｓｉナノパウダー、粒子径＜１００ｎｍ）を使用した。
実施例１
　天然黒鉛１００部に粉末状の架橋重合体Ｌｉ塩Ｒ－１を３．２部秤量し、予めよく混合した後、イオン交換水１６０部を加えてディスパーで予備分散を行った後、薄膜旋回式ミキサー（プライミクス社製、ＦＭ－５６－３０）を用いて周速度２０ｍ／秒の条件で本分散を１５秒間行うことにより、スラリー状の負極合剤層用組成物を得た。
　可変式アプリケーターを用いて、厚さ２０μｍの銅箔（日本製箔社製）上に上記合剤層用組成物を塗布し、通風乾燥機内で１００℃×１５分間の乾燥を行うことにより合剤層を形成した。その後、合剤層の厚みが５０±５μｍ、充填密度が１．７０±０．２０ｇ／ｃｍ3になるよう圧延した。
　得られた合剤層の外観を目視により観察し、以下の基準に基づいて塗工性を評価した結果、「○」と判断された。
＜塗工性判定基準＞
　○：表面に筋ムラ、ブツ等の外観異常がまったく認められない。
　△：表面に筋ムラ、ブツ等の外観異常がわずかに認められる。
　×：表面に筋ムラ、ブツ等の外観異常が顕著に認められる。
＜９０°剥離強度（結着性）＞
　上記で得られた負極電極を２５ｍｍ幅の短冊状に裁断した後、水平面に固定された両面テープに上記試料の合剤層面を貼付け、剥離試験用試料を作成した。試験用試料を６０℃、1晩減圧条件下で乾燥させた後、引張速度５０ｍｍ／分における９０°剥離を行い、合剤層と銅箔間の剥離強度を測定した。剥離強度は１５．２Ｎ／ｍと高く、良好であった。
実施例２～２０、及び比較例１～２
　活物質及びバインダーとして使用する架橋重合体塩を表３又は表４の通り用いた以外は実施例１と同様の操作を行うことにより合剤層組成物を調製した。なお、実施例２及び実施例３では、天然黒鉛及びケイ素粒子を、遊星ボールミル（ＦＲＩＴＳＣＨ社製、Ｐ－５）を用いて４００ｒｐｍで１時間撹拌し、得られた混合物に粉末状の架橋重合体Ｌｉ塩Ｒ－１を３．２部秤量し、予めよく混合した後、実施例１と同様の操作を行うことにより合剤層組成物を調製した。各合剤層組成物について塗工性及び９０°剥離強度を評価した。結果を表３又は表４に示す。
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
　各実施例は、本発明に属する非水電解質二次電池電極用バインダーを含む電極合剤層組成物及びこれを用いて電極を作製したものである。各合剤層組成物（スラリー）の塗工性は良好であり、得られた電極の合剤層と集電体との剥離強度はいずれも高い値が得られており、優れた結着性を示すものであった。
　実施例１３及び２３では、２０％～２５％という高い単量体濃度条件下であっても架橋重合体が安定に得られ、当該架橋重合体を含むバインダーは優れた結着性を示した。
　一方、架橋重合体（塩）Ｒ－２２は、塩基不存在下で重合反応を行った例であり、得られた架橋重合体は分散安定性が不十分であり、平均粒子径及び粒子径分布の大きなものであった。また結着性も不十分なものであった（比較例１）。また、重合時の単量体濃度が低い架橋重合体をバインダーとした比較例２も、十分な剥離強度が得られない結果が示された。
　本発明の非水電解質二次電池電極用バインダーは、合剤層において優れた結着性を示すこのため、上記バインダーを使用して得られた電極を備えた非水電解質二次電池は、良好な耐久性（サイクル特性）を示すと予想され、車載用二次電池への適用が期待される。また、シリコンを含む活物質の使用にも有用であり、電池の高容量化への寄与が期待される。

Claims (9)

  1. 　架橋重合体又はその塩を含有する非水電解質二次電池電極用バインダーであって、
    　前記架橋重合体は、エチレン性不飽和カルボン酸単量体に由来する構造単位を含み、塩基化合物存在下、１３．０質量％以上の単量体濃度で重合して得られたものであり、かつ、中和度８０～１００モル％に中和された後、水媒体中で測定した粒子径が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下である、非水電解質二次電池電極用バインダー。
  2. 　前記塩基化合物は、有機アミン化合物である請求項１に記載の非水電解質二次電池電極用バインダー。
  3. 　前記有機アミン化合物は、当該有機アミン化合物に存在する窒素原子数に対する炭素原子数の比で表される値（Ｃ／Ｎ）が３以上である請求項２に記載の非水電解質二次電池電極用バインダー。
  4. 　前記架橋重合体の重合に用いる単量体の総量に対する前記エチレン性不飽和カルボン酸単量体の濃度が、１０質量％以上、１００質量％以下である請求項１～３のいずれか１項に記載の非水電解質二次電池電極用バインダー。
  5. 　前記エチレン性不飽和カルボン酸単量体に対する前記塩基化合物の使用量が、０．００１モル％以上、４．０モル％以下である請求項１～４のいずれか１項に記載の非水電解質二次電池電極用バインダー。
  6. 　非水電解質二次電池電極用バインダーに用いられる架橋重合体又はその塩の製造方法であって、
    　塩基化合物存在下、エチレン性不飽和カルボン酸単量体を含む単量体成分を１３．０質量％以上の単量体濃度で沈殿重合法により重合する重合工程を備え、
    　前記架橋重合体又はその塩は、中和度８０～１００モル％に中和された後、水媒体中で測定した粒子径が、体積基準メジアン径で０．１μｍ以上、１０μｍ以下である、方法。
  7. 　請求項１～５のいずれか１項に記載のバインダー、活物質及び水を含む非水電解質二次電池電極合剤層用組成物。
  8. 　負極活物質として炭素系材料またはケイ素系材料を含む請求項７に記載の非水電解質二次電池電極合剤層用組成物。
  9. 　集電体表面に、請求項７又は８に記載の非水電解質二次電池電極合剤層用組成物から形成される合剤層を備えた非水電解質二次電池電極。
PCT/JP2018/026640 2017-07-21 2018-07-17 非水電解質二次電池電極用バインダー及びその用途 WO2019017315A1 (ja)