WO2018199138A1 - ポリビニルアルコール系フィルム、偏光膜および偏光板、ならびにポリビニルアルコール系フィルムの製造方法 - Google Patents
ポリビニルアルコール系フィルム、偏光膜および偏光板、ならびにポリビニルアルコール系フィルムの製造方法 Download PDFInfo
- Publication number
- WO2018199138A1 WO2018199138A1 PCT/JP2018/016751 JP2018016751W WO2018199138A1 WO 2018199138 A1 WO2018199138 A1 WO 2018199138A1 JP 2018016751 W JP2018016751 W JP 2018016751W WO 2018199138 A1 WO2018199138 A1 WO 2018199138A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- polyvinyl alcohol
- ave
- alcohol film
- polarizing
- Prior art date
Abstract
Description
そして、上記膨潤工程において重要なことは、ポリビニルアルコール系フィルムを厚み方向に速やかに膨潤させること、および上記染色工程においてフィルム内部に染料がスムーズに浸入できるようにポリビニルアルコール系フィルムを均一に膨潤させることである。
また、上記延伸工程は、染色後のフィルムを流れ方向(MD)に延伸して、ポリビニルアルコール系フィルム中の二色性染料を高度に配向させる工程であり、偏光膜の偏光性能を向上させるためには、この延伸工程において、原反となるポリビニルアルコール系フィルムが流れ方向(MD)に良好な延伸性を示すことが重要である。
また、ポリビニルアルコール系フィルムの延伸性を改良する方法として、例えば、フィルムを製膜する時のキャストドラムの速度と最終的なポリビニルアルコール系フィルムの巻き取り速度との比を特定する方法(例えば、特許文献2参照)、キャストドラムで製膜後にその製膜されたフィルムを浮遊させて乾燥する方法(例えば、特許文献3参照)、製膜されたフィルムの乾燥工程における引っ張り具合を制御する方法(例えば、特許文献4参照)、ポリビニルアルコール系重合体フィルムの流れ方向(MD)の複屈折率をそのポリビニルアルコール系重合体フィルムの厚み方向に平均化した値〔Δn(MD)Ave〕、およびポリビニルアルコール系重合体フィルムの幅方向(TD)の複屈折率をそのポリビニルアルコール系重合体フィルムの厚み方向に平均化した値〔Δn(TD)Ave〕が、特定の関係を満たすよう調整する方法(例えば、特許文献5および特許文献6参照)が提案されている。
また、上記特許文献4に開示の技術では、ポリビニルアルコール系フィルムの膜厚を均一にできるものの、高分子の配向までは制御できず、偏光膜製造時の膨潤性や延伸性を改良するには不充分である。
Δn(MD)Ave≧2.2×10-3・・・(A)
Δn(TD)Ave≧2.0×10-3・・・(B)
〔上記式(A)中のΔn(MD)Aveは、上記ポリビニルアルコール系フィルムの長さ方向(MD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。また、上記式(B)中のΔn(TD)Aveは、上記ポリビニルアルコール系フィルムの幅方向(TD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。〕
Δn(MD)Ave≧2.2×10-3・・・(A)
Δn(TD)Ave≧2.0×10-3・・・(B)
〔上記式(A)中のΔn(MD)Aveは、上記ポリビニルアルコール系フィルムの流れ方向(MD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。また、上記式(B)中のΔn(TD)Aveは、上記ポリビニルアルコール系フィルムの幅方向(TD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。〕
本発明のポリビニルアルコール系フィルムは、下記式(A)および(B)を満足することを特徴とする長尺のポリビニルアルコール系フィルムである。
Δn(MD)Ave≧2.2×10-3・・・(A)
Δn(TD)Ave≧2.0×10-3・・・(B)
[上記式(A)中のΔn(MD)Aveは、上記ポリビニルアルコール系フィルムの長さ方向(MD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。また、上記式(B)中のΔn(TD)Aveは、上記ポリビニルアルコール系フィルムの幅方向(TD)の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。]
上記Δn(MD)Aveの値が低すぎると、後述する偏光膜製造時の膨潤工程で皺が発生し偏光膜に色ムラが発生してしまうため、本発明の目的を達成することができない。
なお、上記Δn(MD)Aveの上限は、通常1.5×10-2(好ましくは1.0×10-2)であり、Δn(MD)Aveの値が大きすぎても、偏光膜に色ムラが発生しやすい傾向がある。
上記Δn(TD)Aveの値が低すぎると、後述する偏光膜製造時の膨潤工程で皺が発生し、偏光膜に色ムラが発生しやすくなり、本発明の目的を達成することができない。
なお、上記Δn(TD)Aveの上限は、通常1.5×10-2(好ましくは1.0×10-2)であり、Δn(TD)Aveの値が大きすぎても、偏光膜に色ムラが発生しやすくなる傾向がある。
(1)ポリビニルアルコール系フィルムの流れ方向(MD)の任意の位置で、ポリビニルアルコール系フィルムの幅方向(TD)における中央部からMD×TD=5mm×10mmの大きさの細片を切り出す。ついで、その細片を厚み100μmのPET(ポリエチレンテフタレート)フィルムで両側を挟み、それをさらに木枠に挟んでミクロトーム装置に取り付ける。
(2)つぎに、上記(1)で切り出した細片を、細片の流れ方向(MD)と平行に10μm間隔でスライスし、観察用の(MD×TD=5mm×10μm)を作製する。
(3)ついで、スライス面が観察できるように、スライス片を倒してスライス面を上向きとしてスライドガラス上に載せてカバーガラスとリン酸トリクレジル(屈折率1.557)で封じ、二次元光弾性評価システム「PA-micro」(フォトニックラティス社製)を用いてスライス片3個のレタデーションを測定する。
(4)スライス片のレタデーション分布を「PA-micro」の測定画面に表示した状態で、スライス片を横切るように当初の上記ポリビニルアルコール系フィルムの表面に垂直な線分Xを引き、その線分X上でライン解析を行ってスライス片の厚み方向のレタデーション分布データを取得する。なお、観察は対物レンズ40倍を用いて行い、線幅を3画素としてレタデーションの平均値を採用する。
(5)得られたスライス片の厚み方向のレタデーション分布データをスライス片の厚み10μmで除して、スライス片の厚み方向の複屈折率Δn(MD)分布を求め、スライス片の厚み方向の複屈折率Δn(MD)分布の平均値をとる。スライス片3個について求めたそれぞれのスライス片の厚み方向の複屈折率Δn(MD)分布の平均値をさらに平均して、上記ポリビニルアルコール系フィルムの「Δn(MD)Ave」とする。
(1)ポリビニルアルコール系フィルムの流れ方向(MD)の任意の位置で、ポリビニルアルコール系フィルムの幅方向(TD)における中央部からMD×TD=10mm×5mmの大きさの細片を切り出す。そして、その細片を厚み100μmのPETフィルムで両側を挟み、それをさらに木枠に挟んでミクロトーム装置に取り付ける。
(2)つぎに、上記(1)で切り出した細片を、細片の幅方向(TD)と平行に10μm間隔でスライスし、観察用のスライス片(MD×TD=10μm×5mm)を作製する。
(3)ついで、スライス面が観察できるように、スライス片を倒してスライス面を上向きとしてスライドガラス上に載せてカバーガラスとリン酸トリクレジル(屈折率1.557)で封じ、二次元光弾性評価システム「PA-micro」(フォトニックラティス社製)を用いてスライス片3個のレタデーションを測定する。
(4)スライス片のレタデーション分布を「PA-micro」の測定画面に表示した状態で、スライス片を横切るように当初の上記ポリビニルアルコール系フィルムの表面に垂直な線分Xを引き、その線分X上でライン解析を行ってスライス片の厚み方向のレタデーション分布データを取得する。なお、観察は対物レンズ40倍を用いて行い、線幅を3画素としてレタデーションの平均値を採用する。
(5)得られたスライス片の厚み方向のレタデーション分布データをスライス片の厚み10μmで除して、スライス片の厚み方向の複屈折率Δn(TD)分布を求め、スライス片の厚み方向の複屈折率Δn(TD)分布の平均値をとる。スライス片3個について求めたそれぞれのスライス片の厚み方向の複屈折率Δn(TD)分布の平均値をさらに平均して、上記ポリビニルアルコール系フィルムの「Δn(TD)Ave」とする。
まず、本発明で使用されるポリビニルアルコール系樹脂、およびそのポリビニルアルコール系樹脂水溶液に関して説明する。
本発明において、ポリビニルアルコール系フィルムを構成するポリビニルアルコール系樹脂としては、通常、未変性のポリビニルアルコール系樹脂、すなわち、酢酸ビニルを重合して得られるポリ酢酸ビニルをケン化して製造される樹脂が用いられる。必要に応じて、酢酸ビニルと、少量(通常、10モル%以下、好ましくは5モル%以下)の酢酸ビニルと共重合可能な成分との共重合体をケン化して得られる樹脂を用いることもできる。酢酸ビニルと共重合可能な成分としては、例えば、不飽和カルボン酸(例えば、塩、エステル、アミド、ニトリル等を含む)、炭素数2~30のオレフィン類(例えば、エチレン、プロピレン、n-ブテン、イソブテン等)、ビニルエーテル類、不飽和スルホン酸塩等があげられる。これらは単独でもしくは2種以上併せて用いることができる。また、ケン化後の水酸基を化学修飾して得られる変性ポリビニルアルコール系樹脂を用いることもできる。
ここで、本発明における平均ケン化度は、JIS K 6726に準じて測定されるものである。
本発明のポリビニルアルコール系フィルムは、キャスト法や溶融押出し法で製造されるが、本発明においては、透明性、厚み精度、表面平滑性等の点から、キャスト法が好ましく、特に好ましくは、生産性の点から、連続キャスト法である。
ここで、上記キャスト型がキャストドラムである場合の製膜工程を説明する。
上記ポリビニルアルコール系樹脂水溶液の温度が低すぎると、流動不良となる傾向があり、高すぎると、発泡する傾向がある。
上記ポリビニルアルコール系樹脂水溶液の粘度が低すぎると、流動不良となる傾向があり、高すぎると、流延が困難となる傾向がある。
上記吐出速度が遅すぎると、生産性が低下する傾向があり、速すぎると、流延が困難となる傾向がある。
上記キャストドラムの直径が小さすぎると、乾燥長が不足し速度が出にくい傾向があり、大きすぎると、輸送性が低下する傾向がある。
上記キャストドラムの幅が小さすぎると、生産性が低下する傾向がある。
上記キャストドラムの回転速度が遅すぎると、生産性が低下する傾向があり、速すぎると、乾燥が不充分となる傾向がある。
上記キャストドラムの表面温度が低すぎると、乾燥不良となる傾向があり、高すぎると、発泡してしまう傾向がある。
上記製膜されたフィルムの含水率は、0.5~15重量%であることが好ましく、特に好ましくは1~13重量%、さらに好ましくは2~12重量%である。上記含水率が低すぎても高すぎても、目的とする膨潤性や延伸性の発現が困難となる傾向にある。
上記含水率の調整は、幅方向(TD)の延伸前のフィルムの含水率が高すぎる場合は、幅方向(TD)への延伸前にフィルムを乾燥することが好ましく、逆に、幅方向(TD)の延伸前のフィルムの含水率が低すぎる場合は、幅方向(TD)への延伸前に調湿することが好ましい。特に好ましくは、含水率が上記範囲となるように乾燥工程の条件を調整することである。
上記クリップのピッチが広すぎると、延伸後のフィルムにたわみが生じたり、得られるポリビニルアルコール系フィルムの幅方向両端部におけるΔn(MD)Ave、Δn(TD)Aveの変動が大きくなったりする傾向がある。また、クリップの挟持位置(クリップの先端部)は、製膜されたフィルムの幅方向両端縁から100mm以下が好ましい。クリップの挟持位置(先端部)がフィルムの幅方向中心部に位置しすぎると、破棄するフィルム端部が増大し、製品幅が狭くなる傾向にある。
幅固定の搬送工程を挿入する場合、固定幅を、1段階目の連続的な延伸後の幅よりも狭めることも可能である。延伸直後のフィルムは応力緩和のために収縮しやすく、脱水に伴う収縮も起きるため、固定幅をこれらの収縮幅まで狭めることが可能である。ただし、収縮幅以上に狭めると、フィルムにたわみが生じるため、好ましくない。
上記連続的な延伸は、先に述べたように、フィルムの乾燥工程後に行われることが好ましいが、フィルムの乾燥工程前、乾燥工程中、および乾燥工程後の少なくとも一つにて行われる。
この場合、一時的に1.3倍を超えて延伸した後、延伸倍率1.05~1.5の固定幅で、フィルムを単純に搬送すればよい。この方法により、フィルムの応力緩和がなされ、特に薄型フィルムの場合に、破断を回避することが可能になる。
上記熱処理温度が低すぎると、寸法安定性が低下しやすい傾向があり、逆に、高すぎると、偏光膜製造時の延伸性が低下する傾向がある。
また、熱処理時間は1~60秒間であることが好ましく、特に好ましくは5~30秒間である。熱処理時間が短すぎると、寸法安定性が低下する傾向があり、逆に、長すぎると、偏光膜製造時の延伸性が低下する傾向がある。
このようにして、本発明のポリビニルアルコール系フィルムが得られる。このポリビニルアルコール系フィルムは、流れ方向(MD)に長く、芯管にロール状に巻き取られることにより、フィルム巻装体に作製される。
本発明のポリビニルアルコール系フィルムの厚みは、面内位相差の点から通常5~50μmであり、好ましくは、偏光膜の薄型化の点で5~45μmが好ましく、特に好ましくは、破断回避の点で10~40μm、さらに好ましくは10~30μmである。
本発明の偏光膜は、上記ポリビニルアルコール系フィルムを、前記フィルム巻装体から繰り出して水平方向に搬送し、膨潤、染色、ホウ酸架橋、延伸、洗浄、乾燥等の工程を経て製造される。
なお、偏光度は、一般的に2枚の偏光膜を、その配向方向が同一方向になるように重ね合わせた状態で、波長λにおいて測定した光線透過率(H11)と、2枚の偏光膜を、配向方向が互いに直交する方向になる様に重ね合わせた状態で、波長λにおいて測定した光線透過率(H1)より、下記式にしたがって算出される。
偏光度(%)=〔(H11-H1)/(H11+H1)〕1/2
単体透過率は、分光光度計を用いて偏光膜単体の光線透過率を測定して得られる値である。
本発明の偏光膜は、色ムラが少なく、偏光性能に優れた偏光板を製造するのに好適である。
本発明の偏光板は、本発明の偏光膜の片面または両面に、接着剤を介して、光学的に等方性を有する樹脂フィルムを保護フィルムとして貼合することにより、作製される。保護フィルムとしては、たとえば、セルローストリアセテート、セルロースジアセテート、ポリカーボネート、ポリメチルメタクリレート、シクロオレフィンポリマー、シクロオレフィンコポリマー、ポリスチレン、ポリエーテルスルホン、ポリアリーレンエステル、ポリ-4-メチルペンテン、ポリフェニレンオキサイド等のフィルムまたはシートがあげられる。
(1)得られたポリビニルアルコール系フィルムの流れ方向(MD)の任意の位置で、ポリビニルアルコール系フィルムの幅方向(TD)における中央部からMD×TD=5mm×10mmの大きさの細片を切り出した。ついで、その細片を厚み100μmのPETフィルムで両側を挟み、それをさらに木枠に挟んでミクロトーム装置に取り付けた。
(2)つぎに、上記(1)で切り出した細片を、細片の流れ方向(MD)と平行に10μm間隔でスライスし、観察用のスライス片(MD×TD=5mm×10μm)を作製した。
(3)ついで、スライス面が観察できるように、スライス片を倒してスライス面を上向きとしてスライドガラス上に載せてカバーガラスとリン酸トリクレジル(屈折率1.557)で封じ、二次元光弾性評価システム「PA-micro」(フォトニックラティス社製)を用いてスライス片3個のレタデーションを測定した。
(4)スライス片のレタデーション分布を「PA-micro」の測定画面に表示した状態で、スライス片を横切るように当初の上記ポリビニルアルコール系フィルムの表面に垂直な線分Xを引き、その線分X上でライン解析を行ってスライス片の厚み方向のレタデーション分布データを取得した。なお、観察は対物40倍レンズを用いて行い、線幅を3画素としてレタデーションの平均値を採用した。
(5)得られたスライス片の厚み方向のレタデーション分布データをスライス片の厚み10μmで除してスライス片の厚み方向の複屈折率Δn(MD)分布を求め、スライス片の厚み方向の複屈折率Δn(MD)分布の平均値をとった。スライス片3個について求めたそれぞれのスライス片の厚み方向の複屈折率Δn(MD)分布の平均値をさらに平均して、上記ポリビニルアルコール系フィルムの「Δn(MD)Ave」とした。
(1)得られたポリビニルアルコール系フィルムの流れ方向(MD)の任意の位置で、ポリビニルアルコール系フィルムの幅方向(TD)における中央部からMD×TD=10mm×5mmの大きさの細片を切り出した。ついで、その細片を厚み100μmのPETフィルムで両側を挟み、それをさらに木枠に挟んでミクロトーム装置に取り付けた。
(2)つぎに、上記(1)で切り出した細片を、細片の幅方向(TD)と平行に10μm間隔でスライスし、観察用のスライス片(MD×TD=10μm×5mm)を作製した。
(3)ついで、スライス面が観察できるように、スライス片を倒してスライス面を上向きとしてスライドガラス上に載せてカバーガラスとリン酸トリクレジル(屈折率1.557)で封じ、二次元光弾性評価システム「PA-micro」(フォトニックラティス社製)を用いてスライス片3個のレタデーションを測定した。
(4)スライス片のレタデーション分布を「PA-micro」の測定画面に表示した状態で、スライス片を横切るように当初の上記ポリビニルアルコール系フィルムの表面に垂直な線分Xを引き、その線分X上でライン解析を行ってスライス片の厚み方向のレタデーション分布データを取得した。なお、観察は対物40倍レンズを用い行い、線幅を3画素としてレタデーションの平均値を採用した。
(5)得られたスライス片の厚み方向のレタデーション分布データをスライス片の厚みの10μmで除して、スライス片の厚み方向の複屈折率Δn(TD)分布を求め、スライス片の厚み方向の複屈折率Δn(TD)分布の平均値をとった。スライス片3個について求めたそれぞれのスライス片の厚み方向の複屈折率Δn(TD)分布の平均値をさらに平均して、上記ポリビニルアルコール系フィルムの「Δn(TD)Ave」とした。
得られた偏光膜の幅方向(TD)の中央部から、長さ4cm×幅4cmの試験片を切り出し、自動偏光フィルム測定装置(日本分光社製:VAP7070)を用いて、偏光度(%)と単体透過率(%)を測定した。
得られた偏光膜の幅方向(TD)の中央部から、長さ30cm×幅30cmの試験片を切り出し、クロスニコル状態の2枚の偏光板(単体透過率43.5%、偏光度99.9%)の間に45°の角度で挟んだのちに、表面照度14,000lxのライトボックスを用いて、透過モードで光学的な色ムラを観察し、下記の基準で評価した。
(評価基準)
○・・・色ムラがなかった
△・・・かすかに色ムラがあった
×・・・はっきりとした色ムラがあった
(ポリビニルアルコール系フィルムの作製)
5,000Lの溶解缶に、重量平均分子量142,000、ケン化度99.8モル%のポリビニルアルコール系樹脂1,000kg、水2,500kg、可塑剤としてグリセリン105kg、および界面活性剤としてポリオキシエチレンラウリルアミン0.25kgを入れ、撹拌しながら150℃まで昇温して加圧溶解を行い、濃度調整により樹脂濃度25重量%のポリビニルアルコール系樹脂の水溶液を得た。ついで、そのポリビニルアルコール系樹脂水溶液を、2軸押出機に供給して脱泡した後、水溶液温度を95℃にし、T型スリットダイ吐出口より、表面温度が80℃のキャストドラムに吐出(吐出速度1.3m/分)および流延して製膜した。その製膜したフィルムをキャストドラムから剥離し、流れ方向(MD)に搬送しながら、そのフィルムの表面と裏面とを合計10本の熱ロールに交互に接触させながら乾燥を行った。それにより、含水率7重量%のフィルム(幅2m、厚み30μm)を得た。つぎに、上記フィルムの左右両端部をクリップピッチ45mmのクリップで挟持し、そのフィルムを流れ方向(MD)に速度8m/分で搬送しながら、延伸機を用いて80℃で幅方向(TD)に1.2倍延伸した後、そのフィルムを固定幅2.4mで130℃の乾燥機中を搬送させ、ポリビニルアルコール系フィルム(幅2.4m、厚み25μm、長さ2km)を得た。得られたポリビニルアルコール系フィルムの特性は後記の表1に示される通りであった。最後に、そのポリビニルアルコール系フィルムを芯管にロール状に巻き取り、フィルム巻装体を得た。
得られたポリビニルアルコール系フィルムを上記フィルム巻装体から繰り出し、水平方向に搬送しながら、水温30℃の水槽に浸漬して膨潤させながら流れ方向(MD)に1.7倍に延伸した。その膨潤工程で、フィルムに折れや皺は発生しなかった。ついで、ヨウ素0.5g/L、ヨウ化カリウム30g/Lよりなる30℃の水溶液中に浸漬して染色しながら流れ方向(MD)に1.6倍に延伸し、つぎに、ホウ酸40g/L、ヨウ化カリウム30g/Lの組成の水溶液(50℃)に浸漬してホウ酸架橋しながら流れ方向(MD)に2.1倍に一軸延伸した。最後に、ヨウ化カリウム水溶液で洗浄を行い、50℃で2分間乾燥して総延伸倍率5.8倍の偏光膜を得た。この偏光膜製造中に破断は起きなかった。また、得られた偏光膜の特性は後記の表1に示される通りであった。
上記で得られた偏光膜の両面に、ポリビニルアルコール水溶液を接着剤として用いて、膜厚40μmのトリアセチルセルロースフィルムを貼合し、70℃で乾燥して偏光板を得た。
実施例1において、ポリビニルアルコール系樹脂水溶液を表面温度が88℃のキャストドラムに吐出(吐出速度1.9m/分)および流延して製膜した以外は同様に行い、含水率10重量%のフィルム(幅2m、厚み45μm)を得た。つぎに、実施例1と同様にして、そのフィルムを、延伸機を用いて80℃で幅方向(TD)に1.2倍延伸した後、固定幅2.4mで135℃の乾燥機中を搬送し、ポリビニルアルコール系フィルム(幅2.4m、厚み35μm、長さ2km)を得た。得られたポリビニルアルコール系フィルムの特性は後記の表1に示される通りであった。
さらに、上記ポリビニルアルコール系フィルムを用いて、実施例1と同様にして、偏光膜および偏光板を得た。偏光膜製造時の膨潤工程において、上記ポリビニルアルコール系フィルムに折れや皺の発生はなく、また破断も起きなかった。得られた偏光膜の特性は後記の表1に示される通りであった。
実施例1において、製膜時の吐出速度を0.8m/分にして吐出し流延して製膜した以外は同様に行い、含水率5重量%のフィルム(幅2m、厚み20μm)を得た。つぎに、実施例1と同様にして、そのフィルムを、延伸機を用いて80℃で幅方向(TD)に1.4倍延伸した後、固定幅2.8mで130℃の乾燥機中を搬送し、ポリビニルアルコール系フィルム(幅2.8m、厚み14μm、長さ2km)を得た。得られたポリビニルアルコール系フィルムの特性は後記の表1に示される通りであった。
さらに、上記ポリビニルアルコール系フィルムを用いて、実施例1と同様にして、偏光膜および偏光板を得た。偏光膜製造時の膨潤工程において、上記ポリビニルアルコール系フィルムに折れや皺の発生はなく、また破断も起きなかった。得られた偏光膜の特性は後記の表1に示される通りであった。
実施例1において、表面温度が90℃のキャストドラムにポリビニルアルコール系樹脂水溶液を吐出(吐出速度2.5m/分)および流延して製膜した。その製膜したフィルムに対しては、延伸機を用いた幅方向(TD)への延伸を行わずに、フローティングドライヤーを用いて110℃で熱処理を行った以外は実施例1と同様にして、含水率2.5重量%のポリビニルアルコール系フィルム(幅2m、厚み60μm、長さ2km)を得た。得られたポリビニルアルコール系フィルムの特性は後記の表1に示される通りであった。
さらに、上記ポリビニルアルコール系フィルムを用いて、実施例1と同様にして、偏光膜および偏光板を製造したところ、膨潤工程において、上記ポリビニルアルコール系フィルムに折れや皺が発生した。得られた偏光膜の特性は後記の表1に示される通りであった。
実施例1において、表面温度が88℃のキャストドラムにポリビニルアルコール系樹脂水溶液を吐出(吐出速度1.9m/分)および流延して製膜した。その製膜したフィルムに対しては、延伸機を用いた幅方向(TD)への延伸を行わずに、表面温度105℃の熱処理ロールで熱処理を行った以外は実施例1と同様にして、含水率2.0重量%のポリビニルアルコールフィルム(幅2m、厚み45μm、長さ2km)を得た。得られたポリビニルアルコール系フィルムの特性は下記の表1に示される通りであった。
さらに、上記ポリビニルアルコール系フィルムを用いて、実施例1と同様にして、偏光膜および偏光板を製造したところ、膨潤工程において、上記ポリビニルアルコール系フィルムに折れや皺が発生した。得られた偏光膜の特性は下記の表1に示される通りであった。
一方、これに対してΔn(MD)AveおよびΔn(TD)Aveの値が式(A)および(B)で特定する範囲よりも小さな値である比較例1,2のポリビニルアルコール系フィルムから得られる偏光膜は、偏光特性に劣り、色ムラも観察されてしまうものであることがわかる。
Claims (6)
- 長尺のポリビニルアルコール系フィルムであって、下記式(A)および(B)を満足することを特徴とするポリビニルアルコール系フィルム。
Δn(MD)Ave≧2.2×10-3・・・(A)
Δn(TD)Ave≧2.0×10-3・・・(B)
上記式(A)中のΔn(MD)Aveは、上記ポリビニルアルコール系フィルムの長さ方向の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。また、上記式(B)中のΔn(TD)Aveは、上記ポリビニルアルコール系フィルムの幅方向の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。 - 上記ポリビニルアルコール系フィルムの厚みが5~50μmであることを特徴とする請求項1記載のポリビニルアルコール系フィルム。
- 請求項1または2記載のポリビニルアルコール系フィルムが用いられていることを特徴とする偏光膜。
- 請求項3記載の偏光膜と、その偏光膜の少なくとも片面に設けられた保護フィルムとを備えていることを特徴とする偏光板。
- ポリビニルアルコール系樹脂の水溶液を連続キャスト法により製膜する製膜工程と、その製膜したフィルムを、流れ方向に搬送しながら、そのフィルムに対し連続的な乾燥および連続的な延伸を施す乾燥・延伸工程とを備えたポリビニルアルコール系フィルムの製造方法であって、製造されるポリビニルアルコール系フィルムが、下記式(A)および(B)を満足するようにすることを特徴とするポリビニルアルコール系フィルムの製造方法。
Δn(MD)Ave≧2.2×10-3・・・(A)
Δn(TD)Ave≧2.0×10-3・・・(B)
上記式(A)中のΔn(MD)Aveは、上記ポリビニルアルコール系フィルムの流れ方向の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。また、上記式(B)中のΔn(TD)Aveは、上記ポリビニルアルコール系フィルムの幅方向の複屈折率を、そのポリビニルアルコール系フィルムの厚み方向に平均化した値を示す。 - 上記乾燥・延伸工程において、上記製膜したフィルムを幅方向に1.05~1.5倍延伸することを特徴とする請求項5記載のポリビニルアルコール系フィルムの製造方法。