WO2016204530A1 - 이차전지용 바인더 조성물, 이를 사용한 전극 및 리튬 이차전지 - Google Patents

이차전지용 바인더 조성물, 이를 사용한 전극 및 리튬 이차전지 Download PDF

Info

Publication number
WO2016204530A1
WO2016204530A1 PCT/KR2016/006395 KR2016006395W WO2016204530A1 WO 2016204530 A1 WO2016204530 A1 WO 2016204530A1 KR 2016006395 W KR2016006395 W KR 2016006395W WO 2016204530 A1 WO2016204530 A1 WO 2016204530A1
Authority
WO
WIPO (PCT)
Prior art keywords
monomer
acrylate
group
methacrylate
latex
Prior art date
Application number
PCT/KR2016/006395
Other languages
English (en)
French (fr)
Inventor
강민아
류동조
최철훈
한선희
한혜수
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to EP16811943.6A priority Critical patent/EP3312918B1/en
Priority to PL16811943T priority patent/PL3312918T3/pl
Priority to CN201680003059.3A priority patent/CN106797032B/zh
Priority to US15/516,820 priority patent/US11223046B2/en
Publication of WO2016204530A1 publication Critical patent/WO2016204530A1/ko

Abstract

본 발명은, 콘쥬케이트 디엔(conjugated dienes) 라텍스(latex) 입자(A)와 코폴리머(compolymer) 라텍스(latex) 입자(B)가 독립적인 상으로 존재하는 복합 라텍스를 포함하며, 상기 복합 라텍스의 pH가 7 이하인 것을 특징으로 하는 이차전지용 바인더 조성물에 관한 것이다.

Description

이차전지용 바인더 조성물, 이를 사용한 전극 및 리튬 이차전지
본 출원은 2015년 06월 17일자 한국 특허 출원 제2015-0085579호에 기초한 우선권의 이익을 주장하며, 해당 한국 특허 출원의 문헌에 개시된 모든 내용은 본 명세서의 일부로서 포함된다.
본 발명은 이차전지용 바인더 조성물, 이를 사용한 전극 및 리튬 이차전지에 관한 것이다.
최근 휴대용 컴퓨터, 휴대용 전화기, 카메라 등의 휴대용 기기에 대한 기술 개발과 수요가 증가함에 따라 에너지원으로서 이차전지의 수요가 급격히 증가하고 있고, 그러한 이차전지 중 높은 에너지 밀도와 작동 전위를 나타내고 사이클 수명이 길며 자기방전율이 낮은 리튬 이차전지에 대해 많은 연구가 행해져 왔고, 또한 상용화되어 널리 사용되고 있다.
일반적으로, 리튬 이차전지는, 양극의 리튬 이온이 음극으로 삽입되고 탈리되는 과정을 반복하면서 충전과 방전이 진행된다. 이러한 리튬 이온의 삽입, 탈리가 반복적으로 진행되면서, 전극 활물질 또는 도전재 사이의 결합이 느슨해지고, 입자간 접촉저항이 증가하게 된다. 그 결과 전극의 옴저항이 상승하여 전지 특성이 저하될 수 있다. 따라서, 바인더는 전극에서의 리튬 이온의 삽입, 탈리에 따른 전극 활물질의 팽창, 수축에 대해 완충작용을 할 수 있어야 하므로, 탄성을 갖는 고분자인 것이 바람직하다.
또한, 바인더는 극판 건조 과정에서 전극 활물질과 집전체 사이의 결착력이 유지될 수 있을 정도의 접착력도 요구된다. 특히, 방전 용량을 높이기 위해, 이론적 방전 용량이 372 mAh/g인 천연 흑연에 방전 용량이 큰 실리콘, 주석, 실리콘-주석 합금 등과 같은 재료를 복합하여 사용하는 경우, 충전 및 방전이 진행됨에 따라 재료의 부피 팽창이 현저히 증가하게 되고, 이로 인해 음극재의 이탈이 발생하여, 결과적으로, 반복적인 사이클이 진행되면서 전지의 용량이 급격히 저하될 수 있다.
따라서, 전극 제조시 전극 활물질 간 또는 전극 활물질과 집전체 사이의 분리를 방지하고, 강한 물성으로 반복되는 충방전 시 발생되는 전극 활물질의 부피 팽창을 제어하여 수백 사이클 이후에도 전극의 구조적 안정성 및 이로 인한 전지의 성능향상을 도모할 수 있는 바인더 및 전극 재료에 대한 연구가 당업계에서 절실히 요구되고 있다.
더 나아가, 바인더는 그 자체로서 저항으로 작용할 수 있기 때문에 바인더 자체가 저항 및 이온 전도도 특성에 크게 영향을 미치지 않아야 한다. 중대형 전지의 경우, 높은 출력을 요구하는 사양이 많기 때문에 저항이 전지의 중요한 물성의 하나이며, 저항이 낮은 바인더에 대한 연구도 절실히 요구되고 있다.
따라서, 접착력이 우수하면서도 저항이 낮은 바인더 개발에 대한 필요성이 높은 실정이다.
상기한 바와 같이, 바인더는 탄성을 가진 것이 바람직하며, 이차 전지 내에서 접착력 및 접착 유지력이 우수하여 충방전 사이클 진행 후에 용량이 유지되며, 저항이 낮아 전지의 출력을 높일 수 있는 것이 바람직하다.
이에 본 출원의 발명자들은 심도있는 연구를 거듭한 끝에, 콘쥬게이트 디엔 라텍스 입자를 아크릴계 코폴리머 라텍스 입자와 소정의 비율로 혼합하고, 최종 라텍스의 pH가 7 이하가 되도록 바인더 조성물을 제조하는 경우, 바인더 조성물의 접착력을 향상시킬 수 있고, 이를 리튬 이차전지에 적용하는 경우, 전지의 저항을 감소시키는 동시에 우수한 용량 유지율을 나타낼 수 있음을 확인하고, 본 발명을 완성하기에 이르렀다.
본 발명에 따른 이차전지용 바인더 조성물은, 콘쥬케이트 디엔(conjugated dienes) 라텍스(latex) 입자(A)와 코폴리머(compolymer) 라텍스(latex) 입자(B)가 독립적인 상으로 존재하는 복합 라텍스를 포함하며, 상기 복합 라텍스의 pH가 7 이하인 것을 특징으로 한다.
구체적으로, 상기 복합 라텍스의 pH는 상세하게는 3 내지 7일 수 있고, 더욱 상세하게는 3 내지 6.5일 수 있다. 또한, 상기 복합 라텍스의 pH는 이를 구성하는 상기 라텍스 입자(A)와 라텍스 입자(B)에 의해 영향을 받는 바, 여기서, 상기 라텍스 입자(A) 및 라텍스 입자(B)의 pH 역시 3 내지 7일 수 있고, 상세하게는, 3 내지 6.5일 수 있다.
상기 범위를 벗어나, pH가 3 미만인 경우에는 음극 슬러리의 pH와 크게 차이가 나서 바인더 투입 시에 응집이 생길 수 있는 문제가 있고, 7을 초과하는 경우에는 두 바인더 사이에 응집이 발생하거나, 응집이 생기지 않더라도 접착력의 저하가 발생하는 문제가 있는 바 바람직하지 않다.
한편, 상기 복합 라텍스의 평균 입경은 100nm 내지 700 nm 이하일 수 있다. 여기서, 평균입경이 100 nm 미만인 경우, 접착력이 저하될 수 되고, 평균 입경이 700 nm 를 초과하는 경우, 저항이 커질 수도 있는 바, 바람직하지 않다.
이하에서는 상기 복합 라텍스를 이루는 구성들에 대해 자세히 설명한다.
상기 아크릴계 코폴리머 라텍스 입자(B)는 전해액 스웰링도가 높으므로, 전극의 저항을 낮추고, 이온 전도도를 증가시킬 수 있는 바, 이를 바인더 조성물에 포함하는 경우, 리튬 이차전지의 제반 성능을 향상시킬 수 있다.
다만, 상기 아크릴계 코폴리머 라텍스 입자(B)는, 카보네이트계 전해액과 친화성이 좋은 단량체를 포함하므로, 전지를 고온에서 방치할 경우, 전해액 스웰링 현상이 촉진되어 전해액이 분해되거나 부반응이 일어나 전극의 두께가 증가하고, 종국에는 전극의 탈리를 유발할 수 있는 문제가 있다.
따라서, 본 발명에 따른 효과를 가장 효과적으로 나타내기 위해, 본 발명에 따른 바인더 조성물은, 상세하게는, 콘쥬게이트 디엔 라텍스 입자(A)를 고형분 전체 중량을 기준으로 1 내지 50 중량%로 포함할 수 있다.
이러한 상기 콘쥬게이트 디엔 라텍스 입자(A)는, 바인더 조성물에 포함됨으로써 고온에서 전해액 스웰링 현상이 작고, 고무 탄력성을 가진 바인더로서 전극의 두께 및 가스 발생 현상을 감소시킬 뿐 아니라, 전극 활물질과 집전체 사이의 결착력이 유지될 수 있도록 접착력 또한 향상시키는 역할을 수행한다.
다만, 상기 콘쥬게이트 디엔 라텍스 입자(A)가, 고형분 중량을 기준으로 50 중량%를 초과하는 경우에는, 그 자체로서 저항으로 작용할 수 있기 때문에, 상기 범위로 함유되는 것이 바람직하다.
상기 콘쥬게이트 디엔 라텍스 입자(A)는, (가) 공액 디엔계 단량체 또는 공액 디엔계 중합체; (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체; (다) 불포화 카르본산계 단량체; 및 (라) 히드록시기 함유 단량체;로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체의 중합물을 포함하고 있을 수 있고, 더욱 상세하게는, (가) 공액 디엔계 단량체 또는 공액 디엔계 중합체; (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체; 및 (다) 불포화 카르본산계 단량체;로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체, 및 (라) 히드록시기 함유 단량체의 중합물을 포함할 수 있다. 즉, (라) 히드록시기 함유 단량체를 필수적으로 포함할 수 있다.
상기 공액 디엔계 단량체는, 1,3-부타디엔, 이소프렌, 클로로프렌, 및 피레리덴으로 이루어진 군에서 선택되는 하나의 단량체일 수 있다.
상기 공액 디엔계 중합체는, 예를 들어, 1,3-부타디엔, 이소프렌, 클로로프렌, 및 피레리덴으로 이루어진 군에서 선택되는 둘 이상의 단량체들의 중합체, 스티렌-부타디엔 공중합체, 아크릴로니트릴-부타디엔 공중합체, 스티렌-이소프렌 공중합체, 아크릴레이트-부타디엔 고무, 아크릴로니트릴-부타디엔-스티렌 고무, 에틸렌-프로필렌-디엔계 중합체 또는 이들 중합체가 부분적으로 수소화, 에폭시화, 브롬화된 중합체 및 이들의 혼합물 등일 수 있다.
상기 아크릴계 코폴리머 라텍스 입자(B)는 (가) (메타)아크릴산 에스테르계 단량체; (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체; (다) 불포화 카르본산계 단량체; 및 (라) 히드록시기 함유 단량체;로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체의 중합물을 포함하고 있을 수 있고, 더욱 상세하게는, (가) (메타)아크릴산 에스테르계 단량체; (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체; 및 (다) 불포화 카르본산계 단량체;로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체, 및 (라) 히드록시기 함유 단량체의 중합물을 포함할 수 있다. 즉, (라) 히드록시기 함유 단량체를 필수적으로 포함할 수 있다.
상기 (메타)아크릴산 에스테르계 단량체는 메틸아크릴레이트, 에틸아크릴레이트, 프로필아크릴레이트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 이소부틸아크릴레이트, n-아밀아크릴레이트, 이소아밀아크릴레이트, n-에틸헥실아크릴레이트, 2-에틸헥실아크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 프로필메크릴레이트, 이소프로필메크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-아밀메타크릴레이트, 이소아밀메타크릴레이트, n-헥실메타크릴레이트, n-에틸헥실 메타크릴레이트, 2-에틸헥실 메타크릴레이트 라우릴 아크릴레이트, 세릴 아크릴레이트, 스테아릴 아크릴레이트, 라우릴 메타 아크릴레이트, 세틸 메타 아크릴레이트, 및 스테아릴 메타 아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상의 단량체일 수 있다.
상기 아크릴레이트계 단량체는 메타아크릴록시 에틸에틸렌우레아, β-카르복시 에틸아크릴레이트, 알리파틱 모노아크릴레이트, 디프로필렌 디아크릴레이트, 디트리메틸로프로판 테트라아크릴레이트, 디펜타에리트리올 헥사아크릴레이트, 펜타에리트리올 트리아크릴레이트, 펜타에리트리올 테트라아크릴레이트, 글리시딜 메타 아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상의 단량체일 수 있다.
상기 비닐계 단량체는 스티렌, α-메틸스티렌, β-메틸스티렌, p-t-부틸스티렌 및 디비닐벤젠으로 이루어진 군으로부터 선택되는 1종 이상의 단량체일 수 있다.
상기 (메타)아크릴 아미드계 단량체는 아크릴 아미드, n-메틸올 아크릴아미드, n-부톡시 메틸아크릴아미드, 메타크릴아미드, n-메틸올 메타크릴아미드, n-부톡시 메틸메타크릴아미드로 이루어진 군으로부터 선택되는 1종 이상의 단량체일 수 있다.
상기 니트릴계 단량체는, 알케닐 시아나이드(cyanide)일 수 있고, 상세하게는, 아크릴로니트릴, 메타크릴로니트릴, 알릴 시아나이드 등일 수 있다.
상기 불포화 카르본산계 단량체는, 말레인산, 푸마르산, 메타크릴산, 아크릴산, 글루타르산, 이타콘산, 테트라하이드로프탈산, 코로톤산, 이소크로톤산 및 나딕산으로 이루어진 군에서 선택되는 1종 이상의 단량체일 수 있다.
상기 히드록시기 포함 단량체는 하이드록시에틸 아크릴레이트, 하이드록시부틸 아크릴레이트, 히드록시프로필 아크릴레이트, 히드록시에틸 메타크릴레이트, 히드록시프로필 메타크릴레이트, 히드록시 부틸 메타크릴레이트로 이루어진 군에서 선택되는 1종 이상의 단량체일 수 있다.
상기 콘쥬게이트 라텍스 입자(A)와 아크릴계 코폴리머 라텍스 입자(B)의 제조방법은 특별히 제한되지 않고, 공지의 현탁 중합법, 유화 중합법, 시드 중합법 등에 따라 제조될 수 있다. 라텍스 입자를 제조하기 위한 단량체 혼합물에는 중합 개시제, 가교제, 커플링제, 버퍼, 분자량 조절제, 유화제 등의 기타의 성분들을 하나 또는 둘 이상 포함할 수 있다.
구체적으로, 상기 라텍스 입자(A)와 라텍스 입자(B)는 유화 중합법에 의해 제조할 수 있고, 이 경우, 상기 라텍스 입자(A) 및 라텍스 입자(B)의 평균 입경은, 유화제의 양에 의해 조절할 수 있으며, 일반적으로 유화제의 양이 증가할수록 입자의 크기는 작아지고, 유화제의 양이 감소할수록 입자의 크기는 커지는 경향을 나타낸다. 원하는 입자의 크기, 반응시간, 반응 안정성 등을 고려하여 유화제 사용량을 조절 사용하여 소망하는 평균 입경을 구현할 수 있다.
중합 온도 및 중합 시간은 중합 방법 중합 개시제의 종류 등에 따라 적절히 결정할 수 있으며, 예를 들어, 중합 온도는 50℃ 내지 300℃ 일 수 있고, 중합 시간은 1 내지 20 시간일 수 있다.
상기 중합 개시제는 무기 또는 유기 과산화물이 사용될 수 있으며, 예를 들어, 포타슘 퍼설페이트, 소듐 퍼설페이트, 암모늄 퍼설페이트 등을 포함하는 수용성 개시제와, 큐멘 하이드로 퍼옥사이드, 벤조일 퍼옥사이드 등을 포함하는 유용성 개시제를 사용할 수 있다. 또한, 상기 중합개시제와 함께 과산화물의 개시반응을 촉진시키기 위해 활성화제를 더욱 포함할 수 있으며, 상기 활성화제로는 소듐 포름알데히드 설폭실레이트, 소듐 에틸렌디아민 테트라아세테이트, 황산 제1철 및 덱스트로오스로 이루어진 군으로부터 1종 이상 선택되는 것일 수 있다.
상기 가교제는, 바인더의 가교를 촉진시키는 물질로서, 예를 들어, 디에틸렌트리아민(diethylene triamine), 트리에틸렌 테트라아민(triethylene tetramine), 디에틸아미노 프로필아민(diethylamino propylamine), 자일렌 디아민(xylene diamine), 이소포론 디아민(isophorone diamine) 등의 아민류, 도데실 석시니 안하이드리드(dodecyl succinic anhydride), 프탈릭 안하이드리드(phthalic anhydride) 등의 산무수물, 폴리아미드 수지, 폴리설파이드 수지, 페놀수지, 에틸렌 글리콜 디메타크릴레이트, 디에틸렌 글리콜 디메타크릴레이트, 트리에틸렌 글리콜 디메타크릴레이트, 1,3-부탄디올 디메타크릴레이트, 1,6-헥산디올 디메타크릴레이트, 네오펜틸 글리콜 디메타크릴레이트, 트리 메틸롤 프로판 트리메타크릴레이트, 트리 메틸롤 메탄 트리아크릴레이트, 글리시딜 메타 아크릴레이트 등이 사용되며, 그라프팅제는 아릴 메타크릴레이트(AMA), 트리아릴 이소시아누레이트(TAIC), 트리아릴 아민(TAA), 디아릴 아민(DAA) 등이 사용될 수 있다.
상기 커플링제는 활물질과 바인더 사이의 접착력을 증가시키기 위한 물질로서, 두 개 이상의 기능성기를 가지고 있는 것을 특징으로 하며, 하나의 기능성기는 실리콘, 주석, 또는 흑연계 활물질 표면의 히드록실기나 카르복시기와 반응하여 화학적인 결합을 형성하고, 다른 기능성기는 본 발명에 따른 나노 복합체와의 반응을 통하여 화합결합을 형성하는 재료라면 특별히 제한되는 것은 아니며, 예를 들면, 트리에톡시실일프로필 테트라설파이드 (triethoxysilylpropyl tetrasulfide), 머캅토프로필 트리에톡시실란(mercaptopropyl triethoxysilane), 아미노프로 필트리에톡시실란(aminopropyl triethoxysilane), 클로로프로필트리에톡시실란 (chloropropyl triethoxysilane), 비닐 트리에톡시실란(vinyltriethoxysilane), 메타아크릴옥시 프로필 트리에톡시실란(methacryloxytpropyl triethoxysilane), 메타아크릴옥시프로필 트리에톡시실란(methacryloxypropyl triethoxysilane), 글리시독시프로필 트리에톡시실란 (glycidoxypropyl triethoxysilane), 이소시안아토프로필 트리에톡시실란(isocyanatopropyl triethoxysilane), 시안아토프로필트리에톡시실란(cyanatopropyl triethoxysilane) 등의 실란계 커플링제가 사용될 수 있다.
상기 버퍼는, 예를 들어, NaHCO3, NaOH, 및 NH4OH 로 이루어진 군에서 선택된 하나일 수 있다.
상기 분자량 조절제로는, 예를 들어, 메르캅탄류 또는 터비놀렌, 디펜텐, t-테르피엔 등의 테르핀류나 클로로포름, 사염화탄소 등의 할로겐화 탄화수소 등을 사용할 수 있다.
상기 유화제는, 친수성(hydrophilic) 기와 소수성(hydrophobic) 기를 동시에 가지고 있는 물질이다. 하나의 구체적인 예에서, 음이온성 유화제와 비이온성 유화제로 이루어진 군에서 선택되는 하나 이상일 수 있다.
비이온성 유화제를 음이온 유화제와 함께 사용하면, 입자 크기와 분포 조절에 도움이 되며, 이온성 유화제의 정전기적 안정화에 더하여 고분자 입자의 반데르발스 힘을 통한 콜로이드 형태의 추가적인 안정화를 제공할 수 있다. 비이온성 유화제를 단독으로 사용하는 경우는 많지 않은데, 이는 음이온 유화제보다 덜 안정한 입자가 생성되기 때문이다.
음이온성 유화제는, 포스페이트계, 카르복실레이트계, 설페이트계, 석시네이트계, 설포석시네이트계, 설포네이트계, 디설포네이트계로 이루어진 군에서 선택되는 것일 수 있다. 예를 들어, 소디움 알킬 설페이트, 소디움 폴리옥시에틸렌 설페이트, 소디움 라우릴 에테르 설페이트, 소디움 폴리옥시에틸렌 라우릴 에테르 설페이트(Sodium polyoxyethylene lauryl ether sulfate), 소디움 라우릴 설페이트(Sodium lauryl sulfate), 소디움 알킬 설포네이트, 소디움 알킬 에테르 설포네이트, 소디움 알킬벤젠 설포네이트, 소디움 리니어 알킬벤젠 설포네이트, 소디움 알파-올레핀 설포네이트, 소디움 알코올 폴리옥시에틸렌 에테르 설포네이트, 소디움 디옥틸 설포석시네이트(Sodium dioctyl sulfosuccinate), 소디움 퍼플루오로옥탄설포네이트, 소디움 퍼플루오로부탄설포네이트, 알킬디페닐옥사이드 디설포네이트(Alkyl diphenyloxide disulfonate), 소디움 디옥틸 설포석시네이트(Sodium dioctyl sulfosuccinate, DOSS), 소디움 알킬-아릴 포스페이트, 소디움 알킬 에테르 포스테이트, 소디움 라우오릴 사르코시네이트 등으로 이루어진 군에서 선택된 것일 수 있다. 다만, 이들로 제한되는 것은 아니고, 공지된 음이온성 유화제들은 모두 본 발명의 내용으로 포함될 수 있다.
상기 비이온성 유화제는, 에스테르형, 에테르형, 에스테르·에테르형 등일 수 있다. 예를 들어, 폴리옥시에틸렌글리콜, 폴리옥시에틸렌글리콜메틸에테르, 폴리옥시에틸렌모노알릴에테르, 폴리옥시에틸렌비스페놀-A 에테르, 폴리프로필렌글 리콜, 폴리옥시에틸렌네오펜틸에테르, 폴리옥시에틸렌세틸에테르, 폴리옥시에틸렌라 우릴에테르, 폴리옥시에틸올레일에테르, 폴리옥시에틸렌스테아릴 에테르, 폴리옥시에틸렌데실에테르, 폴리옥시에틸렌옥틸에테르 등일 수 있다. 다만, 이들로 제한되는 것은 아니고, 공지된 비이온성 유화제들은 모두 본 발명의 내용으로 포함될 수 있다.
이와 같이 제조된 콘쥬게이트 라텍스 입자(A)에는 라텍스 입자(A) 전체 중량을 기준으로 상기 (가) 공액 디엔계 단량체 또는 공액디엔계 중합체는 10 내지 97.4 중량%로 포함되어 있고, 상기 (나)군 단량체는 1 내지 70 중량%로 포함되어 있으며, (다) 불포화 카르본산계 단량체는 1 내지 20 중량% 포함되어 있고, (라) 히드록시기 함유 단량체는 0.5 내지 5 중량% 포함되어 있을 수 있다. 상기 유화제, 버퍼, 가교제 등의 기타 성분들은 선택적으로 0.1 내지 10 중량%의 범위 내에서 포함되어 있을 수 있다.
이와 유사하게, 상기와 같이 제조된 아크릴계 코폴리머 라텍스 입자(B)에는 라텍스 입자(B) 전체 중량을 기준으로 (가) (메타)아크릴산 에스테르계 단량체는 10 내지 96.9 중량%로 포함되어 있고, 상기 (나)군 단량체는 1 내지 60 중량%로 포함되어 있으며, (다) 불포화 카르본산계 단량체는 1 내지 10 중량% 포함되어 있고, (라) 히드록시기 함유 단량체는 1 내지 10 중량% 포함되어 있을 수 있다. 유화제, 버퍼, 가교제 등의 기타 성분들은 선택적으로 0.1 내지 10 중량%의 범위 내에서 포함되어 있을 수 있다.
한편, 본 발명에 따른 바인더 조성물에서 라텍스 입자(A)와 라텍스 입자(B)는, 독립적인 상으로 존재할 때 접착력의 향상 효과가 향상되므로, 상기 입자 간 응집(agglomeration)이 일어나지 않도록 하는 것이 매우 중요하다.
하나의 구체적인 예에서, 각각 제조된 라텍스 입자(A)와 라텍스 입자(B)의 pH를 조절하여 혼합물에서 상기 입자들(A, B)이 응집되지 않고 독립된 상을 유지할 수 있다.
따라서, 본 발명의 라텍스 입자(A)와 라텍스 입자(B)의 pH는, 상기에서 설명한 바와 같이, 3 내지 7 이하로 조절하여 낮은 pH에서 두 라텍스 입자를 혼합할 때 응집되지 않고 독립상을 유지하도록 할 수 있다.
본 발명에 있어서, 상기 바인더 조성물에는 상기 라텍스 입자들과 함께 산화 방지제 및 방부제가 첨가될 수 있다. 특히, 콘쥬게이트 디엔 라텍스 입자(A)가 바인더 조성물에 포함되어 사용되는 경우, 전지의 작동 과정에서 연화, 겔화 등으로 물성의 열화를 일으키기 쉬워 전지의 수명이 단축될 수 있으므로, 이러한 열화를 감소시키기 위하여 산화 방지제가 바람직하게 사용될 수 있다.
또한, 상기 바인더 조성물에는 점도 조절제 및 충진제로 이루어진 군에서 선택되는 1 이상의 물질이 더 포함되어 있을 수 있다. 상기 점도 조절제 및 충진제에 대해서는 이후에서 더욱 상세히 설명한다.
한편, 하나의 구체적인 예에서, 이와 같은 구성을 갖는 본 발명에 따른 바인더 조성물은, 전해액에 대한 스웰링도 (swelling index)가 1.5 내지 5일 수 있다.
상기 전해액에 스웰링도는 상기 바인더 조성물이 전해액을 흡수하여 팽창하는 정도를 나타내는 지표로서, 상기 조성물은 전해액에 대해 부피 팽창%, 즉, 원래 부피 대비 팽창된 부피의 백분율이 50% 내지 400%로 이뤄질 수 있으므로, 상기 값을 가질 수 있다. 이러한 전해액에 대한 스웰링도는 하기 식으로 계산될 수 있다.
*스웰링도(swelling index): (전해액 접촉에 따른 팽창 후 부피)/(팽창 전 부피=원부피)
본 발명은 또한, 상기 바인더 조성물과, 리튬을 흡장, 방출할 수 있는 전극 활물질을 포함하는 이차전지의 전극 합제를 제공한다. 상기 이차전지의 전극 합제는 도전재를 추가로 포함할 수 있다. 상기 도전재에 대해서는 이후에서 더욱 상세히 설명한다.
상기 전극 활물질의 구체적인 예로는 리튬 전이금속 산화물 분말 또는 탄소 분말을 들 수 있다. 본 발명은 또한, 상기 전극 합제가 집전체에 도포되어 구성되는 이차전지용 전극을 제공한다. 상기 전극은 전극 합제를 집전체 상에 도포한 후, 건조 및 압연하여 제조할 수 있다. 상기 이차전지용 전극은 양극일 수도 있고, 음극일 수도 있다.
양극은 예를 들어, 양극 집전체 상에 양극 활물질, 도전재, 바인더 등의 혼합물을 도포한 후 건조하여 제조하며, 음극은 음극 집전체 상에 음극 활물질, 도전재, 바인더 등의 혼합물을 도포한 후 건조하여 제조한다. 경우에 따라서는, 음극에 도전재가 포함되지 않을 수도 있다.
상기 양극 활물질은 리튬 전이금속 산화물로서, 2 이상의 전이금속을 포함하고, 예를 들어, 1 또는 그 이상의 전이금속으로 치환된 리튬 코발트 산화물(LiCoO2), 리튬 니켈 산화물(LiNiO2) 등의 층상 화합물; 1 또는 그 이상의 전이금속으로 치환된 리튬 망간 산화물; 화학식 LiNi1 - yMyO2 (여기서, M = Co, Mn, Al, Cu, Fe, Mg, B, Cr, Zn 또는 Ga 이고 상기 원소 중 하나 이상의 원소를 포함, 0.01≤y≤0.7 임)으로 표현되는 리튬 니켈계 산화물; Li1 + zNi1 / 3Co1 / 3Mn1 / 3O2, Li1 +zNi0.4Mn0.4Co0.2O2 등과 같이 Li1 + zNibMncCo1 - (b+c+d)MdO(2-e)Ae (여기서, -0.5≤z≤0.5, 0.1≤b≤0.8, 0.1≤c≤0.8, 0≤d≤0.2, 0≤e≤0.2, b+c+d<1 임, M = Al, Mg, Cr, Ti, Si 또는 Y 이고, A = F, P 또는 Cl 임)으로 표현되는 리튬 니켈 코발트 망간 복합산화물; 화학식 Li1 + xM1 - yM'yPO4 - zXz(여기서, M = 전이금속, 바람직하게는 Fe, Mn, Co 또는 Ni 이고, M' = Al, Mg 또는 Ti 이고, X = F, S 또는 N 이며, -0.5≤x≤+0.5, 0≤y≤0.5, 0≤z≤0.1 임)로 표현되는 올리빈계 리튬 금속 포스페이트 등을 들 수 있지만, 이들만으로 한정되는 것은 아니다.
음극 활물질로는, 예를 들어, 천연 흑연, 인조 흑연, 팽창 흑연, 탄소섬유, 난흑연화성 탄소, 카본블랙, 카본나노튜브, 플러렌, 활성탄 등의 탄소 및 흑연재료; 리튬과 합금이 가능한 Al, Si, Sn, Ag, Bi, Mg, Zn, In, Ge, Pb, Pd, Pt, Ti 등의 금속 및 이러한 원소를 포함하는 화합물; 금속 및 그 화합물과 탄소 및 흑연재료의 복합물; 리튬 함유 질화물 등을 들 수 있다. 그 중에서도 탄소계 활물질, 규소계 활물질, 주석계 활물질, 또는 규소-탄소계 활물질이 더욱 바람직하며, 이들은 단독으로 또는 둘 이상의 조합으로 사용될 수도 있다.
상기 도전재는 전극 활물질의 도전성을 더욱 향상시키기 위한 성분으로서, 전극 합제 전체 중량을 기준으로 0.01 ~ 30 중량%로 첨가될 수 있다. 이러한 도전재는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 천연 흑연이나 인조 흑연 등의 흑연; 카본블랙, 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙 등의 카본블랙; 탄소 나노튜브나 플러렌 등의 탄소 유도체, 탄소 섬유나 금속 섬유 등의 도전성 섬유; 불화 카본, 알루미늄, 니켈 분말 등의 금속 분말; 산화아연, 티탄산 칼륨 등의 도전성 위스키; 산화 티탄 등의 도전성 금속 산화물; 폴리페닐렌 유도체 등의도전성 소재 등이 사용될 수 있다.
상기 전극에서 집전체는 활물질의 전기화학적 반응에서 전자의 이동이 일어나는 부위로서, 전극의 종류에 따라 양극 집전체와 음극 집전체가 존재한다.
상기 양극 집전체는 일반적으로 3 ~ 500 ㎛의 두께로 만들어진다. 이러한 양극 집전체는, 당해 전지에 화학적 변화를 유발하지 않으면서 높은 도전성을 가지는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 또는 알루미늄이나 스테인리스 스틸의 표면에 카본, 니켈, 티탄,은 등으로 표면처리한 것 등이 사용될 수 있다.
상기 음극 집전체는 일반적으로 3 ~ 500 ㎛의 두께로 만들어진다. 이러한 음극 집전체는, 당해 전지에 화학적변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 구리, 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 구리나 스테인리스 스틸의 표면에 카본, 니켈, 티탄, 은 등으로 표면 처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다.
이들 집전체들은 그것의 표면에 미세한 요철을 형성하여 전극 활물질의 결합력을 강화시킬 수도 있으며, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.
전극 활물질, 도전재, 바인더 등의 혼합물(전극 합제)에는 점도 조절제 및 충진제로 이루어진 군에서 선택되는 1종 이상의 물질이 더 포함될 수도 있다.
상기 점도 조절제는 전극 합제의 혼합 공정과 그것의 집전체 상의 도포 공정이 용이할 수 있도록 전극 합제의 점도를 조절하는 성분으로서, 전극 합제 전체 중량을 기준으로 30 중량%까지 첨가될 수 있다. 이러한 점도 조절제의 예로는, 카르복시메틸셀룰로우즈, 폴리아크릴산 등이 있지만, 이들만으로 한정되는 것은 아니다.
상기 충진제는 전극의 팽창을 억제하는 보조성분으로서, 당해 전지에 화학적 변화를 유발하지 않으면서 섬유상 재료라면 특별히 제한되는 것은 아니며, 예를 들어, 폴리에틸렌, 폴리프로필렌 등의 올레핀계 중합체; 유리섬유, 탄소섬유 등의 섬유상 물질이 사용된다.
본 발명은 상기 전극을 포함하는 리튬 이차전지를 제공한다.
상기 리튬 이차전지는 일반적으로 전극 외에도 분리막 및 리튬염 함유 비수 전해질을 더 포함하는 것으로 구성되어 있다.
상기 분리막은 양극과 음극 사이에 개재되며 높은 이온 투과도와 기계적 강도를 가지는 절연성의 얇은 박막이 사용된다. 분리막의 기공 직경은 일반적으로 0.01 ~ 10 ㎛이고, 두께는 일반적으로 5 ~ 300 ㎛이다. 이러한 분리막으로는, 예를 들어, 내화학성 및 소수성의 폴리프로필렌 등의 올레핀계 폴리머, 유리섬유 또는 폴리에틸렌 등으로 만들어진 시트나 부직포 등이 사용된다. 전해질로서 폴리머 등의 고체 전해질이 사용되는 경우에는 고체 전해질이 분리막을 겸할 수도 있다.
상기 리튬 함유 비수계 전해액은 비수 전해액과 리튬염으로 이루어져 있다.
상기 비수 전해액으로는, 예를 들어, N-메틸-2-피롤리디논, 프로필렌 카르보네이트, 에틸렌 카르보네이트, 부틸렌 카르보네이트, 디메틸 카르보네이트, 디에틸 카르보네이트, 감마-부틸로 락톤, 1,2-디메톡시 에탄, 테트라히드록시 프랑(franc), 2-메틸 테트라하이드로푸란, 디메틸술폭시드, 1,3-디옥소런, 포름아미드, 디메틸포름아미드, 디옥소런, 아세토니트릴, 니트로메탄, 포름산 메틸, 초산메틸, 인산 트리에스테르, 트리메톡시 메탄, 디옥소런 유도체, 설포란, 메틸 설포란, 1,3-디메틸-2-이미다졸리디논, 프로필렌 카르보네이트 유도체, 테트라하이드로푸란 유도체, 에테르, 피로피온산 메틸, 프로피온산 에틸 등의 비양자성 유기용매가 사용될 수 있다.
상기 리튬염은 상기 비수계 전해액에 용해되기 좋은 물질로서, 예를 들어, LiCl, LiBr, LiI, LiClO4, LiBF4, LiB10Cl10, LiPF6, LiCF3SO3, LiCF3CO2, LiAsF6, LiSbF6, LiAlCl4, CH3SO3Li, (CF3SO2)2NLi, 클로로 보란 리튬, 저급 지방족 카르본산 리튬, 4 페닐 붕산 리튬, 이미드 등이 사용될 수 있다.
경우에 따라서는 유기 고체 전해질, 무기 고체 전해질 등이 사용될 수도 있다.
상기 유기 고체 전해질로는, 예를 들어, 폴리에틸렌 유도체, 폴리에틸렌 옥사이드 유도체, 폴리프로필렌 옥사이드 유도체, 인산 에스테르 폴리머, 폴리 에지테이션 리신(agitation lysine), 폴리에스테르 술파이드, 폴리비닐알코올, 폴리 불화 비닐리덴, 이온성 해리기를 포함하는 중합체 등이 사용될 수 있다.
상기 무기 고체 전해질로는, 예를 들어, Li3N, LiI, Li5NI2, Li3N-LiI-LiOH, LiSiO4, LiSiO4-LiI-LiOH, Li2SiS3, Li4SiO4, Li4SiO4-LiI-LiOH, Li3PO4-Li2S-SiS2 등의 Li의 질화물, 할로겐화물, 황산염 등이 사용될 수 있다.
또한, 비수계 전해액에는 충방전 특성, 난연성 등의 개선을 목적으로, 예를 들어, 피리딘, 트리에틸포스파이트, 트리에탄올아민, 환상 에테르, 에틸렌 디아민, n-글라임(glyme), 헥사 인산 트리 아미드, 니트로벤젠 유도체, 유황, 퀴논 이민 염료, N-치환 옥사졸리디논, N, N-치환 이미다졸리딘, 에틸렌 글리콜 디알킬 에테르, 암모늄염, 피롤, 2-메톡시 에탄올, 삼염화 알루미늄, 등이 첨가될 수도 있다. 경우에 따라서는, 불연성을 부여하기 위하여, 사염화탄소, 삼불화에틸렌 등의 할로겐 함유 용매를 더 포함시킬 수도 있고, 고온 보존 특성을 향상시키기 위하여 이산화탄산 가스를 더 포함시킬 수도 있으며, FEC(Fluoro-Ethylene carbonate), PRS(Propenesultone) 등을 더 포함시킬 수 있다.
본 발명에 따른 이차전지는 소형 디바이스의 전원으로 사용되는 전지셀에 사용될 수 있을 뿐만 아니라, 중대형 디바이스의 전원으로 사용되는 다수의 전지셀들을 포함하는 중대형 전지모듈에 단위전지로도 바람직하게 사용될 수 있다.
상기 중대형 디바이스의 바람직한 예로는 전지적 모터에 의해 동력을 받아 움직이는 파워 툴(power tool); 전기 자동차(Electric Vehicle, EV), 하이브리드 전기자동차(Hybrid Electric Vehicle, HEV), 플러그-인 하이브리드 전기자동차(Plug-in Hybrid Electric Vehicle, PHEV) 등을 포함하는 전기차; 전기 자전거(E-bike), 전기 스쿠터(E-scooter)를 포함하는 전기 이륜차; 전기 골프 카트(electric golf cart); 전력 저장 장치(Energy Storage System) 등을 들 수 있으나, 이에 한정되는 것은 아니다.
이하의 실시예, 비교예 및 실험예에서 본 발명의 내용을 보다 구체적으로 설명하지만, 본 발명이 이에 제한되는 것은 아니다.
<실시예 1>
<1-1 라텍스 입자(A1)의 제조>
단량체는 1,3-부타디엔(45g), 스티렌(50g), 아크릴산(3g), 히드록시에틸아크릴레이트(2g), 버퍼(buffer)로서 NaHCO3(0.4g), 소디움 라우릴 설페이트(0.4g), 분자량 조절제로 도데실 메르캅탄(0.5g)를 일괄 투여한다. 이들을 혼합하여 80℃까지 승온시킨 후, 중합 개시제로서 포타슘 퍼설페이트를 넣어 반응을 개시한 후, 6 시간동안 80℃를 유지하면서 반응시켜 부타디엔 라텍스 입자(A1)를 수득하였으며, 중합된 라텍스 입자의 pH는 4.5이었다. 평균 입경은 유화제의 양에 의해 조절하게 되는데, 일반적으로 유화제의 양이 증가할수록 입자의 크기는 작아지므로 원하는 크기, 반응시간, 반응 안정성 등을 고려하여 유화제 사용량을 조절해 사용할 수 있다.
<1-2 라텍스 입자(B1)의 제조>
단량체는 부틸 아크릴레이트(70g), 스티렌(20g), 아크릴산(5g), 히드록시 부틸아크릴레이트(5g), 버퍼로서 NaHCO3(0.4g), 유화제로서 소디움 라우릴 설페이트(0.4g)를 사용하여 이들을 혼합하여 75℃까지 승온시킨 후, 중합 개시제로서 암모늄 퍼설페이트를 넣어 중합을 시작한다. 온도 75℃를 유지하며 약 6시간 동안 반응시켜 라텍스 입자(B1)를 제조하였다. 라텍스 입자의 pH는 3.5 였다.
<1-3 바인더 조성물의 제조>
상기 수득한 바인더를 고형물 중량 비율로 라텍스 입자(A1): 라텍스 입자(B1) = 40: 60 으로 혼합하여 복합 라텍스를 포함하는 바인더 조성물을 제조하였다. 복합 라텍스의 pH는 약 4였다. 혼합 후 200mesh 체로 걸러 잔량을 확인하여 응집(agglomeration)현상이 발생하지 않았음을 확인하였다.
<1-4 전극 슬러리 및 전극의 제조>
음극은 물을 분산매로 하여 전체 고형분 100g 중량 기준으로 인조 흑연 95.5(g), 아세틸렌 블랙(1g), 상기 제조한 이차전지용 바인더(2.5g), 증점제로 카르복시 메틸 셀룰로우즈(1g)를 혼합하고, 전체 고형분 함량이 48 중량%가 되도록 하여 음극용 슬러리를 제조하고 구리 호일에 200 마이크로미터의 두께로 도포한 후 진공 건조하고 프레스하여 음극을 제조하였다.
양극은, NMP(N-methyl-2-pyrrolidone)를 분산매로 사용하고, 활물질인 LiCoO2(96g), 아세틸렌 블랙(2g) 및 PVDF 바인더(2g)를 혼합하여 슬러리를 제조한 후 알루미늄 호일에 250 마이크로미터의 두께로 코팅하여 건조한 후 압착하여 양극을 제조하였다.
<1-5 리튬 이차전지의 제조>
제조된 음극 극판을 표면적 13.33 cm2로 뚫고, 양극 극판은 표면적 12.60 cm2로 뚫어 단일셀(mono-cell)을 제작하였다. 탭을 상기 양극의 상부 및 상기 음극의 상부에 부착하고, 음극과 양극 사이에 폴리올레핀 미세 다공막으로 만들어진 분리막으로 개재시켜 상기 결과물을 알루미늄 파우치에 적재한 후, 전해액 500 mg을 파우치 내부에 주입하였다. 전해액은, EC(Ethyl carbonate): DEC(Diethyl carbonate): EMC(Ethyl-methyl carbonate) = 4:3:3(체적비) 혼합용매를 사용하여 LiPF6 전해질을 1M의 농도로 용해시켜 제조하였다. 이후, 진공포장기를 이용하여 상기 파우치를 밀봉하고 상온에서 12시간 동안 유지시킨 후, 약 0.05도 비율로 정전류 충전하고 전류의 약 1/6이 될 때까지 전압을 유지시켜주는 정전압 충전 과정을 거친다. 이 때, 셀 내부에 가스가 발생하므로, 탈 가스(degassing)와 재실링(resealing)과정을 수행하여 리튬 이차전지를 완성하였다.
<실시예 2>
고형물 중량 비율로 라텍스 입자(A1): 라텍스 입자(B1) = 30: 70으로 혼합하여 바인더 조성물을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다. 복합 라텍스의 pH는 약 3.8였다.
<실시예 3>
고형물 중량 비율로 라텍스 입자(A1): 라텍스 입자(B1) = 20: 80으로 혼합하여 바인더 조성물을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다. 복합 라텍스의 pH는 약 3.7였다.
<실시예 4>
라텍스 입자(B1)의 pH를 4.5로 조절하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다. 이때, 복합 라텍스의 pH는 4.5였다.
<실시예 5>
고형분 중량 비율로 라텍스 입자(A1): 라텍스 입자(B1) = 80: 20으로 혼합하여 바인더 조성물을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다. 복합 라텍스의 pH는 약 4.1였다.
<실시예 6>
고형물 중량 비율로 라텍스 입자(A1): 라텍스 입자(B1) = 90: 10으로 혼합하여 바인더 조성물을 제조하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다. 복합 라텍스의 pH는 약 4.2였다.
<비교예 1>
바인더 조성물에 라텍스 입자(A1)만을 단독으로 첨가하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다.
<비교예 2>
바인더 조성물에 라텍스 입자(B1)만을 단독으로 첨가하였다는 점을 제외하고는, 실시예 1과 동일한 방법으로 리튬 이차전지를 제조하였다.
<비교예 3>
라텍스 입자(B1)의 pH를 8로 조절한 점을 제외하고는, 실시예 3과 동일한 방법으로 리튬 이차전지를 제조하였다. 이때, 복합 라텍스의 pH는 7.3였다.
<실험예 1>
<전지 테스트>
상기 실시예 1 내지 6 및 비교예 1 내지 3에서 제조된 전지의 충방전 실험을 행하였다. 우선 충방전 전류 밀도를 0.2C로 하고, 충전 종지 전압을 4.2V(Li/Li+), 방전 종지 전압을 3V(Li/Li+)로 한 충방전 시험을 2회 시행하였다. 뒤이어, 충방전 전류 밀도를 1C로 하고 충전 종지 전압을 4.2V(Li/Li+), 방전 종지 전압을 3V(Li/Li+)로 한 충방전 시험을 100회 시행하였다. 모든 충전은 정전류/정전압으로 행하고, 정전압 충전의 종지 전류는 0.05C로 하였다. 총 102 사이클의 시험을 완료한 후 102번째 사이클의 방전 용량을 세번째 사이클의 방전 용량으로 나누는 용량비(102th/3rd)를 구하여 100 사이클의 용량 유지율로 간주하였다. 이들의 결과를 하기 표 1에 나타내었다.
<실험예 2>
<전지 테스트>
충방전 전류 밀도를 0.2C로 하고 방전용량의 50% 를 충전한 다음 5C의 고전류로 30초 동안 방전하여 DC-IR 저항을 측정하고 결과를 하기 표 1에 나타내였다.
Figure PCTKR2016006395-appb-T000001
상기 표 1을 참조하면, 비교예 3의 경우 응집이 생겨서 전극 테스트를 진행하지 못하였다.
비교예 2를 제외하고는 실시예 1 내지 6의 바인더 및 비교예 1의 바인더의 용량 유지율은 유사하지만, 비교예 1의 바인더에 비해 실시예 1 내지 6의 바인더의 저항이 낮음을 확인할 수 있고, 반면, 비교예 2의 경우 저항특성은 낮지만 나머지 바인더에 비해 용량유지율이 상당히 떨어짐을 확인할 수 있다.
즉, 본 발명에 따른 조건을 만족해야 용량 유지율이 우수하고, 저항이 낮은 특성을 가질 수 있음을 알 수 있다.
한편, 실시예들끼리 비교해보면, 라텍스 입자(A1)을 고형분 전체 중량을 기준으로 50 중량% 이하로 포함한 실시예 1 내지 4의 바인더가 라텍스 입자(A1)을 50 중량%를 초과하여 포함한 실시예 5 및 6의 바인더보다 더욱 우수한 저항 특성을 나타냄을 확인할 수 있다.
이상, 본 발명에 따른 실시예를 참조하여 발명의 내용을 상술하였지만, 본 발명이 속한 분야에서 통상의 지식을 가진 자라면 상기 내용을 바탕으로 본 발명의 범주내에서 다양한 응용 및 변형을 행하는 것이 가능할 것이다.
이상에서 설명한 바와 같이, 본 발명에 따른 바인더 조성물을 전극 합제 및 리튬 이차전지에 적용할 경우, 충방전 시 부피 변화를 겪는 전극 물질들 상호간 및 전극 물질과 집전체 사이의 우수한 결합력을 유지시켜 용량 유지율이 우수하고, 전극의 저항 및 이온전도도 특성을 향상시키므로 출력특성이 우수한 전지를 제공할 수 있는 효과가 있다.

Claims (19)

  1. 이차전지용 바인더 조성물로서,
    콘쥬케이트 디엔(conjugated dienes) 라텍스(latex) 입자(A)와 코폴리머(compolymer) 라텍스(latex) 입자(B)가 독립적인 상으로 존재하는 복합 라텍스를 포함하며,
    상기 복합 라텍스의 pH가 7 이하인 것을 특징으로 하는 조성물.
  2. 제 1 항에 있어서, 상기 콘쥬게이트 디엔 라텍스 입자(A)는,
    (가) 공액 디엔계 단량체 또는 공액 디엔계 중합체;
    (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체;
    (다) 불포화 카르본산계 단량체; 및
    (라) 히드록시기 함유 단량체;
    로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체의 중합물을 포함하는 것을 특징으로 하는 조성물.
  3. 제 1 항에 있어서, 상기 아크릴계 코폴리머 라텍스 입자(B)는,
    (가) (메타)아크릴산 에스테르계 단량체;
    (나) 아크릴레이트계 단량체, 비닐계 단량체, (메타)아크릴 아미드계 단량체 및 니트릴계 단량체로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체;
    (다) 불포화 카르본산계 단량체; 및
    (라) 히드록시기 함유 단량체;
    로 이루어진 군에서 선택되는 하나 또는 둘 이상의 단량체의 중합물을 포함하는 것을 특징으로 하는 조성물.
  4. 제 2 항에 있어서, 콘쥬게이트 라텍스 입자(A) 전체 중량을 기준으로 상기 (가) 공액 디엔계 단량체 또는 공액 디엔계 중합체는 10 내지 97.4 중량%로 포함되어 있고, 상기 (나)군 단량체는 1 내지 70 중량%로 포함되어 있으며, (다) 불포화 카르본산계 단량체는 1 내지 20 중량% 포함되어 있고, (라) 히드록시기 함유 단량체는 0.5 내지 5 중량% 포함되어 있는 것을 특징으로 하는 조성물.
  5. 제 3 항에 있어서, 아크릴계 코폴리머 라텍스 입자(B) 전체 중량을 기준으로 상기 (가) (메타)아크릴산 에스테르계 단량체는 10 내지 96.9 중량%로 포함되어 있고, 상기 (나)군 단량체는 1 내지 60 중량%로 포함되어 있으며, (다) 불포화 카르본산계 단량체는 1 내지 10 중량% 포함되어 있고, (라) 히드록시기 함유 단량체는 1 내지 10 중량% 포함되어 있는 것을 특징으로 하는 조성물.
  6. 제 2 항에 있어서, 상기 공액 디엔계 단량체는, 1,3-부타디엔, 이소프렌, 클로로프렌, 및 피레리덴으로 이루어진 군에서 선택되는 하나의 단량체이고, 상기 공액 디엔계 중합체는, 1,3-부타디엔, 이소프렌, 클로로프렌, 및 피레리덴으로 이루어진 군에서 선택되는 둘 이상의 단량체들의 중합체, 스티렌-부타디엔 공중합체, 아크릴로니트릴-부타디엔 공중합체, 스티렌-이소프렌 공중합체, 아크릴레이트-부타디엔 고무, 아크릴로니트릴-부타디엔-스티렌 고무, 에틸렌-프로필렌-디엔계 중합체 또는 이들 중합체가 부분적으로 수소화, 에폭시화, 브롬화된 중합체 및 이들의 혼합물인 것을 특징으로 하는 조성물.
  7. 제 3 항에 있어서, 상기 (메타)아크릴산 에스테르계 단량체는 메틸아크릴레이트, 에틸아크릴레이트, 프로필아크릴레이트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 이소부틸아크릴레이트, n-아밀아크릴레이트, 이소아밀아크릴레이트, n-에틸헥실아크릴레이트, 2-에틸헥실아크릴레이트, 메틸메타크릴레이트, 에틸메타크릴레이트, 프로필메크릴레이트, 이소프로필메크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-아밀메타크릴레이트, 이소아밀메타크릴레이트, n-헥실메타크릴레이트, n-에틸헥실 메타크릴레이트, 2-에틸헥실 메타크릴레이트 라우릴 아크릴레이트, 세릴 아크릴레이트, 스테아릴 아크릴레이트, 라우릴 메타 아크릴레이트, 세틸 메타 아크릴레이트, 및 스테아릴 메타 아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  8. 제 2 항 또는 제 3 항에 있어서, 상기 아크릴레이트계 단량체는 메타아크릴록시 에틸에틸렌우레아, β-카르복시 에틸아크릴레이트, 알리파틱 모노아크릴레이트, 디프로필렌 디아크릴레이트, 디트리메틸로프로판 테트라아크릴레이트, 디펜타에리트리올 헥사아크릴레이트, 펜타에리트리올 트리아크릴레이트, 펜타에리트리올 테트라아크릴레이트, 글리시딜 메타 아크릴레이트로 이루어진 군으로부터 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  9. 제 2 항 또는 제 3 항에 있어서, 상기 비닐계 단량체는 스티렌, α-메틸스티렌, β-메틸스티렌, p-t-부틸스티렌 및 디비닐벤젠으로 이루어진 군으로부터 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  10. 제 2 항 또는 제 3 항에 있어서, 상기 (메타)아크릴 아미드계 단량체는 아크릴 아미드, n-메틸올 아크릴아미드, n-부톡시 메틸아크릴아미드, 메타크릴아미드, n-메틸올 메타크릴아미드, n-부톡시 메틸메타크릴아미드로 이루어진 군으로부터 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  11. 제 2항 또는 제 3 항에 있어서, 상기 니트릴계 단량체는 알케닐 시아나이드인 것을 특징으로 하는 조성물.
  12. 제 11 항에 있어서, 상기 알케닐 시아나이드는, 아크릴로니트릴, 메타크릴로니트릴, 및 알릴 시아나이드로 이루어진 군으로부터 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  13. 제 2 항 또는 제 3 항에 있어서, 상기 불포화 카르본산계 단량체는, 말레인산, 푸마르산, 메타크릴산, 아크릴산, 글루타르산, 이타콘산, 테트라하이드로프탈산, 코로톤산, 이소크로톤산 및 나딕산으로 이루어진 군에서 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  14. 제 2 항 또는 제 3 항에 있어서, 상기 히드록시기를 포함하는 단량체는 하이드록시에틸 아크릴레이트, 하이드록시부틸 아크릴레이트, 히드록시프로필 아크릴레이트, 히드록시에틸 메타크릴레이트, 히드록시프로필 메타크릴레이트, 히드록시 부틸 메타크릴레이트로 이루어진 군에서 선택되는 1종 이상의 단량체인 것을 특징으로 하는 조성물.
  15. 제 1 항에 있어서, 상기 바인더 조성물은 콘쥬게이트 디엔 라텍스 입자(A)를 복합 라텍스의 고형분 전체 중량을 기준으로 1 내지 50 중량%로 포함하는 것을 특징으로 하는 조성물.
  16. 제 1 항에 있어서, 상기 바인더 조성물은 전해액에 대한 스웰링도(swelling index)가 1.5 내지 5인 것을 특징으로 하는 조성물.
  17. 제 1 항에 따른 바인더 조성물과, 리튬을 흡장, 방출할 수 있는 전극 활물질을 포함하는 것을 특징으로 하는 이차전지의 전극 합제.
  18. 제 17 항에 따른 전극 합제가 집전체에 도포되어 있는 것을 특징으로 하는 이차전지용 전극.
  19. 제 18 항에 따른 이차전지용 전극을 포함하는 것을 특징으로 하는 리튬 이차전지.
PCT/KR2016/006395 2015-06-17 2016-06-16 이차전지용 바인더 조성물, 이를 사용한 전극 및 리튬 이차전지 WO2016204530A1 (ko)