WO2016076106A1 - Électrode de génération d'hydrogène - Google Patents

Électrode de génération d'hydrogène Download PDF

Info

Publication number
WO2016076106A1
WO2016076106A1 PCT/JP2015/080226 JP2015080226W WO2016076106A1 WO 2016076106 A1 WO2016076106 A1 WO 2016076106A1 JP 2015080226 W JP2015080226 W JP 2015080226W WO 2016076106 A1 WO2016076106 A1 WO 2016076106A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
hydrogen
hydrogen generating
generating electrode
semiconductor layer
Prior art date
Application number
PCT/JP2015/080226
Other languages
English (en)
Japanese (ja)
Inventor
一成 堂免
尚俊 佐藤
耕 嶺岸
啓 熊谷
Original Assignee
富士フイルム株式会社
国立大学法人東京大学
人工光合成化学プロセス技術研究組合
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社, 国立大学法人東京大学, 人工光合成化学プロセス技術研究組合 filed Critical 富士フイルム株式会社
Priority to JP2016558960A priority Critical patent/JP6388665B2/ja
Publication of WO2016076106A1 publication Critical patent/WO2016076106A1/fr

Abstract

Cette invention concerne une électrode de génération d'hydrogène qui produit de l'hydrogène à partir d'une solution d'électrolyte aqueux, en utilisant de la lumière. Ladite électrode de génération d'hydrogène comprend : une couche conductrice; une couche de semi-conducteur inorganique qui est disposée sur la couche conductrice et comprend une jonction pn; une couche métallique qui est formée sur la surface de la couche de semi-conducteur inorganique; et un promoteur qui est supporté par la surface de la couche métallique. La lumière est incidente sur celle-ci à partir du côté du promoteur.
PCT/JP2015/080226 2014-11-12 2015-10-27 Électrode de génération d'hydrogène WO2016076106A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016558960A JP6388665B2 (ja) 2014-11-12 2015-10-27 水素発生電極

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2014229653 2014-11-12
JP2014-229653 2014-11-12
JP2015-169713 2015-08-28
JP2015169713 2015-08-28

Publications (1)

Publication Number Publication Date
WO2016076106A1 true WO2016076106A1 (fr) 2016-05-19

Family

ID=55954198

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/080226 WO2016076106A1 (fr) 2014-11-12 2015-10-27 Électrode de génération d'hydrogène

Country Status (2)

Country Link
JP (1) JP6388665B2 (fr)
WO (1) WO2016076106A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018135144A1 (fr) * 2017-01-18 2018-07-26 日立化成株式会社 Méthode de production d'hydrogène gazeux et méthode de production d'un dispositif semi-conducteur
KR20190081406A (ko) * 2017-12-29 2019-07-09 인천대학교 산학협력단 광 촉매 전극, 그 제조 방법 및 광 촉매 장치
WO2019172014A1 (fr) * 2018-03-06 2019-09-12 富士フイルム株式会社 Électrode photocatalytique pour électrolyse et dispositif d'électrolyse
WO2023283687A1 (fr) * 2021-07-15 2023-01-19 Australian National University Photoélectrode et son procédé de fabrication
WO2023089656A1 (fr) * 2021-11-16 2023-05-25 日本電信電話株式会社 Procédé de production d'une photoélectrode à semi-conducteur

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS51151273A (en) * 1975-06-20 1976-12-25 Toray Ind Inc A light radiation type water electrolysis system
JPS5237574A (en) * 1975-09-19 1977-03-23 Sanyo Electric Co Ltd Water decomposition apparatus using light energy
JP2012046385A (ja) * 2010-08-27 2012-03-08 Mitsubishi Chemical Holdings Corp 光水分解用電極、光水分解用電極の製造方法、および、水分解方法
JP2014101550A (ja) * 2012-11-20 2014-06-05 Toshiba Corp 光化学反応システム
JP2014101551A (ja) * 2012-11-20 2014-06-05 Toshiba Corp 光化学反応装置

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8388818B1 (en) * 2007-07-16 2013-03-05 Shalini Menezes Photoelectrochemical generation of hydrogen
KR102014990B1 (ko) * 2013-01-29 2019-08-27 삼성전자주식회사 광전극 구조체용 복합 보호층, 이를 포함하는 광전극 구조체 및 이를 포함하는 광전기화학 전지

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS51151273A (en) * 1975-06-20 1976-12-25 Toray Ind Inc A light radiation type water electrolysis system
JPS5237574A (en) * 1975-09-19 1977-03-23 Sanyo Electric Co Ltd Water decomposition apparatus using light energy
JP2012046385A (ja) * 2010-08-27 2012-03-08 Mitsubishi Chemical Holdings Corp 光水分解用電極、光水分解用電極の製造方法、および、水分解方法
JP2014101550A (ja) * 2012-11-20 2014-06-05 Toshiba Corp 光化学反応システム
JP2014101551A (ja) * 2012-11-20 2014-06-05 Toshiba Corp 光化学反応装置

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018135144A1 (fr) * 2017-01-18 2018-07-26 日立化成株式会社 Méthode de production d'hydrogène gazeux et méthode de production d'un dispositif semi-conducteur
KR20190081406A (ko) * 2017-12-29 2019-07-09 인천대학교 산학협력단 광 촉매 전극, 그 제조 방법 및 광 촉매 장치
KR102050206B1 (ko) 2017-12-29 2019-11-29 인천대학교 산학협력단 광 촉매 전극, 그 제조 방법 및 광 촉매 장치
WO2019172014A1 (fr) * 2018-03-06 2019-09-12 富士フイルム株式会社 Électrode photocatalytique pour électrolyse et dispositif d'électrolyse
CN111836779A (zh) * 2018-03-06 2020-10-27 富士胶片株式会社 水分解用光催化剂电极及水分解装置
JPWO2019172014A1 (ja) * 2018-03-06 2021-02-04 富士フイルム株式会社 水分解用光触媒電極および水分解装置
JP7026773B2 (ja) 2018-03-06 2022-02-28 富士フイルム株式会社 水分解用光触媒電極および水分解装置
WO2023283687A1 (fr) * 2021-07-15 2023-01-19 Australian National University Photoélectrode et son procédé de fabrication
WO2023089656A1 (fr) * 2021-11-16 2023-05-25 日本電信電話株式会社 Procédé de production d'une photoélectrode à semi-conducteur

Also Published As

Publication number Publication date
JPWO2016076106A1 (ja) 2017-09-07
JP6388665B2 (ja) 2018-09-12

Similar Documents

Publication Publication Date Title
JP6388665B2 (ja) 水素発生電極
US11098410B2 (en) Artificial photosynthesis module
JP6316436B2 (ja) 水素発生電極、および人工光合成モジュール
US10258971B2 (en) Photocatalyst electrode and artificial photosynthesis module
Gaillard et al. Wide-bandgap Cu (In, Ga) S2 photocathodes integrated on transparent conductive F: SnO2 substrates for chalcopyrite-based water splitting tandem devices
JP2011171707A (ja) 太陽電池および太陽電池の製造方法
JP7026773B2 (ja) 水分解用光触媒電極および水分解装置
JP6470868B2 (ja) 人工光合成モジュール
WO2015087682A1 (fr) Module de photosynthèse artificielle
WO2015087828A1 (fr) Système d'électrolyse de l'eau
JP2011176285A (ja) 光電変換素子、薄膜太陽電池および光電変換素子の製造方法
JP5815848B2 (ja) 光電変換装置の製造方法
JP6412417B2 (ja) 水素発生電極およびその製造方法
Gaillard et al. Development of chalcogenide thin film materials for photoelectrochemical hydrogen production
KR101036165B1 (ko) 칼코지나이드계 태양전지의 제조방법
JP6322558B2 (ja) 水素発生電極の再生方法
JP6559710B2 (ja) 水素発生電極
JP2011159796A (ja) 絶縁層付基板および薄膜太陽電池
JP2010232427A (ja) 光電変換素子、その製造方法、それに用いられる陽極酸化基板及び太陽電池
TW201427054A (zh) 光電變換元件及其製造方法、光電變換元件的緩衝層的製造方法與太陽電池
JP7320775B2 (ja) 水素発生用電極及び水素発生用電極の製造方法
JPWO2014002646A1 (ja) 光電変換装置の製造方法
JP2012182340A (ja) 化合物半導体及び太陽電池
JP5964683B2 (ja) 光電変換装置の製造方法
JP2015056421A (ja) 光電変換素子の製造方法および光水分解用電極

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15859919

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016558960

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15859919

Country of ref document: EP

Kind code of ref document: A1