WO2016031946A1 - Film d'augmentation de luminosité et dispositif d'affichage à cristaux liquides - Google Patents

Film d'augmentation de luminosité et dispositif d'affichage à cristaux liquides Download PDF

Info

Publication number
WO2016031946A1
WO2016031946A1 PCT/JP2015/074321 JP2015074321W WO2016031946A1 WO 2016031946 A1 WO2016031946 A1 WO 2016031946A1 JP 2015074321 W JP2015074321 W JP 2015074321W WO 2016031946 A1 WO2016031946 A1 WO 2016031946A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
layer
brightness enhancement
enhancement film
plate
Prior art date
Application number
PCT/JP2015/074321
Other languages
English (en)
Japanese (ja)
Inventor
阿出川　豊
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2016545629A priority Critical patent/JPWO2016031946A1/ja
Publication of WO2016031946A1 publication Critical patent/WO2016031946A1/fr

Abstract

La présente invention concerne un film d'augmentation de luminosité ayant une lame λ/4 et un polariseur réfléchissant, où la lame λ/4 comprend une couche de résine I, la couche de résine I comprend un polymère ayant une valeur de biréfringence intrinsèque négative, le polymère comprend un motif de répétition dérivé d'un monomère d'anhydride d'acide, le polymère comprend de 5 à 50 % en poids du motif de répétition dérivée du monomère d'anhydride d'acide, le polariseur réfléchissant comprend une couche de réflexion de lumière formée par fixation d'une phase cristalline liquide cholestérique, et dans lequel la couche de réflexion de lumière est une couche laminée avec une couche d'alignement en contact direct avec la lame λ/4 intercalée entre celles-ci. L'invention concerne en outre un dispositif d'affichage à cristaux liquides utilisant le film d'augmentation de luminosité. Lorsqu'il est installé dans le dispositif d'affichage à cristaux liquides, le film d'augmentation de luminosité produit un taux d'amélioration de luminosité élevée et est capable de supprimer un changement de couleur en diagonale.
PCT/JP2015/074321 2014-08-29 2015-08-28 Film d'augmentation de luminosité et dispositif d'affichage à cristaux liquides WO2016031946A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2016545629A JPWO2016031946A1 (ja) 2014-08-29 2015-08-28 輝度向上フィルムおよび液晶表示装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014176188 2014-08-29
JP2014-176188 2014-08-29

Publications (1)

Publication Number Publication Date
WO2016031946A1 true WO2016031946A1 (fr) 2016-03-03

Family

ID=55399829

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/074321 WO2016031946A1 (fr) 2014-08-29 2015-08-28 Film d'augmentation de luminosité et dispositif d'affichage à cristaux liquides

Country Status (2)

Country Link
JP (1) JPWO2016031946A1 (fr)
WO (1) WO2016031946A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016113555A (ja) * 2014-12-16 2016-06-23 日本ゼオン株式会社 液晶性組成物、円偏光分離素子及びその製造方法、偽造防止用媒体及びその製造方法、輝度向上フィルム並びにセキュリティ媒体
WO2016190435A1 (fr) * 2015-05-28 2016-12-01 日本ゼオン株式会社 Film séparateur de lumière à polarisation circulaire et procédé de fabrication de ce film
JP6055569B1 (ja) * 2016-05-18 2016-12-27 日本ゼオン株式会社 重合性化合物、混合物、重合性液晶組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム
JPWO2016114346A1 (ja) * 2015-01-16 2017-04-27 Dic株式会社 重合性組成物及びそれを用いた光学異方体
JP6146526B1 (ja) * 2016-10-06 2017-06-14 日本ゼオン株式会社 混合物、重合性組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム、並びに重合性化合物の使用方法
JP2017206504A (ja) * 2017-04-27 2017-11-24 日本ゼオン株式会社 化合物、重合性化合物、混合物、重合性液晶組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム
JP2022510576A (ja) * 2018-11-19 2022-01-27 ヒョスン ケミカル コーポレーション セルロースエステル位相差フィルム

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004233666A (ja) * 2003-01-30 2004-08-19 Nippon Zeon Co Ltd 光学積層体原反の製造方法、光学積層体、バックライトユニット及び液晶表示装置
JP2005189392A (ja) * 2003-12-25 2005-07-14 Nitto Denko Corp 高輝度偏光板および画像表示装置
JP2008273925A (ja) * 2006-12-15 2008-11-13 Fujifilm Corp 光学フィルムおよび位相差板、並びに液晶化合物
JP2009237533A (ja) * 2007-11-30 2009-10-15 Jsr Corp 積層光学フィルムの製造方法、積層光学フィルムおよびその用途
JP2010181710A (ja) * 2009-02-06 2010-08-19 Nippon Zeon Co Ltd 偏光板、及び液晶表示装置
JP2011118137A (ja) * 2009-12-03 2011-06-16 Nippon Zeon Co Ltd 輝度向上フィルム、製造方法及び液晶表示装置

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004233666A (ja) * 2003-01-30 2004-08-19 Nippon Zeon Co Ltd 光学積層体原反の製造方法、光学積層体、バックライトユニット及び液晶表示装置
JP2005189392A (ja) * 2003-12-25 2005-07-14 Nitto Denko Corp 高輝度偏光板および画像表示装置
JP2008273925A (ja) * 2006-12-15 2008-11-13 Fujifilm Corp 光学フィルムおよび位相差板、並びに液晶化合物
JP2009237533A (ja) * 2007-11-30 2009-10-15 Jsr Corp 積層光学フィルムの製造方法、積層光学フィルムおよびその用途
JP2010181710A (ja) * 2009-02-06 2010-08-19 Nippon Zeon Co Ltd 偏光板、及び液晶表示装置
JP2011118137A (ja) * 2009-12-03 2011-06-16 Nippon Zeon Co Ltd 輝度向上フィルム、製造方法及び液晶表示装置

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016113555A (ja) * 2014-12-16 2016-06-23 日本ゼオン株式会社 液晶性組成物、円偏光分離素子及びその製造方法、偽造防止用媒体及びその製造方法、輝度向上フィルム並びにセキュリティ媒体
JPWO2016114346A1 (ja) * 2015-01-16 2017-04-27 Dic株式会社 重合性組成物及びそれを用いた光学異方体
JPWO2016190435A1 (ja) * 2015-05-28 2018-03-15 日本ゼオン株式会社 円偏光分離フィルム及びその製造方法
WO2016190435A1 (fr) * 2015-05-28 2016-12-01 日本ゼオン株式会社 Film séparateur de lumière à polarisation circulaire et procédé de fabrication de ce film
US10620352B2 (en) 2015-05-28 2020-04-14 Zeon Corporation Circularly polarized light separating film and method for producing same
JP6055569B1 (ja) * 2016-05-18 2016-12-27 日本ゼオン株式会社 重合性化合物、混合物、重合性液晶組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム
JP2017206460A (ja) * 2016-05-18 2017-11-24 日本ゼオン株式会社 重合性化合物、混合物、重合性液晶組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム
WO2018066486A1 (fr) * 2016-10-06 2018-04-12 日本ゼオン株式会社 Mélange, composition polymérisable, polymère, film optique, objet optiquement anisotrope, polariseur, dispositif d'affichage à écran plat, dispositif d'affichage électroluminescent organique, film antiréfléchissant, et procédé d'utilisation d'un composé polymérisable
JP2018058998A (ja) * 2016-10-06 2018-04-12 日本ゼオン株式会社 混合物、重合性組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム、並びに重合性化合物の使用方法
JP6146526B1 (ja) * 2016-10-06 2017-06-14 日本ゼオン株式会社 混合物、重合性組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム、並びに重合性化合物の使用方法
JP2017206504A (ja) * 2017-04-27 2017-11-24 日本ゼオン株式会社 化合物、重合性化合物、混合物、重合性液晶組成物、高分子、光学フィルム、光学異方体、偏光板、フラットパネル表示装置、有機エレクトロルミネッセンス表示装置および反射防止フィルム
JP2022510576A (ja) * 2018-11-19 2022-01-27 ヒョスン ケミカル コーポレーション セルロースエステル位相差フィルム
JP7157248B2 (ja) 2018-11-19 2022-10-19 ヒョスン ケミカル コーポレーション セルロースエステル位相差フィルム

Also Published As

Publication number Publication date
JPWO2016031946A1 (ja) 2017-07-20

Similar Documents

Publication Publication Date Title
JP6321052B2 (ja) 輝度向上フィルム、光学シート部材および液晶表示装置
JP6441899B2 (ja) 組成物、光反射膜、輝度向上フィルム、バックライトユニット及び液晶表示装置
WO2016031946A1 (fr) Film d'augmentation de luminosité et dispositif d'affichage à cristaux liquides
JP6375381B2 (ja) 光学フィルム、照明装置および画像表示装置
TWI257508B (en) Methods of making polarization rotators and articles containing the polarization rotators
WO2016088708A1 (fr) Miroir ayant une fonction d'affichage d'image
US20180143363A1 (en) Mirror with image display function
JP2019079064A (ja) 光学フィルムおよび液晶表示装置、ならびに光学フィルムの製造方法
JP2007065314A (ja) 円偏光分離シート
JP6262351B2 (ja) フィルム、フィルムの製造方法、輝度向上フィルム、光学シート部材および液晶表示装置
JP5025121B2 (ja) 円偏光分離シート及びその製法、並びにそれを用いた液晶表示装置
WO2017145580A1 (fr) Rétroviseur de véhicule à fonction d'affichage d'image et procédé de fabrication associé
JP2004226686A (ja) 広帯域１／４波長板原反、広帯域円偏光板原反、光学素子原反及び表示装置
KR102140552B1 (ko) 광학 소자, 광학 소자의 제조 방법 및 액정 표시 장치
WO2017057316A1 (fr) Film optique, film à luminance améliorée, unité de rétro-éclairage comprenant un film à luminance améliorée et dispositif d'affichage à cristaux liquides
JP2017068111A (ja) 偏光板および液晶表示装置
WO2017104433A1 (fr) Miroir de véhicule ayant une fonction d'affichage d'image et procédé pour sa production
JP4307181B2 (ja) 光学異方性層、それを用いた位相差板、楕円偏光板及び液晶表示装置
JP2005062672A (ja) 光学異方性層、それを用いた位相差板、楕円偏光板及び液晶表示装置
JP6321210B2 (ja) 液晶表示装置
JP4570377B2 (ja) 光学積層体及び輝度向上フィルム
JP2017067964A (ja) 光学シートとその製造方法、液晶表示装置
JP2011145705A (ja) 円偏光分離シート及びその製法、並びにそれを用いた液晶表示装置
JP2004309598A (ja) 位相差板、楕円偏光板および液晶表示装置
JP2004309596A (ja) 楕円偏光板および液晶表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15836132

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2016545629

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15836132

Country of ref document: EP

Kind code of ref document: A1