WO2015093342A1 - Procédé pour fabriquer un film conducteur, film conducteur, élément électronique organique et panneau tactile - Google Patents

Procédé pour fabriquer un film conducteur, film conducteur, élément électronique organique et panneau tactile Download PDF

Info

Publication number
WO2015093342A1
WO2015093342A1 PCT/JP2014/082514 JP2014082514W WO2015093342A1 WO 2015093342 A1 WO2015093342 A1 WO 2015093342A1 JP 2014082514 W JP2014082514 W JP 2014082514W WO 2015093342 A1 WO2015093342 A1 WO 2015093342A1
Authority
WO
WIPO (PCT)
Prior art keywords
conductive
polyester resin
acid
conductive film
film
Prior art date
Application number
PCT/JP2014/082514
Other languages
English (en)
Japanese (ja)
Inventor
中村　和明
松村　智之
Original Assignee
コニカミノルタ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by コニカミノルタ株式会社 filed Critical コニカミノルタ株式会社
Priority to JP2015553489A priority Critical patent/JPWO2015093342A1/ja
Publication of WO2015093342A1 publication Critical patent/WO2015093342A1/fr

Abstract

Un but de la présente invention est de fournir : un procédé pour fabriquer un film conducteur qui est dépourvu de déformation d'une base et possède d'excellentes transparence, conductivité électrique et rugosité de surface ; et un film conducteur. Un autre but de la présente invention est de fournir un élément électronique organique et un panneau tactile, chacun d'eux comportant un film conducteur qui est fabriqué par le procédé de fabrication susmentionné. Un procédé pour fabriquer un film conducteur selon la présente invention est caractérisé par le fait qu'il comprend au moins une étape (A) et une étape (B), et est également caractérisé par une résine polyester qui contient, en tant que constituant, un acide dicarboxylique qui contient un acide dicarboxylique aromatique ayant au moins un groupe d'acide sulfonique à un taux à l'intérieur de la plage de 1-15% par mole. Ce procédé pour fabriquer un film conducteur est en outre caractérisé par le fait qu'un rayonnement de lumière infrarouge, qui possède un rapport de la radiance spectrale de la longueur d'onde de 5,8 µm par rapport à la radiance spectrale de la longueur d'onde de 3,0 µm de 5% ou moins, est réalisée à l'étape (B).
PCT/JP2014/082514 2013-12-16 2014-12-09 Procédé pour fabriquer un film conducteur, film conducteur, élément électronique organique et panneau tactile WO2015093342A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2015553489A JPWO2015093342A1 (ja) 2013-12-16 2014-12-09 導電性フィルムの製造方法、導電性フィルム、有機電子素子及びタッチパネル

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2013259156 2013-12-16
JP2013-259156 2013-12-16

Publications (1)

Publication Number Publication Date
WO2015093342A1 true WO2015093342A1 (fr) 2015-06-25

Family

ID=53402691

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/082514 WO2015093342A1 (fr) 2013-12-16 2014-12-09 Procédé pour fabriquer un film conducteur, film conducteur, élément électronique organique et panneau tactile

Country Status (2)

Country Link
JP (1) JPWO2015093342A1 (fr)
WO (1) WO2015093342A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012243460A (ja) * 2011-05-17 2012-12-10 Teijin Dupont Films Japan Ltd 導電性フィルム
JP2013131319A (ja) * 2011-12-20 2013-07-04 Konica Minolta Inc 透明導電膜及び有機エレクトロルミネッセンス素子並びに透明導電膜の製造方法
WO2013111511A1 (fr) * 2012-01-23 2013-08-01 日本碍子株式会社 Procédé de séchage et four de séchage de film de revêtement pour un film de revêtement formé sur une surface de film de pet

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2012243460A (ja) * 2011-05-17 2012-12-10 Teijin Dupont Films Japan Ltd 導電性フィルム
JP2013131319A (ja) * 2011-12-20 2013-07-04 Konica Minolta Inc 透明導電膜及び有機エレクトロルミネッセンス素子並びに透明導電膜の製造方法
WO2013111511A1 (fr) * 2012-01-23 2013-08-01 日本碍子株式会社 Procédé de séchage et four de séchage de film de revêtement pour un film de revêtement formé sur une surface de film de pet

Also Published As

Publication number Publication date
JPWO2015093342A1 (ja) 2017-03-16

Similar Documents

Publication Publication Date Title
JP5987843B2 (ja) 透明電極形成用組成物、透明電極、有機電子素子および透明電極の製造方法
JP5888084B2 (ja) 有機電子素子用透明電極、有機電子素子用透明電極の製造方法、及び有機電子素子
JP6020554B2 (ja) 導電膜及び有機エレクトロルミネッセンス素子
WO2016147481A1 (fr) Électrode transparente, procédé de fabrication d'électrode transparente, et élément électroluminescent organique
JP6319090B2 (ja) 透明電極の製造方法
JP5761058B2 (ja) 透明導電膜の製造方法及び有機エレクトロルミネッセンス素子
JP6024351B2 (ja) 導電膜及び有機エレクトロルミネッセンス素子並びに導電膜の製造方法
WO2014034920A1 (fr) Électrode transparente, procédé de production et dispositif électronique organique correspondants
JP5655745B2 (ja) 透明電極及び有機エレクトロルミネッセンス素子
WO2013061967A1 (fr) Film conducteur transparent et élément électroluminescent organique
JP2014229397A (ja) 導電膜の製造方法、導電膜、有機電子素子及びタッチパネル
JP5782855B2 (ja) 透明電極及び有機エレクトロルミネッセンス素子
JP5949494B2 (ja) 塗布液、導電膜製造方法及び有機エレクトロルミネッセンス素子製造方法
JP6003582B2 (ja) 透明電極の製造方法
JP5903874B2 (ja) 透明導電膜及び有機エレクトロルミネッセンス素子並びに透明導電膜の製造方法
US10103347B2 (en) Transparent electrode, method for manufacturing same, and organic electroluminescent element
JP6015764B2 (ja) 透明導電膜及び有機エレクトロルミネッセンス素子
JP2016110769A (ja) 透明電極の製造方法、透明電極、透明電極の製造装置、電子機器
JP5831303B2 (ja) 透明導電膜及び有機エレクトロルミネッセンス素子
JP5884671B2 (ja) 透明導電膜、有機エレクトロルミネッセンス素子及び透明導電膜の製造方法
JP5834954B2 (ja) 透明導電膜及び有機エレクトロルミネッセンス素子
WO2015093342A1 (fr) Procédé pour fabriquer un film conducteur, film conducteur, élément électronique organique et panneau tactile
JP2012138311A (ja) 透明導電膜基板および有機エレクトロルミネッセンス素子
JP2012243401A (ja) 透明導電膜及び有機エレクトロルミネッセンス素子

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14872536

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2015553489

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14872536

Country of ref document: EP

Kind code of ref document: A1