WO2015046614A1 - Matériau isolant thermique par le vide - Google Patents

Matériau isolant thermique par le vide Download PDF

Info

Publication number
WO2015046614A1
WO2015046614A1 PCT/JP2014/076227 JP2014076227W WO2015046614A1 WO 2015046614 A1 WO2015046614 A1 WO 2015046614A1 JP 2014076227 W JP2014076227 W JP 2014076227W WO 2015046614 A1 WO2015046614 A1 WO 2015046614A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas barrier
layer
heat insulating
vacuum heat
insulating material
Prior art date
Application number
PCT/JP2014/076227
Other languages
English (en)
Japanese (ja)
Inventor
浩介 植田
雄介 小賦
佳史子 川合
瞬也 南郷
Original Assignee
東洋製罐グループホールディングス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東洋製罐グループホールディングス株式会社 filed Critical 東洋製罐グループホールディングス株式会社
Publication of WO2015046614A1 publication Critical patent/WO2015046614A1/fr

Abstract

La présente invention concerne un matériau isolant thermique par le vide (1) comprenant un matériau central (2) et un matériau extérieur (3) recouvrant le matériau central (2), l'intérieur du matériau isolant thermique par le vide (1) étant scellé par dépressurisation, où : le matériau extérieur (3) comprend un objet stratifié barrière de gaz ayant au moins une couche thermosoudée (4), une couche de dépôt en phase vapeur (7b), et un matériau barrière de gaz (6) ; le matériau barrière de gaz (6) comprend un polymère d'acide polycarboxylique ; et le matériau isolant thermique par le vide a une couche barrière de gaz contenant au plus 1,4 % massique d'un élément métallique monovalent, au moins 5,0 % massique d'un élément métallique polyvalent, et entre 0,01 et 3,0 % massique d'un élément azoté par rapport à la masse totale d'azote et de carbone, le matériau isolant thermique par le vide étant f'une qualité exceptionnelle en termes de performance d'isolation thermique et propriétés de barrière de gaz, pouvant présenter une exceptionnelle performance d'isolation thermique pendant une longue durée, et ayant d'exceptionnelles propriétés de flexibilité et résistance à l'eau.
PCT/JP2014/076227 2013-09-30 2014-09-30 Matériau isolant thermique par le vide WO2015046614A1 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
JP2013-205341 2013-09-30
JP2013205340 2013-09-30
JP2013-205342 2013-09-30
JP2013-205340 2013-09-30
JP2013205342 2013-09-30
JP2013205341 2013-09-30

Publications (1)

Publication Number Publication Date
WO2015046614A1 true WO2015046614A1 (fr) 2015-04-02

Family

ID=52743735

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/076227 WO2015046614A1 (fr) 2013-09-30 2014-09-30 Matériau isolant thermique par le vide

Country Status (1)

Country Link
WO (1) WO2015046614A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105864579A (zh) * 2016-05-31 2016-08-17 苏州市君悦新材料科技股份有限公司 一种新型保温结构
CN108081713A (zh) * 2017-12-18 2018-05-29 厦门菲尔牡真空技术有限公司 一种低热桥效应阻隔膜及采用该阻隔膜的真空绝热板
EP3360680A4 (fr) * 2017-02-28 2018-10-10 Cj Cheiljedang Corporation Matériau stratifié pour matériau de revêtement de panneau d'isolation sous vide, et matériau de revêtement de panneau d'isolation sous vide le comprenant
CN110603403A (zh) * 2017-05-09 2019-12-20 大日本印刷株式会社 真空绝热材料用外包材料、真空绝热材料和带真空绝热材料的物品

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004130654A (ja) * 2002-10-10 2004-04-30 Toppan Printing Co Ltd 真空断熱材
JP3685206B1 (ja) * 2004-08-03 2005-08-17 松下電器産業株式会社 真空断熱材、真空断熱材を適用した保温保冷機器および事務機器
JP2005337405A (ja) * 2004-05-27 2005-12-08 Kureha Chem Ind Co Ltd 真空断熱材
JP2006308086A (ja) * 2005-03-30 2006-11-09 Kuraray Co Ltd 真空断熱体
JP2010236638A (ja) * 2009-03-31 2010-10-21 Kuraray Co Ltd 真空断熱体
JP2012135892A (ja) * 2010-12-24 2012-07-19 Dainippon Printing Co Ltd 直線引き裂き性透明積層フィルム並びにこれを用いた積層体及び包装袋

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004130654A (ja) * 2002-10-10 2004-04-30 Toppan Printing Co Ltd 真空断熱材
JP2005337405A (ja) * 2004-05-27 2005-12-08 Kureha Chem Ind Co Ltd 真空断熱材
JP3685206B1 (ja) * 2004-08-03 2005-08-17 松下電器産業株式会社 真空断熱材、真空断熱材を適用した保温保冷機器および事務機器
JP2006308086A (ja) * 2005-03-30 2006-11-09 Kuraray Co Ltd 真空断熱体
JP2010236638A (ja) * 2009-03-31 2010-10-21 Kuraray Co Ltd 真空断熱体
JP2012135892A (ja) * 2010-12-24 2012-07-19 Dainippon Printing Co Ltd 直線引き裂き性透明積層フィルム並びにこれを用いた積層体及び包装袋

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105864579A (zh) * 2016-05-31 2016-08-17 苏州市君悦新材料科技股份有限公司 一种新型保温结构
EP3360680A4 (fr) * 2017-02-28 2018-10-10 Cj Cheiljedang Corporation Matériau stratifié pour matériau de revêtement de panneau d'isolation sous vide, et matériau de revêtement de panneau d'isolation sous vide le comprenant
CN110603403A (zh) * 2017-05-09 2019-12-20 大日本印刷株式会社 真空绝热材料用外包材料、真空绝热材料和带真空绝热材料的物品
CN110603403B (zh) * 2017-05-09 2021-02-19 大日本印刷株式会社 真空绝热材料用外包材料、真空绝热材料和带真空绝热材料的物品
CN108081713A (zh) * 2017-12-18 2018-05-29 厦门菲尔牡真空技术有限公司 一种低热桥效应阻隔膜及采用该阻隔膜的真空绝热板

Similar Documents

Publication Publication Date Title
JP2015092106A (ja) 真空断熱材
US9605128B2 (en) Gas barrier material and gas barrier laminate
TW201640713A (zh) 蓄電裝置用外裝材
JP6379555B2 (ja) 真空断熱材
TWI634692B (zh) Lithium-ion battery exterior materials
CN103155207A (zh) 锂离子电池用外包装材料
WO2015046614A1 (fr) Matériau isolant thermique par le vide
EP3299166A1 (fr) Stratifié formant barrière contre les gaz
JP5756408B2 (ja) アンダーコート用塗料組成物
US9132613B2 (en) Gas barrier laminate and method of producing the same
CN110998895A (zh) 蓄电装置用外包装材料
JP2023075950A (ja) 電池用包装材料、その製造方法、電池用包装材料の巻取体、電池
JP2013235719A (ja) リチウムイオン二次電池用外装材
WO2020158873A1 (fr) Matériau de conditionnement externe pour batteries entièrement solides et batterie entièrement solide l'utilisant
JP2015092105A (ja) 真空断熱材
WO2016051584A1 (fr) Matériau d'isolation thermique à vide
JP2017019238A (ja) ガスバリア性積層体
JP2015091651A (ja) 真空断熱材
JP2017087616A (ja) ガスバリア性積層体
WO2021230251A1 (fr) Matériau d'extérieur pour dispositif de stockage d'énergie, son procédé de fabrication et dispositif de stockage d'énergie
WO2015022991A1 (fr) Matériau de barrière aux gaz, et stratifié faisant barrière aux gaz
JP2018049704A (ja) 電池用外装材
WO2023048067A1 (fr) Revêtement pour dispositif de stockage d'énergie et dispositif de stockage d'énergie l'utilisant
CN117941131A (zh) 蓄电装置用封装材料以及使用了该蓄电装置用封装材料的蓄电装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14846842

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14846842

Country of ref document: EP

Kind code of ref document: A1