WO2014014110A1 - パッシベーション層形成用組成物、パッシベーション層付半導体基板、パッシベーション層付半導体基板の製造方法、太陽電池素子、太陽電池素子の製造方法及び太陽電池 - Google Patents
パッシベーション層形成用組成物、パッシベーション層付半導体基板、パッシベーション層付半導体基板の製造方法、太陽電池素子、太陽電池素子の製造方法及び太陽電池 Download PDFInfo
- Publication number
- WO2014014110A1 WO2014014110A1 PCT/JP2013/069700 JP2013069700W WO2014014110A1 WO 2014014110 A1 WO2014014110 A1 WO 2014014110A1 JP 2013069700 W JP2013069700 W JP 2013069700W WO 2014014110 A1 WO2014014110 A1 WO 2014014110A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- passivation
- passivation layer
- composition
- layer
- solar cell
- Prior art date
Abstract
Description
まず、光閉じ込め効果を促して高効率化を図るよう、受光面側にテクスチャー構造を形成したp型シリコン基板を準備し、続いてオキシ塩化リン(POCl3)、窒素及び酸素の混合ガス雰囲気において800℃~900℃で数十分の処理を行って一様にn型拡散層を形成する。この従来の方法では、混合ガスを用いてリンの拡散を行うため、受光面である表面のみならず、側面及び裏面にもn型拡散層が形成される。そのため、側面に形成されたn型拡散層を除去するためのサイドエッチングを行っている。また、裏面に形成されたn型拡散層はp+型拡散層へ変換する必要がある。このため、裏面全体にアルミニウムペーストを付与し、これを熱処理(焼成)することで、n型拡散層をp+型拡散層に変換するのと一括して、アルミニウム電極を形成してオーミックコンタクトを得ている。
このような受光面とは反対の面(以下、「裏面」ともいう)にポイントコンタクト構造を有する太陽電池の場合、アルミニウム電極以外の部分の表面において、少数キャリアの再結合速度を抑制する必要がある。そのためのパッシベーション層として、SiO2膜等が提案されている(例えば、特開2004-6565号公報参照)。このようなSiO2膜を形成することによるパッシベーション効果としては、シリコン基板の裏面の表層部におけるケイ素原子の未結合手を終端させ、再結合の原因となる表面準位密度を低減させる効果がある。
このようなパッシベーション層は、一般的にはALD(Atomic Layer Deposition)法、CVD(Chemical Vapor Deposition)法等の方法で形成される(例えば、Journal of Applied Physics, 104(2008), 113703-1~113703-7参照)。また、半導体基板上に酸化アルミニウム膜を形成する簡便な手法として、ゾルゲル法による手法が提案されている(例えば、Thin Solid Films, 517(2009), 6327-6330、及びChinese Physics Letters, 26(2009), 088102-1~088102-4参照)。
<1> 下記一般式(I)で表される化合物と、樹脂と、を含有するパッシベーション層形成用組成物。
前記半導体基板上の全面又は一部に設けられる、前記<1>~<5>のいずれか1項に記載のパッシベーション層形成用組成物の熱処理物であるパッシベーション層と、
を有するパッシベーション層付半導体基板。
前記組成物層を熱処理してパッシベーション層を形成する工程と、
を有するパッシベーション層付半導体基板の製造方法。
前記半導体基板上の全面又は一部に設けられる、前記<1>~<5>のいずれか1項に記載のパッシベーション層形成用組成物の熱処理物であるパッシベーション層と、
前記p型層及び前記n型層からなる群より選択される1以上の層上に配置される電極と、
を有する太陽電池素子。
前記組成物層を熱処理して、パッシベーション層を形成する工程と、を有する太陽電池素子の製造方法。
前記太陽電池素子の電極上に配置される配線材料と、
を有する太陽電池。
本発明のパッシベーション層形成用組成物は、下記一般式(I)で表される化合物(以下、「式(I)化合物」ともいう)と、樹脂と、を含む。前記パッシベーション層形成用組成物は必要に応じてその他の成分を更に含んでいてもよい。
また、本発明のパッシベーション層形成用組成物を用いる手法は、蒸着装置等を必要としない簡便で生産性の高い方法である。更にマスク処理等の煩雑な工程を要することなく、所望の形状にパッシベーション層を形成できる。またパッシベーション層形成用組成物は、式(I)化合物を含むことで、ゲル化等の不具合の発生が抑制されて経時的な保存安定性に優れる。
粘度変化率(%)=|η30-η0|/η0×100 (式)
パッシベーション層形成用組成物は、前記一般式(I)で表される化合物(式(I)化合物)の少なくとも1種を含む。式(I)化合物は、Nb、Ta、V、Y、及びHfからなる群より選択される少なくとも1種の金属元素を含むアルコキシド化合物である。パッシベーション層形成用組成物が式(I)化合物を含有することで、優れたパッシベーション効果を有するパッシベーション層を形成することができる。この理由について以下のように考えることができる。
R1で表されるアリール基として具体的には、フェニル基を挙げることができる。
R1で表されるアルキル基及びアリール基は、置換基を有していてもよい。アルキル基の置換基としては、ハロゲン原子、アミノ基、ヒドロキシル基、カルボキシル基、スルホン基、ニトロ基等が挙げられる。アリール基の置換基としては、ハロゲン原子、メチル基、エチル基、イソプロピル基、アミノ基、ヒドロキシル基、カルボキシル基、スルホン基、ニトロ基等が挙げられる。
中でもR1は、保存安定性とパッシベーション効果の観点から、炭素数1~8の無置換のアルキル基であることが好ましく、炭素数1~4の無置換のアルキル基であることがより好ましい。
本発明のパッシベーション層形成用組成物は、更に、下記一般式(II)で表される化合物(以下、「特定有機アルミニウム化合物」という)の少なくとも1種を含有してもよい。
また一般式(II)におけるR5は、保存安定性及びパッシベーション効果の観点から、水素原子又は炭素数1~8の無置換のアルキル基であることが好ましく、水素原子又は炭素数1~4の無置換のアルキル基であることがより好ましい。
より好ましくは、一般式(II)で表される化合物は、nが0であり、R2がそれぞれ独立して炭素数1~4の無置換のアルキル基である化合物、並びにnが1~3であり、R2がそれぞれ独立して炭素数1~4の無置換のアルキル基であり、X2及びX3の少なくとも一方が酸素原子であり、前記酸素原子に結合するR3又はR4が炭素数1~4のアルキル基であり、X2又はX3がメチレン基の場合、前記メチレン基に結合するR3又はR4が水素原子であり、R5が水素原子である化合物からなる群より選ばれる少なくとも1種である。
特定有機アルミニウム化合物の含有率を0.5質量%以上とすることで、パッシベーション層形成用組成物の保存安定性が向上する傾向にある。また特定有機アルミニウム化合物の含有率を80質量%以下とすることで、パッシベーション効果が向上する傾向にある。
パッシベーション層形成用組成物は、樹脂の少なくとも1種を含有する。樹脂を含むことで、パッシベーション層形成用組成物が半導体基板上に付与されて形成される組成物層の形状安定性がより向上し、組成物層が形成された領域に、パッシベーション層を所望の形状で選択的に形成することができる。
尚、本明細書における「(メタ)アクリル酸」とは「アクリル酸」及び「メタクリル酸」の少なくとも一方を意味し、「(メタ)アクリレート」とは「アクリレート」及び「メタクリレート」の少なくとも一方を意味する。
(検出器:L-2490型RI[株式会社日立ハイテクノロジーズ])
(カラムオーブン:L-2350[株式会社日立ハイテクノロジーズ])
カラム:Gelpack GL-R440 + Gelpack GL-R450 + Gelpack GL-R400M(計3本)(日立化成株式会社、商品名)
カラムサイズ:10.7mm(内径)×300mm
溶離液:テトラヒドロフラン
試料濃度:10mg/2mL
注入量:200μL
流量:2.05mL/分
測定温度:25℃
パッシベーション層形成用組成物は、更に液状媒体(溶媒又は分散媒)を含んでいてもよい。パッシベーション層形成用組成物が液状媒体を含有することで、粘度の調整がより容易になり、付与性がより向上し、より均一なパッシベーション層を形成することができる傾向にある。液状媒体としては特に制限されず、必要に応じて適宜選択することができる。中でも式(I)化合物及び樹脂、並びに必要に応じて添加される特定有機アルミニウム化合物を溶解して均一な溶液を与えることができる液状媒体が好ましく、有機溶剤の少なくとも1種を含むことがより好ましい。
式(I)化合物は、そのままの状態では加水分解、重合反応等を容易に起こし固化するものもあるが、式(I)化合物を液状媒体中に溶解又は分散させることによって反応が抑制されるため保存安定性が向上しやすい傾向がある。
パッシベーション層形成用組成物は、酸性化合物又は塩基性化合物を含有してもよい。パッシベーション層形成用組成物が酸性化合物又は塩基性化合物を含有する場合、保存安定性の観点から、酸性化合物又は塩基性化合物の含有率が、パッシベーション層形成用組成物中にそれぞれ1質量%以下であることが好ましく、0.1質量%以下であることがより好ましい。
R9CONH-R10-NHCOR9・・・・(2)
R9NHCO-R10-CONHR9・・・・(3)
R9CONH-R10-N(R11)2・・・・(4)
パッシベーション層形成用組成物の粘度は特に制限されず、半導体基板への付与方法等に応じて適宜選択することができる。例えば、パッシベーション層形成用組成物の粘度は、0.01Pa・s~10000Pa・sとすることができる。中でもパターン形成性の観点から、パッシベーション層形成用組成物の粘度は0.1Pa・s~1000Pa・sであることが好ましい。尚、粘度は、回転式せん断粘度計を用いて、25℃、せん断速度1.0s-1で測定される。
パッシベーション層形成用組成物の製造方法には特に制限はない。例えば、一般式(I)で表される特定の化合物と、樹脂と、必要に応じて含まれる特定有機アルミニウム化合物と、液状媒体等とを、通常用いられる混合方法で混合することで製造することができる。
本発明のパッシベーション層付半導体基板は、半導体基板と、前記半導体基板上の全面又は一部に設けられる前記パッシベーション層形成用組成物の熱処理物(焼成物)であるパッシベーション層と、を有する。パッシベーション層付半導体基板は、パッシベーション層形成用組成物の熱処理物層(焼成物層)であるパッシベーション層を有することで優れたパッシベーション効果を示す。
本発明のパッシベーション層付半導体基板の製造方法は、半導体基板上の全面又は一部に、前記パッシベーション層形成用組成物を付与して組成物層を形成する工程と、前記組成物層を熱処理(焼成)してパッシベーション層を形成する工程とを有する。前記製造方法は必要に応じてその他の工程を更に含んでいてもよい。
本発明のパッシベーション層形成用組成物を用いることで、優れたパッシベーション効果を有するパッシベーション層を所望の形状に、簡便な方法で形成することができる。
組成物層の熱処理(焼成)条件は、組成物層に含まれる式(I)化合物及び必要に応じて含まれる特定有機アルミニウム化合物を、その熱処理物(焼成物)である金属酸化物又は複合酸化物に変換可能であれば特に制限されない。パッシベーション層に効果的に固定電荷を与え、より優れたパッシベーション効果を得るために、具体的には、熱処理(焼成)温度は300℃~900℃が好ましく、450℃~800℃がより好ましい。ここでいう熱処理(焼成)温度は、熱処理(焼成)に用いる炉の中の最高温度を意味する。また熱処理(焼成)時間は、熱処理(焼成)温度等に応じて適宜選択できる。例えば、熱処理(焼成)時間は0.1時間~10時間とすることができ、0.12時間~5時間であることが好ましい。ここでいう熱処理(焼成)時間は、最高温度での保持時間を意味する。
尚、形成されたパッシベーション層の平均膜厚は、干渉式膜厚計(例えば、F20膜厚測定システム、フィルメトリクス株式会社)を用いて常法により、3点の厚みを測定し、その算術平均値として算出される。
本発明の太陽電池素子は、p型層及びn型層がpn接合されてなる半導体基板と、前記半導体基板上の全面又は一部に設けられる前記パッシベーション層形成用組成物の熱処理物(焼成物)であるパッシベーション層と、前記p型層及びn型層の少なくとも一方の層上に配置される電極とを有する。太陽電池素子は、必要に応じてその他の構成要素を更に有していてもよい。
太陽電池素子は、本発明のパッシベーション層形成用組成物から形成されたパッシベーション層を有することで、変換効率に優れる。
太陽電池素子の形状及び大きさに制限はない。例えば、一辺が125mm~156mmの正方形であることが好ましい。
本発明の太陽電池素子の製造方法は、p型層及びn型層が接合されてなるpn接合を有し、前記p型層及び前記n型層からなる群より選択される1以上の層上に電極を有する半導体基板の、前記電極を有する面の一方又は両方の面上に、前記パッシベーション層形成用組成物を付与して組成物層を形成する工程と、前記組成物層を熱処理(焼成)して、パッシベーション層を形成する工程と、を有する。太陽電池素子の製造方法は、必要に応じてその他の工程を更に有していてもよい。
パッシベーション層形成用組成物を用いてパッシベーション層を形成する方法の詳細は、既述のパッシベーション層付半導体基板の製造方法と同様であり、好ましい態様も同様である。
図1は、本実施形態にかかるパッシベーション層を有する太陽電池素子の製造方法の一例を模式的に示す工程図を断面図として示したものである。但し、この工程図は、本発明をなんら制限するものではない。
太陽電池は、前記太陽電池素子と、太陽電池素子の電極上に設けられる配線材料と、を有する。配線材料が配置される電極は、出力取出し電極等である。太陽電池は更に必要に応じて、配線材料を介して複数の太陽電池素子が連結され、更に封止材で封止されて構成される。前記配線材料及び封止材としては特に制限されず、当業界で通常用いられているものから適宜選択することができる。
(パッシベーション層形成用組成物の調製)
ペンタエトキシニオブ(北興化学工業株式会社、構造式:Nb(OC2H5)5、分子量:318.2)を1.2g、テルピネオール(日本テルペン化学株式会社、TPOと略記することがある)を18.5g、及びエチルセルロース(日進化成株式会社、商品名:ETHOCEL200cps、ECと略記することがある)を0.3g混合して、パッシベーション層形成用組成物1を調製した。
上記で調製したパッシベーション層形成用組成物1のせん断粘度を、調製直後(12時間以内)に、回転式せん断粘度計(AntonPaar社、MCR301)に、コーンプレート(直径50mm、コーン角1°)を装着し、温度25℃で、せん断速度1.0s-1及び10s-1の条件でそれぞれ測定した。
せん断速度が1.0s-1の条件でのせん断粘度(η1)は35.4Pa・s、せん断速度が10s-1の条件でのせん断粘度(η2)は26.8Pa・sとなった。せん断速度が1.0s-1と10s-1の場合でのチキソ比(η1/η2)は1.32となった。
上記で調製したパッシベーション層形成用組成物1のせん断粘度を、調製直後(12時間以内)及び25℃で30日間保存した後にそれぞれ測定した。せん断粘度の測定は、AntonPaar社、MCR301に、コーンプレート(直径50nm、コーン角1°)を装着し、温度25℃でせん断速度1.0s-1で行った。25℃におけるせん断粘度は、調製直後は35.4Pa・s、25℃で30日間保存した後は36.9Pa・sであった。
保存安定性の評価では、30日間保存した後のせん断粘度の変化率が10%未満のものをA、10%以上30%未満のものをB、30%以上のものをCとしている。評価がA及びBであれば、パッシベーション層形成用組成物の保存安定性としては良好である。表2では、調製直後のせん断粘度の数値と、保存安定性の評価結果を示す。
パッシベーション層形成用組成物の印刷性の評価を行う際は、半導体基板として、表面がミラー形状の単結晶p型シリコン基板(50mm角、厚さ625μm、以下、基板Aと呼ぶ)と、表面にテクスチャー構造が形成された単結晶p型シリコン基板(50mm角、厚さ180μm、以下、基板Bと呼ぶ)の2種類を使用した。
ここで、印刷中に目視によって印刷ムラが生じなかったものが10枚中9枚以上の場合をA、8枚以下かつ6枚以上の場合をB、5枚以下の場合をCとしている。評価がA及びBであれば、パッシベーション層形成用組成物の印刷ムラとしては良好である。
尚、印刷ムラとは、スクリーン版がシリコン基板から離れる際に、一部版離れが悪い部分が生じたためにできる、前記パッシベーション層形成用組成物の厚さが場所によりばらつく現象を指す。
その後、パッシベーション層形成用組成物1を付与した基板A及び基板Bを150℃で3分間加熱し、液状媒体を蒸散させることで乾燥処理した。次いで、基板A及び基板Bを700℃の温度で10分間熱処理(焼成)した後、室温(25℃)で放冷した。
ここで、印刷直後のドット径(La)(368μm)に対し、熱処理(焼成)後のドット径(La)の減少率が10%未満のものをA、10%以上30%未満のものをB、30%以上のものをCとしている。評価がA及びBであれば、パッシベーション層形成用組成物の印刷滲みの抑制としては良好である。
尚、印刷滲みとは、基板上に付与したパッシベーション層形成用組成物が広がる現象を言う。
上記印刷ムラの評価で作製したパッシベーション層形成用組成物1を全面に付与した10枚の基板Aのうち1枚を、150℃で3分間加熱し、液状媒体を蒸散させることで乾燥処理した。次いで基板を700℃の温度で10分間熱処理(焼成)した後、室温(25℃)で放冷し、評価用基板とした。熱処理(焼成)は、拡散炉(ACCURON CQ-1200、株式会社日立国際電気)を用いて、大気中雰囲気下、最高温度700℃、保持時間10分間の条件で行った。
上記で得られた評価用基板の実効ライフタイムを、ライフタイム測定装置(日本セミラボ株式会社、WT-2000PVN)を用いて、室温(25℃)で反射マイクロ波光電導減衰法により測定した。得られた評価用基板において、パッシベーション層形成用組成物を付与した領域の実効ライフタイムは、198μsであった。
上記で得られた評価用基板上のパッシベーション層の厚みを、干渉式膜厚計(フィルメトリクス株式会社、F20膜厚測定システム)を用いて測定したところ、膜厚は74nmであった。
上記で得られた評価用基板について、パッシベーション層上にメタルマスクを介して、直径1mmのアルミニウム電極を複数個蒸着し、MIS(Metal-Insulator-Semiconductor;金属-絶縁体-半導体)構造のキャパシタを作製した。
まず、単結晶p型半導体基板(125mm角、厚さ200μm)を用意し、アルカリエッチングにより、受光面及び裏面にテクスチャー構造を形成した。次いでオキシ塩化リン(POCl3)、窒素及び酸素の混合ガス雰囲気において、900℃の温度で20分間処理し、受光面、裏面及び側面にn+型拡散層を形成した。その後、サイドエッチングを行い、側面のPSG層及びn+型拡散層を除去し、そしてフッ酸を含むエッチング溶液を用いて受光面及び裏面のPSG層を除去した。更に裏面については別途エッチング処理を行い、裏面のn+型拡散層を除去した。その後、受光面のn+型拡散層上に窒化ケイ素からなる反射防止膜をPECVDにより約90nmの厚さで形成した。
各電極ペーストを印刷した後、150℃の温度で5分間加熱し、液状媒体を蒸散させることで乾燥処理を行った。
上記で得られた太陽電池素子1の受光面出力取出し電極及び裏面出力取出し電極の上に、配線部材(太陽電池用はんだめっき平角線、製品名:SSA-TPS 0.2×1.5(20)、厚さ0.2mm×幅1.5mmの銅線にSn-Ag-Cu系鉛フリーはんだを片面あたり最大20μmの厚さでめっきした仕様、日立金属株式会社[(旧)日立電線株式会社])を配置し、タブ線接続装置(NTS-150-M、Tabbing & Stringing Machine、株式会社エヌピーシー)を用い、最高温度250℃、保持時間10秒の条件ではんだを溶融させることで、上記配線部材と受光面出力取出し電極及び裏面出力取出し電極とを接続した。
実施例1において、パッシベーション層形成用組成物にエチルセルロース(日進化成株式会社、商品名:ETHOCEL200cps)及びアルミニウムエチルアセトアセタトジイソプロピレート(ALCH)を加えた。具体的には、各成分の含有量を、ペンタエトキシニオブ(北興化学工業株式会社、構造式:Nb(OC2H5)5、分子量:318.2)を1.6g、ALCHを1.0g、テルピネオールを17.1g、及びエチルセルロースを0.3gと変更したこと以外は、実施例1と同様にして、パッシベーション層形成用組成物2を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物2のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層2の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子2及び太陽電池2を作製し、発電性能を評価した。
各評価には、実施例2において調製したパッシベーション層形成用組成物を用いた。印刷性(印刷ムラ及び印刷滲み)の評価基板の作製、実効ライフタイム及びパッシベーション層の膜厚の測定用基板の作製、太陽電池素子の作製におけるパッシベーション層形成用組成物2の熱処理条件(焼成)を700℃、10分間から、600℃、15分間と変更したこと以外は、実施例1と同様にして、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層3の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定し、太陽電池素子3及び太陽電池3を作製し、発電性能を評価した。
各評価には、実施例2において調製したパッシベーション層形成用組成物を用いた。印刷性(印刷ムラ及び印刷滲み)の評価基板の作製、実効ライフタイム及びパッシベーション層の膜厚の測定用基板の作製、太陽電池素子の作製におけるパッシベーション層形成用組成物2の熱処理(焼成)条件を700℃、10分間から、800℃、8分間と変更したこと以外は、実施例1と同様にして、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層4実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定し、太陽電池素子4及び太陽電池4を作製し、発電性能を評価した。
各成分の含有量を、バナジウム(V)トリエトキシドオキシド(株式会社高純度化学研究所、構造式:VO(OC2H5)3、分子量:546.4)を1.2g、アルミニウムエチルアセトアセタトジイソプロピレート(川研ファインケミカル株式会社、商品名:ALCH)を0.8g、テルピネオールを17.7g、及びエチルセルロース(ETHOCEL200cps)を0.3gと変更したこと以外は、実施例1と同様にして、パッシベーション層形成用組成物3を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物3のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層5の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子5及び太陽電池5を作製し、発電性能を評価した。
各成分の含有量を、テトラ-t-ブトキシハフニウム(株式会社高純度化学研究所、構造式:Hf(O-t-C4H9)4、分子量:470.9)を1.2g、アルミニウムトリスエチルアセトアセテート(川研ファインケミカル株式会社、商品名:ALCH-TR)を1.2g、テルピネオールを17.3g、及びエチルセルロース(ETHOCEL200cps)を0.3gと変更したこと以外は、実施例1と同様にして、パッシベーション層形成用組成物4を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物4のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層6の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子6及び太陽電池6を作製し、発電性能を評価した。
パッシベーション層形成用組成物の調製において、ペンタエトキシニオブ(北興化学工業株式会社、構造式:Nb(OC2H5)5、分子量:318.2)、ペンタ-n-ブトキシタンタル(株式会社高純度化学研究所、構造式:Ta(O-n-C4H9)5、分子量:546.4)、テルピネオール、及びエチルセルロース(ETHOCEL200cps)を用いた。具体的には、各成分の含有量を、ペンタエトキシニオブを1.4g、ペンタ-n-ブトキシタンタルを1.0g、テルピネオールを17.3g、及びエチルセルロースを0.3gと変更したこと以外は、実施例1と同様にして、パッシベーション層形成用組成物5を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物5のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層7の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子7及び太陽電池7を作製し、発電性能を評価した。
パッシベーション層形成用組成物の調製において、ペンタ-n-ブトキシニオブ(株式会社高純度化学研究所、構造式:Nb(O-n-C4H9)5、分子量:458.5)、バナジウム(V)トリエトキシドオキシド(株式会社高純度化学研究所、構造式:VO(OC2H5)3、分子量:546.4)、アルミニウムエチルアセトアセタトジイソプロピレート(川研ファインケミカル株式会社、商品名:ALCH)、テルピネオール、及びエチルセルロース(ETHOCEL200cps)を用いた。具体的には、各成分の含有量を、ペンタ-n-ブトキシニオブを1.6g、バナジウム(V)トリエトキシドオキシドを0.6g、ALCHを0.6g、テルピネオールを17.0g、及びエチルセルロースを0.2gと変更したこと以外は、実施例1と同様にして、パッシベーション層形成用組成物6を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物6のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層8の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子8及び太陽電池8を作製し、発電性能を評価した。
半導体基板へのパッシベーション層形成において、パッシベーション層形成用組成物を用いずに、ALD(Atomic Layer Deposition)法を用いて酸化アルミニウム(Al2O3)からなるパッシベーション層C1を形成した。
具体的には、原子層堆積装置を用いて、Al2O3層が20nmの厚さになるよう、成膜条件を調整した。尚、成膜後の膜厚は干渉式膜厚計(F20膜厚測定システム、フィルメトリックス株式会社)を用いて測定した。
実施例1におけるパッシベーション層形成用組成物の調製において、式(I)化合物(MはNb、Ta、V、Y又はHfから選ばれる金属元素を含む)を用いずに、表1に示すように、トリエトキシビスマス(株式会社高純度化学研究所、構造式:Bi(OC2H5)3、分子量344.2、テルピネオール、及びエチルセルロース(ETHOCEL200cps)からなるパッシベーション層形成用組成物C2を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物C2のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、及びパッシベーション層C2の実効ライフタイムの評価を行い、厚さ及び固定電荷密度を測定した。更に実施例1と同様にして、太陽電池素子C2及び太陽電池C2を作製し、発電性能を評価した。
実施例1におけるパッシベーション層形成用組成物の調製において、式(I)化合物(MはNb、Ta、V、Y又はHfから選ばれる金属元素を含む)を用いずに、表1に示すように、テトラ-i-プロポキシチタン(株式会社高純度化学研究所、構造式:Ti(O-i-C3H7)4、分子量284.2、テルピネオール、及びエチルセルロース(ETHOCEL200cps)からなるパッシベーション層形成用組成物C3を調製した。
その後は、実施例1と同様にして、パッシベーション層形成用組成物C3のチキソ性の評価、保存安定性の評価、印刷性(印刷ムラ及び印刷滲み)の評価、パッシベーション層C3の実効ライフタイムの評価及び厚さを測定した。更に実施例1と同様にして、太陽電池素子C3及び太陽電池C3を作製し、発電性能を評価した。
太陽電池素子の作製において、裏面にパッシベーション層を形成せず、太陽電池素子C4及び太陽電池C4を作製し、発電性能を評価した。
続いて、トンネル炉(1列搬送W/Bトンネル炉、株式会社ノリタケカンパニーリミテド)を用いて大気中雰囲気下、最高温度800℃、保持時間10秒の条件で熱処理(焼成)を行って、所望の電極が形成された太陽電池素子C4を作製した。
実施例1~8で作製したパッシベーション層用組成は、いずれも保存安定性及び印刷性が良好であることが分かった。
以下は、参考実施形態1に係るパッシベーション膜、塗布型材料、太陽電池素子及びパッシベーション膜付シリコン基板である。
前記シリコン基板の受光面側に形成されたn型の不純物拡散層と、
前記シリコン基板の受光面側の前記n型の不純物拡散層の表面に形成された第1電極と、
前記シリコン基板の裏面側の表面に形成され、複数の開口部を有する酸化アルミニウムと酸化ニオブを含むパッシベーション膜と、
前記複数の開口部を通して、前記シリコン基板の裏面側の表面と電気的な接続を形成している第2電極と、
を備える太陽電池素子。
前記シリコン基板の受光面側に形成されたn型の不純物拡散層と、
前記シリコン基板の受光面側の前記n型の不純物拡散層の表面に形成された第1電極と、
前記シリコン基板の裏面側の一部又は全部に形成され、前記シリコン基板より高濃度に不純物が添加されたp型の不純物拡散層と、
前記シリコン基板の裏面側の表面に形成され、複数の開口部を有する酸化アルミニウムと酸化ニオブを含むパッシベーション膜と、
前記複数の開口部を通して、前記シリコン基板の裏面側の前記p型の不純物拡散層の表面と電気的な接続を形成している第2電極と、
を備える太陽電池素子。
前記シリコン基板の受光面側に形成されたp型の不純物拡散層と、
前記シリコン基板の裏面側に形成された第2電極と、
前記シリコン基板の受光面側の表面に形成され、複数の開口部を有する酸化アルミニウムと酸化ニオブを含むパッシベーション膜と、
前記シリコン基板の受光面側の前記p型の不純物拡散層の表面に形成され、前記複数の開口部を通して前記シリコン基板の受光面側の表面と電気的な接続を形成している第1電極と、
を備える太陽電池素子。
前記シリコン基板上の全面又は一部に設けられる<1>~<5>のいずれか1項に記載のパッシベーション膜と、
を有するパッシベーション膜付シリコン基板。
本実施の形態の太陽電池素子の構造について図12~図15を参照しながら説明する。図12~図15は、本実施の形態の裏面にパッシベーション膜を用いた太陽電池素子の第1~第4構成例を示す断面図である。
次に、上記構成をもつ本実施の形態の太陽電池素子(図12~図15)の製造方法の一例について説明する。ただし、本実施の形態は、以下に述べる方法で作製した太陽電池素子に限るものではない。
熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所SYM-AL04、濃度2.3質量%]を3.0gと、熱処理(焼成)により酸化ニオブ(Nb2O5)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所Nb-05、濃度5質量%]を3.0gとを混合して、塗布型材料であるパッシベーション材料(a-1)を調製した。
参考実施例1-1と同様に、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所、SYM-AL04、濃度2.3質量%]と、熱処理(焼成)により酸化ニオブ(Nb2O5)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所、Nb-05、濃度5質量%]とを、比率を変えて混合して、表3に示すパッシベーション材料(a-2)~(a-7)を調製した。
市販のニオブ(V)エトキシド(構造式:Nb(OC2H5)5、分子量:318.21)を3.18g(0.010mol)と、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を1.02g(0.005mol)とをシクロヘキサン80gに溶解して、濃度5質量%のパッシベーション材料(c-1)を調製した。
市販のニオブ(V)エトキシド(構造式:Nb(OC2H5)5、分子量:318.21)を2.35g(0.0075mol)と、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を1.02g(0.005mol)と、ノボラック樹脂10gとを、ジエチレングリコールモノブチルエーテルアセタート10gとシクロヘキサン10gに溶解して、パッシベーション材料(c-2)を調製した。
参考実施例1-1と同様に、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所SYM-AL04、濃度2.3質量%]と、熱処理(焼成)により酸化ニオブ(Nb2O5)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所Nb-05、濃度5質量%]とを、比率を変えて混合して、表4に示すパッシベーション材料(b-1)~(b-7)を調製した。
一方、酸化アルミニウムが100質量%となるパッシベーション材料(b-7)では、負の固定電荷密度を得ることができなかった。
パッシベーション材料(d-1)として、熱処理(焼成)により酸化チタン(TiO2)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所Ti-03-P、濃度3質量%]、パッシベーション材料(d-2)として、熱処理(焼成)によりチタン酸バリウム(BaTiO3)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所BT-06、濃度6質量%]、パッシベーション材料(d-3)として、熱処理(焼成)により酸化ハフニウム(HfO2)が得られる市販の有機金属分解塗布型材料[株式会社高純度化学研究所Hf-05、濃度5質量%]を準備した。
シリコン基板101として、ボロンをドーパントした単結晶シリコン基板を用いて、図14に示す構造の太陽電池素子を作製した。シリコン基板101の表面をテクスチャー処理した後、塗布型のリン拡散材を受光面側に付与し、熱処理により拡散層102(リン拡散層)を形成した。その後、塗布型のリン拡散材を希フッ酸で除去した。
また、パッシベーション膜107として、参考実施例1-3で調製したパッシベーション材料(c-1)を用いたサンプルも別途作製した。
以下は、参考実施形態2に係るパッシベーション膜、塗布型材料、太陽電池素子及びパッシベーション膜付シリコン基板である。
前記シリコン基板の受光面側である第1面側に形成されたn型の不純物拡散層と、
前記不純物拡散層上に形成された第1電極と、
前記シリコン基板の受光面側とは逆の第2面側に形成され、開口部を有するパッシベーション膜と、
前記シリコン基板の第2面側に形成され、前記シリコン基板の第2面側と前記パッシベーション膜の開口部を通して電気的に接続されている第2電極と、を備え、
前記パッシベーション膜は、酸化アルミニウムと、酸化バナジウム及び酸化タンタルからなる群より選択される少なくとも1種のバナジウム族元素の酸化物と、を含む太陽電池素子。
前記第2電極は、前記p型の不純物拡散層と前記パッシベーション膜の開口部を通して電気的に接続されている、<7>に記載の太陽電池素子。
前記シリコン基板の受光面側である第1面側に形成されたp型の不純物拡散層と、
前記不純物拡散層上に形成された第1電極と、
前記シリコン基板の受光面側とは逆の第2面側に形成され、開口部を有するパッシベーション膜と、
前記シリコン基板の第2面側に形成され、前記シリコン基板の第2面側と前記パッシベーション膜の開口部を通して電気的に接続されている第2電極と、を備え、
前記パッシベーション膜は、酸化アルミニウムと、酸化バナジウム及び酸化タンタルからなる群より選択される少なくとも1種のバナジウム族元素の酸化物と、を含む太陽電池素子。
前記第2電極は、前記n型の不純物拡散層と前記パッシベーション膜の開口部を通して電気的に接続されている、<9>に記載の太陽電池素子。
前記シリコン基板上の全面又は一部に設けられる<1>~<5>のいずれか1項に記載の太陽電池素子用パッシベーション膜と、
を有するパッシベーション膜付シリコン基板。
[参考実施例2-1]
熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、SYM-AL04、濃度2.3質量%]を3.0gと、熱処理(焼成)により酸化バナジウム(V2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、V-02、濃度2質量%]を6.0gとを混合して、塗布型材料であるパッシベーション材料(a2-1)を調製した。
参考実施例2-1と同様に、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、SYM-AL04、濃度2.3質量%]と、熱処理により酸化バナジウム(V2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、V-02、濃度2質量%]とを、比率を変えて混合して、表7に示すパッシベーション材料(a2-2)~(a2-7)を調製した。
熱処理(焼成)により酸化バナジウム(V2O5)が得られる化合物として、市販のバナジウム(V)オキシトリエトキシド(構造式:VO(OC2H5)3、分子量:202.13)を1.02g(0.010mol)と、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる化合物として、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を2.04g(0.010mol)とをシクロヘキサン60gに溶解して、濃度5質量%のパッシベーション材料(b2-1)を調製した。
市販のバナジウム(V)オキシトリエトキシド(構造式:VO(OC2H5)3、分子量:202.13)を1.52g(0.0075mol)と、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を1.02g(0.005mol)と、ノボラック樹脂10gとを、ジエチレングリコールモノブチルエーテルアセタート10gとシクロヘキサン10gに溶解して、パッシベーション材料(b2-2)を調製した。
[参考実施例2-5]
熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、SYM-AL04、濃度2.3質量%]と、熱処理により酸化タンタル(Ta2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、Ta-10-P、濃度10質量%]とを比率を変えて混合して、表8に示すパッシベーション材料(c2-1)~(c2-6)を調製した。
熱処理(焼成)により酸化タンタル(Ta2O5)が得られる化合物として、市販のタンタル(V)メトキシド(構造式:Ta(OCH3)5、分子量:336.12)を1.18g(0.0025mol)と、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる化合物として、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を2.04g(0.010mol)とをシクロヘキサン60gに溶解して、濃度5質量%のパッシベーション材料(d2-1)を調製した。
熱処理(焼成)により酸化タンタル(Ta2O5)が得られる化合物として、市販のタンタル(V)メトキシド(構造式:Ta(OCH3)5、分子量:336.12)1.18g(0.005mol)と、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる化合物として、市販のアルミニウムトリイソプロポキシド(構造式:Al(OCH(CH3)2)3、分子量:204.25)を1.02g(0.005mol)と、ノボラック樹脂10gとを、ジエチレングリコールモノブチルエーテルアセタート10gとシクロヘキサン10gの混合物に溶解して、パッシベーション材料(d2-2)を調製した。
[参考実施例2-8]
熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、SYM-AL04、濃度2.3質量%]、熱処理(焼成)により酸化バナジウム(V2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、V-02、濃度2質量%]、及び熱処理(焼成)により酸化タンタル(Ta2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、Ta-10-P、濃度10質量%]を混合して、塗布型材料であるパッシベーション材料(e2-1)を調製した(表9参照)。
参考実施例2-1と同様に、熱処理(焼成)により酸化アルミニウム(Al2O3)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、SYM-AL04、濃度2.3質量%]と、熱処理(焼成)により酸化バナジウム(V2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、V-02、濃度2質量%]、又は熱処理(焼成)により酸化タンタル(Ta2O5)が得られる市販の有機金属薄膜塗布型材料[(株)高純度化学研究所、Ta-10-P、濃度10質量%]を混合して、塗布型材料であるパッシベーション材料(f2-1)~(f2-8)を調製した(表10参照)。
シリコン基板101として、ボロンをドーパントとした単結晶シリコン基板を用いて、図14に示す構造の太陽電池素子を作製した。シリコン基板101の表面をテクスチャー処理した後、塗布型のリン拡散材を受光面側のみに塗布し、熱処理により拡散層102(リン拡散層)を形成した。その後、塗布型のリン拡散材を希フッ酸で除去した。
Claims (10)
- 下記一般式(I)で表される化合物と、樹脂と、を含有するパッシベーション層形成用組成物。
M(OR1)m (I)
[式中、MはNb、Ta、V、Y及びHfからなる群より選択される少なくとも1種の金属元素を含む。R1はそれぞれ独立して炭素数1~8のアルキル基又は炭素数6~14のアリール基を表す。mは1~5の整数を表す。] - 前記樹脂の含有率が0.1質量%~50質量%である請求項1又は請求項2に記載のパッシベーション層形成用組成物。
- 前記一般式(II)において、R2がそれぞれ独立して炭素数1~4のアルキル基である請求項2又は請求項3に記載のパッシベーション層形成用組成物。
- 前記一般式(II)において、nが1~3の整数であり、R5がそれぞれ独立して水素原子又は炭素数1~4のアルキル基である請求項2~請求項4のいずれか1項に記載のパッシベーション層形成用組成物。
- 半導体基板と、
前記半導体基板上の全面又は一部に設けられる、請求項1~請求項5のいずれか1項に記載のパッシベーション層形成用組成物の熱処理物であるパッシベーション層と、
を有するパッシベーション層付半導体基板。 - 半導体基板上の全面又は一部に、請求項1~請求項5のいずれか1項に記載のパッシベーション層形成用組成物を付与して組成物層を形成する工程と、
前記組成物層を熱処理してパッシベーション層を形成する工程と、
を有するパッシベーション層付半導体基板の製造方法。 - p型層及びn型層がpn接合されてなる半導体基板と、
前記半導体基板上の全面又は一部に設けられる、請求項1~請求項5のいずれか1項に記載のパッシベーション層形成用組成物の熱処理物であるパッシベーション層と、
前記p型層及び前記n型層からなる群より選択される1以上の層上に配置される電極と、
を有する太陽電池素子。 - p型層及びn型層が接合されてなるpn接合を有し、前記p型層及び前記n型層からなる群より選択される1以上の層上に電極を有する半導体基板の、前記電極を有する面の一方又は両方の面上に、請求項1~請求項5のいずれか1項に記載のパッシベーション層形成用組成物を付与して組成物層を形成する工程と、
前記組成物層を熱処理して、パッシベーション層を形成する工程と、を有する太陽電池素子の製造方法。 - 請求項8に記載の太陽電池素子と、
前記太陽電池素子の電極上に配置される配線材料と、
を有する太陽電池。