WO2013181208A2 - Cover glass article - Google Patents

Cover glass article Download PDF

Info

Publication number
WO2013181208A2
WO2013181208A2 PCT/US2013/043025 US2013043025W WO2013181208A2 WO 2013181208 A2 WO2013181208 A2 WO 2013181208A2 US 2013043025 W US2013043025 W US 2013043025W WO 2013181208 A2 WO2013181208 A2 WO 2013181208A2
Authority
WO
WIPO (PCT)
Prior art keywords
cover glass
glass article
μιη
glass
bend
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/US2013/043025
Other languages
English (en)
French (fr)
Other versions
WO2013181208A3 (en
Inventor
Karl David EHEMANN
Keith Raymond GAYLO
William Brashear MATTINGLY III
Connor Thomas O'MALLEY
Ljerka Ukrainczyk
Kevin Lee Wasson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Corning Inc
Original Assignee
Corning Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Inc filed Critical Corning Inc
Priority to JP2015515136A priority Critical patent/JP2015527277A/ja
Priority to KR1020147037043A priority patent/KR20150016617A/ko
Priority to EP20156325.1A priority patent/EP3693346B1/en
Priority to CN201380028524.5A priority patent/CN104520249B/zh
Priority to EP21214725.0A priority patent/EP4015476B1/en
Priority to KR1020207012030A priority patent/KR20200049876A/ko
Priority to EP13729841.0A priority patent/EP2855388B1/en
Publication of WO2013181208A2 publication Critical patent/WO2013181208A2/en
Publication of WO2013181208A3 publication Critical patent/WO2013181208A3/en
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Links

Classifications

    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K5/00—Casings, cabinets or drawers for electric apparatus
    • H05K5/02—Details
    • H05K5/03—Covers
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B23/00—Re-forming shaped glass
    • C03B23/02—Re-forming glass sheets
    • C03B23/023—Re-forming glass sheets by bending
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
    • C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
    • C03C21/002—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to perform ion-exchange between alkali ions
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
    • C03C3/087—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal containing calcium oxide, e.g. common sheet or container glass
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
    • C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
    • C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
    • C03C3/093—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium containing zinc or zirconium
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/095—Glass compositions containing silica with 40% to 90% silica, by weight containing rare earths
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C4/00—Compositions for glass with special properties
    • C03C4/18—Compositions for glass with special properties for ion-sensitive glass
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K5/00—Casings, cabinets or drawers for electric apparatus
    • H05K5/0017—Casings, cabinets or drawers for electric apparatus with operator interface units
    • H—ELECTRICITY
    • H05—ELECTRIC TECHNIQUES NOT OTHERWISE PROVIDED FOR
    • H05K—PRINTED CIRCUITS; CASINGS OR CONSTRUCTIONAL DETAILS OF ELECTRIC APPARATUS; MANUFACTURE OF ASSEMBLAGES OF ELECTRICAL COMPONENTS
    • H05K5/00—Casings, cabinets or drawers for electric apparatus
    • H05K5/0086—Casings, cabinets or drawers for electric apparatus portable, e.g. battery operated apparatus
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C2204/00—Glasses, glazes or enamels with special properties
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/13—Hollow or container type article [e.g., tube, vase, etc.]
    • Y10T428/131—Glass, ceramic, or sintered, fused, fired, or calcined metal oxide or metal carbide containing [e.g., porcelain, brick, cement, etc.]

Definitions

  • the present invention relates to covers for mobile or handheld electronic devices.
  • Covers for handheld devices are required to be aesthetically pleasing while being functional.
  • Glass is one of the materials that can be used to make such covers.
  • the present invention relates to a shaped glass article with attributes that make it useful as a cover glass.
  • a cover glass article includes a glass body having a three- dimensional shape, an inside surface, and an outside surface.
  • Each of the inside and outside surfaces has a surface roughness (R a ) less than 1 nm and is free of indentations having diameters larger than 150 ⁇ .
  • each of the inside and outside surfaces has a surface roughness (R a ) less than 0.7 nm.
  • at least one of the inside and outside surfaces has a surface roughness (R a ) less than 0.3 nm.
  • the glass body has a wall thickness in a range from 0.3 mm to 3 mm. In some embodiments, the variation in the wall thickness is less than ⁇ 100 ⁇ .
  • the variation in the wall thickness is within ⁇ 10% or less.
  • the glass body further comprises less than ten non- indentation defects observable by the unaided human eye at 1000 lux in a 25 mm x 25 mm area on any of the surface.
  • the glass body has a flat section. In some embodiments, the flatness of the flat section is better than ⁇ 150 ⁇ over a 10 mm x 10 mm area and in other embodiments the flatness of the flat section is better than ⁇ 50 ⁇ over a 25 mm x 25 mm area. In some embodiments, the glass body has at least one bend section. In some embodiments, the at least one bend section has a bend radius from about 1 mm to about 20 mm. In some embodiments, the at least one bend section is a spline. The bend angle is the angle in degrees the glass is turned around a bend radius.
  • the at least one bend section has a bend angle ranging from greater than 0 to 90°. In some embodiments, the at least one bend section has a bend angle greater than 90°.
  • Embodiments may also have high optical transmission.
  • the glass body has an optical transmission greater than 85% in a wavelength range of 400 nm to 800 nm. In some embodiments, the glass body has an optical transmission greater than 90% in a wavelength range of 400 nm to 800 nm.
  • Embodiments may have improved strength or damage resistance.
  • the glass body has a compressive stress greater than 300 MPa.
  • the glass body has a hardness of greater than 7 on the Mohs scale.
  • the glass body is tempered and may be chemically or thermally tempered.
  • the glass body comprises an ion exchanged glass.
  • the ion-exchanged class has a depth of layer of greater than 15 ⁇ or greater than 25 ⁇ .
  • a cover glass article includes a glass body having a three-dimensional shape, an inside surface, and an outside surface, and further comprising at least one of: a surface roughness (R a ) less than 1 nm and is free of indentations having diameters larger than 150 ⁇ ; a surface roughness (R a ) less than 0.7 nm; a surface roughness (R a ) less than 0.3 nm; a wall thickness in a range from 0.3 mm to 3 mm with a variation in the wall thickness is less than ⁇ 100 ⁇ or a variation in the wall thickness is within ⁇ 10% or less; less than ten non-indentation defects observable by the unaided human eye at 1000 lux in a 25 mm x 25 mm area on any of the surface; a flat section wherein the flatness of the flat section is better than ⁇ 150 ⁇ over a 10 mm x 10 mm area or the flatness of the flat section is better than ⁇ 50 ⁇
  • Embodiments may be used in electronic devices.
  • the glass body is adapted for covering an electronic device having a flat display.
  • the electronic device is a telephone, monitor, television, handheld device, or tablet.
  • Fig. 1 shows one example of a cover glass shape.
  • Fig. 2 shows another example of a cover glass shape.
  • Fig. 5 is a transmission profile of a 3D cover glass.
  • each of the combinations A-E, A-F, B-D, B-E, B-F, C-D, C-E, and C-F are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D.
  • any subset or combination of these is also specifically contemplated and disclosed.
  • the sub-group of A-E, B-F, and C-E are specifically contemplated and should be considered disclosed from disclosure of A, B, and C; D, E, and F; and the example combination A-D.
  • This concept applies to all aspects of this disclosure including, but not limited to any components of the compositions and steps in methods of making and using the disclosed compositions.
  • each of these additional steps can be performed with any specific embodiment or combination of embodiments of the disclosed methods, and that each such combination is specifically contemplated and should be considered disclosed.
  • compositions and methods of the disclosure include those having any value or any combination of the values, specific values, more specific values, and preferred values described herein.
  • a three-dimensional (3D) cover glass can be used to cover an electronic device having a display.
  • the display area is flat or planar.
  • the 3D cover glass will protect the display while allowing viewing of and interaction with the display.
  • the 3D cover glass has a front cover glass section for covering the front side of the electronic device, where the display is located, and one or more side cover glass sections for wrapping around the peripheral side of the electronic device.
  • the front cover glass section is contiguous with the side cover glass section(s).
  • Another aspect comprises a three-dimensional (3D) cover glass for use as a cover for at least part of the back and side portions of an electronic device, referred to as a backplate.
  • the backplate is flat or planar.
  • the backplate can protect the electronic components in the device and/or provide a scratch or damage resistant surface.
  • the electronic device may also have a display on part or all of the back of the device, and in such cases, the backplate may have a planar surface over that region and may act as a second cover for the second display area.
  • the back cover glass section is contiguous with the side cover glass section (s).
  • the 3D cover glass has at least one flat or planar section. In some embodiments, this flat or planar section covers at least part of the display area of the electronic device. In some embodiments, the flat 3D cover glass has a flatness of better than ⁇ 10 ⁇ , ⁇ 25 ⁇ , ⁇ 50 ⁇ , ⁇ 75 ⁇ , ⁇ 100 ⁇ , ⁇ 125 ⁇ , ⁇ 150 ⁇ , ⁇ 100 ⁇ , ⁇ 200 ⁇ , ⁇ 250 ⁇ , ⁇ 300 ⁇ , or ⁇ 400 ⁇ over a 25 mm ⁇ 25 mm area, as measured by a FLATMASTER® tool.
  • the flat 3D cover glass has a flatness of better than ⁇ 10 ⁇ , ⁇ 25 ⁇ , ⁇ 50 ⁇ , ⁇ 75 ⁇ , ⁇ 100 ⁇ , ⁇ 125 ⁇ , ⁇ 150 ⁇ , ⁇ 100 ⁇ , ⁇ 200 ⁇ , ⁇ 250 ⁇ , ⁇ 300 ⁇ , or ⁇ 400 ⁇ over a 200 mm ⁇ 200 mm area, as measured by a FLATMASTER® tool.
  • the flat front cover glass section has a flatness of better than ⁇ 150 ⁇ over a 25 mm x 25 mm area, as measured by a FLATMASTER® tool.
  • the flat front cover glass section has a flatness of better than ⁇ 150 ⁇ over a 200 mm x 200 mm area, as measured by a FLATMASTER® tool. In one embodiment, the flat front cover glass section has a flatness of better than ⁇ 100 ⁇ over a 200 mm x 200 mm area, as measured by a FLATMASTER® tool. In one embodiment, the flat front cover glass section has a flatness of better than ⁇ 50 ⁇ over a 200 mm x 200 mm area, as measured by a FLATMASTER® tool. In one embodiment, the flat front cover glass section has a flatness of better than ⁇ 50 ⁇ over a 25 mm x 25 mm area, as measured by a FLATMASTER® tool. In another embodiment, the front cover glass section may be curved.
  • the 3D cover glass has at least one curved surface, and in some embodiments, may comprise two or more bends.
  • the bend may be constant, having a fixed radius with a constant center point, or may be variable, as in the case of a spline structure.
  • the bend is a complex bend that has a changing radius, such as described by a Burmester curve.
  • the bend angle and radius can be selected based on the peripheral side geometry of the electronic device. In some embodiments, the bend angle is from greater than 0° to 90°. In some embodiments, the bend angle can be greater than 90°. In some embodiments, the bend radius is about 1 mm or greater.
  • the bend radius is from about 1 mm to about 20 mm, about 1 to about 15 mm, about 1 mm to about 10 mm, about 1 mm to about 5 mm, about 2 mm to about 20 mm, about 2 to about 15 mm, about 2 mm to about 10 mm, about 2 mm to about 5 mm, about 5 to about 15 mm, about 5 mm to about 10 mm, or about 1 mm to about 20 mm.
  • the bend radius is about 0.25, 0.5, 0.75, 1.0, 1.25, 1.5, 1.75, 2.0, 2.25, 2.5, 2.75, 3.0, 3.5, 4.0, 4.5, 5.0, 6.0, 7.0, 8.0, 9.0, 10.0, 15.0, 20.0 mm or more.
  • Non-limiting examples of 3D cover glasses are shown in Figs. 1 and 2.
  • the 3D cover glass 100 has a front cover glass section 102 and a side cover glass section 104.
  • the side cover glass section 104 circumscribes the front cover glass section 102 and includes a bend, giving the 3D cover glass 100 a dish shape.
  • the 3D cover glass 200 has a front cover glass section 202 and side cover glass sections 204, 206.
  • the side cover glass sections 204, 206 are on opposite sides of the front cover glass section 202.
  • the 3D cover glass is made from a 2D glass sheet using a thermal reforming process such as described in U.S. Patent Application Publication No. 2010/0000259 (Ukrainczyk, "Method of Making Shaped Glass Articles"), European Patent Application No. 10306317.8 (Corning Incorporated, "Method and Apparatus for Bending a Sheet of Material into a Shaped Article"), U.S. Patent Application No. 13/480172 (Bailey et ah, "Glass Molding System and Related Apparatus and Method"), U.S. Provisional Application No. 61/545,332, and U.S. Provisional Application No. 61/545,329, all incorporated by reference.
  • the 2D glass sheet is made by a fusion process. Although, 2D glass sheets made by other processes, such as the float or rolling, may also be used.
  • Another aspect comprises the uniformity of wall thickness of the glass sheet.
  • wall thickness When glass is bent or manipulated, the thickness of the sheet ("wall thickness") can vary in the bend regions, which can lead to optical distortion and weakened glass strength.
  • the current process uniquely preserves the uniformity of the glass across the surface and in the bend regions.
  • the 3D cover glass has a uniform wall thickness typically in a range from 0.3 mm to 3 mm.
  • the thickness is about 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9, or 3.0 mm.
  • the total variation in the wall thickness of the cover glass wall is within ⁇ 100 ⁇ .
  • the total variation in the wall thickness of the cover glass wall is within ⁇ 10 ⁇ , ⁇ 20 ⁇ , ⁇ 30 ⁇ , ⁇ 40 ⁇ , ⁇ 50 ⁇ , ⁇ 60 ⁇ , ⁇ 70 ⁇ , ⁇ 80 ⁇ , ⁇ 90 ⁇ , ⁇ 100 ⁇ , ⁇ 125 ⁇ , ⁇ 150 ⁇ , ⁇ 200 ⁇ , or ⁇ 250 ⁇ of the average wall thickness of the of the glass sheet.
  • the total variation in the wall thickness of the cover glass wall is ⁇ 10% of the average wall thickness of the glass sheet.
  • the total variation in the wall thickness of the cover glass wall is ⁇ 3% of the average wall thickness of the glass sheet.
  • the total variation in the wall thickness of the cover glass wall is ⁇ 20%, ⁇ 15%, ⁇ 10%, ⁇ 9%, ⁇ 8%, ⁇ 7%, ⁇ 6%, ⁇ 5%, ⁇ 4%, ⁇ 3%, ⁇ 2%, or ⁇ 1% of the average wall thickness of the glass sheet.
  • the 3D cover glass has an inside surface and an outside surface.
  • inside surface 210 and outside surface 212 are indicated in Fig. 2.
  • Fig. 1 shows an inside surface 106 and an outside surface 108.
  • Each surface is smooth, and this smoothness can be characterized by surface roughness.
  • the inside and outside surfaces have different surface roughness.
  • the average surface roughness (R a ) of each surface of the 3D cover glass is less than 1 nm.
  • the average surface roughness of each surface of the 3D cover glass is less than 0.7 nm. In some embodiments, the average surface roughness (R a ) of each surface of the 3D cover glass is less than 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3,
  • the average surface roughness (R a ) of at least one of the surfaces of the 3D cover glass is less than 0.3 nm. In some embodiments, the average surface roughness (R a ) of at least one of the surfaces of the 3D cover glass is less than 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1.0, 1.1, 1.2, 1.3, 1.4,
  • the average surface roughness (R a ) of at least one of the surfaces of the 3D cover glass is about 0.1 nm to about 3.0 nm, about 0.1 nm to about 2.0 nm, about 0.1 nm to about 1.5 nm, about 0.1 nm to about 1.0 nm, about 0.2 nm to about 3.0 nm, about 0.2 nm to about 2.0 nm, about 0.2 nm to about 1.5 nm, about 0.2 nm to about 1.0 nm, about 0.4 nm to about 3.0 nm, about 0.4 nm to about 2.0 nm, about 0.4 nm to about 1.5 nm, about 0.4 nm to about 0.7 nm, or about 0.4 nm to about 1.0 nm
  • the surface roughness of the inside and outside surfaces may be the same or different. The latter may be the case, for example, if the 3D cover glass is made by a mold and only one of the surfaces comes into contact with the mold during forming of the 3D cover glass. Typically, the surface of the 3D cover glass contacting the mold will be the outside surface. However, it is possible to design the mold such that the surface of the 3D cover glass not contacting the mold will be the outside surface.
  • Fig. 3A shows a surface roughness profile 300 of a first surface of a 3D cover glass that came into contact with a mold during forming of the 3D cover glass.
  • the average surface roughness in Fig. 3A is 0.691 nm.
  • Fig. 3B shows a surface roughness profile 302 of a second surface of the 3D cover glass that did not come into contact with the mold.
  • the average surface roughness in Fig. 3B is 0.2731 nm.
  • the 3D cover glass having the surface profiles in Figs. 3A and 3B was made by a thermal reforming process.
  • Table 1 shows surface roughness, including peak-to- valley departure (PV), root mean square (rms), and average surface roughness (R a ) profiles of five 3D glass samples made by machining.
  • PV peak-to- valley departure
  • rms root mean square
  • R a average surface roughness
  • the average surface roughness (R a ) of these samples range from 0.4 nm to 0.7 nm. It is noted that the surface roughness of the first surface of the 3D glass article in Fig. 3A is comparable to the surface roughness achieved by machining. Fig. 4 shows a surface roughness of a flat pristine fusion formed glass. The average surface roughness (R a ) of the flat glass is 0.2651. It is noted that the surface roughness of the second surface of the 3D glass article in Fig. 3B is comparable to the surface roughness of the flat glass. [0037] The surface roughness may be a function of the process of making the 2D glass or the 3D shaping process, and may also be affected by post processing, such as polishing. In some embodiments, the 3D cover glass is not subjected to post processing or has the roughness profile as described above prior to any post processing.
  • the as-formed quality of the 3D cover glass would be as good as the glass sheet from which it is formed.
  • this surface quality is achieved without further rework or polishing of the as-formed surface.
  • Defects include, but are not limited to, indentations (or dimples - depressions in the glass surface), surface checks/cracks, blisters, chips, cords, dice, observable crystals, laps, seeds, stones, and stria.
  • the surfaces of the 3D cover glass are essentially flawless.
  • essentially flawless it is meant that there are no indentations (or dimples) larger than 150 ⁇ in diameter, as measured by an optical microscopy technique, in the surfaces.
  • essentially flawless further comprises that there are no additional defects observable by the unaided human eye at 1000 lux on any of the surfaces.
  • the 3D cover glass is transparent and has an optical transmission greater than 85% in a wavelength range of 400 nm to 800 nm. In some embodiments, the 3D cover glass is transparent and has an optical transmission greater than 75%, 80%, 85%, 87%, 90%, 93%, or 95% in a wavelength range of 400 nm to 800 nm.
  • Fig. 5 shows a transmission profile 500 of an example 3D cover glass. Also shown in Fig. 5 is a delta profile 502 that represents the percent difference between the transmission of the 3D cover glass and a 2D fusion-formed glass.
  • a coating may be deposited on a surface of the 3D cover glass to make a portion of the 3D cover glass semi-transparent or opaque.
  • the portion of the 3D cover glass in which the coating is not deposited can be a clear aperture on the front cover glass section, which would allow for viewing of and interaction with an electronic device display.
  • Another aspect comprises the resistance of the 3D cover glass to damage.
  • a number of processes, such as tempering, increase the ability of a glass substrate to sustain shock and stress without being damaged.
  • the 3D cover glass (or the 2D glass sheet used in making the 3D cover glass) can be subjected to a strengthening process to achieve the compressive stress that is greater than 300 MPa.
  • the glass is chemically or thermally tempered.
  • the glass is chemically tempered.
  • the glass is ion exchanged.
  • the 3D cover glass is subjected to an ion-exchange chemical strengthening process to achieve a combination of a compressive stress greater than 300 MPa and an ion-exchange depth of layer of at least 25 ⁇ .
  • the ion-exchange depth of layer is at least 10, 15, 20, 25, 30, 35, 40, 45, or 50 ⁇ . In some embodiments, the ion-exchange depth of layer is from about 10 ⁇ to about 100 ⁇ . The ion-exchange depth of layer is measured from a surface of the glass into the glass. An ion-exchanged layer is characterized by the presence of oversized ions in the glass lattice structure.
  • the damage resistance of the 3D cover glass may be measured in terms of compressive stress.
  • the compressive stress at surface of glass greater than 300 MPa.
  • the cover glass has a compressive stress greater than 250, 300, 350, 400, 450, 500, 550, 600, 650, 700, 750, 800, 850, 900, 950, 1000 MPa or more.
  • the damage resistance of the 3D cover glass may be measured in terms of hardness and/or scratch resistance.
  • the 3D cover glass has a hardness greater than 7 on the Mohs scale.
  • the 3D cover glass has a hardness of about 6, 6.3, 6.5, 6.7, 7.0, 7.3, 7.5, 7.7, 8, 8.3, 8.5, 8.7, or 9 on the Mohs scale.
  • the 3D cover glass comprises an alkali aluminosilicate glass composition.
  • An exemplary alkali aluminosilicate glass composition comprises from about 60 mol% to about 70 mol% Si0 2 ; from about 6 mol% to about 14 mol% AI2O3; from 0 mol% to about 15 mol% B2O3; from 0 mol% to about 15 mol% Li 2 0; from 0 mol% to about 20 mol% Na 2 0; from 0 mol% to about 10 mol% K 2 0; from 0 mol% to about 8 mol% MgO; from 0 mol% to about 10 mol% CaO; from 0 mol% to about 5 mol% Zr0 2 ; from 0 mol% to about 1 mol% Sn0 2 ; from 0 mol% to about 1 mol% Ce0 2 ; less than about 50 ppm AS2O3; and less than about 50 ppm Sb 2 03; wherein 12 mol% ⁇ Li 2 0 + Na 2 0 + K 2 0 ⁇ 20 mol
  • Another exemplary alkali-aluminosilicate glass composition comprises at least about 50 mol% Si0 2 and at least about 11 mol% Na 2 0, and the compressive stress is at least about 900 MPa.
  • the glass further comprises AI2O3 and at least one of B 2 0 3 , K 2 0, MgO and ZnO, wherein -340 + 27.1-A1 2 0 3 - 28.7-B 2 0 3 + 15.6-Na 2 0 - 61.4-K 2 0 + 8.1 -(MgO + ZnO) ⁇ 0 mol%.
  • the glass comprises: from about 7 mol% to about 26 mol% AI2O3; from 0 mol% to about 9 mol% B2O3; from about 11 mol% to about 25 mol% Na 2 0; from 0 mol% to about 2.5 mol% K 2 0; from 0 mol% to about 8.5 mol% MgO; and from 0 mol% to about 1.5 mol% CaO.
  • This glass composition is described in U.S. Provisional Patent Application No. 61/503,734 by Matthew J. Dejneka et al, entitled "Ion Exchangeable Glass with High Compressive Stress," filed July 1, 2011, the contents of which are incorporated herein by reference in their entirety.
  • glass compositions besides those mentioned above and besides alkali-aluminosilicate glass composition may be used for the 3D cover glass.
  • alkali-aluminoborosilicate glass compositions may be used for the 3D cover glass.
  • the glass compositions used are ion-exchangeable glass compositions, which are generally glass compositions containing small alkali or alkaline-earth metals ions that can be exchanged for large alkali or alkaline-earth metal ions. Additional examples of ion-exchangeable glass compositions may be found in U.S. Patent Nos. 7,666,511 (Ellison et al; 20 November 2008), 4,483,700 (Forker, Jr.
  • the 3D cover glass is made by thermal reforming from a 2D glass sheet as already described above.
  • the 2D glass sheet is extracted from a pristine sheet of glass formed by a fusion process. The pristine nature of the glass may be preserved up until the glass is subjected to a strengthening process, such as an ion-exchange chemical strengthening process.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Microelectronics & Electronic Packaging (AREA)
  • Surface Treatment Of Glass (AREA)
  • Devices For Indicating Variable Information By Combining Individual Elements (AREA)
  • Re-Forming, After-Treatment, Cutting And Transporting Of Glass Products (AREA)
PCT/US2013/043025 2012-05-31 2013-05-29 Cover glass article Ceased WO2013181208A2 (en)

Priority Applications (7)

Application Number Priority Date Filing Date Title
JP2015515136A JP2015527277A (ja) 2012-05-31 2013-05-29 カバーガラス物品
KR1020147037043A KR20150016617A (ko) 2012-05-31 2013-05-29 커버 유리 제품
EP20156325.1A EP3693346B1 (en) 2012-05-31 2013-05-29 Cover glass article
CN201380028524.5A CN104520249B (zh) 2012-05-31 2013-05-29 盖板玻璃制品
EP21214725.0A EP4015476B1 (en) 2012-05-31 2013-05-29 Cover glass article
KR1020207012030A KR20200049876A (ko) 2012-05-31 2013-05-29 커버 유리 제품
EP13729841.0A EP2855388B1 (en) 2012-05-31 2013-05-29 Cover glass article

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201261653476P 2012-05-31 2012-05-31
US61/653,476 2012-05-31
US13/774,238 US9512029B2 (en) 2012-05-31 2013-02-22 Cover glass article
US13/774,238 2013-02-22

Publications (2)

Publication Number Publication Date
WO2013181208A2 true WO2013181208A2 (en) 2013-12-05
WO2013181208A3 WO2013181208A3 (en) 2014-01-30

Family

ID=49670585

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2013/043025 Ceased WO2013181208A2 (en) 2012-05-31 2013-05-29 Cover glass article

Country Status (7)

Country Link
US (4) US9512029B2 (cg-RX-API-DMAC7.html)
EP (3) EP3693346B1 (cg-RX-API-DMAC7.html)
JP (3) JP2015527277A (cg-RX-API-DMAC7.html)
KR (2) KR20150016617A (cg-RX-API-DMAC7.html)
CN (1) CN104520249B (cg-RX-API-DMAC7.html)
TW (1) TWI603926B (cg-RX-API-DMAC7.html)
WO (1) WO2013181208A2 (cg-RX-API-DMAC7.html)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015174428A1 (ja) * 2014-05-15 2015-11-19 旭硝子株式会社 ガラス物品、及びガラス物品の製造方法
CN110642507A (zh) * 2019-10-31 2020-01-03 维沃移动通信有限公司 电子设备的外壳及其制备方法、电子设备

Families Citing this family (55)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5622069B2 (ja) * 2009-01-21 2014-11-12 日本電気硝子株式会社 強化ガラス、強化用ガラス及び強化ガラスの製造方法
US9359251B2 (en) 2012-02-29 2016-06-07 Corning Incorporated Ion exchanged glasses via non-error function compressive stress profiles
US9512029B2 (en) * 2012-05-31 2016-12-06 Corning Incorporated Cover glass article
US9145323B2 (en) 2013-01-21 2015-09-29 Corning Incorporated Molds for shaping glass and methods for making the same
TWI631049B (zh) 2013-05-07 2018-08-01 Corning Incorporated 製造３ｄ玻璃蓋的方法以及用於估計３ｄ玻璃蓋的形狀之電腦實施方法
US11079309B2 (en) 2013-07-26 2021-08-03 Corning Incorporated Strengthened glass articles having improved survivability
KR102102314B1 (ko) * 2013-12-16 2020-04-20 엘지디스플레이 주식회사 휘어진 커버 플레이트 및 그를 이용한 휘어진 디스플레이 장치와 그 제조방법
US9815730B2 (en) * 2013-12-17 2017-11-14 Corning Incorporated Processing 3D shaped transparent brittle substrate
US9321677B2 (en) 2014-01-29 2016-04-26 Corning Incorporated Bendable glass stack assemblies, articles and methods of making the same
US9517968B2 (en) 2014-02-24 2016-12-13 Corning Incorporated Strengthened glass with deep depth of compression
TWI852054B (zh) 2014-06-19 2024-08-11 美商康寧公司 無易碎應力分布曲線的玻璃
US10472277B2 (en) 2014-07-28 2019-11-12 Dell Products L.P. Composite plastic display cover
US10611664B2 (en) 2014-07-31 2020-04-07 Corning Incorporated Thermally strengthened architectural glass and related systems and methods
WO2016019167A1 (en) 2014-07-31 2016-02-04 Corning Incorporated Thermally tempered glass and methods and apparatuses for thermal tempering of glass
WO2017019840A1 (en) * 2015-07-30 2017-02-02 Corning Incorporated Thermally strengthened consumer electronic glass and related systems and methods
US11097974B2 (en) 2014-07-31 2021-08-24 Corning Incorporated Thermally strengthened consumer electronic glass and related systems and methods
US10737467B2 (en) * 2014-08-25 2020-08-11 Dell Products L.P. Multilayer glass composite display cover
CN112340983A (zh) 2014-10-08 2021-02-09 康宁股份有限公司 包含金属氧化物浓度梯度的玻璃和玻璃陶瓷
US10150698B2 (en) 2014-10-31 2018-12-11 Corning Incorporated Strengthened glass with ultra deep depth of compression
CN115572078A (zh) 2014-11-04 2023-01-06 康宁股份有限公司 深层非易碎应力曲线及其制造方法
JP6711824B2 (ja) * 2014-11-05 2020-06-17 コーニング インコーポレイテッド 非平面状の構造的特徴および無アルカリガラス要素を有するガラス物品
US9939295B2 (en) * 2014-12-16 2018-04-10 Carestream Health, Inc. Impact protection for wireless digital detector glass panel
TWI687375B (zh) 2015-03-20 2020-03-11 美商康寧公司 用於成形基於玻璃的材料之模具與製作該模具之方法
JPWO2016158623A1 (ja) * 2015-03-31 2018-01-25 旭硝子株式会社 ガラス板
US11613103B2 (en) 2015-07-21 2023-03-28 Corning Incorporated Glass articles exhibiting improved fracture performance
US10579106B2 (en) 2015-07-21 2020-03-03 Corning Incorporated Glass articles exhibiting improved fracture performance
US12338159B2 (en) 2015-07-30 2025-06-24 Corning Incorporated Thermally strengthened consumer electronic glass and related systems and methods
US10351459B2 (en) 2015-08-14 2019-07-16 Corning Incorporated Molds and methods to control mold surface quality
WO2017087204A1 (en) 2015-11-18 2017-05-26 Corning Incorporated Powder, process of making the powder, and articles made therefrom
WO2017100646A1 (en) 2015-12-11 2017-06-15 Corning Incorporated Fusion-formable glass-based articles including a metal oxide concentration gradient
JP6923555B2 (ja) 2016-01-12 2021-08-18 コーニング インコーポレイテッド 薄厚熱強化及び化学強化ガラス系物品
US11795102B2 (en) 2016-01-26 2023-10-24 Corning Incorporated Non-contact coated glass and related coating system and method
CN111423110A (zh) 2016-04-08 2020-07-17 康宁股份有限公司 包含金属氧化物浓度梯度的玻璃基制品
US10271442B2 (en) 2016-04-08 2019-04-23 Corning Incorporated Glass-based articles including a stress profile comprising two regions, and methods of making
JP6969156B2 (ja) * 2016-05-30 2021-11-24 Ａｇｃ株式会社 印刷層付き板およびその製造方法、および表示装置
TWI756293B (zh) * 2016-11-15 2022-03-01 美商康寧公司 製造具有紋理化表面及3d形狀的玻璃的製程
DE102017102482B4 (de) * 2017-02-08 2019-11-21 Schott Ag Gläser mit verbesserter Ionenaustauschbarkeit und thermischer Ausdehnung
DE102018002397A1 (de) * 2017-03-23 2018-09-27 Asahi Glass Company, Limited Blendschutz-glassubstrat
CN211367401U (zh) * 2017-05-12 2020-08-28 Ａｇｃ株式会社 弯曲基材及支承构件
US11020957B2 (en) * 2017-05-17 2021-06-01 AGC Inc. Producing method of base member provided with printed layer and base member provided with printed layer
US10455747B2 (en) * 2017-07-11 2019-10-22 Microsoft Technology Licensing, Llc Additively manufactured protrusions
TW201920028A (zh) 2017-08-24 2019-06-01 美商康寧公司 具有改良回火能力之玻璃
CN109455906B (zh) 2017-09-06 2022-12-13 Ａｇｃ株式会社 3d罩盖玻璃及其成形用模具、及3d罩盖玻璃的制造方法
CN107635033A (zh) * 2017-09-27 2018-01-26 北京小米移动软件有限公司 曲面玻璃的加工工艺、屏幕模组及电子设备
JP7031230B2 (ja) * 2017-11-01 2022-03-08 Ａｇｃ株式会社 ３ｄカバーガラス、およびその製造方法
WO2019108774A1 (en) 2017-11-29 2019-06-06 Corning Incorporated Methods of making coated glass-based parts
TWI785156B (zh) 2017-11-30 2022-12-01 美商康寧公司 具有高熱膨脹係數及對於熱回火之優先破裂行為的非離子交換玻璃
US11426818B2 (en) 2018-08-10 2022-08-30 The Research Foundation for the State University Additive manufacturing processes and additively manufactured products
CN112969667A (zh) 2018-11-05 2021-06-15 日本板硝子株式会社 具有三维形状的玻璃物品及其制造方法、化学强化玻璃物品及其制造方法
TWI839412B (zh) * 2018-11-27 2024-04-21 美商康寧公司 具有改善的表面及邊緣品質的抬頭顯示器鏡與其形成方法
TWI841629B (zh) * 2018-11-29 2024-05-11 美商康寧公司 用於抬頭顯示系統之反曲率非球面鏡及其形成方法
KR20210154825A (ko) 2019-04-23 2021-12-21 코닝 인코포레이티드 확정 응력 프로파일을 갖는 유리 라미네이트 및 그 제조방법
WO2021025981A1 (en) 2019-08-06 2021-02-11 Corning Incorporated Glass laminate with buried stress spikes to arrest cracks and methods of making the same
DE102019125099A1 (de) * 2019-09-18 2021-03-18 Schott Ag Dreidimensional umgeformtes Dünnglas
US12358827B2 (en) 2019-11-26 2025-07-15 Corning Incorporated 3D glass-ceramic articles and methods for making the same

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4483700A (en) 1983-08-15 1984-11-20 Corning Glass Works Chemical strengthening method
US5674790A (en) 1995-12-15 1997-10-07 Corning Incorporated Strengthening glass by ion exchange
US20100000259A1 (en) 2008-07-02 2010-01-07 Ljerka Ukrainczyk Method of making shaped glass articles
US7666511B2 (en) 2007-05-18 2010-02-23 Corning Incorporated Down-drawable, chemically strengthened glass for cover plate
US8158543B2 (en) 2008-02-26 2012-04-17 Corning Incorporated Fining agents for silicate glasses

Family Cites Families (62)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5046075A (cg-RX-API-DMAC7.html) 1973-08-28 1975-04-24
FR2338229A1 (fr) 1976-01-14 1977-08-12 Bfg Glassgroup Procede pour le pliage de feuilles de verre, dispositif et installation pour la mise en oeuvre du procede
US4164402A (en) 1978-02-27 1979-08-14 Yamamura Glass Co., Ltd. Strengthening of thin-walled, light glass containers
JPS57123629A (en) 1981-01-23 1982-08-02 Toshiba Corp U-shaped curving device for glass tube
NL8100602A (nl) 1981-02-09 1982-09-01 Philips Nv Werkwijze voor het precisie-persen van glazen voorwerpen,werkwijze voor het vervaardigen van een mal en mal voor het precisie-persen van glazen voorwerpen.
CH660398A5 (de) 1982-01-21 1987-04-15 Peter Lisec Abstandhalterrahmen fuer isolierglasscheiben sowie verfahren zur herstellung desselben und vorrichtung zur durchfuehrung des verfahrens.
JP2577055B2 (ja) 1988-07-13 1997-01-29 ホーヤ株式会社 ガラス成形型
JP3020180B2 (ja) 1990-12-25 2000-03-15 日本板硝子株式会社 平板材の製造方法及びこの方法を用いた三次元形状の板材の製造方法
JPH04357174A (ja) 1991-05-30 1992-12-10 Toshiba Tungaloy Co Ltd 工具用被覆窒化ケイ素燒結体
RU2245851C2 (ru) 1999-03-23 2005-02-10 Шотт Глас Способ и устройство для равномерного прогревания стекол и/или стеклокерамики с помощью инфракрасного излучения
WO2000056674A1 (de) 1999-03-23 2000-09-28 Schott Glas Verfahren zur formgebung von glaskeramikteilen und/oder glasteilen
DE10118260A1 (de) 2001-04-11 2002-10-24 Schott Glas Verfahren und Vorrichtung zum Umformen von Gläsern und/oder Glaskeramiken
KR100847618B1 (ko) 2001-09-05 2008-07-21 니혼 이타가라스 가부시키가이샤 고 투과 글래스판 및 고 투과 글래스판의 제조방법
US6935137B2 (en) 2001-10-09 2005-08-30 General Electric Company Method of and apparatus for forming discharge tubes of low-pressure discharge lamps
TWI314135B (en) 2002-11-15 2009-09-01 Nippon Electric Glass Co Cover glass for solid-state image pickup device
JP5378158B2 (ja) * 2003-02-19 2013-12-25 日本電気硝子株式会社 半導体パッケージ用カバーガラス
US7727917B2 (en) 2003-10-24 2010-06-01 Schott Ag Lithia-alumina-silica containing glass compositions and glasses suitable for chemical tempering and articles made using the chemically tempered glass
WO2005080285A1 (en) 2004-02-20 2005-09-01 Waseda University Method for strengtehning glass and strengthened glass produced by the method
JP5046075B2 (ja) 2005-11-09 2012-10-10 日本電気硝子株式会社 ガラス物品の成形方法及び成形装置
DE102007002725A1 (de) 2007-01-18 2008-07-31 Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. Gehäuse für in mobilen Anwendungen eingesetzte mikromechanische und mikrooptische Bauelemente
JP5215314B2 (ja) 2007-09-26 2013-06-19 第一工業製薬株式会社 導電性高分子電極の製造方法及びそれを備えた色素増感太陽電池
CN101910079A (zh) 2007-11-29 2010-12-08 康宁股份有限公司 具有改进的韧性和抗刮性的玻璃
KR101512213B1 (ko) * 2007-12-18 2015-04-14 호야 가부시키가이샤 휴대 단말기용 커버 글래스 및 그 제조 방법, 및 휴대 단말 장치
EP2323955A1 (en) 2008-07-03 2011-05-25 Corning Inc. Durable glass-ceramic housings/enclosures for electronic devices
CN102123960A (zh) 2008-08-21 2011-07-13 康宁股份有限公司 用于电子设备的耐久性玻璃机壳/封罩
US20100055395A1 (en) * 2008-08-28 2010-03-04 Ljerka Ukrainczyk Method of Making Shaped Glass Articles
EP2365945A1 (en) 2008-11-25 2011-09-21 Corning Inc. Progressive pressing to form a glass article
JP5622069B2 (ja) * 2009-01-21 2014-11-12 日本電気硝子株式会社 強化ガラス、強化用ガラス及び強化ガラスの製造方法
US8341976B2 (en) 2009-02-19 2013-01-01 Corning Incorporated Method of separating strengthened glass
US8802581B2 (en) 2009-08-21 2014-08-12 Corning Incorporated Zircon compatible glasses for down draw
TWI478879B (zh) 2009-11-30 2015-04-01 Corning Inc 製造成形物品之方法及裝置
US8835011B2 (en) 2010-01-07 2014-09-16 Corning Incorporated Cover assembly for electronic display devices
US9232670B2 (en) 2010-02-02 2016-01-05 Apple Inc. Protection and assembly of outer glass surfaces of an electronic device housing
CN102167507B (zh) 2010-02-26 2016-03-16 肖特玻璃科技(苏州)有限公司 用于3d紧密模压的薄锂铝硅玻璃
US8561535B2 (en) 2010-02-27 2013-10-22 Corning Incorporated Method of screen printing on 3D glass articles
DE102010020439A1 (de) 2010-05-12 2011-11-17 Schott Ag Verfahren zur Herstellung geformter Glasartikel und Verwendung der verfahrensgemäß hergestellten Glasartikel
US20110281072A1 (en) * 2010-05-17 2011-11-17 Robert Sabia Laminable shaped glass article and method of making the same
CN102249542B (zh) 2010-05-18 2015-08-19 肖特玻璃科技(苏州)有限公司 用于3d精密模压和热弯曲的碱金属铝硅酸盐玻璃
US8778820B2 (en) 2010-05-27 2014-07-15 Corning Incorporated Glasses having low softening temperatures and high toughness
US20120052275A1 (en) 2010-08-30 2012-03-01 Avanstrate Inc. Glass substrate, chemically strengthened glass substrate and cover glass, and method for manufactruing the same
EP2616404B1 (en) 2010-09-14 2019-07-10 Corning Incorporated Appliance fascia and mounting therefore
US9434644B2 (en) 2010-09-30 2016-09-06 Avanstrate Inc. Cover glass and method for producing cover glass
JP5605176B2 (ja) * 2010-11-10 2014-10-15 旭硝子株式会社 フラットパネルディスプレイ用カバーガラス及びその製造方法
US9346703B2 (en) 2010-11-30 2016-05-24 Corning Incorporated Ion exchangable glass with deep compressive layer and high damage threshold
EP2457881B1 (en) 2010-11-30 2019-05-08 Corning Incorporated Method and apparatus for bending a sheet of material into a shaped article
US8778496B2 (en) 2010-11-30 2014-07-15 Corning Incorporated Anti-glare glass sheet having compressive stress equipoise and methods thereof
JP5437351B2 (ja) 2010-12-27 2014-03-12 Ｈｏｙａ株式会社 携帯型電子機器用カバーガラスのガラス基板、携帯型電子機器用画像表示装置、携帯型電子機器
WO2012118612A1 (en) 2011-02-28 2012-09-07 Corning Incorporated Method of forming a 3d glass article from a 2d glass sheet
CN102690059B (zh) 2011-03-23 2016-08-03 肖特玻璃科技(苏州)有限公司 用于化学钢化的铝硅酸盐玻璃和玻璃陶瓷
CN102740623A (zh) 2011-04-15 2012-10-17 巍思有限公司 立体结构玻璃及其制造方法
JP5881414B2 (ja) 2011-04-20 2016-03-09 Hoya株式会社 携帯機器用カバーガラス
WO2012150476A1 (en) 2011-05-02 2012-11-08 Corning Incorporated Glass panel with formed edges and method of making it
US20120288661A1 (en) 2011-05-10 2012-11-15 Weis Limited Solid structure glass and method for making the same
US8783066B2 (en) 2011-05-27 2014-07-22 Corning Incorporated Glass molding system and related apparatus and method
US8889575B2 (en) 2011-05-31 2014-11-18 Corning Incorporated Ion exchangeable alkali aluminosilicate glass articles
TWI591039B (zh) 2011-07-01 2017-07-11 康寧公司 具高壓縮應力的離子可交換玻璃
JP5201542B2 (ja) 2011-08-24 2013-06-05 日本電気硝子株式会社 ディスプレイ基板
JP6310393B2 (ja) 2011-10-10 2018-04-11 コーニング インコーポレイテッド 薄型ガラスシートの再成形
JP2015501274A (ja) 2011-10-10 2015-01-15 コーニング インコーポレイテッド 薄型ガラスシートに弛みなく曲げを形成する装置および方法
JP2015026874A (ja) 2011-11-15 2015-02-05 パナソニック株式会社 無線通信システム、親無線装置、及び子無線装置
JP2012076997A (ja) 2012-01-24 2012-04-19 Nippon Electric Glass Co Ltd ガラス物品
US9512029B2 (en) * 2012-05-31 2016-12-06 Corning Incorporated Cover glass article

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4483700A (en) 1983-08-15 1984-11-20 Corning Glass Works Chemical strengthening method
US5674790A (en) 1995-12-15 1997-10-07 Corning Incorporated Strengthening glass by ion exchange
US7666511B2 (en) 2007-05-18 2010-02-23 Corning Incorporated Down-drawable, chemically strengthened glass for cover plate
US8158543B2 (en) 2008-02-26 2012-04-17 Corning Incorporated Fining agents for silicate glasses
US20100000259A1 (en) 2008-07-02 2010-01-07 Ljerka Ukrainczyk Method of making shaped glass articles

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015174428A1 (ja) * 2014-05-15 2015-11-19 旭硝子株式会社 ガラス物品、及びガラス物品の製造方法
CN106458683A (zh) * 2014-05-15 2017-02-22 旭硝子株式会社 玻璃物品以及玻璃物品的制造方法
JPWO2015174428A1 (ja) * 2014-05-15 2017-04-20 旭硝子株式会社 ガラス物品、及びガラス物品の製造方法
CN107814476A (zh) * 2014-05-15 2018-03-20 旭硝子株式会社 玻璃物品以及玻璃物品的制造方法
US11280939B2 (en) 2014-05-15 2022-03-22 AGC Inc. Glass article and production method for glass article
US11448802B2 (en) 2014-05-15 2022-09-20 AGC Inc. Glass article and production method for glass article
EP4074665A1 (en) 2014-05-15 2022-10-19 Agc Inc. Glass article and production method for glass article
CN116062989A (zh) * 2014-05-15 2023-05-05 Ａｇｃ株式会社 玻璃物品以及玻璃物品的制造方法
CN110642507A (zh) * 2019-10-31 2020-01-03 维沃移动通信有限公司 电子设备的外壳及其制备方法、电子设备
CN110642507B (zh) * 2019-10-31 2022-01-11 维沃移动通信有限公司 电子设备的外壳及其制备方法、电子设备

Also Published As

Publication number Publication date
EP4015476A1 (en) 2022-06-22
EP4015476B1 (en) 2024-10-02
KR20200049876A (ko) 2020-05-08
US20180343758A1 (en) 2018-11-29
JP2021038139A (ja) 2021-03-11
US20200163244A1 (en) 2020-05-21
CN104520249B (zh) 2017-09-08
US10051753B2 (en) 2018-08-14
US20170196109A1 (en) 2017-07-06
TWI603926B (zh) 2017-11-01
TW201402477A (zh) 2014-01-16
KR20150016617A (ko) 2015-02-12
EP2855388A2 (en) 2015-04-08
EP3693346B1 (en) 2022-04-06
EP3693346A1 (en) 2020-08-12
US20130323444A1 (en) 2013-12-05
US9512029B2 (en) 2016-12-06
EP2855388B1 (en) 2020-03-18
US10575422B2 (en) 2020-02-25
WO2013181208A3 (en) 2014-01-30
US11297726B2 (en) 2022-04-05
CN104520249A (zh) 2015-04-15
JP2019163204A (ja) 2019-09-26
JP2015527277A (ja) 2015-09-17

Similar Documents

Publication Publication Date Title
US11297726B2 (en) Cover glass article
US11765846B2 (en) Display screen protector
JP7225329B2 (ja) 薄厚熱強化及び化学強化ガラス系物品
CN106458700B (zh) 玻璃制品及其形成方法
EP3110769B1 (en) Ion exchangeable glass article for three-dimensional forming
KR102728430B1 (ko) 높은 굽힘 강도의 박형 유리 기판 및 이의 제조 방법
WO2014052711A1 (en) Glass-ceramic(s); associated formable and/or color-tunable, crystallizable glass(es); and associated process(es)
CN113248159A (zh) 提高具有多个厚度的玻璃制品上的iox加工性的方法
EP3519368A1 (en) Glass-based articles with engineered stress profiles and methods of manufacture
KR20210030385A (ko) 비대칭 표면을 갖는 강화된 물품을 제조하는 비대칭 이온-교환 방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13729841

Country of ref document: EP

Kind code of ref document: A2

ENP Entry into the national phase

Ref document number: 2015515136

Country of ref document: JP

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2013729841

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 20147037043

Country of ref document: KR

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13729841

Country of ref document: EP

Kind code of ref document: A2