WO2013175910A1 - Produit feuilleté barrière aux gaz, et procédé de fabrication d'un produit feuilleté barrière aux gaz - Google Patents

Produit feuilleté barrière aux gaz, et procédé de fabrication d'un produit feuilleté barrière aux gaz Download PDF

Info

Publication number
WO2013175910A1
WO2013175910A1 PCT/JP2013/061569 JP2013061569W WO2013175910A1 WO 2013175910 A1 WO2013175910 A1 WO 2013175910A1 JP 2013061569 W JP2013061569 W JP 2013061569W WO 2013175910 A1 WO2013175910 A1 WO 2013175910A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas barrier
energy ray
group
layer
meth
Prior art date
Application number
PCT/JP2013/061569
Other languages
English (en)
Japanese (ja)
Inventor
悠太 鈴木
Original Assignee
リンテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リンテック株式会社 filed Critical リンテック株式会社
Publication of WO2013175910A1 publication Critical patent/WO2013175910A1/fr

Abstract

L'invention concerne un produit feuilleté barrière aux gaz présentant d'excellentes propriétés de barrière aux gaz, une excellente résistance aux rayures et une excellente résistance aux solvants, et un procédé de fabrication efficace pour un tel produit feuilleté. L'invention concerne un produit feuilleté barrière aux gaz ayant une couche barrière aux gaz sur au moins une surface d'un substrat, et un procédé de fabrication pour un tel produit feuilleté. La présente invention est caractérisée en ce que : la couche barrière aux gaz est issue d'une matière barrière aux gaz comprenant un polymère contenant du silicium et un composant durcissable sous l'action d'un rayonnement énergétique ; et la matière barrière aux gaz est soumise sous l'action d'un rayonnement énergétique et à une injection d'ions plasma. Le composant durcissable par rayons d'énergie est soit un monomère durcissable sous l'action d'un rayonnement énergétique soit un oligomère durcissable sous l'action d'un rayonnement énergétique. On préfère que le polymère contenant du silicium soit un composé polysilazane. On préfère également que la vitesse de transmission de vapeur d'eau d'un tel produit feuilleté barrière aux gaz ne soit pas supérieure à 0,1 g/(m2/jour).
PCT/JP2013/061569 2012-05-21 2013-04-19 Produit feuilleté barrière aux gaz, et procédé de fabrication d'un produit feuilleté barrière aux gaz WO2013175910A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012-115310 2012-05-21
JP2012115310 2012-05-21

Publications (1)

Publication Number Publication Date
WO2013175910A1 true WO2013175910A1 (fr) 2013-11-28

Family

ID=49623611

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/061569 WO2013175910A1 (fr) 2012-05-21 2013-04-19 Produit feuilleté barrière aux gaz, et procédé de fabrication d'un produit feuilleté barrière aux gaz

Country Status (2)

Country Link
TW (1) TW201347985A (fr)
WO (1) WO2013175910A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3786219A4 (fr) * 2018-04-25 2021-06-02 Lg Chem, Ltd. Film barrière

Families Citing this family (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN105744768A (zh) 2014-12-11 2016-07-06 深圳富泰宏精密工业有限公司 壳体、该壳体的制备方法及应用该壳体的电子装置
KR102432417B1 (ko) * 2016-06-10 2022-08-12 닛토덴코 가부시키가이샤 투명 도전성 필름 및 터치 패널
TWI708680B (zh) * 2019-01-08 2020-11-01 穎華科技股份有限公司 高分子塑膠前面板及其製法

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07278328A (ja) * 1994-04-14 1995-10-24 Toyota Autom Loom Works Ltd 薄膜形成方法
JPH11268196A (ja) * 1998-03-23 1999-10-05 Asahi Glass Co Ltd 透明被覆成形品およびその製造方法
WO2001044371A1 (fr) * 1999-12-16 2001-06-21 Asahi Glass Company, Limited Composition de polysilazane et article moule revetu comportant un objet traite elabore a partir de cette composition
WO2010107018A1 (fr) * 2009-03-17 2010-09-23 リンテック株式会社 Article moulé, procédé de fabrication de l'article moulé, élément pour dispositif électronique et dispositif électronique
WO2012039355A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Film formant une barrière contre les gaz, procédé de fabrication associé, élément pour dispositifs électroniques, et dispositif électronique
WO2012039357A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Corps formé, son procédé de production, élément de dispositif électronique et dispositif électronique
WO2012039387A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Corps formé, procédé de fabrication associé, élément pour dispositifs électroniques et dispositif électronique

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07278328A (ja) * 1994-04-14 1995-10-24 Toyota Autom Loom Works Ltd 薄膜形成方法
JPH11268196A (ja) * 1998-03-23 1999-10-05 Asahi Glass Co Ltd 透明被覆成形品およびその製造方法
WO2001044371A1 (fr) * 1999-12-16 2001-06-21 Asahi Glass Company, Limited Composition de polysilazane et article moule revetu comportant un objet traite elabore a partir de cette composition
WO2010107018A1 (fr) * 2009-03-17 2010-09-23 リンテック株式会社 Article moulé, procédé de fabrication de l'article moulé, élément pour dispositif électronique et dispositif électronique
WO2012039355A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Film formant une barrière contre les gaz, procédé de fabrication associé, élément pour dispositifs électroniques, et dispositif électronique
WO2012039357A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Corps formé, son procédé de production, élément de dispositif électronique et dispositif électronique
WO2012039387A1 (fr) * 2010-09-21 2012-03-29 リンテック株式会社 Corps formé, procédé de fabrication associé, élément pour dispositifs électroniques et dispositif électronique

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3786219A4 (fr) * 2018-04-25 2021-06-02 Lg Chem, Ltd. Film barrière
US11591445B2 (en) 2018-04-25 2023-02-28 Lg Chem, Ltd. Barrier film

Also Published As

Publication number Publication date
TW201347985A (zh) 2013-12-01

Similar Documents

Publication Publication Date Title
JP6883127B2 (ja) 長尺のガスバリア性積層体およびその製造方法
EP2832539B1 (fr) Stratifié à film barrière aux gaz, élément pour dispositif électronique et dispositif électronique
KR102168722B1 (ko) 가스 배리어 필름 및 그 제조 방법, 가스 배리어 필름 적층체, 전자 디바이스용 부재, 그리고 전자 디바이스
KR101495482B1 (ko) 가스 배리어성 필름 및 그의 제조 방법
US10967618B2 (en) Curable composition for forming primer layer, gas barrier laminated film, and gas barrier laminate
WO2013175910A1 (fr) Produit feuilleté barrière aux gaz, et procédé de fabrication d'un produit feuilleté barrière aux gaz
KR20150135520A (ko) 적층체 및 그 제조 방법, 전자 디바이스용 부재, 그리고 전자 디바이스
CN113226746A (zh) 阻气性层叠体
CN113226750B (zh) 阻气性层叠体
WO2014103756A1 (fr) Film barrière aux gaz
JPWO2013168647A1 (ja) ガスバリア性フィルムの製造方法
JP6544832B2 (ja) ガスバリア性積層体、電子デバイス用部材および電子デバイス
WO2013125351A1 (fr) Structure de barrière de gaz et procédé de formation de structure de barrière de gaz
WO2015152076A1 (fr) Stratifié de barrière contre les gaz allongé, procédé pour sa production, élément de dispositif électronique, et dispositif électronique
JP6694380B2 (ja) ガスバリア性積層体、電子デバイス用部材、および電子デバイス
TW201808632A (zh) 層積體、電子裝置用元件以及電子裝置
JP2016140994A (ja) ガスバリアー性フィルム及び電子デバイス
WO2013175911A1 (fr) Feuille barrière aux gaz et procédé de fabrication d'une feuille barrière aux gaz

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13794080

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13794080

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP