WO2013153501A1 - Colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension, et accessoires de câble - Google Patents

Colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension, et accessoires de câble Download PDF

Info

Publication number
WO2013153501A1
WO2013153501A1 PCT/IB2013/052794 IB2013052794W WO2013153501A1 WO 2013153501 A1 WO2013153501 A1 WO 2013153501A1 IB 2013052794 W IB2013052794 W IB 2013052794W WO 2013153501 A1 WO2013153501 A1 WO 2013153501A1
Authority
WO
WIPO (PCT)
Prior art keywords
sealing glue
siloxane polymer
rubber body
filler
cable
Prior art date
Application number
PCT/IB2013/052794
Other languages
English (en)
Inventor
Yugang LI
Peng Li
Lizhang Yang
Original Assignee
Tyco Electronics (Shanghai) Co. Ltd.
Tyco Electronics Uk Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tyco Electronics (Shanghai) Co. Ltd., Tyco Electronics Uk Ltd filed Critical Tyco Electronics (Shanghai) Co. Ltd.
Publication of WO2013153501A1 publication Critical patent/WO2013153501A1/fr

Abstract

La présente invention concerne une colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension et son procédé de préparation, et concerne également des accessoires de câble. La colle d'étanchéité contient a) un premier polymère de siloxane contenant un motif répété représenté par la formule (I) : RaSiO(4-a)/2, le groupe R étant un groupe substitué ou non substitué contenant 1 à 20 atomes de carbone, a valant 0, 1, 2 ou 3, le poids moléculaire moyen en nombre du premier polymère de siloxane allant de 150 000 à 900 000 g/mole ; b) un second polymère de siloxane contenant un motif représenté par la formule (I), la viscosité cinématique du second polymère de siloxane allant de 5 000 cst à 100 Mcst ; et c) une charge ; la charge représentant plus de 10 % du poids de la colle d'étanchéité. Par rapport à l'art antérieur, la seconde molécule de polymère de siloxane utilisée dans la colle d'étanchéité de la présente invention est relativement grande et le second polymère de siloxane pénètre difficilement dans le corps de caoutchouc. Ainsi, la performance du corps de caoutchouc n'est pas facilement affectée par la colle d'étanchéité, ce qui peut prolonger la vie du corps de caoutchouc et stabiliser la qualité de protection d'une tête de câble.
PCT/IB2013/052794 2012-04-09 2013-04-08 Colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension, et accessoires de câble WO2013153501A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201210101372.4 2012-04-09
CN201210101372.4A CN103361022B (zh) 2012-04-09 2012-04-09 用于中高压电缆附件的硅橡胶密封胶泥以及电缆附件

Publications (1)

Publication Number Publication Date
WO2013153501A1 true WO2013153501A1 (fr) 2013-10-17

Family

ID=48539311

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2013/052794 WO2013153501A1 (fr) 2012-04-09 2013-04-08 Colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension, et accessoires de câble

Country Status (2)

Country Link
CN (1) CN103361022B (fr)
WO (1) WO2013153501A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9425605B2 (en) 2013-03-14 2016-08-23 Tyco Electronics Corporation Method for protecting a cable splice connection with a cover assembly
US10389103B2 (en) 2016-10-18 2019-08-20 Te Connectivity Corporation Breakout boot assemblies and methods for covering electrical cables and connections
CN111849046A (zh) * 2020-07-31 2020-10-30 上海蓝昊电气江苏有限公司 一种耐高温电缆用半导电外屏蔽材料

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103595011A (zh) * 2013-12-03 2014-02-19 深圳市沃尔核材股份有限公司 一种冷缩管
CN103595008A (zh) * 2013-12-03 2014-02-19 深圳市沃尔核材股份有限公司 冷缩封帽
CN103595009A (zh) * 2013-12-03 2014-02-19 深圳市沃尔核材股份有限公司 冷收缩式电缆附件
CN104734106B (zh) * 2013-12-19 2018-03-23 泰科电子(上海)有限公司 将冷缩式终端安装在电力电缆上的方法和冷缩式终端组件
CN103986115A (zh) * 2014-05-06 2014-08-13 昆山达功电子有限公司 超导电缆绝缘连接管
CN105524467B (zh) * 2014-09-29 2018-05-29 开封市翰园铁路橡塑实业有限公司 弹性胶泥及其制备方法
CN104830070A (zh) * 2015-05-29 2015-08-12 深圳科创新源工业材料有限公司 一种密封胶泥及其工艺方法
CN105038248A (zh) * 2015-08-28 2015-11-11 深圳科创新源工业材料有限公司 一种高介电常数防水密封胶泥及其工艺方法
CN106590517A (zh) * 2016-12-20 2017-04-26 国网福建省电力有限公司泉州供电公司 一种密封胶及其制备方法
CN113999628B (zh) * 2021-11-04 2023-04-11 荣耀终端有限公司 绝缘胶、绝缘胶带及绝缘胶的制备方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5248716A (en) * 1992-01-30 1993-09-28 General Electric Company Silicone pressure-sensitive adhesives with control removal property
US20080045648A1 (en) * 2004-08-30 2008-02-21 Lorrene Bayon Liquid Silicone Elastomer Composition For Material Having High Tear Strength
US20090042043A1 (en) * 2005-07-22 2009-02-12 Edouard Joseph Organosiloxane Compositions

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5880244A (en) * 1997-05-13 1999-03-09 Lexmark International, Inc. Sealant materials for toner cartridges
JP4494543B2 (ja) * 1998-11-20 2010-06-30 東レ・ダウコーニング株式会社 室温硬化性シリコーンゴム組成物
CN101560372B (zh) * 2009-04-02 2012-12-12 佛山市华联有机硅有限公司 一次成型有机硅自粘性压敏胶的制备方法
FR2954341B1 (fr) * 2009-12-21 2014-07-11 Bostik Sa Composition adhesive reticulable par chauffage

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5248716A (en) * 1992-01-30 1993-09-28 General Electric Company Silicone pressure-sensitive adhesives with control removal property
US20080045648A1 (en) * 2004-08-30 2008-02-21 Lorrene Bayon Liquid Silicone Elastomer Composition For Material Having High Tear Strength
US20090042043A1 (en) * 2005-07-22 2009-02-12 Edouard Joseph Organosiloxane Compositions

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
GAQSIQ, SAC: "(GB/T 12828-2006) raw and unvalcanized compounded - Determination of plasticity number and recovery number -Parallel plate method", 29 December 2006 (2006-12-29)
NBS: "(GB/T265-1988 )Petroleum Products - Determination of Kinematic Viscosity and Calculation of Dynamic Viscosity", 1 April 1989 (1989-04-01)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9425605B2 (en) 2013-03-14 2016-08-23 Tyco Electronics Corporation Method for protecting a cable splice connection with a cover assembly
US10411456B2 (en) 2013-03-14 2019-09-10 Te Connectivity Corporation Cover assemblies and methods for covering electrical cables and connections
US10389103B2 (en) 2016-10-18 2019-08-20 Te Connectivity Corporation Breakout boot assemblies and methods for covering electrical cables and connections
CN111849046A (zh) * 2020-07-31 2020-10-30 上海蓝昊电气江苏有限公司 一种耐高温电缆用半导电外屏蔽材料
CN111849046B (zh) * 2020-07-31 2022-05-06 上海蓝昊电气江苏有限公司 一种耐高温电缆用半导电外屏蔽材料

Also Published As

Publication number Publication date
CN103361022A (zh) 2013-10-23
CN103361022B (zh) 2015-01-28

Similar Documents

Publication Publication Date Title
WO2013153501A1 (fr) Colle d'étanchéité en caoutchouc de silicone utilisée dans des accessoires de câble moyenne et haute tension, et accessoires de câble
JP5804948B2 (ja) 電力ケーブル気中終端接続部及び電力ケーブル気中終端接続部の製造方法
US5801332A (en) Elastically recoverable silicone splice cover
US8637773B2 (en) Electric insulation device and an electric device provided therewith
JP4917164B2 (ja) 電力ケーブル部材
CN1441695A (zh) 凝胶组合物
JPS6136868B2 (fr)
JP7070751B2 (ja) 高誘電絶縁性シリコーンゴム組成物及び電界緩和層
US6235992B1 (en) Electric device with silicone insulating filler
JP2016520675A (ja) アクリレートゴムシール材
CA2577002C (fr) Composition d'elastomere de silicone liquide pour fabriquer un materiau a haute resistance au dechirement
BR112019012297A2 (pt) composição semicondutora curável
CN110350450A (zh) 具有提高的热导率的电缆附件
JP6888593B2 (ja) ミラブル型シリコーンゴム組成物及び電界緩和層
JP5338036B2 (ja) 電気レオロジーゲル素子および電気レオロジーゲルの製造方法
WO2015110139A1 (fr) Câble électrique haute tension
JP5622241B2 (ja) 電力ケーブル気中終端接続部及び電力ケーブル気中終端接続部の製造方法
JP7197671B1 (ja) 電力ケーブル用絶縁性樹脂組成物、電力ケーブルおよび電力ケーブル接続部
CA3218659A1 (fr) Procede d'injection dans un cable bloque a torons
CN116218419A (zh) 电缆线芯导电密封材料及其制备方法、电缆附件
KR20210114977A (ko) 비옴성 조성물, 케이블 접속용 유닛, 및 케이블 접속용 유닛의 제조 방법
JPH08289454A (ja) ゴムモールドストレスコーン
KR20170081333A (ko) 케이블의 종단접속함용 절연유
HU197763B (en) Electric insulating material composition based on silicone rubber
EP2876650A1 (fr) Caoutchouc de revêtement externe pour un isolant de polymère

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13726276

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13726276

Country of ref document: EP

Kind code of ref document: A1