WO2012133161A1 - Adhésif photodurcissable, plaque de polarisation, et élément optique stratifié - Google Patents

Adhésif photodurcissable, plaque de polarisation, et élément optique stratifié Download PDF

Info

Publication number
WO2012133161A1
WO2012133161A1 PCT/JP2012/057475 JP2012057475W WO2012133161A1 WO 2012133161 A1 WO2012133161 A1 WO 2012133161A1 JP 2012057475 W JP2012057475 W JP 2012057475W WO 2012133161 A1 WO2012133161 A1 WO 2012133161A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizer
adhesive
polarizing plate
protective film
formula
Prior art date
Application number
PCT/JP2012/057475
Other languages
English (en)
Japanese (ja)
Inventor
悦夫 久米
岩田　智
Original Assignee
住友化学株式会社
株式会社Adeka
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社, 株式会社Adeka filed Critical 住友化学株式会社
Priority to KR1020137028370A priority Critical patent/KR101979467B1/ko
Priority to CN201280015670.XA priority patent/CN103443236B/zh
Publication of WO2012133161A1 publication Critical patent/WO2012133161A1/fr

Abstract

Cette invention concerne un adhésif photodurcissable pour coller un film protecteur comprenant une résine transparente sur un polariseur comprenant un film de résine alcool polyvinylique, l'adhésif photodurcissable contenant 100 parties en poids d'un composant durcissable par voie photocationique (A) et 1 à 10 parties en poids d'un amorceur de polymérisation photocationique (B), le composant durcissable par voie photocationique (A) contenant les composés (A1)-(A3) suivants dans les quantités suivantes par rapport à sa quantité totale : 60 à 75 % en poids d'un composé diépoxy alicyclique (A1) représenté par la formule (I) ; 5 à 35 % en poids d'un composé diglycidylique (A2) représenté par la formule (II) ; et 2 à 15 % en poids d'un composé époxy monofonctionnel (A3) représenté par la formule (III).
PCT/JP2012/057475 2011-03-29 2012-03-23 Adhésif photodurcissable, plaque de polarisation, et élément optique stratifié WO2012133161A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020137028370A KR101979467B1 (ko) 2011-03-29 2012-03-23 광 경화성 접착제, 편광판 및 적층 광학 부재
CN201280015670.XA CN103443236B (zh) 2011-03-29 2012-03-23 光固化性粘合剂、偏振片和层叠光学构件

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011-072906 2011-03-29
JP2011072906A JP5677883B2 (ja) 2011-03-29 2011-03-29 光硬化性接着剤、偏光板および積層光学部材

Publications (1)

Publication Number Publication Date
WO2012133161A1 true WO2012133161A1 (fr) 2012-10-04

Family

ID=46930885

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/057475 WO2012133161A1 (fr) 2011-03-29 2012-03-23 Adhésif photodurcissable, plaque de polarisation, et élément optique stratifié

Country Status (5)

Country Link
JP (1) JP5677883B2 (fr)
KR (1) KR101979467B1 (fr)
CN (1) CN103443236B (fr)
TW (1) TWI582200B (fr)
WO (1) WO2012133161A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015034228A (ja) * 2013-08-08 2015-02-19 株式会社Adeka エネルギー線感受性組成物
WO2017070552A1 (fr) 2015-10-23 2017-04-27 Sharp Gary D Filtre optique avec accentuation de couleurs

Families Citing this family (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102155921B1 (ko) * 2013-02-20 2020-09-14 스미또모 가가꾸 가부시키가이샤 광경화성 접착제, 및 그것을 이용한 편광판, 적층 광학 부재 및 액정 표시 장치
US20160252660A1 (en) 2013-10-29 2016-09-01 Sumitomo Chemical Company, Limited Polarizing plate
KR101719883B1 (ko) * 2013-12-25 2017-03-24 도아고세이가부시키가이샤 광 경화성 접착제 조성물, 편광판과 그 제조법, 광학 부재 및 액정 표시 장치
JP6488125B2 (ja) * 2013-12-26 2019-03-20 日東電工株式会社 積層偏光フィルム、その製造方法、積層光学フィルムおよび画像表示装置
JP2015206967A (ja) * 2014-04-23 2015-11-19 住友化学株式会社 複合偏光板の製造方法
KR20160006403A (ko) 2014-07-09 2016-01-19 동우 화인켐 주식회사 접착제 조성물 및 이를 포함하는 편광판
WO2016052244A1 (fr) * 2014-09-29 2016-04-07 株式会社Adeka Adhésif photodurcissable, et plaque de polarisation, élément optique stratifié et dispositif d'affichage à cristaux liquides utilisant cet adhésif
CN104432973B (zh) * 2014-11-25 2016-09-14 东莞市莞信企业管理咨询有限公司 一种鞋面贴
CN105739003B (zh) * 2014-12-26 2019-12-24 住友化学株式会社 偏振板
WO2017048079A1 (fr) * 2015-09-15 2017-03-23 주식회사 엘지화학 Film protecteur de polariseur, plaque polarisante comprenant celui-ci, et dispositif d'affichage à cristaux liquides comprenant la plaque polarisante
JP6232486B2 (ja) * 2016-01-19 2017-11-15 住友化学株式会社 光学積層体の製造方法
JP6408046B2 (ja) * 2016-02-17 2018-10-17 住友化学株式会社 光硬化性接着剤、並びにそれを用いた偏光板及び積層光学部材
WO2018016396A1 (fr) 2016-07-21 2018-01-25 住友化学株式会社 Plaque polarisante
JP2018159911A (ja) * 2017-01-27 2018-10-11 住友化学株式会社 偏光板及び画像表示装置
CN111876092B (zh) 2017-09-28 2022-05-27 日东电工株式会社 增强薄膜
KR20240088752A (ko) 2021-09-28 2024-06-20 닛토덴코 가부시키가이샤 편광 필름, 화상 표시 장치 및 편광 필름의 제조 방법

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004143222A (ja) * 2002-10-22 2004-05-20 Sekisui Chem Co Ltd 光カチオン重合性粘着型接着剤
JP2004245925A (ja) * 2003-02-12 2004-09-02 Sumitomo Chem Co Ltd 偏光板、その製造法、光学部材及び液晶表示装置
JP2004245924A (ja) * 2003-02-12 2004-09-02 Sumitomo Chem Co Ltd 偏光板、その製造方法、光学部材及び液晶表示装置
JP2008257199A (ja) * 2007-03-15 2008-10-23 Sumitomo Chemical Co Ltd 光硬化性接着剤、該光硬化性接着剤を用いた偏光板およびその製造方法、光学部材および液晶表示装置
JP2012007080A (ja) * 2010-06-25 2012-01-12 Toyo Ink Sc Holdings Co Ltd 偏光板形成用光硬化性接着剤及び偏光板

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3454437B2 (ja) * 1992-10-02 2003-10-06 ナショナル スターチ アンド ケミカル インベストメント ホールディング コーポレイション 低粘度無溶媒の一液型エポキシ樹脂接着性組成物
JP2004155954A (ja) * 2002-11-07 2004-06-03 Mitsubishi Chemicals Corp 光硬化性組成物及びその製造方法、並びに硬化物
JP4063099B2 (ja) * 2003-02-13 2008-03-19 日産自動車株式会社 金属ベルトの製造方法および製造時の支持治具
JP5221893B2 (ja) * 2007-05-07 2013-06-26 協立化学産業株式会社 積層フィルムの製造方法
JP5557281B2 (ja) * 2009-06-26 2014-07-23 住友化学株式会社 偏光板及びそれを用いた積層光学部材

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2004143222A (ja) * 2002-10-22 2004-05-20 Sekisui Chem Co Ltd 光カチオン重合性粘着型接着剤
JP2004245925A (ja) * 2003-02-12 2004-09-02 Sumitomo Chem Co Ltd 偏光板、その製造法、光学部材及び液晶表示装置
JP2004245924A (ja) * 2003-02-12 2004-09-02 Sumitomo Chem Co Ltd 偏光板、その製造方法、光学部材及び液晶表示装置
JP2008257199A (ja) * 2007-03-15 2008-10-23 Sumitomo Chemical Co Ltd 光硬化性接着剤、該光硬化性接着剤を用いた偏光板およびその製造方法、光学部材および液晶表示装置
JP2012007080A (ja) * 2010-06-25 2012-01-12 Toyo Ink Sc Holdings Co Ltd 偏光板形成用光硬化性接着剤及び偏光板

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015034228A (ja) * 2013-08-08 2015-02-19 株式会社Adeka エネルギー線感受性組成物
WO2017070552A1 (fr) 2015-10-23 2017-04-27 Sharp Gary D Filtre optique avec accentuation de couleurs
EP3365711A4 (fr) * 2015-10-23 2019-07-10 Gary D. Sharp Filtre optique avec accentuation de couleurs

Also Published As

Publication number Publication date
JP5677883B2 (ja) 2015-02-25
TW201245382A (en) 2012-11-16
CN103443236B (zh) 2016-06-29
TWI582200B (zh) 2017-05-11
JP2012208250A (ja) 2012-10-25
CN103443236A (zh) 2013-12-11
KR101979467B1 (ko) 2019-05-16
KR20140020978A (ko) 2014-02-19

Similar Documents

Publication Publication Date Title
JP5677883B2 (ja) 光硬化性接着剤、偏光板および積層光学部材
JP5855947B2 (ja) 光硬化性接着剤、それを用いた偏光板および積層光学部材
TWI654273B (zh) 光硬化性接著劑，以及使用該接著劑之偏光板、積層光學構件與液晶顯示裝置
JP6802708B2 (ja) 光硬化性接着剤、並びにそれを用いた偏光板、積層光学部材及び液晶表示装置
JP6408101B2 (ja) 光硬化性接着剤、並びにそれを用いた偏光板及び積層光学部材
JP2011028234A (ja) 偏光板及びそれを用いた積層光学部材
JP5827483B2 (ja) 光硬化性接着剤を使用した偏光板および積層光学部材
JP2016118779A (ja) 光硬化性接着剤、それを用いた偏光板および積層光学部材
JP5596207B2 (ja) 光硬化性接着剤組成物、偏光板とその製造法、光学部材及び液晶表示装置
JP7375506B2 (ja) 光硬化性接着剤、偏光板および積層光学部材
TWI819142B (zh) 光硬化性接著劑、偏光板及積層光學構件
JP5966310B2 (ja) 偏光板及びそれを用いた積層光学部材
JP2013205720A (ja) 偏光板及びそれを用いた積層光学部材
JP2017122883A (ja) 光硬化性接着剤、並びにそれを用いた偏光板、積層光学部材及び液晶表示装置
JP6777399B2 (ja) 光硬化性接着剤、並びにそれを用いた偏光板及び積層光学部材
CN107090259B (zh) 光固化性胶粘剂、以及使用其的偏振板及层叠光学构件
TWI721078B (zh) 光硬化性接著劑，以及使用該接著劑之偏光板及積層光學構件
JP2017122882A (ja) 光硬化性接着剤、並びにそれを用いた偏光板及び積層光学部材
JP2018199806A (ja) 接着剤組成物及び偏光板

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12764155

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20137028370

Country of ref document: KR

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 12764155

Country of ref document: EP

Kind code of ref document: A1