WO2011118746A1 - Procédé de fabrication de nanofibres cellulosiques - Google Patents

Procédé de fabrication de nanofibres cellulosiques Download PDF

Info

Publication number
WO2011118746A1
WO2011118746A1 PCT/JP2011/057283 JP2011057283W WO2011118746A1 WO 2011118746 A1 WO2011118746 A1 WO 2011118746A1 JP 2011057283 W JP2011057283 W JP 2011057283W WO 2011118746 A1 WO2011118746 A1 WO 2011118746A1
Authority
WO
WIPO (PCT)
Prior art keywords
cellulose
dispersion
raw material
oxidized
cellulose nanofiber
Prior art date
Application number
PCT/JP2011/057283
Other languages
English (en)
Japanese (ja)
Inventor
志穂 勝川
宮脇　正一
裕 阿部
知章 小柳
Original Assignee
日本製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本製紙株式会社 filed Critical 日本製紙株式会社
Priority to JP2012507077A priority Critical patent/JPWO2011118746A1/ja
Publication of WO2011118746A1 publication Critical patent/WO2011118746A1/fr

Abstract

La présente invention concerne un procédé de fabrication d'un liquide de dispersion très concentré à base de nanofibres cellulosiques qui possède une fluidité et une transparence élevées, à basse énergie et à haut rendement. Particulièrement, en présence (1) d'un composé N-oxyle et (2) de bromures, d'iodures, ou d'un mélange de ces composants, un matériau de départ cellulosique est oxydé dans de l'eau en utilisant un agent oxydant pour préparer un matériau de départ cellulosique oxydé, et en présence de cellulase et/ou d'hémicellulase, un homogénéisateur à ultra-haute pression est utilisé pour réaliser la défibration/dispersion à une pression supérieure ou égale à 100 MPa.
PCT/JP2011/057283 2010-03-26 2011-03-25 Procédé de fabrication de nanofibres cellulosiques WO2011118746A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2012507077A JPWO2011118746A1 (ja) 2010-03-26 2011-03-25 セルロースナノファイバーの製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2010-072264 2010-03-26
JP2010072264 2010-03-26

Publications (1)

Publication Number Publication Date
WO2011118746A1 true WO2011118746A1 (fr) 2011-09-29

Family

ID=44673288

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2011/057283 WO2011118746A1 (fr) 2010-03-26 2011-03-25 Procédé de fabrication de nanofibres cellulosiques

Country Status (2)

Country Link
JP (1) JPWO2011118746A1 (fr)
WO (1) WO2011118746A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2013047218A1 (fr) * 2011-09-30 2013-04-04 日本製紙株式会社 Procédé de fabrication de nanofibres de cellulose
JP2014009414A (ja) * 2012-06-29 2014-01-20 Nippon Paper Industries Co Ltd セルロースナノファイバーの製造方法
JP2014055323A (ja) * 2012-09-12 2014-03-27 Toppan Printing Co Ltd 金属／セルロース複合化微細繊維、その製造方法、ならびに金属／セルロース複合化微細繊維を含む透明導電膜
JP2014114332A (ja) * 2012-12-06 2014-06-26 Kao Corp セルロースナノファイバーの製造方法
JP2016501926A (ja) * 2012-11-03 2016-01-21 ウーペーエム−キュンメネ コーポレイションＵＰＭ−Ｋｙｍｍｅｎｅ Ｃｏｒｐｏｒａｔｉｏｎ ナノフィブリル化セルロースの製造方法
JP2016535123A (ja) * 2013-10-15 2016-11-10 レンツィング アクチェンゲゼルシャフト セルロース懸濁物、その調製方法、及び使用
JP2018059217A (ja) * 2016-10-03 2018-04-12 大王製紙株式会社 セルロースナノファイバーの製造方法
WO2020085479A1 (fr) * 2018-10-26 2020-04-30 王子ホールディングス株式会社 Composition contenant de la cellulose fibreuse fine et procédé de fabrication correspondant
US10731298B2 (en) 2012-06-15 2020-08-04 University Of Maine System Board Of Trustees Release paper and method of manufacture
US20220002442A1 (en) * 2018-10-16 2022-01-06 Oji Holdings Corporation Fibrous cellulose, fibrous cellulose dispersion, and production method for fibrous cellulose
EP4230658A1 (fr) * 2022-02-16 2023-08-23 Fundación Centro Technológico de Investigación Multisectorial Procédé d'obtention de nanocellulose

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008001728A (ja) * 2006-06-20 2008-01-10 Asahi Kasei Corp 微細セルロース繊維
JP2008169497A (ja) * 2007-01-10 2008-07-24 Kimura Chem Plants Co Ltd ナノファイバーの製造方法およびナノファイバー
WO2009122982A1 (fr) * 2008-03-31 2009-10-08 日本製紙株式会社 Additif destiné à la fabrication du papier et papier contenant cet additif
WO2010116826A1 (fr) * 2009-03-30 2010-10-14 日本製紙株式会社 Procédé pour la production de nanofibres de cellulose

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2008001728A (ja) * 2006-06-20 2008-01-10 Asahi Kasei Corp 微細セルロース繊維
JP2008169497A (ja) * 2007-01-10 2008-07-24 Kimura Chem Plants Co Ltd ナノファイバーの製造方法およびナノファイバー
WO2009122982A1 (fr) * 2008-03-31 2009-10-08 日本製紙株式会社 Additif destiné à la fabrication du papier et papier contenant cet additif
WO2010116826A1 (fr) * 2009-03-30 2010-10-14 日本製紙株式会社 Procédé pour la production de nanofibres de cellulose

Cited By (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5285197B1 (ja) * 2011-09-30 2013-09-11 日本製紙株式会社 セルロースナノファイバーの製造方法
CN103827146A (zh) * 2011-09-30 2014-05-28 日本制纸株式会社 纤维素纳米纤维的制造方法
WO2013047218A1 (fr) * 2011-09-30 2013-04-04 日本製紙株式会社 Procédé de fabrication de nanofibres de cellulose
US9365973B2 (en) 2011-09-30 2016-06-14 Nippon Paper Industries Co., Ltd. Method for producing cellulose nanofibers
CN103827146B (zh) * 2011-09-30 2016-09-07 日本制纸株式会社 纤维素纳米纤维的制造方法
US10731298B2 (en) 2012-06-15 2020-08-04 University Of Maine System Board Of Trustees Release paper and method of manufacture
JP2014009414A (ja) * 2012-06-29 2014-01-20 Nippon Paper Industries Co Ltd セルロースナノファイバーの製造方法
JP2014055323A (ja) * 2012-09-12 2014-03-27 Toppan Printing Co Ltd 金属／セルロース複合化微細繊維、その製造方法、ならびに金属／セルロース複合化微細繊維を含む透明導電膜
US9797093B2 (en) 2012-11-03 2017-10-24 Upm-Kymmene Corporation Method for producing nanofibrillar cellulose
JP2016501926A (ja) * 2012-11-03 2016-01-21 ウーペーエム−キュンメネ コーポレイションＵＰＭ−Ｋｙｍｍｅｎｅ Ｃｏｒｐｏｒａｔｉｏｎ ナノフィブリル化セルロースの製造方法
JP2014114332A (ja) * 2012-12-06 2014-06-26 Kao Corp セルロースナノファイバーの製造方法
JP2016535123A (ja) * 2013-10-15 2016-11-10 レンツィング アクチェンゲゼルシャフト セルロース懸濁物、その調製方法、及び使用
JP2018059217A (ja) * 2016-10-03 2018-04-12 大王製紙株式会社 セルロースナノファイバーの製造方法
JP7219533B2 (ja) 2016-10-03 2023-02-08 大王製紙株式会社 セルロースナノファイバーの製造方法
US20220002442A1 (en) * 2018-10-16 2022-01-06 Oji Holdings Corporation Fibrous cellulose, fibrous cellulose dispersion, and production method for fibrous cellulose
US11945884B2 (en) * 2018-10-16 2024-04-02 Oji Holdings Corporation Fibrous cellulose, fibrous cellulose dispersion, and production method for fibrous cellulose
WO2020085479A1 (fr) * 2018-10-26 2020-04-30 王子ホールディングス株式会社 Composition contenant de la cellulose fibreuse fine et procédé de fabrication correspondant
JPWO2020085479A1 (ja) * 2018-10-26 2021-10-07 王子ホールディングス株式会社 微細繊維状セルロース含有組成物およびその製造方法
JP7355028B2 (ja) 2018-10-26 2023-10-03 王子ホールディングス株式会社 微細繊維状セルロース含有組成物およびその製造方法
EP4230658A1 (fr) * 2022-02-16 2023-08-23 Fundación Centro Technológico de Investigación Multisectorial Procédé d'obtention de nanocellulose
WO2023156575A1 (fr) 2022-02-16 2023-08-24 Fundación Centro Tecnológico De Investigación Multisectorial Procédé d'obtention de nanocellulose

Also Published As

Publication number Publication date
JPWO2011118746A1 (ja) 2013-07-04

Similar Documents

Publication Publication Date Title
JP5178931B2 (ja) セルロースナノファイバーの製造方法
WO2011118746A1 (fr) Procédé de fabrication de nanofibres cellulosiques
JP5285197B1 (ja) セルロースナノファイバーの製造方法
JP5330882B2 (ja) セルロースゲル分散液の製造方法
WO2010116826A1 (fr) Procédé pour la production de nanofibres de cellulose
WO2011118748A1 (fr) Procédé de production de nanofibres cellulosiques
WO2012132903A1 (fr) Procédé de production de nanofibres en cellulose
JP5329279B2 (ja) セルロースナノファイバーの製造方法
JP5381338B2 (ja) セルロースナノファイバーの製造方法
JP5731253B2 (ja) セルロースナノファイバーの製造方法
JP2010235679A (ja) セルロースナノファイバーの製造方法
JP2009263652A (ja) セルロースナノファイバーの製造方法
WO2013137140A1 (fr) Procédé de production d'un liquide de dispersion de nanofibres de cellulose modifiées par un anion
JP5179616B2 (ja) セルロースナノファイバーの製造方法
JP5404131B2 (ja) セルロースナノファイバーの製造方法
JP6405751B2 (ja) 微小セルロースの製造方法
JP2018100383A (ja) カルボキシル化セルロースナノファイバーの製造方法
JPWO2012132663A1 (ja) セルロースナノファイバーの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11759550

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2012507077

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11759550

Country of ref document: EP

Kind code of ref document: A1