Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
  • C09J133/02—Homopolymers or copolymers of acids; Metal or ammonium salts thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
  • C08L33/02—Homopolymers or copolymers of acids; Metal or ammonium salts thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
  • C08L33/24—Homopolymers or copolymers of amides or imides
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J133/00—Adhesives based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides, or nitriles thereof; Adhesives based on derivatives of such polymers
  • C09J133/24—Homopolymers or copolymers of amides or imides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/02—Polymer mixtures characterised by other features containing two or more polymers of the same C08L -group

Definitions

• the present invention relates to a composition that may be used as a pressure sensitive adhesive.
• PSA Pressure sensitive adhesives
• the removable adhesive must provide sufficient tack to quickly fix the adhesive to the desired substrate, adequate peel strength to prevent damage of the surface when the adhesive is removed, and have the appropriate cohesive strength to control the transfer of adhesive to the substrate.
• Cohesive strength must also be controlled so to limit the cold flow of the adhesive on a surface, a process which leads to an undesirable building of peel strength over time.
• the cohesive strength of a PSA may be improved in a variety of ways. For example, cohesive strength may be enhanced through the covalent crosslinking of the adhesive.
• Some types of chemical crosslinkers are thermally activated and thus cannot be used with hot melt processable PSAs.
• To covalently crosslink hot melt coated PSAs one typically must use a post-coating radiation crosslinking process such as one initiated by ultraviolet or electron beam radiation. Such processes require expensive equipment.
• the present application is directed to a non-aqueous composition.
• composition comprises a blend of an acidic copolymer derived from a first group of monomers comprising at least one acidic monomer and the acidic copolymer is substantially free of basic monomer, and a basic copolymer derived from a second group of monomers comprising at least one basic monomer.
• the basic copolymer comprises an amide functionality.
• the application is directed to a non-aqueous composition
• a non-aqueous composition comprising a blend of an acidic copolymer derived from a first group of monomers comprising at least one acidic monomer, and a basic copolymer derived from a second group of monomers comprising at least one basic monomer and the basic copolymer is substantially free of acidic monomer.
• the basic copolymer comprises an amide functionality.
• the application is directed to a non-aqueous pressure sensitive adhesive composition
• a non-aqueous pressure sensitive adhesive composition comprising an acidic (meth)acrylic copolymer having a glass transition temperature (Tg) less than 0°C, which is derived from a first group of monomers comprising at least one acidic monomer, and a basic (meth)acrylic copolymer having a Tg less than 0°C, which is derived from a second group of monomers comprising at least one basic monomer.
• the basic copolymer comprises an amide functionality.
• the application is directed to a composition
• a composition comprising a blend of an acidic copolymer derived from a first group of monomers comprising at least one acidic monomer, and a basic copolymer derived from a second group of monomers comprising at least one basic monomer.
• the composition comprises a minimum of 0.10 moles of acid/base pairs per kilogram of composition. Additionally, the composition comprises between 10% and 90%> by weight of the acidic copolymer and between 10%> and 90%) by weight of the basic copolymer.
• an "acidic copolymer” is a polymer that has an electron accepting group and may be derived from at least one acidic monomer and may have at least one non-acidic copolymerizable monomer (i.e., a monomer that can not be titrated with a base).
• at least one copolymerizable monomer is a (meth)acrylate monomer such as an alkyl (meth)acrylate monomer.
• the acidic copolymer may optionally be derived from other copolymerizable monomers, such as vinyl monomers and basic monomers, as long as the resultant copolymer can still be titrated with a base.
• the acidic copolymer is substantially free of basic monomer.
• the acidic copolymer is substantially free of basic monomer if it has less than 0.5% by weight basic monomer in the chain, for example 0%.
• a “basic copolymer” is a polymer that has an electron donating group and may be derived from at least one basic monomer and may have at least one nonbasic
• copolymerizable monomer i.e., a monomer that cannot be titrated with an acid.
• Other monomers can be copolymerized with the basic monomers (e.g., acidic monomers, vinyl monomers, and (meth)acrylate monomers), as long as the basic copolymer retains its basicity (i.e., it can still be titrated with an acid).
• at least one copolymerizable monomer is a (meth)acrylate monomer such as an alkyl (meth)acrylate monomer.
• the basic copolymer is substantially free of acidic monomer
• the basic copolymer is substantially free of acidic monomer if it has less than 0.5% by weight acidic monomer in the chain, for example 0%.
• the acidic and the basic copolymers have a low Tg.
• a low Tg is a Tg of less than or equal to 0°C. Such a low Tg generally allows for the copolymers to behave as pressure sensitive adhesives.
• the adhesive compositions may be a pressure sensitive adhesive.
• Pressure sensitive adhesives are well known to one of ordinary skill in the art to possess properties including the following: (1) aggressive and permanent tack, (2) adherence with no more than finger pressure, (3) sufficient ability to hold onto an adherend, and (4) sufficient cohesive strength to be removed cleanly from the adherend.
• Materials that have been found to function well as PSAs include polymers designed and formulated to exhibit the requisite viscoelastic properties resulting in a desired balance of tack, peel adhesion, and shear holding power.
• the adhesive composition is non-aqueous. Generally, this allows for a
• composition of 100% solids or non-aqueous solvent blends Surfactants are therefore also generally not present in the adhesive composition.
• the composition is hot melt processable, for example by extrusion.
• Useful acidic monomers include, but are not limited to, those selected from ethylenically unsaturated carboxylic acids, ethylenically unsaturated sulfonic acids, ethylenically unsaturated phosphonic acids, and mixtures thereof.
• Such compounds include those such as acrylic acid, methacrylic acid, itaconic acid, fumaric acid, crotonic acid, citraconic acid, maleic acid, oleic acid, B-carboxy ethyl acrylate, 2- sulfoethyl methacrylate, styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, vinyl phosphonic acid, and the like, and mixtures thereof.
• Acidic monomers of the present invention are typically the ethylenically unsaturated carboxylic acids.
• acidic monomers include the ethylenically unsaturated sulfonic acids and ethylenically unsaturated phosphonic acids. Sulfonic and phosphonic acids generally provide a stronger interaction with a basic polymer. This stronger interaction can lead to greater improvements in cohesive strength, as well as higher temperature resistance and solvent resistance of the adhesive.
• the basic monomer of the present application may comprise amide functionality.
• the basic monomer may also comprise amino or other nitrogen containing functionality.
• Exemplary basic monomers include N, N dimethyl (meth)acrylamide (NNDMA); N,N- diethyl (meth)acrylamide; ⁇ , ⁇ -dimethylaminopropyl methacrylamide (DMAPMAm); ⁇ , ⁇ -diethylaminopropyl methacrylamide (DEAPMAm); N,N-dimethylaminoethyl acrylamide (DMAEAm); ⁇ , ⁇ -dimethylaminoethyl methacrylamide (DMAEMAm); N,N- diethylaminoethyl acrylamide (DEAEAm); ⁇ , ⁇ -diethylaminoethyl methacrylamide (DEAEMAm); N-vinyl formamide, (meth)acrylamide; N-methyl acrylamide, N-ethyl acrylamide; ⁇ , ⁇ -dimethylaminoethyl acrylate (DMAEA); ⁇ , ⁇ -diethylaminoethyl acrylate (DEAEA
• tertiary amino- functionalized styrene e.g., 4-(N,N-dimethylamino)-styrene (DMAS), 4-(N,N- diethylamino)-styrene (DEAS)
• DMAS 4-(N,N-dimethylamino)-styrene
• DEAS 4-(N,N- diethylamino)-styrene
• N-vinyl pyrrolidone N-vinyl caprolactam
• acrylonitrile acrylonitrile
• the polymers herein can be prepared by any conventional free radical
• the polymerization method including solution, radiation, bulk, dispersion, emulsion, and suspension processes.
• the monomers along with a suitable inert organic solvent, are charged into a four-neck reaction vessel that is equipped with a stirrer, a thermometer, a condenser, an addition funnel, and a temperature controller.
• a crosslinking additive may be incorporated into the blend.
• additives may be added to the resultant adhesive composition provided the additive causes no adverse affect to the desired properties, such as optical clarity and environmental stability over time.
• compatible tackifiers and/or plasticizers may be added to aid in optimizing the ultimate tack and peel properties of the PSA.
• useful tackifiers include, but are not limited to, rosin, rosin derivatives, polyterpene resins, coumarone-indene resins, and the like.
• Plasticizers which may be added to the adhesive of the invention may be selected from a wide variety of commercially available materials. In each case, the added plasticizer must be compatible with the PSA.
• Representative plasticizers include polyoxyethylene aryl ether, dialkyl adipate, 2-ethylhexyl diphenyl phosphate, t-butylphenyl diphenyl phosphate, 2- ethylhexyl adipate, toluenesulfonamide. dipropylene glycol dibenzoate, polyethylene glycol dibenzoate, polyoxypropylene aryl ether, dibutoxyethoxyethyl formal, and dibutoxyethoxyethyl adipate. UV stabilizers as known in the art may also be added.
• the adhesive composition may be included in an adhesive article comprising a backing and an adhesive layer upon the backing.
• the adhesive article additionally includes a release liner on the adhesive layer opposite the backing.
• the adhesive article may be manufactured using extrusion technology, including extrusion coating of the adhesive onto the liner or the backing or by coextruding a first extrudable feedstock in contact with a second extrudable feedstock to form a coextruded film.
• the first extrudable feedstock comprises the pressure sensitive adhesive.
• the second extrudable feedstock comprises a backing material or a release material.
• the coextruded film then comprises an adhesive layer comprising the pressure sensitive adhesive and either a backing layer or a release layer.
• additional feedstocks are added on one or both sides of the first or second feedstock.
• a third extrudable feedstock may be used to make an adhesive layer comprising a backing, an adhesive layer and a release layer.
• the backing layer may be, for example, a graphic film such as polyvinyl chloride or an olefmic graphic film substrate like that described in U.S. 6,589,636 (Emslander, et al.) or a tape backing such as ethylene acrylic acid copolymer or another layer comprising a release agent. Additional backing layers could include films used as labelstock, graphic protection films and antigraffiti films.
• Coextrusion is a known method of manufacturing films.
• Coextrusion means, for the present application, the simultaneous melt processing of multiple molten streams and the combination of such molten streams into a single unified structure, or coextruded film, for example from a single extrusion die.
• Adhesive articles have been manufactured with extrusion technology as shown, for example, in U.S. Patent 5,660,922 (coextruding double sided adhesive tapes) and U.S. Patent Number 6,777,053. It is also known to extrude release material blends to form a release film. See, for example, U.S. Patent Application 2004-0127121.
• a coextruded film is generally a composite of all the molten feedstocks placed within the co-extrusion process.
• the resulting co-extruded films are generally multilayer.
• the layers are in contact with one another in the molten state. In certain embodiments, the layers are in contact throughout the extrusion, for example they are in contact as soon as they are molten.
• the coextruded film may further be processed, for example by orientation.
• orientation of a film is biaxial orientation.
• Biaxial orientation involves stretching the film in two directions perpendicular to each other, generally in the down- web direction and cross-web direction.
• the freshly extruded molten film is fed onto a chill roll to produce a quenched amorphous film which is briefly heated and stretched in the down- web direction, and then conducted through a tenter frame where it is stretched transversely with moderate heating.
• Down-web direction stretching may be accomplished by passing between two sets of nip rolls, the second set rotating at a higher speed than the first.
• the release layer comprises a release agent.
• the release layer may also comprise other polymers, blended with the release agent.
• Suitable release agent include, for example, this disclosed in Attorney Docket Number 65043WO003 (PCT Application Number US2009/068632) and in Attorney Docket Number 64700WO003 (PCT Application Number US2009/054322) incorporated herein by reference.
• At least the adhesive composition is subject to post extrusion processing, either in the coextruded film or after separation from the release liner.
• the adhesive may be crosslinked. Examples
• the peel adhesion strength and removability were evaluated by the following method.
• Adhered samples were aged at 65°C for 7 days and then allowed to return to a controlled room temperature (72°F, 50% relative humidity) before testing.
• the strips were peeled from the panel using an Instron universal testing machine with a crosshead speed of 12 in/min. The peel force was measured and the panels were observed to see if visible adhesive residue remained on the panel.
• the photoinitiator used was a 2,2-dimethoxy-l,2-diphenyl-ethanone, available under the tradename IRGACURE 651 from Ciba Specialty Chemicals Incorporated, Tarrytown, NY.
• the antioxidant used was an octadecyl 3,5-di-(tert)-butyl-4-hydroxyhydrocinnamate, available under the tradename IRGANOX 1076 from Ciba Specialty Chemicals
• the acrylic polymer compositions were used to prepare different blends compositions using a twin screw extruder.
• the Polymer A and Polymer B pouches were fed to separate ports on the twin screw extruder using two BonnotTM extruders coupled with gear pumps to feed the two different polymers at a controlled ratio.
• the total extruder throughput was about 10 lb/hr (5 kg/hr).
• the screw speed was 180-200 rpm.
• the extruder was an 18 mm co-rotating twin screw extruder with a sequence of mixing and conveying sections, operating at a temperature of 350°F (175°C).
• the compounded mixture exiting the twin screw extruder was collected as a "rope" of adhesive on a release liner.
• the liner was wrapped around the adhesive rope to allow storage and transport of the adhesive composition.
• These compounded adhesive compositions were then reprocessed by feeding the rope to a single screw extruder with a 3 ⁇ 4" diameter screw and extruded through a flat die to coat the adhesive between a release liner and a cast vinyl film having a thickness of 50 microns.
• the cast vinyl film had been previously primed by coating with a solution of an acrylic polymer modified with 2-methylaziridine in ethyl acetate.
• the number of moles of acid per kg of blend is calculated using the following formula: (lOOOg x % A polymer x % acid in A polymer) / FW of acid monomer.
• FW stands for the formula weight.
• the relevant formula weights are shown in Table 5.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Adhesive Tapes (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Compositions Of Macromolecular Compounds (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=44278017

Family Applications (1)

Country Status (6)

Cited By (1)

Families Citing this family (9)

Family Cites Families (38)

• 2010
  • 2010-01-15 US US12/688,476 patent/US8791207B2/en active Active
• 2011
  • 2011-01-12 EP EP11733303.9A patent/EP2524003A4/en not_active Withdrawn
  • 2011-01-12 JP JP2012549024A patent/JP5801823B2/ja not_active Expired - Fee Related
  • 2011-01-12 CN CN201180010005.7A patent/CN102762656B/zh not_active Expired - Fee Related
  • 2011-01-12 WO PCT/US2011/020962 patent/WO2011088101A2/en not_active Ceased
  • 2011-01-12 BR BR112012017404A patent/BR112012017404A2/pt not_active Application Discontinuation

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events