Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F110/00—Homopolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F110/04—Monomers containing three or four carbon atoms
  • C08F110/06—Propene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/02—Carriers therefor
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07F—ACYCLIC, CARBOCYCLIC OR HETEROCYCLIC COMPOUNDS CONTAINING ELEMENTS OTHER THAN CARBON, HYDROGEN, HALOGEN, OXYGEN, NITROGEN, SULFUR, SELENIUM OR TELLURIUM
  • C07F3/00—Compounds containing elements of Groups 2 or 12 of the Periodic Table
  • C07F3/003—Compounds containing elements of Groups 2 or 12 of the Periodic Table without C-Metal linkages
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07F—ACYCLIC, CARBOCYCLIC OR HETEROCYCLIC COMPOUNDS CONTAINING ELEMENTS OTHER THAN CARBON, HYDROGEN, HALOGEN, OXYGEN, NITROGEN, SULFUR, SELENIUM OR TELLURIUM
  • C07F3/00—Compounds containing elements of Groups 2 or 12 of the Periodic Table
  • C07F3/02—Magnesium compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/02—Carriers therefor
  • C08F4/025—Metal oxides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/62—Refractory metals or compounds thereof
  • C08F4/64—Titanium, zirconium, hafnium or compounds thereof
  • C08F4/65—Pretreating the metal or compound covered by group C08F4/64 before the final contacting with the metal or compound covered by group C08F4/44
  • C08F4/652—Pretreating with metals or metal-containing compounds
  • C08F4/654—Pretreating with metals or metal-containing compounds with magnesium or compounds thereof

Definitions

• the present invention relates to a spherical magnesium halide adduct, and to a catalyst component and a catalyst prepared from the adduct as support and being useful in olefin polymerization, in particular propylene polymerization. More specifically, the present invention relates to a spherical magnesium halide adduct comprising at least three components: a magnesium halide, an alcohol and an o-alkoxy benzoate compound, to a catalyst component comprising a reaction product of the adduct with a titanium compound and optionally an internal electron donor compound, and to the use of the catalyst component.
• An adduct of a magnesium halide and an alcohol is often used as the active magnesium halide support, and reacts with a titanium halide and an electron donor compound to give a spherical catalyst component, which, together with a cocatalyst and optionally an external electron donor compound, constitutes a catalyst.
• a catalyst When used in olefin polymerization, in particular in propylene polymerization, such a catalyst exhibits a relatively high polymerization activity and a higher stereospecificity.
• Known magnesium halide/alcohol adducts comprise generally binary components: magnesium di chloride and an alcohol. Some of known alcohol adducts further comprise a minor amount of water. Such alcohol adducts may be prepared by known processes, such as spray drying processes, spray cooling processes, high-pressure extruding processes, or high-speed stirring processes.
• the magnesium dichloride/alcohol adducts are described in, for example, US 4,421,674, US 4,469,648, WO 8707620, WO 9311166, US 5,100,849, US 6,020,279, US 4,399,054, EP 0 395 383, US 6,127,304 and US 6,323,152.
• the technique as disclosed in Chinese Patent ZL02136543.1 and CN1563112A introduces an internal electron donor well-known in the art, such as a phthalate, in the preparation of the support so as to form a spherical "magnesium dichloride-alcohol-phthalate" multi-component support, which then reacts with titanium tetrachloride to form a catalyst component.
• an internal electron donor well-known in the art, such as a phthalate
• the spherical multi-component support is likely viscous during the preparation thereof, it is difficult to form spherical particles having a desired particle diameter (the disclosed spherical supports have average particle sizes, D50, in the range of from 70 to 200 microns).
• the catalyst when used in propylene polymerization, the catalyst exhibits a catalytic activity of at most 406gPP/gcat. Therefore, the catalyst is not satisfied.
• Chinese patent application CNl 01050245 A discloses a spherical adduct support having a general formula of MgX 2 mROH nE pH 2 O, wherein E is a gem-dihydrocarbyloxy hydrocarbon compound.
• the support has a narrower particle size distribution and the average particle size of the support can be easily controlled.
• the catalyst component prepared by reacting the adduct support with a titanium compound has a good hydrogen response when used in olefin polymerization, in particular in propylene polymerization, and the resultant polymer has a good particle morphology.
• the catalyst component is used in propylene polymerization at a higher hydrogen concentration, its stereospecificity, especially the isotacticity index of the obtained polymer having a higher melt index, needs to be further enhanced.
• Chinese patent application CN85101441A discloses a process for the polymerization of an alpha monoolefin in the presence of certain supported coordination catalyst systems which comprise (a) a procatalyst, (b) a cocatalyst, and (c) a selectivity control agent, wherein (a) is a solid composition comprising magnesium dichloride, titanium tetrachloride, and an electron donor; (b) is an aluminium trialkyl; and (c) is a combination of a strong selectivity control agent and a weak selectivity control agent.
• certain supported coordination catalyst systems which comprise (a) a procatalyst, (b) a cocatalyst, and (c) a selectivity control agent, wherein (a) is a solid composition comprising magnesium dichloride, titanium tetrachloride, and an electron donor; (b) is an aluminium trialkyl; and (c) is a combination of a strong selectivity control agent and a weak selectivity control agent.
• Said strong selectivity control agent may be an alkoxy benzoate, preferably a p-alkoxy benzoate, and the weak selectivity control agent is an ether or a tertiary amine.
• the resultant polymers have lower isotacticity indices, when either the alkoxy benzoate alone or the combination of the strong selectivity control agent and the weak selectivity control agent is used.
• Chinese patent application CN1743347A discloses the incorporation of o-alkoxybenzoate compounds as internal electron donor into olefin polymerization catalyst components. Said patent application discloses that, when a combination of an o-alkoxybenzoate compound and a phthalate compound is used as internal electron donor, the hydrogen response of the resultant catalyst can be improved. However, by using such a catalyst, the obtained polypropylene having a high melt index will have a lower isotacticity index.
• catalysts for olefin polymerization which will exhibit a relatively high polymerization activity, a higher stereospecificity and the performance that can obtain higher isotactic index polypropylene with higher melt index at a higher hydrogen concentration, and which will give a polymer having a good particle morphology and a higher bulk density.
• the inventors made diligently studies and, as a result, they have surprisingly found that incorporating an o-alkoxybenzoate compound, either formed in situ or added as such, into a magnesium halide/alcohol adduct support gives excellent results, in comparison with the case where no o-alkoxybenzoate compound is used or an o-alkoxybenzoate compound is introduced during the preparation of a solid catalyst component from a magnesium halide/alcohol adduct support.
• the resultant supports have good particle morphology, and when used in olefin polymerization, especially in propylene polymerization, the catalysts prepared from such o-alkoxybenzoate-containing supports exhibit a relatively high stereospecificity, even at a higher hydrogen concentration provided for preparing a polymer having a higher melt index.
• Such a polymer having a higher melt index and a higher isotacticity index will have good mechanical properties and a good processibility, and thus is desired.
• the catalysts prepared from the o- alkoxybenzoate-containing supports exhibit higher polymerization activities, and the resulting polymers have good particle morphology and less fines so that the catalysts are quite suitable for the industrial scale production of polypropylene.
• an object of the invention is to provide a spherical magnesium halide adduct comprising a magnesium halide, an alcohol and an o-alkoxybenzoate compound.
• Another object of the invention is to provide a process for preparing the spherical magnesium halide adduct according to the invention.
• Still another object of the invention is to provide a titanium-containing catalyst component for olefin polymerization, which comprises a reaction product of the spherical magnesium halide adduct of the invention, a titanium compound, and optionally an internal electron donor.
• Still another object of the invention is to provide a catalyst for olefin polymerization, comprising a reaction product of
• polymerization intends to encompass homopolymerization and copolymerization.
• polymer intends to encompass homopolymer, copolymer and terpolymer.
• catalyst component intends to means main catalyst component or procatalyst, which, together with a conventional cocatalyst, for example an alkyl alumimium, and optionally an external electron donor compound, constitutes the catalyst for olefin polymerization.
• catalyst is synonymous with the term “catalyst system”, and comprises a catalyst component, a cocatalyst, and optionally an external electron donor compound.
• the present invention provides a magnesium halide adduct represented by the following formula (I):
• X is chlorine, bromine, a C 1 -Ci 2 alkoxy, a C 3 -Ci 0 cycloalkoxy or a C 6 -Ci 0 aryloxy, with the proviso that at least one X is chlorine or bromine;
• R is a Ci-Ci 2 alkyl, a C 3 -C] 0 cycloalkyl or a C 6 -Ci 0 aryl;
• E is an o-alkoxybenzoate compound represented by the formula (II):
• Ri and R 2 groups are independently a Ci-Ci 2 linear or branched alkyl, a C 3 -Ci 0 cycloalkyl, a C 6 -Ci 0 aryl, a C 7 -Ci 0 alkaryl or an C 7 -Ci 0 aralkyl, the Ri and R 2 groups are identical to or different from the R group;
• m is in a range of from 1.0 to 5.0, preferably from 1.5 to 3.5;
• n is in a range of from O.OOlto 0.5, preferably from 0.005 to 0.2;
• p is in a range of from 0 to 0.8.
• X is preferably chlorine.
• examples of the magnesium halide MgX 2 useful in the preparation of the magnesium halide adduct include, but are not limited to, magnesium dichloride, magnesium dibromide, phenoxy magnesium chloride, isopropoxy magnesium chloride, and butoxy magnesium chloride, with magnesium dichloride being preferred.
• the magnesium halides may be used alone or in combination.
• the alcohols useful in the preparation of the magnesium halide adduct may be represented by a formula ROH, wherein R is a Ci-Ci 2 alkyl, a C 3 -Ci 0 cycloalkyl or a C 6 -Ci 0 aryl, preferably a Ci-C 4 alkyl.
• alcohols examples include, but are not limited to, methanol, ethanol, n- propanol, iso-propanol, n-butanol, iso-butanol, n-pentanol, iso-pentanol, n-hexanol, n-octanol, 2-ethylhexanol, ethylene glycol and propylene glycol.
• Ri and R 2 are independently a Ci-Ci 2 linear or branched alkyl, a C 3 - Ci 0 cycloalkyl, a C 6 -Ci 0 aryl, a C 7 -Ci 0 alkaryl or a C 7 -Ci 0 aralkyl, such as methyl, ethyl, propyl, isopropyl, butyl, iso-butyl, t-butyl, pentyl, hexyl, iso-pentyl, cyclopentyl, cyclohexyl, phenyl, tolyl, indenyl, benzyl or phenyl ethyl.
• Ri and R 2 are independently a Ci-C 6 linear or branched alkyl, a C 3 -C 6 cycloalkyl, or a C 6 -Cj 0 aryl. More preferably, Ri and R 2 are independently methyl, ethyl, propyl, isopropyl, butyl, iso-butyl, t-butyl, or pentyl.
• Examples of the o-alkoxybenzoate compounds represented by the formula (II) include methyl o-methoxybenzoate, ethyl o-methoxybenzoate, n-propyl o-methoxybenzoate, isopropyl o-methoxybenzoate, n-butyl o-methoxybenzoate, isobutyl o-methoxybenzoate, methyl o- ethoxybenzoate, ethyl o-ethoxybenzoate, n-propyl o-ethoxybenzoate, isopropyl o- ethoxybenzoate, n-butyl o-ethoxybenzoate, and isobutyl o-methoxybenzoate.
• the magnesium halide adduct according to the invention has a composition represented by the formula (I),
• Ri is methyl, ethyl, n-propyl, isopropyl, n-butyl or iso-butyl
• R 2 is identical to or different from R, and is methyl, ethyl, n-propyl, isopropyl, n-butyl, or iso-butyl
• p is as defined above.
• the above adduct may be prepared by processes well-known in the art, such as spray drying processes, spray cooling processes, high-pressure extruding processes, high-speed stirring processes, or super-gravity rotary bed processes (such as the process as described in CN1580136A).
• a magnesium halide, an alcohol, and an o-alkoxybenzoate or its precursor react at first with each other in the presence or in the absence of an inert liquid medium at an elevated temperature, with the final temperature being high enough to melt the reaction mixture, and preferably in the range of from 100°C to 140 0 C.
• the inert liquid medium is generally an inert aliphatic hydrocarbon solvent, such as kerosene, paraffin oil, vaseline oil, white oil, hexane, and heptane, and when necessary, contains optionally an organic silicon compound, such as an organic silicon oil, for example, dimethyl silicone oil or the like, and/or a surfactant.
• an organic silicon compound such as an organic silicon oil, for example, dimethyl silicone oil or the like, and/or a surfactant.
• the resulting melt is solidified in a cooling medium to form solid particles
• the cooling medium may be an inert hydrocarbon solvent having a relatively low boiling point, such as pentane, hexane, heptane, gasoline, petroleum ether, and the like, and may be controlled at a temperature of from -60 °C to 30 °C, preferably from -40 0 C to 0 °C, prior to its contacting with the magnesium halide adduct melt stream.
• the magnesium halide adduct according to the invention may be prepared by a process comprising the steps of
• a closed reactor mixing the magnesium halide, the alcohol, the o-alkoxybenzoate or its precursor (e.g., o-alkoxy benzoyl halide, such as chloride) and an inert liquid medium, and heating the resultant mixture to a temperature of from 100 to 140 °C while stirring, to form a melt of a magnesium halide adduct,
• the o-alkoxybenzoate or its precursor e.g., o-alkoxy benzoyl halide, such as chloride
• magnesium halide is added in an amount of from 0.1 to 1.0 mol/liter of the inert liquid medium, and the alcohol and the o-alkoxybenzoate or its precursor are added in an amount of from 1 to 5 moles and from 0.001 to 0.5 moles, respectively, with respect to one mole of the magnesium halide;
• the application of the shearing action may be accomplished by a conventional method, such as a high-speed stirring process (see, for example, CN 1330086), a spraying process (see, for example, US 6,020,279), a super-gravity rotary bed process (see, for example, CN 1580136A), or an emulsification apparatus process (see, for example, CN 1463990A);
• a high-speed stirring process see, for example, CN 1330086
• a spraying process see, for example, US 6,020,279
• a super-gravity rotary bed process see, for example, CN 1580136A
• an emulsification apparatus process see, for example, CN 1463990A
• the cooling medium is as described above.
• the above-prepared spherical adduct particles may be used in the preparation of catalyst components for olefin polymerization.
• the present invention provides a titanium-containing catalyst component for olefin polymerization, which comprises a reaction product of (1) the spherical magnesium halide adduct of the invention, (2) a titanium compound, and optionally (3) an internal electron donor compound.
• the titanium compound may be selected from those represented by formula TiX 3 or Ti(OR 3 ) 4-m X m , in which R 3 (s) is/are independently Ci-C 14 aliphatic hydrocarbyl group, X(s) is/are independently F, Cl, Br or I, and m is an integer of from 1 to 4.
• titanium compound examples include, but are not limited to, titanium tetrachloride, titanium tetrabromide, titanium tetraiodide, tetrabutoxy titanium, tetraethoxy titanium, tributoxy titanium chloride, dibutoxy titanium dichloride, butoxy titanium trichloride, triethoxy titanium chloride, diethoxy titanium dichloride, ethoxy titanium trichloride, titanium trichloride, and mixtures thereof, with titanium tetrachloride being preferred.
• the titanium-containing catalyst component for olefin polymerization according to the invention may be prepared by methods known in the art, for example, by reacting the particulate magnesium halide adduct with a titanium compound.
• the titanium- containing catalyst component is prepared by a method comprising the steps of: suspending the magnesium halide adduct of the invention in chilled titanium tetrachloride or a mixture of titanium tetrachloride and an inert solvent, with the temperature of the liquid being generally in a range of from -30°C to 0°C, preferably from -20°C to -10°C; then heating the resulting mixture to a temperature of from 40°C to 130 0 C, preferably from 6O 0 C to 120 0 C, and maintaining at that temperature for 0.5 to 2.0 hours; and then filtering off the liquid and recovering the solids.
• Such a treatment with titanium tetrachloride may be performed for one or more times, and preferably for 2 to 4 times.
• the inert solvent is preferably an aliphatic or aromatic hydrocarbon, such as hexane, heptane, octane, decane, toluene, and the like.
• At least one internal electron donor compound may optionally be used to treat the magnesium halide adduct.
• Use of internal electron donor compounds in catalyst components for olefin polymerization is well known in the art.
• the incorporation of an internal electron donor compound in a catalyst component for propylene polymerization may be quite necessary, in order to obtain propylene polymers having high isotacticity indices. All internal electron-donor compounds commonly used in the art can be used in the present invention.
• Suitable internal electron donor compounds include esters, ethers, ketones, amines, silanes, and the like. Esters of aliphatic and aromatic mono- and poly-basic carboxylic acids, esters of diols, and di-ethers are preferred.
• esters of aliphatic and aromatic mono- and poly-basic carboxylic acids include, for example, benzoates, phthalates, malonates, succinates, glutarates, pivalates, adipates, sebacates, maleates, naphthalene dicarboxylates, trimellitates, benzene-l,2,3-tricarboxylates, pyromellitates and carbonates.
• Examples include ethyl benzoate, diethyl phthalate, di-iso-butyl phthalate, di-n-butyl phthalate, di-iso-octyl phthalate, di-n-octyl phthalate, diethyl malonate, dibutyl malonate, diethyl 2,3-di-iso- ⁇ ropylsuccinate, di-iso-butyl 2,3-di-isopropylsuccinate, din-butyl 2,3-diisopropylsuccinate, dimethyl 2,3-di-isopropylsuccinate, di-iso-butyl 2,2- dimethylsuccinate, di-iso-butyl 2-ethyl-2-methylsuccinate, diethyl 2-ethyl-2-methylsuccinate, diethyl adipate, dibutyl adipate, diethyl sebacate, dibutyl sebacate, diethy
• Ri to R 6 and R 1 to R 2n which are identical or different, are hydrogen, halogen, or optionally substituted linear or branched Ci-C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 mono-ring or multi-ring aryl, C 7 -C 20 alkylaryl, C 7 -C 20 arylalkyl, C 2 -Ci 0 alkenyl, or C 2 -Ci 0 ester group, with the proviso that Ri and R 2 are not hydrogen, R 3 to R 6 and R 1 to R 2n optionally comprise one or more heteroatoms, which are selected from the group consisting of nitrogen, oxygen, sulfur, silicon, phosphorus and halogen, replacing for carbon or hydrogen or the both, and one or more ofR 3 to R ⁇ and R 1 to R 2n may be linked to form a ring; and n is an integer ranging from O to 10, as disclosed in CN1436766, all relevant contents of which are incorporated herein by
• ester compounds of diols the preferred are compounds of the formula (IV),
• Ri-R 6 groups are as defined for the formula (III); R's are identical or different, and represent hydrogen, halogen, linear or branched Ci-C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 7 - C 20 alkylaryl, or C 7 -C 20 arylalkyl.
• ester compounds of diols include: propan-l,3-diol dibenzoate, 2-methyl- propan-l,3-diol dibenzoate, 2-ethyl-propan-l,3-diol dibenzoate, 2-propyl-propan-l,3-diol dibenzoate, 2-butyl-propan-l,3-diol dibenzoate, 2,2-dimethyl-propan-l,3-diol dibenzoate, (R)-I- phenyl-propan-l,3-diol dibenzoate, (S)-l-phenyl-propan-l,3-diol dibenzoate, 1,3-diphenyl- propan-l,3-diol dibenzoate, l,3-diphenyl-2-methyl-propan-l,3-diol dibenzoate, 1,3-diphenyl- propan-l,3-di
• ester compounds of diols are disclosed in detail in CN1453298A, CN1436796A, CN1436766A, WO 03/068828 and WO 03/068723, all relevant contents of which are incorporated herein by reference.
• the preferred ether compounds include 1,3-diether compounds represented by the formula (VI):
• R 1 , R 11 , R 1 ", R ⁇ , R v and R VI are independently selected from the group consisting of hydrogen, halogen, linear or branched Ci-C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 7 -C 20 alkylaryl and C 7 -C 20 arylalkyl;
• R v ⁇ and R vi ⁇ are independently selected from the group consisting of linear or branched C 1 -C 20 alkyl, C 3 -C 20 cycloalkyl, C 6 -C 20 aryl, C 7 -C 20 alkylaryl and C 7 -C 20 arylalkyl; and two or more of R 1 to R V1 groups are optionally bonded to each other to form a ring.
• Those 1,3-diethers wherein R v ⁇ and R v ⁇ " are independently Ci-C 4 alkyl are preferred.
• di-ether compounds include: 2-(2-ethyl hexyl)-l,3-dimethoxypropane, 2- isopropyl-l,3-dimethoxypropane, 2-butyl-l,3-dimethoxypropane, 2-sec-butyl-l,3- dimethoxypropane, 2-cyclohexyl-l,3-dimethoxypropane, 2-phenyl-l,3-dimethoxypropane, 2-(2- phenyl ethyl)- 1 ,3-dimethoxypropane, 2-(2-cyclohexyl ethyl)- 1 ,3-dimethoxypropane, 2-(p- chlorophenyl)-l ,3-dimethoxypropane, 2-(diphenylmethyl)-l ,3-dimethoxypropane, 2,2-di- cyclohexyl- 1 ,3-dimethoxypropane, 2,2-
• di-ether compounds are disclosed in detail in CN1020448C, CN 100348624C and CNl 141285A, all relevant contents of which are incorporated herein by reference.
• the titanium compound is used in an amount of from 5 to 50 moles, with respect to one mole of magnesium halide in the magnesium halide adduct; and the internal electron donor compound is used in an amount of from 0 to 0.8 moles, preferably from 0.01 to 0.5 moles, with respect to one mole of magnesium halide in the magnesium halide adduct.
• the present invention provides a catalyst for olefin polymerization, comprising a reaction product of the following components:
• the preferred are tri ethyl aluminum, triisobutyl aluminum, tri-n-butyl aluminum, tri-n-hexyl aluminum, tri-n-octyl aluminum, alkyl aluminum chlorides, such as AlEt 2 Cl, etc.
• These alkylaluminum compounds can be used alone or in combination, hi general, the alkylaluminum compound(s) is/are used in such an amount that molar ratio of Al/Ti is in a range of from 1 to 1000; and
• an external electron donor compound such as mono- or multi-functional carboxylic acids, carboxylic anhydrides, esters of carboxylic acids, ketones, ethers, alcohols, lactones, organic phosphorus compounds, and organic silicon compounds, in an amount ranging from 0.005 to 0.5 moles, preferably from 0.01 to 0.25 moles, with respect to one mole of the alkylaluminum compound.
• Preferred external electron donor compounds include silicon compounds of formula R' a R 2 bSi(OR 3 ) c , wherein a and b are independently an integer of from 0 to 2, c is an integer of from 1 to 3, and the sum of (a+b+c) is 4; R 1 , R 2 and R 3 are independently Ci-Ci 8 hydrocarbyl optionally containing heteroatom(s).
• R 1 and R 2 are selected from the group consisting of branched alkyl, alkenyl, cycloalkyl or aryl having 3 to 10 carbon atoms and optionally containing heteroatom(s), and R 3 is a Ci-Ci 0 alkyl, especially methyl, are particularly preferred.
• silicon compounds include cyclohexyl methyl dimethoxy silane, diisopropyl dimethoxy silane, di-n- butyl dimethoxy silane, di-iso-butyl dimethoxy silane, diphenyl dimethoxy silane, methyl tert- butyl dimethoxy silane, dicyclopentyl dimethoxy silane, 2-ethylpiperidino tert-butyl dimethoxy silane, l,l,l-trifluoro-propan-2-yl 2-ethylpiperidino dimethoxy silane and 1,1,1-trifluoro- propan-2-yl methyl dimethoxy silane.
• silicon compounds wherein a is 0, c is 3, R 2 is a branched alkyl or cycloalkyl optionally containing heteroatom(s), and R 3 is methyl are also preferred.
• silicon compounds include cyclohexyl trimethoxy silane, tert- butyl trimethoxy silane and tert-hexyl trimethoxy silane.
• the alkyl aluminium cocatalyst b) and the optional external electron donor compound c) can contact and react with the active component a) separately or as a mixture.
• the polymerization of olefin(s) can be carried out in liquid phase of the liquid olefin monomer(s) or a solution of the olefin monomer(s) in an inert solvent, or in gas phase, or in a combination of gas phase and liquid phase, according to the processes known per se.
• the polymerization is generally carried out at a temperature of from 0°C to 150°C, preferably from 60°C to 100°C, and at a normal or higher pressure.
• Isotacticity index of polymers measured by heptane extraction method carried out as follows: 2 g of a dry polymer sample is extracted with boiling heptane in an extractor for 6 hours, then the residual substance is dried to constant weight, and the ratio of the weight of the residual polymer (g) to 2 is regarded as isotacticity index.
• Particle size distribution average particle size and particle size distribution of the particulate magnesium halide adducts are measured on Masters Sizer Model 2000 (manufactured by Malvern Instruments Co., Ltd.). Example 1
• the mixture was added into 300 ml of dimethyl silicone oil (having a viscosity of 250-350 mm 2 /s at 25 0 C, obtained from the Second Chemical Factory of Beijing, Beijing) preheated to 120 °C in a 1000ml reactor, and stirred at 1600 rpm for 15 min. Then the mixture was discharged into 2 liters of hexane which had previously been cooled to -30 °C in a 3000ml reactor. After filtering off the liquid, the solid was washed with hexane for five times and then dried under vacuum, to give 50 g of spherical magnesium dichloride adduct, the D50 of which was 75 microns.
• dimethyl silicone oil having a viscosity of 250-350 mm 2 /s at 25 0 C, obtained from the Second Chemical Factory of Beijing, Beijing
• Example 2 The procedure as described in Example 1 was repeated, except for that the o- methoxybenzoyl chloride was not used in the preparation of the magnesium halide adduct. The results are shown in the Table 1 and Table 2 below.
• Example 2 The procedure as described in Example 1 was repeated, except for that l,3-dimethyl-l,3- propandiol dibenzoate was used to replace for the di-iso-butyl phthalate in the preparation of the catalyst component. The results are shown in the Table 1 and Table 2 below.
• a magnesium dichloride adduct was prepared by following the procedure as described in Example l .A, except for that o-methoxybenzoyl chloride was replaced with 2,2-di- methoxypropane.
• a spherical catalyst component was prepared by following the procedure as described in Example 1.B, except for that the magnesium dichloride adduct prepared above was used as the support.
• a catalyst component was prepared by following the procedure as described in

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)

Priority Applications (10)

Applications Claiming Priority (1)

Related Child Applications (2)

Publications (2)

Family

ID=43448857

Family Applications (1)

Country Status (9)

Cited By (6)

Families Citing this family (7)

Citations (9)

Family Cites Families (36)

• 2009
  • 2009-07-15 IN IN631DEN2012 patent/IN2012DN00631A/en unknown
  • 2009-07-15 ES ES09847203.8T patent/ES2478017T3/es active Active
  • 2009-07-15 SG SG2012002820A patent/SG177665A1/en unknown
  • 2009-07-15 JP JP2012519864A patent/JP5898073B2/ja active Active
  • 2009-07-15 WO PCT/CN2009/000796 patent/WO2011006278A1/en not_active Ceased
  • 2009-07-15 EP EP09847203.8A patent/EP2454290B1/en active Active
  • 2009-07-15 US US13/384,419 patent/US9499569B2/en active Active
  • 2009-07-15 BR BR112012000866-8A patent/BR112012000866B1/pt active IP Right Grant
  • 2009-07-15 KR KR1020127003788A patent/KR101541749B1/ko active Active
• 2016
  • 2016-10-13 US US15/292,467 patent/US10239969B2/en active Active

Patent Citations (9)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events