WO2010134501A1 - Couche poreuse et accumulateur - Google Patents

Couche poreuse et accumulateur Download PDF

Info

Publication number
WO2010134501A1
WO2010134501A1 PCT/JP2010/058309 JP2010058309W WO2010134501A1 WO 2010134501 A1 WO2010134501 A1 WO 2010134501A1 JP 2010058309 W JP2010058309 W JP 2010058309W WO 2010134501 A1 WO2010134501 A1 WO 2010134501A1
Authority
WO
WIPO (PCT)
Prior art keywords
graft polymer
polymer
slurry
porous film
particles
Prior art date
Application number
PCT/JP2010/058309
Other languages
English (en)
Japanese (ja)
Inventor
康尋 脇坂
真弓 福峯
裕次郎 豊田
Original Assignee
日本ゼオン株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本ゼオン株式会社 filed Critical 日本ゼオン株式会社
Priority to JP2011514408A priority Critical patent/JP5561276B2/ja
Publication of WO2010134501A1 publication Critical patent/WO2010134501A1/fr

Abstract

L'invention concerne une couche poreuse comprenant : des particules non conductrices et un polymère greffé ; une pâte pour une couche poreuse, qui comporte des particules non conductrices, un polymère greffé et un solvant ; et une électrode destinée à un accumulateur, qui est constituée d'un collecteur de courant, d'une couche de mélange d'électrode qui est amenée à adhérer à ce collecteur de courant et qui se compose d'un liant et d'un matériau actif d'électrode, ladite couche poreuse étant stratifiée sur la surface de la couche de mélange d'électrode. La couche poreuse peut présenter une grande dispersibilité des particules non conductrices et un bon niveau de maintien de la solution électrolytique, et en même temps, il est possible d'éviter très efficacement la survenue d'un court-circuit électrique ainsi que la contraction par refroidissement, et l'introduction de la couche poreuse permet d'obtenir d'excellentes propriétés à haute température et un excellent rendement.
PCT/JP2010/058309 2009-05-18 2010-05-17 Couche poreuse et accumulateur WO2010134501A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2011514408A JP5561276B2 (ja) 2009-05-18 2010-05-17 多孔膜及び二次電池

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009119443 2009-05-18
JP2009-119443 2009-05-18

Publications (1)

Publication Number Publication Date
WO2010134501A1 true WO2010134501A1 (fr) 2010-11-25

Family

ID=43126179

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/058309 WO2010134501A1 (fr) 2009-05-18 2010-05-17 Couche poreuse et accumulateur

Country Status (3)

Country Link
JP (1) JP5561276B2 (fr)
KR (1) KR101579639B1 (fr)
WO (1) WO2010134501A1 (fr)

Cited By (19)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2011040562A1 (fr) * 2009-09-30 2011-04-07 日本ゼオン株式会社 Membrane poreuse pour batterie secondaire et batterie secondaire
WO2012020737A1 (fr) * 2010-08-09 2012-02-16 日本ゼオン株式会社 Membrane poreuse pour batterie auxiliaire, procédé de fabrication et utilisation
WO2013154090A1 (fr) * 2012-04-13 2013-10-17 東レバッテリーセパレータフィルム株式会社 Film poreux multicouches, séparateur de cellule électrique et cellule électrique
JP2015041502A (ja) * 2013-08-22 2015-03-02 協立化学産業株式会社 非水系蓄電素子用コート剤組成物及び非水系蓄電素子
WO2015145967A1 (fr) * 2014-03-24 2015-10-01 日本ゼオン株式会社 Liant, composition et film poreux pour pile rechargeable à électrolyte non aqueux, et pile rechargeable à électrolyte non aqueux
WO2015198534A1 (fr) * 2014-06-27 2015-12-30 日本ゼオン株式会社 Composition pour couche fonctionnelle de pile rechargeable non aqueuse, couche fonctionnelle pour pile rechargeable non aqueuse, et pile rechargeable non aqueuse
JP2016004758A (ja) * 2014-06-19 2016-01-12 日本ゼオン株式会社 非水系二次電池多孔膜用バインダー組成物、非水系二次電池多孔膜用組成物、非水系二次電池用多孔膜および非水系二次電池
JP2016033921A (ja) * 2013-11-27 2016-03-10 旭化成イーマテリアルズ株式会社 蓄電デバイス用セパレータ、蓄電デバイス及びリチウムイオン二次電池
JP2016105398A (ja) * 2014-11-21 2016-06-09 三星エスディアイ株式会社Samsung SDI Co., Ltd. 二次電池用セパレータ（ｓｅｐａｒａｔｏｒ）及び二次電池
JP2016122648A (ja) * 2012-07-26 2016-07-07 旭化成株式会社 蓄電デバイス用セパレータ、積層体、及び多孔膜
JP2016534531A (ja) * 2013-11-06 2016-11-04 エルジー・ケム・リミテッド 電気化学素子用分離膜
JP2016213019A (ja) * 2015-05-01 2016-12-15 旭化成株式会社 蓄電デバイス用セパレータ、蓄電デバイス、及びリチウムイオン二次電池
WO2017094250A1 (fr) * 2015-11-30 2017-06-08 日本ゼオン株式会社 Composition pour une couche adhésive d'une batterie rechargeable non aqueuse, couche adhésive pour une batterie rechargeable non aqueuse et batterie rechargeable non aqueuse
WO2018181243A1 (fr) * 2017-03-30 2018-10-04 三井化学株式会社 Accumulateur au lithium-ion
CN111211277A (zh) * 2020-02-19 2020-05-29 重庆云天化纽米科技股份有限公司 一种pmma凝胶涂布隔膜的制备方法
JP2020170590A (ja) * 2019-04-01 2020-10-15 旭化成株式会社 蓄電デバイス用セパレータ、及びそれを用いた捲回体、リチウムイオン二次電池、並びに蓄電デバイス
CN113577554A (zh) * 2021-07-05 2021-11-02 溥畅(杭州)智能科技有限公司 一种分离式纤维基原电池及其制备方法
CN113871566A (zh) * 2021-09-18 2021-12-31 苏州清陶新能源科技有限公司 一种干法电极膜、其制备方法和应用
CN114507863A (zh) * 2021-03-10 2022-05-17 中国工程物理研究院电子工程研究所 一种钛材的表面处理方法及高温贮氢钛材

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101723993B1 (ko) * 2013-01-18 2017-04-07 (주)포스코켐텍 리튬 이차 전지용 음극 및 이의 제조 방법, 및 이를 포함하는 리튬 이차 전지
CN108448032B (zh) * 2017-02-16 2022-10-18 帝人株式会社 非水系二次电池用隔膜及非水系二次电池

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62274550A (ja) * 1986-05-19 1987-11-28 ダブリュー・アール・グレイス・アンド・カンパニー　―　コネチカット アルカリ電池系用のシ−ト材料、その製造法およびそれを用いたアルカリ電池
JPH05217571A (ja) * 1992-02-03 1993-08-27 Nitto Denko Corp 電池用セパレータ
JP2008004442A (ja) * 2006-06-23 2008-01-10 Hitachi Maxell Ltd リチウム二次電池用セパレータおよびリチウム二次電池
JP2008066094A (ja) * 2006-09-07 2008-03-21 Hitachi Maxell Ltd 電池用セパレータおよびリチウム二次電池

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0582114A (ja) * 1991-09-18 1993-04-02 Fuji Photo Film Co Ltd 二次電池
JP3371301B2 (ja) 1994-01-31 2003-01-27 ソニー株式会社 非水電解液二次電池
WO2005049318A1 (fr) * 2003-11-19 2005-06-02 Tonen Chemical Corporation Film microporeux composite et procede de production et d'utilisation de celui-ci
JP4649862B2 (ja) 2004-04-02 2011-03-16 パナソニック株式会社 リチウムイオン二次電池及びその製造方法
JP2008503049A (ja) 2004-07-07 2008-01-31 エルジー・ケム・リミテッド 有機無機複合多孔性フィルム及びこれを用いる電気化学素子
JP2008041581A (ja) * 2006-08-10 2008-02-21 Hitachi Maxell Ltd 巻回体電極群、角形二次電池およびラミネート形二次電池

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62274550A (ja) * 1986-05-19 1987-11-28 ダブリュー・アール・グレイス・アンド・カンパニー　―　コネチカット アルカリ電池系用のシ−ト材料、その製造法およびそれを用いたアルカリ電池
JPH05217571A (ja) * 1992-02-03 1993-08-27 Nitto Denko Corp 電池用セパレータ
JP2008004442A (ja) * 2006-06-23 2008-01-10 Hitachi Maxell Ltd リチウム二次電池用セパレータおよびリチウム二次電池
JP2008066094A (ja) * 2006-09-07 2008-03-21 Hitachi Maxell Ltd 電池用セパレータおよびリチウム二次電池

Cited By (33)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5742717B2 (ja) * 2009-09-30 2015-07-01 日本ゼオン株式会社 二次電池用多孔膜及び二次電池
JPWO2011040562A1 (ja) * 2009-09-30 2013-02-28 日本ゼオン株式会社 二次電池用多孔膜及び二次電池
WO2011040562A1 (fr) * 2009-09-30 2011-04-07 日本ゼオン株式会社 Membrane poreuse pour batterie secondaire et batterie secondaire
WO2012020737A1 (fr) * 2010-08-09 2012-02-16 日本ゼオン株式会社 Membrane poreuse pour batterie auxiliaire, procédé de fabrication et utilisation
US9496532B2 (en) 2010-08-09 2016-11-15 Zeon Corporation Porous membrane for secondary battery, production method therefor, and use thereof
WO2013154090A1 (fr) * 2012-04-13 2013-10-17 東レバッテリーセパレータフィルム株式会社 Film poreux multicouches, séparateur de cellule électrique et cellule électrique
CN104185551A (zh) * 2012-04-13 2014-12-03 东丽电池隔膜株式会社 层叠多孔膜、电池用隔膜以及电池
JPWO2013154090A1 (ja) * 2012-04-13 2015-12-17 東レバッテリーセパレータフィルム株式会社 積層多孔質膜、電池用セパレーター及び電池
JP2016122648A (ja) * 2012-07-26 2016-07-07 旭化成株式会社 蓄電デバイス用セパレータ、積層体、及び多孔膜
JP2015041502A (ja) * 2013-08-22 2015-03-02 協立化学産業株式会社 非水系蓄電素子用コート剤組成物及び非水系蓄電素子
US10505167B2 (en) 2013-11-06 2019-12-10 Lg Chem, Ltd. Separator for electrochemical device
JP2016534531A (ja) * 2013-11-06 2016-11-04 エルジー・ケム・リミテッド 電気化学素子用分離膜
JP2016033921A (ja) * 2013-11-27 2016-03-10 旭化成イーマテリアルズ株式会社 蓄電デバイス用セパレータ、蓄電デバイス及びリチウムイオン二次電池
JP2015185353A (ja) * 2014-03-24 2015-10-22 日本ゼオン株式会社 非水系二次電池多孔膜用バインダー、非水系二次電池多孔膜用組成物、非水系二次電池用多孔膜および非水系二次電池
WO2015145967A1 (fr) * 2014-03-24 2015-10-01 日本ゼオン株式会社 Liant, composition et film poreux pour pile rechargeable à électrolyte non aqueux, et pile rechargeable à électrolyte non aqueux
KR20160137516A (ko) 2014-03-24 2016-11-30 니폰 제온 가부시키가이샤 비수계 이차전지 다공막용 바인더, 비수계 이차전지 다공막용 조성물, 비수계 이차전지용 다공막 및 비수계 이차전지
US11807698B2 (en) 2014-03-24 2023-11-07 Zeon Corporation Binder for non-aqueous secondary battery porous membrane-use, composition for non-aqueous secondary battery porous membrane-use, porous membrane for non-aqueous secondary battery-use, and non-aqueous secondary battery
JP2016004758A (ja) * 2014-06-19 2016-01-12 日本ゼオン株式会社 非水系二次電池多孔膜用バインダー組成物、非水系二次電池多孔膜用組成物、非水系二次電池用多孔膜および非水系二次電池
WO2015198534A1 (fr) * 2014-06-27 2015-12-30 日本ゼオン株式会社 Composition pour couche fonctionnelle de pile rechargeable non aqueuse, couche fonctionnelle pour pile rechargeable non aqueuse, et pile rechargeable non aqueuse
JPWO2015198534A1 (ja) * 2014-06-27 2017-04-20 日本ゼオン株式会社 非水系二次電池機能層用組成物、非水系二次電池用機能層および非水系二次電池
JP2016105398A (ja) * 2014-11-21 2016-06-09 三星エスディアイ株式会社Samsung SDI Co., Ltd. 二次電池用セパレータ（ｓｅｐａｒａｔｏｒ）及び二次電池
JP2016213019A (ja) * 2015-05-01 2016-12-15 旭化成株式会社 蓄電デバイス用セパレータ、蓄電デバイス、及びリチウムイオン二次電池
WO2017094250A1 (fr) * 2015-11-30 2017-06-08 日本ゼオン株式会社 Composition pour une couche adhésive d'une batterie rechargeable non aqueuse, couche adhésive pour une batterie rechargeable non aqueuse et batterie rechargeable non aqueuse
CN110495044A (zh) * 2017-03-30 2019-11-22 三井化学株式会社 锂离子二次电池
JPWO2018181243A1 (ja) * 2017-03-30 2020-02-06 三井化学株式会社 リチウムイオン二次電池
EP3605713A4 (fr) * 2017-03-30 2020-12-23 Mitsui Chemicals, Inc. Accumulateur au lithium-ion
WO2018181243A1 (fr) * 2017-03-30 2018-10-04 三井化学株式会社 Accumulateur au lithium-ion
JP2020170590A (ja) * 2019-04-01 2020-10-15 旭化成株式会社 蓄電デバイス用セパレータ、及びそれを用いた捲回体、リチウムイオン二次電池、並びに蓄電デバイス
CN111211277A (zh) * 2020-02-19 2020-05-29 重庆云天化纽米科技股份有限公司 一种pmma凝胶涂布隔膜的制备方法
CN114507863A (zh) * 2021-03-10 2022-05-17 中国工程物理研究院电子工程研究所 一种钛材的表面处理方法及高温贮氢钛材
CN114507863B (zh) * 2021-03-10 2023-08-22 中国工程物理研究院电子工程研究所 一种钛材的表面处理方法及高温贮氢钛材
CN113577554A (zh) * 2021-07-05 2021-11-02 溥畅(杭州)智能科技有限公司 一种分离式纤维基原电池及其制备方法
CN113871566A (zh) * 2021-09-18 2021-12-31 苏州清陶新能源科技有限公司 一种干法电极膜、其制备方法和应用

Also Published As

Publication number Publication date
JP5561276B2 (ja) 2014-07-30
JPWO2010134501A1 (ja) 2012-11-12
KR101579639B1 (ko) 2015-12-22
KR20120027245A (ko) 2012-03-21

Similar Documents

Publication Publication Date Title
JP5561276B2 (ja) 多孔膜及び二次電池
JP5765228B2 (ja) 二次電池用多孔膜及び二次電池
JP5621772B2 (ja) 二次電池用電極及び二次電池
JP5742717B2 (ja) 二次電池用多孔膜及び二次電池
JP5549739B2 (ja) 二次電池多孔膜スラリー、二次電池多孔膜、二次電池電極、二次電池セパレーター及び二次電池
JP5605591B2 (ja) 二次電池多孔膜スラリー、二次電池多孔膜、二次電池電極、二次電池セパレーター、二次電池、及び二次電池多孔膜の製造方法
JP5522422B2 (ja) 二次電池多孔膜スラリー、二次電池多孔膜、二次電池電極、二次電池セパレーター及び二次電池
JP5867731B2 (ja) 二次電池多孔膜スラリー、二次電池多孔膜、二次電池電極、二次電池セパレーター、二次電池及び二次電池多孔膜の製造方法
JP5598472B2 (ja) 二次電池用多孔膜及び二次電池
JP5751414B2 (ja) 二次電池多孔膜用スラリー組成物
WO2012057324A1 (fr) Membrane poreuse de batterie secondaire, bouillie pour membrane poreuse de batterie secondaire, et batterie secondaire
KR20140004156A (ko) 이차 전지용 다공막, 이차 전지 다공막용 슬러리 및 이차 전지
WO2010024328A1 (fr) Membrane poreuse, électrode de batterie secondaire, et batterie secondaire au lithium ion
WO2010016476A1 (fr) Electrode pour batterie secondaire lithium-ion
WO2013147006A1 (fr) Membrane poreuse pour une pile rechargeable, bouillie pour membrane poreuse pour une pile rechargeable, particules non conductrices, électrode pour une pile rechargeable, séparateur pour une pile rechargeable et pile rechargeable

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10777734

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2011514408

Country of ref document: JP

ENP Entry into the national phase

Ref document number: 20117027357

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10777734

Country of ref document: EP

Kind code of ref document: A1