WO2010076864A1 - 圧電素子 - Google Patents

圧電素子 Download PDF

Info

Publication number
WO2010076864A1
WO2010076864A1 PCT/JP2009/070404 JP2009070404W WO2010076864A1 WO 2010076864 A1 WO2010076864 A1 WO 2010076864A1 JP 2009070404 W JP2009070404 W JP 2009070404W WO 2010076864 A1 WO2010076864 A1 WO 2010076864A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
piezoelectric
film
piezoelectric element
ceramic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2009/070404
Other languages
English (en)
French (fr)
Inventor
昌宣 鶴子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Brother Industries Ltd
Original Assignee
Brother Industries Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Brother Industries Ltd filed Critical Brother Industries Ltd
Publication of WO2010076864A1 publication Critical patent/WO2010076864A1/ja
Anticipated expiration legal-status Critical
Ceased legal-status Critical Current

Abstract

【課題】エアロゾルデポジション法により形成された薄膜を有しながら、膜剥離が発生しにくく、電気評価が良好であるので歩留りが改善されるとともに、優れた圧電特性を達成できる積層型圧電素子を提供すること。 【解決手段】基板の上に、第一層、第二層、及び第三層がこの順序で積層された四層構造の圧電素子において、第一層、第二層、及び第三層は、それぞれがエアロゾルデポジション法によって成膜されたセラミックス膜であり、第一層の弾性率は第二層の弾性率よりも大きく、第二層の弾性率は第三層の弾性率よりも大きい。第一層／第二層／第三層の具体的態様としては、ＺｒＯ２／ＰＺＴ／ＰＺＴ、Ａｌ２Ｏ３／ＺｒＯ２／ＰＺＴ、Ａｌ２Ｏ３／ＰＺＴ／ＰＺＴがある。

Description

圧電素子
　本発明は、エアロゾルデポジション法によって成膜したセラミックス薄膜を圧電膜として有する圧電素子に関する。
　インクジェットプリンタ等に用いられる圧電アクチュエータにおける圧電膜を形成する方法として、近年、エアロゾルデポジション法が注目されている。エアロゾルデポジション法は、気体中にセラミックス微粒子を分散することにより形成されるエアロゾルをノズルから噴射し、高速で基板表面に吹き付けることによって、上記基板上で微粒子を粉砕し堆積させてセラミックス薄膜を形成する成膜方法である。この成膜方法は、基板表面へのセラミックス微粒子の衝突で発生する局所的な衝撃エネルギーが開放することに起因したメカノケミカル反応の誘起によって起こる常温衝撃固化現象を利用しており、粒子衝突時の衝撃力を膜形成時の反応エネルギーとして作用させる成膜技術である。この成膜方法は常温で実施されるので、従来のセラミックス形成法において実施されていた９００℃以上での焼結プロセスが不要となる。そのため、寸法精度を考慮した薄膜設計を行う必要がなくなる。また、この成膜方法では微粒子の破砕によって緻密なナノ結晶組織を形成することができる。
　エアロゾルデポジション法を利用してステンレス基板上に直接圧電層を成膜する場合には、特許文献３に示されるように成膜後に比較的高温の加熱による粒成長アニール処理が行われる。しかしながら、この粒成長アニール処理によりステンレス中のＦｅやＣｒが圧電層に拡散し、圧電特性が低下してしまうことが知られている。なお、粒成長アニール処理とは、エアロゾルデポジション法により形成された薄膜を加熱して薄膜内の結晶粒を成長させて、薄膜の圧電特性等を向上させることを目的とした処理である。
　圧電特性の低下を防止するために、ステンレス基板と圧電層の間に、絶縁性セラミックス材料や、金属材料、導電性酸化物等からなる拡散防止層を設けることによって上述の拡散を防止することが特許文献１にて提案されている。
　さらに、エアロゾルデポジション法において基板のダメージを低減して積層体構造の機械的強度の低下を防ぐことを目的として、基板とエアロゾルデポジション法による堆積膜との間に、酸化物材料からなる中間膜を設けることが特許文献２にて提案されている。
特開２００６－２６１６５６号公報 特開２００１－１５２３６１号公報 特開２００７－８８４４９号公報
　しかしながらエアロゾルデポジション法により形成されたセラミックス膜を上述した圧電層及び拡散防止層として用いた場合には、粒成長アニール処理をおこなった後に、圧電層と拡散防止層との間の膜界面で膜剥離がきわめて発生しやすいという問題があった。また、たとえ膜剥離が発生しなくとも、製造した圧電素子にクラックやピンホールが形成されることにより圧電層を挟む一対の電極が導通して短絡し、圧電素子の歩留りが向上しないという問題もあった。これらに加えて、圧電素子の圧電特性についてもさらに改善することが望まれていた。
　そこで本発明は、圧電層及び拡散防止層として、エアロゾルデポジション法により形成されたセラミックス膜を有するものでありながら、上述した膜剥離や短絡が発生しにくい優れた圧電特性を達成できる積層型圧電素子を提供することを目的とする。
　本発明に係る圧電素子は、基板の上に、第一層、第二層、及び、圧電層である第三層がこの順序で積層された四層構造の圧電素子であって、第一層、第二層、及び第三層は、それぞれがエアロゾルデポジション法によって成膜されたセラミックス膜であり、第一層の弾性率は第二層の弾性率よりも大きく、第二層の弾性率は第三層の弾性率よりも大きいことを特徴とする。
　本発明によると、エアロゾルデポジション法により形成されたセラミックス膜を有しながらも、膜剥離が発生しにくく、電気評価が良好であるので歩留りが改善されるとともに、優れた圧電特性を達成できる積層型圧電素子を提供することができる。
本発明に係る圧電素子を製造する際に使用し得る、エアロゾルデポジション法に基づいた成膜装置の概略図である。 本発明に係る４層構造の圧電素子の層構造を示す概略図である。 実施例１～３で測定した、４層構造の圧電素子を構成する各層の弾性率を示すグラフである。 比較例１で測定した、３層構造の圧電素子を構成する各層の弾性率を示すグラフである。
　以下に、本発明の実施形態を図面に基づいて説明する。まずエアロゾルデポジション法に用いる成膜装置について説明する。この成膜装置は、キャリアガスに材料粒子を分散させてエアロゾルを発生させるためのエアロゾル生成器１と、内部で成膜を実施するためのチャンバ２とを備えている。
　エアロゾル生成器１には所定量の材料粒子が収納されており、キャリアガスが導入される。エアロゾル生成器１は、キャリアガス導入の際に巻き上げガスを発生させ、さらに下部から超音波加振装置を用いた振動を加えることによって、キャリアガスに材料粒子を分散させて、エアロゾルを発生する。前記キャリアガスとしては、例えば、ヘリウム、アルゴン等の不活性ガスや、窒素、空気、酸素等を使用することができる。
　エアロゾル生成器１の上部にはエアロゾル供給管３の一端が挿入されている。エアロゾル供給管３の他端はチャンバ２の内部に配置され、噴射ノズル４が接続されている。
　チャンバ２には、メカニカルブースターポンプとロータリーポンプ等が接続されており、これらのポンプはチャンバ２の内部を減圧できる。これによって、チャンバ２の内圧がエアロゾル生成器１の内圧と比較して低圧になる。そして、チャンバ２の内圧とエアロゾル生成器１の内圧との差圧によって、エアロゾル生成器１内で発生したエアロゾルがエアロゾル供給管３に吸い込まれ、噴射ノズル４に供給される。
　噴射ノズル４の内部の空洞は、内部を進行するに従い横断面積が減少していくような形状を有している。このため、噴射ノズル４の導入開口から噴射ノズル４の内部に進入したエアロゾルは、加速されたうえで、噴射ノズル４の射出開口から、エアロゾル流５として高速で基板７に吹き付けられる。基板７の表面に衝突した材料粒子が破砕し、堆積することによって、薄膜が形成される。
　チャンバ２の内部には、噴射ノズル４の射出開口の上方に、基板７を下面に取り付けるための保持手段としての基板ホルダー６が配置されている。基板ホルダー６は矩形板状である。基板ホルダー６は駆動手段としての駆動装置８によって水平姿勢でチャンバ２の天井からつり下げられている。駆動装置８は、基板ホルダー６を、図１での左右方向に駆動する。この左右方向での往復運動によって、基板７に対する走査成膜が行われる。この走査成膜によって、基板７の所定の広範な範囲に薄膜が形成される。
　成膜対象物である基板としては、代表的にはステンレス製の基板が挙げられるが、これに限定されず、例えば、他の金属、シリコン、半導体、樹脂等からなる基板でもよい。
　前記材料粒子を構成する材料、すなわちエアロゾルデポジション法により形成される薄膜の材料としては、代表的にはチタン酸ジルコン酸鉛（ＰＺＴ）が挙げられる。チタン酸ジルコン酸鉛は通常数μｍ程度の膜厚で所望の圧電効果を達成する材料として知られている。そのほか、圧電材料としては、チタン酸バリウム、チタン酸鉛、マグネシウムニオブ酸鉛（ＰＭＮ）、ニッケルニオブ酸鉛（ＰＮＮ）、亜鉛ニオブ酸鉛等を使用することができる。本発明では第三層を構成する材料として上述のような圧電材料を使用するが、第一層及び第二層を構成する材料としては、前記の圧電材料のほか、酸化アルミニウム、酸化ジルコニウム、シリカ、ムライト等の金属酸化物を使用することができる。
　材料粒子の粒径は、エアロゾルデポジション法に使用可能な粒径であればよく、例えば、０．５μｍ～５．０μｍ程度のものでよい。
　エアロゾルデポジション法により形成される薄膜の膜厚は通常、数μｍ～数十μｍ程度である。
　図２で示す本発明の圧電素子は、基板１４の上に第一層としての第一セラミックス層１１が積層されている。第一セラミックス層１１の上に第二層としての第二セラミックス層１２が積層されている。第二セラミックス層１２の上に下部電極１５が形成されている。下部電極１５の上に圧電アクチュエータの変形に貢献する圧電層である第三層としての第三セラミックス層１３が積層されている。第三セラミックス層１３の上に上部電極１６が積層されている。
　第一セラミックス層１１、第二セラミックス層１２、第三セラミックス層１３を構成するセラミックスとしては各種セラミックスの中から、上述した弾性率の関係を満足するものを選択すればよい。ただし、この積層体が圧電素子として機能するために、第三セラミックス層１３は圧電層とする必要がある。このため、少なくとも第三セラミックス層１３は圧電材料により構成される。第一セラミックス層１１及び第二セラミックス層１２については、圧電材料により構成されてもよいし、圧電材料以外のセラミックス材料により構成されてもよい。本発明では、各層が上述したエアロゾルデポジション法によって成膜されている。
　第二セラミックス層１２と第三セラミックス層１３との界面にある第二セラミックス層１２の表面には、全面にわたって下部電極１５が設けられている。下部電極１５は、アースされて常時グランド電位となるグランド電極として使用される。第三セラミックス層１３の上表面には、複数の独立した領域によって電極パターンとして構成されている上部電極１６が設けられている。上部電極１６は、個々の領域それぞれにリード部が接続され、リード部を介して駆動回路ＩＣに接続される。これによって上部電極１６は、駆動回路ＩＣによってグランド電位とグランド電位とは異なる電位が選択的に付与される駆動電極として使用される。これら電極層は、Ａｕ、Ｐｔ等の金属により構成されることが好ましい。
　本発明の圧電素子の具体的な製法を以下に説明する。まず、基板の表面に、上述したエアロゾルデポジション法により第一セラミックス層１１を形成する。次に、第一セラミックス層１１表面の粉体を除去したあと、第一セラミックス層１１の表面に、エアロゾルデポジション法により第二セラミックス層１２を形成する。次に、第二セラミックス層１２表面の粉体を除去したあと、第二セラミックス層１２の表面に、蒸着法やスパッタ法、あるいは金属粒子を含むペーストの塗布及び乾燥等によって、下部電極１５を成膜する。続いて、第一セラミックス層１１と第二セラミックス層１２の応力を開放するために、比較的低温（およそ５００℃程度）での加熱による応力開放アニール処理をおこなう。
　ここで応力開放アニール処理とは、エアロゾルデポジション法により形成された薄膜を加熱して、膜内に混入した成膜ガスおよび水分等を除去するとともに、薄膜の残留応力を開放させる目的で行われる処理である。
　前記の応力開放アニール処理のあと、下部電極１５の表面に、ふたたびエアロゾルデポジション法により圧電層である第三セラミックス層１３が形成される。表面の粉体の除去後、圧電層の結晶粒を成長させるため、比較的高温（およそ８００～９００℃程度）での加熱による粒成長アニール処理をおこなう。
　ここで粒成長アニール処理とは、エアロゾルデポジション法により形成された圧電層を加熱して、薄膜内の結晶粒の成長や、格子欠陥の修正を達成し、薄膜の圧電特性等を向上させる目的で行われる処理である。上述のとおり、エアロゾルデポジション法により形成された圧電層は、この粒成長アニール処理によって、その界面付近での弾性率がおおきく変化するが、本発明に係る層構成を採用することによって膜剥離等の問題を回避できる。
　最後に、第三セラミックス層１３の表面に、上部電極１６を形成する。上部電極１６を形成するには、マスキングをして蒸着法やスパッタ法を実施すればよい。あるいは蒸着法やスパッタ法により第三セラミックス層１３の全面に金属層を形成した後、フォトリソグラフィ・エッチングを利用して所定のパターンに形成してもよい。また、第三セラミックス層１３の表面に直接スクリーン印刷をすることによって上部電極１６を形成してもよい。以上によって、本発明に係る圧電素子を製造できる。
　本発明に係る圧電素子は、４層構造を構成する第一セラミックス層１１の弾性率は第二セラミックス層１２の弾性率よりも大きく、第二セラミックス層１２の弾性率は第三セラミックス層１３の弾性率よりも大きくなるように構成されている。このように構成することによって、各セラミックス層間の弾性率のギャップを小さくすることができるので、各層の間で発生する応力が低減されて、圧電層の界面剥離が発生しにくくなる。また、クラックやピンホールも形成されにくくなるので、短絡も発生しにくくなる。これとともに圧電層の内部応力の低減によって、圧電素子の圧電特性も向上する。
　本発明でいうセラミックス膜の弾性率は、ナノインデンテーション法によって測定することができる。具体的には、エリオニクス社製の超微小押込み硬さ試験機：ＥＮＴ－１１００ａを用いて、押込み荷重を５ｍＮとして測定した値である。なお、ここでいう弾性率は、各層を形成したあとアニール処理を行う以前に測定された値である。
　また、圧電特性は圧電定数－ｄ３１の値を算出し、この値の大きさで評価した。この圧電定数－ｄ３１は、後述するように、圧電アクチュエータの変位を測定すること等の作業によって算出した。
　本発明の第一実施形態によると、前記圧電素子は、第一層が酸化ジルコニウムからなり、第二層及び第三層がチタン酸ジルコン酸鉛からなり、第二層は第三層よりも膜厚が薄い。
　この実施形態では、第二層の膜厚を第三層の膜厚よりも薄くすることによって、第二層の弾性率を第三層の弾性率よりも大きくする。一般に、エアロゾルデポジション法で形成されたセラミックス膜の弾性率は、セラミックスの種類のほか、セラミックス膜の膜厚にも依存している。すなわち、同じ材料からなるセラミックス膜の場合には、うすいセラミックス膜のほうが硬くなり、すなわち弾性率が大きくなる。また、上述のとおり、上記セラミックス膜の下層の弾性率にも影響される。本実施形態では、これらの性質を利用して第二層と第三層の弾性率の関係が調整される。
　本発明の第二実施形態によると、前記圧電素子は、第一層が酸化アルミニウムからなり、第二層が酸化ジルコニウムからなり、第三層がチタン酸ジルコン酸鉛からなる。
　酸化アルミニウム薄膜は一般に、酸化ジルコニウム薄膜よりも弾性率が大きいので、本実施形態はこの関係を利用している。
　本発明の第三実施形態によると、前記圧電素子は、第一層が酸化アルミニウムからなり、第二層及び第三層がチタン酸ジルコン酸鉛からなり、第二層は第三層よりも膜厚が薄い。
　この実施形態では、第一実施形態と同様の性質を利用して第二層と第三層の弾性率の関係が調整される。
　これら実施形態における具体的な層構成によると、第一層の弾性率は第二層の弾性率よりも大きく、第二層の弾性率は第三層の弾性率よりも大きいという関係を満足できる。このことにより、従来の三層構造の圧電素子と比較すると、各セラミックス層間での弾性率のギャップを小さく抑制できる。このため、エアロゾルデポジション法による成膜後にアニール処理をおこなっても、膜界面での剥離が発生しにくく、電気評価も良好である。よって、歩留りが改善されるとともに、優れた圧電特性を達成することができる。
　以下に実施例を掲げて本発明をさらに詳細に説明するが、本発明はこれら実施例に限定されるものではない。
　（実施例１）
　１．基板の準備
　拡散接合ＳＵＳ基板および評価用ＳＵＳ基板：１５×３５×０．４ｔを準備した。ナノインデンターを用いて、荷重：５ｍＮにて評価用ＳＵＳ基板の弾性率を測定した。
　２．第一層の形成
　これら基板に対して、上述した実施形態に基づくエアロゾルデポジション法に基づいた成膜装置にて、拡散防止層である第一層としてＺｒＯ２膜を形成した。
　以下本工程を具体的に説明する。エアロゾル生成器にＺｒＯ２粉末：１６０ｇを投入した。基板ホルダーにＳＵＳ基板をセットし、成膜範囲以外をテープで貼付した。基板ホルダーを成膜室内のＸＹステージにセットし、往復スキャンを開始した。なお、ステージ移動は「コの字移動」を繰返しており、２列（２枚）成膜を同一バッチにて行った。成膜室であるチャンバを真空引きして、到達真空圧：１０～２０Ｐａとした。キャリアガスを３系統（流動、破砕、加速）から導入し、原料粉体を流動攪拌した。所定の総流量（３系統の合計）に合わせ、流動状態を見ながら流動ガス流量を一定に定めた。その後、破砕ガスと加速ガスの比率を変更することで所望のエアロゾル濃度に調整した。成膜範囲外で空噴射：５ｍｉｎを行った後、所定の成膜時間で各ＳＵＳ基板上にエアロゾル噴射した。所定の成膜時間が終了した後、成膜ガスを止め、成膜室を真空開放した。基板ホルダーをＸＹステージから取り外し、第一層が表面に形成されたＳＵＳ基板を得た。
　第一層が形成されたＳＵＳ基板は表面をエアブローし、付着した粉体を除去した。段差計を用いて、ＳＵＳ基板上の第一層の膜厚を測定したところ、１．６μｍであった。次に、ナノインデンターを用いて、荷重：５ｍＮにて、評価用ＳＵＳ基板上の第一層の弾性率を測定した。弾性率の測定結果を図３に示す。
　３．第二層の形成
　こうして得られたＳＵＳ基板上のＺｒＯ２膜に対して、前述と同様のエアロゾルデポジション法にて、ＺｒＯ２粉末：１６０ｇの代わりにＰＺＴ粒子：２００ｇを使用して、第二層としてＰＺＴ膜を形成した。
　第二層が形成されたＳＵＳ基板に対して、純水にて処理時間：１ｍｉｎの超音波洗浄を行い、付着した粉体を除去した。１５０℃×３０ｍｉｎにて水分除去し、乾燥した。段差計を用いて、ＳＵＳ基板上の第二層の膜厚を測定したところ、１．５μｍであった。次に、ナノインデンターを用いて、荷重：５ｍＮにて、評価用ＳＵＳ基板上の第二層の弾性率を測定した。
　４．下部電極の形成
　スパッタ装置を用いて、第二層の表面に、下部電極となるＴｉ（０．０５μｍ）／Ｐｔ（０．５μｍ）層を形成した。
　５．応力開放アニール処理
　得られた積層体をマッフル炉に投入して、５００℃×３０ｍｉｎでアニール処理を行い、Ｐｔ残留応力を開放した。
　６．第三層（圧電層）の形成
　応力開放アニール処理後の積層体に対して、第二層形成時と同様のエアロゾルデポジション法にて、第三層である圧電層としてＰＺＴ膜を形成した。
　積層体の表面をエアブローし、付着した粉体を除去した。段差計を用いて、ＳＵＳ基板上の圧電層の膜厚を測定したところ、４．９μｍであった。さらに、ナノインデンターを用いて、荷重：５ｍＮにて、評価用ＳＵＳ基板上の圧電層の弾性率を測定した。
　７．粒成長アニール処理
　得られた積層体をマッフル炉に投入して、８５０℃×３０ｍｉｎでアニール処理を行い、ＳＵＳ基板上のＰＺＴ結晶粒を成長させた。
　上記の粒成長アニール処理後のＰＺＴ膜の外観形状を観察し、全面剥離があった場合は、膜剥離ありと判定した。多数のサンプルについて膜剥離の有無を判定し、全サンプル数に対する膜剥離が発生したサンプル数の割合を、膜剥離の発生率として以下の表１に示す。
　８．上部電極の形成
　拡散接合ＳＵＳ基板上の圧電膜の表面に、メタルマスクを介して上部電極となるＡｕ（０．２μｍ）を形成した。これによって、ＳＵＳ基板／ＺｒＯ２／ＰＺＴ／ＰＺＴからなる４層構造の圧電素子を製造した。
　９．電気評価
　導通テスタを用いて、下部電極：Ｐｔおよび上部電極：Ａｕ層間の様々な箇所でのショート確認を行った。ショートの場合は電気評価を不良、測定可能な場合は電気評価を良好と判断した。多数のサンプルについて電気評価を行い、全サンプル数に対する電気評価が不良であったサンプル数の割合を、電気評価の不良率として以下の表１に示す。
　１０．分極処理
　まず、電気評価で良好と判断された欠陥のない箇所の上部電極と下部電極に、それぞれ電圧印加のための端子を接続した。そして、熱処理炉にて２５０℃に加熱してから各端子の間に、分極条件：６ｋｖ/ｃｍ×１５minにて膜厚に相当する直流電圧を印加した。その後５０℃まで冷却してから直流電圧の印加を停止した。最後に端子を取り外した。
　１１．変位測定
　再び、上部電極と下部電極に電圧印加のための端子を接続した。次に、端子間に交流電圧（入力波形：０～２０Ｖの正弦波、周波数４ｋＨｚ）を印加し、そのときのアクチュエ－タの振動板（拡散接合ＳＵＳ基板）の動的変位をレーザドップラー法にて測定した。
　１２．圧電定数の算出
　圧電アクチュエータの構造体の変位と圧電定数の関係を、予めＡＮＳＹＳによって周波数応答性から解析しておき、このシミュレーション結果と上記の変位測定結果とを比較して、圧電定数－ｄ３１を算出した。本実施例においては、圧電定数－ｄ３１は、５３ｐｍ/Ｖであった。
　（実施例２）
　第一層の形成工程においてＺｒＯ２粉末：１６０ｇの代わりにＡｌ２Ｏ３粉末：１４０ｇを使用し、第二層の形成工程ではＰＺＴ粒子：２００ｇの代わりにＺｒＯ２粉末：１６０ｇを使用したこと以外は実施例１と同様にして、ＳＵＳ基板／Ａｌ２Ｏ３／ＺｒＯ２／ＰＺＴからなる４層構造の圧電素子を製造した。分極処理以降の工程は行わなかった。なお、第一層の膜厚は１．３μｍ、第二層の膜厚は４．５μｍ、圧電層の膜厚は５．２μｍであった。
　（実施例３）
　第一層の形成工程においてＺｒＯ２粉末：１６０ｇの代わりにＡｌ２Ｏ３粉末：１４０ｇを使用したこと以外は実施例１と同様にして、ＳＵＳ基板／Ａｌ２Ｏ３／ＰＺＴ／ＰＺＴからなる４層構造の圧電素子を製造した。分極処理以降の工程は行わなかった。なお、第一層の膜厚は１．９μｍ、第二層の膜厚は１．６μｍ、圧電層の膜厚は７．０μｍであった。
　（比較例１）
　第二層の形成工程を省略したこと以外は実施例３と同様にして、ＳＵＳ基板／Ａｌ２Ｏ３／ＰＺＴからなる３層構造の圧電素子を製造した。また、実施例１と同様に分極処理以降の工程も全て行い、圧電定数－ｄ３１は、３８ｐｍ/Ｖであった。なお、第一層の膜厚は２．０μｍ、圧電層の膜厚は５．０μｍであった。上記と同様にして測定した弾性率を測定した結果を図４に示す。また、膜剥離と電気評価の判定結果については表１に示す。
　図３と図４より、実施例１～３で示される本発明に係る４層構造の圧電素子では、第一層と圧電層とのあいだに第一層よりも弾性率が低い第二層を形成することで、比較例１で示される従来の３層構造の圧電素子と比較すると、各セラミックス膜間の弾性率のギャップを低減できていることが分かる。
Figure JPOXMLDOC01-appb-T000001
 
 
　表１より、比較例１で示される従来の３層構造の圧電素子では膜剥離が発生しやすく、また電気評価が不良になりやすいので良品率はわずか２２．２％にとどまっているが、実施例１～３で示される本発明に係る４層構造の圧電素子では、６０．０％以上という良品率を達成できたことが分かる。
　また、実施例１と比較例１との対比によって、圧電定数－ｄ３１が大幅に向上していることが認められ、圧電素子として圧電特性も向上することが確認された。
１　エアロゾル生成器
２　チャンバ
３　エアロゾル供給管
４　噴射ノズル
５　エアロゾル流
６　基板ホルダー
７　基板
８　駆動装置
１１　第一セラミックス層
１２　第二セラミックス層
１３　第三セラミックス層
１４　基板
１５　下部電極
１６　上部電極

Claims (4)

  1. 　基板（１４）の上に、第一層（１１）、第二層（１２）、及び、圧電層である第三層（１３）がこの順序で積層された四層構造の圧電素子であって、
    　第一層（１１）、第二層（１２）、及び第三層（１３）は、それぞれがエアロゾルデポジション法によって成膜されたセラミックス膜であり、
    　第一層（１１）の弾性率は第二層（１２）の弾性率よりも大きく、第二層（１２）の弾性率は第三層（１３）の弾性率よりも大きい、圧電素子。
  2. 　第一層（１１）が酸化ジルコニウムからなり、第二層（１２）及び第三層（１３）がチタン酸ジルコン酸鉛からなり、第二層（１２）は第三層（１３）よりも膜厚が薄い、請求項１記載の圧電素子。
  3. 　第一層（１１）が酸化アルミニウムからなり、第二層（１２）が酸化ジルコニウムからなり、第三層（１３）がチタン酸ジルコン酸鉛からなる、請求項１記載の圧電素子。
  4. 　第一層（１１）が酸化アルミニウムからなり、第二層（１２）及び第三層（１３）がチタン酸ジルコン酸鉛からなり、第二層（１２）は第三層（１３）よりも膜厚が薄い、請求項１記載の圧電素子。
PCT/JP2009/070404 2008-12-29 2009-12-04 圧電素子 Ceased WO2010076864A1 (ja)