WO2010071302A2 - 생분해성 광고 소재 및 이의 제조방법 - Google Patents
생분해성 광고 소재 및 이의 제조방법 Download PDFInfo
- Publication number
- WO2010071302A2 WO2010071302A2 PCT/KR2009/006685 KR2009006685W WO2010071302A2 WO 2010071302 A2 WO2010071302 A2 WO 2010071302A2 KR 2009006685 W KR2009006685 W KR 2009006685W WO 2010071302 A2 WO2010071302 A2 WO 2010071302A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film layer
- layer
- biodegradable
- biodegradable film
- advertising material
- Prior art date
Abstract
Description
Claims (15)
- 표면필름층/점착층/이형층이 순차적으로 적층되어 이루어지며, 상기 표면 필름층은 폴리락트산계 중합체 5 내지 40중량%와 지방족 폴리에스터 95 내지 60중량%로 이루어진 생분해성 필름층인 것을 특징으로 하는 광고 소재.
- 제 1항에 있어서, 상기 폴리락트산계 중합체는 비중 1 내지 2이고, 융점 100 내지 150℃인 폴리라틱산(PLA) 투명 수지인 것을 특징으로 하는 광고 소재.
- 제 1항에 있어서, 상기 지방족 폴리에스터는 폴리하이드록시부틸레이트(PHB), 폴리하이드록시알카노에이트(PHA), 폴리카프로락톤(PCL), 및 폴리부틸렌 아디페이트 테레프탈레레이트(PBAT)로 이루어진 그룹으로부터 선택된 1종 이상인 것을 특징으로 하는 광고 소재.
- 제 1 항에 있어서, 상기 생분해성 필름층의 두께는 50 ~ 200㎛인 것을 특징으로 하는 광고 소재.
- 제 1 항에 있어서, 상기 생분해성 필름층은 이산화티탄(Tio2), 탄산칼슘(CaCO3), 탈크(Talc) 및 황산바륨(BaSO4), 규회석(CaSiO3)로 이루어진 그룹으로부터 선택된 1종 이상의 은폐력 개선 물질을 포함하는 것을 특징으로 하는 광고 소재.
- 제 1 항에 있어서, 상기 생분해성 필름층은 상이한 색상을 가지는 2층 이상으로 구성됨을 특징으로 하는 광고 소재.
- 제 6항에 있어서, 상기 생분해성 필름층은 이산화티탄(Tio2), 탄산칼슘(CaCO3), 탈크(Talc), 카본 블랙, 황산바륨(BaSO4) 및 규회석(CaSiO3)으로 이루어진 그룹으로부터 선택된 1종 이상의 안료를 포함하는 것을 특징으로 하는 광고 소재.
- 제 1항에 있어서, 상기 생분해성 필름층 상부에 표면처리층을 추가로 포함한 것을 특징으로 하는 광고 소재.
- 제 8항에 있어서, 상기 표면처리층은 아크릴계 수지 및 불소계 수지로 이루어진 그룹으로부터 선택된 1종 이상임을 특징으로 하는 광고 소재.
- 제 1 항에 있어서, 상기 점착층은 10~50㎛ 두께의 아크릴계 유성 또는 수성 점착제인 것을 특징으로 하는 광고 소재.
- 제 1항에 있어서, 상기 점착층은 백색, 흑색 및 회색 안료로 이루어진 그룹으로부터 선택된 1종 이상의 은폐력 개선 물질을 포함하는 것을 특징으로 하는 광고 소재.
- 제 1항에 있어서, 상기 이형층은 종이 또는 폴리에스터 기재 필름 상에 실리콘 수지로 도포된 것을 특징으로 하는 광고 소재.
- 표면필름층을 제조하는 제1단계;이형층에 점착층을 코팅하는 제2단계; 및상기 점착층이 코팅된 이형층과 상기 표면필름층을 합판하는 제3단계를 포함하는 제 1항에 따른 광고 소재의 제조 방법.
- 제 13항에 있어서, 상기 표면필름층은 폴리락트산계 중합체 5 내지 40중량%와 지방족 폴리에스터 95 내지 60중량%로 이루어진 생분해성 필름층인 것을 특징으로 하는 광고 소재의 제조 방법.
- 제 13항에 있어서, 추가적으로 상기 표면필름층 상부에 표면처리층 코팅 단계를 포함하는 것을 특징으로 하는 광고 소재의 제조 방법.