WO2009147991A1 - 加飾シートおよび加飾操作パネル並びにその製造方法 - Google Patents

加飾シートおよび加飾操作パネル並びにその製造方法 Download PDF

Info

Publication number
WO2009147991A1
WO2009147991A1 PCT/JP2009/059768 JP2009059768W WO2009147991A1 WO 2009147991 A1 WO2009147991 A1 WO 2009147991A1 JP 2009059768 W JP2009059768 W JP 2009059768W WO 2009147991 A1 WO2009147991 A1 WO 2009147991A1
Authority
WO
WIPO (PCT)
Prior art keywords
decorative
operation panel
light
black ink
resin
Prior art date
Application number
PCT/JP2009/059768
Other languages
English (en)
French (fr)
Inventor
友也 渡瀬
Original Assignee
日本写真印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本写真印刷株式会社 filed Critical 日本写真印刷株式会社
Publication of WO2009147991A1 publication Critical patent/WO2009147991A1/ja

Abstract

　遮光部から光を漏らすことなく透光表示柄を明瞭に表示できるとともに、静電容量スイッチに誤動作や不動作を生じさせない静電容量スイッチ用操作パネルを得るための加飾シートであり、基体シート上に遮光部に囲まれた透光部が透光表示柄として形成され、遮光部が絶縁性黒色インクで形成され、その絶縁性黒色インクが複数の着色顔料を含有し、そのうちの１種が前記絶縁性黒色インク全体の不揮発成分中３０重量％以下の炭素質粉体からなることを特徴とする。

Description

加飾シートおよび加飾操作パネル並びにその製造方法
　本発明は、例えば携帯電話やデジタル音楽プレーヤーといった電子機器の操作パネルを製造するために使用される加飾シートおよび加飾操作パネル並びにその製造方法に関する。
　従来、電化製品などに使用される表示パネルとして、パネル裏面に設けられたＬＥＤなどの光源から光が照射されることによって、パネル表面に柄を表示するものがある。
　図６に示すように、この種の表示パネルは、加飾シートの一種である転写シート１０１を使用して形成することができる。
　図７に示すように、転写シート１０１を使用して形成される表示パネル１１１は、樹脂成形品１０９の表面に、柄を形成するための透光部１０３と遮光部１０４を少なくとも備えており、さらに、剥離層１０５、加飾層１０６および接着層１０７を備えることもある。
　表示パネル１１１は、パネル裏面から照射される光が透光部１０３を通過する一方で遮光部１０４については通過しないようにしてパネル表面に柄を表示するように構成されているため、遮光部１０４には光を完全に遮る隠蔽性が必要とされる。
　遮光部１０４が効果的に遮光できるようにするには黒色インクを用いるとよい。また、デザイン面においても操作パネルを黒色にする場合が多い。
　グラビア印刷によって遮光部１０４を形成した加飾フィルムを用い、表示パネル１１１を作製する場合、遮光部１０４の膜厚は通常、数μｍ程度と薄いため、遮光部１０４を形成する際には遮光性の高いインクを使用する必要がある。
特開平７－８４５３３号公報
　近年、携帯電話やデジタル音楽プレーヤーなどの電子機器において、内部に静電容量スイッチと呼ばれる入力デバイスを搭載することが増えてきている。静電容量スイッチとは、指を電極に近づけると電極の静電容量が変化する現象を利用したスイッチである。
　このような電子機器１５１に対して、静電容量スイッチの検出部１２１の上部に、従来の表示パネル１１１を操作パネルとして配置し、透光部１０３と遮光部１０４からなる操作アイコンなどの透光表示柄を形成すると（図７参照）、スイッチに触れたところと別のスイッチが作動したり（誤動作）、スイッチに触れてもスイッチが作動しないこと（不動作）が発生する場合がある。
　これは、表示パネル１１１の遮光部１０４が炭素質粉体を含むインクで形成されていて導電性を有することに起因しており、指１３１が触れる部位の電極１２２とは別の電極１２３に微弱電流が流れて指１３１が触れた部位として検出してしまうためである。
　本発明は、遮光部に十分な隠蔽性を備えつつ静電容量スイッチに誤動作や不動作を生じさせない、加飾シートおよび加飾操作パネル並びにその製造方法を提供することを目的とする。
　前記目的を達成するための本発明は、以下のような特徴を備える。
　本発明の静電容量スイッチ操作パネル形成用の加飾シートは、基体シート上に遮光部に囲まれた透光部が透光表示柄として形成され、前記遮光部が絶縁性黒色インクで形成され、その絶縁性黒色インクが複数の着色顔料を含有し、そのうちの１種が前記絶縁性黒色インク全体の不揮発成分中３０重量％以下の炭素質粉体からなることを要旨とする。
　また、上記の発明において、絶縁性黒色インクが少なくとも４種以上の着色顔料を含有し、そのうちの１種が前記炭素質粉体からなり、残りの少なくとも３種以上がそれぞれ色調の異なる顔料からなることが好ましい。
　また、上記の発明において、遮光部がグラビア印刷によって絶縁性黒色インクを２層以上の積層することによって形成することが好ましい。
　本発明の加飾操作パネルの製造方法は、上記のいずれかの構成からなる加飾シートを、前記遮光部が形成されていない前記基体シートの面が金型キャビティに面するように金型内に配置し、前記金型内に成形樹脂を流し込み、冷却固化後に前記基体シートを前記加飾シートから剥離することを要旨とする。
　本発明の加飾操作パネルの製造方法は、上記のいずれかの構成からなる加飾シートと樹脂成形品とを粘着剤で貼り合せて一体化することを要旨とする。
　本発明の加飾操作パネルは、樹脂成形品の表面に透光表示柄を形成する透光部と遮光部とが形成され、前記遮光部が絶縁性黒色インクで形成されていることを要旨とする。
　また、上記加飾パネルにおいて、前記透光表示柄の表面上に隣接する２箇所のスイッチタッチ面の間のＬＣＲメーターによる直列等価抵抗値（ＥＳＲ）を１０ＭΩ以上とすることが望ましい。
　本発明の電子機器は、静電容量スイッチと、この静電容量スイッチに対向して設けられる加飾操作パネルとから構成され、
　前記加飾操作パネルは、樹脂成形品と、前記樹脂成形品の表面に形成される透光表示柄とを有し、この透光表示柄は、透光部と遮光部とによって形成されるとともに、前記遮光部が絶縁性黒色インクで形成されたものであることを要旨とする。
　本発明の加飾シートによれば、遮光部が絶縁性黒色インクで形成されているため、遮光部から光を漏らすことなく透光表示柄を明瞭に表示することができる。
　本発明の加飾シートを用いた加飾操作パネルによれば、静電容量スイッチに誤動作や不動作を生じさせない操作パネルを得ることができる。
本発明に係る加飾シートの縦断面図である。 (ａ)および(ｂ)は成形同時転写法により本発明の操作パネルを製造する一工程を示す縦断面図である。 本発明に係る操作パネルの縦断面図である。 本発明に係る操作パネルの正面図である。 本発明に係る電子機器の縦断面図である。 従来の表示パネルの縦断面図である。 従来の電子機器の縦断面図である。
　以下、図面を参照しながらこの発明の実施の形態について詳しく説明する。
　まず、本発明の静電容量スイッチ操作パネルを形成するための加飾シートについて説明する。
　図１において、上記加飾シートとは、樹脂成形品の表面を加飾するために用いられるシートであり、例えば転写シート１を使用することができる。
　転写シート１は少なくとも転写層８が形成されたものであり、その転写層８は、基体シート２上（図では基体シート２の下側）に透光表示柄として形成されており、遮光部４に囲まれた透光部３が備えられている。
　図２(ａ)に示す成形同時転写法によって、樹脂成形品９の成形と同時にその樹脂成形品９に転写シート１を融着させ、脱型後、転写シート１の基体シート２を剥離すれば、図２(ｂ)に示すように、転写シート１の転写層８が樹脂成形品９の表面に転写され、静電容量スイッチ操作パネルを形成することができる。なお、成形同時転写法については後述する。
　上記基体シート２としては、ポリエステル系樹脂、ポリプロピレン系樹脂、塩化ビニル樹脂、ポリエチレン樹脂、ポリエチレンテレフタレート樹脂、ポリカーボネート樹脂、ナイロン樹脂、ビニロン樹脂、アセテート樹脂、ポリエチレン系樹脂、ポリアミド系樹脂、ポリアクリル系樹脂、ポリ塩化ビニル系樹脂などのプラスチックシートを使用することができる。
　基体シート２の厚さは、１０～１００μｍのものを使用するとよい。
　基体シート２はそれ自体、剥離性を備えているものを用いるとよい。また、より剥離性を安定させるために、転写層８との間に離型層を形成してもよい。
　離型層は転写工程後に基体シート２とともに除去される層である。
　離型層の材質としては、シリコーン樹脂、メラミン樹脂、アルキッド樹脂、エポキシ樹脂などの硬化性樹脂を用いるとよい。
　離型層の形成方法としては、ロールコート法、スプレーコート法などのコート法、グラビア印刷法、スクリーン印刷法などの印刷法がある。
　また、基体シート２あるいは上記離型層との剥離をより確実にするために、必要に応じて加飾層６との間に剥離層５を形成してもよい。
　剥離層５は、成形同時転写後に基体シート２を剥離した際に、基体シート２または離型層から剥離して転写層６側に残り、被転写物の最外面となる層を形成する。
　剥離層５の材質としては、アクリル系樹脂、ポリエステル系樹脂、ポリ塩化ビニル系樹脂、セルロース系樹脂、ゴム系樹脂、ポリウレタン系樹脂、ポリ酢酸ビニル系樹脂などのほか、塩化ビニル－酢酸ビニル共重合体系樹脂、エチレン－酢酸ビニル共重合体系樹脂などのコポリマーを用いるとよい。
　剥離層５に硬度が必要な場合には、紫外線硬化性樹脂などの光硬化性樹脂、電子線硬化性樹脂などの放射線硬化性樹脂、熱硬化性樹脂などを選定して用いるとよい。
　剥離層５の形成方法としては、グラビアコート法、ロールコート法、コンマコート法などのコート法、グラビア印刷法、スクリーン印刷法などの印刷法がある。
　また、意匠性を付与するため転写層８に加飾層６を付加してもよい。
　加飾層６の材質としては、ポリビニル系樹脂、ポリアミド系樹脂、ポリエステル系樹脂、アクリル系樹脂、ポリウレタン系樹脂、ポリビニルアセタール系樹脂、ポリエステルウレタン系樹脂、セルロースエステル系樹脂、アルキド樹脂などの樹脂をバインダーとし、適切な色の顔料または染料を着色剤として含有する着色インクを用いるとよい。
　加飾層６の形成方法としては、グラビア印刷法、スクリーン印刷法、オフセット印刷法などの通常の印刷法などを用いるとよい。加飾層６の厚さとしては、１～３０μｍが好ましい。
　遮光部４に囲まれた透光部３が透光表示柄となるように、遮光部４の平面形状を決定する。
　詳しくは、透光表示柄とは操作パネル裏面からの光の照射有無によって、表示されたり表示されなかったり表示状態が切り換えられる柄のことである。
　上記透光表示柄としては三角形や四角形などの単純な幾何学模様に限らず、例えば操作アイコンの柄を形成するようにしてもよい。
　上記遮光部４は絶縁性黒色インクで形成される。
　絶縁性黒色インクは、裏面から光を照射しても遮光部４に光漏れを起こさない隠蔽性と、操作パネルの操作中に静電容量スイッチの誤動作や不動作を引き起こさないための絶縁性とを操作パネルに付与するためのインクである。
　上記絶縁性黒色インクは少なくとも４種以上の着色顔料からなり、そのうちの１種が絶縁性黒色インク全体の不揮発成分中３０重量％以下の濃度の炭素質粉体からなることが好ましい。
　上記炭素質粉体の濃度を３０重量％以下にすれば、印刷用黒色インクに絶縁性が得られ、操作パネルの静電容量スイッチが、誤動作や不動作を引き起こさないようにすることができる。
　炭素質粉体の粒子径は１～２００ｎｍであることが望ましい。２００ｎｍより大きいと文字再現性について印刷適性が悪くなり、１ｎｍより小さいと黒色度や隠蔽性が落ちてしまうからである。
　残りの少なくとも３種の着色顔料は青色系、赤色系、黄色系の顔料を使用することが望ましい。混ぜることによって黒色となるからである。
　青色系顔料としては、例えば、Pigment Blue 15（銅フタロシアニン）等が、赤色系顔料としては、例えば、Pigment Red 149（パーマネントレッドＢＬ）、Pigment Red 144(Cromophtal Red typel)等が、黄色系顔料としては、例えば、Pigment Yellow 12（ジスアゾイエロー）等を使用できる。
　青色系、赤色系、黄色系以外の顔料としては、例えば、黒色系顔料としてPigment Black 1（アニリンブラック）、Pigment Black 11（鉄黒）等を使用してもよい。
　絶縁性黒色インクに使用する樹脂バインダーは、アクリル系樹脂、ウレタン系樹脂、塩化ビニル／酢酸ビニル共重合体樹脂のいずれか、あるいはこれらの組み合わせを主成分とするものである。
　遮光部４をグラビア印刷で形成する場合は２層以上に積層すると十分な隠蔽性を得ることができる。
　また、遮光部４におけるインク層全体の膜厚は２０μｍ以下であるのが好ましい。この膜厚が２０μｍより大きいと、樹脂成形品９に対しロール転写法などで転写層８を転写する後転写加工によって操作パネル１１を形成する場合に、遮光部４のインキ層膜厚と遮光部４以外の部分の膜厚との間で段差が生じ、外観の見栄えが悪くなるからである。
　また、後述する貼り合せ法で操作パネル１１を形成する場合にも上記と同様の段差が生じて目立ちやすい。
　さらにまた、成形同時転写法で操作パネル１１を形成する場合においてインク層の膜厚が厚いと、溶融した成形樹脂３２の熱圧によりインクが溶融して流動しやすくなり、遮光部４の形成パターンが歪んだりするいわゆるインク流れが起こりやすくなる。
　また、必要に応じて転写層８に接着層７を付加してもよい。
　上記接着層７は、成形同時転写法により転写シートを樹脂成形品９に接着させるための層である。
　樹脂成形品９の材質がポリアクリル系樹脂の場合は、接着層７の材質としてポリアクリル系樹脂を用いるとよい。また、樹脂成形品９の材質がポリフェニレンオキシド・ポリスチレン系樹脂、ポリカーボネート系樹脂、スチレン共重合体系樹脂、ポリスチレン系ブレンド樹脂の場合は、これらの樹脂と親和性のあるポリアクリル系樹脂、ポリスチレン系樹脂、ポリアミド系樹脂などを、接着層７の材質として使用すればよい。
　接着層７の形成方法としては、グラビアコート法、ロールコート法、コンマコート法などのコーティングや、グラビア印刷、スクリーン印刷法などを用いるとよい。
　接着層７の乾燥膜厚は、１～５μｍとするのが一般的である。
　次に、図２を参照しながら成形同時転写法によって操作パネル１１を製造する方法について説明する。
　まず、可動型と固定型とからなる成形用金型３１内に転写シート１を送り込む。
　その際、枚葉の転写シート１を１枚ずつ送り込んでもよいし、長尺の転写シート１の転写柄部分を間欠的に送り込んでもよい。
　上記長尺の転写シート１を使用する場合、位置決め機構を備えた送り装置を使用して、転写シート１と成形用金型３１との見当が一致するようにするとよい。
　また、転写シート１を間欠的に送り込む際に、転写シート１に印刷されたマークをセンサーで検出することにより、転写シート１の送り量をコントロールし、転写柄部分と金型キャビティとの位置合せを行い、転写シート１を可動型と固定型とで固定するようにしてもよい。
　転写シート１は転写層８が形成されていない基体シート２の面が金型キャビティに面するようにして成形用金型３１内に配置する。
　成形用金型３１を閉じた後、金型のゲートから成形樹脂３２を成形用金型３１内に射出充填し、樹脂成形品９を形成するのと同時にその成形面に転写シート１を接着させる（図２（ａ）参照）。
　樹脂成形品９を冷却固化した後、成形用金型３１を開いて基体シート２を剥がすと、転写層８が樹脂成形品９の表面に転写され、転写工程が完了する（図２（ｂ）参照）。こうして成形表面に転写層８を有する操作パネル１１が形成される（図３参照）。
　操作パネル１１を形成するための樹脂成形品９に用いられる成形樹脂３２としては、例えばポリエチレン、ポリプロピレン等のポリオレフィン系樹脂、
　ポリスチレン系樹脂、ポリ塩化ビニル系樹脂、ポリ（メタ）アクリレート系樹脂、アクリル系樹脂、ポリアセタール樹脂、
　ポリエチレンテレフタレート、ポリブチレンテレフタレート等のポリエステル樹脂、
　ポリアミド樹脂、ポリカーボネート樹脂、ポリフェニレンサルファイド樹脂、ポリイミド樹脂等の公知の熱可塑性樹脂がいずれも使用できる。これらの樹脂は単独あるいは２種以上を混合して使用することも可能である。
　本発明の加飾シートは、先に説明した転写シート１に限らず、貼り合せシート（図示せず）を使用することもできる。
　上記貼り合せシートは、転写シート１の層構成から剥離層５と接着層７を除いたものであり、樹脂成形品の表面に接着されて一体となり、樹脂成形品からはみ出た外周部分が切り離されるものである。
　貼り合せシートを用いた貼り合せ法により静電容量スイッチ操作パネルを形成するには、まず、樹脂成形品の表面に粘着剤を塗布しその上に上記貼り合せシートを樹脂成形品の表面に接着し、その後樹脂成形品からはみ出た外周部分を切り離せばよい。
　上記転写シート１または上記貼り合せシートを用いて形成された操作パネル１１は、透光表示柄を備えるだけでなく、電子機器５１を操作するために触れるべき箇所を示すスイッチタッチ面４１、４２も備えている（図４、図５参照）。
　また、図５において、操作パネル１１は、静電容量スイッチの指を検出するための基板である検出部２１の上面側に配置される。
　上記検出部２１は基材２４上に電極２２、２３が形成された構成からなり、スイッチタッチ面４１、４２は、電極２２、２３に対応してそれらの上面に位置しているが、必ずしも透光表示柄である透光部３の位置と重ねて配置する必要はない。
　なお、図中５２は電子機器筐体を示している。
　静電容量スイッチ用の操作パネルには、表面だけでなく内部の層にも絶縁性が要求される。しかし、内部の層が絶縁性であるかどうかは、通常の絶縁抵抗計では確認できない。
　そこで、測定物（操作パネル）を抵抗値、電気容量、インダクタンスの等価回路とみなし、それぞれを独立に測定できるＬＣＲメーターを使用して、直列等価抵抗値（ＥＳＲ）を測定すれば、絶縁性を評価することができる。
　ＬＣＲメーターで操作パネル１１のＥＳＲを測定するには、操作パネル１１の操作部、詳しくはパネル表面上の隣接する２箇所のスイッチタッチ面４１、４２（図５の破線で示した円）に、ＬＣＲメーターの２本のテスター棒をそれぞれ接触させればよい。
　このスイッチタッチ面４１、４２の位置は電極２２、２３の上方の位置である。測定条件によってＥＳＲの値が大きく変わるものではないが、本実施形態においては、周波数（ＦＲＥＱ）２０ｋＨｚ、定電圧印加（ＣＶ）１．２５Ｖの条件で測定するものとする。
　ＬＣＲメーターで測定したＥＳＲが１０ＭΩ以上になることが好ましい。ＥＳＲが１０ＭΩ以上であれば、操作パネル１１の静電容量スイッチが誤動作や不動作を引き起こす虞れがないようにすることができる。
　厚さ３８μｍのポリエチレンテレフタレートフィルムを基体シート２とし、次いで、剥離層５、加飾層６、および遮光部４に囲まれた透光部３が透光表示柄となるように遮光部４、および接着層７を順次グラビア印刷法により形成して、転写シート１を得た。
　剥離層５、加飾層６は、それぞれアクリル系樹脂からなるインキを用いて形成した。遮光部４は、下記の絶縁性黒色インクを用い、グラビア印刷機で２層刷り重ねた。
　接着層７は塩化ビニル－酢酸ビニル共重合体系樹脂からなるインキを用いて形成した。
　ａ絶縁性黒色インクの組成
　　顔料（不揮発成分）　　　　　　　　　　　１０．０％
　　アクリル樹脂（不揮発成分）　　　　　　　１８．０％
　　ビニル樹脂（不揮発成分）　　　　　　　　　４．０％
　　分散剤（不揮発成分）　　　　　　　　　　　０．４％
　　ＭＥＫ（揮発成分）　　　　　　　　　　　　約３１％
　　トルエン（揮発成分）　　　　　　　　　　　約３５％
　ａ′上記顔料の組成
　　三菱化学株式会社製カーボンブラック　ＭＡ８　４０％
　　青色系顔料　　　　　　　　　　　　　　　　　２１％
　　赤色系顔料　　　　　　　　　　　　　　　　　１６％
　　黄色系顔料　　　　　　　　　　　　　　　　　２３％
　絶縁性黒色インクは上記したように４種の着色顔料ａ′を含有しており、そのうちの１種、すなわちカーボンブラックは、黒色インク全体の不揮発成分（１０．０＋１８．０＋４．０＋０．４＝３２．４％）中の４０％であるから約１３％（０．３２４×０．４）となり、黒色インク全体の不揮発成分中３０重量％以下となる。
　成形同時転写法により図３に示した操作パネル１１を得た。得られた操作パネル１１の操作部の抵抗値を、日置電機株式会社製3532-50 LCR HiTESTERを使用し、周波数（ＦＲＥＱ）２０ｋＨｚ、定電圧印加（ＣＶ）１．２５Ｖの条件で測定したところ、直列等価抵抗値（ＥＳＲ）は１５０ＭΩであり、静電容量スイッチ用の操作パネルとして使用したところ、スイッチの誤動作や不動作は生じなかった。
　また、操作パネル１１の裏側からＬＥＤ光源１２の光を照らしたところ、透光部３から透光表示柄が明瞭に浮かび上がり遮光部４からの光漏れはなかった。
　（比較例１）
　遮光部４を以下の黒色インクとしたこと以外は実施例１と同様にして形成した転写シートを用い、成形同時転写法により操作パネルを得た。
　ｂ黒色インクの組成
　　顔料　　　　　　　　　　　　　　　　　　　１０．０％
　　アクリル樹脂　　　　　　　　　　　　　　　１８．０％
　　ビニル樹脂　　　　　　　　　　　　　　　　　４．０％
　　分散剤　　　　　　　　　　　　　　　　　　　０．４％
　　ＭＥＫ　　　　　　　　　　　　　　　　　　　約３１％
　　トルエン　　　　　　　　　　　　　　　　　　約３５％
　ｂ′上記顔料の組成
　　三菱化学株式会社製カーボンブラック　ＭＡ８　１００％
　この場合のカーボンブラックは、黒色インク全体の不揮発成分（３２．４％）中の１００％であるから約３２．４％となり、黒色インク全体の不揮発成分中３０重量％以下という条件を満足しない。
　得られた操作パネルの操作部の抵抗値を、実施例１と同条件で測定したところ、直列等価抵抗値（ＥＳＲ）は０．５ＭΩであり、静電容量スイッチ用の操作パネルとして使用したところ、スイッチの誤動作が生じてしまった。
　厚さ５０μｍのポリエチレンテレフタレートフィルムを基体シート２とし、次いで、加飾層６および遮光部４に囲まれた透光部３が透光表示柄となるように、遮光部４を順次グラビア印刷法により形成して、貼り合せシートを得た。
　遮光部は下記の絶縁性黒色インクを用い、グラビア印刷機で２層刷り重ねた。
　ｃ絶縁性黒色インクの組成
　　顔料　　　　　　　　　　　　　　　　　　１０．０％
　　アクリル樹脂　　　　　　　　　　　　　　１８．０％
　　ビニル樹脂　　　　　　　　　　　　　　　　４．０％
　　分散剤　　　　　　　　　　　　　　　　　　０．４％
　　ＭＥＫ　　　　　　　　　　　　　　　　　　約３１％
　　トルエン　　　　　　　　　　　　　　　　　約３５％
　ｃ′上記顔料の組成
　　三菱化学株式会社製カーボンブラック　ＭＡ８　４０％
　　青色系顔料　　　　　　　　　　　　　　　　　２１％
　　赤色系顔料　　　　　　　　　　　　　　　　　１６％
　　黄色系顔料　　　　　　　　　　　　　　　　　２３％
　得られた貼り合せシートを貼り合せ法によって厚さ１ｍｍのポリカーボネート透明板に貼り合せ、一体化することで、操作パネルを得た。
　得られた操作パネルの操作部の抵抗値を、日置電機株式会社製3532-50 LCR HiTESTERを使用し、周波数（ＦＲＥＱ）２０ｋＨｚ、定電圧印加（ＣＶ）１．２５Ｖの条件で測定したところ、直列等価抵抗値（ＥＳＲ）は８６ＭΩであった。
　静電容量スイッチ用の操作パネルとして使用したところ、スイッチの誤動作や不動作は生じなかった。また、操作パネルの裏側からＬＥＤ光源１２の光を照らしたところ、透光部３から透光表示柄が明瞭に浮かび上がり遮光部４からの光漏れはなかった。
　上述した通り、本発明は、添付図面を参照しながら好ましい実施形態に関連して充分に記載しているが、当該技術分野の熟練者にとっては種々の変形や修正を加えて実施することは可能である。そのような変形や修正は、本発明の技術的範囲を逸脱しない限りにおいて、本発明に含まれると理解されるべきである。
　本発明の加飾シートは、静電容量スイッチを備えた操作パネルの製造に好適であり、この加飾シートによって加飾された操作パネルは、携帯電話やデジタル音楽プレーヤー等の電子機器に適用することができる。
　　１　転写シート
　　２　基体シート
　　３　透光部
　　４　遮光部
　　５　剥離層
　　６　加飾層
　　７　接着層
　　８　転写層
　　９　樹脂成形品
　１１　操作パネル
　１２　光源
　２１　検出部
　２２，２３　電極
　２４　基材
　３１　成形用金型
　３２　成形樹脂
　４１，４２　スイッチタッチ面
　５１　電子機器
　５２　電子機器筐体

Claims (8)

  1. 　基体シート上に遮光部に囲まれた透光部が透光表示柄として形成され、前記遮光部が絶縁性黒色インクで形成され、その絶縁性黒色インクが複数の着色顔料を含有し、そのうちの１種が前記絶縁性黒色インク全体の不揮発成分中３０重量％以下の炭素質粉体からなることを特徴とする静電容量スイッチ操作パネル形成用の加飾シート。
  2. 　前記絶縁性黒色インクが少なくとも４種以上の着色顔料を含有し、そのうちの１種が前記炭素質粉体からなり、残りの少なくとも３種以上がそれぞれ色調の異なる顔料からなる請求項１記載の加飾シート。
  3. 　前記遮光部が、グラビア印刷によって前記絶縁性黒色インクを２層以上積層することによって形成されている請求項１または２のいずれか１項に記載の加飾シート。
  4. 　請求項１～３のいずれか１項に記載の前記加飾シートを、前記遮光部が形成されていない前記基体シートの面が金型キャビティに面するように金型内に配置し、前記金型内に成形樹脂を流し込み、冷却固化後に前記基体シートを前記加飾シートから剥離することを特徴とする加飾操作パネルの製造方法。
  5. 　請求項１～３のいずれか１項に記載の前記加飾シートと樹脂成形品とを粘着剤で貼り合せて一体化することを特徴とする加飾操作パネルの製造方法。
  6. 　樹脂成形品の表面に透光表示柄を形成する透光部と遮光部とが形成され、前記遮光部が絶縁性黒色インクで形成されたものであることを特徴とする加飾操作パネル。
  7. 　前記透光表示柄の表面上に隣接する２箇所のスイッチタッチ面の間のＬＣＲメーターによる直列等価抵抗値（ＥＳＲ）が１０ＭΩ以上である請求項６に記載の加飾操作パネル。
  8. 　静電容量スイッチと、この静電容量スイッチに対向して設けられる加飾操作パネルとから構成され、
    　前記加飾操作パネルは、
    　樹脂成形品と、前記樹脂成形品の表面に形成される透光表示柄とを有し、この透光表示柄は、透光部と遮光部とによって形成されるとともに、前記遮光部が絶縁性黒色インクで形成されたものであることを特徴とする電子機器。
PCT/JP2009/059768 2008-06-04 2009-05-28 加飾シートおよび加飾操作パネル並びにその製造方法 WO2009147991A1 (ja)