Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K3/00—Materials not provided for elsewhere
  • C09K3/14—Anti-slip materials; Abrasives
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10F—INORGANIC SEMICONDUCTOR DEVICES SENSITIVE TO INFRARED RADIATION, LIGHT, ELECTROMAGNETIC RADIATION OF SHORTER WAVELENGTH OR CORPUSCULAR RADIATION
  • H10F71/00—Manufacture or treatment of devices covered by this subclass
  • H10F71/138—Manufacture of transparent electrodes, e.g. transparent conductive oxides [TCO] or indium tin oxide [ITO] electrodes
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09G—POLISHING COMPOSITIONS; SKI WAXES
  • C09G1/00—Polishing compositions
  • C09G1/02—Polishing compositions containing abrasives or grinding agents
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
  • C09K3/00—Materials not provided for elsewhere
  • C09K3/14—Anti-slip materials; Abrasives
  • C09K3/1454—Abrasive powders, suspensions and pastes for polishing
  • C09K3/1463—Aqueous liquid suspensions
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K30/00—Organic devices sensitive to infrared radiation, light, electromagnetic radiation of shorter wavelength or corpuscular radiation
  • H10K30/80—Constructional details
  • H10K30/81—Electrodes
  • H10K30/82—Transparent electrodes, e.g. indium tin oxide [ITO] electrodes
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10K—ORGANIC ELECTRIC SOLID-STATE DEVICES
  • H10K50/00—Organic light-emitting devices
  • H10K50/80—Constructional details
  • H10K50/805—Electrodes
  • H10K50/81—Anodes
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
  • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
  • Y02E10/00—Energy generation through renewable energy sources
  • Y02E10/50—Photovoltaic [PV] energy

Definitions

• This invention relates to polishing compositions and methods for polishing a substrate using the same. More particularly, this invention relates to chemical-mechanical polishing compositions suitable for polishing substrates comprising indium tin oxide (ITO) and CMP methods utilizing the compositions.
• ITO indium tin oxide
• ITO indium tin oxide
• Flat panel display devices typically utilize a thin layer of ITO substantially covering a flat panel surface.
• the ITO layer is configured to have an equipotential surface and an electrical conductivity lower than that of a solid metallic sheet.
• ITO is also used as a transparent electrode to construct organic light emitting diode (OLED) devices, as a window material for solar cells, and as an antistatic film.
• OLED organic light emitting diode
• the typically high surface roughness of ITO, along with non-uniformities, such as spikes, scratches, and surface residues (foreign materials adsorbed on the ITO surface) provide pathways for current leakage to flow through diodes adjacent to the ITO layer, resulting in cross-talk and undesirably low resistance.
• Cross-talk can have a direct impact on device performance, both electrically and optically.
• a smooth clean surface on the ITO layer is needed to minimize the level of unstable pixel-generating cross-talk in ITO devices, and to minimize leakage current. Reducing non-uniformities in the ITO surface provides an improvement in the overall performance, and thus better image quality in flat panel systems.
• polishing compositions also known as polishing slurries, CMP slurries, and CMP compositions
• CMP chemical-mechanical polishing
• metal-containing surfaces of semiconductor substrates typically contain an oxidizing agent, various additive compounds, abrasives, and the like.
• a substrate carrier or polishing head is mounted on a carrier assembly and positioned in contact with a polishing pad in a CMP apparatus.
• the carrier assembly provides a controllable pressure ("down force") to the substrate, urging the substrate against the polishing pad.
• the pad is moved relative to the carrier, with attached substrate, which serves to abrade the surface of the substrate to remove a portion of the material from the substrate surface, thereby polishing the substrate.
• the polishing of the substrate surface typically is further aided by the chemical activity of the polishing composition (e.g., by oxidizing agents present in the CMP composition) and/or the mechanical activity of an abrasive suspended in the polishing composition.
• Typical abrasive materials include silicon dioxide, cerium oxide, aluminum oxide, zirconium oxide, and tin oxide.
• polishing e.g., surface treatments (e.g., plasma treatment), as well as controlled ITO deposition techniques.
• surface treatments e.g., plasma treatment
• controlled ITO deposition techniques One polishing method that has been proposed to improve ITO surface uniformity is dry-polishing with a fixed abrasive pad or tape. Fixed abrasive pads typically create undesirable scratches on the ITO surface.
• CMP Chemical mechanical polishing
• the present invention provides chemical-mechanical polishing (CMP) compositions and methods for polishing an ITO surface.
• the CMP compositions of the invention comprise a particulate zirconium oxide (ZrO 2 ) or colloidal silica (SiO 2 ) abrasive having a mean particle size of not more than 150 nm, as determined by light scattering.
• the abrasive is suspended in an aqueous carrier (e.g., deionized water), which preferably has a pH of not more than 5.
• compositions of the invention comprise a particulate zirconium oxide abrasive having a mean particle size of not more than 150 nm (preferably not more than 100 nm) and a surface area in the range of 40 to 75 m 2 /g.
• the zirconium, oxide abrasive is suspended in an aqueous carrier, which preferably has a pH of not more than 5, more preferably not more than 3.
• compositions of the invention comprise a particulate colloidal silica abrasive having a mean particle size in the range of 20 to 140 nm, preferably having a surface area in the range of 80 to 220 m 2 /g, as determined by gas adsorption using the BET method.
• the colloidal silica abrasive is suspended in an aqueous carrier, which preferably has a pH of not more than 5, more preferably not more than 3.
• the CMP compositions of the invention provide a significantly lower surface roughness when used to polish an ITO surface, compared to the results obtained with CMP compositions comprising ceria or alumina, for example.
• the present invention also provides a method of polishing a surface of an ITO substrate utilizing a CMP composition of the invention.
• a preferred method comprises the steps of contacting a surface of an ITO-containing substrate with a polishing pad and an aqueous CMP composition of the invention, and causing relative motion between the polishing pad and the substrate, while maintaining a portion of the CMP composition in contact with the surface between the pad and the substrate. The relative motion is maintained for a period of time sufficient to abrade at least a portion of the ITO from the surface of the substrate.
• the present invention provides CMP compositions useful for polishing an indium tin oxide (ITO) surface.
• the CMP compositions of the invention provide for even removal of an ITO with reduced surface roughness relative to conventional CMP compositions.
• the CMP compositions contain a particulate zirconium oxide or colloidal silica abrasive material suspended in an aqueous carrier.
• the particulate abrasive material has a mean particle size of not more than 150 nm, as determined by laser light scattering techniques.
• the abrasive particles preferably have a surface area, as determined by BET gas adsorption, in the range of 40 to 220 m 2 /g.
• the pH of the aqueous carrier is not more than 5, more preferably not more than 3.
• the CMP composition comprises a particulate zirconium oxide abrasive having a particle size of not more than 150 nm, preferably not more than 100 nm, and a BET surface area in the range of 40 to 75 m 2 /g.
• the zirconium oxide abrasive is suspended in an aqueous carrier, which preferably has a pH of not more than 5, preferably not more than 3.
• the zirconium oxide abrasive can optionally comprise 0.5 to 5 percent by weight of yttrium oxide (Y2 ⁇ 3 ).
• an acidic pH is beneficial when using the zirconium oxide abrasive, in particular, because the zeta potentials of ITO and of zirconium, oxide are both positive at low pH (e.g., less than pH 5).
• the positive zeta potential of the zirconium particles causes the particles to be slightly repelled by the positive ITO surface.
• the repulsion between the particles and the ITO surface beneficially affords reduced levels of scratching, a reduced amount of adhering zirconia particles on the surface, and improved cleanability of the ITO surface.
• the CMP composition comprises a particulate colloidal silica abrasive having a particle size in the range of 20 to 140 nm.
• the colloidal silica preferably has a BET surface area in the range of 80 to 220 m 2 /g.
• the silica abrasive is suspended in an aqueous carrier, which preferably has a pH of not more than 5, more __ preferably not more than 3.
• colloidal silica likely contributes to its effectiveness for polishing ITO, particularly compared to the performance of fumed silica. Fumed silica tends to have particles with relatively sharp edges, which can lead to scratching when used to polish ITO surfaces. In contrast, colloidal silica has a more uniform particle size distribution and smoother surface than fumed silica, which may contribute, at least in part, to the improved ITO surface roughness observed after polishing with colloidal silica-based composition of the invention.
• the abrasive material is present in the compositions of the invention in an amount in the range of 0.1 to 10 percent by weight, more preferably in the range of 0.5 to 5 percent by weight.
• the abrasive is suspended in the in the aqueous carrier component of the CMP composition and preferably is colloidally stable in the carrier.
• colloid refers to the suspension of abrasive particles in the liquid carrier.
• Colloidal stability refers to the maintenance of that suspension over time.
• an abrasive is considered colloidally stable if, when the abrasive is placed into a 100 mL graduated cylinder and allowed to stand without agitation for a time of 2 hours, the difference between the concentration of particles in the bottom 50 mL of the graduated cylinder ([B] in terms of g/mL) and the concentration of particles in the top 50 mL of the graduated cylinder ([T] in terms of g/mL) divided by the initial concentration of particles in the abrasive composition ([C] in terms of g/mL) is less than or equal to 0.5 (i.e., ([B] - [T])/[C] ⁇ 0.5).
• the value of ([B]-[T])/[C] desirably is less than or equal to 0.3, and preferably is less than or equal to 0.1.
• the CMP compositions of the invention can have any suitable pH, generally in the range of 2 to 11.
• the compositions have a pH of not more than 5 (e.g., 2 to 5), more preferably not more than 3.
• the CMP compositions can be adjusted to the desired pH value by addition of an acid or a base.
• an inorganic acid, an organic acid or combination thereof can be used to lower the pH, while a basic material, such as sodium hydroxide or an amine can be used to raise the pH.
• the aqueous solution may also contain a pH buffering agent to maintain the pH at the desired level.
• the pH buffering agent can be any suitable buffering agent, for example, phosphates, acetates, borates, sulfonates, carboxylates, ammonium salts, combinations thereof, and the like.
• the CMP compositions of the invention can comprise any suitable amount of pH adjustor or pH buffering agent, provided such amount is sufficient to achieve and/or maintain the desired pH.
• the CMP compositions of the invention can include optional additive materials such as rheology modifiers, dispersants, chelating agents, biocides, and the like, so long as the additives do not cause undesirable aggregation of the abrasive particles or unfavorably affect surface roughness when used to polish ITO.
• additive materials such as rheology modifiers, dispersants, chelating agents, biocides, and the like, so long as the additives do not cause undesirable aggregation of the abrasive particles or unfavorably affect surface roughness when used to polish ITO.
• the CMP compositions of the invention can be prepared by any suitable technique, many of which are known to those skilled in the art.
• the CMP composition can be prepared in a batch or continuous process.
• the CMP composition can be prepared by combining the components thereof in any order.
• component includes individual ingredients (e.g., abrasives, acids, bases, buffers, and the like), as well as any combination of ingredients.
• an abrasive can be dispersed in water, and any buffering agents or other additives can be added to the suspension, and mixed by any method that is capable of incorporating the components into the CMP composition.
• the pH can be adjusted at any suitable time, as needed.
• the CMP compositions of the present invention also can be provided as a concentrate, which is intended to be diluted with an appropriate amount of water prior to use.
• the CMP composition concentrate can include the various components dispersed or dissolved in aqueous solvent in amounts such that, upon dilution of the concentrate with an appropriate amount of aqueous solvent, each component of the polishing composition will be present in the CMP composition in an amount within the appropriate range for use (e.g., to afford the desired pH level after dilution).
• the invention also provides a method of chemically-mechanically polishing a substrate that includes an ITO surface.
• the preferred method comprises (i) contacting the ITO surface of the substrate with a polishing pad and a CMP composition of the invention as described herein, and (ii) moving the polishing pad relative to the surface of the substrate with the polishing composition therebetween, thereby abrading at least a portion of an ITO from the surface.
• the CMP methods of the present invention are particularly suited for use in conjunction with a chemical-mechanical polishing apparatus.
• the CMP apparatus comprises a platen, which, when in use, is in motion and has a velocity that results from orbital, linear, and/or circular motion, a polishing pad in contact with the platen and moving with the platen when in motion, and a carrier that holds a substrate to be polished in contact with the pad and moving relative to the surface of the polishing pad.
• a CMP composition is typically pumped onto the polishing pad to aid in the polishing process.
• the polishing of the substrate is accomplished by the combined abrasive action of the moving polishing pad and the CMP composition of the invention present on the polishing pad, which abrades at least a portion of the surface of the substrate, and thereby polishes the surface.
• a substrate can be planarized or polished with a CMP composition of the invention using any suitable polishing pad (e.g., polishing surface).
• suitable polishing pads include, for example, woven and non-woven polishing pads.
• suitable polishing pads can comprise any suitable polymer of varying density, hardness, thickness, compressibility, ability to rebound upon compression, and compression modulus.
• Suitable polymers include, for example, polyvinylchloride, polyvinylfluoride, nylon, fluorocarbon, polycarbonate, polyester, polyacrylate, polyether, polyethylene, polyamide, polyurethane, polystyrene, polypropylene, coformed products thereof, and mixtures thereof.
• the CMP apparatus further comprises an in situ polishing endpoint detection system, many of which are known in the art.
• Techniques for inspecting and monitoring the polishing process by analyzing light or other radiation reflected from a surface of the workpiece are known in the art. Such methods are described, for example, in U.S. Patent 5,196,353 to Sandhu et al, U.S. Patent 5,433,651 to Lustig et al., U.S. Patent 5,949,927 to Tang, and U.S. Patent 5,964,643 to Birang et al.
• the inspection or monitoring of the progress of the polishing process with respect to a workpiece being polished enables the determination of the polishing end-point, i.e., the determination of when to terminate the polishing process with respect to a particular workpiece.
• This example illustrates the performance of conventional CMP compositions for removal of ITO from a substrate, compared to compositions of the invention.
• Wafers (4 inches by 4 inches) having an ITO surface layer (1500 A of ITO deposited on a glass substrate) were polished on a Hyprez table-top polisher using a Betalap or FK-Nl polishing pad, with a platen speed of 45-65 rpm, a carrier speed of 40-60 rpm, a down force of 0.3 to 1.75 psi, and a slurry flow rate of 40 mL/minute.
• the CMP slurry compositions which were evaluated had the formulations shown below.
• Slurry A 12% by weight of fumed silica (mean particle size of 140 nm, surface area of 90 m 2 /g) dispersed in deionized water. The pH of slurry was adjusted to 10 with potassium hydroxide.
• Slurry B - 5% by weight of colloidal silica (mean particle size of 75 run, surface area of 80 m 2 /g), dispersed in deionized water. The pH of slurry was adjusted to 10 with potassium hydroxide.
• Slurry C - 0.5% by weight of ceria (mean particle size of 80 nm, surface area of 60 m 2 /g) dispersed in deionized water.
• the pH of slurry was adjusted to 2 with nitric acid.
• Slurry D 0.5% by weight of ceria (mean particle size of 80 nm, surface area of 60 m 2 /g) dispersed in deionized water.
• the pH of slurry was adjusted to 5 with nitric acid.
• Slurry E 0.5% by weight of ceria (mean particle size of 80 nm, surface area of 60 m 2 /g) dispersed in deionized water.
• the pH of slurry was adjusted to 10.5 with potassium hydroxide.
• the pH of slurry was adjusted to 5 with nitric acid.
• the pH of slurry was adjusted to 10.5 with potassium hydroxide.
• the pH of slurry was adjusted to 10.5 with potassium hydroxide.
• Slurry J - 5% by weight of colloidal silica (mean particle size of 25 nm, surface area of 200 m 2 /g) dispersed in deionized water.
• the pH of slurry was adjusted to 2.5 with nitric acid.
• Slurry K - 5% by weight of colloidal silica (mean particle size of 40 nm, surface area of 80 m 2 /g) dispersed in deionized water. The pH of slurry was adjusted to 2.5 with nitric acid.
• Slurry L - 5% by weight of colloidal silica (mean particle size of 43 nm, surface area of 130 m 2 /g) dispersed in deionized water. The pH of slurry was adjusted to 2.5 with nitric acid.
• the pH of slurry was adjusted to 2.5 with nitric acid.
• the surface roughness of the ITO wafers was determined before and after polishing.
• the mean surface roughness values (Ra, nm) were determined by atomic force microscopy (AFM).
• Table 1 provides mean surface roughness values (Ra) for the center and edge of each wafer, and the observed percentage of improvement in roughness after polishing.
• the improvement in surface roughness was determined by taking the difference between the pre-polisbing and post-polishing roughness, dividing by the pre- polishing roughness, and then multiplying by 100.
• the results in Table 1 indicate that the compositions of the invention comprising zirconium oxide (zirconia) or colloidal silica, and having a mean particle size of not more than 150 nm, provided a significantly and unexpectedly greater improvement in surface roughness compared to the other compositions tested. This was particularly evident for compositions N, O, and P, which exhibited improvements of 80% or greater, and post-polishing mean surface roughness values in that range of 0.1S5 to 0.243.
• the light transmittance of the ITO wafer polished with composition J was also evaluated at three wavelengths: 700 nm (red), 530 nm (green), and 465 ran (blue).
• the transmittance at 700 nm went from 83.1 percent (pre-polishing), to 85.6 percent (post polishing).
• the transmittance at 465 nm went from 86 percent (pre-polishing), to 89.8 percent (post polishing).
• the green light transmittance remained the same (83.1 percent pre-polishing and 82.2 percent post-polishing).

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Finish Polishing, Edge Sharpening, And Grinding By Specific Grinding Devices (AREA)
• Mechanical Treatment Of Semiconductor (AREA)

Priority Applications (3)

Applications Claiming Priority (4)

Publications (1)

Family

ID=38371856

Family Applications (1)

Country Status (7)

Cited By (2)

Families Citing this family (16)

Citations (3)

Family Cites Families (13)

• 2007
  • 2007-02-14 CN CN2007800029169A patent/CN101370898B/zh not_active Expired - Fee Related
  • 2007-02-14 JP JP2008554444A patent/JP5431736B2/ja not_active Expired - Fee Related
  • 2007-02-14 WO PCT/US2007/003978 patent/WO2007095322A1/en not_active Ceased
  • 2007-02-14 TW TW096105914A patent/TWI341325B/zh not_active IP Right Cessation
  • 2007-02-14 KR KR1020087022358A patent/KR101333866B1/ko not_active Expired - Fee Related
  • 2007-02-14 US US11/706,929 patent/US20070190789A1/en not_active Abandoned
• 2008
  • 2008-08-12 MY MYPI20083062A patent/MY154806A/en unknown