WO2007094379A1 - ハニカム構造体及びハニカム触媒体 - Google Patents

ハニカム構造体及びハニカム触媒体 Download PDF

Info

Publication number
WO2007094379A1
WO2007094379A1 PCT/JP2007/052652 JP2007052652W WO2007094379A1 WO 2007094379 A1 WO2007094379 A1 WO 2007094379A1 JP 2007052652 W JP2007052652 W JP 2007052652W WO 2007094379 A1 WO2007094379 A1 WO 2007094379A1
Authority
WO
WIPO (PCT)
Prior art keywords
peak
honeycomb
honeycomb structure
catalyst
pore
Prior art date
Application number
PCT/JP2007/052652
Other languages
English (en)
French (fr)
Inventor
Shinji Yamaguchi
Original Assignee
Ngk Insulators, Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ngk Insulators, Ltd. filed Critical Ngk Insulators, Ltd.
Priority to EP07714205A priority Critical patent/EP1985365A1/en
Priority to JP2008500532A priority patent/JPWO2007094379A1/ja
Publication of WO2007094379A1 publication Critical patent/WO2007094379A1/ja
Priority to US11/858,659 priority patent/US20080070776A1/en

Abstract

　触媒担持性に優れるとともに、ハニカム触媒体に適用された場合、浄化効率に優れ、圧力損失が小さく、限られた空間であっても搭載可能なハニカム触媒体とすることが可能なハニカム構造体、及び浄化効率に優れ、圧力損失が小さく、限られた空間であっても搭載可能なハニカム触媒体を提供する。二つの端面２ａ，２ｂ間を連通する複数のセル３が形成されるように配置された、多数の細孔を有する多孔質な隔壁４と、セル端部２ａ，２ｂまたはセル内部の少なくとも一部にガス通過防止部１０を備え、実質的に隔壁４内をガスが流れるようにした触媒担体用のハニカム構造体１において、隔壁４の細孔２５の細孔径分布（細孔径の大きさを横軸にその細孔容積を縦軸にしてプロットされたグラフで表示される）を、細孔径の大きさが０．０５μｍ以上の領域において、細孔容積に関し、２つ以上のピークを有するように構成する。

Description

明 細 書
ハニカム構造体及びハニカム触媒体
技術分野
[0001] 本発明は、 自動車用、建設機械用、及び産業用定置エンジン、並びに燃焼機器等 力 排出される排ガスに含まれる、一酸化炭素（C〇）、炭化水素 (HC)、窒素酸化物 (NO )、硫黄酸化物（SO )等の被浄化成分の浄化に好適に用いられるハニカム構
X X
造体及びハニカム触媒体に関する。
背景技術
[0002] 現在、各種エンジン等から排出される排ガスを浄化するために、ハニカム構造体に 触媒を担持したハニカム触媒体が用いられている。このハニカム触媒体は、図 5に示 すように、セル 3を形成する隔壁 4の表面に触媒層 15が担持された構造を有するもの である。また、図 6、 7に示すように、このハニカム触媒体 60 (ハニカム構造体 11)を用 いて排ガスを浄化するに際しては、一の端面 2a側力 ハニカム触媒体 60のセル 3に 排ガスを流入させ、隔壁 4表面の触媒層（図示せず）に排ガスを接触させ、次いで、 他の端面 2bの側から外部へと流出させることにより行われる（例えば、特許文献 1参 照）。
[0003] このようなハニカム触媒体を用いて排ガスを浄化する場合には、排ガスから隔壁表 面の触媒層に向けての、排ガスに含まれる被浄化成分の伝達を可能な限り促進させ 、浄化効率を向上させる必要がある。排ガスの浄化効率を向上させるためには、セル の水力直径を小さくすること、及び隔壁の表面積を大きくすること等が必要である。具 体的には、単位面積当りのセル数 (セル密度）を増加させる方法等が採用される。
[0004] ここで、排ガスから隔壁表面の触媒層に向けての被浄化成分の伝達率は、セルの 水力直径の二乗に反比例して増加することが知られている。このため、セル密度を増 カロさせるほど、被浄化成分の伝達率は向上する。し力しながら、圧力損失も、セルの 水力直径の二乗に反比例して増加する傾向にある。従って、被浄化成分の伝達率 の向上に伴って、圧力損失が増加してしまうという問題がある。
[0005] なお、隔壁表面の触媒層の厚さは、通常、数十 μ m程度である。ここで、触媒層内 におレ、て被浄化成分が拡散する速度が不十分である場合には、ハニカム触媒体の 浄化効率が低下する傾向にある。この傾向は、特に低温条件下で顕著である。この ため、浄化率が低い分、触媒担持量を増やすと触媒層が厚くなり、圧力損失が上昇 する。同一触媒量の場合、触媒層を薄くし、触媒担持面積を増やして、浄化率を確 保する必要があるが、表面積を増やすとセル密度が増加し、圧力損失が上昇すると レ、う問題がある。
[0006] 排ガスの浄化効率を高めつつ、圧力損失を低減させるためには、ハニカム触媒体 の流入径を大きくするとともに、流通させる排ガスの流速を下げる必要がある。しかし 、ハニカム触媒体を大型化等した場合には、例えば車載用のハニカム触媒体等につ レ、ては搭載スペースが限定されるため、搭載が困難になる場合もある。
特許文献 1 :特開 2003— 33664号公報
発明の開示
[0007] 本発明は、上述の従来技術の有する問題点に鑑みてなされたものであり、触媒担 持性に優れるとともに、ハニカム触媒体に適用された場合、浄化効率に優れ、圧力 損失が小さぐ限られた空間であっても搭載可能なハニカム触媒体とすることが可能 なハニカム構造体、及び浄化効率に優れ、圧力損失が小さぐ限られた空間であつ ても搭載可能なハニカム触媒体を提供することを目的とする。尚、本発明は、スス捕 集を目的としたフィルターではなレ、。 50 z m以上の細孔ピークを有することにより、例 えススを有する排気ガスが流れた場合でも、スス閉塞を起こしにくぐ圧損上昇を防ぐ こと力 Sできる。
[0008] 上記目的を達成するため、本発明によれば、以下のハニカム構造体及びハニカム 触媒体が提供される。
[0009] [1]二つの端面間を連通する複数のセルが形成されるように配置された、多数の細 孔を有する多孔質な隔壁と、セル端部またはセル内部の少なくとも一部にガス通過 防止部（目封じ部）を備え、実質的に前記隔壁内をガスが流れるようにした触媒担体 用のハニカム構造体であって、前記隔壁の細孔の細孔径分布（細孔径の大きさを横 軸にその細孔容積を縦軸にしてプロットされたグラフで表示される）力 細孔径の大き さが 0. 05 μ ΐη以上の領域において、細孔容積に関し、 2つ以上のピークを有し、 2 つ以上のピークのうちの少なくとも 1つが、細孔径の大きさが 50 /i m以上の領域に存 在することを特徴とするハニカム構造体。
[0010] [2]前記 2つ以上のピークのうちの任意の 2つのピークである第 1のピーク（P1)及び 第 2のピーク（P2)において、前記第 1のピーク（P1)における細孔容積 (N1)を対数（ log)微分細孔容積で表した場合、その値が、 0. 0：!〜 3. OccZgであり、前記第 2の ピーク (P2)における細孔容積 (N2)を対数 (log)微分細孔容積で表した場合、その 値力 0. 01-5. OccZgである前記 [1]に記載のハニカム構造体。
[0011] [3]前記 2つ以上のピークのうちの任意の 2つのピークである第 1のピーク（P1)及び 第 2のピーク（P2)において、前記第 1のピーク（P1)における細孔容積 (N1)と前記 第 2のピーク (P2)における細孔容積 (N2)との比 (N1： N2)が、 1： 100〜10： 1であ る前記 [1]に記載のハニカム構造体。
[0012] [4]前記第 1のピーク（P1)における細孔径の大きさ（S1)力 S、：!〜 35 x mであり、前 記第 2のピーク（P2)における細孔径の大きさ（S2)力 50-500 μ mである前記 [1]
〜 [3]のレ、ずれかに記載のハニカム構造体。
[0013] [5]前記第 1のピーク（P1)における細孔径の大きさ（S1)と前記第 2のピーク（P2)に おける細孔径の大きさ (S2)との比 (S1： S2)が、 1： 10000〜4： 5である前記 [2]〜 [
4]のレ、ずれかに記載のハニカム構造体。
[0014] [6]前記 [1]〜[5]のいずれかに記載のハニカム構造体に、触媒が担持されてなる ハニカム触媒体。
[0015] [7]前記ハニカム構造体が、前記触媒の担持された状態においても、前記 [1]〜[5] のいずれかに記載の、前記隔壁の細孔における細孔径分布の条件を満足する前記 [6]に記載のハニカム触媒体。
[0016] [8]前記 [1]〜[5]のいずれかに記載のハニカム構造体、又は前記 [6]又は [7]に 記載のハニカム触媒体を用いた排ガス処理システム。
[0017] 本発明によって、触媒担持性に優れるとともに、ハニカム触媒体に適用された場合 、浄化効率に優れ、圧力損失が小さぐ限られた空間であっても搭載可能なハニカム 触媒体とすることが可能なハニカム構造体、及び浄化効率に優れ、圧力損失が小さ ぐ限られた空間であっても搭載可能なハニカム触媒体が提供される。 図面の簡単な説明
[0018] [図 1]本発明のハニカム構造体及びハニカム触媒体の一の実施の形態を模式的に 示す説明図である。
[図 2]図 1に示すハニカム構造体及びハニカム触媒体の断面図である。
[図 3]図 1に示すハニカム構造体及びハニカム触媒体の一部を拡大した部分拡大図 である。
[図 4]図 1〜3に示すハニカム構造体及びハニカム触媒体の隔壁の細孔の細孔径分 布の一例を示すグラフである。
[図 5]従来のハニカム触媒体の一例を模式的に示す部分拡大図である。
[図 6]従来のハニカム構造体及びハニカム触媒体の一例を模式的に示す正面図であ る。
[図 7]従来のハニカム構造体及びハニカム触媒体の一例を模式的に示す断面図であ る。
[図 8]実施例 4のハニカム触媒体の隔壁の細孔の細孔径分布を示すグラフである。 符号の説明
[0019] 1 ：ハニカム構造体
2a :端面
2b :端面
3 ：セル
4 ：隔壁
5 ：触媒層
10 :ガス通過防止部
15 :触媒層
11 :ハニカム構造体
20 :外壁
21 :ハニカム構造体
25 :細孔
31 :ハニカム構造体 35 :触媒層担持細孔
41 :ハニカム構造体
50 :ハニカム触媒体
60 :ハニカム触媒体
D ：セル水力直径
H ：リブ残り高さ
P ：セルピッチ
τ ：隔壁厚さ。
発明を実施するための最良の形態
[0020] 以下、本発明を実施するための最良の形態を図面を参照しつつ具体的に説明する 図 1は、本発明のハニカム構造体及びハニカム触媒体の一の実施の形態を模式的 に示す説明図である。図 2は、図 1示すハニカム構造体及びハニカム触媒体の断面 図である。図 3は、図 1に示すハニカム構造体及びハニカム触媒体の一部を拡大した 部分拡大図である。図 4は、図 1〜3に示すハニカム構造体及びハニカム触媒体の隔 壁の細孔の細孔径分布の一例を示すグラフである。図:!〜 4に示すように、本実施の 形態のハニカム構造体は、二つの端面 2a， 2b間を連通する複数のセル 3が形成さ れるように配置された、多数の細孔 25 (図 3参照）を有する多孔質な隔壁 4と、二つの 端面 2a， 2bにおけるセル 3の端部のいずれか一方を交互に封止するように配置され た目封止部 10とを備えた触媒担体用のハニカム構造体 1であって、隔壁 4の細孔 25 の細孔径分布（細孔径の大きさを横軸にその細孔容積を縦軸にしてプロットされたグ ラフで表示される）力 細孔径の大きさが 0. 05 z m以上の領域において、細孔容積 に関し、 2つ以上のピークを有する（図 4においては、 2つのピーク Pl、 P2を示す）こ とを特徴とするものである。なお、図 1中、符号 20は外壁、符号 Pはセルピッチ、符号 Dはセル水力直径、及び符号 Tは隔壁厚さをそれぞれ示す。
[0021] このように細孔径の大きさが 0. 05 /i m以上、好ましくは、 0. 5 μ ΐη以上の領域にお いて、細孔容積に関し、 2つ以上のピークを有するものとすることによって、ひとつの ピークを示す細孔内に触媒層を担持し、もうひとつのピークを示す細孔は、触媒担持 工程において、隔壁内に触媒層を導入する流路となった上で、触媒担持後には、表 面積を多く持つ排ガスの実質的な流路とすることができる。その結果、触媒担持性に 優れるとともに、ハニカム触媒体に適用された場合、触媒担持表面積が増えることに より浄化効率に優れ、片方のピークを示す細孔内に触媒が染み込み、保持されるこ とにより、もうひとつのピークを示す細孔径を狭めることが少ないため、圧力損失が小 さぐ限られた空間であっても搭載可能なハニカム触媒体とすることが可能なハニカ ム構造体を提供することができる。
[0022] 本実施の形態においては、 2つ以上のピークのうちの少なくとも 1つ力 細孔径の大 きさが 50 μ m以上の領域に存在することが好ましぐ 71 μ m以上の領域に存在する ことがさらに好ましい。ススを含む排気ガスが流れる場合においては、 l OO x m以上 の領域に存在することが望ましぐ更に、 150 z m以上の領域に存在することが、スス 閉塞による圧損上昇を防止できる点で好ましい。
[0023] このように 2つ以上のピークのうちの少なくとも 1つが、細孔径の大きさが 50 μ m以 上の領域に存在するものとすることによって、触媒を壁内に導入可能とし、 自らの細 孔を塞ぐことなぐ薄く均一に触媒担持することができる上、高い触媒担持面積を確 保できる。従って、浄化効率の向上及び圧力損失の低減を図ることができる。
[0024] 本実施の形態においては、 2つ以上のピークのうちの任意の 2つのピークである第 1のピーク（P1 )及び第 2のピーク（P2)において、第 1のピーク（P1 )における細孔容 積 (N1 )を対数 (log)微分細孔容積で表した場合、その値が、 0. 01〜3. Occ/gで あることが好ましぐ 0. ：!〜 1. 5cc/gであることが、圧損上昇なぐ強度を確保できる ため、さらに好ましぐ第 2のピーク（P2)における細孔容積 (N2)を対数 (log)微分細 孔容積で表した場合、その値が、 0. 01 -5. Occ/gであることが好ましぐ 0. 4〜2. Occ/gであることが、圧損上昇なぐ強度を確保できるため、さらに好ましレ、。なお、「 対数 (log)微分細孔容積」とは、 dV/d (logD)です。これは、差分細孔容積 dVを、細 孔径の対数扱レ、の差分値 d (logD)で割った値を求め、これを各区間の平均細孔径 にメ寸してフロットしたもの (nttp://www.smmadzu.co.jp/ powder/lecture/practice/ p02/ lesson06.html解説参照）を意味する。
[0025] 第 1のピーク（P1 )における細孔容積 (N 1 )を対数 (log)微分細孔容積で表した場 合、その値が、 0. 01-3. Occ/gの範囲を外れたり、第 2のピーク（P2)における細 孔容積 (N2)を対数 (log)微分細孔容積で表した場合、その値が、 0. 01〜5. Occ /gの範囲を外れると、触媒担持性、浄化効率、及び圧力損失が悪化することがある
[0026] 前記第 1のピーク（P1)における細孔容積 (N1)と前記第 2のピーク（P2)における 細孔容積（N2)との比（Nl : N2)が、 1： 100〜10： 1であることが好ましレ、。この範囲 を外れると、触媒担持性、浄化効率、及び圧力損失が悪化することがある。前者は圧 力損失が良好であり、後者は浄化効率、触媒担持性、強度に優れる。圧力損失と触 媒担持性、浄化効率、強度のバランスを考えると、 1 : 30〜10 : 12が好ましい。
[0027] 本実施の形態においては、第 1のピーク（P1)における細孔径の大きさ（S1)力 1 〜35 z mであることが好ましぐ強度を確保する上では、 l〜10 z mであること力 触 媒性能面、圧損面からは、 10〜30 x mであることがさらに好ましぐ第 2のピーク（P2 )における細孔径の大きさ（S2)力 50〜500 111でぁることカ 子ましく、 71〜300 /i mであること力 スス閉塞を起こしにくく、高い浄化率を得ることができ、さらに好ましい 。第 1のピーク（P1)における細孔径の大きさ（S1)力 ：!〜 35 μ ΐηの範囲を外れたり、 第 2のピーク（P2)における細孔径の大きさ（S2)力 50-500 μ mの範囲を外れると 、触媒担持性、浄化効率、及び圧力損失が悪化することがある。
[0028] 本実施の形態においては、第 1のピーク（P1)における細孔径の大きさ（S1)と第 2 のピーク (P2)における細孔径の大きさ (S2)との比 (S1： S2)力 1： 10000〜4： 5で あることが好ましぐ 1 : 600〜： 1 : 5であることがさらに好ましい。第 1のピーク（P1)にお ける細孔径の大きさ（S1)と第 2のピーク（P2)における細孔径の大きさ（S2)との比（ S1 : S2)力 1 : 10000〜4 : 5の範囲を外れると、触媒担持性、浄化効率、及び圧力 損失が悪化することがある。
[0029] また、複数のセル 3の単位体積当たりの分布密度が 7〜200個 Zcm2、隔壁 4の厚 さが 0. 03〜lmm、平均細孔径が 10〜500 μ m、及び気孔率力 0〜80%であるこ と力好ましく、複数のセル 3の単位体積当たりの分布密度が 12〜： 120個 Zcm2、隔 壁 4の厚さが 0.：!〜 0. 6mm、平均細孔径が 45〜200 μ m、及び気孔率が 48〜65 %であることがさらに好ましい。複数のセル 3の単位体積当たりの分布密度が 7個 Zc m2未満であると、浄化性能が悪化することがあり、 200個/ cm2を超えると、圧力損 失が増加し、エンジン出力の低下を招くことがある。隔壁 4の厚さが 0. 03mm未満で あると、強度が弱くキヤユングできないことがあり、 1mmを超えると、圧力損失が増加 しエンジン出力の低下を招くことがある。平均細孔径が 10 z m未満であると、排気ガ ス中の微粒子が捕集され、細孔の閉塞を招くことがあり、 500 z mを超えると、浄化性 能が悪化することがある。また、気孔率が 40%未満であると、隔壁通過流速が増大 化し、浄化性能が悪化することがあり、 75%を超えると、強度が不十分となることがあ る。
[0030] なお、「気孔率」の定義については後述する。
[0031] このように構成することによって、触媒担持性及び浄化性能に優れ、圧力損失も許 容範囲内にあってエンジン出力の低下を起こすことがないとともに、排気中の微粒子 による閉塞も起こすことがなぐ長期間性能を維持することができる。
[0032] 本実施の形態のハニカム構造体 1を構成する材料としては、セラミックスを主成分と する材料、又は焼結金属等を好適例として挙げることができる。具体的には、セラミツ タスを主成分とする材料からなるものである場合、セラミックスとしては、炭化珪素、コ ージエライト、アルミナタイタネート、サイアロン、ムライト、窒化珪素、リン酸ジノレコニゥ ム、ジルコニァ、チタニア、アルミナ、若しくはシリカ、又はこれらを組み合わせたもの を好適例として挙げることができる。特に、炭化珪素、コージエライト、ムライト、窒化珪 素、アルミナ、アルミナタイタネート等のセラミックス力 S、耐アルカリ特性上好適である。 中でも酸化物系のセラミックスは、コストの点でも好ましい。
[0033] 本実施の形態のハニカム構造体 1の、 40〜800°Cにおける、セルの連通方向の熱 膨張係数は、 1. 0 X 10_6/°C未満であることが好ましぐ 0. 8 X 1CT6未満 /°Cであ ること力 車両床下搭載の場合にさらに好ましぐ 0. 5 X 10_6未満 /°Cであることが、 エンジン直下搭載の場合に特に好ましい。 1. 0 X 10— 6/°C未満であると、高温の排 気ガスに晒された際の発生熱応力を許容範囲内に抑えられ、ハニカム構造体の熱 応力破壊を防止することができる。
[0034] また、本実施の形態のハニカム構造体 1の、セルの連通方向に垂直な面で切断し た断面の形状は、設置しょうとする排気系の内形状に適した形状であることが好まし レ、。具体的には、円、楕円、長円、台形、三角形、四角形、六角形、又は左右非対称 な異形形状を挙げることができる。中でも、円、楕円、長円が好ましい。
[0035] 本発明のハニカム構造体は、例えば、従来公知のディーゼルパティキュレートフィ ルター（DPF)の製造方法に準拠して、製造することができる。従って、例えば、材料 の化学組成を適宜調整することによって、また、原料の粒子径を適宜選択することに よって、さらに、造孔剤を用いて多孔質構造とする場合には、用いる造孔剤の種類、 粒子径、添加量等を適宜調整すること等によって、気孔率、細孔径を所定の数値範 囲内とすることができる。
[0036] 次に、本発明のハニカム触媒体の一の実施の形態について説明する。図:!〜 3に 示すように、本実施の形態のハニカム触媒体 50は、上述のハニカム構造体 1に、触 媒が担持されてなるものであり、図 3には、ハニカム構造体 1と、触媒を含有する触媒 層 5とを備えたものとして示されている。触媒層 5は、細孔 25の内表面に担持されて おり、多数の触媒担持細孔 35が隔壁 4の内部に形成されている。なお、触媒担持細 孔 35は、隣接するセル 3同士を相互に連通している。また、触媒層 15は、セル 3の、 触媒担持細孔 35を除く内表面に形成されてレ、てもよレ、。
[0037] ハニカム構造体 1の隔壁 4は、上述のように、ハニカム構造体 1の細孔 25内表面に 触媒層 5を担持した本実施の形態のハニカム触媒体 50においては、ディーゼルェン ジン力 排出される排ガスに含まれるカーボン微粒子等が隔壁 4で捕捉され難ぐそ れらのほとんどが通過する。即ち、図 2に示すように、一の端面 2a側からハニカム触 媒体 50のセル 3に流入した排ガスは、隔壁 4を通過して隣接するセル 3へと移動し、 次いで、他の端面 2bの側から外部へと流出する。従って、本実施の形態のハニカム 触媒体 50は、圧力損失が小さぐまた長期間使用した場合であっても圧力損失の上 昇し難レ、ものである。
[0038] 本実施の形態のハニカム触媒体 50は、セル 3の内表面に触媒層 5が担持されたガ ス通過防止部（目封じ部と同義）を持たない従来のハニカム触媒体とは異なり、セル 3 (隔壁 4)の細孔 25の内表面にも触媒層 5が担持され、セル端部または内部の少なく とも一部にガス通過防止部を備え、実質的に隔壁内をガスが流れるような構造とした ものである。従って、表面積の増加により、ガスと担体との接触機会が増加し、従来の ハニカム触媒体に比してより浄化効率に優れ、限られた空間であっても搭載可能な、 コンパクトな触媒体となる。
[0039] 本実施の形態のハニカム触媒体 50は、ハニカム構造体 1が、触媒の担持された状 態においても、上述のような、隔壁の細孔における細孔径分布の条件を満足するも のであることが好ましい。このように構成することによって、上述の効果を十全に発揮 させること力できる。
[0040] また、上述のように、触媒層 5が担持された状態、すなわち、触媒担持細孔 35が形 成された状態の場合における隔壁 4の気孔率は、 30〜75%であることが好ましぐ 4 0〜65%であることがさらに好ましい。 30%未満であると、隔壁通過流速が増大化し 、浄化性能が悪化することがある。 75%を超えると、強度が不十分となることがある。
[0041] 本実施の形態のハニカム触媒体 50を構成する触媒層 5に含有される触媒の具体 例としては、（1)ガソリンエンジン排ガス浄化三元触媒、（2)ガソリンエンジン又はディ ーゼルエンジン排ガス浄化用の酸化触媒、（3) NO選択還元用 SCR触媒、 (4) NO
X
吸蔵触媒、を挙げることができる。
X
[0042] ガソリンエンジン排ガス浄化三元触媒は、ハニカム構造体 (ハニカム担体）の隔壁を 被覆する担体コートと、この担体コートの内部に分散担持される貴金属とを含むもの である。担体コートは、例えば、活性アルミナにより構成されている。また、担体コート の内部に分散担持される貴金属としては、 Pt、 Rh、若しくは Pd、又はこれらを組み合 わせたものを好適例として挙げることができる。さらに、担体コートには、例えば、酸化 セリウム、酸化ジノレコニァ、シリカ等の化合物、又はこれらを組み合わせた混合物が 含有される。なお、貴金属の合計量を、ハニカム構造体の体積 1リットル当り、 0. 17 〜7. 07gとすることが好ましい。
[0043] ガソリンエンジン又はディーゼルエンジン排ガス浄化用の酸化触媒には、貴金属が 含有される。この貴金属としては、 Pt、 Rh、及び Pdからなる群より選択される一種以 上が好ましい。なお、貴金属の合計量を、ハニカム構造体の体積 1リットル当り、 0. 1 7〜7. 07gとすることが好ましい。また、 N〇選択還元用 SCR触媒は、金属置換ゼ
X
オライト、バナジウム、チタニア、酸化タングステン、銀、及びアルミナからなる群より選 択される少なくとも一種を含有するものである。 [0044] NO吸蔵触媒には、アルカリ金属、及び/又はアルカリ土類金属が含有される。ァ
X
ルカリ金属としては、 K、 Na、 Liを挙げること力 Sできる。アルカリ土類金属としては、 Ca を挙げることができる。なお、 K、 Na、 Li、及び Caの合計量を、ハニカム構造体の体 積 1リットル当り、 5g以上とすることが好ましい。
[0045] 本発明のハニカム触媒体は、上述のハニカム構造体に、従来公知の方法に準じた 製造方法に従って、触媒を担持することにより製造することができる。具体的には、先 ず、触媒を含有する触媒スラリーを調製する。次いで、この触媒スラリーを、吸引法等 の方法により、ハニカム構造体の隔壁の細孔表面にコートする。その後、室温又は加 熱条件下で乾燥することにより、本発明のハニカム触媒体を製造することができる。
[0046] また、本実施の形態のハニカム構造体及びハニカム触媒体は、種々の排ガス処理 システムに有効に用いることができる。
実施例
[0047] 以下、本発明を実施例に基づいて具体的に説明するが、本発明はこれらの実施例 に限定されるものではない。なお、本実施例において、細孔径及び細孔分布、気孔 率、触媒担持性、浄化指数、並びに圧力損失は、以下のようにして測定した。
[0048] [細孔径及び細孔分布]：
細孔径が 300 x m以下の場合、 JIS R1655— 2003に準拠し、水銀ポロシメータ 一にて測定した。具体的には、 1cm3の測定試料を切り出して測定し、細孔径と細孔 容積の関係を求め、「細孔分布」とし、測定上の区間平均細孔径を「細孔径」とした。 測定上の細孔径区間は、市販の水銀ポロシメーターで定義されるが、以下のように 水銀圧入時の圧力から求められる。対数で等間隔になることが好ましぐ細孔径 1桁 あたり 8〜： 16分割する。 l x m以下は 3— 8分割とする。水銀圧入法による圧力例を 以下の表 1に示す。
[0049] [表 1] 水銀圧入圧力 換算された細孔径
(psia) ( ^ m )
0.60 300.00
0.66 272.10
0.95 1 90.71
1.24 145.26
1.55 1 16.81
1.95 92.70
2.45 73.53
3.05 59.24
3.83 47.08
4.84 37.26
6.1 3 29.44
7.82 23.08
9.91 18.20
1 2.52 14.42
1 5.80 1 1.42
20.09 8.98
23.48 7.69
26.63 6.78
28.1 9 6.40
29.76 6.06
33.76 5.35
37.81 4.77
47.84 3.77
60.77 2.97
76.98 2.34
97.42 1 .85
1 98.39 0.91
822.1 1 0.22
3407.88 0.05
9961.32 0.02
細孔径を測定する際の圧力変動等のノィズは無視する。 細孔径が 300 μ m以上の場合、画像解析により細孔径を測定し、各細孔径の空隙 面積比率を算出した。具体的には、隔壁断面の SEM写真を、測定対象細孔径の 10 100倍の視野について少なくとも 5視野観察する。壁断面厚みが足りない場合が 想定されるので、その場合は、少なくとも 1方向での視野が確保されていれば良い。 次いで、観察したそれぞれの視野内で、各空隙中の最大直線距離とその空隙面積 を計測する。計測は、観察写真を画像処理することで求めることができる。空隙が連 通して見える場合、最大径に対し、 1/10の隙間は連通していないと見なす。各空隙 の各最大径とその空隙面積を上記方法により求め、そのトータル空隙面積に対する 比率から、各細孔径の空隙面積比率を求める。 300 μ ΐη以下との連続性を比較する 場合、境界となる 300 / mと空隙面積率を基準とし、相対比較として、対数微分容積 を各比率で表すことができる。細孔径区間は、対数で等間隔となるよう設定する。区 間は 100 a m力 1000 μ mを 8分割以上 16分割以下とする。
[0051] [気孔率] :
細孔径が 300 x m未満の場合、水銀ポロシメーターにて測定した。具体的には、 1 cm3の測定試料を切り出して細孔容積を測定し、次式により「気孔率」を求めた。 気孔率 =総細孔容積/〔 ( 1 /真比重） +総細孔容積〕
細孔径が 300 μ m以上の場合、材料理論密度から求められる容積当たりの重量と 、実際の試験片重量の比から求めた。
気孔率 = (1一（実際の試験片重量 Z理論密度から求めた重量)） X 100
ハニカム構造状の試験片から気孔率を求める場合は、そのセル形状（開口率）を考 慮して算出する。
[0052] [触媒担持性] :
隔壁断面の SEM写真により、隔壁内部まで触媒担持されているかを観察し、セル 内壁表面から、どれだけ触媒担持されているかどうかで判断した。隔壁厚みの 20% 以上担持されていることが好ましぐ隔壁総厚みまで担持されていることが更に好まし レ、。ここでの触媒担持部は、隔壁厚み方向に連通する一つのピークをもつ細孔内を 示す。なお、表中、◎は、 40— 100%担持、〇は、 20— 40%担持、 Xは、く 10%担 持を示す。
[0053] [浄化指数] :
酸素 7体積％、水蒸気 10体積％、二酸化炭素 10体積％、炭化水素 200 (カーボン モル数) ppm、及び残部が窒素からなる燃焼ガスを、空間速度（SV OOOOOIT1 温度 200°Cの条件でハニカム構造体内、又はハニカム触媒体内に流入させた。流入 前後における燃焼ガスの炭化水素濃度から、浄化率（％)を算出した。比較対照のハ 二カム触媒体を使用して浄化率 (基準浄化率（％) )を算出し、この基準浄化率に対 する割合として、浄化指数（％)を算出した。ここで、浄化指数 = 200%とは、比較対 照のハニカム触媒体の 2倍の浄化率であることを意味する。なお、自動車用途を想定 したハニカム触媒体については、セル密度 600cpsi (93個/ cm2)、隔壁厚さ 4. 5mi 1 (0. 1143mm)の単純ハニカム構造体（目封止部なし）に触媒を担持したものを用 レ、た場合を比較対照とした。また、産業用途を想定したハニカム触媒体については、 セル密度 30cpsi (4. 65個/ cm2)、隔壁厚さ 32mil (0. 8128mm)の単純ハニカム 構造体（目封止部なし）に触媒を担持したものを用いた場合を比較対照とした。なお 、表中、 © fま、 > 150ο/ο、〇ίま、 100- 150%, X fま、 < 70ο/οを示す。
[0054] [圧力損失] :
ハニカム構造体の容積当たり 3g/Lのスス発生量相当の時間、排気ガスを通気し た後、ハニカム構造体の容積当たり 2. 4Nm3/minLの空気を通気させた時の圧力 損失を測定した。なお、表中、◎は、 < 7. 5kPa、〇は、 7. 5 _ 10kPa、△は、 10— 15kPa、 Xは、 > 15kPaを示す。
[0055] (実施例:!〜 7)
タルク、カオリン、仮焼カオリン、アルミナ、水酸化カルシウム、及びシリカのうちから 複数を組み合わせて、その化学組成が、 Si〇 42〜56質量％、 Al O 0〜45質量％
2 2 3
、及び Mg012〜： 16質量％となるように所定の割合で調合されたコージエライトィ匕原 料 100質量部に対して、造孔剤としてグラフアイトを 12〜25質量部、及び合成樹脂 を 5〜： 15質量部を添カ卩した。さらに、メチルセルロース類、及び界面活性剤をそれぞ れ適当量添加した後、水を加えて混練することにより坏土を調製した。調製した坏土 を真空脱気した後、押出成形することによりハニカム成形体を得た。得られたハニカ ム成形体を乾燥後、最高温度 1400〜1430°Cの温度範囲で焼成することにより、ハ 二カム焼成体を得た。得られたハニカム焼成体のセルのいずれかの端部に、巿松模 様状となるように目封止剤を詰めて再度焼成することにより、表 2に示すような隔壁の 細孔構造を有する、直径 144mm、全長 152mmのハニカム構造体（作製番号:!〜 7 )を作製した (得られたハニカム構造体は、本来、本発明における実施例であり、実施 例の番号で表示することもできるが、便宜上、ハニカム構造体は作製番号による表示 とし、これらのハニカム構造体を用いて最終的にハニカム触媒体としたものを実施例 としてその番号を表示した）。なお、隔壁の細孔構造は、コージエライト化原料の化学 組成、造孔剤の粒子径、造孔剤の添加量等を適宜調整することにより調整した。また
、 目封止部の目封止深さは、端面から 5mmとした。
[0056] 次いで、貴金属として白金 (Pt)を含有し、活性アルミナ、及び酸素吸蔵剤としての セリアをさらに含有する触媒スラリーを調製した。吸引法により、上記で得られた作製 番号 1〜7のハニカム構造体の隔壁内表面、及び細孔内表面に、調製した触媒スラリ 一のコート層を形成した。次いで、加熱乾燥することにより、隔壁 (触媒層つき）の細 孔構造を有するハニカム触媒体（実施例:!〜 7)を作製した。なお、ハニカム構造体（ 担体） 1リットルあたりの貴金属（Pt)の量は 2gとした。また、ハニカム構造体 (担体） 1リ ットルあたりの触媒スラリーのコート量は 100gとした。
[0057] 実施例 1〜7で作製したハニカム触媒体に用いたハニカム構造体の作製番号、径
X長さ、セル密度（cpsi)、セル密度（1/cm2)、隔壁厚さ（mil)、隔壁厚さ（mm)、細 孔径、ピークの存在する領域、第 1のピーク (P1)の対数 (log)微分細孔容積、第 2の ピーク（P2)の対数 (log)微分細孔容積、第 1のピーク（P1)における細孔容積 (N1) と第 2のピーク（P2)における細孔容積 (N2)との比（N1： N2)、第 1のピーク（P1)に おける細孔径の大きさ（S1)、第 2のピーク（P2)における細孔径の大きさ（S2)、第 1 のピーク（P1)における細孔径の大きさ（S1)と第 2のピーク（P2)における細孔径の 大きさ（S2)との比（S1 : S2)、気孔率、触媒担持性、浄化指数及び圧力損失を、表 2 に示す。
[0058] (比較例:!〜 5)
実施例 1と同様の構造で、セル密度、リブ厚、細孔径、細孔分布が異なるハニカム 構造体 (作製番号が比較：!〜 5)を作製し、このハニカム構造体を用いて実施例 1と同 様にして触媒体を作製した。比較例 1〜5で作製した触媒体に用いたハニカム構造 体の作製番号、径 X長さ、セル密度（cpsi)、セル密度（lZcm2)、隔壁厚さ（mil)、 隔壁厚さ（mm)、細孔径、ピークの存在する領域、第 1のピーク（P1)の対数 (log)微 分細孔容積、第 2のピーク（P2)の対数 (log)微分細孔容積、第 1のピーク (P1)にお ける細孔容積 (N1)と第 2のピーク（P2)における細孔容積 (N2)との比（N1： N2)、 第 1のピーク（P1)における細孔径の大きさ（S1)、第 2のピーク（P2)における細孔径 の大きさ（S2)、第 1のピーク（P1)における細孔径の大きさ（S1)と第 2のピーク（P2) における細孔径の大きさ（S2)との比（SI : S2)、気孔率、触媒担持性、浄化指数及 ぴ圧力損失を、表 2に示す。
[表 2]
Figure imgf000019_0001
察）
実施例 1は、本発明の代表的な（最良の）実施例を示しており、実施例 2は、第 2の ピーク（P2)における細孔径の大きさ（S2)が小さい場合を示す。実施例 3は、第 1の ピーク (P1)の対数 (log)微分細孔容積及び第 2のピーク（P2)の対数 (log)微分細 孔容積が小さい場合であり、圧力損失が増加し、やや不利である。実施例 4は、第 1 のピーク（P1)における細孔径の大きさ（S1)が大きい場合であり、触媒担持性及び 浄化特性が優れる。なお、図 8は、実施例 4のハニカム触媒体の隔壁の細孔の細孔 径分布を示している。実施例 5は、隔壁厚さが 8milと薄い場合であり、圧力損失の点 で優れる。実施例 6は、第 2のピーク（P2)における細孔径の大きさ（S2)が大きい場 合を示す。実施例 7は、第 1のピーク（P1)における細孔径の大きさ（S1)が大きい場 合であり、触媒担持性に優れ、セル数が少なくても（セル密度が小さい）浄化特性が 良好で、低圧力損失である。
[0061] 比較例:!〜 2は、細孔径の大きさが 0. 05 z m以上の領域においてピークが 1つの 場合である。比較例 1は隔壁厚さが 4. 5milと極めて薄い場合であり、浄化特性が劣 り、比較例 2は、細孔径が 15 μ ΐη、第 1のピーク（PI)の対数 (log)微分細孔容積が 0 . 75cc/gで、圧力損失が増加する。比較例 3〜5は、細孔径の大きさが 0· 05 /i m 以上の領域において 2つのピークを有する場合である。比較例 3は、第 1のピーク（P 1)の対数 (log)微分細孔容積及び第 2のピーク (P2)の対数 (log)微分細孔容積が ともに所定以上に小さい場合で、触媒担持性、浄化特性及び圧力損失のすべてが 劣る。比較例 4は、第 1のピーク（P1)における細孔径の大きさ（S1)が所定以上に小 さぐ一方第 2のピーク（P2)における細孔径の大きさ（S2)が所定以上に大きい場合 であり、圧力損失の点では良いものの、触媒担持性及び浄化特性に劣る。比較例 5 は、第 2のピーク (P2)の対数 (log)微分細孔容積が所定以上に小さい場合で、圧力 損失が増加する。
産業上の利用可能性
[0062] 本発明のハニカム構造体及びハニカム触媒体は、排ガスに含まれる被浄化成分の 浄化を必要とする各種産業分野、例えば、内燃機関、燃焼機器等からの排ガスの浄 化を必要とする自動車産業、機械産業、窯業等の産業分野において好適に利用さ れる。

Claims

請求の範囲
二つの端面間を連通する複数のセルが形成されるように配置された、多数の細孔 を有する多孔質な隔壁と、セル端部またはセル内部の少なくとも一部にガス通過防 止部（目封じ部）を備え、実質的に前記隔壁内をガスが流れるようにした触媒担体用 のハニカム構造体であって、
前記隔壁の細孔の細孔径分布（細孔径の大きさを横軸にその細孔容積を縦軸にし てプロットされたグラフで表示される）が、細孔径の大きさが 0. 05 /i m以上の領域に おいて、細孔容積に関し、 2つ以上のピークを有し、
2つ以上のピークのうちの少なくとも 1つが、細孔径の大きさが 50 μ m以上の領域に 存在することを特徴とするハニカム構造体。
前記 2つ以上のピークのうちの任意の 2つのピークである第 1のピーク（P1)及び第 2のピーク（P2)において、前記第 1のピーク（P1)における細孔容積 (N1)を対数 (lo g)微分細孔容積で表した場合、その値が、 0. 01〜3. Occ/gであり、前記第 2のピ ーク (P2)における細孔容積 (N2)を対数 (log)微分細孔容積で表した場合、その値 、 0. 01 -5. Occ/gである請求項 1に記載のハニカム構造体。
前記 2つ以上のピークのうちの任意の 2つのピークである第 1のピーク（P1)及び第 2のピーク（P2)において、前記第 1のピーク（P1)における細孔容積 (N1)と前記第 2 のピーク (P2)における細孔容積 (N2)との比 (N1： N2)が、 1： 100〜10： 1である請 求項 1に記載のハニカム構造体。
前記第 1のピーク（P1)における細孔径の大きさ（S 1)力 ：!〜 35 x mであり、前記 第 2のピーク（P2)における細孔径の大きさ（S2)力 50-500 μ mである請求項：!〜 3のレ、ずれかに記載のハニカム構造体。
前記第 1のピーク（P1)における細孔径の大きさ（S 1)と前記第 2のピーク（P2)にお ける細孔径の大きさ (S2)との比 (S1： S2)が、 1： 10000〜4： 5である請求項 2〜4の いずれかに記載のハニカム構造体。
請求項 1〜5のいずれかに記載のハニカム構造体に、触媒が担持されてなるハニカ ム触媒体。
前記ハニカム構造体が、前記触媒の担持された状態においても、請求項:!〜 5のい ずれかに記載の、前記隔壁の細孔における細孔径分布の条件を満足する請求項 6 に記載のハニカム触媒体。
請求項:!〜 5のいずれかに記載のハニカム構造体、又は請求項 6若しくは 7に記載 のハニカム触媒体を用いた排ガス処理システム。
PCT/JP2007/052652 2006-02-14 2007-02-14 ハニカム構造体及びハニカム触媒体 WO2007094379A1 (ja)