WO2007076769A2 - Matériau de revêtement de substrats contenant un lubrifiant pour des processus de formage - Google Patents
Matériau de revêtement de substrats contenant un lubrifiant pour des processus de formage Download PDFInfo
- Publication number
- WO2007076769A2 WO2007076769A2 PCT/DE2006/002188 DE2006002188W WO2007076769A2 WO 2007076769 A2 WO2007076769 A2 WO 2007076769A2 DE 2006002188 W DE2006002188 W DE 2006002188W WO 2007076769 A2 WO2007076769 A2 WO 2007076769A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating material
- zinc
- substrate
- aluminum
- weight
- Prior art date
Abstract
L'invention concerne un matériau de revêtement de substrats. L'invention vise à mettre en oeuvre un matériau de revêtement présentant une effet de protection contre la corrosion et un effet tribologique. A cet effet, le matériau de revêtement contient de 0,5 à 90 % en poids, de préférence de 5 à 60 % en poids de lubrifiants destinés à réduire la résistance de friction de la surface au cours de processus de formage, jusqu'à 95 % en poids, de préférence de 10 à 75 % en poids d'un liant adapté et de 0 à 90 % en poids de pigments ou de charges, le matériau de revêtement peut être lié fixement à la surface du substrat, et le matériau de revêtement peut être formé avec le substrat dans des processus de formage à froid ou à chaud.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP06828637A EP1960484A2 (fr) | 2005-12-12 | 2006-12-07 | Materiau de revetement de substrats |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE200510059613 DE102005059613A1 (de) | 2005-12-12 | 2005-12-12 | Beschichtungsmaterial für Substrate |
DE102005059613.4 | 2005-12-12 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2007076769A2 true WO2007076769A2 (fr) | 2007-07-12 |
WO2007076769A3 WO2007076769A3 (fr) | 2007-11-01 |
Family
ID=37944092
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/DE2006/002188 WO2007076769A2 (fr) | 2005-12-12 | 2006-12-07 | Matériau de revêtement de substrats contenant un lubrifiant pour des processus de formage |
Country Status (3)
Country | Link |
---|---|
EP (1) | EP1960484A2 (fr) |
DE (1) | DE102005059613A1 (fr) |
WO (1) | WO2007076769A2 (fr) |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008134096A1 (fr) * | 2007-02-28 | 2008-11-06 | The Boeing Company | Revêtements barrières pour substrats polymères |
RU2495068C1 (ru) * | 2012-04-10 | 2013-10-10 | Общество с ограниченной ответственностью "ЗелТехПрогресс" | Антикоррозионная огнестойкая краска |
EP2683843A1 (fr) * | 2011-03-08 | 2014-01-15 | ThyssenKrupp Steel Europe AG | Produit plat en acier et procédé de fabrication d'un produit plat en acier |
CN106065088A (zh) * | 2016-06-06 | 2016-11-02 | 同济大学 | 一种接枝硅磷元素的改性膨胀石墨的制备方法 |
CN106633639A (zh) * | 2016-11-23 | 2017-05-10 | 杭州欣隆实业有限公司 | 一种热浸塑钢质线缆保护管道及其制备方法 |
RU2653171C1 (ru) * | 2017-02-14 | 2018-05-07 | федеральное государственное бюджетное образовательное учреждение высшего образования "Тольяттинский государственный университет" | Краска антикоррозионная, огнестойкая |
CN109486348A (zh) * | 2018-11-07 | 2019-03-19 | 沈阳化工大学 | 一种防火防腐涂料制备方法 |
CN116769334A (zh) * | 2023-06-14 | 2023-09-19 | 陕西星航智钛新材料有限公司 | 一种用于航空紧固件丝材的耐高温高润滑涂层及其应用 |
Families Citing this family (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102007037592B3 (de) * | 2007-08-06 | 2009-03-19 | Gfe Fremat Gmbh | Halbzeug aus Refraktärmetallen, insbesondere aus Molybdän oder Titan, welches mit einer Schutzschicht versehen ist und Verfahren zur Herstellung der Schutzschicht |
DE102007038215A1 (de) * | 2007-08-13 | 2009-02-19 | Nano-X Gmbh | Verfahren zur Herstellung einer aktiven Korrosionsschutzbeschichtung auf Bauteilen aus Stahl |
DE102009002716A1 (de) * | 2009-04-29 | 2010-11-11 | Federal-Mogul Nürnberg GmbH | Verschleißfester Gleitlack für die Beschichtung von Motorkolben |
DE102009002715B4 (de) * | 2009-04-29 | 2017-02-09 | Federal-Mogul Nürnberg GmbH | Verwendung eines wasserverdünnbaren Gleitlacks für die Beschichtung von Motorkolben |
DE102009052398B4 (de) * | 2009-11-10 | 2013-05-16 | Acs Coating Systems Gmbh | Beschichtung für ein Substrat und Verfahren zu dessen Herstellung |
EP2865723B1 (fr) * | 2013-10-23 | 2016-09-14 | Fuchs Europe Schmierstoffe GmbH | Moyen de protection contre la corrosion pour application à froid |
DE102015210459B4 (de) | 2015-06-08 | 2021-03-04 | Volkswagen Aktiengesellschaft | Verfahren zur Warmumformung eines Stahlbauteils |
DE102017204880A1 (de) | 2017-03-23 | 2018-09-27 | BSH Hausgeräte GmbH | Verfahren zum Herstellen eines Blechteils |
CN112538309B (zh) * | 2020-11-12 | 2022-03-11 | 浙江机电职业技术学院 | 一种耐磨抗震涂层及其制备方法 |
CN112920634A (zh) * | 2021-01-29 | 2021-06-08 | 杭州凯诺恩新材料有限公司 | 一种氟改性纳米防锈颜料 |
CN114891413B (zh) * | 2021-02-28 | 2024-01-02 | 营口赛斯德型材有限公司 | 一种自润滑耐磨涂层 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3537479A1 (de) * | 1985-10-22 | 1987-04-23 | Majewski Klaus Peter | Korrosionsschutzmittel mit gleichzeitigem schmiereffekt |
WO2000032351A2 (fr) * | 1998-12-01 | 2000-06-08 | Ppg Industries Ohio, Inc. | Substrats metalliques revetus, soudables, et procedes pour preparer ces substrats et les proteger contre la corrosion |
DE10256286A1 (de) * | 2002-12-03 | 2004-06-24 | Georg Gros | Gemisch zum Aufbringen eines polymeren korrosionsbeständigen elektrisch schweißbaren Überzugs und Verfahren zum Herstellen dieses Überzugs |
WO2005005559A1 (fr) * | 2003-07-15 | 2005-01-20 | Dacral | Utilisation d'yttrium, de zirconium, de lanthane, de cerium, de praseodyme et/ou de neodyme comme agent de renfort dans une composition de revetement anticorrosion |
WO2006040030A1 (fr) * | 2004-10-08 | 2006-04-20 | Volkswagen Aktiengesellschaft | Procede de revetement de surfaces metalliques |
-
2005
- 2005-12-12 DE DE200510059613 patent/DE102005059613A1/de not_active Withdrawn
-
2006
- 2006-12-07 WO PCT/DE2006/002188 patent/WO2007076769A2/fr active Application Filing
- 2006-12-07 EP EP06828637A patent/EP1960484A2/fr not_active Withdrawn
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE3537479A1 (de) * | 1985-10-22 | 1987-04-23 | Majewski Klaus Peter | Korrosionsschutzmittel mit gleichzeitigem schmiereffekt |
WO2000032351A2 (fr) * | 1998-12-01 | 2000-06-08 | Ppg Industries Ohio, Inc. | Substrats metalliques revetus, soudables, et procedes pour preparer ces substrats et les proteger contre la corrosion |
DE10256286A1 (de) * | 2002-12-03 | 2004-06-24 | Georg Gros | Gemisch zum Aufbringen eines polymeren korrosionsbeständigen elektrisch schweißbaren Überzugs und Verfahren zum Herstellen dieses Überzugs |
WO2005005559A1 (fr) * | 2003-07-15 | 2005-01-20 | Dacral | Utilisation d'yttrium, de zirconium, de lanthane, de cerium, de praseodyme et/ou de neodyme comme agent de renfort dans une composition de revetement anticorrosion |
WO2006040030A1 (fr) * | 2004-10-08 | 2006-04-20 | Volkswagen Aktiengesellschaft | Procede de revetement de surfaces metalliques |
Cited By (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US7878054B2 (en) | 2007-02-28 | 2011-02-01 | The Boeing Company | Barrier coatings for polymeric substrates |
US8603592B2 (en) | 2007-02-28 | 2013-12-10 | The Boeing Company | Barrier coatings for polymeric substrates |
US9403992B2 (en) | 2007-02-28 | 2016-08-02 | The Boeing Company | Barrier coatings for polymeric substrates |
WO2008134096A1 (fr) * | 2007-02-28 | 2008-11-06 | The Boeing Company | Revêtements barrières pour substrats polymères |
EP2683843B1 (fr) * | 2011-03-08 | 2021-06-16 | ThyssenKrupp Steel Europe AG | Produit plat en acier et procédé de fabrication d'un produit plat en acier |
EP2683843A1 (fr) * | 2011-03-08 | 2014-01-15 | ThyssenKrupp Steel Europe AG | Produit plat en acier et procédé de fabrication d'un produit plat en acier |
RU2495068C1 (ru) * | 2012-04-10 | 2013-10-10 | Общество с ограниченной ответственностью "ЗелТехПрогресс" | Антикоррозионная огнестойкая краска |
CN106065088A (zh) * | 2016-06-06 | 2016-11-02 | 同济大学 | 一种接枝硅磷元素的改性膨胀石墨的制备方法 |
CN106633639B (zh) * | 2016-11-23 | 2018-10-16 | 杭州欣隆实业有限公司 | 一种热浸塑钢质线缆保护管道及其制备方法 |
CN106633639A (zh) * | 2016-11-23 | 2017-05-10 | 杭州欣隆实业有限公司 | 一种热浸塑钢质线缆保护管道及其制备方法 |
RU2653171C1 (ru) * | 2017-02-14 | 2018-05-07 | федеральное государственное бюджетное образовательное учреждение высшего образования "Тольяттинский государственный университет" | Краска антикоррозионная, огнестойкая |
CN109486348A (zh) * | 2018-11-07 | 2019-03-19 | 沈阳化工大学 | 一种防火防腐涂料制备方法 |
CN109486348B (zh) * | 2018-11-07 | 2020-08-21 | 沈阳顺风新材料有限公司 | 一种防火防腐涂料制备方法 |
CN116769334A (zh) * | 2023-06-14 | 2023-09-19 | 陕西星航智钛新材料有限公司 | 一种用于航空紧固件丝材的耐高温高润滑涂层及其应用 |
Also Published As
Publication number | Publication date |
---|---|
EP1960484A2 (fr) | 2008-08-27 |
DE102005059613A1 (de) | 2007-06-28 |
WO2007076769A3 (fr) | 2007-11-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2007076769A2 (fr) | Matériau de revêtement de substrats contenant un lubrifiant pour des processus de formage | |
DE102005059614A1 (de) | Beschichtungsmaterial zum Schutz von Metallen, insbesondere Stahl, vor Korrosion und/oder Verzunderung, Verfahren zum Beschichten von Metallen und Metallelement | |
EP1809714B1 (fr) | Procede de revetement de surfaces metalliques | |
EP2337877A1 (fr) | Procédé permettant de constituer des couches anticorrosion déformables sur des surfaces métalliques | |
EP2191030A2 (fr) | Procédé de fabrication d'un revêtement actif, cathodique, anticorrosion sur des composants en acier | |
DE60219841T2 (de) | Überzug enthaltend teilchenförmige Metalllegierung zum Korrisionsschutz | |
JP2012505963A5 (fr) | ||
WO2001085860A1 (fr) | Revetements organiques conducteurs | |
EP1907492A1 (fr) | Feuille d'acier pre-scellee presentant une anticorrosion et une soudabilite ameliorees et procede de preparation de celle-ci | |
DE69833346T2 (de) | Vorbeschichtetes Chromstahlblech mit guter Haftfestigkeit von Farben für Ausspuffverwendung | |
EP2743320B1 (fr) | Procédé en plusieurs étapes de recouvrement d'acier avant un formage à chaud | |
WO2009129783A2 (fr) | Procédé pour protéger un métal contre la corrosion | |
EP2178987B1 (fr) | Procédé pour protéger contre la corrosion les composants de carrosserie, de châssis et de moteur ou les systèmes d'échappement | |
EP2743376B1 (fr) | Agent aqueux et procédé de revêtement pour le traitement anti-corrosion de substrats métalliques | |
JP3124266B2 (ja) | 塗膜密着性と加工部の耐食性に優れ環境負荷の小さい塗装鋼板 | |
DE10006270B4 (de) | Lackierverfahren und damit hergestelltes Metallbauteil | |
JP2010242155A (ja) | 防食鋼材及びその製造方法 | |
JP3185828B2 (ja) | 摺動部用に適した電着塗料 | |
DE102013102566A1 (de) | Verfahren zur Herstellung eines metallischen Bauteils eines Beschlages, Beschlag, Ofen und Möbel oder Haushaltsgerät | |
JPH05138805A (ja) | 加工後耐食性に優れた有機複合被覆鋼板 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application | ||
DPE1 | Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 2006828637 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 2006828637 Country of ref document: EP |