WO2006129604A1 - 昇華転写プリント塗装皮革製品及びその製造方法 - Google Patents

昇華転写プリント塗装皮革製品及びその製造方法 Download PDF

Info

Publication number
WO2006129604A1
WO2006129604A1 PCT/JP2006/310668 JP2006310668W WO2006129604A1 WO 2006129604 A1 WO2006129604 A1 WO 2006129604A1 JP 2006310668 W JP2006310668 W JP 2006310668W WO 2006129604 A1 WO2006129604 A1 WO 2006129604A1
Authority
WO
WIPO (PCT)
Prior art keywords
leather
resin
layer
sublimation transfer
sublimation
Prior art date
Application number
PCT/JP2006/310668
Other languages
English (en)
French (fr)
Inventor
Sadao Takahashi
Toru Amano
Original Assignee
I. S. Paint Co., Ltd.
Amano Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by I. S. Paint Co., Ltd., Amano Co., Ltd. filed Critical I. S. Paint Co., Ltd.
Publication of WO2006129604A1 publication Critical patent/WO2006129604A1/ja

Abstract

　本発明は、天然皮革に対する熱昇華転写法の適用を可能とし、それによって皮革本来の風合いを損なうことなく、美麗、かつ堅牢なプリントを施した皮革製品を提供することを目的とする。 　本発明は、単層あるいは複層の一般皮革塗装用樹脂を含む下塗り層、染着性樹脂と架橋剤を含む上塗り層及び所望により剥離性樹脂よりなる剥離層を順次形成した皮革の表面に、昇華性染料を含む画像を転写してなる昇華転写プリント塗装皮革、並びに熱昇華転写法により、皮革の表面に画像を転写して昇華転写プリント塗装皮革を製造する方法を提供する。

Description

明 細 書
昇華転写プリント塗装皮革製品及びその製造方法
技術分野
[0001] 本発明は、皮革、特に天然皮革に熱昇華転写法により画像をプリントしてなる塗装 皮革製品、及びその製造方法に関するものである。
背景技術
[0002] 皮革、繊維布、陶器などの基材に対してパーソナルユース的に多品種少量の画像 をプリントする方法として、予め画像を印刷した転写紙を基材の表面に熱圧して画像 を転写する方法が知られている (特許文献 1〜3参照)。この熱転写法には熱融溶転 写法と熱昇華転写法とがあり、後者は転写紙上の画像の中の昇華性染料が加熱に よって昇華し、気体分子として基材の中に染み込んで染着するので、転写画像が美 麗で且つ階調性が高ぐ耐摩耗性に優れるという大きな長所がある。
[0003] ところが、昇華性を示す染料は、殆ど分散染料に限られているため、基材は分散染 料〖こ染着されるものであること、高い昇華温度に耐えられることが必要とされていた。 そのため、この方法が適用される基材は、ポリエステル製布などに限られ、木綿等の 天然繊維製布は勿論のこと、皮革に対しても実施されて ヽなかった。
特許文献 1：実公平 6— 38009号公報
特許文献 2：特許第 3069064号公報
特許文献 3：特開平 4 57538号公報
発明の開示
発明が解決しょうとする課題
[0004] 本発明の目的は、天然皮革等の皮革に対する熱昇華転写法の適用を可能とし、美 麗、かつ堅牢なプリントを施した皮革製品、とりわけ多品種少量の印刷を施した皮革 製品とその製造方法を提供することである。
課題を解決するための手段
[0005] 本発明者らは、上記課題を解決すべく鋭意検討を重ねた結果、熱昇華転写法によ り皮革表面に昇華性染料を染着することを可能とする皮革塗装膜の開発に成功し、 加熱下での皮革の変性を防ぎ皮革本来の柔軟性を保持させた状態で、昇華性染料 の画像を皮革に熱転写することができる技術を確立して、本発明を完成するに至つ たのである。
[0006] すなわち、請求項 1に記載の本発明は、単層あるいは複層の一般皮革塗装用榭脂 を含む下塗り層及び染着性榭脂と架橋剤を含む上塗り層を形成した皮革の表面に、 昇華性染料を含む画像を転写してなる昇華転写プリント塗装皮革である。
請求項 2に記載の本発明は、単層あるいは複層の一般皮革塗装用榭脂を含む下 塗り層、染着性榭脂と架橋剤を含む上塗り層及び剥離性榭脂よりなる剥離層を順次 形成した皮革の表面に、昇華性染料を含む画像を転写してなる昇華転写プリント塗 装皮革である。
次に、請求項 3に記載の本発明は、下塗り層の一般皮革塗装用榭脂層が、アクリル 系榭脂及び Z又はポリウレタン系榭脂を含むものである請求項 1又は 2に記載の昇 華転写プリント塗装皮革である。
請求項 4に記載の本発明は、上塗り層の染着性榭脂が、ポリエステル系榭脂を含 むものである請求項 1〜3のいずれかに記載の昇華転写プリント塗装皮革である。 請求項 5に記載の本発明は、剥離層の剥離性榭脂が、フッ素系榭脂又はポリアミド イミド系榭脂を含むものである請求項 2〜4のいずれかに記載の昇華転写プリント塗 装皮革である。
[0007] 請求項 6に記載の本発明は、皮革の表面に、少なくとも一層の一般皮革塗装用榭 脂層を付与して下塗り層を形成する工程、染着性榭脂と架橋剤を含む上塗り層を形 成する工程、該上塗り層の上面に昇華性染料を含む画像が印刷された転写シートを 戴置し、加熱圧着して画像を転写する工程を含むことを特徴とする昇華転写プリント 塗装皮革の製造方法である。
また、請求項 7に記載の本発明は、皮革の表面に、少なくとも一層の一般皮革塗装 用樹脂層を付与して下塗り層を形成した後、染着性樹脂と架橋剤を含む上塗り層を 形成する工程、該上塗り層の上面に剥離性榭脂層を付与して剥離層を形成するェ 程、該剥離層の上面に昇華性染料を含む画像が印刷された転写シートを戴置し、加 熱圧着して画像を転写する工程を含むことを特徴とする昇華転写プリント塗装皮革の 製造方法である。
[0008] 請求項 8に記載の本発明は、下塗り層の一般皮革塗装用榭脂層が、アクリル系榭 脂及び Z又はポリウレタン系榭脂を含むものである請求項 6又は 7に記載の昇華転 写プリント塗装皮革の製造方法である。
請求項 9に記載の本発明は、上塗り層の染着性榭脂が、ポリエステル系榭脂である 請求項 6〜8のいずれかに記載の昇華転写プリント塗装皮革の製造方法である。 さらに、請求項 10に記載の本発明は、剥離層の剥離性榭脂が、フッ素系榭脂又は ポリアミドイミド系榭脂を含むものである請求項 7〜9のいずれかに記載の昇華転写プ リント塗装皮革の製造方法である。
発明の効果
[0009] 本発明によれば、天然皮革等の皮革に熱昇華性転写法により美麗、かつ堅牢なプ リントを施すことができる。し力も、本発明の方法により印刷を施された皮革製品は、 天然皮革が本来有する風合いと質感を十分に維持しており、多品種少量の印刷を 施した様々な皮革製品を需要者に提供するというニーズに十分に応えることができる
図面の簡単な説明
[0010] [図 1]本発明の昇華転写プリント塗装皮革の作製に用いる被転写塗装皮革 (実施例 2 のタイプ)の 1例を示す断面図である。
符号の説明
[0011] 1 皮革生地
2 下塗り層の（a)層
3 下塗り層の（b)層
4 上塗り層
5 剥離層
発明を実施するための最良の形態
[0012] 以下、本発明を詳細に説明する。
本発明が適用される皮革としては、天然皮革、合成皮革のいずれでもよいが、特に 天然皮革が好ましい。天然皮革としては、牛皮、馬皮、羊皮、山羊皮、豚皮などが挙 げられ、特に制限はされないが、牛皮、馬皮など平滑な表面を有するものが好ましい 。また、これらの皮革を用いる際に、耐熱、なめし工程などの必要な前処理を行うこと ちでさる。
[0013] 本発明において、皮革表面に形成する下塗り層は、一般皮革塗装用榭脂層を基 本とする単層あるいは複層である。 1例を示すと、皮革表面に接している下層の厚さ 1 0 の一般皮革塗装用榭脂層及び上層である厚さ 10 の一般皮革塗装用榭脂層 力もなる下塗り層を挙げることができる。
[0014] 下塗り層は通常 1〜3層からなり、厚さは全体で 10〜80 μ、好ましくは 15〜40 μが 適当である。なお、床革のような表面の粗い皮革に対しては、平滑性を得るために数 回の塗工で数層を形成させることもある。
ここで、一般皮革塗装用榭脂としては、アクリル系榭脂、ポリウレタン系榭脂、ポリ酢 酸ビュル系榭脂、熱可塑性エラストマ一等の種々の榭脂が使用可能であるが、低温 での柔軟性保持、転写加工温度での耐熱安定性の面から、アクリル系榭脂とポリウレ タン系榭脂の組み合わせが好ましい。さらには、二次転移点 (Tg)がー 20°C以下で ある榭脂を用いることが好まし 、。
これらの榭脂は、水性ェマルジヨン、有機溶媒溶液などの形態で塗工される力 下 塗り層につ 、ては、コストと環境問題の理由力も水性ェマルジヨンとして用いることが 望ましい。なお、コート法については、任意であり既知の方法、例えばロールコーター 法、スプレー法などいずれの方法でも良い。下塗り層には、必要に応じて顔料、増粘 剤、フィラー剤、ワックスなどを適宜配合することができる。
[0015] 次に、上塗り層は、染着性榭脂と架橋剤を含む層であり、上記下塗り層の上に形成 される。染着性榭脂を主成分とする上塗り層は、後記する転写の際に、昇華性染料 を染着して美麗なプリントを形成するために用いられるものである。そのため、可及的 に染着性榭脂を多くして、後記転写工程で昇華してくる染料を有効に捕捉させること が望ましい。
染着性榭脂としては、ポリエステル系榭脂、エポキシ榭脂、アルキド榭脂、セルロー スエステル系榭脂等を用いることができ、これらの榭脂は、単独で、あるいは 2種以上 を組み合わせて使用することができる力 特にポリエステル系榭脂が好ましい。コー ティングに使用し得るポリエステル系榭脂には、種々の共重合体があるが、分子内に 芳香環を有するものが染着性の面力 好まし 、。
ポリエステル系榭脂などの染着性榭脂は、二次転移点 (Tg)が低いものが好ましぐ — 10°C以下、より好ましくは— 15°C以下のものが好適である。その理由は、— 10°C 以上の榭脂は使用環境条件内において、硬ぐかつ脆くなつて風合いを損ねたり、屈 曲時に破損するおそれがある。
また、榭脂液の形態については、下塗り層の場合と同様に水性ェマルジヨン、有機 溶媒溶液などの形態で用いることができ、特に制限されないが、透明な層を形成する ことが望まれるときは、有機溶媒溶液の形態とすべきである。
なお、上塗り層には、上記の他に、紫外線吸収剤、乾燥促進剤なども必要に応じて 配合することが可能である。
[0016] 次に、架橋剤は、染着性榭脂中の官能基と反応して該榭脂の分子運動を拘束、す なわち硬化させ、染着性を改善するために用いられるが、硬化が過ぎると、塗膜が硬 くなる。
架橋剤としては、例えばイソシァネートイ匕合物、アジリジン、エポキシ化合物等が使 用可能である。なお、染着性榭脂としてポリエステル系榭脂を用いた場合、イソシァ ネートイ匕合物を架橋剤として使用すると、塗膜の風合いを損なうことが少ないため、 好ましい。この場合、イソシァネートイ匕合物の割合を多くすると、転写画像の滲み、ボ ケなどが抑制され、画像が安定し、また耐熱性も向上する。そのため、上塗り層の上 に剥離層を設けない場合でも、転写加工時の転写シートの剥離が行い易くなる。しか し、イソシァネートイ匕合物の割合が多すぎると、塗膜が硬くなり、風合いを損ねる。こ の現象は、他の架橋剤を用いた場合も同様である。そのため、ポリエステル系榭脂と イソシァネートイ匕合物の配合比は、イソシァネートイ匕合物が 60〜75重量％となるよう に設定することが好ましい。また、架橋剤の効果として、転写加工時の加熱温度に耐 え、転写シートとの貼りつきを抑える作用がある。
[0017] 上塗り層は、染着性榭脂によって昇華性染料を十分に吸収できる範囲であれば、 厚さは薄い方が好ましいが、 1層で十分な効果が奏されない場合は、 2層以上に重 ね塗りしても良い。通常、上塗り層の厚さは 10〜30 、好ましくは 20 程度が適当 である。また、染着性榭脂を主とする上塗り層は、前記したように、昇華性染料を染着 してプリントを形成する層であるため、透明な材料を選択することにより不透明な下塗 り層とのコントラストが転写画像を引き立たせて、鮮明、かつ美麗感をもたらすことが 好ましい。
[0018] 前記したように、上塗り層の架橋剤により、転写画像の安定化や耐熱性の向上とい う効果が得られるが、上塗り層に用いるポリエステル系榭脂などの染着性榭脂は熱可 塑性が強 、ので、画像が印刷されて 、る転写シート表面が貼りつき易 、。
そのため、上塗り層の上面に剥離層を設けることによって、上塗り層と転写シ一との 直接接触をなくして、このような問題を防ぐことができる。これは、他面から見れば、上 塗り層の樹脂の配合選択に対する自由度を高めるメリットが得られることになる。 この剥離層は、転写時の温度に耐える耐熱性と剥離性が要求される。一方、昇華 性榭脂の転写プリントを保護するという作用も有する。剥離層としては、耐熱性の榭 脂、例えばフッ素榭脂、シリコン系榭脂、ポリアミドイミド系榭脂、ポリエーテルスルホ ン榭脂などが用いられるが、特に耐熱性と剥離性をバランス良く保持しているフッ素 榭脂あるいはポリアミドイミド系榭脂が好適である。なお、剥離層は薄く形成すればよ く、その厚さは通常 0. 1〜0. 01 程度が適当である。
[0019] 以上の各層の塗装方法としては、通常行われている方法であれば特に制限なく適 用することができる。具体的には、ロールコート法、フローコート法、スプレーコート法 、ナイフコート法、手塗り法などが挙げられる力 通常はロールコート法、フローコート 法、スプレーコート法が好ましい。なお、剥離層は、特にスプレーコート法が好ましい
[0020] 本発明の昇華転写プリント塗装皮革は、皮革表面に上記した各層を塗装して得た 塗装皮革 (以下、被転写塗装皮革という。）の塗装表面に、以下に説明する転写シー トの画像を熱昇華転写法により該塗装皮革に転写することにより製造することができ る。
[0021] 本発明における転写シートは、転写基材表面に昇華性染料を含む画像が印刷され たものであり、該画像を前記塗装表面に転写するためのものである。 転写基材としては、昇華性染料を受容して、熱昇華転写法に適用できるものであれ ばよぐ例えば紙、合成紙の他、ポリプロピレン、ポリエチレンなどのポリオレフイン榭 脂、ナイロンなどのポリアミド榭脂などの合成樹脂からなるフィルムなどが挙げられる 力 好ましくは紙製のシートである。昇華性染料を含むインクを強く吸着し過ぎる転写 シートは、画像の転写が不足し易ぐ一方吸着の弱すぎる転写シートは、放置すると 、昇華性染料が飛散するおそれがある。それ故、商品対象や生産条件等を考慮して 適切なものを選択すべきである。
[0022] 本発明における昇華性染料としては、昇華性を有する染料であれば任意に使用す ることができるが、これまでは耐光性のよ!、分散染料が一般に用いられて 、る。
転写基材表面に昇華性染料を含む画像を印刷するには、既知の方法により行えば 良ぐ例えばインクジェット法、スクリーン法、オフセット法、グラビア法、フレキソ法など 、いずれの方法を採用することができる。これらの中では、インクジェット法は、少量多 品種の画像印刷に適して 、るため好ま 、方法である。
上記の画像としては、いかなるものでもよぐ例えば無彩色の線画だけのもの、カラ 一写真、テレビ画面等の画像であってもよい。
なお、当該印刷層の厚さ（あるいは塗布量）は、通常 1〜： LO /zである。
[0023] 次に、熱昇華転写法について説明する。
まず、被転写塗装皮革の塗装表面 (上塗り層又は剥離層）に、上記転写シートの印 刷面を重ねるようにあてた後、転写シートの背面から加熱'圧着させる。すると、昇華 性染料が加熱により昇華し、気体分子として塗装表面の上塗り層の染着性榭脂層に 染着し、画像が転写される。
[0024] 本発明において、転写時の加熱 ·圧着手段としては、熱ロールプレス、熱板プレス などの熱昇華転写法に通常用いられるプレス機を使用して行うことができ、このときの 転写条件については、画像に用いた昇華性染料や転写シートの種類などを考慮し て決定すればよいが、通常は温度： 130〜200°C、好ましくは 150〜190°C、時間： 1 0〜120秒、好ましくは 30〜90秒、圧力：0. l〜60kgZcm2、好ましくは l〜5kgZc m2が適当である。高圧力は、時間を短縮又は温度低下を可能にするので、皮革の 用途に応じ適宜調整できる。 加熱温度が上限を超えると、皮革を劣化させるおそれがある。また、下限未満であ れば、染料の昇華性が悪くなり、塗装表面への染着量が低下するため好ましくない。 圧力が上限を超えると、皮革が押しつぶされたり、硬くなるおそれがある。また、下 限未満であると、染料の昇華性が悪くなり、塗装表面への浸透性、染着量が低下す るので好ましくない。転写時間については、上限を超えると、圧力が上限を超えた場 合と同様となり、一方下限未満であると、圧力が下限未満の場合と同様となり、好まし くない。
実施例
[0025] 以下に実施例等を挙げて本発明を具体的に説明するが、本発明はこれらに限定さ れるものではない。
[0026] (実施例 1)
(1)被転写塗装皮革の作製
牛皮（クロムなめし革、 lOcm X IOcm)に、下塗り層として下記組成の（a)層及び (b) 層を順次塗装した。なお、（a)層はロールコート 1回、（b)層はスプレーコート 4回で塗 装し、乾燥後の各層の厚さは、（a)層 10 、（b)層 であった。
[0027] (a)層
アクリルェマルジヨン（ (株)アイエスペイント社製、榭脂分 38%) 40重量部 ポリウレタンェマルジヨン（商品名：ウレコートブライト 70) 5重量部 顔料ペースト 28重量部
助剤 10重量部
水 11重量部
(b)層
アクリルェマルジヨン（ (株)アイエスペイント社製、榭脂分 38%) 40重量部 ポリウレタンェマルジヨン（商品名：ウレコートブライト 70) 5重量部 顔料ペースト 28重量部
助剤 10重量部
水 41重量部
[0028] 次に、上塗り層として、下記組成のものを下塗り層の（b)層の上にロールコートで 1 回塗工した。乾燥後の層の厚さは、 20 であった。
ポリエステル溶液 （東洋紡績 (株)社製、榭脂分 30%) 40重量部 イソシァネートイ匕合物（ (株)アイエスペイント社製、榭脂分 45%) 20重量部 ウレタンシンナー （(株)アイエスペイント社製） 20重量部
助剤 (紫外線吸収剤を含む） 7重量部
[0029] (2)画像転写用シートの作製
紙製転写シート上に、昇華性染料を含む画像をインクジェット法で印刷したものを 用总し 7 o
[0030] (3)画像の熱昇華転写
前記 (1)で作製した塗装皮革の表面に画像転写用シートを重ね、プレス機を用いて 温度 190°C、圧力 2kgZcm2の条件で 90秒間加熱圧着して画像を転写した。その後 、転写シートを慎重に剥がしたところ、美麗な転写画像を有する塗装皮革が得られた 室温で 24時間放置したのち、目視で判定したところ、画像は安定しており、滲みや 褪色は殆ど認められな力つた。
[0031] (実施例 2)
実施例 1と同様にして作製した塗装皮革の上塗り層の上に、下記組成の剥離層を スプレー法により形成 (厚さ： 0. 1 ）した。
ポリアミドイミド系榭脂 (東洋紡績 (株)社製、榭脂分 25%) 5重量部 シンナー 95重量部
[0032] その後、実施例 1で作製した画像転写用シートと同じものを剥離層の上に重ね合わ せ、実施例 1と同様にして画像の熱昇華転写を行った。
その結果、転写シートは容易に剥がすことができ、しかも滲みや褪色のない安定し た転写画像が得られた。
[0033] (比較例 1)
実施例 1において、上塗り層を省略したこと以外は、実施例 1と同様にして転写画 像を有する塗装皮革を作製した。
この皮革製品は、転写画像が不鮮明であった。 産業上の利用可能性
本発明によれば、美麗、かつ堅牢なプリントを施した皮革製品、並びにその製造方 法を提供することができる。また、本発明の方法によりプリントされた皮革製品は、天 然皮革等が本来有する質感を十分に維持している。本発明は、特にパーソナルユー ス的な多品種少量印刷を施した皮革製品の提供に適している。

Claims

請求の範囲
[1] 単層あるいは複層の一般皮革塗装用榭脂を含む下塗り層及び染着性榭脂と架橋 剤を含む上塗り層を形成した皮革の表面に、昇華性染料を含む画像を転写してなる 昇華転写プリント塗装皮革。
[2] 単層あるいは複層の一般皮革塗装用樹脂を含む下塗り層、染着性樹脂と架橋剤を 含む上塗り層及び剥離性榭脂よりなる剥離層を順次形成した皮革の表面に、昇華性 染料を含む画像を転写してなる昇華転写プリント塗装皮革。
[3] 下塗り層の一般皮革塗装用榭脂層が、アクリル系榭脂及び Z又はポリウレタン系榭 脂を含むものである請求項 1又は 2に記載の昇華転写プリント塗装皮革。
[4] 上塗り層の染着性榭脂が、ポリエステル系榭脂を含むものである請求項 1〜3のい ずれかに記載の昇華転写プリント塗装皮革。
[5] 剥離層の剥離性榭脂が、フッ素系榭脂又はポリアミドイミド系榭脂を含むものである 請求項 2〜4のいずれかに記載の昇華転写プリント塗装皮革。
[6] 皮革の表面に、少なくとも一層の一般皮革塗装用榭脂層を付与して下塗り層を形 成する工程、染着性榭脂と架橋剤を含む上塗り層を形成する工程、該上塗り層の上 面に昇華性染料を含む画像が印刷された転写シートを戴置し、加熱圧着して画像を 転写する工程を含むことを特徴とする昇華転写プリント塗装皮革の製造方法。
[7] 皮革の表面に、少なくとも一層の一般皮革塗装用榭脂層を付与して下塗り層を形 成した後、染着性榭脂と架橋剤を含む上塗り層を形成する工程、該上塗り層の上面 に剥離性榭脂層を付与して剥離層を形成する工程、該剥離層の上面に昇華性染料 を含む画像が印刷された転写シートを戴置し、加熱圧着して画像を転写する工程を 含むことを特徴とする昇華転写プリント塗装皮革の製造方法。
[8] 下塗り層の一般皮革塗装用榭脂層が、アクリル系榭脂及び Z又はポリウレタン系榭 脂を含むものである請求項 6又は 7に記載の昇華転写プリント塗装皮革の製造方法。
[9] 上塗り層の染着性榭脂が、ポリエステル系榭脂である請求項 6〜8のいずれかに記 載の昇華転写プリント塗装皮革の製造方法。
[10] 剥離層の剥離性榭脂が、フッ素系榭脂又はポリアミドイミド系榭脂を含むものである 請求項 7〜9のいずれかに記載の昇華転写プリント塗装皮革の製造方法。
PCT/JP2006/310668 2005-05-30 2006-05-29 昇華転写プリント塗装皮革製品及びその製造方法 WO2006129604A1 (ja)