WO2005112149A1 - 非水電解液二次電池用負極 - Google Patents
非水電解液二次電池用負極 Download PDFInfo
- Publication number
- WO2005112149A1 WO2005112149A1 PCT/JP2005/001500 JP2005001500W WO2005112149A1 WO 2005112149 A1 WO2005112149 A1 WO 2005112149A1 JP 2005001500 W JP2005001500 W JP 2005001500W WO 2005112149 A1 WO2005112149 A1 WO 2005112149A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- active material
- lithium compound
- layer
- negative electrode
- secondary battery
- Prior art date
Abstract
Description
Claims