Classifications

• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B81—MICROSTRUCTURAL TECHNOLOGY
  • B81C—PROCESSES OR APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OR TREATMENT OF MICROSTRUCTURAL DEVICES OR SYSTEMS
  • B81C1/00—Manufacture or treatment of devices or systems in or on a substrate
  • B81C1/00436—Shaping materials, i.e. techniques for structuring the substrate or the layers on the substrate
  • B81C1/00523—Etching material
  • B81C1/00539—Wet etching
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B32—LAYERED PRODUCTS
  • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
  • B32B15/00—Layered products comprising a layer of metal
  • B32B15/04—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material
  • B32B15/08—Layered products comprising a layer of metal comprising metal as the main or only constituent of a layer, which is next to another layer of the same or of a different material of synthetic resin
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C15/00—Surface treatment of glass, not in the form of fibres or filaments, by etching
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
  • C09D125/00—Coating compositions based on homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring; Coating compositions based on derivatives of such polymers
  • C09D125/02—Homopolymers or copolymers of hydrocarbons
  • C09D125/04—Homopolymers or copolymers of styrene
  • C09D125/08—Copolymers of styrene
  • C09D125/12—Copolymers of styrene with unsaturated nitriles
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
  • H10P50/00—Etching of wafers, substrates or parts of devices
  • H10P50/69—Etching of wafers, substrates or parts of devices using masks for semiconductor materials
  • H10P50/691—Etching of wafers, substrates or parts of devices using masks for semiconductor materials for Group V materials or Group III-V materials
  • H10P50/692—Etching of wafers, substrates or parts of devices using masks for semiconductor materials for Group V materials or Group III-V materials characterised by their composition, e.g. multilayer masks or materials
• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
  • H10P50/00—Etching of wafers, substrates or parts of devices
  • H10P50/73—Etching of wafers, substrates or parts of devices using masks for insulating materials
• • C—CHEMISTRY; METALLURGY
  • C03—GLASS; MINERAL OR SLAG WOOL
  • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
  • C03C2218/00—Methods for coating glass
  • C03C2218/30—Aspects of methods for coating glass not covered above
  • C03C2218/355—Temporary coating
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/26—Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension
  • Y10T428/263—Coating layer not in excess of 5 mils thick or equivalent
  • Y10T428/264—Up to 3 mils
  • Y10T428/265—1 mil or less
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/3154—Of fluorinated addition polymer from unsaturated monomers
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/3154—Of fluorinated addition polymer from unsaturated monomers
  • Y10T428/31544—Addition polymer is perhalogenated
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
  • Y10T428/31609—Particulate metal or metal compound-containing
  • Y10T428/31612—As silicone, silane or siloxane
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31652—Of asbestos
  • Y10T428/31663—As siloxane, silicone or silane
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31678—Of metal
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31855—Of addition polymer from unsaturated monomers
  • Y10T428/31935—Ester, halide or nitrile of addition polymer

Definitions

• the present invention is concerned with new protective coatings (primer layer, first protective coating, and optional second protective coating) for use in the manufacture of microelectronic devices such as those used in microelectromechanical systems (MEMS).
• new protective coatings primary layer, first protective coating, and optional second protective coating
• Etchants used for deep etching may vary depending upon the etch selectivity requirements for the devices to be fabricated.
• Basic etchants may contain amines such as ethylene diamine, ethanolamine, and/or water-miscible lower alcohols such as isopropanol to modulate the etching behavior of the solution.
• Bulk silicon etching is typically performed at temperatures in the range of 40° to 120°C and most typically at 60° to 90°C. The etching times range from 1 to 24 hours and most typically are in the range of 5 to 15 hours.
• Acidic etchants include aqueous solutions of hydrofluoric acid (HF), including concentrated (49% to 50%) HF, aqueous dilutions of the same, and buffered oxide etchants comprising aqueous mixtures of HF and ammonium fluoride.
• HF etchants are used primarily for etching silicon dioxide.
• Mixed acid etchants typically comprise mixtures of 70% nitric acid (HNO 3 ), 49% HF, and a diluent acid (e.g., 85% phosphoric acid (H 3 PO 4 ) or 100% acetic acid) and are used primarily for bulk silicon etching.
• Etching times for bulk silicon in these acid mixtures are typically in the range of 5 to 30 minutes and in some cases as long as 120 minutes at room temperature. It is common in silicon etching processes to utilize a thin (100- to 300-nm) silicon nitride or silicon dioxide coating on the silicon substrate as a mask for patterned etching or as a passivating layer to enclose active circuitry. Therefore, the protective coating system described here is commonly applied onto Si 3 N 4 or SiO 2 , which means good adhesion to these substrates is critical for obtaining acceptable protection.
• etch protective coatings or masks for MEMS fabrication processes have been selected primarily by using a trial-and-error method because there are no general-purpose protective coatings on the market.
• the etch selectivity of the etchants to various materials is often used as a guide for MEMS process engineers.
• films of silicon nitride have been used as a protective layer or hardmask during KOH or TMAH bulk silicon etching.
• Silicon dioxide has a higher etch rate than silicon nitride. Therefore, it is only used as a protective/mask layer for very short etches.
• Gold (Au), chromium (Cr), and boron (B) have also been reportedly used in some situations.
• Non-patterned hard-baked photoresists have been used as masks, but they are readily etched in alkaline solutions.
• Polymethyl methacrylate was also evaluated as an etch mask for KOH. However, because of saponification of the ester group, the masking time of this polymer was found to decrease sharply from 165 minutes at 60°C to 15 minutes at 90°C.
• Black wax (Apiezon ® W, available from Scientific Instrument Services, Inc., New Jersey) was also used as a protective coating in a 30%) by weight KOH etch process (70°C). After wet etching, the wax was removed using trichloroethylene.
• Organic polymers are ideal candidates for protective coatings.
• polymeric coating materials as photoresists, anti- reflective coatings, and planarization layers for many years. These materials are conveniently applied as thin films by the spin-on method and then baked or UN-cured to achieve the final coating form.
• One important requirement for the polymer is that it be highly soluble at room temperature in an environmentally friendly solvent. Because of the lack of a proper solvent, semicrystalline polyolefins such as polypropylene and polyethylene, as well as semicrystalline fluoropolymers such as Teflon ® , which are known to have excellent corrosion resistance to strong acids and strong bases, cannot be formulated into spin-coated compositions for protective coating applications.
• thermoplastic polymers such as polystyrene, ⁇ oly(cyclic olefins), polymethyl methacrylate, polydimethylsiloxanes, polyimides, polysulfones, and various photoresist polymers (e.g., polyhydroxystyrene and novolac resins) fail to survive many common, harsh deep-etching processes because of their susceptibility and permeability to the etchants, poor adhesion to the substrate, tendency to form coating defects, or lack of solubility in solvents accepted in the microelectronics industry.
• photoresist polymers e.g., polyhydroxystyrene and novolac resins
• the present invention overcomes these problems by providing spin-applied, polymer coating systems which protect device features from corrosion and other forms of attack during deep-etching processes which utilize concentrated aqueous acids and bases. Furthermore, these coating systems can be easily removed at the end of the processes.
• these systems comprise a first protective layer which is applied to a microelectronic substrate surface.
• the first protective layer is formed from a composition which comprises a polymer dispersed or dissolved in a solvent system.
• Preferred polymers are thermoplastic polymers and comprise recurring monomers having the formula
• each R ' is individually selected from the group consisting of hydrogen and C x -C 8 (and preferably C C 4 ) alkyls; and each R 2 is individually selected from the group consisting of hydrogen, - (and preferably C r C 4 ) alkyls, and C r C 8 (and preferably C C 4 ) alkoxys.
• the polymer preferably comprises at least about 50% by weight of monomer (I), more preferably from about 50-80% by weight of monomer (I), and even more preferably from about 65-78% by weight of monomer (I), based upon the total weight of the polymer taken as 100% by weight.
• the polymer preferably comprises at least about 15% by weight of monomer (II), more preferably from about 15-40% by weight of monomer (II), and even more preferably from about 20-35% by weight of monomer (II), based upon the total weight of the polymer taken as 100%) by weight.
• Monomers other than monomers (I) and (II) can also be present in the polymer, if desired.
• the combined weight of monomers (I) and (LT) in the polymer is preferably at least about 6O% by weight, and more preferably from about 60-99% by weight, based upon the total weight of the polymer taken as 100% by weight.
• Suitable other monomers include those having functional groups which can react with groups in a primer layer (e.g., an organo silane primer layer as discussed herein) are desirable for achieving chemical bonding between the two layers, thereby reducing the likelihood of lifting of the first coating layer during the etching process.
• These monomers may have, by way of example, haloall ⁇ dg., benzyl chloride, 2-chloroethyl methacrylate), ester (methacrylates, acrylates, maleates, fumarates), epoxy, or anhydride functional groups, which react readily with functional groups such as hydroxyl, amino, or oxiranyl groups which can be present in the primer layer.
• Some exemplary co-monomers are represented by the formulas
• each R 5 is individually selected from the group consisting of hydrogen and haloalkyls (preferably C,-C 4 ), with at least one R 5 preferably being a haloalkyl; eachR 6 is individually selected from the group consisting of hydrogen, C r C 10 alkyls (e.g., methyl, ethyl, butyl, isobornyl), haloalkyls (preferably C C 4 , e.g., 2-chloroethyl)), and epoxy-containing groups (preferably C r C 4 , e.g., glycidyl groups);
• functional groups derived from carboxylic acids such as esters or anhydrides, it is important that the corresponding monomer concentration in the thermoplastic copolymer be less than about 20% by weight, and preferably less than about 10% by weight to limit the possibility of hydrolysis and consequent dissolution or swelling of the first coating layer by basic etchants.
• the copolymer may be alloyed with other compatible polymers (e.g., polymethyl methacrylate, polyethyl methacrylate, poly(6-caprolactone), and polyvinyl chloride) that enhance coating adhesion to the primer layer via chemical or physical bonding, or that reduce permeability and chemical susceptibility to basic etchants.
• the polymer should be included in the first protective layer composition at a level of from about 5-30% by weight, preferably from about 10-25% by weight, and evenmore preferably from about 15-22% by weight, based upon the total weight of the first protective layer composition taken as 100% by weight.
• the solvent system utilized in the first protective layer composition should have a boiling point of from about 100-220°C, and preferably from about 140-180°C.
• the solvent system should be utilized at a level of from about 70-95% by weight, preferably from about 75-90% by weight, and more preferably from about 72-85% by weight, based upon the total weight of the first protective layer composition taken as 100% by weight.
• Preferred solvent systems include a solvent selected from the group consisting of methyl isoamyl ketone, di(ethylene glycol) dimethyl ether, propylene glycol monomethyl ether acetate, ethyl lactate, cyclohexanone, and mixtures thereof.
• first protective layer composition can be a cross-linkable composition, it is preferably a non-crosslinkable composition. Furthermore, it is preferred that the first protective layer formed from the first protective layer composition be nonconductive.
• the final first protective layer should also be non-photosensitive (i.e., a pattern cannot be defined in the layer when it is exposed to about 1 J/cm 2 ) and non-alkaline soluble (i.e., it is substantially - less than 0.5% by weight - insoluble in an aqueous solution having a pH of greater than about 8, and preferably greater than about 10).
• primer layer utilized in the protective systems of the invention. This layer should be included between the substrate and the first protective layer.
• Preferred primer layers are formed from primer layer compositions including a silane dispersed or dissolved in a solvent system.
• Aromatic and organo silanes are particularly preferred silanes for use in the primer layers of the invention.
• the most preferred silanes have the formula A A A Bk Si X 3 - ⁇ where:
• Y is selected from the group consisting of oxygen and sulfur
• silanes include phenylsilanes such as phenyltrimethoxysilane, phenyltrichlorosilane, phenyltriethoxysilane, phenyltriacetoxysilane, and diphenylsilanes such as diphenyldimethoxysilane, diphenyldichlorosilane, and diphenylsilanediol.
• the most preferred silanes include 2- phenylethyltrialkoxysilane, p/m-chlorophenyltrimethoxysilane, p/m- bromophenyltrimethoxysilane,(p/m-chloromethyl)phenyltrimethoxysilane, 2-(p/m- m e t h o x y ) p h e n y l e t h y l t r i m e t h o x y s i l a n e , 2 - ( p / m - chloromethyl)phenylethyltrimethoxysilane, 3,4-dichlorophenyltrichlorosilane, 3-phenoxypropyltrichlorosilane, 3-(N-phenylamino)propyltrimethoxysilane, and 2-(diphenylphosphino
• An effective primer layer composition according to the invention is a mixture of diphenyldialkoxysilane (e.g., diphenyldimethoxysilane) andphenyltrialkoxysilane, (e.g., phenyltrimethoxysilane) or, even more preferably, a mixture of diphenylsilanediol and phenyltrimethoxysilane in a solution of 1 -methoxy-2-propanol or 1 -propoxy-2-propanol with from about 5-10% by weight water.
• diphenyldialkoxysilane e.g., diphenyldimethoxysilane
• phenyltrialkoxysilane e.g., phenyltrimethoxysilane
• a particularly effective primer layer composition for first protective layers comprising a poly(styrene-co-acrylonitrile) polymer is an alcohol and water solution containing from about 0.1-1.0%) (preferably from about 0.25-0.5%) by weight diphenylsilanediol and from about 0.1-1.0% (preferably from about 0.25-0.5%) by weight of phenyltrimethoxysilane.
• diphenylsilanediol and phenylsilanetriol the hydrolysis product of phenyltrimethoxysilane
• Another preferred silane has the formula
• Silanes having this structure are not only compatible with stvrene-containing copolymers, but they are also reactive with ester, benzyl chloride, and/or epoxy groups that may be present in the first protective layer, and they are excellent adhesion promoters.
• One particularly preferred silane within the scope of this formula is
• This silane is 3-[N-phenylamino]propyltrimethoxysilane, and it is commercially available from Lancaster Synthesis and Gelest Corporation.
• the silane should be included in the primer layer composition at a level of from about 0.01-5%) by weight, preferably from about 0.1-1% by weight, and even more preferably from about 0.2-0.8% by weight, based upon the total weight of the primer layer composition taken as 100%> by weight.
• the solvent system utilized in the primer layer composition should have a boiling point of from about 100-220°C, and preferably from about 140- 180°C.
• the solvent system should be utilized at a level of from about 80-99.9%) by weight, and preferably from about 85-99% by weight, based upon the total weight of the primer layer composition taken as 100% by weight.
• Preferred solvent systems include a solvent selected from the group consisting of methanol, ethanol, isopropanol, butanol, 1- methoxy-2-propanol, ethylene glycol monomethyl ether, and l-propoxy-2-propanol, and mixtures thereof, hi one preferred embodiment, water is included in the solvent system at a level of from about 2-15% by weight, and preferably from about 5-10% by weight, based upon the total weight of the primer layer composition taken as 100% by weight.
• the primer layer composition can optionally include low levels (e.g., from about 0.01-0.10%) by weight) of a catalyst.
• Suitable catalysts include any inorganic or organic acid (e.g., hydrochloric acid, sulfuric acid, phosphoric acid, acetic acid) or an inorganic or organic base (e.g., potassium hydroxide, TMAH, ammonia, amines).
• the protective system of the invention further includes a second protective layer on top of the first protective layer to provide further protection against concentrated aqueous acids such as hydrofluoric acid, nitric acid, phosphoric acid, acetic acid, and mixtures of the foregoing. This embodiment is useful in situations where a acid etching is utilized.
• Preferred second protective layers are formed from second protective layer compositions comprising a linear, slightly branched, or cyclic halogenated polymer dissolved or dispersed in a solvent system.
• these halogenated polymers should comprise high levels of halogen atoms (at least about 50%> by weight halogen atoms, and preferably at least about 60% by weight halogen atoms).
• the most preferred halogenated polymers are chlorinated polymers such as those comprising recurring monomers having the formula
• halogenated polymers include those selected from the group consisting of poly(vinyl chloride), polyvinylidene chloride, poly(vinylidene dichloride)-co-poly(vinyl chloride), chlorinated ethylene, chlorinated propylene, and mixtures thereof.
• halogenated chlorinated rubber is also very effective.
• the halogenated polymer should be included in the second protective layer composition at a level of from about 8-30% by weight, and preferably from about 10-20% by weight, based upon the total weight of the second protective layer composition taken as 100% by weight.
• the solvent system utilized in the second protective layer composition should have a boiling point of from about 100-220°C, and preferably from about 140-180°C.
• the solvent system should be utilized at a level of from about 70-92% by weight, and preferably from about 80-90% by weight, based upon the total weight f the second protective layer composition taken as 100% by weight.
• TYPICAL APPLICATION PROCESSES Prior to applying the primer layer, it is preferable to prepare the substrate by exposing it to brief (from about 15-60 seconds) oxygen plasma etching to clean and/or chemically activate the substrate surface to improve bonding by the primer layer. Plasma bombardment with heavy ions such as argon can also be beneficial for improving bonding. Such processes are especially effective for improving the bonding of the protective coating system to silicon nitride.
• Preferred substrates for use in this process include those selected from the group consisting of Si substrates, SiO 2 substrates, Si 3 N 4 substrates, SiO 2 on silicon substrates, Si 3 N 4 on silicon substrates, glass substrates, quartz substrates, ceramic substrates, semiconductor substrates, and metal substrates.
• the organosilane solution that makes up the primer layer is spin-applied onto the substrate at about 500-5000 rpm, and preferably from about 1000-2000 rpm, for about 30-90 seconds. It is then baked at greater than about 100°C for about 60-90 seconds to condense the organosilane molecules into a continuous film that is bonded to surface hydroxyl groups present on many microelectronic substrates. It is preferred that the primer layer have an average thickness (as measured by an ellipsometer over 5 different points) of less than about 5 nm and more preferably from about 2-8 nm.
• the thermoplastic polymer is dissolved in a suitable solvent at a concentration of from about 5-25% by weight and spin coated onto the substrate at about 500-5000 rpm, and preferably from about 1000-3000 rpm, for about 30-90 seconds. It is soft-baked at a temperature of from about 80-130°C for about 60- 120 seconds to dry the coating and then is subjected to a final bake at a temperature of from about 130-225 °C for about 60-90 seconds to density the first protective layer and bond it firmly to the primer layer.
• the preferred process for baking styrene-acrylonitrile coatings is to bake them at a temperature of about 130°C for about 120 seconds and then at a temperature of about 200°C for about 60 seconds.
• the polymer solids level and spinning conditions are adjusted typically to achieve a final coating thickness of from about 1-5 ⁇ m, and preferably from about 2-5 ⁇ m, depending upon the degree of coverage required over device topography on the substrate.
• the second protective layer is applied from a solvent solution in a manner similar to that described above with respect to the first protective layer.
• the solvents used to apply the second protective layer should be selected to minimize detrimental interaction with the first protective layer. It is preferred that the second protective layer have an average thickness (as measured by an ellipsometer over 5 different points) of from about 1-5 ⁇ m, and more preferably from about 2-5 ⁇ m. It is prefened that the protective layer(s) or coating(s) be removed after the wet etching processes have been completed.
• a particularly preferred technique is stripping the coating(s) with solvents commonly used in microelectronic processing such as acetone, propylene glycol methyl ether acetate, or ethyl lactate.
• solvents commonly used in microelectronic processing
• the coated substrate is sprayed with, or immersed in, the solvent until the coating layer has fully dissolved.
• the substrate is then rinsed with fresh solvent until clean.
• the protective coating system described here is easily removed by dissolving the thermoplastic layer (the first coating layer) in a solvent such as acetone.
• the second coating layer if present, is either dissolved at the same time or is lifted as the first layer dissolves.
• Practicing the present invention will result in a protective layer system which suffers little or no lifting during etching processes.
• the layer systems will exhibit less than about 3 mm, preferably less than about 2 mm, and more preferably less than about 1 mm of lifting when subjected for about 2 hours to etching in an approximately 30-35%> by weight aqueous KOH solution having a temperature of about 83-87°C. Lifting is determined by measuring from the outside edge of the substrate to the furthest point on the layer system where the layer system is still attached to the substrate. Furthermore, the inventive protective layer system will experience very little or no etchant penetration during etching processes.
• the inventive protective systems when subjected for about 2 hours to etching in an approximately 30-35% by weight aqueous KOH solution having a temperature of about 83-87°C, will have less than about 0.1 pinholes per cm 2 of substrate, and preferably less than about 0.05 pinholes per cm 2 of substrate, when observed under a microscope at 10X magnification.
• Primer I was prepared by dissolving 0.5 g of diphenyldichlorosilane in 99.5 g of xylene followed by filtering with a 0.2/0.45- ⁇ m polypropylene filter.
• Primer II was prepared by dissolving 0.5 g of diphenyldimethoxysilane in 90 g of isopropanol and 10 g of water followed by filtering with a 0.2/0.45- ⁇ m polypropylene filter.
• Primer III was prepared by dissolving 0.5 g of diphenylsilanediol and 0.5 g of phenyltrimethoxysilane in 90 g of propylene glycol monomethyl ether (PGME) and 10 g of water. The primer was aged for at least 24 hours so that the silanes were partially hydrolyzed and condensed. The primer was then it was filtered using a 0.2/0.45- ⁇ m polypropylene filter. Primer IN was prepared by dissolving 1.0 g of diphenylsilanediol and 1.0 g of phenyltrimethoxysilane in 88 g of PGME and 10 g of water.
• PGME propylene glycol monomethyl ether
• Primer N (Comparative Primer)
• Primer N was prepared by adding 1.0 g of 3- aminopropyltriethoxysilane into 95 g of PGME and 5 g of water. The primer was aged for at least 24 hours so that the silane was partially hydrolyzed and condensed. The primer was then filtered using a 0.2/0.45- ⁇ m polypropylene filter.
• EXAMPLE 3 Preparation of Primer NI
• a diethyl fumarate-modified, amino functional silane was prepared by mixing one mole of ⁇ -(3-trimethoxysilyl)-propylethylenediamine with one mole of diethyl fumarate, followed by stirring at room temperature for 48 hours. The mixing process was exothermic, indicating the immediate reaction of the two components.
• Primer VI was prepared by dissolving 1 g of the above modified silane into 90 g of PGME and 10 g of water. The mixture was aged for 24 to 48 hours at room temperature and then filtered using a 0.2/0.45- ⁇ m polypropylene filter for future use.
• Primer N ⁇ Primer Nil i s an adhe si on promo ter b as ed on 3-( ⁇ -phenyl)aminopropyltrimethoxysilane, which is very effective for polystyrene-co-acrylonitrile polymers, especially for coatings containing reactive groups such epoxy, ester, or chloromethyl (benzyl chloride) groups.
• Primer N ⁇ was prepared by dissolving 0.5 g of the aromatic amino silane in 90 g of PGME and 10 g of water. The mixture was aged in a manner similar to the previous examples and filtered using a 0.2/0.45- ⁇ m polypropylene filter.
• MIAK methyl isoamyl ketone
• Composition B was formulated by dissolving 18 g of S AN30 in 41 g of methyl isoamyl ketone (MIAK) and 41 g of di(ethylene glycol) dimethyl ether. Both coating compositions were filtered twice using a 0.2/0.45- ⁇ m polypropylene filter.
• MIAK methyl isoamyl ketone
• a mixed solvent of propylene glycol monomethyl ether acetate (PGMEA) and ethyl lactate in a weight ratio of 9:1 was also used as the solvent.
• the change of solvent did not noticeably change the coating quality or adhesion.
• EXAMPLE 6 Preparation of a Terpolymer and Formulation of Coating Composition C from the Terpolymer
• a terpolymer of styrene, acrylonitrile, and glycidyl methacrylate was prepared.
• Styrene and glycidyl methacrylate were purified by passing through an aluminum oxide column.
• Acrylonitrile was purified by washing sequentially with a 5% by weight H 2 SO 4 solution, a 5% by weight NaOH solution, and water to remove inhibitors and amine impurities that might cause crosslinking of the polymer. It was dried over anhydrous calcium chloride and then 4- A molecular sieves.
• a 500-ml two-neck flask containing a 1-inch magnetic stirring bar was charged with 100 g of cyclohexanone (or PGMEA) and a mixture of purified monomers including 35 g of styrene, 10 g of acrylonitrile, and 5 g of glycidyl methacrylate.
• 300 mg of 2,2'-azobisisobutylnitrile (AJBN) (or benzoyl peroxide) were added to the mixture as an initiator.
• the side neck of the flask was capped with a rubber septum, and the main neck of the flask was connected to a water-cooled condenser with the top end of the condenser linked to a bubbler containing mineral oil.
• the system was purged with nitrogen to remove oxygen through the side neck of the flask through a needle.
• the flask was heated using a hotplate at 80°C for about 8 hours to polymerize the monomer mixture.
• the reactor was slowly purged with nitrogen to prevent oxygen from entering.
• the polymer obtained was then precipitated in a mixture of isopropanol or ethanol containing 20% by weight water in a fast-stirring blender.
• the polymer was recovered by filtration and vacuum-dried to remove any solvent or monomer residues. The yield or conversion of the reaction was 80% to 85%.
• GPC Gel permeation chromatography
• EXAMPLE 7 Preparation of a Terpolymer and Formulation of a Coating Composition D from the Terpolymer
• a mixture of purified monomers including 30 g of styrene, 15 g of acrylonitrile, and 5 g of butyl acrylate was polymerized in PGMEA, and the polymer was recovered using the same method described in Example 3. The conversion or the yield of the polymerization for this system was around 80%.
• composition D (15% solids) was prepared by dissolving 15 g of the recovered dry polymer in 76.5 g of PGMEA and 8.5 g of ethyl lactate. It was filtered twice using a 0.2/0.45- ⁇ m polypropylene filter.
• EXAMPLE 8 Preparation of a Quaterpolymer and Formulation of a Coating Composition E from the Polymer In this procedure, a quaterpolymer of styrene, acrylonitrile, butyl acrylate, and glycidyl methacrylate was prepared.
• styrene, butyl acrylate, and glycidyl methacrylate were purified by passing through a column of aluminum oxide.
• Acrylonitrile was purified by washing with 5 wt%> H 2 SO 4 , 5 wt% NaOH, and deionized water sequentially followed then dried over anhydrous calcium chloride and 4 A molecular sieves.
• a mixture of purified monomers including 25 g of styrene, 15 g of acrylonitrile, 5 g of butyl acrylate, and 5 g of glycidyl methacrylate was polymerized and recovered according to the methods described in Example 6. The conversion or the yield of the polymerization for this system was around 80%.
• Composition E (15 wt% solids) was prepared by dissolving 15 g of the recovered dry polymers in 76.5 g of PGMEA and 8.5 g of ethyl lactate. It was filtered twice using a 0.2/0.45- ⁇ m polypropylene filter.
• Composition G was prepared by dissolving 12 g of chlorinated rubber (CLORTEX ® 20 from American Tartaric Corporation) in 88 g of PGMEA, followed by filtering with a 0.2/0.45- ⁇ m polypropylene filter.
• Composition H was prepared by dissolving 10 g of chlorinated PNC (TempRite 674X571 from ⁇ oven, Inc.) in 90 g of cyclohexanone, followed by filtering with a 0.2/0.45- ⁇ m polypropylene filter.
• EXAMPLE 12 Procedure for Applying Primers I-N ⁇ and Coating Compositions A-G
• the primed wafer was baked on a hotplate at 100- 130°C for 1 minute to promote chemical bonding between the substrate and the primer as well as partial vulcanization of the primer.
• a layer of the particular coating composition e.g., Composition A
• Composition A was spin-applied and then baked on a hotplate sequentially at 100°C for 2 minutes, 130°C for 1 minute, and 205°C for 1 minute.
• EXAMPLE 13 KOH Deep-Etch Tests for Various Coating/Primer Combinations The test equipment included a glass etchant tanker containing about 4000 ml of a 30% to 35% by weight aqueous KOH solution in which a TEFLON ® wafer boat holding the test substrates in a horizontal orientation was fully immersed.
• the etchant solution was heated using an internal heating unit or outer heating unit such as a hotplate, and the temperature of the etchant was controlled to 85°C ⁇ 1.5°C.
• 4-inch wafers of silicon, silicon nitride, or silicon nitride with aluminum deposited at the central circular area (approximately 2 inches in diameter) were used for the test.
• the test was only conducted for 2 to 4 hours because of the high etch rate of silicon in KOH.
• the test was extended to at least 8 hours.
• the solution was bubbled vigorously with nitrogen to provide agitation.
• wafer samples were removed, rinsed, dried, and then inspected for pinholes and edge lift or detachment of the coating layer(s). Because aluminum is very reactive toward KOH solution, any penetration of the coating (either by pinholes or poor KOH resistance of the coating) was indicated by disappearance of aluminum at the area.
• the distance from the edge of the wafer to the front line of coating detachment in the radial direction was used as a measure of the adhesion quality of the primer/coating combination. Results are shown in Table 1.
• EXAMPLE 14 Resistance of Coating Combinations to Concentrated Hydrofluoric Acid The test described in this example provided a means for rating the resistance of coating combinations to hydrofluoric acid and the time for the hydrofluoric acid to penetrate the 1.5-micron thick coating layers. At room temperature, a drop (approximately 0.2 ml) of 49% HF was placed in the center of a silicon wafer coated centrally with aluminum and another drop (approximately 0.2 ml) was placed on the area outside of the aluminum deposit. The wafers were then carefully observed for penetration of hydrofluoric acid through the coating, as indicated by the formation of hydrogen bubbles resulting from the aluminum reacting with hydrofluoric acid.
• the silicon wafers were contained in a wafer carrier boat, which was then placed in the tool for exposure to the etchant. The wafers were tumbled during the entire length of the etching process (approximately 30 minutes). Once removed, the wafers were rinsed and evaluated for coating performance.
• the test was conducted at room temperature, with a constant fresh supply of etching solution applied to the substrates. Results are shown in Table 3.

Landscapes

• Chemical & Material Sciences (AREA)
• Engineering & Computer Science (AREA)
• Organic Chemistry (AREA)
• Life Sciences & Earth Sciences (AREA)
• Materials Engineering (AREA)
• Microelectronics & Electronic Packaging (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Chemical & Material Sciences (AREA)
• Geochemistry & Mineralogy (AREA)
• Manufacturing & Machinery (AREA)
• Wood Science & Technology (AREA)
• Paints Or Removers (AREA)
• Laminated Bodies (AREA)
• Formation Of Insulating Films (AREA)
• Weting (AREA)

Priority Applications (4)

Applications Claiming Priority (2)

Publications (2)

Family

ID=34749694

Family Applications (1)

Country Status (9)

Cited By (3)

Families Citing this family (27)

Citations (2)

Family Cites Families (46)

• 2004
  • 2004-01-16 US US10/759,448 patent/US7316844B2/en not_active Expired - Lifetime
• 2005
  • 2005-01-07 SG SG200902577-6A patent/SG152244A1/en unknown
  • 2005-01-07 AT AT05705442T patent/ATE523263T1/de not_active IP Right Cessation
  • 2005-01-07 EP EP20050705442 patent/EP1715961B1/en not_active Expired - Lifetime
  • 2005-01-07 KR KR1020067014090A patent/KR101189394B1/ko not_active Expired - Fee Related
  • 2005-01-07 WO PCT/US2005/000786 patent/WO2005072489A2/en not_active Ceased
  • 2005-01-07 JP JP2006549513A patent/JP5165247B2/ja not_active Expired - Fee Related
  • 2005-01-07 CN CNB2005800025652A patent/CN100566852C/zh not_active Expired - Fee Related
  • 2005-01-12 TW TW94100834A patent/TWI405263B/zh not_active IP Right Cessation
• 2006
  • 2006-06-30 US US11/428,123 patent/US7758913B2/en active Active
• 2007
  • 2007-09-17 US US11/856,552 patent/US8202442B2/en not_active Expired - Lifetime

Patent Citations (2)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events