WO2005035635A1 - 光硬化性転写シート、これを用いた光情報記録媒体の製造方法、及び光情報記録媒体 - Google Patents

光硬化性転写シート、これを用いた光情報記録媒体の製造方法、及び光情報記録媒体 Download PDF

Info

Publication number
WO2005035635A1
WO2005035635A1 PCT/JP2004/015091 JP2004015091W WO2005035635A1 WO 2005035635 A1 WO2005035635 A1 WO 2005035635A1 JP 2004015091 W JP2004015091 W JP 2004015091W WO 2005035635 A1 WO2005035635 A1 WO 2005035635A1
Authority
WO
WIPO (PCT)
Prior art keywords
photocurable
transfer sheet
photocurable transfer
layer
information recording
Prior art date
Application number
PCT/JP2004/015091
Other languages
English (en)
French (fr)
Other versions
WO2005035635A8 (ja
Inventor
Hideki Kitano
Takato Inamiya
Kenji Murayama
Hidefumi Kotsubo
Yasuhiro Morimura
Original Assignee
Bridgestone Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2003348373A external-priority patent/JP2005116051A/ja
Priority claimed from JP2003348360A external-priority patent/JP2005116050A/ja
Priority claimed from JP2003395799A external-priority patent/JP2005154598A/ja
Priority claimed from JP2003426140A external-priority patent/JP2005182963A/ja
Priority claimed from JP2003426163A external-priority patent/JP2005182964A/ja
Priority claimed from JP2003426599A external-priority patent/JP2005182971A/ja
Priority claimed from JP2004291166A external-priority patent/JP2005158232A/ja
Priority to US10/574,840 priority Critical patent/US8916335B2/en
Priority to EP04792331A priority patent/EP1674505B1/en
Priority to KR1020067006728A priority patent/KR101137306B1/ko
Application filed by Bridgestone Corporation filed Critical Bridgestone Corporation
Publication of WO2005035635A1 publication Critical patent/WO2005035635A1/ja
Publication of WO2005035635A8 publication Critical patent/WO2005035635A8/ja

Abstract

光重合性官能基を有する反応性ポリマーを含む、加圧により変形可能な光硬化性組成物からなる光硬化性転写層を有する光硬化性転写シートであって、光硬化性転写層が、動的粘弾性測定装置を用いるクリープ試験において、常温で、応力50Pa、120秒間の条件で、時間[t](秒)に対する歪み[γ](%)の関係が、直線性を示し、且つ下記式:logγ=a+b・logt (但し、aが実数を表し、bが0.10～0.53の範囲にある)を満足することを特徴とする光硬化性転写シート、これを用いた光情報記録媒体の製造方法及び光情報記録媒体。

Description

明細書
光硬化性転写シート、 これを用いた光情報記録媒体の製造方法、
及び光情報記録媒体
1. 技 分野
本発明は、 DVD (Digital Versatile Disci) 、 CD (Compact Disc) 等の大 容量の文字、 音声、 動画像等の情報をディジタル信号として記録された及び/又 は記録可能な光情報記録媒 、 その製造方法及びこれらに有利に使用される光硬 化性転写シートに関する。
2. 背景技術
ディジタル信号として表面にピット形成された記録済み光情報記録媒体として、 ォ ディォ用 CD、 CD— ROMが広く使用されているが、 最近、 動画像と記録 も可能な両面にピット記録がなされた DVDが、 CDの次世代記録媒体として注 目され、 徐々に使用されるようになってきている。 またピット及びグループが形 成されたユーザが記録可能な CD— R、 CD-RW, DVD-R, DVD-RW 等も注目されている。
両面に記録層を持つ DVDには、 例えば、 図 9に示すようにそれぞれ片面に信 号ビットを形成した 2枚の透明樹脂基板 1， 2の該信号ビット形成面にそれぞれ 反射層 l a， 2 aを形成し、 これら反射層 l a, 2 aを互いに対面させた状態で 基板 1 , 2を接着剤層 3を介して貼り合わせ、接合した両面読み出し方式のもの、 及ぴ、 図 10に示すように、 それぞれ片面に信号ビットを形成した基板 1， 2に おいて、 一方の基板 1の信号ビット面に半透明反射層 1 bを形成すると共に、 他 方の基板 2の信号ビット面に反射層 2 aを形成し、 これら半透明反射層 1 bと反 射層 2 aとを対向させた状態で基板 1 , 2を接着剤層 3を介して貼り合わせ、 接 合した片面読み出し方式のものとが知られている。
両面読み出し DVDの製造は、 従来、 一般に前記信号ピットの凹凸が雄雌反対 の凹凸を有するスタンパを用いて、 ポリカーボネート樹脂を溶融し、 射出成形す ることにより表面に凹凸を有する透明横脂基板を作製し、 この凹凸表面にアルミ 二ゥム等の金属をスパッタリング等により蒸着することによつて反射層を形成し、 この反射層が形成された透明樹脂基板 2枚を反射層を対向させて接着剤で貼り合 わせることにより行われていた。
2 0 0 2年 2月 1 0日に次世代光デイスクめ統一規格 「プル一レイ 'ディスク (Blu-ray Disc) 」 が提案された。 主な仕様は、 記録容量： 2 3 . 3 / 2 5 / 2 7 G B、 レーザ波長： 4 0 5 n m (青紫色レーザ） 、 レンズ開口数 (N/A) : 0 . 8 5、ディスク直径： 1 2 O mm、ディスク厚： 1 . 2 mm, トラックピッチ： 0 . 3 2 m等である。
上記のようにブル—レイ ·ディスクでは、 溝の幅が狭く、 且つピットも小さく なっている。 このため読み取りレーザのスポットを小さく絞る必要があるが、 ス ポットを小さくするとディスクの傾きによる影響を大きく受けるようになり、 再 生しようとする D VDがわずかに曲がっていても再生できなくなる。 このような 不利を補うため、 基板の厚さを薄くし、 またレーザ照射側のピット上のカバー層 の厚さを 0 . 1 mm程度にすることが考えられている。
日経エレクト口 クス (NIKKEI ELECTRONICS)、 2 0 0 1 . 1 1 . 5号の 6 8頁に上記要求に合う D VDの製造方法が記載されている。 図 1 1を参照しなが ら説明する。凹凸表面に反射層（又は言己録層） 6 aを有するディスク基板 (1.1mm) 4 aのその反射層上に紫外線硬化樹脂 5 Aを塗布により設け、 凹凸表面に反射層 (又は記録層） を有するポリカーボネート製スタンパ 4 bの上に紫外 ϋ硬化樹脂 5 Βを塗布により設ける。 次いで、 基板を表裏反転させて、 基板とスタンパを貼 り付け、 スタンパ側から紫外線を照衬して紫外線硬化樹脂樹脂 5 Α及ぴ 5 Bを硬' 化させる。 紫外線硬化榭脂 5 Bの層 らスタンパ 4 bを除去し、 その'凹凸面に反 射層 （又は記録層） 6 bを形成し、 その上にカバー層 （厚さ 0 .' l mm程度） 7 を形成する。
上記の方法において、 ディスク基板及びスタンパの表面には、 塗布により紫外 線硬化樹脂が設けられ、 さらにその後基板を表裏反転させて、 スタンパと貼り付 けている。 このように塗布及ぴ反転の複雑な工程を行う必要があり、 また反転し て基板とスタンパを貼り付けする際、 粘チヨゥな紫外線硬化樹脂同士の接触の際 に気泡の発生等の不利があり、 良好な貼り付けを行うことができないとの問題が ある。 さらに、 上記紫外線硬化樹脂は硬化時に収縮が大きく、 得られる媒体の反 り等の変形が目立つとの問題もある。
上記問題点が改良可能な D V D等の光情報記録媒体の製造方法が、 WO O 3 /
0 3 2 3 0 5 A 1に開示されている。 ここに.は、 光重合性官能基を有する反応性 ポリマーを含み且つ加圧により変形可能な光硬化性組成物からなる光硬化性転写 シートを用いた製造方法が記載されている。 即ち、 上記紫外線硬化性樹脂の代わ りに、 固体状の上記光硬化性転写シートを用いて、 スタンパに押圧することによ り凹凸面を転写して上記問題点が回避できる。
3 . 発明の開示
しかしながら、 上記光硬化性転写シートは、 常温でも押圧により基板やスタン パの凹凸面を転写することができるため、 この転写シートをロール状に製造した り、 口ール状で保存した際、 光硬化个生転写層の成分がにじみ出す場合があること が明らかとなった。 即ち、 上記光硬化性転写シートは、 一般に軟化しやすい光碌 化性転写層の両側を剥離シートで挟んだ構造を有しているが、 実際の製造におい て、 例えばこの光硬化性転写層と剥离佳シートを同一幅で長尺状シート （以下、 フ ルエッジともいう） のロールとした場合、 光硬化性転写層の成分が口ールの側面 にしみ出し、 製造装置、 作業員等を汚染する場合があり、 これにより作業性が低 下するとの問題が発生することが明らかとなった。 さらには、 ロールを貯蔵して いる間に、 その荷重によりシートの厚さが変化する等の問題も発生する。
これらを防止する目的で、 光硬化 転写層に接着する剥離シートの幅を転写層 より大きくした長尺状シート （このような構造のシートを、 以下ドライエッジと も言う） をロールにしたものを用いて作業を行う方法が考えられる。 しかしなが ら、 このような方法を用いても、 作業性 fまやや向上するものの、 前記貯蔵中のシ 一ト厚の変動を抑えることはできない。
従って、 本発明の第 1の側面は、 D VD等の厚さが薄く、 高容量の光情報記録 媒体の製造に有利な光硬化性転写シートであって、 作業性に優れた光硬化性転写 シートを提供することをその目的とする。
また、 本発明の第 1の側面は、 D VD等の厚さが薄く、 高容量の薄い光情報記 録媒体の製造に有利な光硬化性転写シー卜であって、 長尺状シートのロールの状 態でも、 光硬化性転写層の成分のしみ出しが無く、 シート厚の変動も起こさない 光硬化性転写シートを提供することをその目的とする。
さらに、 本発明の第 1の側面は、 上記光硬化性転写シートを用いて光情報記録 媒体の製造方法を提供することをその目的とする。
また、 本発明の第 1の側面は、 上記製造方法により得られる厚さの薄い光情報 記録媒体を提供することをその目的とする。 また、 現在、 実用化されている上記のような D VDの貼り合わせ型の光デイス クは、 一般に、 高反射層にアルミニウム 匕合物を用い、 半透明 （低） 反射層に金 を用いている。 半透明反射層は高反射層に比べレーザを透過させなければならな いため、薄膜ィ匕しなければならず安定な化合物の代表である金が用いられてきた。 しかしながら、 金は高価な材料であるため、 半透明反射層の材料はシリコン化合 物、 銀化合物へと移行してきている。
また、 現在、 記録容量をさらに向上させるために前記ブル一レイ ·ディスク等 に使用される青色レーザの検討が進んでレヽる。 赤色レーザ等の高波長レーザ （波 長： C D = 7 8 0 n m、 D V D = 6 3 5 n m) の場合は半透明反射層が金、 シリ コン又は銀化合物であっても赤色レーザの透過性は問題なかったが、 青色レーザ の 4 0 0 n m付近の低波長光に対する透過性を考慮すると、 半透明反射層の材料 として使用できるのは銀、 銀合金或いは銀化合物が有効であることが確認されて いる。 しかしながら、 銀化合物は金化合物よりも腐食を受けやすく、 不安定であ る。 銀化合物の半透明反射層を使用した貼り合わせディスクでは、 金を半透明反 射層とした従来の貼り合わせ光ディスクと同等の耐久性が得られず、 未だ耐久性 において満足できる接着剤が提供されていない。
上記問題を解決するために、 特開 2 0 0 2— 1 4 6 2 4 1号公報には、 銀又は その合金からなる薄膜に接する硬化 S莫を形成するための紫外線硬化型樹脂組成物 として、 特定のチオールィ匕合物を含む樹脂組成物が提案されている。 この特定の チオールを用いることにより銀化合物の腐食を防止し、 耐久性の良好な光ディス クを得ることができるとしている。 . '
上記公報に記載の光ディスクでは、 酸化防止剤として特定のチオール化合物を 1質量。 /0前後使用する必要がある。 し力 しながら、 このような化合物を添加する ことにより、 耐久性は若干改善するものの、 銀反射層に形成するチオール化合物 を含む保護被膜は強度において満足なものではなく、 充分な耐久性を得ることが できない。 即ち、 通常の紫外線硬ィ匕型オリゴマー、 アタリレートモノマー、 及ぴ 光重合開始剤からなる紫外線硬化型樹脂組成物に上記特定のチオール化合物等の 酸化防止剤を添カ卩しても耐久性が充分に得られ難い場合が多い。
一方、 反射層及び半透明反射層は、.その保護及び他の層との接着のために、 光 硬化性の樹脂組成物を接着して製造されることが一般的である。 この光硬化性樹 脂組成物は、 銀合金等からなる層との接着力の向上のために、 一般にリン酸メタ クリレートを樹脂全体に対して 1 0 0 0 p p m以上含有する。 この技術は、 例え ば特開 2 0 0 2— 2 5 6 2 2 8号公報に記載されている。 このリン酸メタクリレ ートを含有しない場合には、 銀合金等からなる層との接着力が不十分となり、 製 造工程でスタンパからの剥離時に、 しばしば銀合金等からなる層から、 この保護 層 ·接着層が剥離しやすくなり、 製造が困難となることが知られている。
リン酸メタタリレートを含有する光硬化性樹脂組成物を用いる上記従来技術に おいては、 湿熱環境下で反射層及び半透明反射層を接着する層 （接着層、 場合に より保護層） がリンの存在によって黄変するという問題がある。 これにより反射 率が低下するために、 結果として光情報記録媒体の耐久性を低下させていた。 光ディスクの多層化のために積層する半透明反射層においては、 半透明の特性 のために特に薄膜化しなければならず、 この影響は顕著である。
従って、 本発明の第 2の側面は、 耐久性 ίこ優れた、 銀又は銀合金の反射層を有 する光情報記録媒体を提供することもその目的とする。
また、 本発明の第 2の側面は、 上記光情拳艮記録媒体の製造に有利な光硬化性組 成物を提供することをその目的とする。
さらに、 本発明の第 2の側面は、 上記光情報記録媒体の製造に有利な光硬化性 転写シートを提供することをその目的とする。
さらにまた、 本発明の第 2の側面は、 上記光情報記録媒体の製造方法を提供す ることをその目的とする。 本発明は、
光重合性官能基を有する反応性ポリマーを含む、 加圧により変形可能な光硬化 性組成物からなる光硬化性転写層を有する光硬化性転写シートであって、
光硬化性転写層が、 動的粘弾性測定装置を用いるクリープ試験において、 常温 で、 応力 50 P a、 1 20秒間の条件で、 3寺間 [t] (秒） に対する歪み [γ] (%) の関係が、 直線性を示し、 且つ下記式：
l o g y=a+b , l o g t
(但し、 aが実数を表し、 bが 0. 10〜0. 55 (特に 0. 53) の範囲に ある） を満足することを特徴とする光硬化'卜生転写シート①にある。 これは特に本 発明の第 1の側面の目的に適うものである。
上記光硬化性転写シート①において、 ^応性ポリマーのガラス転移温度が 2 0 °C以下 （特に 1 5 °C〜一 10 °C) であること、 反応性ポリマーの数平均分子量 が 10000〜 300000であること、 また重量平均分子量が 10000〜3 00000であることが好ましレ、。 転写性、 作業性の点から好ましい。
反応性ポリマーが、光重合性官能基を 1 ~ 50モル％含むことが適当な硬化性、 硬化被膜強度を得る上で好ましい。 光重合†生官能基が、 （メタ） ァクリロイル基 であることが、 硬化性の点で好ましレ、。 光硬化性 ¾a成物が、 光重合開始剤を 0 . 1〜 1 0質量％含むことが適当な硬化性を得る上で好ましレ、。 光硬化性転写シー トの厚さが 1〜1 2 0 0 πι (特に 5〜3 0 0 μ πι) であること力 転写性、 作 業性の点から好ましい。
光硬化性転写シートは 3 8 0〜 4 2 0 n mの波長領域 （好ましくは 3 8 0〜 6 0 0 n m、 特に 3 8 0〜8 0 0 n mの波長領域） の光透過率が 7 0 %以上である ことが好ましい。 これにより得られる媒体にレーザによる信号の読み取りを行つ た場合に、 エラーの無い操作が保証される。 上記光硬化性転写シートの硬化収縮 率が 8 %以下であることが好ましい。
以上の好ましい態様は、 以下の全ての光硬化性転写シート②〜⑧においても共 通のものである。
上記光硬化性転写シート①における反応性ポリマーは、 活性水素を有する官能 基及び光重合性官能基を有する反応†生ポリマーであり、 且つ反応性ポリマーを含 む光硬化性組成物が、 さらに活性水泰を有する官能基と反応性を有する基を少な くとも 2個有する化合物を含んでいることが好ましい。 このような官能基を有す る化合物を含む光硬化性転写シートは、 反応性ポリマーの活性水素を有する官能 基と反応性を有する基を少なくとも 2個有する化合物とを反応させる （一般に、 塗布後、 常温 2 4時間後） ことにより、 転写層が僅かに架橋し、 これにより転写 層のしみ出し、 厚さ変動が有効に防止される。 この架橋により上記クリープ試験 における特性を容易に得ることができる。 この光硬化性転写シート①において、 活性水素を有する官能基は、 一般にヒ ドキシル基である。 また活性水素を有する 官能基と反応性を有する基がィソシァネート基であることが好ましい。 ィソシァ ネート基は、 ヒドロキシル基等と常温での硬化が可能であり、 作業性が良好であ る。 活性水素を有する官能基と反応†生を有する基を少なくとも 2倔有する化合物 力 S、光硬化性組成物中に 0 . 2〜 2質量％の範囲で含まれていることが好ましい。 転写層のしみ出しを防止するために適当な架橋がもたらされる。 この場合、 基板 ゃスタンパの凹凸の良好な転写性も維持される。 また、 反応性ポリマーが、 活性 水素を有する官能基を 0. 1〜10モル％含んでいることが好ましレ、。 転写層の しみ出しを防止する程度の適当な架橋が得られる。
あるいは、 本発明の光硬化性転写シート①においては、 光硬化性組成物が、 さ らに溶解度パラメータ （SP値） が 8. 50以上の粘着性付与剤を含んでいるこ と、 光硬化性組成物が平均粒径が 3 00 nm以下の透明微粒子を含んでいること が好ましい。
また、 光硬化性転写層における、 周波数 1Ηζ、 0. 01Hz及ぴ 100 H z における貯蔵弾性率が、 25 °Cにおいて、 それぞれ 1 X 103〜9 X 104P a、 5 X 103P a以上、 及ぴ 1 X 107P a以下であることが好ましい。
また、 光硬化性組成物は、 置換基を有するフヱノール化合物を 0. 01〜0. 3質量％含有していることが好ましい。
また、 光硬化性組成物の硬化層表面の水接触角が 60度以上であることが好ま しい。
光硬化性組成物が、 リン酸 （メタ） アタリレート及び/又はその誘導体を 10 〜220 p pm含有していることが好ましい。
本発明は、
活性水素を有する官能基及び光重合性官能基を有する反応性ポリマーを含む、 加圧により変形可能な光硬化性組成物からなる光硬化性転写層を有する光硬化性 転写シートであって、
光硬化性組成物が、 さらに活性水素を有する官能基と反応性を有する基を少な くとも 2個有する化合物を含んでいることを特徴とする光硬化性転写シート②； 光重合性官能基を有する反応性ポリマーを含む、 加圧により変形可能な光硬化 性組成物からなる光硬化性転写層を有する光硬化性転写シートであって、
光硬化性組成物が、 さらに溶解度パラメータ （SP値） が 8. 50以上の粘着 性付与剤を含んでいることを特徴とする光硬化性転写シート③；
光重合性官能基を有する反応性ポリマー及び平均粒径が 300 nm以下の透明 微粒子を含む、 加圧により変形可能な光硬化性組成物からなる光硬化性転写層を 有する光硬化性転写シート④；
光重合性官能基を有する反応性ポリマーを含む光硬化性組成物からなり、 且つ 周波数 1 H z 、 0 . 0 1 H z及び 1 0 0 H zにおける貯蔵弾性率が、 2 5 °Cにお いて、 それぞれ 1 X 1 0 3〜 9 X 1 0 4 P a 、 5 X 1 0 3 P a以上、 及び 1 X 1 0 7 P a以下である光硬化性転写層を有する光硬化性転写シート⑤；にもある。
以上の光硬化性転写シート②〜⑤は、 本発明の特に第 1の側面の目的に適うも のである。
光硬化性転写シート②の好適態様は、 車云写シート①で述べたとおりである。 光硬化性転写シート③の好適態様としては、まず粘着性付与剤 (tackifier)の S P 値が 9 . 5 0以下、 特に 9 . 0 0以下であることである。 反応性ポリマー、 所望 により使用される反応性希釈剤との相溶性が良好で、 転写層に適度な粘性及び粘 着性 （例えば転写層と剥離シートとの接着性の向上） を効率良く （即ち少量で） 付与することができ、転写層の前記浸み广ビし、厚さ変動を抑制することができる。 粘着性付与剤としては、軟化点が 9 0 〜 1 3 5 °C、ガラス転移点が 4 5 〜 6 5 °C の範囲にあることが好ましい。 また粘着'生付与剤の数平均分子量又は重量平均分 子量が 6 0 0 〜 8 0 0の範囲にあること力 S好ましい。
粘着性付与剤が、'一般にロジン誘導体スはテルペン系樹脂である。
前記光硬化性転写シート④の好適態様としては、 まず透明微粒子が、 シリカ、 二酸化チタン及びポリメチルメタタリレートから選択される少なくとも 1種の微 粒子であることであり、 特にシリカ微粒子が好ましレ、。 透明微粒子は、 一般に光 硬化性組成物中に 0 . 5〜 2 0質量％の ¾S囲で含まれる。 また透明微粒子の平均 粒径は、 l〜3 0 0 n mの範囲、 1〜 2 0 0 n mの範囲が好ましい。 これらの態 様は、 しみ出し、 シート厚の変動を抑えながら、 透明性を維持するのに特に有利 である。 ·
前記光硬化性転写シート⑤の好適態様としては、 まず光硬化性組成物は、 一般 にさらに、 分子量が 1 0 0 0以下の、 光重合性官能基を有する可塑化反応性希釈 剤を含んでいることである。 この可塑化反応性希釈剤の量は光硬化性組成物の総 量に対して固形分で 1 0質量％以上（特に 2 0質量。/。以上、特に 2 5質量％以上； 上限は 4 0質量％が好ましい） 含むことが好ましい。 光重合性官能基を有する可 塑化反応性希釈剤は、 一般に （好ましくは直鎖の） アルカンジオールのジ （メタ） アタリレートであり、 アル力ンジオールの炭素原子数が 3〜 1 0個であることが 特に好ましい。 特にアタリレートが好ましい。
本発明は、 上記光硬化性転写シート①〜⑤の'光硬化性組成物にもある。
または本発明は、
表面に記録ピット及び/又はグノレーブとしての凹凸を有する光硬化性組成物の 硬化層、 及び該凹凸表面の凹凸に沿って設けられている銀又は銀合金の反射層を 含む光情報記録媒体であって、
光硬化性組成物が、 上記の光硬ィ匕†生転写シート①〜⑤に記載された組成物であ ることを特徴とする光情報記録媒体：
表面に記録ピット及び/又はグノレープとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀又は銀合金の反射層が設けられた基板の該反射層上に、 該反射 層の凹凸表面に接触するように設けられた光硬化性組成物の硬化層を含む光情報 記録媒体であって、
光硬化性組成物が、 上記の光硬ィ匕†生転写シート①〜⑤に記載された組成物であ ることを特徴とする光情報記録媒体；にもある。
本発明の特に第 2の側面を達成するのに特に好適な光硬化性転写シートは、 光重合性官能基を有する反応性ポリマーを含み、 且つ置換基を有するフエノー ル化合物を 0 . 0 1〜0 . 3質量％含有する光硬化性組成物を含む光硬化性転写 層を有する光硬化性転写シート⑥； '
光重合性官能基を有する反応性ポリマーを含む光硬化性組成物を含む光硬化性 転写層を有し、 その光硬化性転写層の硬化後の表面の水接触角が 6 0度以上であ ることを特徴とする光硬化性転写シート⑦；及び
光重合性官能基を有する反応性ポリマーを含み、 リン酸 （メタ） アタリレート 及び/又はその誘導体を 1 0〜2 2 0 p p m含有する光硬化性組成物を含む光硬 化性転写層を有する光硬化性転写シート⑧；である。
光硬化性転写シート⑥の好適態様としては、 置換基を有するフ ノール化合物 は、 一般に重合防止剤又は酸化防止剤として使用されているものである。 この置 換基を有するフエノール化合物が、 ハイ ドロキノン系化合物又はヒンダ一ドフエ ノール系化合物であることが、 本発明における特定の光硬化性組成物の系では特 に好ましい。
また、 光硬化性組成物が、 さらにアク リル樹脂 （好ましくは、 ガラス転移温度 (Tg) が 50〜： L 30°C、 さらに 60〜： L 00°C、 特に 60〜80°C；重量平 均分子量が 5000〜： L 000000、 特に 50000〜 500000、 数量平 均分子量 5000〜 1000000、 特に 50000〜 500000) を含むこ とが耐久性が向上し、 好ましい。 一般に光硬化性組成物がァクリル樹脂を 5〜 5 0質量％含むことが好ましい。
本発明は、 さらに表面に記録ピット及ぴ Z又はグループとしての凹凸を有する 光硬化性組成物の硬化層、 及び該凹凸表面の凹凸に沿って設けられている銀又は 銀合金の反射層を含む光情報記録媒体であって、
光硬化性組成物が、 光硬化性転写シート⑥で使用される組成物であることを特 徴とする光情報記録媒⑥一 1 ；
表面に記録ピット及び/又はグループとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀又は銀合金の反射層 設けられた基板の該反射層上に、 該反射 層の凹凸表面に接触するように設けられた光硬化性組成物の硬化層を含む光情報 記録媒体であって、
光硬化性組成物が、 光硬化性転写シート⑥で使用される組成物であることを特 徴とする光情報記録媒⑥ー 2 ；
表面に記録ピット及び/又はグループとしての凹凸をする基板の該凹凸表面の 凹凸に沿って銀又は銀合金の反射層が設けられ、 さらに該反射層の凹凸表面に接 触するように、 凹凸表面を有する光硬ィ匕性組成物の硬化層とその凹凸表面上の反 射層との積層単位がこの順で 1単位以 _b設けられてなる光情報記録媒体であって、 光硬化性組成物が、 光硬化性組成物が、 光硬化性転写シート⑥で使用される組 成物であることを特徴とする光情報記録媒⑥ー 3 ；及ぴ
表面に記録ピット及ぴ /又はグノレーブとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀又は銀合金の反 t層が設けられた基板と、 表面に記録ピット及 ぴノ又はグループとしての凹凸を し、 さらに該凹凸表面の凹凸に沿って反射層 が設けられた基板の二枚の基板が、 反射層同士を対向させた状態で、 光硬化性組 成物の硬化層を介して接合されてなる光情報記録媒体であって、
光硬化性組成物が、 光硬化性組成物が、 光硬化性転写シート⑥で使用される組 成物であることを特徴とする光情報記録媒⑥一 4 ；にもある。
上記光硬化性組成物の硬化層の厚さが 5〜 3 0 0 μ mであることが好ましい。 前記光硬化性転写シート⑦における、 本発明の水接触角は、 光硬化性組成物の 硬化層の表面に、 水滴をたらし、 固液界面の水平線と水滴端での接線との 2つの 線のなす角を測定したもので、 詳細は J I S - R 3 2 5 7に記載の静滴法に従つ て行った。
光硬化性転写シート⑦において、 光硬化†生組成物が、 重合性二重結合を有する 反応性希釈剤を含み、 この反応性希釈剤としては、 （メタ） アタリロイル基 （即, ち、 アタリロイル基又はメタクリロイル基） を 2個有する、 分岐アルカン又は環 状アルカン或いは （メタ） アタリロイル基を 1個有する、 長鎖 （一般に炭素原子 数 1 0以上） のアルカン又は環状アルカンが好ましい。 このような希釈剤を使用 することにより硬化層表面の水接 ¾角を容易に高くすることができる。
本発明は、 表面に記録ピット及ぴ Z又ほグループとしての凹凸を有する光硬化 性組成物の硬化層、 及ぴ該凹凸表面の凹凸に沿って設けられている銀又は銀合金 の反射層を含む光情報記録媒体であって、 光硬化性組成物が、 上記光硬化性転写 シート⑦で使用される組成物（即ち、硬化層表面の水接触角が 6 0度以上である） ことを特徴とする光情報記録媒⑦ー 1 ；
表面に記録ピット及ぴ Z又はグノレーブとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀又は銀合金の反衬層が設けられた基板の該反射層上に、 該反射 層の凹凸表面に接触するように設けられた光硬化性組成物の硬化層を含む光情報 記録媒体であって、
光硬化性組成物が上記光硬化性転写シート⑦で使用される組成物であることを 特徴とする光情報記録媒⑦ー 2 ；
表面に記録ピット及び/又はグ /レーブとしての凹凸をする基板の該凹凸表面の 凹凸に沿って銀又は銀合金の反射層が設けられ、 さらに該反射層上に、 該凹凸表 面に接触するように、 表面に凹凸を有する光硬化性組成物の硬化層とその凹凸表 面上の反射層との積層単位がこの MSで 1単位以上設けられてなる光情報記録媒体 であって、
光硬化性組成物が上記光硬化性寧云写シート⑦で使用される糸且成物であることを 特徴とする光情報記録媒⑦一 3 ；及ぴ
表面に記録ピット及び/又はグ /レープとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀又は銀合金の反射層が設けられた光情報記録基板と表面に記録 ピット及び/又はグループとしての凹凸を有し、 さらに該凹凸表面の凹凸に沿つ て反射層が設けられた光情報記録基板の二枚の基板が、 凹凸表面同士を対向させ た状態で、 光硬化性組成物の硬化層を介して接合されてなる光情報記録媒体であ つて、
光硬化性組成物が上記光硬化性転写シート⑦で使用される組成物であることを 特徴とする光情報記録媒⑦一 4 ；にもある。
光硬化性組成物の硬化層の厚さ力 S 5〜3 0 0 mであることが一般的である。 光硬化性転写シート⑧において、 リン酸 （メタ） ァクリレート及び/又はその 誘導体の含有量は、 前記のように光硬化性組成物全体 対して 1 0〜2 2 0 p p mであるが、 1 0 p p mより少ない場合には、銀合金等との接着が不十分となり、 3 6 0 p p m以上であれば、 耐久性は著しく低下する。 リン酸メタクリレートの 含有量が 1 0〜2 2 0 p p mの範囲にあれば、 湿熱環境下での反射率の低下がほ とんど見られず、 なおかつ銀合金等との接着性は十分であり、 特に 5 0〜2 0 0 p p mの範囲ではこの性質が好適に均衡を保つ。 リン酸 （メタ） アタリレート及び/又はその誘導体としては、 次の式：
Figure imgf000016_0001
(但し、 Rは、 H又は CH3であり、 nは、 0〜2. 0であり、 aは、 1. 0〜 3. 0であり、 bは、 0〜2. 0であり、 且つ aと bの和は 3.. 0である） で表される化合物を好適に使用することができ、 特に Rが CH3、 aが平均値 1. 5、 bが平均値 1. 5であり、 且つ n力 SOである混合物が好ましい。
光硬: ί匕性転写シート⑧の光硬化性組成物は、アタリル樹脂を含んでいること力 硬化後の機械的強度の確保の観点から好ましく、アタリル樹脂を 0〜 50質量％、 特に 5〜50質量％含むことが、 機械的耐久性を得るうえで好ましい。 特にァク リル樹脂 （好ましくは、 ガラス転移温度 （Tg) が 50〜： L 30° (：、 特に 60〜 100°C,さらに特に 60〜80°C;重量平均分子量 5000〜 1000000、 特に 50000〜 500000、 数量平均分子量 5000〜： L 000000、 特 に 50000〜 500000) を含むことが、 耐久性の向上の点から好ましい。 上記光硬化性組成物が、 光重合性宫能基を有する反応性希釈剤を含むことが好 ましく、 これにより組成物の性質を適宜調製することができる。 反応性希釈剤を 0〜50質量％含むことが、 適当な硬ィ匕性を得るうえで好ましい。
本発明は、 記録ピット及び/又はグ /レーブとして凹凸を有し、 さらに該凹凸表 面に沿って銀、 銀合金又は銀化合物からなる光反射層が設けられた光硬化性組成 物の硬化層を含む光情報記録媒体であって、
光硬化性組成物が、 上記光硬化性転写シート⑧で使用される組成物であること を特徴とする光情報記録媒体；
表面に記録ピット及ぴ z又はグループとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿つて銀、 銀合金又は銀化合物からなる光反射層が設けられた光情報記 録基板の該光反射層上に、 該光反射層の凹凸表面に接触するように設けられた光 硬化性樹脂組成物の硬化層を含む光情報記録媒体であつて、
光硬化性組成物が、 上記光硬化十生転写シート⑧で使用される組成物であること を特徴とする光情報記録媒体；及び
表面に記録ピット及び/又はグノレーブとしての凹凸を有し、 さらに該凹凸表面 の凹凸に沿って銀、 銀合金又は銀化合物からなる光反射層が設けられた光情報記 録基板 2枚が、 各 HO凸表面側を対向して、 光硬化性樹脂組成物の硬化層により接 着されてなる光情報記録媒体であって、
光硬化性組成物が、 上記光硬化个生転写シート⑧で使用される組成物であること を特徴とする光情報記録媒体；にある。
また、 本発明は、 上記光硬化性転写シート⑥〜⑧の光硬化性組成物にもある。 以上の光硬化性転写シート①〜⑧において、 光硬化性転写層の一方又は両方の 表面に、 剥離シートが設けられたものを、 以下の光情報記録媒体の製造方法に好 適に使用することができる。 この光硬化性転写シートは長尺状であり、 かつ光硬 化性転写層と剥離シートの幅が略同一であることが好ましい。
本発明は、
下記の工程 （2 ) '〜 （4 ) ：
( 2 ) 上記の剥離シートを有する光硬化性転写シートの一方の剥離シートを除 去する工程；
( 3 ) 表面に記録ピット及び/又はグループとしての凹凸を有し、 さらに該凹 凸表面の凹凸に沿って反射層が設けられた基板の亥反射層上に、 該光硬化性転写 シートの光硬化性転写層の表面が該反射層の凹凸表面に接触するように裁置し、 これらを押圧して該光硬化性転写シートの表面が該反射層の凹凸表面に沿って密 着された積層体.を形成する工程；及ぴ '
( 4 ) 該積層体からもう一方の录 ij離シートを除去する工程、
を含むことを特徴とする光情報記録媒体の製造方法にもある。
前記工程 （2 ) の前に、 ( 1 ) 光硬化性転写シートを円盤状に打ち抜く工程；又は
( 1 ) 光硬化性転写シートの光硬化性転写層と一方の剥離シートを円盤状に打 ち抜き、 もう一方の剥離シートをそのまま残す工程；
を行うことが好ましい。
また、 前記工程 〈4 ) を行った後、 さらに
( 5 ) 該積層体の剥離シートが除去された光硬化性転写層の表面に、 記録ピッ ト及び/又はグループとしての凹凸を するスタンパの該凹凸表面を裁置し、 こ れらを押圧して該光硬化性転写シートの表面が該凹凸表面に沿って密着した積層 体を形成する工程；
( 6 ) 該スタンパを有する積層体の) 硬化性転写層を紫外線照射により硬化さ せ、 次いでスタンパを除去することに り、 光硬化性転写層の表面に凹凸を設け る工程；
を行うことが好ましい。
さらに、 前記 （5 ) 〜 （6 ) の工程を行った後、
( 7 ) 光硬化性転写層の凹凸表面に^射層を設ける工程；
を行うことが好ましい。
本発明は、 上記の製造方法により得られる光情報記録媒体にもある。
4 . 図面の簡単な説明
第 1図は、本発明の光硬化性転写シー トの実施形態の一例を示す断面図である。 第 2図は、 本発明の光情報記録媒体 製造方法の一例を示す断面図である。 第 3図は、 本発明の製造方法により られる本発明の光情報記録媒体の一例を 示す断面図である。
第 4図は、 二重真空室方式の装置を用いた押圧法を説明するための該略図であ る。
第 5図は、 本発明の光情報記録媒体の一例を示す断面図である。
第 6図は、 本発明の光情報記録媒体の另 IJの一例を示す断面図である。 第 7図は、 実施例における、 睁間 [t] (秒） に対する歪み [γ] (%) をプ ロットしたグラフである。
第 8図は、 第 7図に基づく 1 0 g γと 1 o g tの関係を示すグラフである。 第 9図は、 従来の光情報記録媒体を示す断面図である。
第 10図は、 従来の別の光情報記録媒体を示す断面図である。
第 1 1図は、 日経エレクトロ二タスに記載ざれた光情報記録媒体の製造方法の 手順を示す断面図である。
5. 発明を実施するための最良の形態
以下に図面を参照して本発明の実施の形態を詳細に説明する。
第 1図は本発明で使用される光硬化性転写シート 10の実施形態の一例を示す 断面図である。 光硬化性転写層 1 1は、 両面に剥離シート 12 a , 12 bを有す る。 剥離シートは一方のみでも、 無くても良い。 使い方により適宜設定される。 光硬化性転写層 1 1は、 スタンパの凹凸表面を押圧することにより精確に転写 できるように、 加圧により変形し易い層であるとともに、 反応性ポリマーを僅か に架橋させること等により転写層のしみ出し、 層厚変動が大きく抑えられた層で ある。 即ち、 本発明の光硬化性転写層は、 動的粘弾性測定装置を用いるクリープ 試験において、 常温で、 応力 50 P a、 120秒間の条件で、 時間 [t] に対す る歪み [γ] (%) の関係が、 j£,線性を示し、 且つ下記式：
l o g y = a + b - l o g t
(伹し、 aが実数を表し、 bカ 0. 10〜0. 53の範囲にある） を満足する 層である。上記条件を満足する光硬化性転写層を有する光硬化性転写シート①は、 転写層のしみ出しが極めて抑制されると共に基板ゃスタンパの凹凸の転写性にも 優れている。 bの値が、 0. 53を超えると、 しみ出しが発生しやすくなり、 0. 10未満の場合は、 光情報記録媒体を作製する際の転写性が劣る傾向にある。 上記光硬化性転写層 1 1は、 例えば、 活性水素を有する官能基及び光重合性官 能基を有する反応性ポリマーを含み、 さらにこのポリマーの活性水素を有する官 能基と反応性を有する基を少なくとも 2個有する化合物 （特に、 ジイソシァネー ト化合物） をも少量含んでいる転写層 （光硬化性転写シート②） であり、 これに より転写層を有するシートの処理中或いは保存中に、 これらが相互に反応して僅 力に架橋し、 転写層の粘度を上昇させる。 これにより、 転写層のしみ出し、 層厚 変動が大きく抑えることができる。
また上記光硬化性転写層 1 1は、 例えば、 光重合性官能基を有する反応性ポリ マーを含み、 さらに特定の溶解度パラメータ （SP値） を有する粘着性付与剤を 含んでいる層 （光硬化性転写シート③） であり、 これにより転写層に適度な粘性 及び粘着性が付与されており、 転写層のしみ出し、 層厚変動が大きく抑えられて いる。 またこの粘着性付与剤の添加により光情報記録媒体作製時の転写性を損な うことはなレ、。
また上記光硬化性転写層 1 1は、 例えば、 スタンパの凹凸表面を押圧すること により精確に転写できるように、 加圧により変形し易い層であるとともに、 平均 粒径 300 nm以下の透明微粒子が導入された転写層 （光硬化性転写シート④） であり、 これにより転写層のしみ出し、 層厚変動が大きく抑えられた層である。 さらに、 光硬化性転写層 1 1は、 例えば、 スタンパの凹凸表面を押圧すること により常温でも精確に転写できるように、 特定の貯蔵弾性率を有する層、 即ち、 周波数 1Ηζ、 0. 01Hz及び 10 ひ H zにおける貯蔵弾性率が、 25 °Cにお いて、 それぞれ l X 103〜9X 104 P a、 5 X 103P a以上 （特に 8 X 1 03 P a以上） 、 及ぴ 1 X 107 P a以下 （特に 5 X 106 P a以下） である加圧によ り変形し易い転写層 （光硬化性転写シート⑤） である。
また、 光硬化性転写層 1 1は、 反応性ポリマーを含み、 置換基を有するフエノ ール化合物を 0. 01〜0. 3質量％含有していることが好ましい （光硬化性転 写シート⑥） 。 硬化層となった場合、 銀又は銀合金からなる反射層の保護作用を 発揮する。
光硬化性転写層 1 1は、 光硬化性組成物から構成される層であるが、 スタンパ の凹凸表面を押圧することにより常温でも精確に転写できるように、 光硬化性組 成物には光重合性官能基を有する反応性ポリマーを含み、 その硬化層の表面の水 接触角が 6 0度以上 （好ましくは 6 5度以上） の極めて疎水性となるように設計 することが好ましい （光硬化性転写シート⑦） 。
光硬化性転写層 1 1は、 スタンパの凹凸表面を押圧することにより常温でも精 確に転写できるように、 光重合性官能基を有する反応性ポリマーを含み、 リン酸
(メタ）アタリレートを 1 0〜2 2 0 p p m含有する層であることが好ましい（光 硬化性転写シート⑧） 。 硬化層となった場合、 銀合金等からなる反射層の保護作 用を顕著に発揮する。 ―
本発明の光硬化性転写シートは、 光硬化性転写層 1 1を構成する光硬化性組成 物（特に反応性ポリマー）のガラス転移温度が 2 0 °C以下（特に 1 5 °C〜一 1 0 °C) であることが好ましい。 また情報の高密度化のため、 再生レーザにより読み取り が容易に行えるように 3 8 0〜4 2 O n mの波長領域の光透過率が 7 0 %以上で あることが好ましい。 特に、 3 8 0〜4 2 0 n mの波長領域の光透過率が 8 0 % 以上であることが好ましい。 従って、 この転写シート用いて作製される本発明の 光情報記録媒体は 3 8 0〜 4 2 0 n mの波長のレーザを用いてピット信号を再生 する方法に有利に使用することができる。
上記光硬化性転写シート 1 0を用レ、て、 本発明の光情報記録媒体を、 例えば下 記の第 2図に示すように製造することができる。 - 光硬化性転写シート 1 0は、 先ず円盤状 （一般に中央に貫通孔を有するドーナ ッ状）に打ち抜かれる。この際、光硬 ί匕性転写層 1 1と両面の剥離シート 1 2 a , 1 2 b全てを打ち抜く場合 （一般にフルエッジの場合） と、 光硬化性転写層 1 1 と一方の剥離シート 1 2 bを円盤状^:打ち抜き、 もう」方の剥離シート 1 2 aを そのまま残す場合 （一般にドライエッジの場合） があり、 適宜選択して行われる
( 1 ) 。 このように予めの打ち抜き作業は、 本発明の光硬化性転写シートを用い ることにより、転写層のしみ出し、はみ出し無く、作業性良く行うことができる。 光硬化性転写シート 1 0から剥離シート 1 2 aを除去し、 剥離シート 1 2 b付 き光硬化性転写層を用意する （2 ) 。 表面に記録ピットとしての凹凸を有する基 板 2 1の該凹凸表面の半透明反射層 2 3 (一般に A g X、 銀合金等の反射率の比 較的低い反射層） 上に、 剥離シートの無い側を対向させて光硬化性転写シート 1 1を押圧する （3 ) 。 これにより光硬化性転写シートの表面が該凹凸表面に沿つ て密着された積層体 （1 1 , 2 3， 2 1からなる） を形成する。 この構成で光情 報記録媒体として使用する場合は、 光硬化性転写シート 1 1を紫外線照射により 硬化させ、 剥離シート 1 2 bを除去する （4 ) 。
次いで、表面に記録ピットとしての凹凸を有するスタンパ 2 4を、積層体から 剥離シート 1 2 bを除去して未硬ィヒ状態の光硬化性転写シート 1 1の表面 （基板 と接触していない側の表面） に押圧する （5 ) 。 光硬化性転写シート 1 1の表面 がスタンパ 2 4の凹凸表面に沿って密着した積層体 （2 1 , 2 3， 1 1， 2 4か らなる） を形成し、 そして積層体の光硬化性転写シートを紫外線照射により硬化 させた （6 ) のちスタンパ 2 4を除去することにより、 硬化シートの表面に記録 ピット等の凹凸を設ける。 これにより、 基板 1 1、 反射層 2 3及び硬化した光硬 化性転写シート 1 1から成る積層体 （光情報記録媒体） を得る。 通常、 この凹凸 上 （硬化シートの表面） に、 反射層 （一般に A 1等の高反射率の反射層） 2 5を 設け （7 ) 、 さらにその上に有機ポリマーフィルム （カバー層） 2 6を接着剤層 を介して貼付する （8 ) 。 これにより第 3図に示す光情報記録媒体を得る。 記録 ピットを有する硬化シートの表面に、 さらに光硬化性転写シートを押圧し、 紫外 線照射により硬化させても良い。 或いは、 硬化シートの表面に紫外線硬化性樹脂 を塗布、硬化させても良い。半透明反射層は、通常の A 1等の反射層でも良い（両 面読み出し用） 。 また反射層 2 3を半透明反射層、 半透明反射層 2 6を高反射率 の反射層としても良い。 さらにスタンパは、 凹凸を有する基板であっても良い。 また、 （7 ) の工程で高反射層の代わりに半透明反射層を設け、 同様に （2 ) 〜 （7 ) の工程を繰り返すことにより、 記録ピッ'トを三層以上形成することもで きる。
上記方法においては、 再生専用の光情報記録媒体について説明をしたが、 記録 可能な光情報記録媒体についても同様に行うことができる。記録可能媒体の場合、 グループ或いはグループ及びピットを^ Γしており、 この場合反射層及び半透明反 射層の代わりに金属記録層 （色素記録層の場合や金属記録層の反射率が低い場合 は、 記録層及ぴ反射層） が一般に設けられる。 それ以外は上記と同様に光情報記 録媒体を製造することができる。
本発明では、 記録ピット及び 又はグループである凹凸形状を、 光硬化性転写 層 1 1と基板 2 1とを 1 0 0 °C以下の]:匕較的低い温度 （好ましくは常温） で押圧 する （好ましくは減圧下） ことにより瘠確に転写されるように光硬化性率云写シー トが設計されている。 基板.2 1と、 光硬化性転写層 1 1 との重ね合わせは、 一般 に圧着ロールや簡易プレスで行われる （好ましくは減圧下） 。 また、 光硬化性転 写層 1 1の硬化後の層は、 基板 2 1の麦面の反射層に用いられる金属との接着力 が良好で剥離することはない。必要により反射層上に接着促進層を設けても良い。 本発明では、 記録ピット及び/又はグループである凹凸形状を、 光硬化性転写 層 1 1 とスタンパ 2 4とを 1 0 0 °C以下の低温（好ましくは常温）で押圧する（好 ましくは減圧下） ことにより精確に転写されるように光硬化性転写シートが設計 されている。 スタンパ 2 1と、 光硬化性転写シート 1 1との重ね合わせは、 一般 に圧着ロールや簡易プレスで行われる （好ましくは減圧下） 。 また、 光硬化性転 写層 1 1の硬化後の層は、 スタンパに用いられるニッケルなどの金属との接着力 が極めて弱く、光硬化性転写シートをスタンパから容易に剥離することができる。 基板 2 1は、 一般に厚板 （通常 0. 3〜： L . 5 mm、 特に 1 . 1 mm程度） で あるので、 従来の射出成形法で作製することが一般的である。 しかし光硬化性転 写シートとスタンパを用いて製造しても良レ、。 本発明の光硬化性転写シートは 3 Ο Ο μ πι以下 （好ましくは 1 5 0 ^ m以下） に薄くすることができるので、 もう 一方の基板を従来法で作製し、 基板の厚さを大きくすることができるのでピット 形状の転写精度を上げることができる。 '
上記工程において、 光硬化性転写層を基板に押圧する際、 或いはスタンパを光 硬化性転写層に押圧する際に、減圧下に押圧を行うことが好ましい。これにより、 気泡の除去等が円滑に行われる。 上記減圧下の押圧は、 例えば、 減圧下に 2個のロール間に、 光硬化性転写シー トとスタンパを通過させる方法、 あるいは真空成形機を用い、 スタンパを型内に 裁置し、 減圧しながら光硬化性転写シートをスタンパに圧着させる方法を挙げる ことができる。
また、 二重真空室方式の装置を用いて減圧下の押圧を行うことができる。 第 4 図を参照しながら説明する。 第 4図には二重真空室方式のラミネータの一例が示 されている。 ラミネータは下室 4 1、 上室 4 2、 シリコーンゴムシート 4 3、 ヒ ータ 4 5を備えている。 ラミ 、ータ内の下室 4 1に、 凹凸を有する基板と光硬化 性転写シートとの積層体 4 9、 又は基板と光硬化性転写シートとスタンパとの積 層体 4 9を置く。 上室 4 2及び下室 4 1共に排気する （減圧する） 。 積層体 4 9 をヒータ 4 5で加熱し、 その後、 下室 4 1を排気したまま上室 4 2を大気圧に戻 し、 積層体を圧着する。 冷却して積層体を取り出し、 次工程に移す。 これにより 排気時に脱泡が十分に行われ、 気泡の無い状態で、 スタンパ又は基板と光硬化性 転写シートとを圧着することができる。
上記本発明の製造方法を利用することにより有利に得られる本発明の光情報記 録媒体を第 5図及び第 6図に示す。 し力 しながら、 本発明の光情報記録媒体は、 本発明の光硬化性転写シート又はこれを構成する光硬化性組成物を用いて製造さ れるものであればどのような光情幸記録媒体であっても良く、 前記本発明の製造 方法で製造されなくても良い。
第 5図は、 本発明の光情報記録媒体の実施形態の一例を示す断面図である。 第 5図には、 表面に記録ピット （及び/又はグループ） としての凹凸を有する基板 2 1、 銀又は銀合金 [例、 AN C (A g、 （1及び〇11の合金） 、 A P C (A g、 P d及び C uの合金） ] 力 なる反射層 （半透明反射層、 即ち低反射率膜） 2 3 及ぴ硬化層 1 1から成る積層体である光情報記録.媒体が示されている。 硬化層 1 1は、 本発明の光硬化性転写層 （又は光硬化性組成物） の硬化した層である。 こ の光情報記録媒体から基板 2 1が除かれた銀又は銀合金からなる反射層 2 3と硬 化層 1 1から成る積層体である光情報記録媒体も、 本発明の媒体である。 即ち、 基板が無くても、 硬化層に自己支持性があればそのまま使用することができ、 或 いは基板の代わりに保護層を用いた場合の態様にも使用することができる。
第 6図には、 本発明の光情報記録媒体の別の実施形態の一例の断面図を示す。 表面に記録ピット （及び Z又はグループ） としての凹凸を有する基板 2 1 aと、 この凹凸表面に設けられた銀又は銀合金からなる反射層 （半透明反射層、 即ち低 反射率膜） 2 3とからなる基板、 及ぴ表面に記録ピット （及ぴ Z又はグループ） としての凹凸を有する基板 2 1 bと、 この凹凸表面に設けられたアルミニウム等 の反射層 （高反射率膜） 2 5とからなる基板の 2枚の基板が、 反射層同士を対向 させて本発明の硬化層 2 3を介して積層された光情報記録媒体が示されている。 前述の製造方法により形成された光 '隋報記録媒体のように、 アルミニウム等の 反射層 （高反射率膜） 2 5上の基板 2 1 bが、 有機ポリマーフィルム （カバー層） 2 6でも良い。
本発明では、 銀又は銀合金からなる反射層 （半透明反射層、 即ち低反射率膜） 2 3上に凹凸に沿って設けられた硬化層 1 1は、 前述の本発明の光硬化性転写シ 一ト①〜⑧を構成する光硬化性転写層 （又は光硬化性組成物） の硬ィヒしたもので ある。 従って、 前述の転写シートで述べた優位性を示す。
特に、 光硬化性転写シート⑥〜⑧から作製され.た硬化層を有する記録媒体にお いては、 反射層に強力に接着し且つ反射層を大きな被膜強度で保護する。 置換碁 の有するフ ノール化合物を含有する場合、 その酸化防止作用が有効に機能する ようにされていることから、 反射層の反射率の低下を顕著に防止している。 従つ てこのような硬化層が設けられた光情報記録媒体は耐久性に優れたものであると いうことができる。 '
また、 銀又は銀合金からなる反射層 （半透明反射層、 即ち低反射率膜） 2 3上 に凹凸に沿って設けられた硬化層 1 1力 S、 表面の水接触角が 6 0度以上 （好まし くは 6 5度以上） の極めて疎水性の光硬化性組成物の硬化層とした場合、 このよ うな層は高温高湿の条件下でも水分の侵入を防止するので、 上記反射層の腐食或 いは剥離等の膜欠陥等による反射率の低下を長期に亘り防止することができる。 従ってこのような硬化層が設けられた光情報記録媒体は耐久性に優れたものであ るということができる。
さらに、銀、銀合金又は銀化合物（銀合金等） からなる反射層 （半透明反射層、 即ち低反射率膜） 2 3上に凹凸に沿って設けられた硬化層 1 1が、 リン酸 (メタ) ァクリレート及び/又はその誘導体を含有する場合、 得られる硬化層は反射層に 強力に接着し、 且つ黄変等することなく保護しており、 これにより反射層の反射 率の低下を防止している。 従ってこのような硬化層が設けられた光情報記録媒体 は耐久性に優れたものである'ということができる。
本発明の光情報記録媒体の反射層に使用される銀合金等は、 反射層に使用され る一般的な銀合金等を好適に使用することができ、 例えば、 AN C (A g、 N d 及び C uの合金） 及ぴ A P C (A g、 卩 及ぴ。11の合金） を好適に使用するこ とができる。
前記本発明の製造方法で有利に使用することができる、 本発明の光硬化性転写 シートは、前記光硬化性転写シート ( 〜⑧、特に①〜⑤の構成を有する。従って、 本発明の光硬化性転写シートは、 加圧により変形可能な光硬化性組成物からなる · 光硬化性転写層を有するものである。 .
本発明の光硬化性転写シート①は、 前記光硬化性転写シート②〜⑧、 特に②〜 ⑤の光硬化性転写層を構成する組成物を適宜調製することにより有利に得ること ができる。
まず前記光硬化性転写シート②を構成する光硬化性組成物について説明する。 光硬化性組成物は、 一般に、 上記活'卜生水素を有する官能基及び光重合性官能基を 有する反応性ポリマー （一般にガラス転移温度が 2 0 °C以下のもの） 、 そして活 性水素を有する官能基と反応性を有する基を少なくとも 2個有する化合物、 さら に光重合性官能基 （好ましくは （メタ） アタリロイル基） を有する化合物 （モノ マー及びオリゴマー） 、 光重合性開女合剤及ぴ、 所望により他の添加剤から構成さ れる。
上記活性水素を有する官能基及び光重合性官能基を有する反応性ポリマーとし ては、 例えばアルキルァクリレート (例、 メチルァクリレート、 ェチルァクリレ ート、 プチルァクリ レート、 2—ェチルへキシルァクリ レート) 及び/又はアル キルメタクリ レー卜 (例、 メチノレメタクリ レート、 ェチルメタクリ レート、 ブチ ルメタタリレート、 2ーェチルへキシルメタクリレート) から得られる単独重合 体又は共重合体 （即ちアクリル樹脂） で、 且つ、 主鎖又は側鎖に光重合性官能基 及び活性水素を有する官能基を有するものである。 従って、 このような反応性ポ リマーは、 例えば、 上記 1種以上の （メタ） アタリ レートと、 ヒドロキシル基等 の官能基を有する （メタ） アタリ レート （例、 2—ヒドロキシェチル （メタ） ァ タリレート） とを共重合させ、 得られた重合体とイソシアナトアルキル （メタ） ァクリレートなどの、 重合体の宫能基と反応し且つ光重合性基を有する化合物と 反応させることにより得ることができる。 その際、 ヒドロキシル基が残るように ィソシアナトアルキル（メタ）ァクリレートの量を調節して使用することにより、 活性水素を有する官能基としてヒ ドロキシル基及び光重合性官能基を有する反応 性ポリマーが得られる。
或いは上記において、 ヒドロキシノレ基の代わりにアミノ基を有する （メタ） 了 タリレート (例、 2—アミノエチノレ.（メタ） アタリレート） を用いることにより 活性水素を有する官能基としてァミノ基を有する、 光重合性官能基含有反応性ポ リマーを得ることができる。 同様に、 活性水素を有する官能基としてカルボキ^ ル基等を有する、 光重合性官能基含有反応性ポリマーも得ることができる。
また、 上記のようにイソシアナトアルキル (メタ） ァクリレート等を用いてゥ レタン結合を介して光重合性基を形成しているが、 他の方法、 例えばカルボン酸 を含むアクリル樹脂を形成し、 このカルボン酸にエポキシ基を有する （メタ） ァ タリレート (例、 グリシジル （メタ） アタリレート） を反応させて光重合性基を 形成することもできる。 ■
本発明では、 前記光重合性官能基をウレタン結合を介して有するアクリル樹脂 が好ましい。
本発明の上記反応性ポリマーは、 光重合性官能基を一般に 1〜5 0モル％、 特 に 5〜30モル％含むことが好ましい。 この光重合性官能基としては、 ァクリロ ィル基、 メタクリロイル基、 ビニル基が好ましく、 特にァクリロイル基、 メタク リロイル基が好ましい。
また、 反応性ポリマーが、 ヒドロキシル基等の活性水素を有する官能基を 0. 1〜10モル0 /0、 特に 0. 5〜5モル％含んでいることが好ましレ、。 転写層のし み出しを防止する程度の適当な架橋が得られる易い。
またこの反応性ポリマーのガラス転移温度は、 一般に 20°C以下であり、 ガラ ス転移温度を 20 °C以下とす 'ることにより、 得られる光硬化性転写層がスタンパ の凹凸面に圧着されたとき、 常温にぉレヽてもその凹凸面に緊密に追随できる可撓 性を有することができる。特に、ガラス車云移温度が 15°C〜一 50°C、特に 15°C 〜一 1 o°cの範囲にすることにより追随性が優れている。 ガラス転移温度が高す ぎると、 貼り付け時に高圧力及び高圧力が必要となり作業性の低下につながり、 また低すぎると、 硬化後の十分な高度;^得られなくなる。
さらに、 本発明の反応性ポリマーは、 一般に数平均分子量が 5000〜100 0000、 好ましくは 10000〜 300000であり、 また重量平均分子量が 一般に 5000〜： 1000000、 好ましくは 10000〜 300000である ことが好ましい。
上記活性水素を有する官能基と反応 1 ^生を有する基を少なくとも 2個有する化合 物としては、イソシァネート化合物、エポキシ化合物等を挙げることができるが、 常温でも高い反応性を有するイソシァネート化合物が使い易く好ましい。
少なくとも 2官能性のィソシァネート化合物としては、 トリレンジイソシァネ ート （TD I) 、 イソホロンジイソシァネート、 キシリ'レンジィソシァネート、 ジフエ二ルメタン一 4， 4—ジィソシァネート、 ジシク口ペンタニルジィソシァ ネート、 へキサメチレンジイソシァネート、 2, 4， 4， ートリメチルへキサメ チレンジイソシァネート、 2, 2 ' , 4一トリメチルへキサメチレンジイソシァ ネートを挙げることができる。 またトリメチロールプロパンの TD I付加体等の 3官能以上のィソシァネート化合物も使用することができる„ これらの中でトリ メチロールプロパンのへキサメチレンジイソシァネート付加体が好ましい。
本発明の活性水素を有する官會 g基と反応性を有する基を少なくとも 2個有する 化合物は、 光硬化性組成物中に 0 . 2〜4質量％、 特に 0 . 2〜 2質量％の範囲 で含まれていることが好ましい。 転写層のしみ出しを防止するために適当な架橋 がもたらされると共に、 基板ゃスタンパの凹凸の良好な転写性も維持される。 上 記化合物と反応性ポリマーとの反応は、 転写層形成後、 徐々に進行し、 常温 （一 般に 2 5 °C) 、 2 4時間でかなり反応している。 転写層形成用の塗布液を調製し た後、塗布するまでの間にも反応は進行するものと考えられる。転写層を形成後、 ロール状態で卷き取る前にある程度硬化させることが好ましいので、 必要に応じ て、 転写層を形成時、 或いはその後、 ロール状態で巻き取る前の間に加熱して反 応を促進させても良い。
次に、前記光硬化性転写シート③を構成する光硬化性組成物について説明する。 上記光硬化性組成物は、一般に、上記光重合性官能基を有する反応性ポリマー（一 般にガラス転移温度が 2 0 °C以下のもの） 、 そして上記 S P値が 8 . 5 0以上の 粘着性付与剤、 さらに光重合性官能基 （好ましくは (メタ) アタリロイル基） を 有する化合物 （モノマー及びオリゴマー） 、 光重合性開始剤及び、 所望により他 の添加剤から構成される。
上記光重合性官能基を有する反応性ポリマーとしては、 例えばアルキルァクリ レート （例、 メチルアタリレート、 ェチルアタリレート、 プチルアタリレート、 2—ェチルへキシルァクリレート） 及び/又はアルキルメタクリレート （例、 メ チルメタクリレート、 ェチルメタクリレート、 プチルメタタリレート、 2—ェチ ルへキシルメタクリレート） から得られる単独重合体又は共重合体 （即ちァクリ ル樹脂）で、且つ、主鎖又は側鎖に光重合性官能基を有するものである。従って、 このような反応性ポリマーは、 iiえば、上記 1種以上の（メタ）アタリレートと、 ヒドロキシル基等の官能基を有する （メタ） アタリレート （例、 2—ヒドロキシ ェチル （メタ） アタリレート） とを共重合させ、 得られた重合体とイソシアナト アルキル （メタ） アタリレートなどの、 重合体の官能基と反応し且つ光重合性基 を有する化合物と反応させることに り得ることができる。
或いは上記において、 ヒドロキシノレ基の代わりにアミノ基を有する （メタ） ァ クリレート (例、 2—アミノエチル （メタ） アタリレート） を用いても、 カルボ キシル基を有する （メタ） アタリレート等を用いても、 光重合性官能基含有反応 性ポリマーも得ることができる。
また、 上記のようにイソシアナトアルキル ('メタ） ァクリレート等を用いてゥ レタン結合を介して光重合性基を形成しているが、 他の方法、 例えばカルボン酸 を含むアクリル樹脂を形成し、 このカルボン酸にエポキシ基を有する （メタ） ァ クリレート （例、 グリシジル (メタ) アタリレート） を反応させて光重合性基を 形成することもできる。
本発明では、 前記光重合性官能基をゥレタン結合を介して有するァクリル樹脂 が好ましい。
本発明の上記反応性ポリマーは、 光重合性官能基を一般に 1〜50モル％、 特 に 5〜 30モル％含むことが好ましい。 この光重合性官能基としては、 アタリ口 ィル基、 メタクリロイル基、 ビュル基が好ましく、 特にアタリロイル基、 メタク リロイル基が好ましい。
またこの反応性ポリマーのガラス云移温度は、 一般に 20°C以下であり、 ガラ ス転移温度を 20 °C以下とすることにより、 得られる光硬化性転写層がスタンパ の凹凸面に圧着されたとき、 常温においてもその凹凸面に緊密に追随できる可撓 性を有することができる。特に、ガラス転移温度が 15°C〜一 50°C、特に 15°C 〜一 15 °Cの範囲にすることにより追随性が優れている。 ガラス転移温度が高す ぎると、 貼り付け時に高圧力及び高 BE力が必要となり作業性の低下につながり、 また低すぎると、 硬化後の十分な高度が得られなくなる。
さらに、 本発明の反応性ポリマー ίま、 一般に数平均分子量が 5000〜 100 0000、 好ましくは 10000〜 300000であり、 また重量平均分子量が 一般に 5000〜 1000000、 好ましくは 10000〜 300000である ことが好ましい。 本発明は、 組成物中に溶解度パラメータ （SP値） が 8. 50以上の粘着性付 与剤を含むことがその特徵的要件である。 このような粘着性付与剤としては、 ゴ ム業界等で一般に使用されている粘着性付与剤で、 上記 S P値を満足するもので あればどのような樹脂でも使用することができる。 粘着性付与剤とは、 一般に、 天然ゴム、 合成ゴム、 ゴム系接着剤、 プラスチック等に配合し、 配合物の表面の 粘着性を増大させるために使用されるものであ'る。
上記粘着性付与剤としては、 例え ί 、 クマロン ·ィンデン樹脂及ぴクマロン樹 脂/ナフテン系油/フエノール樹脂の'混合物等のクマロン樹脂；テルペン樹脂、 変性テルペン榭脂 （例、 芳香族変性テルペン樹脂） 、 テルペン一フエノール樹脂 及ぴ水添テルペン樹脂等のテルペン系樹脂；ガムロジン、 トール油ロジン、 ゥッ ドロジン、 ロジンのペンタエリスリ トーノレ ·エステノレ、 ロジンのグリセローノレ ' エステル、 水素添加ロジン、 水素添力 Πウッドロジン、 水素添加ロジンのメチルェ ステル、 水素添加ロジンのペンタエリスリ トール ·エステル、 水素添加ロジンの トリエチレングリコーノレのエステノレ、 不均ィ匕ロジン、 重合ロジン、 重合ロジンの グリセ口ール ·エステル及ぴ硬化ロジン等の口ジン誘導体；テレピン系粘着付与 剤；芳香族炭化水素樹脂、 脂肪族系 化水素樹脂、 不飽和炭化水素 （ォレフイン 系、 ジォレフイン系） の重合体、 イソプレン系樹脂、 水素添加炭化水素樹脂、 炭 化水素系粘着化樹脂、 ポリブテン、 液状ポリブタジエン及び低分子量ブチルゴム 等の石油系炭化水素樹脂；スチレン系樹脂； フエノール系樹脂； キシレン系樹脂 を挙げることができる。 これらの中で、 テルペン系樹脂、 ロジン誘導体が好まし い。 特に水素添加テルペン系樹脂、 ロジンの各種エステルが好ましい。
本発明で使用される粘着性付与剤の好ましい市販品としては、 テルペン樹脂の YSレジン TR105 (ヤスハラケミカル （株） 製; SP値 =8. 26、 mp = l 05°C，T g = 50°C、 平均分子量 = 600) 、 水添テルペン樹脂のクリアロン M 115 (ヤスハラケミカル （株） 製; S P値 =8. 52S m p = 115°C,T g = 5 9°C、 平均分子量 =650) 、 テルペンフエノール樹脂の YSポリスター TH1 30 (ヤスハラケミカル（株）製； S P値 = 8.8 l、mp = l 30°C，Tg = 74°C、 平均分子量 = 710) ；そしてロジンエステルのパインクリスタル KE— 100 (荒川化学（株）製; S 値=約 8. 5、 mp = 95— 105° (：、酸価 = 2— 10)、 ロジンエステルのパインクリスタル KE—359 (荒川化学 (株) 製; S P値 =約 8. 6、 mp = 94— 104°C、 酸価 = 10— 20) を挙げることができる。 本発明の粘着性付与剤の S P値は、 8. 50〜9. 50、 特に 8. 50〜9. 00の範囲であることが好ましい。 このような粘着付与剤は、 反応性ポリマー、 及び所望により使用される反応性希釈剤との相溶性が特に良好で、 転写層に適度 な粘性及び粘着性（例えば転 ¥層と'剥離シートとの接着性の向上）を効率良く （即 ち少量で） 付与することができ、 転写シートをロール状にした際の浸みだし、 厚 さ変動を抑制することができる。
上記粘着性付与剤は、 軟化点が 90〜 135 ° (、 特に 90〜 120 °Cの範囲、 ガラス転移点が 40〜70°C、 特に 45〜65 °Cの範囲にあることが好ましい。 また粘着性付与剤は、 その数平均分子量が 600〜800の範囲、 特に 630〜 730の範囲にあるか、 又は重量平均分子量が 600〜800の範囲、 特に 63 0〜730の範囲にあることが好ましい。 また、 ロジンについては、 特に酸価が 30以下のものが好ましい。 .
上記各範囲を満足する粘着性付与斉 ϋは、 特に本発明の反応性ポリマーとの相溶 性に優れており、 特に本発明の効果を顕著に得ることができる。 . 本発明の粘着性付与剤は、 光硬化性組成物中に 0. 5〜 30質量％、 特に 1〜 20質量％の範囲で含まれていることが好ましい。
次に、前記光硬化性転写シート④を構成する光硬化性組成物について説明する。 上記光硬化性組成物は、 一般に、 上記平均粒径が 300 nm以下の透明微粒子、 そして上記光重合性官能基を有する反応性ポリマー （一般にガラス転移温度が 2 0°C以下のもの） 、 さらに光重合性官能基 （好ま.しくは （メタ） アタリロイル基） を有する化合物 （モノマー及びオリゴマー） 、 光重合性開始剤及び、 所望により 他の添加剤から構成される。
上記平均粒径が 300 nm以下の透明微粒子は、 上記光重合性官能基を有する 反応性ポリマー等の光硬化性組成物から禱成される光硬化性転写層の転写性、 光 硬化性等を損なうことなく、 光硬化性転写シートをロール状としたときの側面か らの転写層成分の滲み出し、 はみ出し、 そしてシート厚の変動を大きく抑制する ものである。
上記透明微粒子は、透明性を有し、平均粒径が 3 0 0 n m以下のものであれば、 無機微粒子でも、 有機微粒子でも良い。 _b記無機微粒子の例としては、 ガラスビ ーズ、 タノレク、 シリカ、 アルミナ、 マグネシア、 亜鉛華、 炭酸カルシウム、 硫酸 バリウム、 二酸化チタン、 水酸化アルミニウム、.マイ力、 長石粉、 石英粉を拳げ ることができ、 上記有機微粒子の例としては、 アクリル樹脂 （例、 ポリメチルメ タクリ レー卜 ( P MMA) ) 、 ポリスチレン、 スチレン/アクリル共重合体、 ポ リエチレン、 エポキシ樹脂、 シリコーン樹脂、 ポリフッ化ビニリデン、 テフロン (登録商標） 、 ジビュルべンゼン /スチレン共重合体、 フエノール樹脂、 ポリウ レタン、 酢酸セルロース、 ナイロン、 セ /レロース、 ベンゾグアナミン樹脂、 メラ ミン樹脂の微粒子を挙げることができる。 透明微粒子としては、 シリカ、 二酸化 チタン及ぴポリメチルメタクリレートが好ましく、特にシリ力微粒子が好ましい。 これらの微粒子の平均粒径は、 一般に 1〜3 0 0 n mであり、 l〜2 0 0 n mが 好ましい。 3 0 0 n mを超えた場合、 転写性が低下しやすくなる。 反対に小さす ぎると本発明の滲み抑制効果が低下する傾向にある。 . 上記シリカ微粒子は、 平均粒子径 ( 1次粒子径) が:！〜 3 0 0 n m、 さらに 1 〜2 0 0 n m、 特に 1 0〜 1 0 0 n mの範囲にあることが好ましレ、。 上記シリカ 微粒子は、粉体状シリカ又はコロイダル、ンリ力であり、その形状は球状、中空状、 多孔質状、 棒状、 板状、 繊維状、 もしく fま不定形状であり、 好ましくは球状であ る。 シリカ微粒子の比表面積は、一般に 0 . 1〜3 0 0 0 m 2Z gであり、 1 0〜 1 5 0 O m 2 ^が好ましい。 またシリカ微粒子の細孔容積は、一般に 0 . 1〜5 m l / gであり、 0 . 2〜2 m 1 / gが好ましい。 これらのシリカ微粒子の使用 形態は乾燥状態の粉末、 もしくは水もしくは有機溶剤で分散した状態で用いるこ とができ、 コロイダルシリカとして知られてレ、る微粒子状のシリ力微粒子の分散 液を直接用いることもできる。 コロイダルシリカの分散溶媒が水の場合、 その水 素イオン濃度は pH値として 2〜 10の範囲であり、 好ましくは pH3〜7の酸 性コロイダルシリカが用いられる。 また、 コロイダルシリカの分散溶媒が有機溶 剤の場合、 有機溶剤としてメタノール、 イソプロピルアルコール、 エチレンダリ コール、 プ'タノ一/レ、 エチレングリコーノレモノプロピノレエーテノレ、 メチノレエチル. ケトン、 メチルイソブチルケトン、 トノレェン、 キシレン、 ジメチノレホルムアミ ド 等の溶剤もしくはこれらと相溶する有機溶剤もしくは水との混合物として用いて も良レ、。 好ましい分散溶剤はメタノール、 'イソプロピルアルコール、 メチルェチ ルケトン、 キシレンである。 シリカ微粒子 の市販品としては、 例えば、 コロイダ ルシリカとしては日産化学工業（株）製のメタノールシリカゾル、 I PA— ST、 MEK— ST、 NBA— ST、 XBA— ST、 DMAC— S T及び S T— U P、 ST— OUP、 ST— 20、 ST— 40、 ST— C、 ST— N、 ST— 0、 ST 一 50、 ST— OL等を挙げることができる。 また、 粉末状シリカとしては、 日 本ァエロジル (株) 製のァエロジノレ 130、 ァエロジル 300、 ァエロジル 38 0、 ァエロジル TT 600及ぴァエロジル OX50 ；旭硝子 (株) 製のシルデッ タス H31、 H32、 H51、 H5 2、 H121、 H122 ;日本シリカ工業 (株) 製の二プシル VN 3、 E 200 A、 E 220 ；綜研化学 (株) 製のケミスノー MP ；富士シリシァ （株） 製のサイリシァ 470、 日本板硝子 （株） 製の SG7 レーク等を挙げることができ、 特にァエロジル 130、 ァエロジル 300、 ァェ 口ジノレ 380、 ァエロジル TT 600及ぴァエロジル OX 50 ； 日本シリカ工業 (株） 製の二プシル VN— 3 ；綜研化学 （株） 製のケミスノー MPが好ましい。 透明微粒子は、 光硬化性組成物中に一般に 0. 5〜20質量％ (透明微粒子を 含む光硬化性組成物の総固形分量に対する透明微粒子の質量比） 、 特に 1〜10 質量％の範囲で含まれることが好ましい。 この範囲に設定することにより、 しみ 出し、 シート厚の変動を抑えながら、 透明性を維持するのに特に有利となる。 前記のように、 本発明の光硬化性組成物は、 一般に、 上記の平均粒径が 300 nm以下の透明微粒子以外に、 上記光重合性官能基を有する反応性ポリマー （一 般にガラス転移温度が 2 0 °C以下のもの） 、 さらに光重合性官能基 （好ましくは (メタ） ァクリロイル基） を有する化合物 （モノマー及びオリゴマー） 、 光重合 性開始剤及び、 所望により他の添加剤を含んでいる。
光重合性官能基を有する反応性ポリマーとしては、 前記光硬化性転写シート② 及び③で示したものを使用することができる。
次に、前記光硬化性転写シート⑤を構成する光硬化性組成物について説明する。 上記光硬化性組成物は、一般に、上記光重合性官能基を有する反応性ポリマー（一 般にガラス転移温度が 2 0 °C以下のもの） 、 さらに光重合性官能基 （好ましくは (メタ) ァクリロイル基) を有する可塑ィ匕反応性希釈剤 (モノマー及ぴオリゴマ 一） 、 光重合性開始剤及び、 所望により他の添加剤から構成される。
上記光硬化性組成物から得られる光硬化性転写層 1 1は、 スタンパの凹凸表面 を押圧することにより常温付近で精確に事云写できるように、 特定の貯蔵弾性率を 有する層である。 即ち、 光硬化性転写層 1 1は、 周波数 1 Η ζ、 0 . 0 1 H z及 び 1 0 0 H zにおける貯蔵弾性率が、 2 5 °Cにおいて、それぞれ 1 X 1 0 3〜 9 X 1 0 4 P a、 5 X 1 0 3 P a以上 （特に 8 X 1 0 3 P a以上） 、 及ぴ 1 X 1 0 7 P a 以下 （特に 5 X 1 0 6 P a以下） である加圧により変形し易い層である。 Q . 0 1 H zにおける貯蔵弾性率は、未硬化時の貯蔵安定性に関わり、 この値が 5 X 1 0 3 P a未満の場合は口ール状態で保存してレヽる時に端部からの浸みだしが発生し り、 転写層の厚さの変動が起こる。 また 1 0 O H zにおける貯蔵弾性率は、 スタ ンパ等でピット等の凹凸形状を転写する際の硬さに関わり、 この値が 1 X 1 0 7 P aを超えた場合、 転写温度における転写性が充分でなく凹凸形状が精確に転写 されない。 周波数 1 H zにおける貯蔵弹十生率は上記両方の特性に関連する。 周波 数 1 H zにおいて、 1 X 1 0 3 P a未満の湯合は、未硬化時の厚さが変化しやすく、 9 X 1 0 4 P aを超えた場合は転写不良を起こしゃすい。
上記特定の貯蔵弾性率を有する光硬化性転写層は、 主として、 上記反応性ポリ マーと可塑化反応性希釈剤との、 種類及ぴ量の好適な組合せにより得ることがで さる。 ' 光重合性官能基を有する反応性ポリマーとしては、 前記光硬化性転写シート② 及び③で示したものを使用することができる。
可塑化反応性希釈剤としては、 後述する光重合性官能基を有する化合物から適 宜選択して使用することができるが、 これらのなかで、 分子量が 1 0 0 0以下、 更に 5 0 0以下、 特に 2 0 0〜4 0 0を有する化合物が好ましい。 また二官能性 の化合物が好ましい。 好ましい化合物として、' トリシクロデカンジメチロールジ (メタ） アタリレート、 1， 6—へキサンジオールジ (メタ） ァクリレート、 ノ ナンジオールジ (メタ) ァクリレート、 1 , 4—ブタンジォ一ル等を挙げること ができる （本発明では、 特にアタリレート類が好ましい） 。 この可塑化反応性希 釈剤の量は光硬化 ¾組成物の総量に対して固形分で 1 0質量。/。以上 （特に 2 0質 量％以上、 特に 2 5質量％以上；上限は 4 0質量％が好ましい） 含むことが好ま しい。 また反応性ポリマーと可塑ィヒ反応性希釈剤との質量比が、 6 0 ： 1 0〜 5 0が一般的で、 6 0： 2 0〜5 0、特に 6 0： 2 0〜4 5であることが好ましい。 次に、前記光硬化性転写シート⑥を構成する光硬化性組成物について説明する。 上記光硬化性組成物は、一般に、上記光重合性官能基を有する反応性ポリマー（一 般にガラス転移温度が 2 0 °C以下のもの） 、 置換基を有するフエノール化合物、 さらに光重合性官能基 （好ましくは （メタ） ァクリロイル基） を有する反応性希 釈剤 （モノマー及びオリゴマー） 、 アクリル樹脂、 光重合性開始剤及び、 所望に より他の添加剤から構成される。
光重合性官能基を有する反応性ポリマーとしては、 前記光硬化性転写シート② 及び③で示したものを使用することができる。
本発明の置換基を有するフエノールイ匕合物は、 一般に重合防止剤又は酸化防止 剤として使用されているものである。 この置換基を有するフエノール化合物とし ては、 ハイドロキノン系化合物又はヒンダードフエノール系化合物が好ましく、 特に本発明の反応性ポリマーを含む特定の光硬化性組成物の系では有効である。 上記特定のフエノール化合物を光硬化个生,組成物の総量に対して 0 . 0 1〜 0 . 3 質量0 /0、 さらに 0 . 0 1〜0 . 2質量0 /0、 特に 0 . 0 1〜0 . 1質量。/。含むこと が好ましい。 このような少量で、 反射層の黄変を防止し、 反射層を保護する機能 が向上する。
ハイ ドロキノン系化合物の好ましいィ列としては、 4ーメ トキシフエノールを挙 げることができ、 またヒンダードフエノール系化合物の好ましい例としては、 下 記の化合物：
(AO-20) (AO-70) CH2CH2COCH2CH2OCH2十 2 O
Figure imgf000037_0001
(AO-30)
Figure imgf000037_0002
(AO-40)
Figure imgf000037_0003
(AO-50)
t- Bu
H0- O)— CH2-CH2— CO- CisHs?
t- Bu (AO-80)
Figure imgf000038_0001
(AO-330)
Figure imgf000038_0002
(AO-60)
Figure imgf000038_0003
を挙げることができる。 これらは上記のように、 旭電化工業 （株） 製の商品名 ： アデカスタブ AO— 20、 AO— 30、 0— 40、 AO— 50、 AO— 60、 AO— 70、 AO— 80、 AO— 330と して市販されている。 特にフエノール 環を 3個以上有するものが好ましい。
次に、前記光硬化性転写シート⑦を構成する光硬化性組成物について説明する。 上記光硬化性組成物は、 一般に、 反応性希釈剤 （モノマー及びオリゴマー） を少 なくとも含み、好ましくはさらに上記光重合性官能基を有する反応性ポリマー（一 般にガラス転移温度が 2 0 °C以下のもの） 、 光重合開始剤、 アクリル樹脂、 及び 所望により他の添加剤等を含んでいる。
光重合性官能基を有する反応性ポリマーとしては、 前記光硬化性転写シート② 及ぴ③で示したものを使用することができる。 '
上記光硬化性組成物が、 反応性希釈剤を含むことが好ましい。 この反応性希釈 剤としては、 （メタ） ァクリロイル基を 2個有する分岐アルカン又は （メタ） ァ クリロイル基を二個有する環状アルカン、 或いは （メタ） ァクリロイル基を一個 有する長鎖 （一般に炭素原子数 1 0個以上） のアルカン又は （メタ） アタリロイ ル基を 1個有する環状アル力ンが好ましレ、。 上記分岐アル力ンの炭素原子数は 4 〜1 0個、 特に 4〜 8個が好ましい。 また環状アルカンの炭素原子数は 5〜1 5 個、 特に 5〜1 2個が好ましい。 このような希釈剤を使用することにより硬化層 表面の水接触角を容易に高くすることができる。
(メタ） アタリロイル基を二個有する分岐アルカンの例としては、 ネオペンチ ルグリコールジァクリレート (例えば、 共栄社 (株) 製、 ライトアタリレート N P - A) 、 ネオペンチルグリコー/レジメタクリレート、 2—ブチルー 2—ェチル —1 , 3 _プロパンジオールジァクリレート、 2—プチルー 2—ェチルー 1 , 3 —プロパンジオールジメタクリレート、 3—メチルー 1 , 5—ペンタンジオール アタリレート、 3—メチル一 1， 5—ペンタンジオールメタタリレートを挙げる ことができる。 （メタ）ァクリロイル基を二価有する環状アルカンの例としては、 ジメチロールトリシクロデカンジアタリレート （日本化薬 (株) 製、 KAY A R AD R - 6 8 4 ) 、 ジメチロー/レトリシクロデカンジメタクリレートを挙げる ことができる。 '
(メタ） アタリロイル基を一個有する炭素原子数 1 0以上のアルカンの例とし ては、 イソデシルモノアタリレート、 イソデシルモノメタクリレート、 n—ラウ リルモノアクリレート、 n—ラウリルモノメタタリレート、 トリデシルモノアク リレート、 トリデシルモノメタタリレート、 n—ステアリルモノアタリレート、 n—ステアリルモノメタクリレート、 1， 1 0デカンジオールモノアクリレート、 1 , 1 0デカンジオールモノメタクリレー卜、イソミリスチルモノアタリレート、 イソミリスチルモノメタクリレートを挙げることができる。 また （メタ） アタリ ロイル基を一個有する環状アルカンの例と しては、 イソポルニルモノアクリレー ト、 イソボル-ルモノメタタリレート、 ト リシクロデカンモノアタリレート、 ト リシクロデカンモノメタァクリレート、 を挙げることができる。
反応性希釈剤としては、 上記化合物のみ又 ίま上記化合物が主成分として用いられ るが、 上記の化合物以外に後述する希釈剤も適宜使用することができる。
次に、前記光硬化性転写シート⑧を構成する光硬化性組成物について説明する。 本発明の光硬化性転写シートは、 光重合性官能基を有する反応性ポリマーを含み リン酸 （メタ） アタリレートを 1 0〜 2 2 0 p p m含有する光硬化性組成物から なる光硬化性転写層 1 1を有するものである。
上記光硬化性組成物は、 一般に、 上記光重合性官能基を有する反応性ポリマー (一般にガラス転移温度が 2 0 °C以下のもの） 、 金属接着性向上剤としてのリン 酸 （メタ） アタリレート、 さらに光重合性官能基 （好ましくは （メタ） ァクリロ ィル基） を有する反応性希釈剤 （モノマー及ぴオリゴマー） 、 アクリル樹脂、 光 重合性開始剤、 酸化防止剤及び、 所望によ り他の添加剤から構成される。
光重合性官能基を有する反応性ポリマーとしては、 前記光硬化性転写シート② 及ぴ③で示したものを使用することができる。
リン酸（メタ）ァクリレート化合物としては、 リン酸エステル骨格を有する （メ タ） アタリレートであれば、 モノエステノレ、 ジエステルあるいはトリエステルで もよく、 例えば、 エチレンォキシド変性フエノキシ化リン酸 （メタ） アタリレー ト、 エチレンォキシド変性ブトキシ化リン酸 （メ'タ） アタリレート、 エチレンォ キシド変性ォクチルォキシィ匕リン酸 （メタ） アタリレート、 エチレンォキシド変 性リン酸ジ （メタ） アタリレート、 エチレンォキシド変性リン酸トリ （メタ） ァ タリレート等が挙げられる。 リン酸 （メタ） ァクリレートは 1種又は 2種以上を 任意の割合で混合使用することができる。
リン酸 （メタ） アタリレート及ぴノ又はその誘導体としては、 次の式： r 0 O 、ο
CH2-C— C~OCH2CH2 CCH2CH2CH2CH2CH2 0+P~ OH)b
(但し、 Rは、 H又は CH3であり、 nは、 0〜2. 0であり、 aは、 1. 0〜 3. 0であり、 bは、 0〜2. 0であり、 且つ aと bの和は 3. 0である） により表される化合物を好適に使用することができ、特に Rが CH3、 aが平均値 1. 5、 bが平均値 1. 5であり、 且つ nが 0である混合物が好ましい。
また、 その他のリン酸エステル骨格を有する （メタ） アタリレートを使用する ことができ、モノエステル、ジエステノレあるいはトリエステルでもよく、例えば、 エチレンォキシド変性フエノキシ化リン酸 （メタ） アタリレート、 エチレンォキ シド変性ブトキシ化リン酸 （メタ） アタリレート、 エチレンォキシド変性ォクチ ルォキシ化リン酸 （メタ） アタリレート、 エチレンォキシド変性リン酸ジ （メタ） アタリレート、 エチレンォキシド変'性リン酸トリ （メタ） アタリレート等が挙げ られる。 さらに、 これらのリン酸 （メタ） アタリレートは 1種又は 2種以上を混 合して使用することができる。
上記リン酸 （メタ） アタリレート及び Z又はその誘導体の含有量が、 樹脂組成 物全体に対して、 10 p pmより少ない場合には、 銀合金等との接着が不十分と なり、 360 p p m以上であれば、 而腐食性は著しく低下する。 リン酸メタクリ レートの含有量が 10〜220 p p mの範囲にあれば、 湿熱澴境下での反射率の 低下がほぼ見られず、 なおかつ銀合金等との接着性は十分であり、 特に 10〜 1 00 p pmの範囲ではこの性質が好適にパランスする。
本発明の光硬化性組成物は、 前記光硬化性転写シート①〜⑧の組成で示したよ うに、 更に光重合性官能基を有する反応性希釈剤を含むことが好ましレ、。 反応性 希釈剤としては、 例えば、 2—ヒドロキシェチル （メタ） ァクリレート、 2—ヒ ドロキシプロピル （メタ） ァクリレー ト、 4—ヒ ドロキシブチル （メタ） ァクリ レート、 2—ェチルへキシルポリエトキシ （メタ） アタリレート、 ベンジル （メ タ) アタリレート、 イソボル-ル （メタ） アタリレート、 フエニルォキシェチル (メタ） アタリレート、 トリシクロデカンモノ （メタ） アタリレート、 ジシクロ ペンテニルォキシェチル （メタ） アタ リレート、 テトラヒ ドロフルフリル （メタ） アタリレート、 ァクリロイルモルホリン、 N—ビュル力プロラクタム、 2—ヒ ド 口キシ一 3—フエニルォキシプロピノレ （メタ） アタリレート、 o—フエユルフェ ニルォキシェチル （メタ） アタリレー ト、 ネオペンチルグリコールジ （メタ） ァ クリレート、 ネオペンチルグリコー/レジプロポキシジ （メタ） アタリレート、 ヒ ドロキシビバリン酸ネオペンチルグリ コールジ （メタ） アタリレート、 トリシク 口デカンジメチロールジ（メタ） アタ リレート、 1 , 6—へキサンジオー^^ジ（メ タ） アタリレート、 ノナンジオールジ （メタ） ァクリレート、 トリメチロールプ 口パントリ （メタ） アタリレート、 ペンタエリスリ トーノレトリ （メタ） アタリレ ート、 ペンタエリスリ トールテトラ （メタ） アタリレート、 トリス 〔 （メタ） ァ クリロキシェチル〕 イソシァヌレート、 ジトリメチロールプロパンテトラ （メタ） アタリレート等の （メタ） アタリレー トモノマー類、 ポリオール化合物（例えば、 エチレングリコーノレ、 プロピレングリ コーノレ、 ネオペンチノレグリコー/レ、 1 , 6 —へキサンジォーノレ、 3—メチレ一 1 , 5—ペンタンジオール、 1 , 9ーノナン ジオール、 2—ェチル一 2—プチノレ一 1 , 3—プロパンジォーノレ、 トリメチロー ルプロパン、 ジエチレングリコーノレ、 ジプロピレングリコーノレ、 ポリプロピレン グリコール、 1， 4—ジメチロールシクロへキサン、 ビスフエノール Aポリエト キシジオール、 ポリテトラメチレングリコール等のポリオール類、 前記ポリオ一 ル類とコハク酸、 マレイン酸、 ィタコン酸、 アジ'ピン酸、 水添ダイマー酸、 フタ ル酸、 イソフタル酸、 テレフタル酸等の多塩基酸又はこれらの酸無水物類との反 応物であるポリエステルポリオール類、 前記ポリオール類と ε—力プロラタ トン との反応物であるポリ力プロラクトンポリオール類、 前記ポリオール類と前記、 多塩基酸又はこれらの酸無水物類の ε—力プロラク トンとの反応物、 ポリカーボ ネートポリオール、ポリマーポリオール等） と有機ポリイソシァネート （例えば、 トリ レンジイソシァネート、 イソホロンジイソシァネート、 キシリ レンジイソシ ァネートゝ ジフェニ^/メタン一 4 , 4 '— イソシァネート、 ジシクロペンタニノレ ジイソシァネート、 へキサメチレンジイソシァネート、 2 , 4 , 4 'ートリメチノレ へキサメチレンジィソシァネート、 2， 2 4—トリメチルへキサメチレンジィ ソシァネート等） と水酸基含有 （メタ） アタリレート （例えば、 2—ヒ ドロキシ ェチル （メタ） アタリレート、 2—ヒドロキシプロピル (メタ） ァクリレート、 4—ヒ ドロキシブチル （メタ） アタリレー ト、 2—ヒ ドロキシ一 3—フエニルォ キシプロピル （メタ） アタリレート、 シクロへキサン一 1， 4—ジメチロールモ ノ （メタ） アタリレート、 ペンタエリスリ トーノレトリ （メタ） アタリレート、 グ リセリンジ （メタ） アタリレート等） の反応物であるポリウレタン （メタ） ァク リレート、 ビスフエノール Α型エポキシ樹脂、 ビスフエノール F型エポキシ樹脂 等のビスフエノール型エポキシ榭脂と （メ タ） アクリル酸の反応物であるビスフ 工ノール型エポキシ (メタ） アタリレート等の （メタ） アタリレートオリゴマー 類等を挙げることができる。 これら光重合可能な官能基を有する化合物は 1種又 は 2種以上、 混合して使用することができる。
光重合開始剤としては、 公知のどのよう な光重合開始剤でも使用することがで きるが、 配合後の貯蔵安定性の良いもの 望ましい。 このような光重合開始剤と しては、 例えば、 ァセトフエノン系、 ベ ジルジメチルケタールなどのベンゾィ ン系、 ベンゾフエノン系、 イソプロピルチォキサントン、 2— 4—ジェチルチオ キサントンなどのチォキサントン系、 その他特殊なものとしては、 メチルフエ二 ルグリオキシレートなどが使用できる。 待に好ましくは、 2—ヒ ドロキシー 2— メチル— 1一フエニルプロパン— 1一オン、 1— 'ヒ ドロキシシク口へキシルフェ 二ルケトン、 2—メチル—1一 （4一 （ チルチオ） フエニル） 一 2—モルホリ ノプロパン一 1、 ベンゾフエノン等が挙げられる。 これら光重合開始剤は、 必要 に応じて、 4ージメチルァミノ安息香酸のごとき安息香酸系又は、 第 3級ァミン 系などの公知慣用の光重合促進剤の 1種または 2種以上を任意の割合で混合して 使用することができる。 また、 光重合開始剤のみの 1種または 2種以上の混合で 使用することができる。 光硬化性組成物中に、 光重合開始剤を一般に 0 . 1〜2 0質量％、 特に 1〜 1 0質量％含むことが好ましい。
光重合開始剤のうち、 ァセトフエノン系重合開始剤としては、 例えば、 4—フ エノキシジクロロァセトフエノン、 4— t—プチノレージクロロァセトフエノン、 4 - t—ブチルートリクロロァセトフエノン、 ジェトキシァセトフエノン、 2― ヒ ドロキシ一 2—メチル一 1一フエ二/レプロパン一 1—オン、 1一 ( 4—ィソプ 口ピノレフェニル） 一 2—ヒ ドロキシ一 2—メチノレプロパン一 1 一オン、 1 一 （4 —ドデシルフェニル） 一 2—ヒ ドロキシ一 2—メチルプロパン一 1一オン、 4— ( 2—ヒ ドロキシェトキシ) —フエニル ( 2—ヒ ドロキシ一 2—プロピル) ケト ン、 1—ヒ ドロキシシクロへキシルフェニルケトン、 2—メチル一 1— ( 4— (メ チルチオ) フエニル） —2—モルホリノプロパン一 1など、 ベンゾフエノン系重 合開始剤としては、 ベンゾフヱノン、 ベンゾィル安息香酸、 ベンゾィル安息香酸 メチノレ、 4—フエ二ノレべンゾフエノン、 ヒ ドロキシベンゾフエノン、 4—ベンツ ゾィルー 4， ーメチルジフヱニルサルフアイ ド、 3 , 3， —ジメチルー 4ーメ ト キシベンゾフエノンなどが使用できる。
ァセトフエノン系重合開始剤として fま、 特に、 2—ヒ ドロキシー 2—メチル一 1一フエ二ノレプロノヽ。ン一 1—オン、 1—ヒ ドロキシシクロへキシノレフエニノレケト ン、 2—メチル一 1— ( 4 - (メチルチオ) フエニル） 一 2—モルホリノプロパ ン一 1が好ましい。 ベンゾフエノン系重合開始剤としては、 ベンゾフエノン、 ベ ンゾィル安息香酸、 ベンゾィル安息香酸メチルが好まじい。 また、 第 3級ァミン 系の光重合促進剤としては、 トリェタノールァミン、メチルジェタノールァミン、 トリイソプロパノールァミン、 4 , 4， ージメチ^/アミノベンゾフエノン、 4 , 4， ージェチルァミノべンゾフエノン、 2—ジメチルァミノ安息香酸ェチル、 4 —ジメチルァミノ安息香酸ェチル、 4ージメチルァミノ安息香酸（ n—ブトキシ） ェチル、 4一ジメチルァミノ安息香酸ィソァミル、 4ージメチルァミノ安息香酸 2—ェチルへキシルなどが使用できる。特に好ましくは、光重合促進剤としては、 4—ジメチルァミノ安息香酸ェチル、 4ージメチルァミノ安息香酸 （n—ブトキ シ） ェチル、 4ージメチルァミノ安息香酸ィ ソァミル、 4ージメチルァミノ安息 香酸 2—ェチルへキシルなどが挙げられる。 ' 本発明の光硬化性転写層はガラス転移温度が 2 0 °C以下で、 透過率 7 0 %以上 を満たすように光硬化性組成物を設計するこ とが好ましい。 このため、 上記光重 合可能な官能基を有する化合物及び光重合開 台剤に加えて、 所望により下記の熱 可塑性樹脂及び他の添加剤を添加することが好ましい。
上記反応性ポリマー：光重合可能な官能基を有する化合物：光重合開始剤の質 量比は、 一般に、 4 0〜： 1 0 0 : 0〜6 0 ： 0 . 1〜； 1 0、 特に 6 0〜： L 0 0 ： 0〜4 0 ： 1〜1 0から好ましレヽ。
他の添加剤として、 シランカップリング剤 （接着促進剤） を添加することがで きる。 このシランカップリング剤としてはビュルトリエトキシシラン、 ビュルト リス (β—メ トキシェトキシ) シラン、 γ—メ タクリロキシプロビルトリメ トキシ シラン、 ビニルトリァセトキシシラン、 γ—ダリシドキシプロピルトリメ トキシシ ラン、 γ—グリシドキシプロピルトリエトキシシラン、 β— ( 3， 4—エポキシシ クロへキシル） ェチルトリメ トキシシラン、 γ—クロ口プロピルメ トキシシラン、 ビニルトリクロロシラン、 γ—メルカプトプロビルトリメ トキシシラン、 γ—アミ ノプロピルトリエトキシシラン、 Ν— β (アミノエチル） 一γ—ァミノプロビルト リメ トキシシランなどがあり、 これらの 1種を単独で又は 2種以上を混合して用 いることができる。 これらシランカップリ グ剤の添加量は、 上記反応性ポリマ 一 1 0 0質量部に対し通常 0 . 0 1〜 5質量部で十分である。
また同様に接着性を向上させる目的でェポキシ基含有化合物を添加することが できる。 エポキシ基含有化合物としては、 ト リグ 'リシジゾレト リ ス （ 2—ヒドロキ シェチノレ） ィソシァヌレート ；ネオペンチノレグリコーノレジグリシジノレエーテノレ ； 1， 6一へキサンジオールジグリシジルエーテノレ；ァクリノレグリシジノレエーテル； 2—ェチルへキシルグリシジルエーテル； ブェニノレグリシジノレエーテノレ ； フエノ —ルグリシジルエーテル； p— t—ブチルフエ二ルグリシジルエーテル； アジピ ン酸ジグリシジルエステル； o—フタ/レ酸ジグリシジルエステル；グリシジルメ タクリレー卜 ；プチルグリシジルエーテル等が挙げられる。 また、 エポキシ基を 含有した分子量が数百から数千のォリゴマーや重量平均分子量が数千から数十万 のポリマーを添加することによつても同様の効果が得られる。 これらエポキシ基 含有化合物の添加量は上記反応性ポリマー 1 0 0質量部に対し 0 . 1〜 2 0質量 部で十分で、 上記エポキシ基含有化合物の少なくとも 1種を単独で又は混合して 添加することができる。
さらに他の添加剤として、 加工性や貝占り合わせ等の加工性向上の目的で炭化水 素樹脂を添加することができる。 この場合、 添加される炭化水素樹脂は天然樹脂 系、合成樹脂系のいずれでも差支えなレ、。天然樹脂系ではロジン、 ロジン誘導体、 テルペン系樹脂が好適に用いられる。 ロジンではガム系樹脂、 トール油系樹脂、 ゥッド系樹脂を用いることができる。 ロジン誘導体としてはロジンをそれぞれ水 素化、 不均一化、 重合、 エステル化、 金属塩化したものを用いることができる。 テルペン系樹脂では α—ビネン、 β—ピネンなどのテルペン系樹脂のほ力、 テルぺ ンフエノール樹脂を用いることができる。 また、 その他の天然樹脂としてダンマ ル、 コーバル、 シ土ラックを用いても差支えない。 一方、 合成樹脂系では石油系 樹脂、 フエノール系樹脂、 キシレン系樹脂が好適に用いられる。 石油系樹脂では 脂肪族系石油樹脂、 芳香族系石油樹脂、 脂環族系石油樹脂、 共重合系石油樹脂、 水素化石油樹脂、 純モノマー系石油樹月旨、 クマロンインデン樹脂を用いることが できる。 フエノール系樹脂ではアルキノレフェノール樹脂、 変性フエノール樹脂を 用いることができる。 キシレン系樹脂ではキシレン樹脂、 変性キシレン樹脂を用 いることができる。
ァクリル樹脂も添加することができる。 例えば、 アルキルァクリレート （例、 メチルァクリレート、 ェチルァクリレート、 プチルァクリレート） 及び 又はァ ルキルメタクリレート (例、 メチルメタクリレート、 ェチルメタクリレート、 ブ チルメタクリ レート） 力 ら得られる単独重合体又は共重合体を挙げることができ る。 またこれらのモノマーと、 他の共重合可能なモノマーとの共重合体も挙げる ことができる。 特に、 光硬化時の反応性や硬化後の耐久性、 透明性の点からポリ メチルメタクリレート ( P MMA) が好ましい。
上記炭化水素樹脂等のポリマーの添加量は適宜選択されるが、 上記反応性ポリ マー 1 0 0質量部に対して 1〜2 0質量部が好ましく、 より好ましくは 5〜1 5 質量部である。
以上の添加剤の他、 本発明の光硬化性,組成物は紫外線吸収剤、 老化防止剤、 染 料、 加工助剤等を少量含んで :いてもよい。 また、 場合によってはシリカゲル、 炭 酸カルシウム、 シリコン共重合体の微粒子等の添加剤を少量含んでもよい。
本発明の光硬化性組成物からなる光硬化性転写シートは、 反応性ポリマー、 光 重合可能な官能基を有する化合物 （モノマー及びオリゴマー） 、 活性水素と反応 性の官能基を少なくとも 2個有する化合物及ぴ、 所望により他の添加剤とを均一 に混合し、 押出機、 ロール等で混練した後、 カレンダー、 ロール、 Tダイ押出、 インフレーション等の製膜法により所定の形状に製膜して用いることができる。 支持体を用いる場合は、 支持体上に製膜する必要がある。 より好ましい本発明の 光硬化性接着剤の製膜方法は、 各構成成分を良溶媒に均一に混合溶解し、 この溶 液をシリコーンやフッ素樹脂を精密にコートしたセパレーターにフローコート法、 ロールコート法、 グラビアロール法、 マイヤバー法、 リップダイコート法等によ り支持体上に塗工し、 溶媒を乾燥することにより製膜する方法である。
また、 光硬化性転写シートの厚さは1〜1 2 0 0 /^ 111、 特に 5〜5 0 0 μ πιと することが好ましい。 特に 5〜3 0 0 m (好ましくは 1 5 0 / m以下） が好ま しい。 1 μ πιより薄いと封止性が劣り、 透明樹脂基板の凸凹を埋め切れない場合 が生じる。 一方、 1 0 0 0 μ πιより厚いと記録媒体の厚みが増し、 記録媒体の収 納、 アッセンブリー等に問題が生じるおそれがあ ·り、 更に光線透過に影響を与え るおそれもある。
上記光硬化性転写シートの両側には剥離シートが貼り付けられていることが好 ましい。 剥離シートの材料としては、 ガラス転移温度が 5 0 °C以上の透明の有機樹脂が 好ましく、 このような材料としては、 ポリエチレンテレフタレート、 ボリシクロ へキシレンテレフタレート、ポリエチレンナフタレート等のポリエステル系樹脂、 ナイロン 4 6、 変性ナイロン 6 T、 ナイロン MX D 6、 ポリフタルアミ ド等のポ リアミ ド系樹脂、 ポリフエ二レンスノレブイ ド、 ポリチォエーテルサルフォン等の ケトン系樹脂、 ポリサルフォン、 ポリエーテルサルフォン等のサルフォン系樹脂 の他に、 ポリエーテル二トリル、 ポリアリ. レート、 ポリエーテルイミ ド、 ポリア ミ ドィミ ド、 ポリカーボネート、 ポリメチノレメタクリレート、 トリァセチルセル ロース、 ポリスチレン、 ポリビュルクロライ ド等の有機樹脂を主成分とする透明 樹脂基板を用いることができる。 これら中で、 ポリカーボネート、 ポリメチルメ タアタリレート、 ポリビニノレクロライド、 ポリスチレン、 ポリエチレンテレフタ レートが好適に用いることができる。 厚さは 1 0〜2 0 0 μ πιが好ましく、 特に 3 0〜1 0 0 μ πιが好ましい。
表面に凹凸を有する基板 2 1の材料としてはとしては、 ガラス転移温度が 5 0 °C以上の透明の有機樹脂が好ましく、 このような支持体としては、 ポリエチレ ンテレフタレート、 ポリシクロへキシレンテレフタレート、 ポリエチレンナフタ レート等のポリエステル系樹脂、 ナイロン 4 6、 変性ナイロン 6 T、 ナイロン Μ X D 6、 ポリフタルアミ ド等のポリアミ ド系樹脂、 ポリフエ二レンスルフイ ド、. ポリチォエーテルサルフォン等のケトン系樹脂、 ポリサルフォン、 ポリエーテル サルフォン等のサルフォン系樹脂の他に、 ポリエーテル二トリノレ、 ポリアリレー ト、 ポリエーテルイミ ド、 ポリアミ ドイミ ド、 ポリカーボネート、 ポリメチルメ タクリレート、 トリァセチルセルロース、 ポリスチレン、 ポリビュルクロライ ド 等の有機樹脂を主成分とする透明樹脂基板を用いることができる。 これら中で、 ポリカーボネート、 ポリメチルメタァクリ レート ポリビニルクロライド、 ポリ スチレン、 ポリエチレンテレフタレートが転写性、 複屈折の点で優れており、 好 適に用いることができる。 厚さは 2 0 0〜 2 0 0 0 / mが好ましく、 特に 5 0 0 〜 1 5 0 0 mが好ましレヽ。 有機ポリマーフィルムの材料 26と しては、 ガラス転移温度が 50°C以上の透 明の有機樹脂が好ましく、 このような支持体としては、 ポリエチレンテレフタレ ート、 ポリシク口へキシレンテレフタレ一ト、 ポリエチレンナフタレート等のポ リエステル系樹脂、 ナイロン 46、 変†生ナイロン 6T、 ナイロン MXD 6、 ポリ フタルアミ ド等のポリアミ ド系樹脂、 ポリフエ二レンスルフイ ド、 ポリチォエー テルサルフォン等のケトン系樹脂、 ポリサルブオン、 ポリエーテルサルフォン等 のサルフォン系樹脂の他に、 ポリエーテル二トリル、 ポリアリレート、 ポリエー テルイミ ド、ポリアミ ドィミ ド、ポリカーボネート、ポリメチルメタクリレート、 トリァセチルセルロース、 ポリスチレン、 ポリビュルクロライ ド等の有機樹脂を 主成分とする透明樹脂基板を用いることができる。 これら中で、 ポリカーボネー ト、 ポリメチルメタアタリレート、 ポリビニルクロライ ド、 ポリスチレン、 ポリ エチレンテレフタレートが転写性、 複屈折の点で優れており、 好適に用いること ができる。 厚さは 10〜200 zm力 S好ましく、 特に 50〜100 ;umが好まし レ、。
こうして得られる本発明に光硬ィ匕性転写シートは、 ガラス転移温度が 20°C以 下である反応性ポリマーを含む光硬ィ匕十生糸且成物からなるものであるが、 さらに光 硬化性転写層の 380〜420 nmの波長領域の光透過率が 70 %以上であるこ とが好ましい。 即ち、 ガラス転移温度が 20°C以下とすることにより、 光硬化性 転写層がスタンパの凹凸面に圧着されたとき、 その凹凸面に緊密に追随できる可 撓性を有することができる。 特に、 ガラス転移温度が 1 5°C〜一 50 の範囲に することにより追随性が優れている。 ガラス転移温度が高すぎると、 貼り付け時 に高圧力及び高温が必要となり作業性の低下につながり、 また低すぎると、 硬化 後の十分な高度が得られなくなる。
光硬化性転写シートは 380〜420 nm (好ましくは 380〜 800 n m) の波長領域の光透過率が 70%以上であり、 これはレーザによる読み取り信号の 強度低下を防止するためである。 さらに 380〜 420 nmの波長領域の光透過 率が 80%以上であることが好ましレ、。 光硬化性組成物中の反応性ポリマーには重合性官能基を 1〜 5 0モル％有する ことが好ましい。 これにより、 得られる光硬化性転写シートが、 硬化後に形状保 持可能な強度得ることができる。光重合開 剤は前記のように 0 . 1〜 1 0質量％ の範囲が好ましく、 これより少ないと硬化速度が遅すぎて、 作業性が悪く、 多す ぎると転写精度が低下する。
本発明に光硬化性転写シートは、 膜厚精度を精密に制御したフィルム状で提供 することができるため、 基板及ぴスタンパとの貼り合わせを容易にかつ精度良く おこなうことが可能である。 ¾た、 この貼り合わせは、 圧着ロールや簡易プレス などの簡便な方法で 2 0〜1 0 0 °Cで仮圧着した後、 光により常温、 1〜数十秒 で硬化できる上、 本接着剤特有の自着力によりその積層体にズレゃ剥離が起き難 いため、 光硬化まで自由にハンドリングができるという特徴を有している。 本発明の光硬化性転写シートを硬化する場合は、 光源として紫外〜可視領域に 発光する多くのものが採用でき、 例えば超高圧、 高圧、 低圧水銀灯、 ケミカルラ ンプ、 キセノンランプ、 /、ロゲンランプ、 マーキュリー/、ロゲンランプ、 カーボ ンアーク灯、 白熱灯、 レーザ光等が拳げられる。 照射時間は、 ランプの種類、 光 源の強さによって一概には決められないが、 数秒〜数分程度である。
また、 硬化促進のために、 予め積層体を 3 0〜8 0 °Cに加温し、 これに紫外線 を照射してもよい。
得られた本発明の基板の凹凸表面の反射層は、 基板に反射層を金属蒸着 （例え ばスパッタリング、 真空蒸着、 イオンプレーティング等) することにより形成す る。 金属としては、 ァノレミニゥム、 金、 銀、 これらの合金等を挙げることができ る。硬化シート上の半透明反射層は、金属と して銀等を用いて形成される。即ち、 上記反射層より低い反射率の反射層にする必要があり、 成分、 膜厚等が変更され る。 .
硬化シートの反射層上に有機ポリマーフィルムを貼り付ける場合、 一方に接着 剤を塗布し、 その上に他方を重ね、 硬化させる。 接着剤が UV硬化性榭脂の場合 は UV照射により、 ホットメルト接着剤の場合は、 加熱下に塗布し、 冷却するこ とにより得られる。
本発明の光情報記録媒体の製造は、通常、上記のように円盤状で処理されるが、 シート状で連続的に作成し、 最後に円盤状にしてもよレ、。 以下に実施例を示し、 本発明ついてさらに詳述する。
[実施例 1 ]
<光硬化' I·生転写シートの作製 >
(反応性ポリマーの作製）
配合 I
2ーェチルへキシルメタクリレート 7 0質量部 メチルメタクリ レート 2 0質量部
2—ヒドロキシェチノレメタタリレー ト ]
ベンゾフエノン
小ルェン 3 0質量部 酢酸ェチル 3 0質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 6 0 °Cに加熱して重合を開始 させ、 この温度で 1 0時間撹拌し、 側鎖にヒドロキシル基を有するアクリル樹脂 を得た。 その後、 力レンズ MO I ( 2一^ ソシアナトェチルメタタリレート .； 昭和電工 （株） 製） 5質量部を添加し、 窒素雰囲気下で穏やかに撹拌しながら 5 0 で反応させ、 光重合性官能基を有する反応性ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 T gが 0 °Cであり、 側鎖にメタクリロイル基を 5 モル％及びヒ ドロキシル基を 5モル％有していた。 '
配合 II
反応性ポリマー溶液 1 · 1 0 0質量部 へキサンジオールジァクリレート 3 0質量部 ジイソシァネート （BXX5627、 東洋インキ製造 （株） 製） 0 . 5質 I ィルガキュア 1 8 4 (チバガイギー （株） 製） • 上記配合の混合物を均一に溶解、 混練し、 剥離シート （幅 140mm、 長さ 3 00m、 厚さ 75 μπι；商品名 No. 23、 藤森工業 （株） 製） 上に、 全面塗布 し、 乾燥厚さ 20 ± 2 / mの光硬化性転写シートを形成し、 シートの反対側に上 記と同一の剥離シートを貼付し、 ロール状に卷き上げ、 光硬化性転写シートのフ ルエッジタイプのロール （直径 26 Omm) を得た。
[実施例 2]
実施例 1において、 配合 IIのジィソシァネートを 1. 0質量部用いた以外は、 同様にして光硬化性転写シートのロールを得た。
[実施例 3 ]
実施例 1において、 配合 IIのジィソシァネートを 0. 1質量部用いた以外は、 同様にして光硬化性転写シートのロールを得た。
[実施例 4 ]
実施例 1において、 配合 IIのジィソシァネートを 3. 0質量部用いた以外は、 同様にして光硬化性転写シートのロールを得た。
[比較例 1 ]
実施例 1において、 配合 IIのジイソシァネートを用いなかった以外は、 同様に して光硬化性転写シートのロールを得た。
(1) 光硬化性転写シートの評価 . (1— 1) 転写シートのクリープ試験
上記実施例 1〜 4及ぴ比較例 1で得られこ口ールを 25 °Cで 24時間放置した 後、 転写シートの転写層のクリープ試験を、 動的粘弾性測定装置としてレオスト レス R.S 300 (HAAKE社製） を用いて行った。 その際、 φ = 2 Ommのパ ラレルプレートを用いて、 測定厚さ lmm (転写層を積層し成形した） 、 測定温 度 25 °Cにて、 応力 50P a、 120秒閬の条件で行つた。
上記試験結果から、 測定された時間 [t] (秒） に対する歪み [γ] (%) の プロットしたグラフを第 7図に示す。 これに基づき 1 0 g γと 1 0 g tの関係を 示すグラフを第 8図に示す。 第 8図より、 各例の直線近似の式： l o g y = a + b · 1 o g tの a、 bを求めた。
(1 -2) しみ出し
実施例 1〜 4又は比較例 1で得られた口ールを、 常温で 24時間放置した後、 口ール側面の転写層のしみ出しを観察した。 下記のよう評価した。
〇： しみ出しが見られない。
Δ： しみ出しが若干見られる。
X ： しみ出しが相当見られる。
(1— 3) 転写シートの表面硬度 .
ガラス板上に、実施例 1〜4又は比較 ll 1の転写層（厚さ 25 μ m)を転写し、 サンプルを得た。サンプルの転写層の表面を、 Helmut Fischer社から市販されて いる超微小硬度計 （フイツヤースコープ H 1 00) を用いて、 荷重 4. 0mN、 HU (ユニバーサル硬さ；表面硬度） を測定した。ュニバーサノレ硬さについては、 例えば、 材料試験技術、 第 43卷、 No. 2、 148頁 （1998年 4月） に記 載されている。
(1-4) 厚み精度
得られた光硬化性転写シートの厚さを l m2当たり 10力所測定し、厚さのばら つきの程度を測定した。 ばらつきが 5%以内の場合を〇、 5%を超える場合を X とした。
(2) 得られる光情報記録媒体の評価
光硬化性転写シートのロールを円盤状に打ち抜いた後、 一方の剥離シートを除 去し、 得られた円盤状光硬化性転写シー卜を、 射出成形により成形したピットと しての凹凸面を有するポリカーボネート基板 （厚さ 1.' lmm) の凹凸面に設け られた銀合金の半透過反射層上に、 転写シート面と反射層が接触するように配置 し、 シリコーンゴム製のローラを用いて 2 k gの荷重で光硬化性転写シートを押 圧し、 積層体を形成した （第 2図の （3) に対応） 。
積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接觖するように配置して、 シリコーンゴム製 のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体を形成し、 スタンパ の凹凸形状を転写シート表面に転写しこ。
次に、 光硬化性転写シート側から、 メタルハライドランプを用いて、 積算光量 1 000mj/c m2の条件で U V照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬化した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 アルミニウム反射層 （70 nm) を 形成した。 この上に接着剤を介してポリカーボネートフィルム （厚さ 70 μπι ; 商品名ピュアエース C 1 1 0— 70、 帝人 （株） 製）'を貼り付けた。
これにより 2層の凹凸面を有する光' f青報記録媒体を得た。
(2) 光情報記録媒体の評価
(2- 1) 光線透過率 （380〜42 0 n mの波長領域）
—方の光硬化性転写シートを、 J I S -K 6 7 1 7に従レヽ 3 8 0〜420 nm の波長領域の光線透過率を測定した。 Ί 0%以上を〇、 70%未満を Xとした。
(2-2) 転写性 （信号読み取り）
得られた光情報記録媒体の再生波形を、 波長 40 5 nmのレーザを用いて測定 し、 得られた再生波形と製造に用いたスタンパの波形と比較した。 スタンパの波 形と一致しているものを〇、 ほとんど一致しているもの△、 ほとんど一致してい ないものを Xとした。
得られた試験結果を表 1に示す。
表 1
Figure imgf000055_0001
実施例 1 〜 4で得られた光硬化性転写シー卜の口ールはしみ出しがほとんど無 く、 且つこれを用いて得られる光情報記録媒 {本のピット形状はほぼ良好なもので あり、 作業性、 転写性共に優れていた。 特に、 実施例 1及び 2はこれらの特性が —層優れていた。 一方、 比較例 1のジイソシァネートを含まない転写層から得ら れた光情報記録媒体は、 ピット形状は良好なちのであるが、 ロールにしみ出しが あり、 その製造のための作業性は劣っていた。 従って、 本発明の光硬化性転写シ ートは、 得られる光情報記録媒体の特性を劣ィ匕させることなく、 その製造のため の作業性を向上させたものであると言うことができる。
[実施例 5 ]
く光硬化性転写シートの作製 >
(反応性ポリマーの作製）
配合 I
2ーェチノレへキシルメタクリレート 7 0質量部 メチルメタクリレート 2 0質量部
2—ヒ ドロキシェチルメタクリレート 1 0質量部 ベンゾフエノン
30質量部 酢酸ェチル 30質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 60°Cに加熱して重合を'開始 させ、 この温度で 10時間撹拌し、 側鎖にヒ ドロキシル基を有するァクリル樹脂 を得た。 その後、 力レンズ MO I ( 2—ィソシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添加し、 窒素雰囲気下で穏やかに撹拌しながら 5 0°Cで反応させ、 光重合性官能基を有する反^性ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 T gが 0°Cであり、 側鎖にメタタリロイル基を 5 モル0 /0有していた。
配合 II
反応性ポリマー溶液 1 100質量部 トリシクロデカンジアタリレート 30質量部 粘着性付与剤 （SP値 =8.52、 mp =115°C, 10霄量部
Tg=59°C、 平均分子量 =650、
クリアロン Ml 15、 ヤスハラケミカル （株） 製）
1ーヒ ドロキシシクロへキシルフェニルケトン 1質量部 上記配合の混合物を均一に溶解、 混練し、 剥離シート （幅 140mm、 長さ 2 00m、 厚さ 75 μηι；商品名 No. 23、 藤森工業 （株） 製） 上に、 全面塗布 し、 乾燥厚さ 20 ± 2 μ mの光硬化性転写シートを形成し、 シートの反対側に上 記と同一の剥離シートを貼付し、 ロール状に卷き上げ、 光硬化性転写シートのフ ルエッジタイプのロール （直径 0. 2 5m) を得た。 '
[比較例 2]
実施例 5において、配合 IIの粘着性付与剤を用いなかった以外は、 同様にして 光硬化性転写シートのロールを得た。
[比較例 3] ■
実施例 5において、配合 IIの粘着性付与剤として、 YSレジン PX1 150 (S P値 =8.26、 mp =115°C,T g =62°C、平均分子量 =1100；ヤスハラケミカル（株） 製） を同量用いた以外は、 同様にして光碩化性転写シートのロールを得た。
(1) 光硬化性転写シートの評価
(1- 1) しみ出し
実施例 1、 比較例 1及び 2で得られた口ールを、 常温で 24時間放置した後、 口ール側面の転写層のしみ出しを観察した。 下記のよう評価した。
〇： しみ出しが見られない。
△： しみ出しが若干見られる。
X ： しみ出しが相当見られる。
(1-2) 厚み精度
得られた光硬化性転写シートの厚さを lm2当たり 10力所測定し、厚さのばら つきの程度を測定した。 ばらつきが 1%以内の場合を〇、 1%を超える場合を X とした。
(1-3) 転写シートのタリープ試験
上記実施例 5及ぴ比較例 2で得られた口ールを 25 °Cで 24時間放置した後、 転写シートの転写層のクリープ試験を、 動白勺粘弹 I"生測定装置としてレオス トレス RS 300 (HAAKE社製） を用いて行った。 その際、 φ = 2 Ommのパラレ ルプレートを用いて、 測定厚さ lmm (転写層を積層し成形した） 、 測定温度 2 5°Cにて、 応力 50 P a、 120秒間の条件で行った。
上記試験結果から、 測定された時間 [t] (秒） に対する歪み [γ] (%) の プロットし、 これに基づき 1 o g γと 1 0 g tの関係を示すグラフを得、 このグ ラフより、 各例の直線近似の式： 1 0 §ッ= 3 + 1) ' 1' 0 8 1；の13を求めた。
(2) 得られる光情報記録媒体の評価
光硬化性転写シートのロールを円盤状に打ち抜'レヽた後、 一方の剥離シートを除 去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピットと しての凹凸面を有するポリカーボネート基板 （厚さ 1. lmm) の凹凸面に設け られた銀合金の半透過反射層上に、 転写シート面と反射層が接触するように配置 し、 シリコ一ンゴム製のローラを用いて 2 k gの荷重で光硬化性転写シートを押 圧し、 積層体を形成した （第 2図の （3) に対応） 。
積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパ'を、 シート表面とスタンパの凹凸面とが接触するように配置して、 シリコーンゴム製 のローラを用いて 2 k gの荷重でスタン /、°を押圧し、 積層体を形成し、 スタンパ の凹凸形状を転写シート表面に転写した。
次に、 光硬化性転写シート側から、 メタルハライドランプを用いて、 積算光量 l O O OmJ/cm 2の条件で U V照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬化した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 アルミニウム反射層 （70 nm) を 形成した。 この上に接着剤を介してポリカーボネートフィルム （厚さ 70 m ; 商品名ピュアエース C I 10— 70、 帝人 （株） 製） を貼り付けた。
これにより 2層の凹凸面を有する光情報記録媒体を得た。
(2) 光情報記録媒体の評価
(2- 1) 光線透過率'（380〜42 O nmの波長領域）
一方の光硬化性転写シートを、 J I S— K671 7に従い 405 nmの波長領 域の光線透過率を測定した。 .
(2-2) 信号読み取り ·
得られた光情報記録媒体の再生波形を、 波長 405 nmのレーザを用いて測定 し、 得られた再生波形と製造に用いたスタンパの波形と比較した。 スタンパの波 形と一致しているものを〇、 ほとんど一致しているもの△、 ほとんど一致してい ないものを Xとした。
得られた試験結果を表 2に示す。 ' 表 2
Figure imgf000059_0001
実施例 5で得られた光硬化性転写シートは、 bの値が小さく、 の口ールはしみ 出しが無く、 且つこれを用いて得られる光情報記録媒体のピット形状は良好なも のであり、 作業性、 転写特性共に優れて!/、た。 さらに、 光線透過率も高くレーザ の透過に有利であり、 光情報記録媒体として優れた性能を有していると言える。 一方、 比較例 2の本発明の粘着性付与剤を含まなレ、転写層から得られた光情報記 録媒体は、 bの値が大きく、 ピット形状は良好なものであるが、 転写シートの口 ールにしみ出しがあり、 その製造のための作業性は劣っていた。 また、 粘着性付 与剤であっても本発明の S P値未満のものを用いた転写層から得られた光情報記 録媒体 （比較例 3 ) 'は、 ピット形状は良好なものであるが、 ロールにしみ出しが あり、 その製造のための作業性は充分に改善されず、 また光線透過率も劣ってい た。 従って、 本発明の光硬化性転写シートは、 得られる光情報記録媒体の特性を 劣化させることなく、 その製造のための作業性を向上させたものであると言うこ とができる。
[実施例 6 ]
<光硬化性転写シートの作製 >
(反応性ポリマーの作製）
配合 I
2一ェチルへキシルメタクリレート 7 0質量部 メチルメタクリレート 20質量部
2—ヒ ドロキシェチルメタタリレート 10質量部 ベンゾフエノン 5質量部 トルエン 30質量部 酢酸ェチル 30質量部 上記の配合の混合物を、 穏やかに撹拌しな ら、 60°Cに加熱して重合を開始 させ、 この温度で 10時間撹拌し、 側鎖にヒ ドロキシル基を有するアクリル樹脂 を得た。 その後、 力レンズ MO I (2—ィゾシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添加し、 窒素雾囲気下で穏やかに撹拌しながら 5 0°Cで反応させ、 光重合性官能基を有する反応性ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 T gが 0°Cでおり、 側鎖にメタクリロイル基を 5 モル0 /0有していた。
配合 II
反応性ポリマー溶液 1 100質量部 トリシクロデカンジアタリレート 30質量部
1—ヒドロキシシク口へキシルフェニルケトン 1質量部 シリ力微粒子 （平均粒径 50 nm；商品名ケミスノ一 M P、
綜研化学 （株） 製） 5質量部 上記配合の混合物を均一に溶解、 混練し、 剥離シート （幅 30 Omm、 長さ 1 000m、 厚さ 75 μπι；商品名 No. 23、 藤森工業 （株） 製） 上に、 全面塗 布し、 乾燥厚さ 20± 2 μπιの光硬化性転写、ンートを形成し、 シートの反対側に 上記と同一の剥離シートを貼付し、 ロール状に巻き上げ、 光硬化性転写シートの フルエッジタイプのロール （直径 5m) を得た。
[比較例 4] ·
実施例 6において、 配合 IIのシリカ微粒子を用いなかった以外は、 同様にして 光硬化性転写シートのロールを得た。
[比較例 5] 実施例 6において、 配合 IIのシリカ微粒子として、 商品名ケミスノー MP (綜 研化学 （株）製）） の代わりに、 商品名ケミスノー MP (平均粒径 1 000 nm； 綜研化学 （株） 製） を 5質量部用いた以外は、 同様にして光硬化性転写シートの ロールを得た。
(1) 光硬化性転写シートのロールの評価
(1- 1) しみ出し
実施例、 比較例で得られたロールを、 常温で 1000時間放置した後、 ロール 側面の転写層のしみ出しを観察した。 下記のよう評価した。
〇： しみ出しが見られない。
△： しみ出しが若干見られる。
X ： しみ出しが相当見られる。
(1-2) 転写シートのクリープ試験
上記実施例 6及び比較例 4で得られた口ールを 25 °Cで 24時間放置した後、 転写シートの転写層のクリープ試験を、 動的粘弾性測定装置としてレオストレス RS 300 (HAAKE社製） を用いて行った。 その際、 ψ = 2 Ommのパラレ ルプレートを用いて、 測定厚さ lmm (転写層を積層し成形した） 、 測定温度 2 5°Cにて、 応力 50 P a、 120秒間の条件で行った。
上記試験結果から、 測定された時間 [ t] (秒） に対する歪み [y] (%) の プロットし、 これに基づき 1 o g γと 1 o g tの関係を示すグラフを得、 このグ ラフより、 各例の直線近似の式： l o g T/ = a + b ' l o g tの bを求めた。 (2) 得られる光情報記録媒体の評価
光硬化性転写シートのロールを円盤 に打ち抜いた後、 一方の剥離シートを除 去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピットと しての凹凸面を有するポリカーボネート基板 （厚さ 1. 1 mm) の凹凸面に設け られたアルミニウム反射層 （70 nm) 上に、 転写シート面と反射層が接触する ように配置し、 シリコーンゴム製のローラを用いて 2 k gの荷重で光硬化性転写 シートを押圧し、 積層体を形成した （第 2図の （3) に対応） 。 積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接触するように配置して、 シリコーンゴム製 のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体を形成し、 スタンパ の凹凸形状を転写シート表面に転写した。
次に、 光硬化性転写シート側から、 メタルハライドランプを用いて、 積算光量 100 Om j/cm2の条件で UV照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬 f匕した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 銀合金の半透過反射層を形成した。 この上に接着剤を介してポリカーボネートフィルム （厚さ 70 μηι；商品名ピュ ァエース C 1 10— 70、 帝人 （株） 製） を貼り付けた。
これにより 2層の凹凸面を有する光情報記録媒体を得た。
(光情報記録媒体の評価）
(2- 1) 光線透過率 （380〜 420n mの波長領域）
—方の光硬化性転写シートを、 J I S— K 671 7に従い 380〜420 nm の波長領域の光線透過率を測定した。 70 °/o以上を〇、 70 %未満を Xとした。
(2-2) 信号読み取り
得られた光情報記録媒体の再生波形を、 波長 405 nmのレーザを用いて測定 し、 得られた再生波形と製造に用いたスタンパの波形と比較した。 スタンパの波 形と一致しているものを〇、 ほとんど一致していないものを Xとした。
得られた試験結果を表 3に示す。 .
表 3 '
実施例 6 比較例 4 比較例 5 しみ出し 〇 . X 〇
b 0.49 0.59
光線透過率 (380-420nm) 〇 〇 〇 信号読み取り 〇 〇 X 実施例 6で得られた光硬化性転写シートは、 bの値が小さく、 の口ールはしみ 出しが無く、 且つこれを用いて得られる光情報記録媒体のピット形状は良好なも のであり、 作業性、 転写特性共に優れていた。 一方、 比較例 4の、 透明微粒子を 用い.ないロールから得られた光情報記録媒体は、 ピット形状は良好なものである 力 s、 bの値が大きく、 ロールにしみ出しがあり'、 その製造のための作業性は劣つ ていた。 また、 平均粒径が本発明の範囲外の透明微粒子を用いたロールは浸みだ しが無かったが、 これを用いて得られる光情報記録媒体のピット形状は良好とは いえないものであった。 従って、 本発明の光硬化性転写シートは、 得られる光情 報記録媒体の特性を劣化させることなく、 その製造のための作業性を向上させた ものであると言うことができる。
[実施例 7 ]
<光硬化性転写シートの作製〉
(反応性ポリマーの作製）
配合 I
2ーェチノレへキシルメタクリレート 7 0質量部 メチルメタクリレート 2 0質量部
2—ヒ ドロキシェチルメタクリレート 1 0質量部 ベンゾフエノン
トルエン 3 0質量部 酢酸ェチル 3 0質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 6 0 °Cに加熱して重合を開始 させ、 この温度で 1 0時間撹拌し、 側鎖にヒ ドロ'キシル基を有するアクリル樹脂 を得た。 その後、 力レンズ MO I ( 2—ィソシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添加し、 窒素雰囲気下で穏やかに撹拌しながら 5 0 °Cで反応させ、 光重合性官能基を有する反応性ポリマーの溶液 1を得た。 得られた反応性ポリマーは、 T gが 0 °Cであり、 側鎖にメタクリロイル基を 5 モル。 /0有していた。
配合 II
反応性ポリマー溶液 1 100質量部 へキサンジオールジァクリレート 30質量部
1ーヒ ドロキシシクロへキシルフェニノレケドン 1質量部 上記配合の混合物を均一に溶解し、 剥離シート （幅 30 Omm、 長さ 10◦ 0 m、 厚さ 75 μπι；商品名 No. 23、 藤森工業 （株） 製） 上に、 全面塗布し、 乾燥厚さ 20 ± 2 mの光硬化性転写シートを形成し、 シートの反対側に上記と 同一の剥離シートを貼付し、 ロール状に巻き上げ、 光硬化性転写シートのロール (直径 0. 5 m) を得た。
[比較例 6 ]
実施例 7において、配合 IIのへキサンジオールジァクリレートを用いなかった 以外は、 同様にして光硬化性転写シートのロールを得た。
[比較例 7]
実施例 7において、配合 IIのへキサンジオールジァクリレートを 60質量部用 いた以外は、 同様にして光硬化性転写シートのロールを得た。
(1) 光硬化性転写シートの評価
(1-1) 転写シートの貯蔵弾性率の測定
上記実施例 7、比較例 6及び 7で得られた転写シートの転写層の貯蔵弾性率を、 粘弾性測定装置としてレオストレス RS 300 (HAAKE社製） を用いて測定 した。 その際、 ψ = 20mmのパラレルプレートを用いて、 測定厚さ lmm (転 写層を押圧により薄くした） 、 測定温度 25°Cにて、 周波数 0. 01Hz、 1H z、 10 OH zにおいて測定した。 ·
(1— 2) 厚み精度
得られた光硬化性転写シートの厚さを lm2当たり 10力所測定し、厚さのばら つきの程度を測定した。 ばらつきが 5%以内の場合を〇、 5%を超える場合を X とした。
(2) 得られる光情報記録媒体の評価
各例の光硬化性転写シートのロールを円盤 に打ち抜いた後、 一方の剥離シー トを除去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピ ットとしての凹凸面を有するポリカーボネート基板 （厚さ 1. 1mm) の凹凸面 に設けられたアルミニウム反射層 （70 nm) '上に、 転写シート面と反射層が接 触するように配置し、 表面温度が 25°Cのシリ コーンゴム製のローラを用いて 2 k gの荷重で光硬化性転写シートを押圧し、 積層体を形成した （第 2図の （3) に対応） 。
積層体の光硬化性転写シートのもう一方の彔 ϋ離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接触する うに配置して、 表面温度が 25°C のシリコーンゴム製のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体 を形成し、 スタンパの凹凸形状を転写シート袠面に転写した。
次に、 光硬化性転写シート側から、 メタルノ、ライドランプを用いて、 積算光量 1000m J/cm2の条件で UV照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬化した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 銀合金の半透過反射層を形成した。. この上に接着剤を介してポリカーボネートフィルム （厚さ 70 μπι；商品名ピュ ァエース C 1 10— 70、 帝人 （株） 製） を貝占り付けた。
これにより 2層の凹凸面を有する光情報記綠媒体を得た。
(2-1) 得られた光情報記録媒体の光線透過率 （380〜 420 n mの波長 領域）
一方の光硬化性転写シートを、 J I S—K6 7'1 7に従い 380〜420 nm の波長領域の光線透過率を測定した。 70%以上を〇、 70%未満を Xとした。
(2-2) 得られた光情報記録媒体の転写†生 （信号読み取り）
得られた光情報記録媒体の再生波形を、 波長 405 nmのレーザを用いて測定 し、 得られた再生波形と製造に用いたスタンパの波形と比較して、 転写性を評価 した。 スタンパの波形と一致しているものを〇、 ほとんど一致していないものを Xとした。
得られた試験結果を表 4に示す。
表 4
Figure imgf000066_0001
実施例 7で得られた光硬化性転写シートは厚さ精度が良好で作業性に優れ、 且 つこれを用いて得られる光情報記録媒体のピット形状は良好なもので、 常温での 転写性にも優れていることが分かる。 一方、 比較例 6の、 希釈剤を用いない貯蔵 弾性率が本発明の範囲より高い光硬化 転写シートから作製された光情報記録媒 体は、 厚さ精度は良好なものであるが、 転写性は劣っていた。 また、 貯蔵弾性率 が本発明の範囲より低い転写シートから作製された光情報記録媒体は、 転写性は 良好であるが、 厚さ精度は劣っていた。 [実施例 8〜： 1 6 ]
く光硬化性転写シートの作製 >
(反応性ポリマーの作製）
配合 I
2—ェチノレへキシノレメタクリ レート 7 0質量部 メチルメタクリ レート 2 0質量部 2—ヒ ドロキシェチルメタクリ レート ]
ベンゾフエノン
トルエン 30質量部 酢酸ェチル 30質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 60°Cに加熱して重合を開始 させ、 この温度で 10時間撹拌し、 側鎖にヒドロキシル基を有するァクリル樹脂 を得た。 その後、 力レンズ MO I (2—イソシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添加し、 窒素雰囲気下で穏やかに撹拌しながら 5 0 °Cで反応させ、 光重合性官能基を有する反応'卜生ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 Tgが 0°Cであり、 側鎖にメタクリロイル基を 5 モル0 /0有していた。
配合 II
反応性ポリマー溶液 1 (固形分 63. 6質量 100質量部 アクリル樹脂 （ポリメチルメタクリレート； 10質量部
T g ： 65 、 数平均分子量： 230,000
ダイヤナール BR— 90、 三菱レイヨン （株） 製）
へキサンジオールジァクリレート 40質量部 置換基有するフエノール化合物 （表 1に示す） 0. 05質量部 -
1—ヒドロキシシクロへキシルフェニルケトン 1質量部
(ィルガキュア 184、 チパガィギー （株） 製)
上記配合の混合物を均一に溶解し、 剥離シート （幅 30 Omm、 長さ 1000 m、 厚さ 75 μπι ;商品名 No. 23、 藤森工業 （株）'製） 上に、 全面塗布し、 乾燥厚さ 20 ± 2 μ mの光硬化性転写シートを幵成し、 シートの反対側に上記と 同一の剥離シートを貼付し、 口ール状に卷き上ず'、 光硬化性転写シートのロール (直径 5m) を得た。
[比較例 8]
実施例 8において、配合 IIの置換基有するフェノ一ルイヒ合物を用いなかつた以 外は、 同様にして光硬化性転写シートのロールを得た。
<得られる光情報記録媒体の評価 >
各例の光硬化性転写シートのロールを円盤状に打ち抜いた後、 一方の剥離シー トを除去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピ ットとしての凹凸面を有するポリカーボネート基板 （厚さ 1. 1 mm) の凹凸面 に設けられた A g合金 （A PC) の半透明反射層 (70 nm) 上に、 転写シート 面と反射層が接触するように配置し、 表面温度が 25°Cのシリコーンゴム製の口 ーラを用いて 2 k gの荷重で光硬化性転写シートを押圧し、積層体を形成した（台 2図の （3) に対応） 。
積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接触するように配置して、 表面温度が 25 °C のシリコーンゴム製のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体 を形成し、 スタンパの凹凸形状を転写シート表面に転写した。
次に、 光硬化性転写シート側から、 メタノレハライドランプを用いて、 積算光量 1000mj/c m2の条件で U V照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬化した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 アルミニウムの反射層 （70 nm). を形成した。この上に接着剤を介してポリカーボネートフィルム（厚さ 70 ； 商品名ピュアエース C I 10— 70、 帝人 （株） 製） を貼り付けた。
これにより 2層の凹凸面を有する光情報記録媒体を得た。
<光情報記録媒体の評価 > '
(1) 得られた光情報記録媒体の光線透過率 （380〜420 nmの波長領域） 光硬化性転写シート （上記と同様に硬化させた後） を、 J I S— R 3257に 従い 380〜 420 n mの波長領域の光, f泉透過率を測定した。 90 %以上を〇、 90%未満を Xとした。
(2) 得られた光情報記録媒体の反射率の変化量） 得られた光情報記録媒体の A g Xの反射率を基板側から測定し、 次レ、でこの媒 体を温度 8 0 °C、湿度 8 5 %の恒温槽に 2 4時間放置したのち反射率を測定した。 最初の反射率から促進試験後の反射率を差し引いた値を表 5に示した。 尚、 最初 の反射率はいずれも 4 3。/。であった。
得られた試験結果を表 5に示す。
表 5'
Figure imgf000069_0001
表中のアデカスタブは旭電化工業 （株） の商品名。 実施例 8 〜 1 6で得られた光情報記録媒体は、 高温高湿下に長時間曝されても 反射率の低下は少なかったが、 置換基を有するフエノ ル化合物を含まない比較 例 8の光情報記録媒体では反射率の低下が大きかった。
[実施例 1 7 ]
<光硬化性転写シートの作製 >
(反応性ポリマーの作製） 配合 I
2ーェチ /レへキシ /レメタクリレート 70質量部 メチルメタクリ レート 20質量部
2—ヒ ドロキシェチノレメタクリ レート 10質量部 ベンゾフエノン
トルエン 30質量部 酢酸ェチル 30質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 60°Cに加熱して重合を開始 させ、 この温度で 1◦時間撹拌し、 側鎖にヒドロキシル基を有するアクリル樹脂 を得た。 その後、 力レンズ MO I (2—イソシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添カ卩し、 窒素雰囲気下で穏やかに撹拌しながら 5 0°Cで反応させ、 光重合性官能基を有する反応' I"生ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 Tgが 0°Cであり、 側鎖にメタクリロイル基を 5 モル0 /0有していた。
配合 II
反応性ポリマー溶液 1 (固形分 63. 6質量 ° ） 100質量部 アクリル樹脂 （T g ： 65° (：、 数平均分子量： 230，000； 10質量部
ダイヤナール BR— 90、 三菱レイヨン （株） 製）
ネオペンチルグリコールジァクリレート 40質量部
(共栄社 (株) 製、 ライトァクリレート NP— A)
1—ヒ ドロキシシクロへキシルフェニルケトン 1質量部
(ィルガキュア 184、 チバガイギー （株） 製）'
上記配合の混合物を均一に溶解し、 剥離シー卜 （幅 30 Omm、 長さ 1000 m、 厚さ 75 m ;商品名 No. 23、 藤森工業' （株） 製） 上に、 全面塗布し、 乾燥厚さ 20 ± 2 μ mの光硬化性転写シートを汗成し、 シートの反対側に上記と 同一の剥離シートを貼付し、 ロール状に巻き上げ、 光硬化性転写シートのロール (直径 0. 5 m) を得た。 [実施例 18 ]
実施例 17において、配合 IIのネオペンチノレグリコールジァクリレートの代わ りにジメチロールトリシクロデカンジアタリレート （日本化薬 （株） 製、 KAY ARAD R-684) を用いた以外は、 同様にして光硬化性転写シートのロー ルを得た。
[比較例 9〜 12 ]
実施例 17において、配合 IIのネオペンチルグリコールジァクリレートの代わ りに表 1に示す化合物を用いた以外は、 同様にして光硬化性転写シートのロール を得た。
<得られる光情報記録媒体の評価 >
各例の光硬化性転写シートのロールを円盤状に打ち抜いた後、 一方の剥離シー トを除去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピ ットとしての凹凸面を有するポリカーボネート基板 （厚さ 1. 1mm) の凹凸面 に設けられた A g合金 （A PC) の半透明反射層 （70 nm) 上に、 転写シート 面と反射層が接触するように配置し、 表面温度が 25 のシリコーンゴム製の口 ーラを用いて 2k gの荷重で光硬化性転写シートを押圧し、積層体を形成した（第
2図の (3) に対応） 。
積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接触するように配置して、 表面温度が 25 °C のシリコーンゴム製のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体 を形成し、 スタンパの凹凸形状を転写シート表面に転写した。
次に、 光硬化性転写シート側から、 メタルハライドランプを用いて、 積算光量
100 Om】/。1112の条件で11¥照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬ィヒした光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 A g合金の反射層 （70 nm) を形 成した。 この上に接着剤を介してポリカーボネートフィルム （厚さ 70μπι ;商 品名ピュアエース C 110— 70、 帝人 （株） 製） を貼り付けた。
これにより 2層の凹凸面を有する光情報記録媒体を得た。
<光情報記録媒体の評価 >
(1) 得られた光情報記録媒体の光線透過率（3 80〜420 nmの波長領域） 光硬化性転写シ ト （上記と同様に硬化させた後） を、 J I S— R3257に 従い 380〜 420n mの波長領域の光線透過率を測定した。 90 %以上を〇、 90%未満を Xとした。
(2) 得られた光情報記録媒体の硬化層の水接き虫角
光硬化性転写シート （スタンパを用いる前に上記と同じ条件で硬化させた後） の硬化層の水接触角を、 J I S— R 3257に従レ、測定した。 その際、 測定機器 として、 協和界面科学 （株） 製の接触角計 CA— Xを用いた。
(3) 得られた光情報記録媒体の反射率の変化量
得られた光情報記録媒体の A g Xの反射率を基板側から測定し、 次いでこの媒 体を温度 80°C、 湿度 85%の恒温槽に 24時間放置したのち同様に反射率を測 定した。 最初の反射率から促進試験後の反射率を差し引いた値を表 1に示した。 尚、 最初の反射率はいずれも 43%であった。
反射率の変化量が 3%以内を〇、 3%を超えるものを Xと判定した。
得られた試験結果を表 6に示す。 .
表 6
Figure imgf000072_0001
表中、 A— 400 ： ポリエチレングリコールジァクリレート ( (P EG 400) ジァクリレート）
A-TMPT ： トリメチロールプロパントリアタリレート
KS— HDD A： 1 , 6—へキサンジオールジァクリレート
R- 712 ： (商品名： KAYARAD R—712, 日本化薬 （株) 製） 実施例 1 7及び 18で得られた水接触角の高い光情報記録媒体は、 高温高湿下 に長時間曝されても反射率の低下は少なかつだが、 水接触角の低い比較例 9〜 1 2の光情報記録媒体は反射率の低下が大きかった。 従って、 本発明の光情報記録 媒体は耐久性に優れたものである。 [実施例 1 9〜 21及び比較例 1 3〜 16 ]
く光硬化性転写シートの作製 >
(反応性ポリマーの作製）
配合 I
2—ェチノレへキシノレメタクリレート 70質量部 メチルメタクリレート 20質量部
2_ヒドロキシェチルメタクリレート 10質量部 ベンゾフエノン
トノレエン 30質量部 酢酸ェチル 30質量部 上記の配合の混合物を、 穏やかに撹拌しながら、 60°Cに加熱して重合を開始 させ、 この温度で 10時間撹拌し、 側鎖にヒドロキシル基を有するアクリル樹脂 を得た。 その後、 力レンズ MO I (2—イソシアナトェチルメタクリレート ； 昭和電工 （株） 製） 5質量部を添加し、 窒素雰囲気下で穏やかに撹拌しながら 5 0°Cで反応させ、 光重合性官能基を有する反応性ポリマーの溶液 1を得た。
得られた反応性ポリマーは、 Tgが 0°Cであり、 側鎖にメタクリロイル基を 5 モル0 /0有していた。
配合 II 反応性ポリマー溶液 1 (固形分 63. 6質量％) 100質量部 アクリル樹脂 10質量部
(T g ： 65 °C、 数平均分子量： 230， 000；ダイャナール B R— 90、 三菱レイ ヨン （株） 製）
反応' I"生希釈剤 （へキサンジオールジァクリレート） 40質量部 リン酸メタクリレート 表 7の各質量部
(エチレンォキシド変性リン酸ジメタアタリレート、 日本化薬 （株） 製） 光重合開始剤 （ 1ーヒドロキシーシク口へキシルーフエ二ルケトン） 1質量部 (ィルガキュア 184、 チパガィギー （株） 製）
上記配合の混合物を均一に溶解し、 剥離シート （幅 30 Omm、 長さ 1000 m、 厚さ 75 μπι；商品名 No. 23、 藤森工業 （株） 製） 上に、 全面塗布し、 乾燥厚さ 20 ± 2 μ mの光硬化性転写シートを形成し、 シートの反対側に上記と 同一の剥離シートを貼付し、 口ール状に巻き上げ、 光硬化性転写シートのロール (直径 0. 5 m) を得た。
く得られる光情報記録媒体の評価 >
各例の光硬化性転写シートのロールを円盤状に打ち抜いた後、 一方の剥離シー トを除去し、 得られた円盤状光硬化性転写シートを、 射出成形により成形したピ ットとしての凹凸面を有するポリカーボネート基板 （厚さ 1. 1mm) の凹凸面 に設けられた A g合金 （A PC) の半透明反射層 （70nm) 上に、 転写シート 面と反射層が接触するように配置し、 表面温度が 25°Cのシリコーンゴム製の口 ーラを用いて 2 k gの荷重で光硬ィヒ性転写シートを押圧し、積層体を形成した（第 2図の （3) に対応） 。 '
積層体の光硬化性転写シートのもう一方の剥離シートを除去し、 その除去され た転写シート表面に、 ピットとしての凹凸面を有するニッケル製のスタンパを、 シート表面とスタンパの凹凸面とが接触するように配置して、 表面温度が 25°C のシリコーンゴム製のローラを用いて 2 k gの荷重でスタンパを押圧し、 積層体 を形成し、 スタンパの凹凸形状を転写シート表面に転写した。 次に、 光硬化性転写シート側から、 メタルハライドランプを用いて、 積算光量
300 Om J/cm2の条件で U V照射し、 転写シートを硬化させた。
積層体からスタンパを剥離、 除去し、 硬化した光硬化性転写シートの凹凸面上 に銀合金をスパッタリングすることにより、 アルミニウムの反射層 （70nm) を形成した。この上に接着剤を介してポリカーボネートフィルム（厚さ 70 / m； 商品名ピュアエース C 110— 70、 帝人 （株） 製） を貼り付けた。
これにより 2層の凹凸面を有する光情報記録媒体を得た。
<光情報記録媒体の評価 >
(1) スタンパ剥離性
上記 UV照射の後に積層体からスタンパを剥離除去する際に、 その剥離除去が 良好に行われたかどうかを、 目視によって観察して評価した。 積層体に転写シー トが完全に残った場合を〇 （マル） と評価し、 積層体に転写シートが完全には残 らずに端部に捲れや泣き別れが発生した場合を X (パッ） と評価した。
(2) 得られた光情報記録媒体の反射率の変化量
得られた光情報記録媒体の A g合金 （APC) の反射率を基板側から測定し、 次いでこの媒体を温度 80 °C、 湿度 85 %の恒温槽に 240時間放置した後に、
405 nmのレーザ光での反射率を測定した。 最初の反射率から促進試験後の反 射率を差し引いた値を表 7に示した。 尚、 最初の反射率はいずれも 43%であつ 得られた試験結果を表 7に示す。
7
Figure imgf000076_0001
実施例 1 9 〜 2 1で得られた光情報記録媒体は、 製造時には良好なスタンプ剥 離性を示し、 且つ高温高湿下に長時間曝されても反射率の低下は少なく十分な耐 久性を有するものであった。 しかし、 比較例 1 3及び 1 4の光情報記録媒体は、 上記条件下の反射率の低下は少ないものの、 製造時におけるスタンパからの剥離 性は良好とは言えなかった。 また、 比較例 1 5及び 1 6の光情報記録媒体は、 反 射率の低下が大きく耐久性が十分なものとは言えなかった。 6 . 産業上の利用可能性
本発明の光硬化性転写シートは、 D V D等の厚さが薄く、 高容量の光情報記録 媒体の製造に有利な光硬化性転写シートであって、 製造時に使用される長尺状シ ートのロール形態にしても、 光硬化性転写層の成分のしみ出しが無く、 シート厚 の変動もないものであり、 特に作業性に優れた光硬化性転写シートということ力 s できる。 即ち、 常温転写に有利な光重合性官能基を有する反応性ポリマーの光硬 化性転写層を、 特に、 前記光硬化性転写シート①〜⑤に規定した特定の層 （例え ば、 特定のクリープ特性、 特定の粘着性付与剤又は特定の微粒子含有等） とする ことにより、 製造作業中、 貯蔵中の光硬化性転写層からの成分のしみ出しを抑え ることができ、 さらに転写性向上に伴う悪影響として現れやすい、 貯蔵中等にお けるシート厚の変動も抑えることができる。 また、光硬化性転写シート⑥〜⑧を用いて得られる本発明の光情報記録媒体は、 銀又は銀合金の反射層に接する層を、 前記の特定の硬化層とすることにより、 こ の層の反射率の低下 （特に、 銀反射層と硬化層との界面に発生する乱反射の発生 のためと推測される）或いは反射層の腐食を、長期に亘り防止することができる。 このため光ディスクを長期に使用しても、 反射率の低下がほとんど見られないの で、 ディスクを良好に再生することが可能である。 特に光硬化性転写シート⑥を 用いた場合は、 この層の黄変等の膜劣化の防止により、 特に光硬化性転写シート ⑦を用いた場合は、 表面の水接触角が 6 0度以上の極めて疎水性の光硬化性組成 物の硬化層であり、 このような層は高温高湿の条件下でも水分の侵入を抑制する こと力 ら、 上記効果が得られ、 また光硬化性転写シート⑧を用いた場合は、 銀合 金等からなる薄膜と十分に接着しており、 製造途中で剥離することも抑制されて いるために、 上記効果に加えて、 光情報記録媒体の製造が容易となり、 生産性に も優れ、 さらに製造後においても、 硬化層が銀合金等からなる薄膜への優れた接 着力を維持しているために、 銀合金等からなる薄膜の腐食等によると考えられる 反射率の低下も見られない。 特に、 光硬化性転写シート⑧の光硬化性樹脂組成物 は、 スタンパ材料である N iと比較して、 銀合金等との接着性が向上しているた めに、 製造工程でのスタンパ剥離時に、 硬化層がスタンパ側へと残ることなく、 銀合金等の側へと選択的に転写することができる。 このために、 光情報記録媒体 を多層にわたって積層して製造する場合において、 特に有利に使用することがで きる。
また本発明では、 光反応性ポリマーを使用しているため、 硬化層の反射層に対 する接着性に優れ、 また硬化層の被膜強度も大きいので、 反射層の保護機能が高 レ、。

Claims

請求の範囲
1. 光重合性官能基を有する反応性ポリマーを含む、 加圧により変形可能な光 硬化性組成物からなる光硬化性転写層を有する光硬化性転写シートであって、 光硬化性転写層が、 動的粘弾性測定装置を用いるクリープ試験において、 常温 で、 応力 50 P a 1 20秒間の条件で、 時間 [ t ] (秒） に対する歪み [γ ] (%) の関係が、 直線性を示し、 且つ下記式： '
1 o g = a + b · l o g t
(但し、 aが実数を表し、 bが 0. 10〜0. 53の範囲にある） を満足する ことを特徴とする光硬化性転写シート。
2. 反応性ポリマーのガラス転移温度が 20°C以下である請求項 1に記載の 光硬化性転写シート。
3. 反応性ポリマーの数平均分子量が 10000〜 300000である請求 項 1又は 2に記載の光硬化性転写シート。
4. 反応性ポリマーの重量平均分子量が 10000〜 300000である請 求項 1〜 3のいずれかに記載の光硬化性転写シート。 .
5. 反応性ポリマーが、光重合性官能基を 1〜 50モル％含む請求項 1〜 4の いずれかに記載の光硬化性転写シート。
6. 光重合性官能基が、 （メタ）アタリロイル基である請求項 1〜5のいずれ かに記載の光硬化性転写シート。 '
7. 反応性ポリマーが、活性水素を有する官能基及び光重合性官能基を有する 反応性ポリマーであり、 且つ光硬化性組成物が、 さらに活性水素を有する官能基 と反応性を有する基を少なくとも 2個有する化合物を含んでいる請求項 1〜 6の いずれかに記載の光硬化性転写シート。
8. 活性水素を有する官能基がヒドロキシル基である請求項 7に記載の光硬 化性転写シート。
9. 活性水素を有する官能基と反応性を有する基がィソシァネート基である 請求項 7又は 8に記載の光硬化性転写シート。
10. 光硬化性組成物が、 さらに溶解度パラメータ （SP値） が 8. 50以上の 粘着性付与剤を含んでいる請求項 1〜 9のいずれかに光硬化性転写シート。
1 1. 光硬化性組成物が、平均粒径が 300 n m以下の透明微粒子を含む請求項 1〜 10のいずれかに記載の光硬化性転写シート
12. 光硬化性転写層における、周波数 1Ηζ、 0. 01Hz及び 100Hzに おける貯蔵弾性率が、 25°Cにおいて、 それぞれ l X 103〜9 X 104P a、 5
X 103 P a以上、 及び 1 X 107 P a以下である請求項 1〜 12のいずれかに記 載の光硬化性転写シート。
1 3. 光硬化性組成物が、置換基を有するフエノールイヒ合物を 0. 01〜0. 3 質量％含有する請求項 1〜 12のいずれかに記載の光硬化性転写シート。
14. 光硬化性組成物の硬化層表面の水接触角が 60度以上である請求項 1〜 1 3のいずれかに記載の光硬化性転写シート。
1 5. 光硬化性組成物が、 リン酸 （メタ） アタリレート及び/又はその誘導体を 10〜220 p p m含有する請求項 1〜 14のいずれかに記載の光硬化性転写シ —ト。
16. 活性水素を有する官能基及び光重合性官能基を有する反応性ポリマーを 含む、 加圧により変形可能な光硬化性組成物からなる光硬化性転写層を有する光 硬化性転写シートであって、
光硬化性組成物が、 さらに活性水素を有する官能基と反応性を有する基を少な くとも 2個有する化合物を含んでいることを特徴とする光硬化性転写シート。
17. 光重合性官能基を有する反応性ポリマーを含む、 加圧により変形可能な 光硬化性組成物からなる光硬化性転写層を有する光硬化性転写シートであって、 光硬化十生糸且成物が、 さらに溶解度パラ'メータ （SP値） が 8. 50以上の粘着 性付与剤を含んでいることを特徴とする光硬化性転写シート。
18. 光重合性官能基を有する反応性ポリマー及び平均粒径が 300 n m以下 の透明微粒子を含む、 加圧により変形可能な光硬化性組成物からなる光硬化性転 写層を有する光硬化性転写シート。
1 9. 光重合性官能基を有する反応性ポリマーを含む光硬化性組成物からなり、 且つ周波数 1 H z、 0. 01Hz及ぴ 1 00 H zにおける貯蔵弾性率が、 25 °C において、 それぞれ l X 103〜9 X 104P a、 5 X 103P a以上、 及び 1 X 107 P a以下である光硬化性転写層を有する光硬化性転写シート。
20. 光重合性官能基を有する反応性ポリマー'を含み、 .且つ置換基を有するフ ェノール化合物を 0. 01~0. 3質量％含有する光硬化性組成物を含む光硬化 性転写層を有する光硬化性転写シート。
2 1 . 光重合性官能基を有する反応性ポリマーを含む光硬化性転写層を有し、 その光硬化性転写層の硬化後における表面の水接触角が 6 0度以上であることを 特徴とする光硬化性転写シート。
2 2 . 光重合性官能基を有する反応性ポリマーを含み、 リン酸 （メタ） アタリ レート及ぴ Z又はその誘導体を 1 0〜 2 2 0 p' p m含有する光硬化性組成物を含 む光硬化性転写層を有する光硬化性転写シート。
2 3 . 光硬化性転写層の一方又は両方の表面に、 剥離シートが設けられている 請求項 1〜 2 2のいずれかに記載の光硬化性転写シート。
2 4 . 光硬化性転写シートが長尺状であり、 力 光硬化性転写層と剥離シートの 幅が略同一である請求項 2 3に記載の光硬化性転写シート。
2 5 . 下記の工程 ( 2 ) 〜 （4 ) ：
( 2 ) 請求項 2 3又は 2 4に記載の光硬化性転写シートの一方の剥離シートを 除去する工程；
( 3 ) 表面に記録ピット ¾び/又はグループとしての凹凸を有し、 さらに該凹 凸表面の凹凸に沿って反射層が設けられた基板の該反射層上に、 該光硬化性転写 シートの光硬化性転写層の表面が該反射層の凹凸表面に接触するように裁置し、 これらを押圧して該光硬化性転写シートの表面が該反射層の凹凸表面に沿って密 着された積層体を形成する工程；及び '
( 4 ) 該積層体からもう一方の剥離シートを除去する工程、
を含むことを特徴とする光情報記録媒体の製造方法。
2 6 . 前記工程 （2 ) の前に、
( 1 ) 光硬化性転写シートを円盤状に打ち抜く工程；又は ( 1 ) 光硬化性転写シートの光硬化性転写層と一方の剥離シートを円盤状に打 ち抜き、 もう一方の剥離シートをそのまま残す工程；
を行う請求項 2 5に記載の光情報記録媒体の製造方法。 2 7 , 前記工程 （4 ) を行った後、 さらに
( 5 ) 該積層体の剥離シートが除去された光硬化性転写層の表面に、 記録ピッ ト及び/又はグループとしての凹凸を有するスタンパの該凹凸表面を裁置し、 こ れらを押圧して該光硬化性車云写シートの表面が該凹凸表面に沿って密着した積層 体を形成する工程；
( 6 ) 該スタンパを有する積層体の光硬化性転写層を紫外線照射により硬化さ せ、 次いでスタンパを除去することにより、 光硬化性転写層の表面に凹凸を設け る工程；
を含む請求項 2 5又は 2 6に記載の光情報記録媒体の製造方法。 2 8 . 前記 （5 ) 〜 （6 ) の工程を行った後、 さらに
( 7 ) 光硬化性転写層の凹凸表面に反射層を設ける工程；
を含む請求項 2 9に記載の光情報記録媒体の製造方法。
2 9 . 請求項 2 5〜 2 8のいずれかに記載の製造方法により得られる光情報記 録媒体。
3 0 . 表面に記録ピット及び Z又はグルーブとしての凹凸を有する光硬化性組 成物の硬化層、 及び該凹凸表面の凹凸に沿って設けられている銀又は銀合金の反 射層を含む光情報記録媒体であって、 '
光硬化性組成物が、 請求項 1〜 2 2のいずれかに記載された組成物であること を特徴とする光情報記録媒体。
3 1 . 表面に記録ピット及び/又はグループとしての凹凸を有する光情報記録 基板、 該凹凸表面の凹凸に沿って設けられている銀、 銀合金又は銀化合物からな る反射層、 及び該反射層の凹凸表面に接触するように設けられた光硬化性樹脂組 成物の硬化層を含む光情報記録媒体であって、
光硬化性組成物が、 請求項 1〜 2 2のいずれかに記載された組成物であること を特徴とする光情報記録媒体。
PCT/JP2004/015091 2003-10-07 2004-10-06 光硬化性転写シート、これを用いた光情報記録媒体の製造方法、及び光情報記録媒体 WO2005035635A1 (ja)