WO2004088366A1 - Procede de production d'un film a cristaux liquides cholesteriques a large bande, plaque de polarisation circulaire, polariseur lineaire, appareil d'eclairage et afficheur a cristaux liquides - Google Patents

Procede de production d'un film a cristaux liquides cholesteriques a large bande, plaque de polarisation circulaire, polariseur lineaire, appareil d'eclairage et afficheur a cristaux liquides Download PDF

Info

Publication number
WO2004088366A1
WO2004088366A1 PCT/JP2004/003718 JP2004003718W WO2004088366A1 WO 2004088366 A1 WO2004088366 A1 WO 2004088366A1 JP 2004003718 W JP2004003718 W JP 2004003718W WO 2004088366 A1 WO2004088366 A1 WO 2004088366A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
plate
film
polarizing element
cholesteric liquid
Prior art date
Application number
PCT/JP2004/003718
Other languages
English (en)
Japanese (ja)
Inventor
Takahiro Fukuoka
Kazutaka Hara
Miki Shiraogawa
Naoki Takahashi
Kentarou Takeda
Original Assignee
Nitto Denko Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nitto Denko Corporation filed Critical Nitto Denko Corporation
Publication of WO2004088366A1 publication Critical patent/WO2004088366A1/fr

Abstract

L'invention concerne un procédé de production d'un film à cristaux liquides cholestériques à large bande consistant à revêtir un substrat d'alignement d'un mélange de cristaux liquides contenant un composé mésogène polymérisable (A) et un agent chiral polymérisable (B), et à exposer ce mélange de cristaux liquides à un rayonnement ultraviolet de manière à produire une polymérisation et un durcissement, l'étape de polymérisation par ultraviolets consistant (1) à exposer le côté de substrat d'alignement du mélange de cristaux liquides, en contact avec un gaz oxygéné, à un rayonnement ultraviolet à une température supérieure ou égale à 20 °C au moyen d'un irradiateur à ultraviolets de 20 à 200 mW/cm2 pendant 0,2 à 5 secondes, puis (2) à exposer le côté de substrat d'alignement de la couche de cristaux liquides, en contact avec un gaz oxygéné, à un rayonnement ultraviolet d'une intensité inférieure à celle de l'étape (1) pendant 10 secondes ou plus tout en augmentant la température jusqu'à une température finale supérieure à celle de l'étape (1) et non inférieure à 60 °C à une vitesse supérieure ou égale à 2 °C/s, et (3) à réaliser une irradiation aux ultraviolets en l'absence d'oxygène. Ce procédé permet d'obtenir un film à cristaux liquides cholestériques à large bande possédant une bande de réflexion dans une zone de grande longueur d'onde uniforme.
PCT/JP2004/003718 2003-03-31 2004-03-19 Procede de production d'un film a cristaux liquides cholesteriques a large bande, plaque de polarisation circulaire, polariseur lineaire, appareil d'eclairage et afficheur a cristaux liquides WO2004088366A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2003094605 2003-03-31
JP2003-094605 2003-03-31
JP2003-365759 2003-10-27
JP2003365759A JP4293882B2 (ja) 2003-03-31 2003-10-27 広帯域コレステリック液晶フィルムの製造方法、円偏光板、直線偏光素子、照明装置および液晶表示装置

Publications (1)

Publication Number Publication Date
WO2004088366A1 true WO2004088366A1 (fr) 2004-10-14

Family

ID=33134318

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2004/003718 WO2004088366A1 (fr) 2003-03-31 2004-03-19 Procede de production d'un film a cristaux liquides cholesteriques a large bande, plaque de polarisation circulaire, polariseur lineaire, appareil d'eclairage et afficheur a cristaux liquides

Country Status (3)

Country Link
JP (1) JP4293882B2 (fr)
TW (1) TW200428041A (fr)
WO (1) WO2004088366A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2042895A1 (fr) * 2006-07-13 2009-04-01 Zeon Corporation Procédé de fabrication d'une feuille d'isolation à la lumière polarisée circulairement, et appareil de formation du film de revêtement

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4931167B2 (ja) * 2004-06-14 2012-05-16 日東電工株式会社 着色反射材、着色反射フィラーおよびこれらを用いた用途
KR101455427B1 (ko) * 2007-02-22 2014-10-27 니폰 제온 가부시키가이샤 콜레스테릭 액정 조성물, 원편광 분리 시트 및 제조 방법
JP4888853B2 (ja) 2009-11-12 2012-02-29 学校法人慶應義塾 液晶表示装置の視認性改善方法、及びそれを用いた液晶表示装置
CN107656332B (zh) 2010-06-22 2021-10-15 东洋纺株式会社 液晶显示装置、偏振板及偏振片保护膜
JP6180113B2 (ja) 2011-05-18 2017-08-16 東洋紡株式会社 三次元画像表示対応液晶表示装置に適した偏光板及び液晶表示装置
US10180597B2 (en) 2011-05-18 2019-01-15 Toyobo Co., Ltd. Liquid crystal display device, polarizing plate, and polarizer protection film
CN103309074B (zh) * 2013-05-24 2016-02-24 京东方科技集团股份有限公司 一种pdlc液晶面板的制备方法
KR20180098698A (ko) * 2013-08-26 2018-09-04 후지필름 가부시키가이샤 휘도 향상 필름, 광학 시트 부재 및 액정 표시 장치
KR102508041B1 (ko) * 2014-08-29 2023-03-08 스미또모 가가꾸 가부시키가이샤 광학 필름의 제조 방법
WO2019093446A1 (fr) * 2017-11-08 2019-05-16 富士フイルム株式会社 Film optique stratifié et dispositif d'affichage électroluminescent organique
KR102532379B1 (ko) * 2018-06-12 2023-05-12 후지필름 가부시키가이샤 광학 이방성층의 제조 방법

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06281814A (ja) * 1993-01-11 1994-10-07 Philips Electron Nv コレステリック偏光子及びその製造方法
JPH1180733A (ja) * 1997-06-19 1999-03-26 Consortium Elektrochem Ind Gmbh 光重合可能なコレステリック液晶のコレステリック反射帯域を拡張する方法およびこの方法により製造した光学素子
JP2002286935A (ja) * 2001-03-28 2002-10-03 Dainippon Printing Co Ltd 円偏光制御光学素子及びその製造方法
JP2002308832A (ja) * 2001-04-12 2002-10-23 Nitto Denko Corp 重合性液晶化合物および光学フィルム
JP2004029743A (ja) * 2002-04-23 2004-01-29 Nitto Denko Corp 偏光素子、偏光光源およびそれらを用いた画像表示装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH06281814A (ja) * 1993-01-11 1994-10-07 Philips Electron Nv コレステリック偏光子及びその製造方法
JPH1180733A (ja) * 1997-06-19 1999-03-26 Consortium Elektrochem Ind Gmbh 光重合可能なコレステリック液晶のコレステリック反射帯域を拡張する方法およびこの方法により製造した光学素子
JP2002286935A (ja) * 2001-03-28 2002-10-03 Dainippon Printing Co Ltd 円偏光制御光学素子及びその製造方法
JP2002308832A (ja) * 2001-04-12 2002-10-23 Nitto Denko Corp 重合性液晶化合物および光学フィルム
JP2004029743A (ja) * 2002-04-23 2004-01-29 Nitto Denko Corp 偏光素子、偏光光源およびそれらを用いた画像表示装置

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP2042895A1 (fr) * 2006-07-13 2009-04-01 Zeon Corporation Procédé de fabrication d'une feuille d'isolation à la lumière polarisée circulairement, et appareil de formation du film de revêtement
EP2042895A4 (fr) * 2006-07-13 2012-07-11 Zeon Corp Procédé de fabrication d'une feuille d'isolation à la lumière polarisée circulairement, et appareil de formation du film de revêtement

Also Published As

Publication number Publication date
JP2004318062A (ja) 2004-11-11
JP4293882B2 (ja) 2009-07-08
TW200428041A (en) 2004-12-16
TWI341928B (fr) 2011-05-11

Similar Documents

Publication Publication Date Title
US7393570B2 (en) Broad-band-cholesteric liquid-crystal film, process for producing the same, circularly polarizing plate, linearly polarizing element, illiminator, and liquid-crystal display
JP2004264322A (ja) 広帯域コレステリック液晶フィルムおよびその製造方法、円偏光板、直線偏光子、照明装置および液晶表示装置
JP4247894B2 (ja) 光学素子、集光バックライトシステムおよび液晶表示装置
JP4416119B2 (ja) 広帯域コレステリック液晶フィルムの製造方法
JP4293888B2 (ja) 広帯域コレステリック液晶フィルムの製造方法、円偏光板、直線偏光素子、照明装置および液晶表示装置
WO2004088366A1 (fr) Procede de production d'un film a cristaux liquides cholesteriques a large bande, plaque de polarisation circulaire, polariseur lineaire, appareil d'eclairage et afficheur a cristaux liquides
JP4008417B2 (ja) 広帯域コレステリック液晶フィルム、その製造方法、円偏光板、直線偏光子、照明装置および液晶表示装置
JP2004302075A (ja) 広帯域コレステリック液晶フィルムの製造方法、円偏光板、直線偏光素子、照明装置および液晶表示装置
JP2006133385A (ja) 平行光化システム、集光バックライトシステム及び液晶表示装置
KR100910954B1 (ko) 광학소자, 집광 백라이트 시스템 및 액정 표시 장치
JP4323205B2 (ja) 液晶フィルムの製造方法
JP2005308988A (ja) 円偏光型反射偏光板、光学素子、集光バックライトシステムおよび液晶表示装置
JP2005258192A (ja) 広帯域コレステリック液晶フィルムの製造方法
JP4133839B2 (ja) 広帯域コレステリック液晶フィルムの製造方法
JP2006098946A (ja) 光学素子、偏光素子、照明装置および液晶表示装置
JP2006024519A (ja) 直下型バックライトおよび液晶表示装置
JP2004212911A (ja) 広帯域コレステリック液晶フィルムの製造方法、円偏光板、直線偏光子、照明装置および液晶表示装置
JP2004219559A (ja) 偏光素子および液晶表示装置
JP2005351956A (ja) 光学素子、集光バックライトシステムおよび液晶表示装置
JP2009128793A (ja) 傾斜配向位相差フィルムの製造方法
JP2004219522A (ja) 広帯域コレステリック液晶フィルム、その製造方法、円偏光板、直線偏光子、照明装置および液晶表示装置
WO2004063780A1 (fr) Film a cristaux liquides cholesterique a bande large et procede de production associe, plaque a polarisation circulaire, element a polarisation lineaire, illuminateur, et affichage a cristaux liquides
JP4397757B2 (ja) 光学素子、集光バックライトシステムおよび液晶表示装置
JP2004212909A (ja) 広帯域コレステリック液晶フィルムの製造方法、円偏光板、直線偏光子、照明装置および液晶表示装置
JP2005128214A (ja) 光学素子、集光バックライトシステムおよび液晶表示装置

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

DPEN Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed from 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
122 Ep: pct application non-entry in european phase