Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
  • C08J5/18—Manufacture of films or sheets
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F10/02—Ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/16—Copolymers of ethene with alpha-alkenes, e.g. EP rubbers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
  • C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
  • C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F110/00—Homopolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F110/02—Ethene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2323/00—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers
  • C08J2323/02—Characterised by the use of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Derivatives of such polymers not modified by chemical after treatment
  • C08J2323/04—Homopolymers or copolymers of ethene
  • C08J2323/08—Copolymers of ethene
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31855—Of addition polymer from unsaturated monomers
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31855—Of addition polymer from unsaturated monomers
  • Y10T428/31909—Next to second addition polymer from unsaturated monomers

Definitions

• the present invention relates to a film with good mechanical properties, in particular to a film of a bimodal terpolymer with a good impact strength.
• Bimodal ethylene polymers are well known and can be used for many applications as pressure pipes, cable jacketing, wire coating, pipe coating, blow moulding and films.
• Such polymers consist in general of two polymers one having a relatively high molecular weight and one having a relatively low molecular weight.
• the proper- ties of these polymers are a good tensile strength, a high ultimate elongation, a good puncture resistance and a good impact strength.
• Document EP-0 369 436 A2 is related to a process for the in-situ blending of polymers comprising continuously contacting under polymerisation conditions, a mixture of ethylene and at least one ⁇ -olefin having at least three carbon atoms.
• the final polymer comprises a low melt index copolymer and a high melt index copolymer whereby both copolymers consist of ethylene and an ⁇ -olefin.
• the document is related to a process and does not show any specific reasons why the polymers would be useful in manufacturing films.
• Document EP-0 435 624 Al provides a low density polyethylene having a rela- tively broad molecular weight distribution and therefore good processability at high molecular weights.
• the polymer used as a film is produced by blending the first polymer component of high molecular weight with a second polymer component of low molecular weight, whereby both polymer components having substantially the same melt index corrected density or a dissimilar corrected density.
• Document EP-0 691 367 Bl is related to an extruded film of ethylene copoly- mers prepared in a series of polymerisation reactors, whereby a high molecular weight fraction consists of a copolymer of ethylene and ⁇ -olefm comonomer(s) having 5 to 12 carbon atoms and a low molecular weight fraction consists of a copolymer of ethylene, 1-butene and optionally an ⁇ -olef ⁇ n comonomer(s) having 3 to 12 carbon atoms.
• WO-97/49476 is related to cable constructions, particularly jacketing for telecommunication cables. Best mechanical results for such cable jackets can be obtained when 1-butene is used as a comonomer in the low molecular weight fraction and 1-hexene in the high molecular fraction or vice versa.
• the prior art document WO-97/49476 does not disclose films and properties that are important in the production.
• the present invention is based on the finding that these objects can be solved by a film of a bimodal terpolymer comprising a low molecular weight polymer which contains at least ethylene and a high molecular weight polymer which is a binary copolymer or a terpolymer depending on the composition of the low molecular weight polymer.
• bimodal terpolymer comprising a) a low molecular weight homopolymer of ethylene and
• a low molecular weight polymer which is a binary copolymer of ethylene and a C 4 to C i2 ⁇ -olefin and
• a high molecular weight polymer which is either a binary copolymer of ethylene and 1-butene, if the low molecular weight polymer of a) is a binary copolymer of ethylene and a C 6 to C 12 ⁇ -olefin, or a terpolymer of ethylene, 1-butene and a C 6 to C 12 ⁇ -olefm.
• the present invention provides a film of a bimodal, high molecular weight terpolymer with at least a broad molecular weight distribution and excellent impact strength, especially a film with at least a high dart drop value
• the present invention provides a film of a bimodal, medium molecular weight terpolymer with a relatively narrow molecular weight distribution and moderate dart drop value accompanied by good optical property.
• the present invention provides a process for producing the film of a bimodal terpolymer with the above mentioned properties.
• the film of the first embodiment is a bimodal, high molecular weight terpolymer with a very broad molecular weight distribution whereby its remarkable feature is the excellent impact strength, especially a film with a very high dart drop value.
• a film with such properties is characterized in that the film consists of either a bimodal terpolymer comprising
• a low molecular weight polymer which is a binary copolymer of ethylene and a C to C 12 ⁇ -olefin and
• a high molecular weight polymer which is either a binary copolymer of ethylene and 1-butene, if the low molecular weight polymer of a) is a binary copolymer of ethylene and a C 6 to C 12 ⁇ -olefin, or a terpolymer of ethylene, 1-butene and a C 6 to C ⁇ 2 ⁇ -olefin.
• the expression of modality of a polymer refers to the form of its molecular weight distribution (MWD) curve, i.e. the appearance of the graph of the polymer weight fraction as a function of its molecular weight. If the polymer is produced in a sequential step process i.e. by utilizing reactors coupled in series and using different conditions in each reactor, the different polymer fraction produced in the different reactors will each have their own molecular weight distribution which may considerably differ from each another.
• MWD molecular weight distribution
• the molecular weight distribution curve of the resulting final polymer can be looked at as the supe ⁇ osition of the molecular weight distribution curve of the polymer fractions which will accordingly show two or more distinct maxima or at least be distinctly broadened compared with the curves of the individual fractions.
• a polymer showing such a molecular weight distribution curve is called bimodal or multimodal, respectively.
• Multimodal, especially bimodal, polymers can be produced according to several processes which are described e.g. in EP-0 517 868 Bl or WO-A-96/18662.
• the multimodal polyethylene preferably is produced in a multi-stage process in a multi-step reaction sequence such as described in EP-0 517 868 Bl and WO-A- 96/18662. The contents of these documents are included herein by reference.
• ethylene is polymerized in a loop reactor in the liquid phase of an inert low boiling hydrocarbon medium. Then the reaction mixture is discharged from the loop reactor and at least the inert hydrocarbon medium is removed from the reaction mixture and the polymers transferred into one or more gas phase reactors where the polymerisation is continued in the presence of gaseous ethylene.
• the multimodal polymer produced according to this process has a superior homogenity with respect to the distribution of the different polymer fractions which cannot be obtained e.g. by a polymer mix.
• the catalyst for the production of the ethylene polymer may be e.g. a chromium, a Ziegler-Natta-type or a single-site catalyst.
• a Ziegler-Natta catalyst like one of those disclosed in EP-A-0 688 794 and EP-A-0 949 274 or a single-site catalyst like one of those disclosed in WO-A-97/28170 is used.
• Multimodal polymers in particular ethylene polymers, show superior mechanical properties such as low shrinkage, low abrasion, hard surface and good barrier properties accompanied by a good processability.
• the bimodal te ⁇ olymer according to the first embodiment comprises a low molecular weight fraction (LMW) of a homopolymer of ethylene or a binary copolymer of ethylene and a C to C ⁇ 2 ⁇ -olefin and a high molecular weight frac- tion (HMW) of a binary copolymer of ethylene and 1 -butene if the low molecular weight polymer of a) is a binary copolymer of ethylene and a C 6 to C 12 ⁇ -olefin, or a te ⁇ olymer of ethylene, 1-butene and a C 6 to C ⁇ 2 ⁇ -olefin.
• LMW low molecular weight fraction
• HMW high molecular weight frac- tion
• homopolymer of ethylene refers to a polyethylene that consists substantially, i.e. to at least 98 % by weight, preferably at least 99 % by weight, more preferably at least 99.5 % by weight, most preferably at least 99.8 % by weight of ethylene.
• the impact strength characterizes the material behaviour and a high speed loading (impact). Pendulum and falling weight type testers are applied here. Specimen can be either plaques, notched or unnotched bars or parts of finished prod- ucts. There are several impact methods like “Cha ⁇ y impact test”, “Izod impact test”, “tensile impact test”, “instrumented puncture test” and the “dart drop test”. Generally, an impact test shows the energy which is needed to break or puncture specimen under specified conditions. By the dart drop test the dart drop value is determined to verify the impact strength of a film. A free-falling dart of specific weight and geometry is therefore from a specified height dropped onto a film. The weight at which 50 % of the film samples break is reported as the dart drop value. All dart drop values are measured by method ISO 7765-1.
• the film according to the first embodiment if extruded on a Collin film line into a thickness of 25 ⁇ m with a die diameter of 30 mm, a die gap of 0.75 mm, a BUR (blow-up ratio) of 3.2 and a frost line height of 160 mm, has a dart drop value preferably of at least 1,400 g, more preferably of at least 1,500 g and most preferably of at least 1,700 g.
• the bimodal te ⁇ olymer composition comprises, as stated above, a low molecular weight copolymer fraction and a high molecular weight copolymer fraction.
• the low molecular copolymer fraction contains, provided that a binary copolymer is used, a C 4 to C 12 ⁇ -olefin.
• the C 4 to C[ 2 ⁇ -olefin of the low mo- lecular weight copolymer fraction is selected from the group of 1-butene, 1- hexene, 4-methyl-l-pentene, 1-octene and 1-decene.
• the C 6 to C ⁇ 2 ⁇ -olefin of the high molecular weight copolymer fraction is preferably selected from the group of 1-hexene, 4-methyl-l-pentene, 1-octene and 1-decene.
• the weight average molecular weight of the bimodal te ⁇ olymer is preferably between 190,000 to 400,000 g/mol, more preferably between 200,000 to 300,000 g/mol.
• the low molecular weight polymer fraction has a weight average molecular weight preferably of 4,500 to 55,000 g/mol, more preferably of 5,000 to 50,000 g/mol and the high molecular weight polymer has a weight average mo- lecular weight preferably of 450,000 to 1,000,000 g/mol, more preferably of 500,000 to 1,000,000 g/mol.
• the molecular weight distribution of the polymer is further characterized by the way of its melt flow rate (MFR) according to ISO 1133 at 190°C.
• MFR melt flow rate
• the melt flow rate is preliminary depending on the mean molecular weight. This is, because long, well-packed molecules give the material a lower flow tendency than short, less-packed molecules.
• An increase in molecular weight means a decrease in MFR value.
• the melt flow rate is measured in g/lOmin of the polymer discharge under a specified temperature and pressure condition and is a measure of the viscosity of the polymer, which in turn for each type of polymer is mainly influenced by its molecular weight distribution, but also by its degree of branching etc.
• the melt flow rate measured under a load 2.16 kg (ISO 1133) is denoted as MFR 2 .
• the melt flow rate measured with 21.6 kg is denoted as MFR 2 [.
• the final bimodal te ⁇ olymer has a melt flow rate MFR 21 preferably of 7 to 40 g/lOmin, more preferably of 15 to 30 g/lOmin.
• the low molecular weight polymer has a melt index MFR 2 preferably of 200 to 800 g/lOmin, more preferably of 300 to 600 g/lOmin.
• melt flow rate and the density of the material are decisive for strength properties, while the density only is decisive for the melting point, surface hardness, permeability and water abso ⁇ tion.
• the density of the final bimodal te ⁇ olymer is preferably of 910 to 950 kg/m 3 , more preferably of 915 to 940 kg/m 3 .
• the density of the low molecular weight polymer is preferably of 940 to 980 kg/m 3 , more preferably of 945 to 975 kg/m 3 .
• the film of the bimodal te ⁇ olymer according to the present invention consists preferably in 30 to 60 %, more preferably 35 to 50 % and most preferably 38 to 45 % by weight of low molecular weight copolymer with regard to the total composition.
• the overall comonomer content in the total polymer is 1 to 7 % by mol, preferably 2 to 6 % by mol and in the low molecular weight polymer is the comonomer content 0 to 2.5 % by mol, preferably 0 to 2 % by mol.
• the high molecular weight polymer is the comonomer content 2.5 to 11 % by mol, preferably 3 to 10 % by mol.
• the molecular weight of the high molecular weight copolymer fraction should be such that when the low molecular weight copolymer fraction has the melt index and density specified above, the final bimodal te ⁇ olymer has the melt index and density as discussed above.
• the bimodal te ⁇ olymer has a melt flow rate MFR 2 ⁇ of about 10 to 40 g/lOmin and a density of 918 to 928 kg/m 3 .
• the bimodal te ⁇ olymer has a melt flow rate MFR 2 ⁇ of about 7 to 30 g/lOmin and a density of 930 to 940 kg/m 3 .
• the bimodal te ⁇ olymer has a melt flow rate MFR 2 ⁇ of about 7 to 20 g/lOmin and a density of 940 to 950 kg/m 3 .
• the bimodal te ⁇ olymer comprises a low molecular weight copolymer fraction consisting in a binary copolymer of ethylene and a C 6 to 2 ⁇ -olefin and a high molecular weight copolymer fraction consisting in a binary copolymer of ethylene and 1-butene.
• the melt flow rate MFR 2 ⁇ of the final bimodal te ⁇ olymer is of about 10 to 40 g/lOmin and the density amounts to 918 to 928 kg/m 3 , whereby the low molecular weight copolymer fraction has a melt flow rate MFR 2 of 200 to 500 g/lOmin and a density of 945 to 955 kg/m 3 .
• a bimodal te ⁇ olymer with properties as stated in this paragraph has, as a film, a dart drop value preferably of at least 1400 g, more preferably of at least 1500 g, if the film is extruded on a Collin film line into a thickness of 25 ⁇ m, with a die diameter of 30 mm, a die gap of 0.75 mm, a BUR (blow-up ratio) of 3.2 and a frost line height of 160 mm.
• the bimodal te ⁇ olymer comprises a low mo- lecular weight copolymer fraction consisting in a binary copolymer of ethylene and a C 6 to 2 ⁇ -olefin and a high molecular weight copolymer fraction consisting in a binary copolymer of ethylene and 1-butene.
• the melt flow rate MFR 2 ⁇ of the final bimodal te ⁇ olymer is about 7 to 30 g/lOmin and the density amounts to 930 to 940 kg/m , whereby the low molecular weight copolymer fraction has a melt flow rate MFR 2 of 200 to 800 g/lOmin and a density of 955 to 965 kg/m 3 .
• the amount of the low molecular weight copolymer fraction is 38 to 43 % of the total composition and the amount of high molecular weight copolymer fraction is 57 to 62 % of the total composition.
• the bimodal te ⁇ olymer comprises a low molecular weight copolymer fraction consisting in a homopolymer of ethylene or a binary copolymer of ethylene and 1-butene and a high molecular weight copolymer fraction consisting in a te ⁇ olymer of ethylene, 1-butene and a C 6 to 2 ⁇ -olefin.
• the melt flow rate MFR 2 ⁇ of the final bimodal te ⁇ olymer is about 7 to 30 g/lOmin and the density amounts to 930 to 940 kg/m 3 , whereby the low molecular weight copolymer fraction has a melt flow rate MFR 2 of 200 to 800 g/lOmin and a density of 955 to 975 kg/m 3 .
• the amount of the low molecular weight copolymer fraction is 38 to 43 % of the total composition and the amount of high molecular weight copolymer fraction is 57 to 62 % of the total composition.
• the film of the second embodiment is a bimodal, high molecular te ⁇ olymer with a broad molecular weight distribution whereby its remarkable feature is the excellent impact strength, especially a film with a high dart drop value. Furthermore, the film of the second embodiment has higher stiffness and moisture properties than those of the first and third embodiment, due to the higher density of the film. A film with such properties is characterized in that the film consists of
• the bimodal te ⁇ olymer of the second embodiment can be produced in the same manner as already described in the first embodiment. This relates also to the catalyst types which can be used.
• homopolymer of ethylene refers to a polyethylene that consists substantially, i.e. to at least 98 % by weight, preferably at least 99 % by weight, more preferably at least 99.5 % by weight, most preferably at least 99.8 % by weight of ethylene.
• the C 6 to C 12 ⁇ -olefin is selected from the group of 1-hexene, 4- methyl-1-pentene, 1-octene and 1-decene.
• the film according to the second embodiment if extruded on a CoUin film line into a thickness of 25 ⁇ m, with a die diameter of 30 mm, a die gap of 0.75 mm, a BUR (blow-up ratio) of 3.2 and a frost line height of 160 mm, has a dart-drop value of at least 180 g, preferably of at least 200 g.
• the weight average molecular weight of the bimodal te ⁇ olymer is between 240,000 to 500,000 g/mol, preferably 250,000 to 400,000 g/mol.
• the low molecular weight polymer fraction has a weight average molecular weight preferably of 4,500 to 55,000 g/mol, more preferably of 5,000 to 50,000 g/mol and the high molecular weight polymer has a weight average molecular weight preferably of 450,000 to 1,000,000 g/mol, more preferably of 500,000 to 1,000,000 g/mol.
• the final bimodal te ⁇ olymer has a melt flow rate MFR 2 ⁇ preferably of 2 to 25 g/lOmin, more preferably of 3 to 20 g/lOmin.
• the low molecular weight polymer has a melt index MFR 2 preferably of 300 to 1,200 g/lOmin, more preferably of 300 to 600 g/lOmin.
• the density of the final bimodal te ⁇ olymer is preferably of 935 to 970 kg/m 3 , more preferably of 940 to 965 kg/m 3 .
• the density of the low molecular weight polymer is preferably of 970 to 980 kg/m 3 , more preferably of 972 to 978 kg/m 3 , most preferably 975 kg/m 3 .
• the film of the bimodal te ⁇ olymer according to the present invention consists preferably in 30 to 60 %, more preferably 35 to 50 % and most preferably 38 to 45 % by weight of low molecular weight copolymer with regard to the total composition.
• the overall comonomer content in the total polymer is 0.5 to 2.5 % by mol, pref- erably 0.5 to 2.5 % by mol and in the high molecular weight polymer is the comonomer content 0.5 to 3.5 % by mol, preferably 0.7 to 3.0 % by mol.
• the molecular weight of the high molecular weight copolymer fraction should be such that when the low molecular weight copolymer fraction has the melt index and density specified above, the final bimodal te ⁇ olymer has the melt index and density as discussed above.
• the bimodal te ⁇ olymer has a melt flow rate MFR 2 ⁇ of about 3 to 20 g/lOmin and a density of 955 to 965 kg/m .
• the bimodal te ⁇ olymer comprises a low molecular weight copolymer fraction consisting of a homopolymer of ethylene and a high molecular weight copolymer fraction consisting in a te ⁇ olymer of ethylene, 1- butene and a C 6 to C ⁇ 2 ⁇ -olefin.
• the melt flow rate MFR 2 ⁇ of the final bimodal te ⁇ olymer is about 3 to 20 g/lOmin and the density amounts to 940 to 950 kg/m 3 , whereby the low molecular weight copolymer fraction has a melt flow rate MFR 2 of 300 to 1200 g/lOmin.
• a bimodal te ⁇ olymer with properties as stated in this paragraph has, as a film, a dart drop value preferably of at least 190 g, more preferably of at least 200 g, if the film is extruded on a Collin film line into a thickness of 25 ⁇ m, with a die diameter of 30 mm, a die gap of 0.75 mm, a BUR (blow-up ratio) of 3.2.
• the bimodal te ⁇ olymer comprises a low molecular weight copolymer fraction consisting in a homopolymer of ethylene and a high molecular weight copolymer fraction consisting in a te ⁇ olymer of ethylene, 1-butene and a C 6 to C] 2 ⁇ -olefin.
• the melt flow rate MFR 2 ⁇ of the final bimodal te ⁇ olymer is about 3 to 20 g/lOmin and the density amounts to 955 to 965 kg/m 3 , whereby the low molecular weight ethylene polymer fraction has a melt flow rate MFR 2 of 300 to 1200 g/lOmin.
• the amount of the low molecular weight copolymer fraction is 38 to 43% of the total composition and the amount of high molecular weight copolymer fraction is 57 to 62 % of the total composi- tion.
• the film of the third embodiment consists in a medium molecular weight polymer having a relative narrow molecular weight distribution, whereby the film has moderate dart drop value accompanied by good optical properties.
• These films are mainly used in packaging where the strength is not a decisive factor but transparency is important.
• the bimodal te ⁇ olymer of the third embodiment can be produced in the same manner as already described in the first embodiment. This relates also to the catalyst types which can be used.
• the bimodal te ⁇ olymer composition comprises as stated above a low molecular copolymer fraction and a high molecular copolymer fraction.
• the low molecular copolymer fraction contains a C 4 to C ⁇ 2 ⁇ -olefin, which is preferably selected from the group of 1-butene, 1-hexene, 4-methyl-l-pentene, 1-octene and 1- decene.
• the C 6 to C] 2 ⁇ -olefin of the high molecular weight copolymer fraction is preferably selected from the group of 1-hexene, 4-methyl-l-pentene, 1-octene and 1-decene.
• the film according to the third embodiment if extruded on a Collin film line into a thickness of 25 ⁇ m, with a die diameter of 60 mm, die gap of 1.5 mm, BUR (blow-up ratio) of 2 and a frost line height of 120 mm, has a dart-drop value preferably over 50 g, more preferably over 60 g and most preferably over 63 g.
• the film with a dart-drop value as stated in the above paragraph has pref- erably haze value equal or less than 20, more preferably equal or less than 16, and has preferably a gloss value of at least 60, more preferably of at least 73.
• the weight average molecular weight of the bimodal te ⁇ olymer is between 110,000 to 210,000 g/mol, preferably 120,000 to 200,000 g/mol.
• the low molecular weight polymer fraction has a weight average molecular weight prefera- bly of 25,000 to 110,000 g/mol, more preferably of 30,000 to 100,000 g/mol and the high molecular weight polymer has a weight average molecular weight preferably of 100,000 to 400,000 g/mol, more preferably of 150,000 to 370,000 g/mol.
• the final bimodal te ⁇ olymer has a melt flow rate MFR 21 preferably of 15 to 80 g/lOmin, more preferably of 20 to 70 g/lOmin.
• the low molecular weight polymer has a melt index MFR 2 preferably of 1 to 50 g/lOmin, more preferably of 2 to 20 g/10min.
• the density of the final bimodal te ⁇ olymer is preferably of 900 to 935 kg/m 3 , more preferably of 915 to 930 kg/m and in particular 920 to 925 kg/m .
• the density of the low molecular weight polymer is preferably of 925 to 950 kg/m 3 , more preferably of 930 to 940 kg/m 3 .
• the film of the bimodal te ⁇ olymer according to the third embodiment consists preferably in 30 to 60 %, more preferably 35 to 50 % and most preferably 38 to 45 % by weight of low molecular weight copolymer with regard to the total composition.
• the overall comonomer content in the total polymer is 1 to 7 % by mol, preferably 2 to 6 % by mol and in the low molecular weight polymer is the comonomer content 0.5 to 3.5 % by mol, preferably 1 to 3 % by mol.
• the high molecular weight polymer is the comonomer content 3.5 to 10.5 % by mol, preferably 4 to 10 % by mol.
• the molecular weight of the high molecular weight copolymer fraction should be such that when the low molecular weight copolymer fraction has the melt index and density specified above, the final bimodal te ⁇ olymer has the melt index and density as discussed above.
• the bimodal te ⁇ olymer comprises a low molecular weight copolymer fraction consisting in a binary copolymer of ethylene and 1-butene and a high molecular weight copolymer fraction consisting in a terpolymer of ethylene, 1-butene and a C 6 to C ⁇ 2 ⁇ -olefm.
• the melt flow rate MFR 2 of the final bimodal te ⁇ olymer is about 0.5 to 2 g/lOmin and the density amounts to 918 to 928 kg/m 3 , whereby the low molecular weight copolymer fraction has a melt flow rate MFR 2 of 2 to 20 g/lOmin and a density of 930 to 950 kg/m 3 .
• the amount of the low molecular weight copolymer fraction is 38 to 43 % of the total composition and the amount of the high molecular weight copolymer fraction is 57 to 62 % of the total composition.
• composition may also contain antioxidants, process stabilizers, pigments and other additives known in the art.
• stabilizers are hindered phenols, hindered amines, phosphates, phosphites and phosphonites.
• pigments are carbon black, ultra marine blue and titanium dioxide.
• additives examples include clay, talc, calcium carbonate, calcium ste- arate, zinc stearate and antistatic additives like those sold under trademark name "Lankrostat”.
• the bimodal te ⁇ olymers according to all three embodiments may be produced using any known methods where ethylene is polymerized in the presence of a catalyst, preferably a Ziegler-Natta or single-site catalyst. They may be produced by a solution polymerization process, a slurry polymerization process or a gas polymerization process. Preferably, the bimodal te ⁇ olymer is produced in a multi stage process like those disclosed in EP-B-0 517 868 and WO-A-96/18662.
• the polymerization takes place either in the presence of a Ziegler-Natta catalyst like one of those disclosed in EP-A-0 688 794 and EP-A-0 949 274, or in the presence of a single- site catalyst like one disclosed in WO-A-97/28170.
• a Ziegler-Natta catalyst like one of those disclosed in EP-A-0 688 794 and EP-A-0 949 274, or in the presence of a single- site catalyst like one disclosed in WO-A-97/28170.
• the low molecular weight copolymer fraction is produced in one stage of a multi stage polymerization process and the high molecular weight copolymer fraction in another stage of the process. More preferably, the low molecular weight copolymer fraction is produced in a continuously operating loop reactor where ethylene is polymerized in the presence of a polymerization catalyst as stated above and chain transfer agent such as hydrogen.
• the diluent is an inert aliphatic hydrocarbon, preferably isobutane or propane.
• a C 4 to 2 ⁇ -olefin comonomer is preferably added to control the density of the low molecular weight copolymer fraction.
• the hydrogen concentration is selected so that the low molecular weight copolymer fraction has the desired melt flow rate. More preferably, the molar ratio of hydrogen to ethylene is between 0.1 and 1.0 mol/mol, most preferably, between 0.2 and 0.8 mol/mol.
• the target density of the low molecular weight copolymer fraction exceeds 955 kg/m 3
• a preferred range of temperature is then from 90 to 110 °C and the range of pressures is from 50 to 80 bar.
• the slurry is intermittently or continuously removed from the loop reactor and transferred to a separation unit where the hydrocarbons including the eventually used C 4 to C 12 ⁇ -olefin comonomer and especially the chain transfer agents are separated from the polymer.
• the polymer containing the active catalyst is intro- pokerd into a gas phase reactor where the polymerization proceeds in the presence of additional ethylene, 1-butene and optional C 4 to 2 ⁇ -olefin comonomer and optionally chain transfer agent to produce the high molecular weight copolymer fraction.
• the polymer is intermittently or continuously withdrawn from the gas phase reactor and the remaining hydrocarbons are separated from the polymer.
• the polymer collected from the gas phase reactor is the bimodal te ⁇ olymer.
• the conditions in the gas phase reactor are selected so that the ethylene polymer has the desired properties.
• the temperature in the reactor is between 70 and 100 °C and the pressure is between 10 to 40 bar.
• the hydrogen to ethylene molar ratio ranges from preferably 0.0001 to 0.02 mol/mol, more preferably 0.001 to 0.1 mol/mol and the ⁇ -olefin comonomer to ethylene molar ratio ranges from preferably 0.03 to 0.7 mol/mol, more preferably 0.04 to 0.6 mol/mol and most preferably 0.05 to 0.5 mol/mol.
• MFR was measured according to ISO 1133 at 190 °C.
• the load has been indicated as a subscript, i.e. MFR 2 denotes the measurement has been carried out un- der a load of 2.16 kg and MFR 2 ⁇ denotes the measurement has been carried out under a load of 21.6 kg, respectively.
• Flow Rate Ratio is a ratio of two melt flow rates, measured under different loads. The loads are denoted in the subscript. Thus, FRR 21 2 denotes the ratio of MFR 2 ⁇ to MFR 2 .
• Shear Thinning Index (SHI) of polymers has been determined using Rheometrics RDA II Dynamic Rheometer. The measurements have been carried out at 190 °C temperature under nitrogen atmosphere. The measurements give storage modulus (G') and loss modulus (G") together with absolute value of complex viscosity ( ⁇ *) as a function of frequency ( ⁇ ) or absolute value of complex modulus (G*).
• ⁇ *( ⁇ ) is the same as conventional viscosity function (viscosity as a function of shear rate), if frequency is taken in rad/s. If this empiric equation is valid, then absolute value of complex modulus corresponds shear stress in conventional (that is stedy state) viscosity measurements. This means that the function ⁇ *( ⁇ ) is the same as vis- cosity as a function of shear stress.
• viscosity at a low shear stress or ⁇ * at a low G* (which serve as an approximation of so called zero viscosity) is used as a measure of average molecular weight.
• shear thinning that is the decrease of viscosity with G*, gets more pronounced the broader is molecular weight dis- tribution.
• SHI shear thinning index
• ⁇ *o is the zero shear rate viscosity
• storage modulus function, , G'( ⁇ ), and loss modulus function G"( ⁇ ), are obtained as primary functions from dynamic measurements.
• Density was measured from compression moulded specimen at 23 °C in a water bath according to an ultrasound measurement method using Tecrad DS 500 equipment. The method was calibrated with samples having a density deter- minded according to ISO 1183.
• the puncture test was performed as follows. The film was mechanically clamped allowing circular testing area of diameter 50 mm. The film was then punctured by a striker (diameter 20 mm). The force and travel to the puncturing point were measured and the required energy was calculated. Travelling speed of the striker was 200 mm/min.
• the molecular weight distribution is measured by using the size exclusion chromatography (SEC). In the examples this was done by using a Waters 150 CV plus no. 1115. A refractive index (RI) detector and a viscosity detector were used. The instrument was calibrated with a narrow molecular weight distribution polystyrene sample. The columns were 3 HT6E styragel from Waters at an oven temperature of 140 °C.
• SEC size exclusion chromatography
• the slurry was withdrawn from the reactor and introduced into another, 500 dm 3 loop reactor, operated at 80 °C temperature and 42 bar pressure, where additional isobutane, ethylene, 1-hexene and hydrogen were added, so that 32 kg/h of polymer having MFR 2 of 310 g/lOmin and a density of 949 kg/m 3 was with- drawn from the reactor.
• the polymer slurry was led into a flash tank, where the hydrocarbons were removed from the polymer.
• the polymer was then introduced into a fluidized bed gas phase reactor, where additional ethylene and hydrogen together with 1- butene comonomer were introduced.
• the powder was mixed with additives (Ca-stearate, antioxidant and process stabilizer) and compounded in a counterrotating twin screw extruder (JSW C1M90P extruder).
• the pelletized polymer had an MFR 2 ⁇ of 27 g/lOmin and a density of 923 kg/m 3 .
• Example 1 The process of Example 1 was repeated with slightly different process conditions.
• the material property can be found in Table 1.
• Table 1 Properties of the polymers of Examples 1 to 4.
• Example 1 film materials were blown to a film of 25 ⁇ m thickness an a Collin film line, with a die diameter of 30 mm, a die gap of 0.75 mm, a BUR (blow-up ratio) of 3.2 and a frost line height of 160 mm.
• the results are shown in Table 2. They are referred to as Type 1 film materials.
• Table 2 Type 1 film properties for a film prepared on an Collin laboratory line
• Example 1 The process of Example 1 was repeated except that 1-butene was used as a comonomer and propane as a diluent in the loop reactor and a mixture of 1-butene and 1-hexene was used as comonomers in a gas phase reactor.
• the process conditions were set to obtain materials according to Table 3.
• Example 5 The procedure of Example 5 was repeated except that the film thickness was 25 ⁇ m, die diameter 60 mm, die gap 1.5 mm, BUR (blow-up ratio) 2 and frost line height 120 mm, and that the materials of Examples 6 to 7 and Comparative Examples 2 to 3 were used.
• the data is shown in Table 4. These are referred to as Type 2 film materials.
• Table 4 Type 2 film properties an Collin laboratory line
• the slurry was withdrawn from the reactor and introduced into another, 500 dm 3 loop reactor, operated at 95 °C temperature and 60 bar pressure, where additional propane, ethylene and hydrogen were added, so that 32 kg/h of ethylene homopolymer having MFR 2 of 450 g/10 min and density of 975 kg/m 3 was withdrawn from the reactor.
• the polymer slurry was led into a flash tank where the hydrocarbons were removed from the polymer.
• the polymer was then introduced into a fluidized bed gas phase reactor, operated at 75 °C temperature and 20 bar pressure, where additional ethylene and hydrogen, together with 1-butene and 1-hexene comonomers, were introduced. From the gas phase reactor polymer was withdrawn at a rate of 80 kg/h.
• the powder was mixed with additives (Castearate, antioxidant and process stabilizer) and compounded in a counterrotating twin screw extruder JSW CIM90P extruder.
• the palletized polymer had an MFR 2 ⁇ of 7.5 g/10 min and density of 944 kg/m 3 .
• the data can be found in table 5.
• Example 9 The process of Example 9 was repeated except that only 1-butene was used as a comonomer in the gas phase reactor.
• the data can be found in Table 5.
• N.M. denotes fro not measured
• Example 9 The polymers of Example 9 and Comparative Example 4 were blown to films by using the equipment and procedure described in Example 5. The data is shown in Table 6. Table 6: Type 1 film properties on Collin laboratory line

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Manufacturing & Machinery (AREA)
• Engineering & Computer Science (AREA)
• Inorganic Chemistry (AREA)
• Materials Engineering (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Laminated Bodies (AREA)
• Treatments Of Macromolecular Shaped Articles (AREA)

Priority Applications (2)

Applications Claiming Priority (2)

Publications (1)

Family

ID=8185431

Family Applications (2)

Family Applications After (1)

Country Status (13)

Cited By (43)

Families Citing this family (53)

Citations (5)

Family Cites Families (27)

• 2002
  • 2002-02-04 EP EP20020002578 patent/EP1333044B2/en not_active Expired - Lifetime
  • 2002-02-04 DE DE2002602660 patent/DE60202660T3/de not_active Expired - Lifetime
  • 2002-02-04 AT AT02002578T patent/ATE287420T1/de not_active IP Right Cessation
  • 2002-02-04 ES ES02002578T patent/ES2236371T5/es not_active Expired - Lifetime
• 2003
  • 2003-02-03 US US10/503,611 patent/US7524897B2/en not_active Expired - Lifetime
  • 2003-02-03 WO PCT/EP2003/001042 patent/WO2003066698A1/en not_active Ceased
  • 2003-02-03 RU RU2004123882A patent/RU2354669C2/ru active
  • 2003-02-03 AU AU2003206823A patent/AU2003206823A1/en not_active Abandoned
  • 2003-02-03 CN CNB038028557A patent/CN100506868C/zh not_active Expired - Lifetime
  • 2003-02-04 RU RU2004121679A patent/RU2296775C2/ru not_active IP Right Cessation
  • 2003-02-04 CN CNB038032392A patent/CN1304448C/zh not_active Expired - Fee Related
  • 2003-02-04 EP EP20030701623 patent/EP1472298B1/en not_active Expired - Lifetime
  • 2003-02-04 DE DE2003601617 patent/DE60301617T2/de not_active Expired - Lifetime
  • 2003-02-04 PL PL37344503A patent/PL373445A1/xx not_active Application Discontinuation
  • 2003-02-04 US US10/501,625 patent/US7256239B2/en not_active Expired - Lifetime
  • 2003-02-04 KR KR1020047011624A patent/KR100702098B1/ko not_active Expired - Fee Related
  • 2003-02-04 ES ES03701623T patent/ES2244917T3/es not_active Expired - Lifetime
  • 2003-02-04 AU AU2003202712A patent/AU2003202712B2/en not_active Ceased
  • 2003-02-04 JP JP2003566066A patent/JP2005533131A/ja active Pending
  • 2003-02-04 AT AT03701623T patent/ATE304562T1/de not_active IP Right Cessation
  • 2003-02-04 BR BR0307246A patent/BR0307246A/pt not_active IP Right Cessation
  • 2003-02-04 WO PCT/GB2003/000480 patent/WO2003066699A1/en not_active Ceased