WO2003027183A1 - Composition de resine et element comprenant cette composition de resine - Google Patents

Composition de resine et element comprenant cette composition de resine Download PDF

Info

Publication number
WO2003027183A1
WO2003027183A1 PCT/JP2002/009836 JP0209836W WO03027183A1 WO 2003027183 A1 WO2003027183 A1 WO 2003027183A1 JP 0209836 W JP0209836 W JP 0209836W WO 03027183 A1 WO03027183 A1 WO 03027183A1
Authority
WO
WIPO (PCT)
Prior art keywords
resin composition
ink
isobutylene
weight
based polymer
Prior art date
Application number
PCT/JP2002/009836
Other languages
English (en)
French (fr)
Inventor
Naruhiko Mashita
Tadashi Utsunomiya
Youkou Saito
Original Assignee
Bridgestone Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bridgestone Corporation filed Critical Bridgestone Corporation
Priority to DE60227966T priority Critical patent/DE60227966D1/de
Priority to EP02772903A priority patent/EP1431343B1/en
Priority to US10/487,667 priority patent/US7163980B2/en
Priority to JP2003530764A priority patent/JP4532111B2/ja
Publication of WO2003027183A1 publication Critical patent/WO2003027183A1/ja

Description

明細書 樹脂組成物及び該樹脂組成物から構成されてなる部材 技術分野
本発明は、 低硬度で高ロス性 (制振性) 及び耐気体透過性が良好で 、 しかも射出成形性に優れ、 寸法精度が安定した射出成形が可能な樹 脂組成物に関するものである。
本発明はまた、 イ ンクジヱッ トプリ ンタ一用弾性部材、 イ ンク タン ク及びイ ンクジヱッ トプリ ンタ一に関し、 さ らに詳しく は、 記録へッ ドにィ ンクを供給して記録媒体に印字を記録するィ ンクジヱッ トプリ ン夕一などで用いられるィ ンクタンクにおいて、 ィ ンク タンク弁ゃィ ンク タンクのシ一ル部材などと して使用され、 また、 イ ンクジヱッ ト プリ ンター本体部において、 記録へッ ドからイ ンクが洩れるのを防止 するシール部材などと して使用され、 二色成形法による射出成形が可 能で、 かつシール性及びオイルブリ一ド性に優れた材料からなる弾性 部材、 並びにこのものを用いたイ ンクタンク及びイ ンクジヱッ トプリ ン夕一に関するものである。
本発明はまた、 記録媒体駆動装置用ィ ンシュ レーターに関し、 さ ら に詳しく は、 高ロス性 (制振性) 及びオイル保持性が良好で、 低硬度 で、 かつ圧縮永久歪みが小さいなど、 所望の性能を有し、 C D (コ ン ノヽ。ク トディスク) 、 C D— R O M、 光ディスクなどの記録媒体の駆動 装置の制振に好適に使用されるィ ンシユレ一夕一に関するものである, 本発明はまた、 気体気密性及び物質の耐浸透性 · 耐透過性が良好で 、 且つ有害ガスの発生の少ない H D D (ハー ドディスク装置) 用ガス ケッ ト及び該 H D D用ガスケッ トがカバ一と一体的に成形されてなる H D D用カバ——体型ガスケッ 卜に関するものである。
本発明はまた、 H D D用の衝撃吸収材に関し、 特に、 衝撃吸収性に 優れ、 且つガス発生量の少ない H D D用衝撃吸収材に関するものであ る。 背景技術
熱可塑性樹脂は、 射出成形が可能であり、 多岐の分野で使用されて いるが、 使用目的に応じて異なる要求特性に対応するため、 複数の樹 脂を組み合わせて使用することが、 広く行われている。
ゴム系の樹脂を添加して耐衝撃性を向上させるのもその 1例であり 、 ゴム系の樹脂と して、 ブロッ ク共重合体からなる熱可塑性エラス 卜 マーを使用することも試みられている。
かかる熱可塑性エラス トマ一と しては、 例えば、 特開平 8 - 3 0 1 9 5 5号公報ゃ特開平 1 1 — 2 4 6 7 3 3号公報などに開示されてい るイ ソブチレン系ブロッ ク共重合体からなる熱可塑性エラス トマ一が あるが、 これらの熱可塑性エラス トマ一を使用した樹脂組成物は、 硬 度、 ロス特性、 耐気体透過性、 射出成形性等の点で、 必ずしも満足し 得るものではなかった。
また、 イ ンクジエツ トプリ ンター用弾性部材、 記録媒体駆動装置 用イ ンシユ レ一夕一、 H D D用ガスケッ ト及び H D D用衝撃吸収材 と して、 熱可塑性エラス トマ一を使用した樹脂組成物から構成され てなるものが提案されているが、 各々次のよ うな問題を有しており 、 これらの部材を構成するに適した樹脂組成物が求められている。 先ず、 イ ンクジヱ ッ トプリ ンター用弾性部材について述べる。
従来、 イ ンクジヱッ トプリ ンターにおいては、 イ ンクが充填される ィ ンク室と、 記録へッ ド部にィ ンクを供給するィ ンク供給部とを有す るイ ンク タ ンクが装着されている。 そ して、 このイ ンク タ ンクの形式 と しては、 例えばキヤ リ ッジに対し固定的に取付けられた記録へッ ド に対して、 装置内に配置されたチューブを介してイ ンクを供給するよ うに構成され、 装置に対して着脱自在なもの、 或いは記録へッ ドとー 体的に構成され、 キャ リ ッジに対して着脱自在なものなどがある。 前者のィ ンクタ ンクにおいては、 記録へッ ドに対して水頭差を設け ることで、 一方、 後者においては、 イ ンクタンク側に負圧発生源を備 えることで、 記録へッ ドにィ ンクを供給する形態をとつている。
近年、 装置の小型化ゃメ ンテナンスの容易性などの面から、 後者の 形態のィ ンク タンクを.採用する装置が多く提案されている。
これらのイ ンクジヱッ トプリ ンタ一用のイ ンク タンクには、 記録時 に記録へッ ドから吐出されるイ ンク量に見合ったィ ンクを良好に供給 できること、 及び、 非記録時においては吐出口からのイ ンクの洩れな どがないことが要求される。
このような要求を満たすイ ンクタンクと しては、 例えば記録へッ ド とイ ンク タンクとが一体化され、 キャ リ ッジに対して着脱自在とされ たカート リ ッジであって、 イ ンク タンク内に吸収体 (発泡体) が充填 されているものがある。 このよ うに、 イ ンクタンク内に吸収体を充填 することで、 吸収体の毛細管力によってイ ンク タ ンク内でイ ンクが保 持され、 記録へッ ドのィ ンク吐出部で安定したィ ンクのメニスカスを 維持することができる。 この場合、 イ ンクタンク内ほぼ全体に吸収体 が充填されていることが必要である。 そして、 吸収体が保持可能なィ ンク最大量よ り もやや少ないィ ンク量を吸収体に保持させておく こと によ り、 毛細管力を利用して内部負圧を発生させている。 したがって 、 記録へッ ド及びィ ンクタンクに振動などの機械的入力や温度変化な どの熱的入力があった場合でも、 記録へッ ドの吐出部ゃィ ンク タンク の大気連通部からのィ ンクの洩出が少なく、 安定したイ ンクの保持を 行う ことができる。
しかしながら、 イ ンクタンク内全体に吸収体を充填した方式は、 ィ ンクの消費に伴って吸収体の負圧が大き く なり、 記録へッ ドに供給さ れずにィ ンク タンク内に残るィ ンク量が多く、 使用効率が悪いという 問題を有している。 このような問題を解決するために、 例えばイ ンク タ ンク内を、 下部 に通孔を備えた壁によ りィ ンク溜めと空洞とに分離し、 この通孔にァ ンブレラチヱッ クバルブを移動可能に設けて、 記録へッ ドのィ ンク圧 が低下した時点で、 バルブを開弁してィ ンク溜めのィ ンクを空洞に排 5 出させて記録へッ ドに供給するように構成したィ ンクジヱッ 卜記録へ ッ ド用のイ ンクカー ト リ ツジが提案されている (特開昭 6 2— 2 3 1 7 5 9号公報) 。
これによれば、 カー ト リ ツジ内に吸収体を収容する必要がなく なる ため、 タンク内の実質的ィ ンク収容量を大きくすることが可能となる
1 0 が、 一般的にアンブレラチヱッ クバルブは、 記録ヘッ ドのイ ンクの供 給を精密に調整するには、 そのオフセッ ト量が大きすぎ、 イ ンク供給 量に変動を来して印字品質の低下を招く という大きな問題がある。 一方、 アンブレラチェッ クバルブが閉弁した状態では、 イ ンク溜部 と記録へッ ドとが完全に遮断されるため、 環境温度の変化で空洞のィ i s ンクが 2 〜 5 %程度体積膨張した場合には、 空洞の圧力が上昇して、 記録へッ ドとの接続口のシールを破損してイ ンクが漏洩したり、 また 記録へッ ドに装着されている状態では、 この圧力がそのまま記録へッ ドに作用して、 記録へッ ドとイ ンクタ ンクとの間での負圧を維持でき なく なって、 記録へッ ドからイ ンクが漏洩するという問題がある。
2 0 さ らに、 このアンブレラチヱッ クバルブは、 記録ヘッ ドへの安定な ィ ンク供給を行うために維持すべき数十 m m水柱程度の圧力差では閉 弁力が弱いため、 キヤ リ ツジの移動によるィ ンクの揺動に応動して開 弁する恐れがあり、 印字の安定性に劣るという問題がある。
そこで、 このようなアンプレラチエツ クバルブを装着したィ ンクタ
2 5 ンクが持つ問題を解決するために、 例えばィ ンク室とィ ンク供給部と を分割する位置に設けられ、 かつ該イ ンク室とィ ンク供給部との圧力 差によ り移動し、 ィ ンク室に充填されたィ ンクを記録へッ ド部に供給 するイ ンク タ ンク弁の使用が試みられている (特開平 8— 1 7 4 8 6 0号公報) 。
このよ うなイ ンク タ ンク弁を装着する ことによ り、 記録へッ ドとの 間の微小な差圧に確実に応動し、 かつキヤ リ ッジの移動によるィ ンク の揺動に左右されることなく、 記録へッ ドとの間で印字に適した負圧 を維持して記録へッ ドに確実にィ ンクを供給でき、 さ らには温度変化 によるイ ンク供給口からのイ ンクの漏洩や、 記録へッ ドからのイ ンク の漏洩を防止することができる。
このィ ンク タ ンク弁においては、 通常、 弾性材料が用いられており 、 また、 例えばプラスチッ ク基材に弾性材料を接着したものなどが用 いられている。 そして、 従来、 この弾性材料と しては、 一般に熱硬化 性ゴムが使用されていた。 しかしながら、 この熱硬化性ゴムでは、 プ ラスチッ クとの二色成形法による射出成形が困難であり、 上記弁を作 製するのに製造コス 卜が高くつく上、 低硬度化した材料で所望形状の 部材を成形、 加硫するのが困難であるという問題があつた。
一方、 取替え用ィ ンク タ ンクには、 従来、 ィ ンク供給口にポリ ウ レ 夕ンフォームなどのフォーム状の弾性部材を取り付けることによ り、 ィ ンクが漏洩するのを防止しているが、 長期間使用しているとィ ンク が保持できない場合があり、 耐久性に優れた弾性部材が求められてい た。
また、 イ ンクジエツ トプリ ンターにおいて、 プリ ンタ一が未動作の 場合、 記録へッ ドはィ ンクジエツ トプリ ンター本体部の端で待機させ るが、 このよ うな待機の際に記録へッ ドからイ ンクが洩れることを防 止するため、 上記プリ ンター本体部に設けた凹部に沿って配置された シール部材上に記録へッ ドを収容している。 通常この部材と しては熱 硬化性ゴムが使用されているが、 この熱硬化性ゴムには上記と同様の 問題があつた。
また、 特開平 2 0 0 0— 9 7 8号公報に見られるよ うに、 スチレン 系エラス 卜マーを用いたイ ンクジヱッ 卜プリ ンター用弾性部材に関す る出願があるが、 該公報に記載されているスチレン系エラス トマ一は
、 S E P S, S E B S , S B S , S I Sなど、 ソフ トセグメ ン トがポ リエチレンプロピレン, ポリエチレンブチレン, ポリブタジェン, ポ リイ ソプレンのものである。 汎用のゴム材料に関する知見と してよ く 知られるよ うに、 これらのポリマーは、 その気体透過性、 湿度透過性 が必ずしも優れた物ではなく、 よ り低い透気体性能、 透湿度性能を求 められる場合には、 満足な性能を発現しない場合があつた。
次いで、 記録媒体駆動装置用ィ ンシュ レーターについて述べる。
C D、 C D— R O M、 光ディスクなどの情報が書き込まれた記録媒 体の駆動装置は、 装置内部に記録媒体を記録及び/又は再生する記録 媒体駆動部を備えており、 この記録媒体駆動部には記録媒体を駆動す るモータとか、 記録媒体を記録及び/又は再生するピッ クアップ手段 などを搭載しているが、 これらは機構上、 外部及び内部からの振動に 弱い。 このため、 振動絶縁を目的と して、 熱可塑性ゴム等からなるィ ンシュレー夕一が装着されている。
従来、 この記録媒体駆動装置用ィ ンシュレーターの材料と しては、 シ リ コーンゴム、 ブチルゴム等の一般ゴム材料やゲル、 オイルダンパ 一等が使用されている。 これらのうちゴム材料は、 その硬度が、 J I S A硬度で 2 0〜 5 0 ° 前後である。
これらのゴム材料のロスファ ク タ一はあま り大き く ないため、 共振 周波 数周辺における振動伝達率が高く、 特に一般に低速回転で行われ る記録媒体への書き込みの際に制振が十分でなく なり、 エラーの原因 となることが多かった。
このため、 ゴム材料を制振材料と して用いる場合には、 肉薄成形な どの方法によ り複雑な形状に成形し、 材料の特性ではなし得ない低周 波数域における制振性を、 制振材の形状を工夫することで達成してき た。
しかしながら、 肉薄にすると強度が低下し、 成形時に損傷を受けや すく 、 生産性を挙げることが困難であった。 さ らに、 加硫ゴムにおい ては、 加硫剤である硫黄が残留して電子部品に影響を与える懸念があ り、 シリ コーンゴムでは、 低分子量シリ コーンによる接点障害の可能 性があるという問題があった。
また、 低周波数域の制振を達成するために、 よ り柔軟な材料、 例え ばゲルなどを使用することも考えられるが、 低硬度の材料は、 圧縮に よ り変形し易く、 制振性が経時的に低下したり、 材料中の低分子量成 分がブリー ド し、 制振を要するディスクなどに悪影響を与える懸念が めった。
次いで、 H D D用ガスケッ トについて述べる。
近年、 コンピュータ等の電子機器は高性能化、 小型化が進み、 複雑 な回路構成を有するよ うになつており、 わずかな塵によっても障害が 起こるため、 実用上、 防塵の必要性が高まっており、 通常は、 これら の電子機器を内蔵する箱状の本体とカバーとの接合面にガスケッ 卜を 挟持して取付ボルト等によ り締結して密封一体化することがなされて おり、 さ らに、 使用時の取り扱いを簡単にするため、 ガスケッ 卜 と力 バーとがー体となつたカバ一一体型ガスケッ トの形でも多く用いられ る。
しかしながら、 電子部品の高密度化などのため、 従来のものよ り塵 や化学物質をも透過せず、 且つ有毒なアウ トガス (ケミ カルコンタミ ネイシヨ ンの発生のないガスケッ ト、 シール部材に対するニーズが高 まっていた。
次いで、 H D D用衝撃吸収材について述べる。
ハードディスク装置 (H D D ) のァクチューターは、 高速へッ ド位 置決め機構の一部を構成するァクチユエ一夕の先端に設けられた磁気 へッ ドを位置決めし、 当該へッ ドによ り磁気ディスクに磁気信号を記 録 . 再生する装置である。 磁気へッ ドの位置決めは、 ボイスコイルモ —夕と、 ァクチユエ一夕に支持されたコイルによって生じるローレン ッカを、 前記コィルに流す電流を制御するこ とによ って行われている このァクチユエ一夕の近傍には、 へッ ド位置決め機構が故障等によ つて制御不能となり暴走した時に磁気へッ ドやへッ ドジンバルァッセ ンブリが他部材に衝突したり脱落したり して損傷することを防止する ための H D D用衝撃吸収材と称するス ト ツバ機構を備えている。
従来このような H D D用衝撃吸収材と しては、 ウレタ ン系及び塩化 ビニル系の熱可塑性エラス トマ一からなる弾性体が多く用いられてい る。 しかし、 これらの弾性体からなる H D D用衝撃吸収材は、 有毒ガ スの発生量が多く、 又、 衝撃吸収性も、 例えばクラッシュス ト ップと して使用するには、 十分ではなかった。
本発明は、 以上のよ うな状況下で、
( 1) 低硬度で高ロス性 (制振性) 及び耐気体透過性が良好で、 しかも 射出成形性に優れ、 寸法精度が安定した射出成形が可能な樹脂組成物. (2) イ ンクジヱッ トプリ ンターにおいて、 特にイ ンク室とイ ンク供給 部とを分割する位置に設けられ、 かつ該イ ンク室とィ ンク供給部との 圧力差によ り移動し、 ィ ンク室に充填されたィ ンクを記録へッ ド部に 供給するィ ンク タ ンク弁、 あるいはィ ン ク供給口に設けられ、 かつ該 ィ ンク供給口からィ ンクが洩れるのを防止するシール部材などと して 好適に用いられ、 また、 イ ンクジヱッ トプリ ンター本体部に設けられ 、 記録へッ ドからィ ンクが洩れることや記録へッ ドが乾燥することを 防止するシール部材などと して好適に用いられ、 二色成形法による射 出成形が可能で、 かつシール性及びオイルブリ一ド性に優れた材料か らなるイ ンクジヱッ トプリ ンター用弾性部材、 並びにこの弾性部材を 用いたイ ンク タンク及びイ ンクジヱッ 卜プリ ンター、
(3) 特にハー ドディスク装置 (H D D ) に適した、 気体気密性及び物 質の浸透 · 透過性が良好で、 且つ有害ガスの発生の少ないガスケッ 卜 及びカバ——体型ガスケッ ト、 (4) 高ロス性 (制振性) 及びオイル保持性が良好で、 低硬度で、 かつ 圧縮永久歪みが小さいなどの特性を有する材料を用いることによ り、 軽量物の制振性、 特に低周波数域での制振性に優れ、 かつ耐久性に優 れた記録媒体駆動装置用イ ンシュレーター、 及び
(5) 有毒ガスの発生量が少なく、 且つ十分な衝撃吸収性を有する H D D用衝撃吸収材
を提供することを目的とするものである。
本発明者らは、 前記目的を達成するために鋭意研究を重ねた結果、 上記各部材を、 特定のプロッ ク共重合体を含む熱可塑性エラス トマ一 に特定の成分を配合した樹脂組成物で構成することによ り、 その目的 を達成しうることを見出した。 本発明は、 かかる知見に基づいて完成 したものである。
すなわち、 本発明は、
( 1 ) イ ソブチレン系重合体プロッ クと芳香族ビニル系重合体プロッ クとからなるイ ソブチレン系ブ口ッ ク共重合体を含む熱可塑性エラス トマ一 1 0 0重量部に対してポリオレフィ ン樹脂 1〜 5 0重量部を配 合してなる樹脂組成物、
( 2 ) 上記 ( 1 ) の樹脂組成物から構成されてなるィ ンクジエツ トプ リ ンター用弾性部材、
( 3 ) 上記 ( 1 ) の樹脂組成物から構成されてなる記録媒体駆動装置 用イ ンシユ レ一ター、
( 4 ) 上記 ( 1 ) の樹脂組成物から構成されてなる H D D用ガスケッ 卜、
( 5 ) 上記 ( 1 ) の樹脂組成物から構成されてなる H D D用衝撃吸収 ネ刁、
( 6 ) 芳香族ビニル系重合体ブロッ クを形成する芳香族ビニル系化合 物が、 スチレン, α—メチルスチレン及び p—メチルスチレンからな る群から選ばれた少なく と も一種である上記 ( 1 ) の樹脂組成物、 ( 7 ) イ ソブチレン系ブロッ ク共重合体における、 イソブチレン系重 合体プロッ ク と芳香族ビニル系重合体プロッ クとの重量割合が 6 0 : 4 0〜 8 0 : 2 0である上記 ( 1 ) の樹脂組成物。
( 8 ) ポリオレフイ ン樹脂が、 ァイ ソタクティ ッ クポリプロピレンま たはその共重合体である上記 ( 1 ) の樹脂組成物、
( 9 ) ポリオレフィ ン樹脂が、 変性ポリオレフィ ンである上記 ( 1 ) の樹脂組成物、
( 1 0 ) イ ソブチレン系ブ口ッ ク共重合体を含む熱可塑性エラス 卜マ —が、 ィ ソプチレン系ブ口ッ ク共重合体と共にその他の熱可塑性エラ ス トマ一を含む上記 ( 1 ) の樹脂組成物、
( 1 1 ) さ らに、 イソブチレン系重合体プロッ クと芳香族ビニル系重 合体ブロッ ク とからなるイ ソブチレン系ブ口ッ ク共重合体を含む熱可 塑性エラス トマ一 1 0 0重量部に対してポリ フエ二レンエーテル 1 0 0重量部以下を配合してなる上記 ( 1 ) の樹脂組成物、
( 1 2 ) さ らに、 イソブチレン系重合体プロッ クと芳香族ビュル系重 合体プロッ クとからなるィ ソプチレン系ブ口ッ ク共重合体を含む熱可 塑性エラス トマ一 1 0 0重量部に対してゴム用非芳香族系軟化剤 2 0 0重量部以下を配合してなる上記 ( 1 ) の樹脂組成物、
( 1 3 ) さ らに、 ィ ソブチレン系重合体ブロッ クと芳香族ビュル系重 合体ブロッ ク とからなるイ ソプチレン系ブロッ ク共重合体を含む熱可 塑性エラス トマ一 1 0 0重量部に対して石油系炭化水素樹脂 1 0〜 1 0 0重量部を配合してなる上記 ( 1 ) の樹脂組成物、
( 1 4 ) イ ンクジヱッ トプリ ン夕一本体部に設けられ、 かつシール部 材と して用いられる上記 ( 2 ) のイ ンクジヱッ トプリ ン夕一用弾性部 材、
( 1 5 ) 上記 ( 2 ) の弾性部材を用いたことを特徴とするイ ンク タ ン ク、
( 1 6 ) 上記 ( 1 4 ) の弾性部材を用いたことを特徴とするィ ンク 夕 ンク、
( 1 7 ) 上記 ( 2 ) の弾性部材を用いたことを特徴とするイ ンクジニ ッ トプリ ン夕一、
( 1 8 ) 上記 ( 1 4 ) の弾性部材を用いたことを特徴とするィ ンクジ エツ トプリ ン夕一、
及び、
( 1 9 ) 上記 ( 4 ) の H D D用ガスケッ トがカバーと一体的に成形さ れてなる H D D用力バ一一体型ガスケッ ト
である。 発明を実施するための最良の形態
本発明の樹脂組成物を構成するィ ソブチレン系ブ口ッ ク共重合体は ィ ソブチレン系重合体プロッ クと芳香族ビニル系重合体プロッ クとか らなるものである。
各プロッ クは、 各々、 ィソブチレン、 及び、 芳香族ビュル系化合物 からなるが、 本発明の効果を阻害しない範囲で、 他の成分を共重合さ せたブロッ クであってもよい。
即ち、 イ ソブチレン系重合体ブロッ クは、 イ ソブチレンを主構成成 分とする連鎖であるが、 イ ソプチレンとイ ソブチレン以外のカチオン 重合性単量体との共重合プロッ クであることもできる。
ただし、 ィ ソブチレン系重合体ブロッ クは、 イ ソブチレン単位を 6 0重量%以上、 さ らには 8 0重量%以上含有するプロッ クであること が好ましく 、 6 0重量%未満の含有量では、 物性及び重合特性等のバ ランスが低下する。
ィ ソブチレン系重合体ブロッ クにおいてイ ソプチレンと共重合させ 得るカチオン重合性単量体と しては、 たとえば、 脂肪族ォレフィ ン類 、 ジェン類、 ビュルエーテル類等を挙げるこ とができる。
同様に、 芳香族ビニル系重合体ブロッ クは、 芳香族ビニル系化合物 を主構成成分とする連鎖であるが、 芳香族ビニル系化合物と芳香族ビ ニル系化合物以外のカチォン重合性単量体との共重合ブロッ クである こ と もできる。
ただし、 芳香族ビニル系重合体ブロッ クは、 芳香族ビニル系化合物 単位を 6 0重量%以上、 さ らには 8 0重量%以上含有するプロッ クで あることが好ま しく、 6 0重量%未満の含有量では、 物性及び重合特 性等のバラ ンスが低下する。
芳香族ビュル系化合物の例と しては、 スチ レンをはじめ、 α —メチ ルスチレン : α —ェチルスチレン ; α _メチル一 ρ —メ チルスチレン などの α —アルキル置換スチ レン、 0 —メチルスチ レン ; m—メ チル スチ レン ; p —メ チルスチレン : 2 , 4 —ジメ チルスチレン ; ェチル スチレン ; 2 , 4 , 6 — ト リ メチルスチレン ; 0— t —プチルスチレ ン ; p— t —ブチルスチレン ; p —シクロへキシルスチレンなどの核 アルキル置換スチレ ン、 o — ク ロロスチレン : m—ク ロロスチレン ; p — ク ロロスチ レン : p —ブロモスチレン ; 2 —メ チルー 4 —ク ロ口 スチ レンなどの核ハロゲン化スチレン、 さ らには、 1 —ビュルナフ タ レン等のビニルナフ タ レン誘導体、 イ ンデン誘導体、 ジビュルべンゼ ンなどが挙げられる。 これらの中で、 スチレ ン : α —メ チルスチレン 及び Ρ —メチルスチレンが好適である。 これらの芳香族ビュル化合物 は単独で用いてもよ く 、 二種以上を組み合わせて用いてもよい。
芳香族ビニル系重合体ブロッ クにおいて芳香族ビニル系化合物と共 重合させ得るカチオン重合性単量体と しては、 たとえば、 脂肪族ォレ フ ィ ン類、 ジェン類、 ビニルエーテル類等を挙げるこ とができる。 ィ ソブチレン系ブロッ ク共重合体における、 イ ソブチレン系重合体 プロッ クと芳香族ビニル系重合体プロッ クとの重量割合は、 得られる 樹脂組成物の物性のバランスの点から、 6 0 : 4 0 〜 8 0 : 2 0が好 ま しい。
本発明の樹脂組成物には、 熱可塑性エラス トマ一と して、 ィ ソブチ レン系ブロ ッ ク共重合体以外のスチレン系、 ォレフ ィ ン系、 ウ レタ ン 系、 エステル系等の熱可塑性エラス トマ一を併用することができ、 か かる熱可塑性エラス 卜マ一と しては、
① ポリブ夕ジェンとブタジエン一スチレンランダム共重合体との プロッ ク共重合体を水添して得られる結晶性ポリエチレンとエチレン /プチレン一スチレンラ ンダム共重合体とのブロッ ク共重合体、
② ポリブタジエンとポリスチレンとのブロッ ク共重合体、 及びポ リイ ソプレンとポリスチレンとのブロッ ク共重合体、 あるいは、 ポリ ブタジエン又はエチレン一ブタジエンランダム共重合体とポリスチレ ンとのブロッ ク共重合体を水添して得られる、 例えば、 結晶性ポリエ チ レンとポリ スチレンとのジブロ ッ ク共重合体、 スチレン一エチ レン
/プチレン一スチレンの ト リブロッ ク共重合体 ( S E B S ) 、 スチレ ン一エチレ ン/プロ ピレン一スチレンの ト リブロッ ク共重合 ( S E P S ) など、 中でも、 スチレン一エチ レン/ブチレン一スチレンブロ ッ ク共重合体又はスチレ ン一エチ レン/プロ ピレ ン一スチレンブロ ッ ク 共重合体、
などを挙げることができる。
これらのイ ソブチレン系ブ口ッ ク共重合体以外の熱可塑性エラス 卜 マ一を併用する場合においては、 イ ソブチレン系ブロッ ク共重合体に 対するそれ以外の熱可塑性エラス トマ一の使用量は、 前者 1 0 0重量 部に対し 1 0 0重量部以下とするのが好ましい。
(なお、 以下の記述においては、 単に 「熱可塑性エラス トマ一」 と 記載した場合は、 ィ ソブチレン系ブ口ッ ク共重合体単体の場合とィ ソ ブチレン系ブロッ ク共重合体以外の熱可塑性エラス 卜マ一を併用する 場合の双方を含むものとする。 )
本発明の樹脂組成物において使用するポリオレフィ ン樹脂は特に制 限されず、 目的、 用途に応じて適宜選択することができ、 例えば、 ポ リエチレン、 ポリプロピレン、 ポリブテン (特には結晶性ポリブテン ) などを挙げることができる。 中でも、 ァイ ソタクティ ッ クポリプロ ピレン又はその共重合体を好適に使用することができる。 また、 その
J I S K 7 2 1 0 : 1 9 9 9 に準拠して測定したメルトマスフ口一 レー ト (M F R ) が 0 . 1 〜 5 0 / 1 0分、 特に 0 . 5 ~ 3 0 g / 1 0分の範囲のものが好適に使用できる。
また、 ポリオレフイ ン樹脂は、 いわゆる変性ポリオレフイ ン樹脂を 含んでいても良い。 変性ポリオレフィ ン樹脂は、 上述のポリオレフィ ン樹脂に、 マレイ ン酸, 無水マレイ ン酸等の不飽和ポリカルボン酸、 ァク リル酸類や水酸基を有する重合性モノマーをグラフ トまたは共重 合させた樹脂である。 このような変性ポリオレフイ ン樹脂と しては、 例えば、 三井デュポンポリケミ カル (株) 製ニュク レルシリーズ (商 品名) , 三洋化成 (株) 製ユーメ ッ クスシリーズ (商品名) , ェクソ ン化学社製ェクセラーシリーズ (商品名) , ュニロイヤル社製ポリ ド ンシリーズ (商品名) , 三井化学 (株) 製ァ ドマーシ リ一ズ (商品名 ) などと して市販されている物を使用できる。
これらのポリオレフィ ン樹脂の配合量は、 熱可塑性エラス トマ一 1 0 0重量部に対し、 2 0 0重量部以下の量で好適に選択することがで きる。 この量が 2 0 0重量部を超えると軟化剤がブリードしやすく な り、 かつ樹脂組成物の機械的強度が低下する原因となることがある。 十分な効果を得るためには 1 重量部以上を配合することがさ らに好ま しく 、 5重量部以上とすることが特に好ましい。 'また、 諸物性のバラ ンスを考慮すると、 1 0 0重量部以下とすることが更に好ましく 、 5 0重量部以下とすることが特に好ま しい。
本発明の樹脂組成物には、 材料の圧縮永久歪みを改善するなどの目 的で、 ポリ フヱニレンエーテルを配合することができる。
このポリ フエ二レンェ一テルと しては公知のものを用いることがで き、 具体的には、 ポリ ( 2 , 6 —ジメチルー し 4 一フエ二レンェ一 テル) 、 ポリ ( 2 —メチル一 6 —ェチルー 1 , 4 —フエ二レンェ一テ ル) 、 ポリ ( 2 , 6 —ジフエニル一 1 , 4 —フエ二レンエーテル) 、 ポリ ( 2 —メチル一 6 —フエ二ルー 1 , 4 —フエ二レンエーテル) 、 ポリ ( 2 , 6 —ジクロ口一 1 , 4 —フエ二レンエーテル) などが挙げ られ、 また、 2 , 6 —ジメチルフエノールと 1 価のフエノール類 (例 えば、 2 , 3 , 6 — ト リメチルフヱノールや 2 _メチル _ 6 —ブチル フエノール) との共重合体の如きポリ フヱニレンエーテル共重合体も 用いることができる。 なかでも、 ポリ ( 2 , 6 —ジメチルー 1 , 4— フエ二レンエーテル) や 2 , 6 —ジメチルフヱノールと 2, 3 , 6 - 卜 リ メチルフヱノールとの共重合体が好ましく 、 さ らに、 ポリ ( 2 , 6—ジメチルー 1 , 4 —フエ二レンエーテル) が好ましい。
これらのポリ フヱニレンェ一テルの配合量は、 熱可塑性エラス トマ - 1 0 0重量部に対して 1 0 0重量部以下の量で好適に選択すること ができる。 この配合量が 1 0 0重量部を超えると熱可塑性エラス 卜マ 一の硬度が高く なるおそれがあり、 好ま しく ない。 十分な効果を得る ためには 1重量部以上を配合することがさ らに好ましく 、 5重量部以 上とすることが特に好ましい。 また、 諸物性のバランスを考慮すると 、 7 5重量部以下とすることが更に好ま しく、 5 0重量部以下とする ことが特に好ま しい。
本発明の樹脂組成物には、 熱可塑性エラス トマ一を低硬度化する目 的で、 ゴム用非芳香族系軟化剤を配合することができる。 このゴム用 非芳香族系軟化剤と しては、 物性的には、 1 0 0 °Cにおける粘度が 5 X 1 0 5 センチボイズ以下、 特に、 1 X 1 0 5 センチボイズ以下であ るものが好ま しい。 また、 分子量の観点からは、 数平均分子量は 2 0 0 0 0未満、 特に 1 0 0 0 0以下、 と りわけ 5 0 0 0以下であるもの が好ましい。 このようなゴム用非芳香族系軟化剤と しては、 特に、 鉱 物油系のパラフィ ン系オイル, ナフテン系オイル又は合成系のポリィ ソプチレン系オイルであって、 その数平均分子量が 4 5 0〜 5 0 0 0 であるものが好ま しい。 なお、 これらの軟化剤は一種を単独で用いてもよ く 、 互いの相溶性 が良好であれば二種以上を混合して用いてもよい。
これらの軟化剤の配合量は特に制限はないが、 熱可塑性エラス トマ
- 1 0 0重量部に対し、 2 0 0重量部以下の量で好適に選択すること 5 ができる。 この量が 2 0 0重量部を超えると軟化剤がブリー ドしゃす く なり、 かつ樹脂組成物の機械的強度が低下する原因となることがあ る。 なお、 この軟化剤の配合量は、 熱可塑性エラス トマ一の分子量及 び該エラス トマ一に添加される他の成分の種類に応じて、 上記範囲で 適宜選定することが好ましい。
1 0 本発明の樹脂組成物には、 t a n 5を目的とする用途の使用温度域 へずらしたり、 高ロス性を改良する目的で、 石油系炭化水素樹脂を配 合することができる。 このような石油系炭化水素樹脂と しては、 合成 テルペン樹脂、 芳香族系炭化水素樹脂、 脂肪族系炭化水素樹脂等を挙 げることができる。 又、 その配合量は、 熱可塑性エラス トマ一 1 0 0 i s 重量部に対し、 1 0 〜 1 0 0重量部の範囲であることが好ましい。 こ の量が 1 0重量部未満では、 配合の効果が十分に発揮されないことが あ り、 1 0 0重量部を超えるとク リ一プが大き く なり過ぎて、 成型品 使用時に変形が大き く なり使えないことがある。
また、 本発明の樹脂組成物には、 ク レー, 珪藻土, シリカ, タルク
2 0 , 硫酸バ リ ウム, 炭酸カルシウム, 炭酸マグネシウム, 金属酸化物, マイ 力, グラフ アイ 卜, 水酸化アルミ ニウムなどの無機系充填材、 各 種の金属粉, ガラス粉, セラミ ッ クス粉, 粒状あるいは粉末ポリマ一 等の粒状あるいは粉末状固体充填材, その他の各種の天然または人工 の短繊維, 長繊維 (各種のポリマーファイバ一等) などを配合するこ
2 5 とができる。 無機系充填材は、 リ ン片状であることが好ましい。
また、 本発明の樹脂組成物は、 内部に気泡を含有していてもよい。 気泡を含有させることによ り、 軽量化を図ることができる。
気泡を含有させる方法は特に限定されないが, 例えば、 ガラスバル ーン, シ リ カバル一ンなどの無機中空フ イ ラ一、 ポリ フ ッ化ビニ リ デ ン, ポリ フッ化ビ二リデン共重合体などからなる有機中空フイラ一を 配合する方法、 各種発泡剤を混入する方法、 また、 混合時等に機械的 に気体を混ぜ込む方法等を挙げることができる。
また、 他の添加剤と して、 必要に応じて、 難燃剤, 抗菌剤, ヒ ンダ 一ドアミ ン系光安定剤, 紫外線吸収剤, 酸化防止剤, 着色剤, シリ コ —ンオイ ル, シ リ コーンポリ マ一, クマロ ン樹脂, クマロ ン一イ ンデ ン樹脂, フユ ノールテルペン樹脂, 石油系炭化水素, ロジン誘導体な どの各種粘着付与剤 (タツキフアイャ一) , レオス トマ一 B (商標 : 理研ビニル社製) などの各種接着性エラス トマ一などを併用すること ができる。
本発明の樹脂組成物の製造方法は、 特に限定されず、 公知の方法を 適用するこ とができる。 例えば、 前記の各成分及び所望によ り用いら れる添加剤成分を加熱混練機、 例えば、 一軸押出機, 二軸押出機, 口 —ル, ノ ンバリ一ミ キサー, プラベンダー, ニーダ一, 高剪断型ミキ サ一などを用いて溶融混練し、 さ らに、 所望によ り有機パーォキサイ ドなどの架橋剤、 架橋助剤などを添加したり、 又は、 これら必要な成 分を同時に混合し、 加熱溶融混練することによ り、 容易に製造するこ とができる。
また、 高分子有機材料と軟化剤とを混練した樹脂組成物を予め用意 し、 この材料を、 ここで用いたものと同種か若しく は種類の異なる一 種以上の高分子有機材料に更に混ぜ合わせて製造することもできる。
さ らに、 本発明の樹脂組成物においては、 有機パ一ォキサイ ドなど の架橋剤, 架橋助剤などを添加して架橋することも可能である。
以上の如き本発明の樹脂組成物は、 特に、 ィ ンクジエツ トプリ ンタ 一用弾性部材、 記録媒体駆動装置用イ ンシユ レ一夕一、 H D D用ガス ケッ ト、 及び H D D用衝撃吸収材を構成するのに適したものである。 而して、 本発明のィ ンク ジエツ 卜プリ ン夕一用弾性部材、 記録媒体 駆動装置用ィ ンシユ レ一ター、 H D D用ガスケッ ト及び H D D用衝撃 吸収材は、 前記した如き問題点を払拭したものである。
本発明の樹脂組成物から構成された本発明のィ ンクジエツ トプリ ン 夕一用弾性部材は、 イ ンクジヱッ トプリ ンターにおける、 イ ンクが充 填されるイ ンク室と、 記録へッ ド部にィ ンクを供給するィ ンク供給部 とを有するィ ンクタ ンクに好適に用いられる。
この弾性部材は、 前記イ ンク タンクにおいて、 弾性部材を必要とす るパーツであれば、 特に制限はなく、 いかなるパーツにも使用するこ とができるが、 例えば、 イ ンク室とィ ンク供給部とを分割する位置に 設けられ、 かつ該ィ ンク室とィ ンク供給部との圧力差によ り移動し、 ィ ンク室に充填されたィ ンクを記録へッ ド部に供給するィ ンク タンク 弁と して、 あるいはィ ンク タンクのイ ンク供給口に設けられ、 かつ該 ィ ンク供給口からィ ンクが洩れるのを防止するィ ンク タンクのシール 部材と して使用するのが、 特に好ま しい。
これらの弾性部材にィソブチレン系ブロッ ク共重合体を含有する本 発明の樹脂組成物を使用することによ り、 以下に示す効果を奏する。 前記ィ ンクタ ンク弁は、 たとえばプラスチッ ク基材の表面に弾性材 料が一体的に形成された構造を有しており、 このような構造の成形物 を作製する場合には、 工程が簡単で、 製造コス トの低い二色成形法に よる射出成形が有利である。 該弾性材料として従来用いられている熱 硬化性ゴムでは、 プラスチッ クとの二色成形が困難であつたが、 本発 明のように、 ィ ソブチレン系ブ口ッ ク共重合体を含む材料を用いるこ とによ り、 二色成形が容易となり、 低いコス トでィ ンク タンク弁を作 製することができる。
また、 従来の熱硬化性ゴムでは、 低硬度化した材料で所望形状の部 材を成形, 加硫するのが困難であつたが、 本発明のように、 イ ソプチ レン系ブ口ッ ク共重合体を含む材料を用いることによ り、 これが可能 となり、 適度の弾性を有し、 かつ機械物性に優れた成形体が得られる さ らに、 樹脂組成物においてィ ソプチレン系ブ口ッ ク共重合体など の熱可塑性エラス トマ一を低硬度化する際に使用するオイル成分と し て、 パラフィ ン系オイルなど、 イ ンクに対して極性の大きく異なる液 体を使用することができ、 しかも、 それらのオイルは、 イソプチレン 系ブロッ ク共重合体の凝集ドメイ ンであるスチレンブロッ クに対して 相溶しにく く 、 エラス トマ一の強度などの物性に対して、 影響が少な い。 また、 イ ソブチレン系ブ口ッ ク共重合体を含む熱可塑性エラス ト マーを使用すると、 ィ ンクなどの溶媒による膨潤などの変化が小さ く 、 耐久性に優れるィ ンクタンク弁やイ ンクタンクのシール部材、 記録 へッ ドからィ ンクが洩れるのを防止するシール部材などを与えること ができる。
なお、 本発明のシール部材は、 イ ンク供給口に設置するほか、 イ ン ク供給部と記録へッ ドを連結する結合部等にも使用することができる 本発明はまた、 このィ ンクジヱッ トプリ ンター用弾性部材を、 特に 好ま しく はイ ンク タンク弁及び/又はイ ンク タンクのシール部材と し て用いたイ ンク タ ンクをも提供する。
本発明のィ ンク タンクは、 該弾性部材を用いたものであればよ く 、 特に制限されず、 イ ンクをポリ ウ レタンなどの発泡体で保持したもの であってもよ く、 このような発泡体を充填していないものであっても よい。
また、 前記ィ ンク タンク弁やイ ンク タンクのシール部材の形状と し ては、 特に制限はなく、 従来イ ンク タ ンクに使用されているものと同 じ形状のものを挙げることができる。 それらの製造方法については、 例えばィ ンク タンクのシール部材の場合は、 射出成形や押出成形など 、 従来公知の成形方法を採用することができる。 一方、 イ ンクタ ンク 弁の場合は、 例えば基材となるプラスチッ クを金型内に溶融射出成形 し、 次いでその上に本発明の樹脂組成物を溶融射出成形してプラスチ ッ ク成形物の表面に、 該樹脂組成物を積層して一体化させる二色成形 法を採用することができる。 あるいは、 まず、 プラスチッ クを金型内 に溶融射出成形したのち、 その成形物を他の金型にィ ンサ一卜 し、 そ 5 の表面に、 本発明の樹脂組成物を溶融射出成形して、 プラスチッ ク成 形物の表面に、 該樹脂組成物を積層して一体化させるィ ンサー 卜成形 法を採用することができる。
本発明の記録媒体駆動装置用ィ ンシュレーターは、 本発明の樹脂組 成物を、 公知の方法、 例えば射出成形などによ り所望の形状に成形し 1 0 てなるものであり、 音響機器, 情報関連機器, 情報伝達機器, ゲーム 関連機器, その他に好適に使用することができ、 具体的には、 例えば 音響機器と しては、 C Dプレイヤ一や自動車搭載 C D用のイ ンシユ レ 一ター、 ハー ドディスク ドライブやフロッ ピィディスク ドライブのィ ンシユレ一ター、 各種パソコン機器、 家庭用ゲーム機器や各種計測器 i s 用に使用される C D— R〇 Mのイ ンシュレーターなどが挙げられる。
本発明の H D D用ガスケッ トは、 本発明の樹脂組成物を、 公知の方 法、 例えば射出成形などによ り所望の形状に成形してなるものであり 、 ガスケッ 卜 と して、 又はカバ一と一体的に成形して、 カバ一一体型 ガスケッ ト と して使用する。
2 0 カバ——体型ガスケッ 卜におけるカバ一と しては、 硬質樹脂からな るものも使用し得るが、 加工性等からは金属製が好ま しい。 金属と し ては、 特に制限はなく、 例えば冷延鋼板, 亜鉛めつき鋼板, アルミ二 ゥム /亜鉛合金めつ き鋼板, ステンレス鋼板, アルミニウム板, アル ミニゥム合金板, マグネシウム板, マグネシウム合金板などの中から
2 5 、 適宜選択して用いることができる。 また、 マグネシウムを射出成形 したものも用いることができる。 耐食性の点から、 無電解ニッケルめ つき処理を施した金属が好適である。 この無電解ニッゲルめつき処理 方法と しては、 従来金属素材に適用されている公知の方法、 例えば硫 酸ニッケル, 次亜リ ン酸ナ ト リ ウム, 乳酸, プロピオン酸などを適当 な割合で含有する p H4. 0〜5. 0程度で、 かつ温度 8 5〜 9 5 °C程度 の水溶液からなる無電解ニッゲルめつき浴中に、 金属板を浸漬する方 法などを用いることができる。 カバーの厚さは、 適宜選定されるが、 通常 0. 3〜 1 . O mm、 好ま しく は 0. 4 〜 0 . 6 mmの範囲であ る。
本発明の H D D用衝撃吸収材は、 本発明の樹脂組成物を、 公知の方 法、 例えば射出成形などによ り所望の形状に成形してなるものであり 、 例えばクラッシュス トップと して使用する。
なお、 本出願は、 日本特許出願第 2 0 0 1 — 2 9 0 8 1 0号、 第 2 0 0 1 - 2 9 0 8 1 1号、 第 2 0 0 1 — 2 9 0 8 1 2号、 第 2 0 0 1 - 2 9 0 8 1 3号及び第 2 0 0 1 - 2 9 0 8 1 0号に基く優先権を主 張し、 その全体はそれらの明細書を援用するものである。 実施例
次に、 本発明を実施例によ り さ らに詳しく説明するが、 本発明はこ れらの例によってなんら限定されるものではない。
なお、 以下の実施例, 比較例及び参考例における物性評価は、 下記 の方法によ り行った。
( 1 ) 硬度
J I S K 6 3 0 1 - 1 9 9 3 に従って硬度を測定し、 その結果 を比較例 1 での硬度を 1 0 0 と した相対値と して示した。
( 2 ) t a η δ
2 5 ΐ:、 1 5 Η ζ、 1 %歪によ り t a η 5を測定し、 その結果を比 較例 1 での硬度を 1 と した相対値と して示した。
( 3 ) 射出成形性
射出成形を行い、 寸法精度が土 1 %以内で成形できた場合を〇、 で きなかつた場合を Xと した。 ( 4 ) オイルブリ一ド性
弾性部材をィ ンクに浸漬して、 7 0 °C 2 4時間オイル染み出しの有 無を観察した。
( 5 ) シール性
5 弾性部材から金型温度 8 0 °C , 樹脂温度 1 7 0 °Cの製造条件にて、 シール部材を作成し、 イ ンクタ ンクに設置し、 イ ンクジヱッ トプリ ン ターに適用して、 2 5 °Cで 1 ヶ月使用した時の、 シール漏れの有無を 観察した。
( 6 ) 制振性
, ο 樹脂組成物から作成したィ ンシユ レ一夕を、 市販の C D— R O M起 動装置に組み込み稼動した際の、 駆動装置の設置床への振動伝達率を 測定し、 その結果を比較例 5での振動伝達率 ¾ 1 0 0 と した相対値と して示した。
( 7 ) ガス発生量
, 5 樹脂組成物 1 0 m gから 1 5 0 ° (:、 2 0分間における発生ガス量を
G C — M Sを使用して測定し、 その結果を比較例 7及び比較例 9 (同 配合割合) での発生ガス量を 1 0 0 と した相対値と して示した。
( 8 ) ガス透過性
樹脂組成物から作成した厚さ 2 mm、 5 c m角のシー トを用意し、 20 環状ジメチルシロキサン ( D 4 ) の 6 0 °Cで 2 4時間当たりの透過量 を計測し、 その結果を比較例 7での透過量を 1 0 0 と した相対値と し て示した。
( 9 ) 衝撃吸収性
樹脂組成物から作成した厚さ 2 mm、 5 c m角のシ一 トを用意し、 25 その上に 1 k gの鉄球を高さ 1 mの位置から落下させて鉄球の跳ね返 り高さを求め、 2 c m以上なら X、 2 c m未満 (測定不能も含む) を 〇と評価した。
また、 以下の実施例, 比較例及び参考例における配合原料は、 各々 次のものである。
ポリマ一 A : スチ レン一イ ソブテン一スチレン ブロッ ク共重合体 〔 スチレ ン量 : 3 0重量0 /0
ポリ マー B : スチレ ン一エチ レン/ブチ レン一スチレン ブロ ッ ク共 重合体 〔ク レイ ト ンポリマ一社製, 商標 : ク レイ ト ン G
1 6 5 0 、 スチレン量 : 3 0重量%〕
ポリマ一 C : ポリ プロ ピレ ン 〔チッ ソ (株) 製, 商標 : ポリ プロ C F
3 0 3 1 ]
ポリマー D : 変性ポリ フヱニレンエーテル 〔旭化成 (株) 製, 商標 : ザイロン X 0 1 0 8〕
ポリマー E : 芳香族石油系炭化水素樹脂 〔新日本石油 (株) 製, 商標 : 日石ネオポリマ一 1 1 0 〕
ポリマー F : ウ レタ ンゴム 〔クラレ (株) 製, 商標 : クラミ ロン U〕 オイ ル A : 液状ポリブテン 〔日石化学 (株) 製, 商標 : H V 1 0 0 〕 オイル B : パラフィ ン系オイル 〔三井化学 (株) 製, 商標: ル一力 ン 卜 H C - 1 5 0 〕
オイル C : パラフ ィ ン系オイル 〔出光興産 (株) 製, 商標: ダイアナ プロセスオイル P W 3 8 0 〕 実施例 1 〜 5及び比較例 1 , 1
第 1表に示した配合からなる各成分を充分に混練して樹脂組成物の サンプルを調製し、 物性の評価を行った。
その結果、 第 1表から明らかなよ うに、 実施例 1 〜 5 の樹脂組成物 は、 低硬度で高ロス性 (制振性) に優れ、 気体透過性が小さ く、 しか も射出成形性に優れ、 寸法精度が安定した射出成形が可能である。 第 1 表
Figure imgf000026_0001
実施例 6〜 1 0及び比較例 3, 4
第 2表に示した配合からなる各成分を充分に混練して樹脂組成物の サンプルを調製し、 イ ンクジヱッ トプリ ン夕一用弾性部材に必要とさ れる物性 (オイルブリ — ド性及びシール性) の評価を行った。
その結果、 第 2表から明らかなように、 実施例 6〜 1 0の材料では オイルブリ一ドの染み出し及びシール漏れは観測できなかったが、 比 較例の材料ではオイルの染み出し及びシール漏れが観測された。 実 施 例 比 較 例
6 7 8 9 10 3 4 ポリマ一 A 100 100 100 50 50
ポリマー
ム B 50 50 100 100 口
ポリマー C 15 15 15 15 15 15 15 害 α |リ|
ポリマー D 5 10 15 15 15 15 ム
オイル A 150 75 75 150 里 オイル B 150 75 150 部
オイル C 150 75
評 オイルプリ -ド 性 なし なし なし なし なし あり あり 価 シール性 なし なし なし なし なし あり あり 実施例 1 1 〜 1 6及び比較例 5 , 6
第 3表に示した配合からなる各成分を充分に混練して樹脂組成物の サンプルを調製し、 記録媒体駆動装置用ィ ンシュ レーターに必要とさ れる物性 (オイルブリード性及び制振性) の評価を行った。
その結果、 第 3表から明らかなように、 実施例 1 1 〜 1 6の材料で はオイルの染み出しは観測できず、 比較例の材料よ り も優れた制振性 を示したが、 比較例の材料ではオイルの染み出しが観測された。
3 表
Figure imgf000028_0001
実施例 1 7〜 2 1及び比較例 7, 8
第 4表に示した配合からなる各成分を充分に混練して樹脂組成物の サンプルを調製し、 H D D用ガスケッ 卜に必要とされる物性 (発生ガ ス量及びガス透過性) の評価を行った。
その結果、 第 4表から明らかなように、 実施例 1 7〜 2 1 の材料で は比較例 7 の材料 (ェチレ ンプロピレンゴム) よ り も優れた低ガス発 生量、 低ガス透過量が観測された。 実 施 例 比 較 例
17 18 19 20 21 7 8 ポリマー A 100 100 100 50 50
ポリマー B 50 50 100 八
ポリマー C 15 15 15 15 15 15 割
ポリマー D 5 10 15 15 15 八
ポリマ一 F 100 里 オイル A 150 75 75
オイル B 150 75 150 評 発生ガス量 30 20 25 25 25 100 30 価 ガス透過性 10 10 10 75 75 100 100
実施例 2 2 2 6及び比較例 9 , 1 0
第 5表に示した配合からなる各成分を充分に混練して樹脂組成物の サンプルを調製し、 H D D衝撃吸収材に必要とされる物性 (発生ガス 量及び衝撃吸収性) の評価を行った。
その結果、 第 5表から明らかなように、 実施例 1 2 2 6の材料で は比較例 9の材料 (ウ レタンゴム) よ り も優れた低ガス発生量と高衝 撃吸収性が観測された。
実 施 例 比 較 例
22 23 24 25 26 9 10 ポリマー A 100 100 100 50 50
ポリマー B 50 50 100 ム σ
ポリマー C 15 15 15 15 15 15 σリ
ポリマー D 5 10 15 15 15 ム
ポリマー F 100 旦
里 オイル A 150 75 75
オイ ル B 150 75 150 評 発生ガス量 50 40 50 50 40 100 50 価 衝撃吸収性 〇 〇 〇 〇 〇 〇 X
産業上の利用可能性
本発明によると、 低硬度で高ロス性 (制振性) 及び耐気体透過性が 良好で、 しかも射出成形性に優れ、 寸法精度が安定した射出成形が可 能な樹脂組成物を提供することができる。 この樹脂組成物は、 特に、 イ ンクジ ッ トプリ ンター用弾性部材、 記録媒体駆動装置用ィ ンシュ レーター、 H D D用ガスケッ 卜、 及び H D D用衝撃吸収材を構成する のに適したものである。
本発明のィ ンクジヱッ トプリ ンター用弾性部材は、 プラスチッ クと の二色成形法による射出成形が可能で、 かつィ ソブチレンと同等のシ 一ル性を有すると共に、 比較的少ないオイル添加量でも低硬度であつ て、 しかも低オイルブリ一 ドシール性に優れるものであって、 特にィ ンク室とィ ンク供給部とを分割する位置に設けられ、 かつ該イ ンク室 とィ ンク供給部との圧力差によ り移動し、 イ ンク室に充填されたイ ン クを記録へッ ド部に供給するィ ンク タンク弁、 あるいはィ ンク供給口 に設けられ、 かつ該ィ ンク供給口からィ ンクが洩れるのを防止するシ —ル部材、 更にはイ ンクジヱッ 卜プリ ンター本体部に設けられ、 記録 へッ ドからイ ンクが洩れるのを防止するシール部材などと して、 好適 である。 また、 イ ンク供給部と記録ヘッ ドを連結する結合部等のシ一 ル部材と しても有効に使用できる。
本発明の記録媒体駆動装置用ィ ンシュ レーターは、 高ロス性 (制振 性) 及びオイル保持性が良好で、 低硬度で、 かつ圧縮永久歪みが小さ いなどの特性を有する材料を用いているため、 軽量物の制振性、 特に 低周波数域での制振性に優れ、 耐久性が高いという効果を奏する。 本発明の H D D用ガスケッ トは、 気体気密性及び物質の浸透 · 透過 性が良好で、 且つ有害ガスの発生の少なく 、 特にハー ドディスク装置 に適したものである。
本発明の H D D用衝撃吸収材は、 ガスの発生量が少なく 、 且つ高い 衝撃吸収性を有するものであり、 例えばス 卜 ツバ一アームの衝撃によ る変位が少ないクラッシュス ト ッパ一と して使用できるものである。

Claims

請求の範囲
1 . ィソブチレン系重合体プロッ クと芳香族ビニル系重合体プロッ ク とからなるイソブチレン系ブ口ッ ク共重合体を含む熱可塑性エラス ト マ一 1 0 0重量部に対してポリオレフィ ン樹脂 1 〜 5 0重量部を配合 してなる樹脂組成物。
2 . 請求項 1 に記載の樹脂組成物から構成されてなるィ ンクジエツ ト プリ ンター用弾性部材。
3 . 請求項 1 に記載の樹脂組成物から構成されてなる記録媒体駆動装 置用ィ ンシユ レ一夕一。
4 . 請求項 1 に記載の樹脂組成物から構成されてなる H D D用ガスケ ッ 卜。
5 . 請求項 1 に記載の樹脂組成物から構成されてなる H D D用衝撃吸 収材。
6 . 芳香族ビニル系重合体プロッ クを形成する芳香族ビニル系化合物 が、 スチ レ ン, α —メ チルスチレン及び p —メ チルスチレンからなる 群から選ばれた少なく とも一種である請求項 1 に記載の樹脂組成物。
7 . イソブチレン系ブロッ ク共重合体における、 イ ソプチレン系重合 体ブロッ ク と芳香族ビュル系重合体プロッ クとの重量割合が 6 0 : 4
0 〜 8 0 : 2 0である請求項 1 に記載の樹脂組成物。
8 . ポリ オ レフ イ ン樹脂が、 ァイ ソ タ クティ ッ クポリ プロ ピレンまた はその共重合体である請求項 1 に記載の樹脂組成物。
9 . ポリオレフイ ン樹脂が、 変性ポリオレフィ ンである請求項 1 に記 載の樹脂組成物。
1 0 . イ ソブチレン系ブロッ ク共重合体を含む熱可塑性エラス トマ一 が、 ィソブチレン系ブ口ッ ク共重合体と共にその他の熱可塑性エラス トマ一を含む請求項 1 に記載の樹脂組成物。
1 1 . さ らに、 イ ソブチレン系重合体ブロッ クと芳香族ビニル系重合 体プロッ クとからなるィソブチレン系ブ口ッ ク共重合体を含む熱可塑 性エラス トマ一 1 0 0重量部に対してポリ フエ二レンエーテル 1 0 0 重量部以下を配合してなる樹脂組成物。
1 2 . さ らに、 イ ソブチレン系重合体ブロッ クと芳香族ビニル系重合 体ブロッ ク とからなるイソプチレン系ブ口ッ ク共重合体を含む熱可塑 性エラス トマ一 1 0 0重量部に対してゴム用非芳香族系軟化剤 2 0 0 重量部以下を配合してなる請求項 1 に記載の樹脂組成物。
1 3 . さ らに、 イ ソブチレン系重合体ブロッ クと芳香族ビニル系重合 体ブロッ クとからなるイソプチレン系ブ口ッ ク共重合体を含む熱可塑 性エラス トマ一 1 0 0重量部に対して石油系炭化水素樹脂 1 0〜 1 0
0重量部を配合してなる請求項 1 に記載の樹脂組成物。
1 4 . イ ンクジヱッ トプリ ンター本体部に設けられ、 かつシ一ル部材 と して用いられる請求項 2 に記載のィ ンクジヱッ 卜プリ ンタ一用弾性 部材。
1 5 . 請求項 2 に記載の弾性部材を用いたことを特徴とするイ ンクタ ンク。
1 6 . 請求項 1 4 に記載の弾性部材を用いたことを特徴とするイ ンク タ ンク。 7. 請求項 2に記載の弾性部材を用いたことを特徴とするイ ンクジェ ッ トプリ ン夕一。 1 8 . 請求項 1 4 に記載の弾性部材を用いたことを特徴とするイ ンク ジエツ トプリ ン夕一。
1 9 . 請求項 4 に記載の H D D用ガスケッ 卜がカバ一と一体的に成形 されてなる H D D用カバ——体型ガスケッ 卜。
PCT/JP2002/009836 2001-09-25 2002-09-25 Composition de resine et element comprenant cette composition de resine WO2003027183A1 (fr)