WO2002089137A1 - Support d'enregistrement d'information optique et appareil d'enregistrement/reproduction d'information optique - Google Patents

Support d'enregistrement d'information optique et appareil d'enregistrement/reproduction d'information optique Download PDF

Info

Publication number
WO2002089137A1
WO2002089137A1 PCT/JP2002/003974 JP0203974W WO02089137A1 WO 2002089137 A1 WO2002089137 A1 WO 2002089137A1 JP 0203974 W JP0203974 W JP 0203974W WO 02089137 A1 WO02089137 A1 WO 02089137A1
Authority
WO
WIPO (PCT)
Prior art keywords
optical information
substrate
information recording
layer
recording medium
Prior art date
Application number
PCT/JP2002/003974
Other languages
English (en)
French (fr)
Inventor
Takuya Wada
Hideki Aikoh
Original Assignee
Matsushita Electric Industrial Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Matsushita Electric Industrial Co., Ltd. filed Critical Matsushita Electric Industrial Co., Ltd.
Priority to JP2002586348A priority Critical patent/JPWO2002089137A1/ja
Priority to US10/475,794 priority patent/US6941572B2/en
Publication of WO2002089137A1 publication Critical patent/WO2002089137A1/ja

Description

明 細 書
光学的情報記録媒体と光学的情報記録再生装置 技術分野
本発明は、 光学的情報記録媒体及び情報を記録もしくは再生する光学 的情報記録再生装置に関する。
背景技術
円盤状の光学的情報記録媒体を使用する光学的情報記録再生装置はコ ンパクトディスク (C D ) プレーヤやミニディスク (M D ) レコーダな どさまざまな形態の装置があるが、 近年さらに情報記録媒体や記録再生 装置の小型化が進められている。
以下図面を参照しながら、 上記した従来の光学的情報記録媒体と光学 的情報記録再生装置の一例について説明する。
図 1 1は従来の光学的情報記録媒体と光学的情報記録再生装置の構成 を示す断面図である。 図 1 1において、 基板 5 1は光入射面 5 1 cとこ れに平行な情報層 5 1 eを有している。 基板 5 1には中心近傍に光入射 面 5 1 cに平行なターンテーブル設置面 5 1 bと、 中心孔である芯出し 部 5 1 aが形成されている。 基板 5 1のターンテーブル設置面 5 1 に 対向する面上には磁性体で形成された吸引板 5 2が固定され光学的情報 記録媒体を構成している。 5 3は基板 5 1を搭載するターンテーブルで あり、 ターンテーブル芯出し部材 5 3 aがー体に構成されている。 夕一 ンテーブル 5 3の中にマグネット 5 4が固定され、 保持部材を構成して いる。 ターンテーブル 5 3は回転部材であるスピンドルモータ 5 5に固 定されている。 ターンテーブル芯出し部材 5 3 aとスピンドルモータ 5 5の回転中心軸は一致している。 基板 5 1の光入射面 5 1 cに光を照射 し情報の記録再生を行うピックアツプ 5 6は基板 5 1に対してターンテ 一ブル 5 3と同じ側に配置されている。 以上のように構成された光学的情報記録媒体と光学的情報記録再生装 置について、 以下その動作について説明する。
基板 5 1に設けられた芯出し部 5 1 aがターンテーブル 5 3上の夕一 ンテーブル芯出し部材 5 3 aに係合するように基板 5 1を夕一ンテ一ブ ル 5 3上に搭載する。 このとき、 基板 5 1の光入射面 5 1 cが夕一ンテ —ブル側にくる。 マグネッ ト 5 4と吸引板 5 2の間に発生する吸引力に よって基板 5 1をターンテーブル 5 3に押し付けている。 スピンドルモ —夕 5 5が回転することによりターンテーブル 5 3と基板 5 1がー体に 回転する。 基板 5 1に対して夕一ンテーブル 5 3と同じ側にあるピック アップ 5 6からの出射光が基板 5 1の光入射面 5 1 cから情報層 5 1 e に照射され、 情報の記録再生が行われる。 ピックアップ 5 6が基板 5 1 の半径方向に移動することによってピックアップ 5 6からの出射光が情 報領域 5 1 d全面にわたって照射可能であり情報の記録再生を行う。 光ディスクなどの円盤状の情報記録媒体は近年小型化が進み、 外形が 小さくなり、 情報の記録できる面積が小さくなつてきている。 図 1 1に おいて従来の光学的情報記録再生装置ではピックアップ 5 3はスピンド ルモータとの干渉により半径 R 2の位置より内周側に移動することが不 可能であり、 基板 5 1の中心近傍はピックアップからの出射光が照射で きないため、 情報の記録再生が不可能な領域となる。 また基板 5 1が夕 —ンテーブル 5 3と接するターンテーブル設置面 5 1 bもピックアップ 5 3からの出射光が照射できないため情報の記録再生が不可能な領域と なる。 例えば、 ミニディスクでは図 1 1中の基板の外径である D 5 1が 6 4 mmであり、 情報領域の直径は 3 2 mmから 6 1 mmである。 直径 6 4 mmの総面積のうち情報領域の面積の割合は 6 6 %である。 基板の 直径を小径の 5 0 mmにすると情報領域の割合は 4 7 %になってしまう c 情報領域の割合を増やすために記録再生が不可能な領域を小さくするに はターンテーブル 5 3およびターンテ一ブル設置面 5 1 bの外径を小さ くする必要がある。 しかし、 ターンテーブル 5 3およびターンテーブル 設置面 5 1 bの外径を小さくすると基板 5 1の保持が不安定になりスピ ンドルモータ 5 5の回転が正確に伝わらなかったり、 基板 5 1の面振れ が大きくなることにより基板 5 1の情報の記録再生が不安定になる恐れ があるため、 ターンテーブル 5 3の外径をあまり小さくすることは不可 能であった。 そのため、 基板 5 1の外径を小さくすると基板 5 1の総面 積に対する情報領域の割合が小さくなる問題を有していた。
発明の開示
本発明は、 前記従来の問題を解決するため、 基板の中心近傍まで記録 再生が可能な光学的情報記録媒体と光学的情報記録再生装置を提供する ことを目的とする。
前記目的を達成するため、 本発明の光学的情報記録媒体は、 基板と前 記基板の上のいずれかの層に光学的情報層を有し、 前記基板側及び前記 基板と反対の面から選ばれる少なくとも一方の面に光入射面を備えた光 学的情報記録媒体であって、 前記光入射面から前記光学的情報層への入 射光を阻害しない位置でかつ前記光学的情報層の一部または全部を覆う 位置に磁性クランプ層を備えたことを特徴とする。
次に本発明の光学的情報記録再生装置は、 基板と前記基板の上のいず れかの層に光学的情報層を有し、 前記基板側及び前記基板と反対の面か ら選ばれる少なくとも一方の面に光入射面を備え、 前記光入射面から前 記情報層への入射光を阻害しない位置でかつ前記光学的情報層の一部ま たは全部を覆う位置に磁性クランプ層を備えた光学的情報記録媒体に対 して、 前記光入射面側から前記情報層に光を照射する光ピックアツプ装 置と、
前記光学的情報記録媒体に対して前記光ピックアツプ装置と反対側に 位置し、 前記光学的情報記録媒体を保持する保持部材と、
前記保持部材に固定され前記クランプ層を磁性的に吸引する吸引部材 と、
前記保持部材を回転させる回転部材とを備えたことを特徴とする。 図面の簡単な説明
図 1は本発明の実施の形態 1における光学的情報記録媒体と光学的情 報記録再生装置を示す斜視図である。
図 2は本発明の実施の形態 1における光学的情報記録媒体と光学的情 報記録再生装置を示す断面図である。
図 3は本発明の実施の形態 1における光学的情報記録媒体と光学的情 報記録再生装置を示す断面図である。
図 4は本発明の実施の形態 1における光学的情報記録媒体の断面図で ある。
図 5は本発明の実施の形態 2における光学的情報記録媒体と光学的情 報記録再生装置の他の例を示す断面図である。
図 6は本発明の実施の形態 2における光学的情報記録媒体と光学的情 報記録再生装置の他の例を示す断面図である。
図 7は本発明の実施の形態 3における光学的情報記録媒体と光学的情 報記録再生装置の他の例を示す断面図である。
図 8は本発明の実施の形態 2における光学的情報記録媒体と光学的情 報記録再生装置の他の例を示す断面図である。
図 9は本発明の実施の形態 4における光学的情報記録媒体と光学的情 報記録再生装置の他の例を示す断面図である。
図 1 0は本発明の実施の形態 6における光学的情報記録媒体と光学的 情報記録再生装置の他の例を示す断面図である。
図 1 1は従来の光学的情報記録媒体と光学的情報記録再生装置を示す 断面図である。
1 基板、 2 吸引板、 3 ターンテーブル、 4 マグネット、 5 ス ピンドルモータ、 6 ピックアップ
発明を実施するための最良の形態
本発明の光学的情報記録媒体は、 光入射面から光学的情報層への入射 光を阻害しない位置でかつ光学的情報層の一部または全部を覆う位置に 磁性クランプ層を備える。 これにより、 光学的情報記録媒体の外径が小 さくなつても、 中心近傍まで情報の記録再生が可能であるので、 従来の 構成より記録容量を大きくすることができる。 また、 光学的情報記録再 生装置に取り付けらた磁性的に吸引する吸引部材と磁性クランプ層とは 互いに引き合うので、 光学的情報記録媒体を安定して固定できる。 本発明においては、 基板と光学的情報層がいずれも単一層であり、 光 入射面と反対の位置に磁性クランプ層を備えていてもよい。 また、 基板 が第 1の基板と第 1の光学的情報層、 および第 2の基板と第 2の光学的 情報層からなり、 第 1の基板と第 2の基板それぞれの光入射面と反対の 面を向かい合わせて貼り合わせる面に磁性クランプ層を形成してもよい 前記クランプ層は薄膜状であり、 蒸着法もしくはスパッ夕法によって 基板に直接形成してもよい。 また、 前記クランプ層は薄膜状であり、 光 学的情報層に密着して反射膜を兼用してもよい。
また、 前記クランプ層は、 前記反射膜に密着した保護層を兼用しても よい。
また、 前記クランプ層は薄板シート状であり、 前記基板に接着固定さ れていてもよい。
前記基板と前記クランプ層は、 樹脂材料を複合成型して固定してもよ い。 また、 前記クランプ層と第 1の基板および第 2の基板は、 樹脂材料 を複合成型して固定してもよい。 前記基板の中心位置を決めるための芯出部は、 前記クランプ層に 1以 上の孔形状及び凸形状から選ばれる少なくとも一つの芯出部を備えたこ とが好ましい。
また、 前記クランプ層の前記剛性が基板の剛性より高く、 かつ前記ク ランプ層の平面度が前記基板の平面度より高く、 前記基板に前記クラン プ層を固定することにより前記基板の平面度が前記クランプ層の平面度 に規制されていてもよい。
また、 前記基板の最大寸法が 8 0 mm以下でありかつ前記情報層の表 面積が前記基板の外形総面積の 8 0 %以上であることが好ましい。
次に本発明の光学的情報記録再生装置においては、 保持部材の外形形 状が前記光学的情報記録媒体の外形形状と略一致していることが好まし レ 。 これにより、 光学的情報記録媒体の外径が小さくなつても、 中心近 傍まで情報の記録再生が可能であるので、 従来の構成より記録容量を大 きくすることができる。
前記クランプ層の外形形状と前記基板の外形形状が略一致した光学的 情報記録媒体の外形形状に対して、 前記保持部材の外形形状を略一致さ せてもよい。
前記保持部材の剛性が前記クランプ層および前記基板の剛性より高く, 前記保持部材の平面度が前記クランプ層および前記基板の平面度より高 く、 前記クランプ層と前記吸引部材との吸引力によって基板の平面度が 前記保持部材の平面度によって規制されていてもよい。
本発明において、 前記クランプ層と前記吸引部材 (マグネッ ト) との 吸引力は 0 . 1 N以上 5 N以下の範囲が好ましく、 さらには 0 . 2 N以 上 3 N以下の範囲が好ましく、 とくに 0 . 2 N以上 2 N以下の範囲が好 ましい。 吸引力が 0 . 1 N未満では吸引効果を発揮することが困難であ り、 また 5 Nを越えるとコストが高くなり好ましくない。 以下、 本発明の実施の形態について、 図面を参照しながら説明する。
(実施の形態 1 )
図 1は光学的情報記録媒体と光学的情報記録再生装置の構成を示す斜 視図、 図 2、 図 3はその断面図である。 図 1及び図 2において、 1は基 板であり、 光入射面 1 cの裏側 1 eに磁性体で形成されたクランプ層で ある吸引板 2が固定され光学的情報記録媒体を構成している。 吸引板 2 の中心近傍には芯出し部 2 aを構成する孔が設けられている。 基板 1は 光入射面 1 cとこれに平行な情報層を有している。
本実施形態で用いたディスク構成は、 0. 34ミクロン毎にグループ とランドが交互に形成された直径 8 Omm、 厚み 0. 6mmのポリカー ポネート製信号記録用トラックを持つ基板を用いた。 図 4に示すように, ディスク状のポリカーボネート基板 2 1の上に A g反射層 22を厚さ 1 00 nmにスパッタリングで形成し、 第 1の誘電体層 2 3として Z n S - S i 02混合膜を厚さ 1 0 0 nmにスパッタリングで形成し、 記録層 24として G e : S b : T e = 20 : 2 5 : 5 5の原子%比の組成物を 厚さ 1 2 nmにスパッタリングで形成した。 その表面に第 2の誘電体層 2 5として T a 205を厚さ 50 nmにスパッタリングで形成し、 その 表面に光硬化アクリル樹脂をスピンコート法で塗布し、 紫外線 (UV) を用いて厚み 1 0 / mの透明保護膜 26を形成した。 次に透明保護膜 2 6の表面に、 ハードコート膜 2 7を形成した。 ハードコート膜 27は、 市販の紫外線硬化型のシリコーン樹脂コ一ト剤をスピンコートにより塗 布し、 その後紫外線硬化を行って形成した。 膜厚は 2 mであった。 こ の光情報ディスクは、 青色レーザ光をハ一ドコート膜 2 7側から入射す るタイプの DVDディスクである。
別に、 厚さ 0. 4mmの鉄にクロムを 1 8重量%含んだ磁性体ステン レス鋼シー卜から金型を用いてプレス工法によって打ち抜き、 直径 5 m mの中心孔を有する直径 4 0腿の円盤とし、 これを図 2に示すように基 板 1の光入射面 1 cの裏側 1 eに吸引板 2 (クランプ層) として、 ェポ キシ系接着剤を用いて貼り付けた。
以上のようにして形成した基板 1をターンテーブル 3に搭載した。 夕 ーンテーブル 3には、 中心近傍にターンテーブル芯出し部材 3 aがー体 に形成されていた。 夕一ンテ一ブル 3にはネオジム ·鉄 ·ボロン磁石で 形成された吸引部材であるマグネット 4が固定され保持部材を構成して いる。 ターンテーブル 3は回転部材であるスピンドルモータ 5に固定さ れている。 図 3において、 6はピックアップで基板 1に出射光を照射し 情報の記録再生を行う。
以上のように構成された光学的情報記録媒体と光学的情報記録再生装 置について、 以下その動作について説明する。
図 2において、 吸引板 2に設けられた芯出し部 2 aがターンテーブル 3に設けられたターンテーブル芯出し部材 3 aに係合するように基板 1 をターンテーブル 3上に搭載した。 このときマグネット 4と吸引板 2の 間に発生する吸引力によって基板 1がターンテーブル 3に押し付けられ た。 この吸引力は 2 Nであった。 ターンテーブル 3はスピンドルモータ 5に固定されており、 スピンドルモータ 5の回転により光学的情報記録 媒体が回転する。 このような動作により光学的情報記録媒体が光学的情 報記録再生装置に搭載された状態を図 3に示す。 図 3において、 ピック アップ 6から出射された光が基板 1の光入射面 1 cから情報層に照射さ れ、 情報の記録再生が行われる。 ピックアップ 6は移送手段 (図示せ ず) によって基板 1の半径方向に移動する。 ターンテーブル 3は基板 1 の光入射面 1 cに対向する面に位置している。
ピックアップ 6は従来例の図 1 1にて説明した R 2より小さい半径 R 1の位置まで移動可能であり、 ピックアップ 6からの出射光が基板 1の 中心近傍から外周までほぼ全面に照射することが可能になった。 すなわ ち、 記録不可能領域のほとんど存在しないほぼ基板全面が情報領域 1 d である光学的情報記録媒体が実現できた。 例えば図 1 1に示す従来の構 成では基板 5 1の外径 D 5 1を 5 0 mmとしたとき総面積に対する情報 領域の割合は 4 7 %であるが、 図 1に示す本実施例では情報領域の内径 を 6 mmとすると情報領域の割合は 8 7 %になる。 また、 従来の構成に おいて、 基板の外径が 5 0 mmの時と同じ面積の情報領域を実現するに は、 情報領域の内径を 6 mmにすると情報領域の外径は 3 6 . 3 mmと なり、 基板 1の外径 D 1を 3 8 mm程度まで小さくすることが可能であ る。
光学的情報記録再生装置のピックアップ 6とスピンドルモー夕 5がそ れぞれ基板 1の表裏にあるのでスピンドルモータ 5の外径は従来例より 大きくすることができるので、 同じトルクを得るのであれば薄型化が可 能である。 将来、 薄膜技術などを用いてピックアップ 6の光軸方向寸法 が小さくなれば情報記録再生装置の光軸方向寸法 (高さ寸法) を従来例 より小さくすることが可能である。
(実施の形態 2 )
この例では吸引板 2がターンテーブル 3に接する例を説明する。
図 5において光学的情報記録媒体を形成する方法は図 3および図 4に て説明した実施の形態 1と同様である。 基板 1の直径が 8 0删であり、 吸引板 2の直径は 7 8 mmであり、 吸引力は 2 Nであった。 実施の形態 2ではピックアップからの出射光が基板 1の中心近傍から外周までほぼ 全面に照射することが可能であり実施の形態 1と同様の効果が得られた。 また、 基板 1より吸引板 2の剛性および平面度を高くすることにより、 基板 1が薄く剛性の低いものであっても剛性および平面度が高い吸引板 2に接着固定することによりその平面度を向上させることができた。 本実施の形態 1では図 3に示すようにターンテーブル 3の中心部近傍 に構成されたターンテーブル芯出し部材 3 aに係合する芯出し部 2 aを 吸引板 2の中心部近傍に形成したが、 図 6に示すように吸引板 2の外周 がターンテーブル 3に係合する構成であっても同等の効果が得られる。 本実施の形態では芯出し部として吸引板に孔を設け、 ターンテーブル に凸形状のターンテーブル芯出し部材を設けたが、 図 8に示すように凸 形状の芯出し部 2 aと凹形状のターンテーブル芯出し部材 3 aを設けて も同等の効果が得られる。
(実施の形態 3 )
この例では吸引板 2挟んで基板が互いに光入射面が外を向くように貼 り合わされた例を説明する。
図 7において、 厚さ 0 . 4 mmの鉄にクロムを 1 8重量%含んだ磁性 体ステンレス鋼シートを金型を用いてプレス工法によって打ち抜き、 直 径 8 O mmの円盤状の吸引板 2を形成した。 吸引力は 2 Nであった。 ま た中心に直径 5 mmの孔を有する直径 8 0 mmの基板 1 1, 1 2に、 図 4にて説明した実施の形態 1と同様に反射層、 誘電体層、 記録層、 保護 膜、 ハードコート膜を形成した。 吸引板 2を挟んで基板 1 1、 1 2が互 いに光入射面が外を向くようにエポキシ系接着剤を用いて貼り合わせ、 光学的情報記録媒体を形成した。 実施の形態 3ではピックアツプからの 出射光が基板 1 1 , 1 2の中心近傍から外周までほぼ全面に照射するこ とが可能であり、 実施の形態 1と同等の効果が得られた。 また、 基板 1 1, 1 2より吸引板 2の剛性および平面度を高くすることにより、 基板 1 1, 1 2が薄く剛性の低いものであっても剛性および平面度が高い吸 引板 2に接着固定することによりその平面度を向上させることができた。
(実施の形態 4 )
この例では反射膜とクランプ層を 1つの材料で兼用した例を説明する。 図 9に示すように基板 1の光入射面 1 Cと反対の面上に蒸着により二 ッケルを 5 厚で積層させ反射膜 7を形成し、 その表面に光硬化ァク リル樹脂をスピンコート法で塗布し、 紫外線を用いて厚み 1 0 mの保 護膜 8を形成した。 ニッケル反射膜 7は磁性体でありマグネット 4に吸 引されるので実施の形態 1と同等の効果が得られた。 吸引力は 0 . 5 N であった。 この例では、 クランプ層として吸引板を接着する必要がない ので低コストな光学的情報記録媒体が実現できた。
(実施の形態 5 )
この例では吸引板に基板を一体成形する例を説明する。
まず、 基板を成形する金型内に吸引板を挿入する。 吸引板は予めクロ ムを 1 8重量%含んだ厚さ 0 . 4 mmのステンレス鋼板をプレスによつ て直径 4 0 mmの円盤状に形成した。 基板の材料であるポリ力一ポネー トを溶融させ金型内に注入した。 ポリカーボネートが冷却硬化し、 吸引 板表面に密着固定された直径 8 0 mmの基板を形成した。 基板の吸引板 が固着した面と反対側の表面に図 4と同様に反射層、 誘電体層、 記録層, 保護膜、 八ードコート膜を形成し、 光学的情報記録媒体を形成した。 吸 引板の吸引力は 2 Nであった。
本例のように、 吸引板を一体成形する構成であっても実施の形態 1と 同等の効果が得られた。 さらに、 吸引板を接着する必要がないので低コ ス卜な光学的情報記録媒体が実現できる。
本実施に形態において、 吸引板 2は厚さ 0 . 1 mm前後のシート状で あり、 基板 1に接着固定された構成であっても同等の効果が得られる。 本実施に形態において、 光ピックアツプにて記録再生される情報が基 板に記録されており、 この基板に吸引板を接着固定する構成であるが、 吸引板に情報が記録されており、 この吸引板に樹脂材料を一体成形する ことにより基板を形成する構成の光学的情報記録媒体であっても同等の 効果が得られる。
(実施の形態 6 )
図 1 0において、 基板 1は図 4にて説明した実施の形態 1と同様に反 射層、 誘電体層、 記録層、 保護膜、 ハードコート膜を形成した。 直径は 8 0 mmであった。 吸引板 2はエポキシ樹脂にネオジム ·鉄 ·ポロン磁 石の粉末を混合したポンド磁石を用いて、 射出成形して厚さ l mm、 直 径 7 0 mmの円盤状に形成した。 基板 1と吸引板 2はエポキシ系接着剤 を用いて貼り合わせ、 光学的情報記録媒体を形成した。 ターンテーブル 3は鉄にクロムを 1 8重量%含んだ磁性体ステンレス鋼を切削加工し形 成した。 吸引板とターンテーブル間に働く磁気吸引力 (2 N ) により基 板が夕一ンテーブル上に固定できた。 実施の形態 6ではピックアップか らの出射光が基板 1の中心近傍から外周までほぼ全面に照射することが 可能であり実施の形態 1と同等の効果が得られた。
本実施の形態では光学的情報記録媒体は円盤形状であるが、 四角形な ど円盤形状以外の形であってもよい。
本実施の形態では光学的情報記録再生装置の動作時は光学的情報記録 媒体はスピンドルモータによって回転する構成であるが、 基板に対し平 行移動する構成であっても同等の効果が得られる。
本実施の形態では光学的情報記録再生装置の動作時は光学的情報記録 媒体はスピンドルモータによって回転しピックアツプが移送手段により 移動する構成であるが、 光学的情報記録媒体は回転動作せずにピックァ ップのみが基板対し平行に移動する構成であっても同等の効果が得られ る。
産業上の利用可能性
本発明は、 光学的情報記録媒体の外径が小さくなつても、 中心近傍ま で情報の記録再生が可能であるので、 従来の構成より記録容量を大きく することができる。 また、 スピンドルモー夕の薄型化も可能であるので 光学的情報記録媒体の小径化と合わせて光学的情報記録再生装置の小型 化が実現可能になる。 また、 基板と吸引板の外径が略同一であると基板 が薄くなり反りなどが生じても吸引板に固定することによって精度を向 上させることが可能である。 保持部材の外径が光学的情報記録媒体の外 径と略同一であると、 光学的情報記録媒体を保持部材上に搭載する際、 保持部材の中心と光学的情報記録媒体の中心が合わせやすくなり、 かつ 光学的情報記録媒体の保持が安定することにより記録再生動作が安定し た光学的情報記録媒体と光学的情報記録再生装置が実現可能となる。

Claims

請求の範囲
1 . 基板と前記基板の上のいずれかの層に光学的情報層を有し、 前記基 板側及び前記基板と反対の面から選ばれる少なくとも一方の面に光入射 面を備えた光学的情報記録媒体であって、 前記光入射面から前記光学的 情報層への入射光を阻害しない位置でかつ前記光学的情報層の一部また は全部を覆う位置に磁性クランプ層を備えたことを特徴とする光学的情 報記録媒体。
2 . 前記基板と前記光学的情報層がいずれも単一層であり、 前記光入射 面と反対の位置に磁性クランプ層を備えた請求項 1に記載の光学的情報 記録媒体。
3 . 前記基板が第 1の基板と第 1の光学的情報層、 および第 2の基板と 第 2の光学的情報層からなり、 前記第 1の基板と前記第 2の基板それぞ れの前記光入射面と反対の面を向かい合わせて貼り合わせる面に磁性ク ランプ層を備えたことを特徴とする光学的情報記録媒体。
4 . 前記クランプ層は薄膜状であり、 蒸着法もしくはスパッ夕法によつ て前記基板に直接形成した請求項 1に記載の光学的情報記録媒体。
5 . 前記クランプ層は薄膜状であり、 光学的情報層に密着した反射膜を 兼用している請求項 1に記載の光学的情報記録媒体。
6 . 前記クランプ層は、 前記反射膜に密着した保護層を兼用している請 求項 5に記載の光学的情報記録媒体。
7 . 前記クランプ層は薄板シート状であり、 前記基板に接着固定されて いる請求項 1に記載の光学的情報記録媒体。
8 . 前記基板と前記クランプ層は、 樹脂材料を複合成型して固定する請 求項 1に記載の光学的情報記録媒体。
9 . 前記クランプ層と第 1の基板および第 2の基板は、 樹脂材料を複合 成型して固定する請求項 2に記載の光学的情報記録媒体。
1 0 . 前記基板の中心位置を決めるための芯出部として、 前記クランプ 層に 1以上の孔形状及び凸形状から選ばれる少なくとも一つの芯出部を 備えた請求項 1に記載の光学的情報記録媒体。
1 1 . 前記クランプ層の前記剛性が基板の剛性より高く、 かつ前記クラ ンプ層の平面度が前記基板の平面度より高く、 前記基板に前記クランプ 層を固定することにより前記基板の平面度が前記クランプ層の平面度に 規制されている請求項 1に記載の光学的情報記録媒体。
1 2 . 前記基板の最大寸法が 8 0 mm以下でありかつ前記情報層の表面 積が前記基板の外形総面積の 8 0 %以上である請求項 1に記載の光学的 情報記録媒体。
1 3 . 基板と前記基板の上のいずれかの層に光学的情報層を有し、 前記 基板側及び前記基板と反対の面から選ばれる少なくとも一方の面に光入 射面を備え、 前記光入射面から前記情報層への入射光を阻害しない位置 でかつ前記光学的情報層の一部または全部を覆う位置に磁性クランプ層 を備えた光学的情報記録媒体に対して、 前記光入射面側から前記情報層 に光を照射する光ピックアップ装置と、
前記光学的情報記録媒体に対して前記光ピックァップ装置と反対側に 位置し、 前記光学的情報記録媒体を保持する保持部材と、
前記保持部材に固定され前記クランプ層を磁性的に吸引する吸引部材 と、
前記保持部材を回転させる回転部材とを備えたことを特徴とする光学 的情報記録再生装置。
1 4 . 前記保持部材の外形形状が前記光学的情報記録媒体の外形形状と 略一致した請求項 1 3に記載の光学的情報記録再生装置。
1 5 . 前記クランプ層の外形形状と前記基板の外形形状が略一致した光 学的情報記録媒体の外形形状に対して、 前記保持部材の外形形状が略一 致した請求項 1 3記載の光学的情報記録再生装置。
1 6. 前記保持部材の剛性が前記クランプ層および前記基板の剛性より 高く、 前記保持部材の平面度が前記クランプ層および前記基板の平面度 より高く、 前記クランプ層と前記吸引部材との吸引力によって基板の平 面度が前記保持部材の平面度によって規制されている請求項 1 3に記載 の光学的情報記録再生装置。
1 7. 前記基板の最大寸法が 8 Omm以下でありかつ前記情報層の表面 積が前記基板の外形総面積の 8 0 %以上である請求項 1 3に記載の光学 的情報記録媒体。
1 8. 前記クランプ層と前記吸引部材との吸引力が 0. 1 N〜 5 Nの範 囲である請求項 1 3に記載の光学的情報記録媒体。
PCT/JP2002/003974 2001-04-23 2002-04-22 Support d'enregistrement d'information optique et appareil d'enregistrement/reproduction d'information optique WO2002089137A1 (fr)