WO2002064480A1 - Cable principal d'ascenseur - Google Patents

Cable principal d'ascenseur Download PDF

Info

Publication number
WO2002064480A1
WO2002064480A1 PCT/JP2001/001130 JP0101130W WO02064480A1 WO 2002064480 A1 WO2002064480 A1 WO 2002064480A1 JP 0101130 W JP0101130 W JP 0101130W WO 02064480 A1 WO02064480 A1 WO 02064480A1
Authority
WO
WIPO (PCT)
Prior art keywords
strand
outer layer
main rope
strands
inner layer
Prior art date
Application number
PCT/JP2001/001130
Other languages
English (en)
French (fr)
Inventor
Takenobu Honda
Original Assignee
Mitsubishi Denki Kabushiki Kaisha
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Denki Kabushiki Kaisha filed Critical Mitsubishi Denki Kabushiki Kaisha
Priority to PCT/JP2001/001130 priority Critical patent/WO2002064480A1/ja
Priority to CNB018081193A priority patent/CN1183026C/zh
Priority to EP01904515A priority patent/EP1371597B1/en
Priority to JP2002564419A priority patent/JP5398944B2/ja
Publication of WO2002064480A1 publication Critical patent/WO2002064480A1/ja

Description

エレべ一夕の主索
技術分野
この発明は、 昇降路内にかごを吊り下げる合成繊維ロープ製のエレべ一夕の主 索に関するものである。 明
背景技術
細
図 5は例えば特開平 7— 2 6 7 5 3 4号公報に示された従来のエレべ一夕の主 索の構造を示す斜視図である。 図において、 心線 2 1の周囲には、 複数本の内層 ストランド 2 2と、 これらの内層ストランド 2 2間の間隙に配置されている充填 ストランド 2 3とを有する内層部 2 4が配置されている。 各内層ストランド 2 2 は、 互いに撚り合わせられているァラミ ド繊維製の複数本の素線とポリウレタン 等の含浸材とにより構成されている。 充填ストランド 2 3は、 例えばポリアミド により構成されている。
複数本の外層ストランド 2 5を有する外層部 2 6は、 内層部 2 4の外周を覆う ように配置されている。 各外層ストランド 2 5は、 内層ストランド 2 2と同様に、 互いに撚り合わせられているァラミド繊維製の複数本の素線とポリウレタン等の 含浸材とにより構成されている。
内層部 2 4と外層部 2 6との間には、 駆動シーブ等の綱車 （図示せず） におけ るストランド 2 2 , 2 5相互間の摩擦によるストランド 2 2， 2 5の摩耗を避け るための内層被覆 （摩擦低減被覆） 2 7が配置されている。 また、 外層部 2 6の 外周部には、 外層被覆 （保護被覆） 2 8が配置されている。
上記のように構成された従来のエレべ一夕の主索では、 エレべ一夕の運転時に 綱車との接触による圧力を受けるとともに、 綱車での曲げにより内部に変形及び 滑りが生じるため、 長期間使用していると、 摩耗による素線の断線が発生する。 このような素線の断線は、 外層ストランド 2 5で多く発生する。
これに対し、 従来の主索では、 内層部 2 4の引張強度と外層部 2 6の引張強度 とが同等に設定されているため、 摩耗により外層ストランド 2 5の素線が損傷し、 外層部 2 6の引張強度が著しく低下した場合、 内層部 2 4のみで荷重を支持する ことになり、 全体の半分の引張強度しか確保されない。
また、 例えば特開平 8— 2 6 1 9 7 2号公報には、 力一ボン繊維からなる導電 線をストランドに撚り合わせ、 その導電線に通電し、 通電状態を監視することで、 導電線の切断を検出し、 ストランドの損傷を検出する方法が示されている。
しかし、 ァラミド繊維よりもカーボン繊維の方が高強度であるため、 導電線の 摩耗が優先的に起こらず、 強度部材であるァラミ ド繊維製の素線が導電線よりも 先に摩耗し断線する可能性があり、 ストランドの損傷を安定して検出することが できず、 ストランドの寿命の判断が難しかった。 発明の開示
この発明は、 上記のような課題を解決するためになされたものであり、 一部の ストランドが寿命に達したときに十分な残存強度を確保することができ、 またス トランドの損傷をより安定して検出することができるエレべ一夕の主索を得るこ とを目的とする。
この発明によるエレべ一夕の主索は、 昇降路内にかごを吊り下げるためのもの であって、 合成樹脂繊維からなる複数本の素線を撚り合わせた複数本の内層スト ランドを有する内層部、 及び合成樹脂繊維からなる複数本の素線を撚り合わせた 複数本の外層ストランドを有し、 内層部の外周を覆うように配置されている外層 部を備え、 外層部の引張強度が内層部の引張強度よりも低く設定されているもの である。 図面の簡単な説明
図 1はこの発明の実施の形態 1によるエレペータの主索の断面図、
図 2は図 1の主索の内部構造を示す側面図、
図 3はこの発明の実施の形態 2によるエレべ一夕の主索の断面図、
図 4はこの発明の実施の形態 3によるエレべ一タの主索の断面図、
図 5は従来のエレべ一夕の主索の構造の一例を示す斜視図である。 発明を実施するための最良の形態
以下、 この発明の好適な実施の形態について図面を参照して説明する。
実施の形態 1 .
図 1はこの発明の実施の形態 1によるエレべ一夕の主索の断面図、 図 2は図 1 の主索の内部構造を示す側面図である。
図において、 内層部 1は、 互いに撚り合わせられている複数本の内層ストラン ド 2と、 これらの内層ストランド 2間の間隙に配置され撚り合わせられている充 填ストランド 3とを有している。 各内層ストランド 2は、 互いに撚り合わせられ ているァラミド繊維製の複数本の素線とポリウレタン等の含浸材とにより構成さ れている。
充填ストランド 3は、 例えばポリアミドにより構成されている。 設計上の内層 部 1の引張強度には、 充填ストランド 3の強度は加算されない。
外層部 4は、 複数本の外層ストランド 5を有し、 内層部 1の外周を覆うように 撚り合わせられ配置されている。 各外層ストランド 5は、 内層ストランド 2と同 様に、 互いに撚り合わせられているァラミド繊維製の複数本の素線とポリウレ夕 ン等の含浸材とにより構成されている。
内層部 1と外層部 4との間には、 駆動シープ等の綱車 （図示せず） におけるス トランド 2， 5相互間の摩擦によるストランド 2 , 5の摩耗を避けるための内層 被覆 （摩擦低減被覆） 6が配置されている。 また、 外層部 4の外周部には、 外層 被覆 （保護被覆） 7が配置されている。
内層部 1と外層部 4とは、 内層被覆 6により区分けされている。 また、 外層ス トランド 5の撚り方向は、 内層ストランド 2の撚り方向に対して逆になつており、 これによつても内層部 1と外層部 4とが区分けされている。
また、 外層部 4の引張強度は、 内層部 1の引張強度よりも低く設定されている c 具体的には、 内層部 1は、 主索全体の引張強度に対して 6 0 %以上の引張強度を 有している。従って、 外層部 4の引張強度は、 主索全体の引張強度に対して 4 0 %未満である。
一部の外層ストランド 5には、 断線されて通電が遮断されることにより外層ス トランド 5の損傷を検出するための導電線 8がそれそれ撚り合わせられている。 導電線 8としては、 例えば導電性の力一ボン繊維を束ねてなる線が用いられる。 また、 導電線 8は、 互いに隣接する少なくとも一対の外層ストランド 5にそれそ れ撚り合わせられている。
図 2に示すように、 導電線 8が撚り合わせられている一対の外層ストランド 5 では、 導電線 8の撚りピッチが互いに異なっている。 また、 導電線 8が撚り合わ せられている一対の外層ストランド 5のうち一方の外層ストランド 5では、 導電 線 8の撚りピッチが導電線 8の太さの 2倍より小さいピッチに設定されている。 例えば直径 2 mmの導電線 8を用いた場合、 その導電線 8の撚りピッチは 4 mm 未満となる。
このような主索では、 主に外層ストランド 5で摩耗による素線の損傷が発生す るため、 内層部 1よりも外層部 4の寿命の方が短いが、 外層部 4の強度が著しく 低下しても、 外層部 4よりも引張強度の高い内層部 1が残っているため、 十分な 残存強度を確保することができる。
一般的なエレべ一夕では、 主索の引張強度は、 安全率を 1 0倍として設計され る。 また、 非常止め装置等の安全装置が作動したときには、 通常運転時に作用す る荷重の約 2〜 6倍の荷重が主索に作用する。 外層部 4の強度が寿命により低下 したとき、 6倍の荷重が作用した場合、 その荷重を内層部 1だけで支持できるこ とが望ましい。 従って、 主索全体の引張強度に対して 6 0 %以上の引張強度を内 層部 1に持たせておけば、 残存強度としては十分であると考えられる。
実際には、 複数本の主索によりかごが吊り下げられていることが多く、 全ての 主索が同時に寿命に達することはないと考えられるため、 1本の主索について、 6 0 %以上の残存強度を有していれば十分である。
また、 外層ストランド 5の撚り方向は、 内層ストランド 2の撚り方向に対して 逆になつているため、 外層ストランド 5は内層ストランド 2に対して交差する。 これにより、 摩耗による素線の損傷は、 外層ストランド 5の内層部 1側で発生し やすくなり、 外層ストランド 5の寿命が主索全体としての寿命を支配することに なる。 従って、 予定外の部位を起点とした主索の損傷による不測の事故を防止す ることができる。 さらに、 主索全体の寿命を支配する外層ストランド 5に導電線 8を配置したの で、 損傷をより安定して検出することができ、 主索の寿命をより正確に把握する ことができる。 具体的には、 導電線 8が切断され、 通電が遮断されると、 エレべ 一夕の運転が停止され、 警報が発せらて、 主索が寿命に達したことが知らされる とになる。
さらにまた、 導電線 8は、 ァラミ ド繊維よりも高強度であるため、 ァラミ ド繊 維との接触では主にァラミ ド繊維が摩耗され、 導電線 8よりも先に素線が断線さ れてしまう。 これに対し、 実施の形態 1では、 互いに隣接する複数対の外層スト ランド 5に導電線 8がそれそれ撚り合わせられているため、 隣接する外層ストラ ンド 5の導電線 8が互いに接触し、 導電線 8相互の接触により導電線 8が摩耗さ れ、 外層ストランド 5の損傷をより安定して検出することができる。
このように、 導電線 8が撚り合わせられた外層ストランド 5の対は、 主索 1本 について、 少なくとも 3箇所以上に配置することが、 外層ストランド 5の損傷を 安定して検出するために好適である。
また、 隣接する外層ストランド 5の導電線 8が互いに等しいピッチで撚り合わ せられていると、 導電線 8相互の接触が生じない可能性がある。 これに対し、 実 施の形態 1では、 隣接する外層ストランド 5の導電線 8の撚りピッチが互いに異 なっているため、 高価なカーボン繊維からなる導電線 8の使用量を最小限に抑え つつ、 より確実に導電線 8相互を接触させることができる。
さらに、 一方の外層ストランド 5で、 導電線 8の撚りピッチが導電線 8の太さ の 2倍より小さいピッチに設定されているため、 導電線 8の使用量を最小限に抑 えつつ、 より確実に導電線 8相互を接触させることができる。
ここで言う撚りピッチは、 1本の外層ストランド 5に対する撚りピッチのこと であり、 例えば 1本の外層ストランド 5に 2本の導電線 8を撚り合わせる場合、 そのうちの 1本の導電線 8だけを見ると、 導電線 8の太さの 4倍より小さいピッ チで撚り合わせられていることになる。 実施の形態 2 .
次に、 図 3はこの発明の実施の形態 2によるエレべ一夕の主索の断面図である c 図において、 外層部 1 1は、 複数本の外層ストランド 1 2を有し、 内層部 1の外 周を覆うように配置されている。 各外層ストランド 1 2は、 内層ストランド 2と 同様に、 互いに撚り合わせられているァラミド繊維製の複数本の素線とポリウレ タン等の含浸材とにより構成されている。
外層ストランド 1 2の撚り方向は、 内層ストランド 2の撚り方向に対して逆に なっている。 一部の外層ストランド 1 2には、 導電線 8がそれそれ撚り合わせら れている。
また、 外層ストランド 1 2の断面形状は、 外層部 1 1の周方向に沿って延びる 偏平形状である。 .内層部 1と外層部 1 1とは直接接触しており、 導電線 8を含む 外層ストランド 1 2に接触する内層ストランド 2には、 外層ストランド 1 2の素 線の強度以上の強度を有する接触線 1 3が撚り合わせられている。 ここでは、 接 触線 1 3として、 導電線 8と同様の材料構成の線が使用される。
さらに、 外層部 1 1の引張強度は、 内層部 1の引張強度よりも低く設定されて いる。 具体的には、 内層部 1は、 主索全体の引張強度に対して 6 0 %以上の引張 強度を有している。 従って、 外層部 1 1の引張強度は、 主索全体の引張強度に対 して 4 0 %未満である。
さらにまた、 外層ストランド 1 2の撚りピッチを内層ストランド 2の撚りビッ チよりも大きくすることにより、 外層部 1 1の単位面積当たりの弓 I張強度が内層 部 1のそれよりも低く設定されている。
このようなエレべ一夕の主索では、 主に外層ストランド 1 2で摩耗による素線 の断線が発生し、 外層部 1 1の強度が著しく低下しても、 外層部 1 1よりも引張 強度の高い内層部 1が残っているため、 十分な残存強度を確保することができる また、 内層部 1と外層部 1 1とを直接接触させ、 導電線 8を含む外層ストラン ド 1 2に接触する内層ストランド 2に接触線 1 3を撚り合わせたので、 接触線 1 3との接触により導電線 8が摩耗され、 外層ストランド 5の寿命を安定して検出 することができる。
なお、 接触線 1 3は導電線 8を摩耗させるための線であるため、 接触線 1 3に は通鼋する必要はない。 しかし、 接触線 1 3を導電性の材料で構成し、 接触線 1
3に通電することにより、 内層ストランド 2の損傷を検出することもできる。 また、 接触線 1 3の強度は、 素線の強度以上であれば、 素線よりも効果的に導 電線 8を摩耗させるが、 導電線 8の強度以上であれば、 より効果的に導電線 8を 摩耗させることができる。
さらに、 外層部 1 1の単位面積当たりの引張強度が内層部 1のそれよりも低く 設定されているため、 主索に過負荷が作用した場合、 内層部 1よりも先に外層部 1 1が破断され、 外層部 1 1の破断が導電線 8の切断により検出される。 即ち、 過負荷による主索全体の破断を未然に防止することができる。
但し、 外層部 1 1の単位面積当たりの引張強度を下げる場合、 通常運転時にお ける内層部 1との接触による外層部 1 1の損傷も顕著になる恐れがあるため、 内 層部 1の径方向外側に配置された内層ストランド 2の素線の撚り方向と外層スト ランド 1 2の素線の撚り方向とを互いに平行にするのが好ましい。基本的には、 内層ストランド 2も外層ストランド 1 2も、 繊維の方向を主索の長さ方向に対し て平行に近付けるのが好ましい。
さらに、 外層ストランド 1 2の断面形状が外層部 1 1の周方向に沿って延びる 偏平形状であるため、 主索の直径を小さく抑えつつ、 強度を確保することができ る。 また、 損傷の検出感度を高めることができるとともに、 曲げにより発生する 応力を低減することができ、 実装密度の高い主索を提供することができる。 さら に、 内層部 1に潤滑油を含浸した場合に、 外層部 1 1外への潤滑油の流出を防止 することができ、 外層ストランド 1 2と外層被覆 7との密着性の低下を防止する ことができる。
なお、 外層ストランド 1 2は、 円形断面で製作された後、 内層部 1の外周に卷 き付けられる際、 加熱軟化され、 ダイスに通して断面形状が変形される。 また、 内層部 1への巻き付け後にダイスに通し、 断面形状を変形させてもよい。 実施の形態 3 .
次に、 図 4はこの発明の実施の形態 3によるエレべ一夕の主索の断面図である c 図において、 内層部 1 5は、 互いに撚り合わせられている複数本の内層ストラン ド 1 6と、 これらの内層ス卜ランド 1 6間の間隙に配置され撚り合わせられてい る充填ストランド 3とを有している。 各内層ストランド 1 6は、 互いに撚り合わ せられているァラミド繊維製の複数本の素線とポリウレ夕ン等の含浸材とにより 構成されている。
外層部 1 1は、 実施の形態 2と同様である。 内層部 1 5と外層部 1 1とは、 直 接接触している。 外層ストランド 1 2の撚り方向は、 内層ストランド 1 6の撚り 方向に対して逆になつている。 少なくとも一部の外層ストランド 1 2の内層スト ランド 1 6側には、 外層部 1 1の長さ方向と平行に延びている導電線 1 7が配置 されている。 導電線 1 7としては、 例えばカーボン繊維を束ねてなる線が用いら れる。
導電線 1 7を含む外層ストランド 1 2に接触する内層ストランド 1 6には、 導 電線 1 7の強度以上の強度を有する接触線 1 3が撚り合わせられている。 ここで は、 接触線 1 3として、 導電線 1 7と同様の材料構成の線が使用される。
また、 外層ストランド 1 2に接触する内層ストランド 1 6の断面形状は、 円形 断面よりも外層ストランド 1 2との接触面積が広がるように異形化されている。 内層ストランド 1 6は、 円形断面で製作された後、 内層部 1 5として撚り合わせ られる際、 加熱軟化され、 ダイスに通して断面形状が変形される。 また、 全ての 内層ストランド 1 6を撚り合わせた後にダイスに通し、 断面形状を変形させても よい。
内層ストランド 1 6間には、 潤滑油が塗布 '含浸されている。 潤滑油としては、 例えばシリコン系やパラフィン系の合成油が使用される。 また、 内層ストランド 1 6の材料として耐油性に優れたポリウレタン樹脂を用いている場合には、 鉱油 系の潤滑油を使用してもよい。
さらに、 外層部 1 1の弓 I張強度は、 内層部 1 5の弓 I張強度よりも低く設定され ている。 具体的には、 内層部 1 5は、 主索全体の引張強度に対して 6 0 %以上の 引張強度を有している。 従って、 外層部 1 1の引張強度は、 主索全体の引張強度 に対して 4 0 %未満である。
このようなエレべ一夕の主索では、 外層ストランド 1 2の内層ストランド 1 6 側に外層部 1 1の長さ方向と平行に導電線 1 7が配置されているため、 接触線 1 3をより確実に導電線 1 7に接触させることができ、 外層ストランド 1 2の損傷 の検出感度を高めることができる。 また、 内層ストランド 1 6の断面形状が異形化されているので、 内層ストラン ド 1 6及び外層ストランド 1 2の接触圧力を低減させることができる。 また、 内 層ストランドが円形断面の場合、 外層ストランド 1 2は内層ストランドの外周の 一部のみと接触し、 内層ストランド間を渡ることになるが、 異形化された内層ス トランド 1 6を用いた場合、 外層ストランド 1 2は、 より広い面積で内層ストラ ンド 1 6と接触しながら撚られるため、 外層ストランド 1 2に生じる曲げ応力を 低減することができ、 外層ストランド 1 2の寿命を延ばすことができる。
さらに、 内層ストランド 1 6間に潤滑油が塗布 '含浸されているため、 異形ィ匕 された内層ストランド 1 6間の滑りを円滑にし、 エレべ一夕運転時に主索が受け る変動荷重による内層ストランド 1 6の微動摩耗を抑制することができる。

Claims

請求の範囲
1 . 昇降路内にかごを吊り下げるエレべ一夕の主索であって、
合成樹脂繊維からなる複数本の素線を撚り合わせた複数本の内層ストランドを 有する内層部、 及び
合成樹脂繊維からなる複数本の素線を撚り合わせた複数本の外層ストランドを 有し、 上記内層部の外周を覆うように配置されている外層部
を備え、 上記外層部の引張強度が上記内層部の引張強度よりも低く設定されて いるエレべ一夕の主索。
2 . 上記内層ストランドは互いに撚り合わされており、 上記外層ストランドは、 上記内層ストランドの撚り方向に対して逆方向に互いに撚り合わされている請求 項 1記載のエレべ一夕の主索。
3 . 上記内層部と上記外層部との間には、 内層被覆が配置されている請求項 1記 載のエレべ一夕の主索。
4 . 上記内層部は、 全体の引張強度に対して 6 0 %以上の引張強度を有している 請求項 1記載のエレべ一夕の主索。
5 . 少なくとも一部の上記外層ストランドには、 断線されて通電が遮断されるこ とにより上記外層ストランドの損傷を検出するための導電線が撚り合わせられて I、る請求項 1記載のエレべ一夕の主索。
6 . 互いに隣接する少なくとも一対の上記外層ストランドに、 上記導電線がそれ それ撚り合わせられている請求項 5記載のェレぺ一夕の主索。
7 . 上記一対の外層ストランドでは、 上記導電線の撚りピッチが互いに異なって いる請求項 6記載のェレべ一夕の主索。
8 . 上記一対の外層ストランドのうち一方の外層ストランドでは、 上記導電線の 撚りピッチが上記導電線の太さの 2倍より小さいピッチに設定されている請求項 6記載のエレべ一夕の主索。
9 . 上記内層部と上記外層部とが直接接触しており、 上記導電線を含む外層スト ランドに接触する内層ストランドには、 上記外層ストランドの素線の強度以上の 強度を有する接触線が撚り合わせられている請求項 5記載のエレべ一夕の主索。
1 0 . 上記外層部の単位面積当たりの引張強度が、 上記内層部のそれよりも低く 設定されている請求項 5記載のエレべ一夕の主索。
1 1 . 上記外層ストランドの撚りピツチが上記内層ストランドの撚りピッチより も大きく設定されている請求項 1 0記載のエレべ一夕の主索。
1 2 . 上記内層部の径方向外側に配置された内層ストランドの素線の撚り方向と 上記外層ストランドの素線の撚り方向とが互いに平行である請求項 1 0記載のェ レペータの主索。
1 3 . 上記外層ストランドの断面形状は、 上記外層部の周方向に沿って延びる偏 平形状である請求項 1記載のエレべ一夕の主索。
1 4 . 上記内層部と上記外層部とが直接接触しており、 少なくとも一部の上記外 層ストランドの上記内層ストランド側には、 上記外層部の長さ方向と平行に延び、 断線されて通電が遮断されることにより上記外層ストランドの損傷を検出するた めの導電線が配置されており、 上記導電線を含む上記外層ストランドに接触する 内層ストランドには、 上記導電線の強度以上の強度を有する接触線が撚り合わせ られている請求項 1 3記載のエレべ一夕の主索。
1 5 . 上記内層部と上記外層部とが直接接触しており、 上記外層ストランドに接 触する上記内層ストランドの断面形状は、 円形断面よりも上記外層ストランドと の接触面積が広がるように異形化されている請求項 1 3記載のエレべ一夕の主索 c
1 6 . 上記内層ストランド間には潤滑油が与えられている請求項 1記載のエレべ 一夕の主索。
PCT/JP2001/001130 2001-02-16 2001-02-16 Cable principal d'ascenseur WO2002064480A1 (fr)