WO2001070518A1 - Films decoratifs transparents unidirectionnellement - Google Patents

Films decoratifs transparents unidirectionnellement Download PDF

Info

Publication number
WO2001070518A1
WO2001070518A1 PCT/JP2001/001815 JP0101815W WO0170518A1 WO 2001070518 A1 WO2001070518 A1 WO 2001070518A1 JP 0101815 W JP0101815 W JP 0101815W WO 0170518 A1 WO0170518 A1 WO 0170518A1
Authority
WO
WIPO (PCT)
Prior art keywords
film
coating layer
transparent resin
transparent
decorative film
Prior art date
Application number
PCT/JP2001/001815
Other languages
English (en)
French (fr)
Inventor
Ken-Ichi Furukawa
Original Assignee
Furukawa Ken Ichi
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Furukawa Ken Ichi filed Critical Furukawa Ken Ichi
Priority to AU2001241066A priority Critical patent/AU2001241066C1/en
Priority to KR1020027011766A priority patent/KR20020081414A/ko
Priority to US09/980,671 priority patent/US6750175B2/en
Priority to BR0109476-9A priority patent/BR0109476A/pt
Priority to AU4106601A priority patent/AU4106601A/xx
Priority to EP01912191A priority patent/EP1275524A4/en
Publication of WO2001070518A1 publication Critical patent/WO2001070518A1/ja

Description

明 細 書 一方向透視性の装飾フィルム 技術分野
本発明はガラス窓や透明アクリル板などに貼付される一方向透視性の装飾 フィルムに関する。 背景技術
従来、 ワンウェイヴィジョン （Oneway Vision) と呼ばれる一方向透視性フ イルムが知られている。 これはフィルムの片面が黒色などの遮光色に、 他面 が白色に塗装され、遮光色面に粘着剤層およびセパレー夕が貼合されており、 かつフィルム全面に直径 1〜 2 mm程度の円形の貫通孔が開孔率 3 0〜 7 0 %程度で無数に穿たれているものである。 このフィルムはセパレ一夕を剥 がし、 部屋のガラス窓に貼って使用される。 これにより日中内部から外部を 見たとき、 遮光色全面の中に無数に配置された貫通孔より明るい世界を見る ことになるので、 目の錯覚でそれほど視界を妨げられない感覚で外部を透視 できる。 それに対して外部から内部を見たときには、 貫通孔より暗い世界を 見ることになるので、 内部をほとんど透視することができない。 このように 一方向からの視界を十分に確保しながらも、 他の方向からの視認に対しては 目隠しになる機能を有している。
かかる一方向透視性フィルムに対して、 近年広告効果やァメニティ性の向 上を狙つて、 そのフィルムの白色面に各種の画像を付与することが行われて いる。 現在、 このような目的で白色面に画像を付与するには、 カラ一静電プ ロッターを用いて静電記録紙に記録した画像を、 フィルムの白色面に熱圧着 して転写する方法が行われている。 これは静電記録紙の構造上から画像が定 着する 3〜5 mの厚みの誘電層 （樹脂製） 力 水分付与や加熱により層ご と剥離できる原理を利用できるからである。
前記方法に用いるフィルムは白色面に画像が付与され、 遮光色面に粘着剤 層が積層された構造であり、 現場作業ではフィルムをガラス窓の外側に貼付 することになるが、 外側に貼付されたフィルムは外部から見たとき、 ガラス 窓特有の透明感を喪失させてしまう欠点がある。 また剥がれやすい上に、 貫 通孔部分が凹凸をなすため汚れやすく清掃しにくい欠点がある。 またこの場 合、 転写画像を含む誘電層の薄い樹脂膜が貫通孔を覆ってしまう仕組みにな るため、 貫通孔の透明感も損なわれてしまう。 加うるにこの状態のままでは 直射日光下では画像の耐光性がない。 耐光性向上するためには、 フィルム全 面に紫外線力ット性のフィルムをラミネー卜するしか手段がなく、 ますます 透明感を喪失させる上に非常にコストアップになってしまう。
したがって、 広告やァメニティ性向上効果を有する一方向透視性フィルム において、 ガラス窓の外部から見たとき、 ガラス窓の透明感及び貫通孔部分 の透明感が維持され、 剥がれにくく、 汚れにくく、 かつ耐光性のあるものが 求められている。
本発明者は、 先に 「画像付きフィルムの作成方法」 に関する技術を開示し ている (曰本特許第 2934948号, 米国特許 No. 5,594,484) 。
これは昇華性染料が拡散し得る透明樹脂フィルム上に、 昇華性染料に対し て非親和性の白色樹脂フィルムを積層してなる転写用フィルムの白色樹脂フ イルム面に、 昇華性染料を含有するインクを用いて画像記録された転写紙を 密着させ加熱して、 昇華性染料を白色樹脂フィルムを通過させ透明樹脂フィ ルムに拡散させ、 透明フィルム側に転写画像を現出させる技術である。
この技術では、 昇華性染料に対して非親和性の白色樹脂フィルムと昇華性 染料が拡散し得る透明樹脂フィルムとからなる積層体フィルムの白色樹脂フ イルム面から、 加熱により昇華性染料が着色画像が色に関係なく、 白色樹脂 フィルム側から反対面の透明樹脂フィルム側に拡散し画像状に転写されるこ とを示している。 発明の開示
本発明者は、前記一方向透視性フィルムの課題解決すべく鋭意検討の結果、 昇華性染料が拡散し得る透明樹脂フィルム上に、 白色塗装層およびその上に 遮光色塗装層を塗装してなる積層体で、 かつ白色塗装層および遮光色塗装層 を構成する樹脂が昇華性染料に非親和性の樹脂である装飾用フィルムを使用 することにより、 前記課題を抜本的に解決できることを見い出し、 本発明に 到達した。
すなわち、昇華性染料を含有するインクを用いて画像記録された転写紙を、 この装飾用フィルムの遮光色塗装面に重ねて密着加熱することにより、 転写 紙上の昇華性染料は遮光色塗装層および白色塗装層を通過せしめ、 透明樹脂 フィルムを高濃度に転写染色することができ、 この時、 透明樹脂フィルム側 に更に粘着剤層及びその上にセパレー夕が積層されていれば、 転写画像が粘 着剤層側から視認できるように現出する。 この状態でセパレ一夕を剥がし、 白色塗装層をバックに転写画像が付与されている装飾フィルムの粘着剤層を、 そのままガラス窓の内側に貼付することが可能となる。 このとき装飾フィル ムに所定の開孔率で貫通孔が穿かれていれば、 ガラス窓の内側からは外部を 明瞭に透視できるが、 外部からは内部を透視できない一方向透視性装飾フィ ルムとして利用できる。
すなわち、 本発明は下記の画像転写前の一方向透視性装飾用フィルム、 及 び画像転写後の一方向透視性装飾フィルムを提供するものである。
1 . 昇華性染料が拡散し得る透明樹脂フィルム（3 )上に、 白色塗装層（2 ) およびその上に遮光色塗装層 （1 ) が設けられ、 透明樹脂フィルム （3 ) の 白色塗装層 （2 ) 面の反対面上に、 粘着剤層 （4 ) およびその上にセパレー 夕 （5) が貼合されている積層体であり、 かつ白色塗装層 （2) および遮光 色塗装層 （1) を構成する樹脂が昇華性染料に非親和性の樹脂であることを 特徴とする一方向透視性装飾用フィルム。
2. 透明樹脂フィルム （3) 、 透明樹脂支持体フィルム （3 a) 上に、 昇華性染料が拡散し得る透明塗装層 （3 b) を積層してなる積層体フィルム である前項 1記載の一方向透視性装飾フィルム。
3. 昇華性染料に非親和性の樹脂が、 フッ素系樹脂、 シリコーン系樹脂、 またはォレフィン系樹脂である前項 1記載の一方向透視性装飾フィルム。
4. 遮光色が、 黒色、 濃喑無彩色、 または濃喑有彩色である前項 1記載の 一方向透視性装飾用フィルム。
5. 透明樹脂フィルム （3) が紫外線防止剤を含有する前項 1記載の一方 向透視性装飾用フィルム。
6. 透明樹脂支持体フィルム （3 a) 及び透明塗装層 （3 b) のいずれか 一方、 または双方が紫外線防止剤を含有する前項 2に記載の一方向透視性装 飾用フィルム。
7. 装飾フィルムの全面に面積 10平方 mm以下の貫通孔 （6) 力 開孔 率 30〜70 %の範囲内で穿たれている前項 1乃至 6のいずれかに記載の一 方向透視性装飾フィルム。
8. 前項 7に記載の一方向透視性装飾用フィルムの遮光色塗装面に、 昇華 性染料を含有するインクを用いて画像記録した転写紙を重ねて密着加熱して、 転写紙上の昇華性染料を遮光色塗装層および白色塗装層を通過せしめ、 透明 樹脂フィルムを高濃度に転写染色してなる染色画像を有する一方向透視性装 飾フィルム。
9. 昇華性染料が拡散し得る透明樹脂フィルム（3)上に、 白色塗装層（2) およびその上に遮光色塗装層 （1) を設けてなり、 透明樹脂フィルム （3) が昇華性染料からなる画像で染色され、 全面に面積 10平方 mm以下の貫通 孔 ( 6 ) が開孔率 3 0〜 7 0 %の範囲内で穿たれ、 透明樹脂フィルム側が透 明体に貼合されている一方向透視性装飾フィルム。 図面の簡単な説明
図 1 Aは、 本発明の一方向透視性装飾用フィルムの基本的な態様を示す断 面図であり、 図 1 Bは平面図である。 発明の詳細な説明
本発明の一方向透視性装飾用フィルムの基本的な構成例を断面図（図 1 A) 及び平面図 （図 1 B ) に示す。
図中 3は、 昇華性染料が拡散し得る樹脂材料からなる透明樹脂フィルムで あり、 その片面に白色塗装層 （2 ) と遮光色塗装層 （1 ) が設けられている。 白色塗装層 （2 ) 及び遮光色塗装層 （1 ) に使用する樹脂としては、 昇華性 染料に非親和性の樹脂が使用される。
透明樹脂フィルム （3 ) の白色塗装層の反対面には、 粘着剤層 （4 ) およ びその上にはセパレ一夕 （5 ) が貼合されている。
本発明で使用する白色塗装層および遮光色塗装層を構成する昇華性染料に 非親和性の樹脂は、 フッ素系樹脂、 シリコーン系樹脂およびォレフィン系樹 脂である。
フッ素系樹脂としては、 フルォロォレフイン類の単独重合体、 フルォロォ レフィン類の共重合体、 あるいはフルォロォレフィン類とフルォロォレフィ ン類以外の単量体との共重合体、 例えば、 ポリビニルフルオライド、 ポリビ 二リデンフルオライド、 ポリテトラフルォロエチレン、 テトラフルォロェチ レン—パーフルォロアルキルビニルエーテル共重合体、 テトラフルォロェチ レン—へキサフルォロプロピレン共重合体、 テトラフルォロエチレン—ェチ レン共重合体、 ポリクロ口トリフルォロエチレンなどが挙げられ、 シリコ一 ン系の樹脂としては、 例えば純シリコーン樹脂、 シリコーン変性樹脂 （アル キド、 エポキシ、 フエノール、 ウレタン、 アクリル、 メラミン） などが挙げ られ、 ォレフィン系樹脂の樹脂としては、 例えばポリエチレン、 ポリプロピ レン、 ポリ塩化ビニルなどが挙げられる。 これらの樹脂には紫外線吸収剤お よび Zまたは酸化防止剤を配合することが好ましい。紫外線吸収剤としては、 ヒドロキシベンゾキノン系、 ベンゾトリアゾール系、 サリチル酸エステル系、 シユウ酸ァニリ ド系化合物等が挙げら、 酸化防止剤としては、 ヒンダード系、 ヒンダードフエノール系、 およびホスフアイト系化合物などが挙げられる。 前記の樹脂は有機溶剤の溶液として使用される。 有機溶剤としては従来慣 用されている、 エステル系 （酢酸ェチル、 酢酸ブチル等） 、 芳香族炭化水素 系 （トルエン等） 、 脂肪族あるいは脂環脂肪族系炭化水素 （へキサン、 シク 口へキサン等） 、 アルコール系 （エタノール、 イソプロパノール等） 、 ケト ン系 （アセトン、 メチルイソプチルケトン等） 、 アミド系 （ジメチルホルム アミド、 ジメチルァセトアミド等） の中から樹脂に適合するように選択使用 される。
白色塗装層および遮光色塗装層の厚みは、 隣り合った背景画像色を遮蔽で きる最小限の厚みでよい。 一般には架橋硬化型塗料の形態で 1〜4 0 m、 好ましくは 3〜2 0 x mの範囲の厚みにコーティング方式により積層される。 遮光色は背景色を遮蔽できる色であれば任意であるが、 遮光色塗装面に転写 画像の残滓が見えないこと、 および外部透視時の錯覚効果を増進するために も、 一般的には明度の低い有彩色、 濃暗色、 特に黒色が好ましい。
本発明において、 透明樹脂フィルム （3 ) として用いられる樹脂は密着加 熱に耐えられる耐熱性があり、 かつ昇華性染料が拡散し得るものであれば別 段種類は問わないが、 前記した昇華性染料に対して非親和性でない樹脂が好 ましい。 これは遮光色塗装層および白色塗装層を通過してくる昇華性染料を 積極的に吸引する機能に優れ、 透明樹脂フィルムが高濃度に染色されるから である。 このような透明樹脂フィルムとしては、 例えば、 ポリエステル系、 ポリカーボネート系、 ポリビニルアルコール系、 ポリウレタン系、 高分子系 可塑剤を添加したポリ塩化ビニル等が挙げられる。
また、 透明樹脂フィルム （3 ) を、 透明樹脂支持体フィルム （3 a ) と、 昇華性染料が拡散し得る透明塗装層 （3 b ) とを積層した透明積層体フィル ムとすることができる。 この場合の透明樹脂支持体フィルム （3 a ) は、 1 華性染料が拡散し得る性質は必要なく、透明性を有する支持体であればよく、 例えば透明なポリエステルフィルムなどを使用し、 その上に昇華性染料をブ リードさせることなく、 安定して担持できる架橋硬化型樹脂を積層すればよ い。 例えば、 ポリエステル系樹脂、 シリコーンポリエステル系樹脂、 ェポキ シ系樹脂、 ポリウレタン系樹脂等が挙げられる。 これらを透明樹脂支持体フ イルム上に 3〜4 0 m、 好ましくは 1 0〜 3 0 の厚みにコーティング して透明塗装層 （3 b ) を積層する。
この場合、 転写される昇華性染料は、 透明樹脂支持体フィルム （3 a ) 自 身および透明塗装層 （3 b ) に保護されることになるため耐光性に優れたも のとなる。
さらに、 耐光性を一層向上させるために、 透明樹脂支持体フィルムと透明 塗装層のいずれか一方または両方に、 この分野で公知で慣用されている、 前 述したような紫外線吸収剤および Zまたは酸化防止剤を配合することが望ま しい。
セパレー夕としてはクラフ卜紙ゃポリエステルフィルムベースの耐熱性セ パレー夕力 粘着剤層としてはアクリル系などの耐熱性粘着剤が用いられる。 本発明の一方向透視性装飾フィルムの製造方法は、 特に限定されるもので はない。
例えば、 透明樹脂フィルムあるいは透明樹脂支持体フィルムと透明塗装層 との透明積層体フィルムに、 まず白色塗装層を所定の厚みに積層硬化させ、 次いで第 2層の遮光色塗装層を所定の厚みに積層し硬化させ、 その後フィル ムの反対面に粘着剤層を積層しセパレ一夕を貼合して製造することができる。 また、 透明樹脂フィルムとして、 ポリエステルフィルムなどと違って、 耐 溶剤性の低いフィルム （ポリウレタン系、 ポリ塩化ビニルなど） を用いる場 合や、 透明樹脂フィルム自身をコーティングで製造する場合は、 製膜はキヤ スティング方式で行われる。 すなわち、 製膜用シート上に、 まず最上層とな る遮光色塗装層を、 次に白色塗装層を、 次に透明樹脂フィルム層を順々に溶 剤塗工により製膜した後、 粘着剤を塗布してセパレ一夕を貼付する。
ついで、 装飾フィルムの全面に、 市販の穿孔器を用いて貫通孔 （6 ) が穿 たれる。 貫通孔 （6 ) の形状、 割合 （開孔率） は用途に応じて任意であるが、 外部よりは目隠しの機能をもち、 かつ内部より違和感なく外部を透視できる ためには、面積 1 0 mm2以内の貫通孔を装飾フィルム全面に開孔率 3 0〜7 0 %程度の範囲内で規則的に穿つことが好ましい。
本発明の一方向透視性装飾用フィルムに画像を染色し、 一方向透視性装飾 フィルムを形成するために用いられる昇華性染料は、 昇華性または蒸発性の 機能を有する染料であればいずれでもよい。 好ましくは、 大気圧下、 7 0〜
2 6 0 °Cで昇華または蒸発する染料である。 これらの染料としては、 例えば ァゾ、 アントラキノン、 キノフタロン、 スチリル、 ジまたはトリフエニルメ タン、 ォキサジン、 トリアジン、 キサンテン、 メチン、 ァゾメチン、 チクリ ジン、 ジァジンなどの昇華または蒸発性を有する染料が挙げられ、 これらの 他に、 1， 4ージメチルァミノアン卜ラキノン、 臭化または塩化 1 , 5—ジ ヒドロォキシ一 4 , 8 —ジァミノアントラキノン、 1， 4ージァミノ一 2，
3 —ジクロローアントラキノン、 1， アミノ一ヒドロォキシ一アントラキノ ン、 1ーァミノ一 4ーヒドロォキシ一 2— ( 3—メトキシーェ卜キシ） ーァ ントラキノン、 1 —ァミノ一 4—ヒドロォキシ一 2 —フエノキシ一アントラ キノン、 1， 4—ジァミノーアントラキノン一 2 —カルボキシル酸のメチル、 ェチル、 プロピルまたはブチルエステル、 1 _アミノー 4—ァニリ ドーアン トラキノン、 1—アミノー 2—シァノー 4ーァニリ ド （またはシクロへキシ ルァミノ） 一アントラキノン、 1—ヒドロォキシ _ 2— （p—ァセトァミノ —フエニルァゾ） 一 4—メチルベンゼン、 3—メチルー 4— (ニトロフエ二 ルァゾ） 一ビラゾロン、 3—ヒドロォキシ—キノフタロンなどの染料も用い ることができる。 また、 塩基性染料として、 例えばマラカイトグリーン、 メ チルバイオレット等を用いることができ、 酢酸ナトリウム、 ナトリウムエタ レ一ト、 ナトリゥムメチラ一卜等で変性した染料も使用することができる。 発明を実施するための最良の形態
以下実施例を挙げて本発明を説明するが、 下記の記載により本発明は何ら 限定されるものではない。 実施例 1 ：
厚さ 5 0 / mの 2軸延伸透明ポリエステルフィルム （ティジンテトロンフ イルム S 6， 商品名， 帝人社製） に、 まず第 1層の白色塗装層を 4フッ化塗 料 （フルォロエチレン一ビニルエーテル共重合体系塗料） （デュフロン 4 F (DUFLON4F) フレッシュ ·ホワイト， 商品名， 日本ペイント社製） を 1 5 mの厚みに積層し硬化させて形成した。 次に第 2層の遮光色塗装層を 4フ ッ化塗料 （デュフロン 4 Fフレッシュ 'ブラック， 商品名， 日本ペイント社 製） 1 5 /z mの厚みに積層し硬化させ、 その後フィルムの反対面に粘着剤層 を積層し、 その上に耐熱性のセパレー夕を貼合した。 このフィルム全面に直 径 1.5mmの円形の貫通孔を、開孔率 5 0 %になるように規則的に孔を穿ち一 方向透視性装飾用フィルムを作成した。 この装飾用フィルムのブラック塗料 塗装面に、 昇華性染料を含有する 「インクジェット用インク （シアン、 マゼ ン夕、 イェロー、 ブラックの 4色セット） 」 （紀和化学工業社製） を用いて 画像記録した転写紙を重ね、 1 6 0 °Cの温度で 4分間密着加熱した。 この装 飾フィルムの背面のセパレー夕を剥離したところ、 粘着剤層下部に白色塗装 面をバックにして、 転写紙の原画に忠実な染色画像が現出した。 ポリエステ ルフィルムは昇華性染料に対して親和性の高い樹脂であるが、 ここで用いた 延伸ポリエステルフィルムは結晶性が高く昇華性染料が侵入しにくいため、 染色画像渡度はあまり高くなかった。 実施例 2
厚さ 5 0 mの 2軸延伸透明ポリエステルフィルム （ティジンテトロンフ イルム S 6 ) に、 まず第 1層の透明塗装層として 1液熱硬化型のポリエステ ル樹脂系クリア一塗料 （セノコイル， 商品名， カシュ一社製） を 3 の 厚みに積層し硬化させた。 次に第 2層の白色塗装層を、 実施例 1と同じ 「デ ュフロン 4 Fフレッシュ ·ホワイト」 を用いて同様の手順で積層した。 次に 第 3層の全く遮光色塗装層を実施例 1と同じ 「デュフロン 4 Fフレッシュ - ブラック」 を同様の手順で積層した。 ついで、 フィルムの反対面に粘着剤層 を積層しその上に耐熱性のセパレー夕を貼合し、 このフィルム全面に実施例 1と同様の貫通孔を穿ち装飾フィルムを作成した。 この装飾フィルムのブラ ック塗料塗装面に、 実施例 1と全く同様の手順で熱転写を行った。 この装飾 フィルムの背面のセパレー夕を剥離したところ、 粘着剤層側の下部に白色塗 装面をバックにして、 転写紙の原画に忠実な染色画像が現出した。 この染色 濃度は実施例 1の場合より歴然と高かった。 実施例 3
厚さ 5 0 z mの 2軸延伸透明ポリエステルフィルム （ティジンテトロンフ イルム S 6 ) に、 まず第 1層の透明塗装層として 2液硬化型アクリルウレ夕 ン樹脂系クリア一塗料 （アクリルウレタン樹脂ワニス 7 9 8 7， 商品名， ィ サム塗料社製） を 3 0 mの厚みに積層し硬化させた。 次に、 第 2層の白色 塗装層を実施例 1と同じ 「デュフロン 4 Fフレッシュ ·ホワイ ト」 を用いて 同様の手順で積層した。 次に第 3層の遮光色塗装層を実施例 1と同じ 「デュ フロン 4 Fフレッシュ ' ブラック」 を用いて同様の手順で積層し、 その後フ イルムの反対面に粘着剤層を積層しその上に耐熱性のセパレー夕を貼合した。 このフィルム全面に実施例 1と全く同様の貫通孔を穿ち装飾フィルムを作成 した。 この装飾フィルムのブラック塗料塗装面に、 実施例 1と同様の手順で 熱転写を行った。 この装飾フィルムの背面のセパレ一夕を剥離したところ、 粘着剤層側下部に白色塗装面をバックにして、 転写紙の原画に忠実な染色画 像が現出した。 この染色濃度は実施例 1の場合より歴然と高かった。 産業上の利用可能性
本発明によれば、 ガラス窓の外部から見たとき、 ガラス窓の透明感及び貫 通孔部分の透明感が維持され、 剥がれにくく、 汚れにくく、 かつ耐光性のあ る、 広告やァメニティ性向上効果を有する鮮明な画像を有する一方向透視性 装飾フィルムを単品として容易に制作することができる。

Claims

請 求 の 範 囲
1. 昇華性染料が拡散し得る透明樹脂フィルム（3)上に、 白色塗装層（2) およびその上に遮光色塗装層 （1) が設けられ、 透明樹脂フィルム （3) の 白色塗装層 （2) 面の反対面上に、 粘着剤層 （4) およびその上にセパレ一 夕 （5) が貼合されている積層体であり、 かつ白色塗装層 （2) および遮光 色塗装層 （1) を構成する樹脂が昇華性染料に非親和性の樹脂であることを 特徴とする一方向透視性装飾用フィルム。
2. 透明樹脂フィルム （3) 力 透明樹脂支持体フィルム （3 a) 上に、 昇華性染料が拡散し得る透明塗装層 （3 b) を積層してなる積層体フィルム である請求の範囲 1記載の一方向透視性装飾フィルム。
3. 昇華性染料に非親和性の樹脂が、 フッ素系樹脂、 シリコーン系樹脂、 またはォレフィン系樹脂である請求の範囲 1記載の一方向透視性装飾フィル ム。
4. 遮光色が、 黒色、 濃喑無彩色、 または濃暗有彩色である請求の範囲 1 記載の一方向透視性装飾用フィルム。
5. 透明樹脂フィルム （3) が紫外線防止剤を含有する請求の範囲 1記載 の一方向透視性装飾用フィルム。
6. 透明樹脂支持体フィルム （3 a) 及び透明塗装層 （3 b) のいずれか 一方、 または双方が紫外線防止剤を含有する請求の範囲 2に記載の一方向透 視性装飾用フィルム。
7. 装飾フィルムの全面に面積 1 0平方 mm以下の貫通孔 （6) 力 開孔 率 30〜7◦ %の範囲内で穿たれている請求の範囲 1乃至 6のいずれかに記 載の一方向透視性装飾用フィルム。
8. 請求の範囲 7に記載の一方向透視性装飾用フィルムの遮光色塗装面に、 昇華性染料を含有するインクを用いて画像記録した転写紙を重ねて密着加熱 して、転写紙上の昇華性染料を遮光色塗装層および白色塗装層を通過せしめ、 透明樹脂フィルムを高濃度に転写染色してなる染色画像を有する一方向透視 性装飾フィルム。
9. 昇華性染料が拡散し得る透明樹脂フィルム（3)上に、 白色塗装層（2) およびその上に遮光色塗装層 （1) を設けてなり、 透明樹脂フィルム （3) が昇華性染料からなる画像で染色され、 全面に面積 10平方 mm以下の貫通 孔 （6) が開孔率 30〜 70%の範囲内で穿たれ、 透明樹脂フィルム側が透 明体に貼合されている一方向透視性装飾フィルム。
PCT/JP2001/001815 2000-03-21 2001-03-08 Films decoratifs transparents unidirectionnellement WO2001070518A1 (fr)