WO1995021277A1 - Agent de traitement de surface pour acier zingue - Google Patents

Agent de traitement de surface pour acier zingue Download PDF

Info

Publication number
WO1995021277A1
WO1995021277A1 PCT/US1995/000977 US9500977W WO9521277A1 WO 1995021277 A1 WO1995021277 A1 WO 1995021277A1 US 9500977 W US9500977 W US 9500977W WO 9521277 A1 WO9521277 A1 WO 9521277A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
composition according
zinciferous
plated steel
group
Prior art date
Application number
PCT/US1995/000977
Other languages
English (en)
Inventor
Masayuki Aoyama
Takao Ogino
Original Assignee
Henkel Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel Corporation filed Critical Henkel Corporation
Priority to MX9603096A priority Critical patent/MX9603096A/es
Priority to US08/687,390 priority patent/US5846342A/en
Priority to EP95909324A priority patent/EP0742849A4/fr
Priority to BR9506685A priority patent/BR9506685A/pt
Publication of WO1995021277A1 publication Critical patent/WO1995021277A1/fr

Abstract

Un agent de traitement de surface liquide aqueux et dépourvu de chrome pouvant conférer une bonne résistance à la corrosion et une bonne adhérence de la peinture à une feuille d'acier zingué est constitué principalement d'acide carboxylique polyhydroxyaryle et/ou d'un depside de ce dernier, et d'un agent de couplage au silane correspondant à la formule (YR)mRnSiX(4-m-n) dans laquelle R représente des groupes alkyle; X représente le groupe méthoxy ou éthoxy; Y représente le groupe vinyle, amino, mercapto, glycidoxy ou méthacryloxy; m représente un entier compris entre 1 et 3; et n représente un entier compris entre 0 et (3-m). Le volume total de ces constituants principaux est, de préférence, de 1 à 50 pour cent en poids.
PCT/US1995/000977 1994-02-03 1995-02-01 Agent de traitement de surface pour acier zingue WO1995021277A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
MX9603096A MX9603096A (es) 1994-02-03 1995-02-01 Agente de tratamiento superficial para acero chapado zincifero.
US08/687,390 US5846342A (en) 1994-02-03 1995-02-01 Surface treatment agent for zinciferous-plated steel
EP95909324A EP0742849A4 (fr) 1994-02-03 1995-02-01 Agent de traitement de surface pour acier zingue
BR9506685A BR9506685A (pt) 1994-02-03 1995-02-01 Composição de tratamento de superficie líquida e aquosa para aço galvanizado com material zincifero e processo para o tratamento de um substrato de aço

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP1169594A JPH07216268A (ja) 1994-02-03 1994-02-03 耐食性、塗装密着性に優れた亜鉛含有金属めっき鋼板用表面処理剤
JP6/11695 1994-02-03

Publications (1)

Publication Number Publication Date
WO1995021277A1 true WO1995021277A1 (fr) 1995-08-10

Family

ID=11785176

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1995/000977 WO1995021277A1 (fr) 1994-02-03 1995-02-01 Agent de traitement de surface pour acier zingue

Country Status (6)

Country Link
EP (1) EP0742849A4 (fr)
JP (1) JPH07216268A (fr)
BR (1) BR9506685A (fr)
CA (1) CA2182395A1 (fr)
MX (1) MX9603096A (fr)
WO (1) WO1995021277A1 (fr)

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998003600A1 (fr) * 1996-07-23 1998-01-29 Ciba Specialty Chemicals Holding Inc. Traitement de surface metallique
DE19642725A1 (de) * 1996-10-17 1998-04-30 Suratech Gmbh Verfahren zur haftfesten Verbindung von Lack oder Klebstoff mit einem Oberflächenbereich eines Werkstücks aus verzinktem Stahl oder verzinkten Eisen-Legierungen und dessen Verwendung
US5868819A (en) * 1996-05-20 1999-02-09 Metal Coatings International Inc. Water-reducible coating composition for providing corrosion protection
WO1999014399A1 (fr) * 1997-09-17 1999-03-25 Brent International Plc Procede et compositions permettant de prevenir la corrosion de substrats metalliques
WO1999051793A1 (fr) * 1998-04-01 1999-10-14 Kunz Gmbh Agent pour le colmatage de couches de base metalliques, en particulier en zinc ou alliages de zinc
EP1002889A2 (fr) * 1998-11-18 2000-05-24 Nippon Paint Co., Ltd. Compositions et procédés de revêtement anticorrosif pour métaux
FR2796655A1 (fr) * 1999-07-22 2001-01-26 Dacral Sa Procede et composition de traitement anti-corrosion d'un substrat metallique prealablement protege par une couche de revetement a base de zinc
WO2001023639A1 (fr) * 1999-09-30 2001-04-05 Dacral Revetement et procede de traitement anticorrosion de pieces metalliques
US6270884B1 (en) 1999-08-02 2001-08-07 Metal Coatings International Inc. Water-reducible coating composition for providing corrosion protection
EP1433877A1 (fr) * 2002-12-24 2004-06-30 Nippon Paint Co., Ltd. Procédé de prétraitement avant revêtement
EP1568800A1 (fr) * 2004-02-25 2005-08-31 Posco Procédé de protection de métaux contre la corrosion utilisant des composés thiols.
EP1847633A1 (fr) * 2005-02-02 2007-10-24 Nihon Parkerizing Co., Ltd. Agent aqueux de traitement de surface pour une matiere en metal, procede de traitement de surface et matiere en metal traitee en surface
CN110129784A (zh) * 2019-05-30 2019-08-16 廊坊师范学院 涂装前中性表面处理剂的制备方法

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1524332B1 (fr) 2002-07-23 2011-09-14 JFE Steel Corporation Tole d'acier rendue resistante a la corrosion blanche par traitement de surface et procede de production correspondant
JP4500113B2 (ja) 2003-06-16 2010-07-14 Ｊｆｅスチール株式会社 高耐食性表面処理鋼板及びその製造方法
JP5688522B2 (ja) * 2010-01-21 2015-03-25 日本ペイント株式会社 銅の表面処理剤
KR20200128955A (ko) * 2019-05-07 2020-11-17 현대자동차주식회사 금속 및 수지의 이종 재질간의 접착력 향상 방법

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5521509A (en) * 1978-07-31 1980-02-15 Toagosei Chem Ind Co Ltd Surface treatment of zincic substrate
JPS59116381A (ja) * 1982-12-24 1984-07-05 Mitsui Mining & Smelting Co Ltd 亜鉛および亜鉛合金面の表面処理法
US5389405A (en) * 1993-11-16 1995-02-14 Betz Laboratories, Inc. Composition and process for treating metal surfaces
US5393605A (en) * 1991-12-12 1995-02-28 Nkk Corporation Zinciferous plated steel sheet excellent in press-formability and corrosion resistance

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4247344A (en) * 1975-10-15 1981-01-27 Nippon Steel Corporation Rust preventing treatment of metal-plated steel materials
JPS5337150A (en) * 1976-09-02 1978-04-06 Nippon Packaging Kk Surface treatment of zinc or zinc alloy
JPS6022067B2 (ja) * 1982-09-30 1985-05-30 日本パ−カライジング株式会社 金属表面の皮膜形成方法

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5521509A (en) * 1978-07-31 1980-02-15 Toagosei Chem Ind Co Ltd Surface treatment of zincic substrate
JPS59116381A (ja) * 1982-12-24 1984-07-05 Mitsui Mining & Smelting Co Ltd 亜鉛および亜鉛合金面の表面処理法
US5393605A (en) * 1991-12-12 1995-02-28 Nkk Corporation Zinciferous plated steel sheet excellent in press-formability and corrosion resistance
US5389405A (en) * 1993-11-16 1995-02-14 Betz Laboratories, Inc. Composition and process for treating metal surfaces

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
See also references of EP0742849A4 *

Cited By (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5868819A (en) * 1996-05-20 1999-02-09 Metal Coatings International Inc. Water-reducible coating composition for providing corrosion protection
WO1998003600A1 (fr) * 1996-07-23 1998-01-29 Ciba Specialty Chemicals Holding Inc. Traitement de surface metallique
US6488805B1 (en) 1996-07-23 2002-12-03 Vantico, Inc. Metal surface treatment
DE19642725A1 (de) * 1996-10-17 1998-04-30 Suratech Gmbh Verfahren zur haftfesten Verbindung von Lack oder Klebstoff mit einem Oberflächenbereich eines Werkstücks aus verzinktem Stahl oder verzinkten Eisen-Legierungen und dessen Verwendung
WO1999014399A1 (fr) * 1997-09-17 1999-03-25 Brent International Plc Procede et compositions permettant de prevenir la corrosion de substrats metalliques
US6203854B1 (en) 1997-09-17 2001-03-20 Brent International Plc Methods of and compositions for preventing corrosion of metal substrates
WO1999051793A1 (fr) * 1998-04-01 1999-10-14 Kunz Gmbh Agent pour le colmatage de couches de base metalliques, en particulier en zinc ou alliages de zinc
EP1002889A2 (fr) * 1998-11-18 2000-05-24 Nippon Paint Co., Ltd. Compositions et procédés de revêtement anticorrosif pour métaux
EP1002889A3 (fr) * 1998-11-18 2000-09-13 Nippon Paint Co., Ltd. Compositions et procédés de revêtement anticorrosif pour métaux
FR2796655A1 (fr) * 1999-07-22 2001-01-26 Dacral Sa Procede et composition de traitement anti-corrosion d'un substrat metallique prealablement protege par une couche de revetement a base de zinc
WO2001007680A1 (fr) * 1999-07-22 2001-02-01 Dacral S.A. Procede et composition de traitement anti-corrosion d'un substrat metallique prealablement protege par une couche de revetement a base de zinc
US6270884B1 (en) 1999-08-02 2001-08-07 Metal Coatings International Inc. Water-reducible coating composition for providing corrosion protection
WO2001023639A1 (fr) * 1999-09-30 2001-04-05 Dacral Revetement et procede de traitement anticorrosion de pieces metalliques
FR2799211A1 (fr) * 1999-09-30 2001-04-06 Dacral Sa Revetement et procede de traitement anticorrosion de pieces metalliques
US6656607B1 (en) * 1999-09-30 2003-12-02 Dacral Method for anticorrosive coating and treatment of metal parts
CZ298072B6 (cs) * 1999-09-30 2007-06-13 Dacral S. A. Antikorozní povlak a zpusob opatrení kovové soucásti antikorozním povlakem
EP1433877A1 (fr) * 2002-12-24 2004-06-30 Nippon Paint Co., Ltd. Procédé de prétraitement avant revêtement
US8075708B2 (en) 2002-12-24 2011-12-13 Nippon Paint Co., Ltd. Pretreatment method for coating
EP1568800A1 (fr) * 2004-02-25 2005-08-31 Posco Procédé de protection de métaux contre la corrosion utilisant des composés thiols.
EP1847633A1 (fr) * 2005-02-02 2007-10-24 Nihon Parkerizing Co., Ltd. Agent aqueux de traitement de surface pour une matiere en metal, procede de traitement de surface et matiere en metal traitee en surface
EP1847633A4 (fr) * 2005-02-02 2011-03-30 Nihon Parkerizing Agent aqueux de traitement de surface pour une matiere en metal, procede de traitement de surface et matiere en metal traitee en surface
CN110129784A (zh) * 2019-05-30 2019-08-16 廊坊师范学院 涂装前中性表面处理剂的制备方法
CN110129784B (zh) * 2019-05-30 2021-03-12 廊坊师范学院 涂装前钢铁表面处理剂的制备方法

Also Published As

Publication number Publication date
CA2182395A1 (fr) 1995-08-10
EP0742849A1 (fr) 1996-11-20
JPH07216268A (ja) 1995-08-15
EP0742849A4 (fr) 1997-02-26
BR9506685A (pt) 1997-11-18
MX9603096A (es) 1997-05-31

Similar Documents

Publication Publication Date Title
AU2006260006B2 (en) Chrome-free composition of low temperature curing for treating a metal surface and a metal sheet using the same
JP3898302B2 (ja) 金属材料用表面処理剤組成物および処理方法
AU2016363456B2 (en) Chromium-free surface-treated tinplate, production method and surface treating agent therefor
EP1163297B1 (fr) Procede de traitement des metaux a l'aide de silanes d'aminos et de silanes a fonction multi-silyl melanges
WO1995021277A1 (fr) Agent de traitement de surface pour acier zingue
JP5252925B2 (ja) 表面化成処理液および化成処理金属板の製造方法
US5294266A (en) Process for a passivating postrinsing of conversion layers
JPH0873775A (ja) 耐指紋性、耐食性、塗装密着性にすぐれた皮膜形成用金属表面処理剤および処理方法
WO1999046342A1 (fr) Composition de traitement de surface pour materiau metallique et procede de traitement
JPS6352114B2 (fr)
KR20040058041A (ko) 도장 전처리 방법
AU609327B2 (en) Chromium-free process for pretreating metallic surfaces prior to coating same with organic materials
NZ198671A (en) Composition and method for post-treatment of conversion-coated metal surface
US4600447A (en) After-passivation of phosphated metal surfaces
CA2251374A1 (fr) Revetement par conversion exempt de chrome et procedes d'utilisation
US5846342A (en) Surface treatment agent for zinciferous-plated steel
JP2013087312A (ja) 塗布型塗装用の塗装前処理剤及び塗布型塗装方法
JPH10251509A (ja) 金属表面処理液および表面処理金属板
WO1999050366A1 (fr) Materiau metallique comportant un revetement composite organique, presentant une resistance a la corrosion et une aptitude au revetement excellentes, et gardant peu les traces de doigts, et procede de production associe
JP2001164182A (ja) 防錆コーティング剤および防錆処理方法
JP3993729B2 (ja) 耐食性、塗装性、耐指紋性及び加工性に優れた金属板材料及びその製造方法
KR100428562B1 (ko) 아연도금 강판용 표면처리 조성물 및 이를 이용하여처리된 아연도금강판
JPH0949086A (ja) 高白色で塗装性に優れた電気亜鉛めっき鋼板の製造方法
JP3475908B2 (ja) 亜鉛系めっき材の耐候性改善方法
JP2003293156A (ja) 耐食性、塗料密着性及び塗装後耐食性に優れたリン酸塩処理鋼板及びその製造方法

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): BR CA MX US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 1995909324

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: PA/a/1996/003096

Country of ref document: MX

Ref document number: 2182395

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 08687390

Country of ref document: US

WWP Wipo information: published in national office

Ref document number: 1995909324

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1995909324

Country of ref document: EP