WO1993016972A1 - Improved process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins - Google Patents
Improved process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins Download PDFInfo
- Publication number
- WO1993016972A1 WO1993016972A1 PCT/US1993/001828 US9301828W WO9316972A1 WO 1993016972 A1 WO1993016972 A1 WO 1993016972A1 US 9301828 W US9301828 W US 9301828W WO 9316972 A1 WO9316972 A1 WO 9316972A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- hydrogenation catalyst
- ruthenium
- surface area
- catalyst
- silica
- Prior art date
Links
- 239000003054 catalyst Substances 0.000 title claims abstract description 129
- 238000000034 method Methods 0.000 title claims abstract description 116
- 230000008569 process Effects 0.000 title claims abstract description 98
- 150000001925 cycloalkenes Chemical class 0.000 title claims abstract description 30
- KJTLSVCANCCWHF-UHFFFAOYSA-N Ruthenium Chemical compound [Ru] KJTLSVCANCCWHF-UHFFFAOYSA-N 0.000 claims abstract description 89
- 229910052707 ruthenium Inorganic materials 0.000 claims abstract description 85
- UHOVQNZJYSORNB-UHFFFAOYSA-N Benzene Chemical compound C1=CC=CC=C1 UHOVQNZJYSORNB-UHFFFAOYSA-N 0.000 claims abstract description 81
- 238000005984 hydrogenation reaction Methods 0.000 claims abstract description 70
- -1 monocyclic aromatic hydrocarbons Chemical class 0.000 claims abstract description 39
- 239000002131 composite material Substances 0.000 claims abstract description 31
- 229910052751 metal Inorganic materials 0.000 claims abstract description 30
- 239000002184 metal Substances 0.000 claims abstract description 30
- 150000004996 alkyl benzenes Chemical class 0.000 claims abstract description 9
- 235000010290 biphenyl Nutrition 0.000 claims abstract description 7
- 150000002790 naphthalenes Chemical class 0.000 claims abstract description 7
- 150000004074 biphenyls Chemical class 0.000 claims abstract description 6
- 239000000463 material Substances 0.000 claims description 50
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims description 37
- 125000003118 aryl group Chemical group 0.000 claims description 37
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 36
- 229910001868 water Inorganic materials 0.000 claims description 32
- 239000000243 solution Substances 0.000 claims description 26
- UFHFLCQGNIYNRP-UHFFFAOYSA-N Hydrogen Chemical compound [H][H] UFHFLCQGNIYNRP-UHFFFAOYSA-N 0.000 claims description 25
- 239000001257 hydrogen Substances 0.000 claims description 24
- 229910052739 hydrogen Inorganic materials 0.000 claims description 24
- 150000003839 salts Chemical class 0.000 claims description 18
- 239000000377 silicon dioxide Substances 0.000 claims description 18
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 claims description 16
- MRELNEQAGSRDBK-UHFFFAOYSA-N lanthanum oxide Inorganic materials [O-2].[O-2].[O-2].[La+3].[La+3] MRELNEQAGSRDBK-UHFFFAOYSA-N 0.000 claims description 15
- 239000007864 aqueous solution Substances 0.000 claims description 13
- 229910052802 copper Inorganic materials 0.000 claims description 13
- 239000011162 core material Substances 0.000 claims description 13
- YXFVVABEGXRONW-UHFFFAOYSA-N Toluene Chemical compound CC1=CC=CC=C1 YXFVVABEGXRONW-UHFFFAOYSA-N 0.000 claims description 12
- 239000000203 mixture Substances 0.000 claims description 12
- 230000002378 acidificating effect Effects 0.000 claims description 10
- 229910052742 iron Inorganic materials 0.000 claims description 10
- 229910052746 lanthanum Inorganic materials 0.000 claims description 10
- FZLIPJUXYLNCLC-UHFFFAOYSA-N lanthanum atom Chemical compound [La] FZLIPJUXYLNCLC-UHFFFAOYSA-N 0.000 claims description 10
- 229910052709 silver Inorganic materials 0.000 claims description 10
- 239000011701 zinc Substances 0.000 claims description 10
- 229910052725 zinc Inorganic materials 0.000 claims description 9
- YNQLUTRBYVCPMQ-UHFFFAOYSA-N Ethylbenzene Chemical compound CCC1=CC=CC=C1 YNQLUTRBYVCPMQ-UHFFFAOYSA-N 0.000 claims description 8
- XLOMVQKBTHCTTD-UHFFFAOYSA-N Zinc monoxide Chemical compound [Zn]=O XLOMVQKBTHCTTD-UHFFFAOYSA-N 0.000 claims description 8
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 claims description 8
- 150000001768 cations Chemical class 0.000 claims description 8
- YBCAZPLXEGKKFM-UHFFFAOYSA-K ruthenium(iii) chloride Chemical compound [Cl-].[Cl-].[Cl-].[Ru+3] YBCAZPLXEGKKFM-UHFFFAOYSA-K 0.000 claims description 8
- URLKBWYHVLBVBO-UHFFFAOYSA-N Para-Xylene Chemical group CC1=CC=C(C)C=C1 URLKBWYHVLBVBO-UHFFFAOYSA-N 0.000 claims description 7
- 229910019891 RuCl3 Inorganic materials 0.000 claims description 7
- CTQNGGLPUBDAKN-UHFFFAOYSA-N O-Xylene Chemical group CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 claims description 6
- GWEVSGVZZGPLCZ-UHFFFAOYSA-N Titan oxide Chemical compound O=[Ti]=O GWEVSGVZZGPLCZ-UHFFFAOYSA-N 0.000 claims description 6
- RWGFKTVRMDUZSP-UHFFFAOYSA-N cumene Chemical compound CC(C)C1=CC=CC=C1 RWGFKTVRMDUZSP-UHFFFAOYSA-N 0.000 claims description 6
- IVSZLXZYQVIEFR-UHFFFAOYSA-N m-xylene Chemical group CC1=CC=CC(C)=C1 IVSZLXZYQVIEFR-UHFFFAOYSA-N 0.000 claims description 6
- 229910052759 nickel Inorganic materials 0.000 claims description 6
- ODLMAHJVESYWTB-UHFFFAOYSA-N propylbenzene Chemical compound CCCC1=CC=CC=C1 ODLMAHJVESYWTB-UHFFFAOYSA-N 0.000 claims description 6
- YTZKOQUCBOVLHL-UHFFFAOYSA-N tert-butylbenzene Chemical compound CC(C)(C)C1=CC=CC=C1 YTZKOQUCBOVLHL-UHFFFAOYSA-N 0.000 claims description 6
- OCKPCBLVNKHBMX-UHFFFAOYSA-N butylbenzene Chemical compound CCCCC1=CC=CC=C1 OCKPCBLVNKHBMX-UHFFFAOYSA-N 0.000 claims description 5
- 229910052737 gold Inorganic materials 0.000 claims description 5
- 229910052763 palladium Inorganic materials 0.000 claims description 5
- 229910052697 platinum Inorganic materials 0.000 claims description 5
- 239000011787 zinc oxide Substances 0.000 claims description 4
- KXUHSQYYJYAXGZ-UHFFFAOYSA-N isobutylbenzene Chemical compound CC(C)CC1=CC=CC=C1 KXUHSQYYJYAXGZ-UHFFFAOYSA-N 0.000 claims description 3
- 229940078552 o-xylene Drugs 0.000 claims description 3
- CETPSERCERDGAM-UHFFFAOYSA-N ceric oxide Chemical compound O=[Ce]=O CETPSERCERDGAM-UHFFFAOYSA-N 0.000 claims description 2
- 229910000422 cerium(IV) oxide Inorganic materials 0.000 claims description 2
- 125000002950 monocyclic group Chemical group 0.000 claims description 2
- 125000005575 polycyclic aromatic hydrocarbon group Chemical group 0.000 claims description 2
- 239000010941 cobalt Substances 0.000 abstract description 17
- 229910017052 cobalt Inorganic materials 0.000 abstract description 17
- GUTLYIVDDKVIGB-UHFFFAOYSA-N cobalt atom Chemical compound [Co] GUTLYIVDDKVIGB-UHFFFAOYSA-N 0.000 abstract description 17
- 125000003367 polycyclic group Chemical group 0.000 abstract description 3
- HGCIXCUEYOPUTN-UHFFFAOYSA-N cyclohexene Chemical compound C1CCC=CC1 HGCIXCUEYOPUTN-UHFFFAOYSA-N 0.000 description 38
- 238000006243 chemical reaction Methods 0.000 description 30
- 239000008346 aqueous phase Substances 0.000 description 19
- 239000000126 substance Substances 0.000 description 14
- 238000011068 loading method Methods 0.000 description 12
- 239000012071 phase Substances 0.000 description 11
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 10
- 150000004945 aromatic hydrocarbons Chemical class 0.000 description 10
- 238000002156 mixing Methods 0.000 description 10
- 239000010949 copper Substances 0.000 description 9
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 8
- 230000007935 neutral effect Effects 0.000 description 8
- 239000007787 solid Substances 0.000 description 8
- 230000000694 effects Effects 0.000 description 7
- 230000009467 reduction Effects 0.000 description 7
- QAOWNCQODCNURD-UHFFFAOYSA-N Sulfuric acid Chemical compound OS(O)(=O)=O QAOWNCQODCNURD-UHFFFAOYSA-N 0.000 description 6
- 229930195733 hydrocarbon Natural products 0.000 description 6
- 150000002430 hydrocarbons Chemical class 0.000 description 6
- 150000002739 metals Chemical class 0.000 description 6
- 239000012074 organic phase Substances 0.000 description 6
- 230000002829 reductive effect Effects 0.000 description 6
- 150000003303 ruthenium Chemical class 0.000 description 6
- BQCADISMDOOEFD-UHFFFAOYSA-N Silver Chemical compound [Ag] BQCADISMDOOEFD-UHFFFAOYSA-N 0.000 description 5
- 239000003929 acidic solution Substances 0.000 description 5
- 238000001816 cooling Methods 0.000 description 5
- 238000004519 manufacturing process Methods 0.000 description 5
- 239000004332 silver Substances 0.000 description 5
- 239000004215 Carbon black (E152) Substances 0.000 description 4
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 4
- 229910052782 aluminium Inorganic materials 0.000 description 4
- 150000001491 aromatic compounds Chemical class 0.000 description 4
- TZCXTZWJZNENPQ-UHFFFAOYSA-L barium sulfate Chemical compound [Ba+2].[O-]S([O-])(=O)=O TZCXTZWJZNENPQ-UHFFFAOYSA-L 0.000 description 4
- 150000001555 benzenes Chemical class 0.000 description 4
- 150000001875 compounds Chemical class 0.000 description 4
- HPXRVTGHNJAIIH-UHFFFAOYSA-N cyclohexanol Chemical compound OC1CCCCC1 HPXRVTGHNJAIIH-UHFFFAOYSA-N 0.000 description 4
- USIUVYZYUHIAEV-UHFFFAOYSA-N diphenyl ether Chemical compound C=1C=CC=CC=1OC1=CC=CC=C1 USIUVYZYUHIAEV-UHFFFAOYSA-N 0.000 description 4
- 238000005470 impregnation Methods 0.000 description 4
- 230000001737 promoting effect Effects 0.000 description 4
- 239000011949 solid catalyst Substances 0.000 description 4
- 150000003752 zinc compounds Chemical class 0.000 description 4
- XDTMQSROBMDMFD-UHFFFAOYSA-N Cyclohexane Chemical compound C1CCCCC1 XDTMQSROBMDMFD-UHFFFAOYSA-N 0.000 description 3
- LYCAIKOWRPUZTN-UHFFFAOYSA-N Ethylene glycol Chemical compound OCCO LYCAIKOWRPUZTN-UHFFFAOYSA-N 0.000 description 3
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 3
- 239000002253 acid Substances 0.000 description 3
- 239000000654 additive Substances 0.000 description 3
- 238000013019 agitation Methods 0.000 description 3
- 125000000217 alkyl group Chemical group 0.000 description 3
- 230000003197 catalytic effect Effects 0.000 description 3
- 239000006185 dispersion Substances 0.000 description 3
- 239000012153 distilled water Substances 0.000 description 3
- 238000010438 heat treatment Methods 0.000 description 3
- 239000007791 liquid phase Substances 0.000 description 3
- 238000002360 preparation method Methods 0.000 description 3
- 230000035484 reaction time Effects 0.000 description 3
- 229910052710 silicon Inorganic materials 0.000 description 3
- 239000002002 slurry Substances 0.000 description 3
- 229910052719 titanium Inorganic materials 0.000 description 3
- 239000010936 titanium Substances 0.000 description 3
- 239000012808 vapor phase Substances 0.000 description 3
- NWONKYPBYAMBJT-UHFFFAOYSA-L zinc sulfate Chemical compound [Zn+2].[O-]S([O-])(=O)=O NWONKYPBYAMBJT-UHFFFAOYSA-L 0.000 description 3
- 229910052726 zirconium Inorganic materials 0.000 description 3
- 229910002651 NO3 Inorganic materials 0.000 description 2
- UFWIBTONFRDIAS-UHFFFAOYSA-N Naphthalene Chemical compound C1=CC=CC2=CC=CC=C21 UFWIBTONFRDIAS-UHFFFAOYSA-N 0.000 description 2
- NHNBFGGVMKEFGY-UHFFFAOYSA-N Nitrate Chemical compound [O-][N+]([O-])=O NHNBFGGVMKEFGY-UHFFFAOYSA-N 0.000 description 2
- WNLRTRBMVRJNCN-UHFFFAOYSA-N adipic acid Chemical compound OC(=O)CCCCC(O)=O WNLRTRBMVRJNCN-UHFFFAOYSA-N 0.000 description 2
- RDOXTESZEPMUJZ-UHFFFAOYSA-N anisole Chemical compound COC1=CC=CC=C1 RDOXTESZEPMUJZ-UHFFFAOYSA-N 0.000 description 2
- 230000015572 biosynthetic process Effects 0.000 description 2
- 229910052804 chromium Inorganic materials 0.000 description 2
- 229940044175 cobalt sulfate Drugs 0.000 description 2
- 229910000361 cobalt sulfate Inorganic materials 0.000 description 2
- XLJKHNWPARRRJB-UHFFFAOYSA-N cobalt(2+) Chemical compound [Co+2] XLJKHNWPARRRJB-UHFFFAOYSA-N 0.000 description 2
- KTVIXTQDYHMGHF-UHFFFAOYSA-L cobalt(2+) sulfate Chemical group [Co+2].[O-]S([O-])(=O)=O KTVIXTQDYHMGHF-UHFFFAOYSA-L 0.000 description 2
- 230000009849 deactivation Effects 0.000 description 2
- 230000001419 dependent effect Effects 0.000 description 2
- ZUOUZKKEUPVFJK-UHFFFAOYSA-N diphenyl Chemical compound C1=CC=CC=C1C1=CC=CC=C1 ZUOUZKKEUPVFJK-UHFFFAOYSA-N 0.000 description 2
- 229910052733 gallium Inorganic materials 0.000 description 2
- 239000007789 gas Substances 0.000 description 2
- 238000001879 gelation Methods 0.000 description 2
- 229910052735 hafnium Inorganic materials 0.000 description 2
- XLYOFNOQVPJJNP-UHFFFAOYSA-M hydroxide Chemical compound [OH-] XLYOFNOQVPJJNP-UHFFFAOYSA-M 0.000 description 2
- 239000007788 liquid Substances 0.000 description 2
- 229910000000 metal hydroxide Inorganic materials 0.000 description 2
- 150000004692 metal hydroxides Chemical class 0.000 description 2
- 239000002923 metal particle Substances 0.000 description 2
- 229910052758 niobium Inorganic materials 0.000 description 2
- 239000002245 particle Substances 0.000 description 2
- BASFCYQUMIYNBI-UHFFFAOYSA-N platinum Chemical group [Pt] BASFCYQUMIYNBI-UHFFFAOYSA-N 0.000 description 2
- 239000002243 precursor Substances 0.000 description 2
- 239000000376 reactant Substances 0.000 description 2
- 239000012429 reaction media Substances 0.000 description 2
- 150000003304 ruthenium compounds Chemical class 0.000 description 2
- 238000003756 stirring Methods 0.000 description 2
- 125000001424 substituent group Chemical group 0.000 description 2
- 229910052715 tantalum Inorganic materials 0.000 description 2
- 235000009529 zinc sulphate Nutrition 0.000 description 2
- 239000011686 zinc sulphate Substances 0.000 description 2
- QWUWMCYKGHVNAV-UHFFFAOYSA-N 1,2-dihydrostilbene Chemical compound C=1C=CC=CC=1CCC1=CC=CC=C1 QWUWMCYKGHVNAV-UHFFFAOYSA-N 0.000 description 1
- YJTKZCDBKVTVBY-UHFFFAOYSA-N 1,3-Diphenylbenzene Chemical group C1=CC=CC=C1C1=CC=CC(C=2C=CC=CC=2)=C1 YJTKZCDBKVTVBY-UHFFFAOYSA-N 0.000 description 1
- ZMXIYERNXPIYFR-UHFFFAOYSA-N 1-ethylnaphthalene Chemical class C1=CC=C2C(CC)=CC=CC2=C1 ZMXIYERNXPIYFR-UHFFFAOYSA-N 0.000 description 1
- QPUYECUOLPXSFR-UHFFFAOYSA-N 1-methylnaphthalene Chemical class C1=CC=C2C(C)=CC=CC2=C1 QPUYECUOLPXSFR-UHFFFAOYSA-N 0.000 description 1
- GPOYJVWXGJBMOK-UHFFFAOYSA-N 1-phenoxy-4-phenylbenzene Chemical group C=1C=C(C=2C=CC=CC=2)C=CC=1OC1=CC=CC=C1 GPOYJVWXGJBMOK-UHFFFAOYSA-N 0.000 description 1
- TVYVQNHYIHAJTD-UHFFFAOYSA-N 2-propan-2-ylnaphthalene Chemical class C1=CC=CC2=CC(C(C)C)=CC=C21 TVYVQNHYIHAJTD-UHFFFAOYSA-N 0.000 description 1
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 1
- GRYLNZFGIOXLOG-UHFFFAOYSA-N Nitric acid Chemical compound O[N+]([O-])=O GRYLNZFGIOXLOG-UHFFFAOYSA-N 0.000 description 1
- 229920002302 Nylon 6,6 Polymers 0.000 description 1
- 229920003171 Poly (ethylene oxide) Polymers 0.000 description 1
- 239000004952 Polyamide Substances 0.000 description 1
- 206010042618 Surgical procedure repeated Diseases 0.000 description 1
- BOTDANWDWHJENH-UHFFFAOYSA-N Tetraethyl orthosilicate Chemical compound CCO[Si](OCC)(OCC)OCC BOTDANWDWHJENH-UHFFFAOYSA-N 0.000 description 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 description 1
- UAPZWZJRQDRPPW-UHFFFAOYSA-N [N].[O].[La] Chemical compound [N].[O].[La] UAPZWZJRQDRPPW-UHFFFAOYSA-N 0.000 description 1
- 238000010521 absorption reaction Methods 0.000 description 1
- 238000009825 accumulation Methods 0.000 description 1
- 230000009471 action Effects 0.000 description 1
- 230000000996 additive effect Effects 0.000 description 1
- 235000011037 adipic acid Nutrition 0.000 description 1
- 239000001361 adipic acid Substances 0.000 description 1
- 125000001931 aliphatic group Chemical group 0.000 description 1
- 229910052783 alkali metal Inorganic materials 0.000 description 1
- 150000004703 alkoxides Chemical class 0.000 description 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 1
- 238000004458 analytical method Methods 0.000 description 1
- 239000012736 aqueous medium Substances 0.000 description 1
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 1
- 229910052788 barium Inorganic materials 0.000 description 1
- DSAJWYNOEDNPEQ-UHFFFAOYSA-N barium atom Chemical compound [Ba] DSAJWYNOEDNPEQ-UHFFFAOYSA-N 0.000 description 1
- 239000002585 base Substances 0.000 description 1
- 239000004305 biphenyl Substances 0.000 description 1
- 229910052797 bismuth Inorganic materials 0.000 description 1
- JCXGWMGPZLAOME-UHFFFAOYSA-N bismuth atom Chemical compound [Bi] JCXGWMGPZLAOME-UHFFFAOYSA-N 0.000 description 1
- 238000009835 boiling Methods 0.000 description 1
- 150000004768 bromobenzenes Chemical class 0.000 description 1
- 125000004432 carbon atom Chemical group C* 0.000 description 1
- 238000006555 catalytic reaction Methods 0.000 description 1
- 239000003638 chemical reducing agent Substances 0.000 description 1
- 239000003795 chemical substances by application Substances 0.000 description 1
- 150000008422 chlorobenzenes Chemical class 0.000 description 1
- 238000004587 chromatography analysis Methods 0.000 description 1
- 239000004927 clay Substances 0.000 description 1
- 229910000152 cobalt phosphate Inorganic materials 0.000 description 1
- VLWBWEUXNYUQKJ-UHFFFAOYSA-N cobalt ruthenium Chemical compound [Co].[Ru] VLWBWEUXNYUQKJ-UHFFFAOYSA-N 0.000 description 1
- GIPIUENNGCQCIT-UHFFFAOYSA-K cobalt(3+) phosphate Chemical compound [Co+3].[O-]P([O-])([O-])=O GIPIUENNGCQCIT-UHFFFAOYSA-K 0.000 description 1
- 239000000084 colloidal system Substances 0.000 description 1
- 238000004891 communication Methods 0.000 description 1
- 238000009833 condensation Methods 0.000 description 1
- 230000005494 condensation Effects 0.000 description 1
- 238000010276 construction Methods 0.000 description 1
- ORTQZVOHEJQUHG-UHFFFAOYSA-L copper(II) chloride Chemical compound Cl[Cu]Cl ORTQZVOHEJQUHG-UHFFFAOYSA-L 0.000 description 1
- 150000001924 cycloalkanes Chemical class 0.000 description 1
- 150000001934 cyclohexanes Chemical class 0.000 description 1
- IGARGHRYKHJQSM-UHFFFAOYSA-N cyclohexylbenzene Chemical compound C1CCCCC1C1=CC=CC=C1 IGARGHRYKHJQSM-UHFFFAOYSA-N 0.000 description 1
- 230000008021 deposition Effects 0.000 description 1
- PWZFXELTLAQOKC-UHFFFAOYSA-A dialuminum;hexamagnesium;carbonate;hexadecahydroxide;tetrahydrate Chemical compound O.O.O.O.[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[OH-].[Mg+2].[Mg+2].[Mg+2].[Mg+2].[Mg+2].[Mg+2].[Al+3].[Al+3].[O-]C([O-])=O PWZFXELTLAQOKC-UHFFFAOYSA-A 0.000 description 1
- 150000002009 diols Chemical class 0.000 description 1
- CZZYITDELCSZES-UHFFFAOYSA-N diphenylmethane Chemical compound C=1C=CC=CC=1CC1=CC=CC=C1 CZZYITDELCSZES-UHFFFAOYSA-N 0.000 description 1
- 238000004090 dissolution Methods 0.000 description 1
- 238000005516 engineering process Methods 0.000 description 1
- 125000001033 ether group Chemical group 0.000 description 1
- 150000008423 fluorobenzenes Chemical class 0.000 description 1
- 239000013505 freshwater Substances 0.000 description 1
- 239000000499 gel Substances 0.000 description 1
- 239000010931 gold Substances 0.000 description 1
- 150000005171 halobenzenes Chemical class 0.000 description 1
- 230000002140 halogenating effect Effects 0.000 description 1
- 239000001307 helium Substances 0.000 description 1
- 229910052734 helium Inorganic materials 0.000 description 1
- SWQJXJOGLNCZEY-UHFFFAOYSA-N helium atom Chemical compound [He] SWQJXJOGLNCZEY-UHFFFAOYSA-N 0.000 description 1
- 150000004677 hydrates Chemical class 0.000 description 1
- 230000007062 hydrolysis Effects 0.000 description 1
- 238000006460 hydrolysis reaction Methods 0.000 description 1
- 229960001545 hydrotalcite Drugs 0.000 description 1
- 229910001701 hydrotalcite Inorganic materials 0.000 description 1
- 150000004679 hydroxides Chemical class 0.000 description 1
- 229910052738 indium Inorganic materials 0.000 description 1
- APFVFJFRJDLVQX-UHFFFAOYSA-N indium atom Chemical compound [In] APFVFJFRJDLVQX-UHFFFAOYSA-N 0.000 description 1
- 238000012844 infrared spectroscopy analysis Methods 0.000 description 1
- 239000000543 intermediate Substances 0.000 description 1
- 150000008424 iodobenzenes Chemical class 0.000 description 1
- FYDKNKUEBJQCCN-UHFFFAOYSA-N lanthanum(3+);trinitrate Chemical compound [La+3].[O-][N+]([O-])=O.[O-][N+]([O-])=O.[O-][N+]([O-])=O FYDKNKUEBJQCCN-UHFFFAOYSA-N 0.000 description 1
- WPBNNNQJVZRUHP-UHFFFAOYSA-L manganese(2+);methyl n-[[2-(methoxycarbonylcarbamothioylamino)phenyl]carbamothioyl]carbamate;n-[2-(sulfidocarbothioylamino)ethyl]carbamodithioate Chemical compound [Mn+2].[S-]C(=S)NCCNC([S-])=S.COC(=O)NC(=S)NC1=CC=CC=C1NC(=S)NC(=O)OC WPBNNNQJVZRUHP-UHFFFAOYSA-L 0.000 description 1
- AUHZEENZYGFFBQ-UHFFFAOYSA-N mesitylene Substances CC1=CC(C)=CC(C)=C1 AUHZEENZYGFFBQ-UHFFFAOYSA-N 0.000 description 1
- 125000001827 mesitylenyl group Chemical group [H]C1=C(C(*)=C(C([H])=C1C([H])([H])[H])C([H])([H])[H])C([H])([H])[H] 0.000 description 1
- 229910044991 metal oxide Inorganic materials 0.000 description 1
- 150000004706 metal oxides Chemical class 0.000 description 1
- UZKWTJUDCOPSNM-UHFFFAOYSA-N methoxybenzene Substances CCCCOC=C UZKWTJUDCOPSNM-UHFFFAOYSA-N 0.000 description 1
- QDBQXOAICGSACD-UHFFFAOYSA-N n'-hexylhexanediamide Chemical compound CCCCCCNC(=O)CCCCC(N)=O QDBQXOAICGSACD-UHFFFAOYSA-N 0.000 description 1
- 229910017604 nitric acid Inorganic materials 0.000 description 1
- 150000002894 organic compounds Chemical group 0.000 description 1
- 230000001590 oxidative effect Effects 0.000 description 1
- 239000001301 oxygen Substances 0.000 description 1
- 229910052760 oxygen Inorganic materials 0.000 description 1
- KDLHZDBZIXYQEI-UHFFFAOYSA-N palladium Substances [Pd] KDLHZDBZIXYQEI-UHFFFAOYSA-N 0.000 description 1
- 230000003094 perturbing effect Effects 0.000 description 1
- DLRJIFUOBPOJNS-UHFFFAOYSA-N phenetole Chemical compound CCOC1=CC=CC=C1 DLRJIFUOBPOJNS-UHFFFAOYSA-N 0.000 description 1
- 239000002574 poison Substances 0.000 description 1
- 231100000614 poison Toxicity 0.000 description 1
- 229920001281 polyalkylene Polymers 0.000 description 1
- 229920002647 polyamide Polymers 0.000 description 1
- 229920000642 polymer Polymers 0.000 description 1
- 229920001451 polypropylene glycol Polymers 0.000 description 1
- 239000011148 porous material Substances 0.000 description 1
- 239000000843 powder Substances 0.000 description 1
- 239000000047 product Substances 0.000 description 1
- 238000010926 purge Methods 0.000 description 1
- 229910052761 rare earth metal Inorganic materials 0.000 description 1
- 230000001172 regenerating effect Effects 0.000 description 1
- 239000012266 salt solution Substances 0.000 description 1
- 239000000741 silica gel Substances 0.000 description 1
- 229910002027 silica gel Inorganic materials 0.000 description 1
- 239000010703 silicon Substances 0.000 description 1
- 239000010944 silver (metal) Substances 0.000 description 1
- 238000002791 soaking Methods 0.000 description 1
- UKLNMMHNWFDKNT-UHFFFAOYSA-M sodium chlorite Chemical compound [Na+].[O-]Cl=O UKLNMMHNWFDKNT-UHFFFAOYSA-M 0.000 description 1
- 229960002218 sodium chlorite Drugs 0.000 description 1
- 238000001179 sorption measurement Methods 0.000 description 1
- 238000010561 standard procedure Methods 0.000 description 1
- 150000005846 sugar alcohols Polymers 0.000 description 1
- 239000000725 suspension Substances 0.000 description 1
- 238000003786 synthesis reaction Methods 0.000 description 1
- ISIJQEHRDSCQIU-UHFFFAOYSA-N tert-butyl 2,7-diazaspiro[4.5]decane-7-carboxylate Chemical compound C1N(C(=O)OC(C)(C)C)CCCC11CNCC1 ISIJQEHRDSCQIU-UHFFFAOYSA-N 0.000 description 1
- 238000002411 thermogravimetry Methods 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 229910052723 transition metal Inorganic materials 0.000 description 1
- 150000003624 transition metals Chemical class 0.000 description 1
- 238000004627 transmission electron microscopy Methods 0.000 description 1
- 150000003751 zinc Chemical class 0.000 description 1
- 229910021511 zinc hydroxide Inorganic materials 0.000 description 1
- 229940007718 zinc hydroxide Drugs 0.000 description 1
- 229910000368 zinc sulfate Inorganic materials 0.000 description 1
- 229960001763 zinc sulfate Drugs 0.000 description 1
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/19—Catalysts containing parts with different compositions
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/10—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of rare earths
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals of the platinum group metals
- B01J23/46—Ruthenium, rhodium, osmium or iridium
- B01J23/462—Ruthenium
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J23/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00
- B01J23/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals
- B01J23/54—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group B01J21/00 of noble metals combined with metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36
- B01J23/56—Platinum group metals
- B01J23/63—Platinum group metals with rare earths or actinides
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J37/00—Processes, in general, for preparing catalysts; Processes, in general, for activation of catalysts
- B01J37/02—Impregnation, coating or precipitation
- B01J37/024—Multiple impregnation or coating
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C5/00—Preparation of hydrocarbons from hydrocarbons containing the same number of carbon atoms
- C07C5/02—Preparation of hydrocarbons from hydrocarbons containing the same number of carbon atoms by hydrogenation
- C07C5/10—Preparation of hydrocarbons from hydrocarbons containing the same number of carbon atoms by hydrogenation of aromatic six-membered rings
- C07C5/11—Partial hydrogenation
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
- B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- B01J35/00—Catalysts, in general, characterised by their form or physical properties
- B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
- B01J35/391—Physical properties of the active metal ingredient
- B01J35/393—Metal or metal oxide crystallite size
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2521/00—Catalysts comprising the elements, oxides or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium or hafnium
- C07C2521/02—Boron or aluminium; Oxides or hydroxides thereof
- C07C2521/04—Alumina
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2521/00—Catalysts comprising the elements, oxides or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium or hafnium
- C07C2521/06—Silicon, titanium, zirconium or hafnium; Oxides or hydroxides thereof
- C07C2521/08—Silica
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2521/00—Catalysts comprising the elements, oxides or hydroxides of magnesium, boron, aluminium, carbon, silicon, titanium, zirconium or hafnium
- C07C2521/12—Silica and alumina
-
- C—CHEMISTRY; METALLURGY
- C07—ORGANIC CHEMISTRY
- C07C—ACYCLIC OR CARBOCYCLIC COMPOUNDS
- C07C2523/00—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00
- C07C2523/38—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of noble metals
- C07C2523/40—Catalysts comprising metals or metal oxides or hydroxides, not provided for in group C07C2521/00 of noble metals of the platinum group metals
- C07C2523/46—Ruthenium, rhodium, osmium or iridium
Definitions
- This is a catalyst and a process for partially hydrogenating polycyclic and monocyclic aromatic hydrocarbons such as benzene, naphthalenes, biphenyls, and alkylbenzenes to produce the corresponding cycloolefins.
- the catalyst is a hydrogenation catalyst comprising ruthenium and a promoter metal, such as cobalt, on a composite support. It is a process in which the product cycloolefin is produced in high yield and with high selectivity.
- Cycloolefins are materials useful in the production of other high value products. For instance, in the commercial production of the polyamide known as NYLON 66, cyclohexene is first converted to cyclohexanol. The cyclohexanol is then oxidized to adipic acid with nitric acid, converted to a salt, and finally converted to the polymer. Other members of the cycloolefin family have similar utility. The previously used hydrogenation processes have fallen into two classes: one class consists of multistep processes starting with benzene or substituted benzenes and produces cyclohexanes or halocyclohexanes as intermediates.
- one such process involved the steps of hydrogenating benzene to form cyclohexane, oxidizing the cyclohexane to produce cyclohexanol, and dehydrating the cyclohexanol to produce cyclohexene.
- the other major multistep process involves the steps of halogenating benzene to produce a halobenzene, hydrogenating the resulting product to halocyclohexane, and dehydrohalogenating the halocyclohexane to cyclohexene.
- the other class of processes is a single step synthesis in which monocyclic aromatics are only partially hydrogenated to form the corresponding cycloolefins. Ruthenium catalysts are often used in these processes.
- U.S. Patent No. 3,912,787 discloses a partial hydrogenation process for the production of cyclic olefins using an aqueous dispersion of a solid ruthenium containing catalyst promoted with a transition metal. The aqueous dispersion is maintained at an essentially neutral or acid pH condition. The catalyst may be supported on well known oxidic supports.
- U.S. Patent No. 4,079,097 to Antos shows a process for dehydrogenating hydrocarbons using composite catalysts of a combination of a platinum group component, a cobalt component, and a bismuth component all on a porous catalytic carrier.
- 4,197,415 shows a process for selectively partially hydrogenating aromatic hydrocarbons to cyclic olefins by contacting the aromatic hydrocarbon with hydrogen and a ruthenium catalyst in an aqueous dispersion containing the salt of a phosphorous acid.
- the ruthenium catalyst may also be promoted by one of a large number of metals preferably, however, indium, copper, or silver.
- U.S. Patent No. 4,392,001 to Don et al. shows a process for the partial hydrogenation of an aromatic hydrocarbon in the gas phase using a ruthenium catalyst. The reaction takes place in the presence of water vapor.
- U.S. Patent No. 4,495,373 to Niwa et al. shows an improved catalyst system for the partial hydrogenation of an aromatic hydrocarbon compound in the liquid phase using an admixture of water and a ruthenium-containing solid catalyst.
- the catalyst is prepared by the hydrolysis gelation of a silicon or aluminum alkoxide in a solution containing a ruthenium compound such as ruthenium alkoxide. After gelation, the gelled material is dried. Copper may be included in the gel catalyst.
- the patent suggests that the resulting catalyst provides "improved catalyst activity and selectivity" in a partial hydrogenation of an aromatic compound over conventional ruthenium-containing catalysts prepared by later impregnation of a preformed silica gel carrier.
- U.S. Patent No. 4,575,572 to Ichihashi et al. also shows a process for partially hydrogenating aromatic hydrocarbons using a catalyst of ruthenium and at least one of iron, cobalt, silver, and copper supported on a barium sulfate carrier all in the presence of water.
- U. S. Patent No. 4,665,274 to Ichihashi et al. discloses a process for producing cycloolefins by partial hydrogenation of the corresponding aromatic hydrocarbon with hydrogen gas in the presence of water and a catalyst of ruthenium and one or more metals selected from iron, cobalt, silver, and copper supported on a barium sulfate carrier.
- the carrier also includes one or more of silica, titania, and alumina.
- U.S. Patent No. 4,678,861 to Mitsui et al (assigned to Asahi Kasei Kogyo K.K.) teaches a process for producing cycloolefins by partially hydrogenating a monocyclic aromatic hydrocarbon in the presence of a supported ruthenium catalyst comprising a rare earth element (apparently preferably lanthanum) .
- the ruthenium may be present in an amount between 0.1 and 10% of the overall weight of the catalyst.
- the process is carried out in a multiphase reaction medium of water, hydrocarbon, catalyst, and hydrogen.
- the aqueous phase preferably is alkaline and contains dissolved ZnO or Zn(0H) 2 .
- U.S. Patent No. 4,734,536 to Nagahara et al. shows a process for producing a cycloolefin by a partial hydrogenation of a monocylic aromatic hydrocarbon using a neutral or acidic aqueous solution in the presence of a particulate hydrogenation catalyst of metallic ruthenium having an average crystallite size of 20 ⁇ A or less, zinc compound as a promoter, and at least one additive selected from the group of oxides, hydroxides, and hydrates of Zr, Hf, Ti, Nb, Ta, Cr, Fe, Co, Al, Ga, and Si.
- Japanese Kokai 61-085,334 discloses the preparation of cycloolefin by partial hydrogenation of aromatic hydrocarbons using a ruthenium-silica catalyst which has been activated through the use of an aliphatic polyhydric alcohol.
- Japanese Kokai 62-045544 (assigned to the Asahi Chemical Industry co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water, finely crystalline metallic ruthenium (desirably below 200 A, most preferably below 100 A) containing zinc, and an acid (preferably sulfuric acid) to form a solution having a pH between 2.0 and 6.5.
- Japanese Kokai 62-081331 to Nagahara et al (assigned to the Asahi Chemical Industry co.) teaches that the deactivation of Ru-metal catalysts in benzene partial hydrogenation reactions using water as the reaction medium may be minimized by using reactors having walls of titanium or zirconium.
- Chemical Industry co. teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water, finely crystalline metallic ruthenium (desirably below 200 A, most preferably belbw 100 A) , salts of Group IA or IIA metals (preferably zinc sulphate) and an acid (preferably sulfuric acid) to form a solution having a pH between 0.5 and 7.0.
- finely crystalline metallic ruthenium desirably below 200 A, most preferably belbw 100 A
- salts of Group IA or IIA metals preferably zinc sulphate
- an acid preferably sulfuric acid
- Japanese Kokai 62-142126 to Ichihashi et al. (assigned to the Sumitomo Chemical Co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water, ruthenium on supports of Group IA alkali metal salts of phosphorous oxoacids, and salts of phosphorous oxoacids as additives (optionally, with a metal of iron, cobalt, nickel, copper, silver, or zinc --particularly zinc, aluminum, barium, and cobalt orthophosphate) .
- An example showed 3.8% conversion of benzene and 50.8% selectivity to cyclohexene.
- Japanese Kokai 62-205037 to Nagahara et al (assigned to the Asahi Chemical Industry co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water, finely crystalline metallic ruthenium (desirably below 200 A, most preferably below 100 A) , and solid basic zinc sulphate.
- Japanese Kokai 62-255438 to Niwa et al (assigned to Fuji K.K.
- Japanese Kokai 62-294,422 assigned to Asahi Chemical Industries, K.K. shows a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water, a hydrogenating catalyst containing fine crystallite ruthenium, and a solid basic zinc sulfate.
- the conversion of benzene is said to be about 70% and the selectivity to cyclohexene is said to be 70% to 80%.
- Japanese Kokai 63-048232 (assigned to the Asahi Chemical Industry Co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of a ruthenium catalyst on a carrier, zinc oxide or hydroxide, and water containing an accelerator selected from salts of Group IA or IIA metals, manganese, zinc or cobalt.
- Japanese Kokai 63-88139 to Nagahara et al. shows a process for partially hydrogenating single ring aromatics using hydrogen in the presence of a neutral to acidic aqueous solution and a hydrogenation catalyst containing metallic ruthenium crystallites with a diameter of 20 ⁇ A or less, at least one separate metal hydroxide or hydrated metal oxide selected from Ti, Zr, Hf, Nb, Ta, Cr, Fe, Co, Al, Ga, and Si, and further containing at least one solid basic zinc salt.
- Japanese Kokai 63-152333 (assigned to the Asahi Chemical Industry co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of solid basic zinc compounds in neutral or acidic water and metallic ruthenium on a support (preferably gamma-alumina) .
- Japanese Kokai 63-243038 (assigned to the Asahi
- Chemical Industry co. teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of zinc compounds in neutral or acidic water and finely crystalline metallic ruthenium (desirably between 3 ⁇ A and 200 A, most preferably between 4 ⁇ A and 100 A) on a support (preferably Zr0 2 or Hf0 2 ) .
- Japanese Kokai 63-243039 (assigned to the Asahi Chemical Industry co.) teaches a process for the partial hydrogenation of monocyclic aromatic hydrocarbons in the presence of water; a hydrogenation catalyst of colloidal metallic ruthenium on a metal salt, hydroxide, or oxide support; and a soluble zinc compound.
- Japanese Kokai 1-159,059 to Nagahara et al. shows a process for regenerating a ruthenium catalyst which has been used for partial hydrogenation of a cycloaromatic.
- the catalyst is regenerated by contacting the catalyst with oxygen or with sodium chlorite.
- a Japanese publication entitled Senryotoyakuhin, 1986, 31 (11) , 297-308 discloses a process for preparing cyclohexene by partial hydrogenation of benzene. The reaction takes place in an aqueous medium at about 150°C to 200°C and 30 atmospheres to 70 atmospheres in the presence of a ruthenium catalyst and a copper, silver, or cobalt promoter. Niwa et al. in a letter in the Journal of
- the catalysts are made by mixing ruthenium chloride and (optionally, copper chloride) with a diol such as ethylene glycol to form a solution of metal complexes. Tetraethoxysilane was added to the prior solution and water was added to hydrolyze the various metal alkoxides formed during the stirring. The material was then gelled and dried to form the catalyst.
- the process of the present invention can be operated at neutral pH and in the absence of added salts and is, therefore, more compatible with lower cost materials of construction than, for example, processes cited in the prior art utilizing sulfuric acid or large amounts of dissolved salts in the aqueous phase.
- This invention is a catalyst and process for partially hydrogenating polycyclic or monocyclic aromatic hydrocarbons to produce the corresponding cycloolefins.
- the catalyst is a hydrogenation catalyst comprising ruthenium and a selectivity promoter, preferably cobalt, on an oxidic, preferably composite, support. It is a process in which the product cycloolefin is produced in high yield, with high selectivity, and with very high productivities and efficiencies based on ruthenium.
- the process is a multiphase operation in which a gaseous hydrogen phase and the solid catalyst are intimately intermixed with two liquid phases: an aqueous phase and a hydrocarbon phase containing both feedstock and product hydrocarbons.
- the catalysts comprise ruthenium metal and a selectivity promoter, preferably cobalt metal, on a composite oxidic support.
- a base oxide such as alumina or silica is at least partially surrounded by a minor amount of a second relatively low inherent surface area oxidic material.
- the second oxidic material may be selected from metal or semimetal oxides or a lanthanum- containing material of the formula:
- Figure 1 is a graph showing the composition versus reaction time for the hydrogenation of benzene to a mixture of cyclohexene and cyclohexane according to the procedure of Example 3.
- the aromatic feedstocks may be such materials as substituted or non- substituted naphthalenes or biphenyls, benzene, or alkylbenzenes such as toluene, o-xylene, m-xylene, p-xylene, ethylbenzene, or similar materials.
- the hydrogenation catalyst comprises ruthenium and a selectivity promoter on a composite support. It is a process in which the product cycloolefin is produced in high yield, with high selectivity, and with very high productivities and efficiencies based on ruthenium.
- the feedstocks suitable for this partial hydrogenation process may comprise monocyclic aromatic hydrocarbons such as benzene and alkylbenzenes.
- Linear and branched alkylbenzene feedstocks may include compounds such as benzene, toluene, o-, m-, p-xylene, ethylbenzene, n-propylbenzene, cumene, butylbenzenes such as t-butylbenzene and isobutylbenzene, phenylcyclohexane, mesitylene; alkoxy-substituted benzenes such as anisole and phenetole; polyalkylene oxide-substituted benzenes such as polyethylene oxide phenyl ether, or polypropylene oxide phenyl ether; halogenated benzenes, such as fluorobenzenes, chlorobenzenes, bromobenzenes, io
- the monocyclic aromatic compound is unsubstituted, or substituted with no more than one substituent such as an alkyl moiety.
- the compound is benzene.
- Other suitable feedstocks include polycyclic aromatic hydrocarbons which are substantially aromatic in character, i.e., the overall compound is not so fused or condensed as to lose its ability to act as an aromatic compound in classic chemical reactions in which aromatics take part.
- the aromatic rings in the polycyclic aromatic compounds may be fused or non-fused. The rings may be substituted at any position with alkyl or ether moieties, preferably, and if present, the substituents are alkyl in nature and contain 1-10 carbon atoms.
- the polycyclic aromatic is unsubstituted or substituted with no more than two C 2 moieties.
- suitable polycyclic aromatic compounds are biphenyl, diphenyl ether, 4-phenoxy-1,1' -biphenyl, terphenyl, tetraphenyl, diphenylmethane, 1,2-diphenylethane, 1,3- iphenylpropane, methylbiphenyls, ethylbiphenyls, 3- or 4- isopropylbiphenyls, naphthalene, methylnaphthalenes, ethylnaphthalenes, beta-isopropylnaphthalenes, and similar naphthalenes.
- the polycyclic aromatic compound is a 12 _ 24 compound. Most preferably the polycyclic aromatic compound are naphthalenes or biphenyls.
- the feedstream may contain other hydrocarbon materials as well so long as they do not substantially interfere with the partial hydrogenation reaction. For instance, short chain linear and cyclic alkanes do not typically detract from the overall reaction and in some instances improve the overall productivity of the process. Catalysts
- the process employs a hydrogenation catalyst comprising ruthenium and a selectivity promoter, preferably cobalt metal, on a composite support.
- Ruthenium is present in at least a catalytic amount, i.e., an amount at least suitable for causing a partial hydrogenation reaction to take place on an aromatic compound.
- the catalyst need contain no more than about 20 % by weight ruthenium (based on the total weight of the ruthenium and the composite support) and preferably less than about 10% by weight and most preferably about 5-10% by weight.
- the catalyst contains ruthenium crystallites which are well dispersed and no more than about 25 A in average diameter.
- the selectivity promoter is present in an amount sufficient to produce enhanced selectivity to the partially hydrogenated cycloolefin product. When it is present in too low an amount no appreciable effect is observed; when it is present in too high an amount it can act as a catalyst poison and cause low reaction rates and low selectivities to the desired cycloolefin.
- the selectivity promoter may be selected from Fe, Co, Ni, Zn, Cu, Ag, Au, Pd, and Pt, It is preferably cobalt metal present in a weight ratio of cobalt-to-ruthenium of 0.05:1 to 5:1, preferably 0.1:1 to 2:1, and more preferably from 0.5:1 to 1.5:1. Similar ratios are appropriate for the other metals.
- That desired impregnation procedure involves dissolving a ruthenium compound such as ruthenium nitrosylnitrate or RuCl 3 hydrate in an acidic solution (preferably containing 1.0 % to 30 % HC1) and then holding the resulting solution at an elevated temperature (preferably between 70°C and the boiling point of the solution) for a period of time sufficient to enhance the resulting catalyst's activity and stability.
- the solution preferably after cooling, is then contacted with a suitable catalyst support and finally treated to dry the solid, which is then reduced to convert the supported ruthenium to its metallic form.
- the method for placing the selectivity promoter onto the support is believed to be critical to the performance of the catalyst. It is considered necessary first to have the ruthenium present on the surface of the support in the metallic state. The selectivity promoter is then loaded onto the support without perturbing the morphology of the supported metallic ruthenium. Our preferred method for loading the selectivity promoter onto the support is by reductive absorption from an aqueous solution of a dissolved salt of the selectivity promoting metal.
- the composite support may comprise a major amount of a first relatively high specific surface area oxidic core material which is at least partially surrounded by a minor amount of a second relatively low inherent surface area oxidic material.
- the second oxidic material may be selected from metal or semimetal oxides or a lanthanum-containing material of the formula:
- the specific surface area of the composite support is substantially higher than that of the second oxidic material.
- Very desirable oxidic core materials are high surface area (greater than about 50 m 2 /gm) silica, alumina, and silica-alumina.
- silica and transition phase aluminas such as eta or gamma phase materials or mixtures of the two are suitable.
- the second oxidic material is either a metal or semimetal oxide having a low inherent surface area (less than about 10 irr/gm) or the lanthanum oxygen-nitrogen material mentioned above.
- Suitable metal or semimetal oxides include lanthanum oxide, zinc oxide, boria, ceria, zirconia, titania, or the like.
- One preferred method of preparing a desired catalyst is the following procedure:
- the high surface area oxidic core material is crushed and sieved to a powder with particle sizes in the range of 0.1 micron to 1 millimeter in diameter.
- a salt precursor to the second oxidic material is loaded onto the oxidic core material from an aqueous solution by standard methods such as incipient wetness, adsorption, or others known to those skilled in the art.
- the composite is calcined in air at 500- 1500°C for 1-20 hours to convert the supported salt precursor to the oxide or to a mixture of oxide, nitrate, and oxynitrate.
- a ruthenium salt solution is prepared by dissolving the ruthenium salt in water that preferably contains HC1; the acidic solution is heated to 80-100°C for about 1 hour; the acidic solution is cooled to room temperature.
- a sufficient quantity of the acidic 5 ruthenium solution to give the desired ruthenium loading is contacted with the composite oxide support to effect loading of the ruthenium onto the composite oxide support. It is preferred to adjust the
- the supported ruthenium salt is reduced to ruthenium metal.
- reducing the supported ruthenium salt is by heating at 200-600°C in flowing hydrogen for 1-20 hours. Other reduction methods and other reducing agents may be used.
- the supported ruthenium metal is suspended in an aqueous solution of a salt of the selectivity promoter, preferably the salt is cobalt sulfate, under hydrogen at elevated pressure and heated to 100-200°C, preferably to 150°C, and agitated for a sufficient time to effect reduction and loading of the cobalt onto the support.
- a salt of the selectivity promoter preferably the salt is cobalt sulfate
- the aqueous solution is removed and replaced with water that has a pH in the range of 2 to 7, preferably 6-7.
- the method for removal and replacement of the aqueous solution is not critical but one preferred method is to perform the operation in a stirred tank reactor and feed several volumes of the replacement water continuously to the reactor while removing the aqueous phase at the same rate as the addition rate. After feeding
- the aqueous phase composition in the reactor will be the same as the replacement water.
- the procedure outlined above for generating the catalyst of the present invention has two key factors which are considered to be important in producing the desired catalyst.
- the first factor is the mild conditions required to effect reduction of the selectivity promoter cation; at these conditions the morphology of the supported ruthenium metal particles is stable.
- the second factor is the requirement that the reduction of the selectivity promoting cation is catalyzed by ruthenium; this results in the selectivity promoting metal being in close physical proximity to the ruthenium metal where its selectivity promoting effect is realized.
- the active catalyst comprises ruthenium metal particles and cobalt metal supported on a composite support wherein the composite support has a BET surface area of at least 50 m 2 /gm and wherein a major fraction of the ruthenium particles are less than 25 A in diameter.
- the process of this invention entails using the noted catalyst in an amount of about 0.01% to about 50% of the weight of the aromatic to be partially hydrogenated.
- the amount of catalyst should be minimized, but 1% to about 20% should be adequate under most circumstances to perform the reaction.
- the amount of catalyst may also be varied depending upon the mode of operation desired and the desired overall reaction rate.
- mode of operation we mean that the process of partial hydrogenation may be carried out in a continuous or a discontinuous mode, in fixed bed, trickle bed or slurry reactors, in a batch, semi-batch, multiple batch reactions, or a continuous stirred tank reactor or a series of continuous stirred tank reactors.
- This process uses an inherently complex four- phase system: a gaseous hydrogen phase; an aqueous phase; a hydrocarbon phase containing aromatic feeds and partially and fully hydrogenated products; and the solid catalyst phase.
- the system is preferably operated in a mode which produces the maximum amount of partially hydrogenated products.
- the ratio of the aqueous phase volume to the organic phase (aromatic plus products) volume is preferably at 1:1 or below 1:1. It is preferred to use the minimum amount of aqueous phase for a given volume of organic phase to reduce the required size of the reactor(s) .
- the actual ratio will depend on the mode of operation. For continuous stirred tank reactors in series or as a single reactor, the preferred volume ratio is from 0.1:1 to 1:1.
- the phase ratio is determined by factors other than reactor size.
- the volumetric flow of the aqueous phase can be much higher than the volumetric flow of the feed aromatic, wherein the volumetric flow of the feed aromatic is dependent upon the desired conversion per unit length of the reactor.
- the volumetric feed ratio of aqueous phase to aromatic feed will generally be greater than 5:1 and could be in the range of 5:1 to 100:1.
- the organic phase be the continuous phase with the aqueous phase being dispersed, under agitation, as small droplets within the continuous organic phase.
- the requirement is generally met when the volume ratio of aqueous phase to organic phase is at 1:1 or less than 1:1.
- partial hydrogenation may be carried out continuously or by batch.
- other reactors employing suspended catalysts may be employed as may fixed or trickle beds.
- the reaction conditions are dependent in large measure upon the chosen form of the catalyst but in general we have found that the overall process pressure (hydrogen pressure plus the vapor pressure of the reactants, water, and products) should be between about 200 psig and 2000 psig, preferably between 300 psig and 800 psig.
- the reaction temperature should be between 100°C and 200°C, preferably between 120°C and 170°C.
- hydrogen is fed "on demand"; that is, the hydrogen pressure is maintained at a constant value and hydrogen is continuously added to the reactor as it is consumed by the partial hydrogenation reaction.
- the" excess volume of hydrogen acts as a stripping agent to remove products from the reaction zone in the vapor phase.
- a particularly preferred mode of operation includes flowing excess hydrogen at a sufficient rate to remove products from the reaction zone at the same molar rate as the feed rate of the aromatic compound being partially hydrogenated. By careful adjustments of the aromatic feed rate and the hydrogen flow rate, the residence time of the aromatic feed in the reaction zone may be controlled.
- This mode of operation greatly simplifies the operational difficulties inherent in modes of operation that require transfer and recycle of the aqueous catalyst slurry.
- the solid catalyst remains in the reactor(s) and the need to pump a solids- containing slurry is eliminated.
- Some of the water in the reactor(s) is also removed through the stripping action of the excess hydrogen flow. This water may be recovered upon cooling and condensation of the vapor phase since the organic compounds form a separate liquid phase. The recovered water may be recycled to the reactor(s) to maintain the aqueous volume at a constant value.
- this water may be discarded and fresh water used to make-up the aqueous volume in the reactor(s) .
- the ratio of hydrogen to aromatic is not a critical parameter, it is required that a sufficient volume of hydrogen be present in the reaction zone to allow for efficient mixing and dissolution of hydrogen in the organic and aqueous phases. This can be accomplished by maintaining a vapor volume in the reactor equal to 0.1 to 1 times the total liquid volume.
- the productivity of the catalyst when used in the inventive process desirably is in the range of 10 to 500 pounds of partially hydrogenated aromatic product per pound of catalyst per hour, preferably 30 to 300 pounds of partially hydrogenated aromatic per pound of catalyst per hour.
- % Yield (Y) (moles of cycloolefin produced/moles of aromatic feed) times 100
- EXAMPLE 1 This example shows the preparation of a composite support of lanthanum oxide and lanthanum oxynitrate on silica.
- a 200 gm sample of powdered silica (Degussa Sipernat 22; average agglomerate size of 100 microns; surface area of 190 m 2 /gm) was heated in air at 500°C for 16 hours.
- a solution of 59.07 gm of La(N0 3 ) 3 • 6H 2 0 (Alfa) in 200 ml distilled water was prepared. After cooling the silica to room temperature, the aqueous solution of lanthanum nitrate was added dropwise with continuous mechanical mixing to load the silica pores.
- This incipient wetness loading method resulted in the formation of a free flowing material which was dried at 80°C for 3 hours with intermittent mixing every 15 minutes during the first hour. The dried solid was heated in air at 500°C for 16 hours.
- the nominal loading of lanthanum species, as weight percent lanthanum, was 9.5 wt.%.
- Infrared spectroscopic analysis confirmed the presence of nitrate in the sample.
- Thermal gravimetric analysis confirmed that the supported component consisted of a mixture of lanthanum oxide and lanthanum oxynitrate.
- the surface area of the composite support was about 130 m 2 /gm.
- EXAMPLE 2 This example shows the preparation of a metallic ruthenium catalyst promoted with metallic cobalt on a composite support.
- the composite supported metallic ruthenium of this example was prepared by the incipient wetness method using an incipient wetness volume of one milliliter per gram of composite support from Example 1.
- the desired loading was 10 wt.% ruthenium, thus the composite support was impregnated twice with sufficient solution to give 5 wt.% ruthenium per impregnation.
- a solution of 20% aqueous HC1 was prepared by adding 237.8 milliliters of concentrated HC1 to 202.2 milliliters of distilled water.
- the first impregnation solution was prepared by dissolving 25.85 gm of RuCl 3 *xH 2 0 (Johnson Matthey, 44.8% ruthenium) in 220 milliliters of the 20% HC1 solution.
- the solution was heated to 90 Q C and held at 90°C for one hour. After cooling to room temperature, the solution was added dropwise, with mechanical mixing, to 220 gm of the composite support from Example 1.
- the resulting free flowing material was dried at 80°C with intermittent mixing every 15 minutes during the first hour.
- the dried material was cooled to room temperature and the incipient wetness loading procedure repeated with a second solution of 28.85 gm of RuCl 3 »xH 2 0 in 220 milliliters of 20% HC1 that had been heated to 90°C, and held at 90°C for one hour, and cooled to room temperature.
- the resulting free flowing material was dried at 80°C with intermittent mixing every 15 minutes during the first hour.
- the supported ruthenium salt was reduced to supported ruthenium metal by placing a quantity (2-5 gm) into a tubular reactor, purging the reactor with helium for 15 minutes at a flow of 2 standard liters per minute, switching to flowing hydrogen at 2 standard liters per minute, heating to 110°C at 7°C per minute, holding at 110°C for 30 minutes, heating to 400°C at 6°C per minute, holding at 400°C for 3 hours, and cooling to room temperature.
- the supported ruthenium metal was stored in an inert atmosphere glove box until use. Analysis of the ruthenium crystallite size using transmission electron microscopy showed that more than 90% of the well dispersed crystallites were smaller than 25 A in diameter.
- a sample (0.3 gm) of the supported metallic ruthenium was added to a one liter TEFLON-lined reactor containing 150 ml of distilled water at 150°C into which 0.9 gm CoS0 4 *7H 2 0 had been dissolved; * *the pressure was maintained at 400 psig with hydrogen and the suspension was stirred at 2000 RPM.
- the pH of the aqueous phase dropped from an initial value of 6-7 to about 3 during this treatment indicating reduction of cobalt(II) and deposition of cobalt metal onto the supported metallic ruthenium.
- the mixing rate was reduced to 50 RPM and 750 ml of deoxygenated water at pH 5 was pumped into the reactor at a rate of about 25 ml per minute; the well mixed aqueous phase was removed at the same rate of addition.
- the aqueous phase remaining in the reactor (150 ml) had a pH of 5 and contained less than 5 ppm of dissolved salts.
- the weight ratio of cobalt-to-ruthenium was approximately 1:1.
- Example 2 To the ruthenium-cobalt on composite support catalyst prepared in Example 2 was added 250 ml of benzene (preheated to 150°) and the total pressure adjusted to 650 psig with hydrogen. Stirring was maintained at 2000 RPM and the pressure at 650 psig for the duration of the reaction; the pH remained at a value of about 5 during the course of the reaction.
- the liquid mixture in the reactor was sampled periodically and the composition was determined by a standard gas chromatographic method. The composition versus time is shown in the Figure. The maximum yield of cyclohexene was 35.7% at 75.0% conversion after a reaction time of 50 minutes. The selectivity to cyclohexene was 47.6%.
- EXAMPLE 4 This example shows the use of a catalyst prepared as in Example 2 with the use of less cobalt sulfate (0.3 gm) in the aqueous phase used to load cobalt onto the composite supported metallic ruthenium and using water at pH 7 to replace the aqueous phase and carry out the hydrogenation of benzene. All other steps and conditions were identical to those used in Example 3.
- the maximum yield of cyclohexene was 34.4% at 77.0% conversion after a reaction time of 75 minutes.
- the selectivity to cyclohexene was 44.7%.
- the productivity was 274 pounds of cyclohexene per pound of catalyst per hour and the efficiency was 2740 pounds of cyclohexene per pound of ruthenium per hour.
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
- Catalysts (AREA)
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP93906270A EP0628020A4 (en) | 1992-02-26 | 1993-02-26 | Improved process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins. |
JP5515112A JPH07504418A (ja) | 1992-02-26 | 1993-02-26 | 芳香族に部分的に水素添加して,シクロオレフィンを生産する水洗触媒および改良プロセス |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US07/843,347 US5414171A (en) | 1992-02-26 | 1992-02-26 | Process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins |
US07/843,347 | 1992-02-26 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO1993016972A1 true WO1993016972A1 (en) | 1993-09-02 |
Family
ID=25289713
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US1993/001828 WO1993016972A1 (en) | 1992-02-26 | 1993-02-26 | Improved process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins |
Country Status (7)
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP0691320A1 (de) | 1994-07-08 | 1996-01-10 | Basf Aktiengesellschaft | Verfahren zur kontinuierlichen Herstellung von Cyclohexen durch partielle Hydrierung von Benzol |
US5569803A (en) * | 1993-12-24 | 1996-10-29 | Mitsubishi Chemical Corporation | Method for producing a cycloolefin |
WO2012059387A1 (de) | 2010-11-02 | 2012-05-10 | Basf Se | Verfahren zur herstellung eines phenylcyclohexans |
US8653313B2 (en) | 2010-11-02 | 2014-02-18 | Basf Se | Process for preparing a phenylcyclohexane |
Families Citing this family (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
BE1009128A3 (fr) * | 1994-12-19 | 1996-12-03 | Mitsubishi Chem Corp | Procede de production de cycloolefines. |
DE10128205A1 (de) * | 2001-06-11 | 2002-12-12 | Basf Ag | Ruthenium-Katalysatoren |
GB0222240D0 (en) * | 2002-09-25 | 2002-10-30 | Ici Plc | Cobalt catalysts |
EP1767270A4 (en) | 2004-07-09 | 2012-09-19 | Asahi Kasei Chemicals Corp | CATALYST FOR PRODUCTION OF CYCLOOLEFINS AND PROCESS FOR PRODUCTION |
FR2882531B1 (fr) * | 2005-02-25 | 2007-04-27 | Inst Francais Du Petrole | Procede de preparation de catalyseurs multimetalliques utilisables dans des reactions de transformation des hydrocarbures |
US20090118119A1 (en) * | 2007-11-01 | 2009-05-07 | Sud-Chemie Inc. | Water gas shift catalyst |
WO2009058569A2 (en) * | 2007-10-31 | 2009-05-07 | Sud-Chemie Inc. | Catalyst for reforming hydrocarbons |
US20090108238A1 (en) * | 2007-10-31 | 2009-04-30 | Sud-Chemie Inc. | Catalyst for reforming hydrocarbons |
SG188100A1 (en) * | 2008-02-01 | 2013-03-28 | Johnson Matthey Plc | Process for the conversion of fatty acids and derivatives thereof |
GB0913193D0 (en) * | 2009-07-29 | 2009-09-02 | Johnson Matthey Plc | Deoxygenation process |
CN103787817B (zh) * | 2012-11-01 | 2015-09-30 | 中国石油化工股份有限公司 | 一种环己烯的制备方法 |
CN103785410B (zh) * | 2012-11-01 | 2016-03-30 | 中国石油化工股份有限公司 | 一种苯制环己烯催化剂及其制备方法和应用 |
JP7087394B2 (ja) * | 2017-09-29 | 2022-06-21 | 東ソー株式会社 | ルテニウムプリカーサを回収するald/cvdプロセス |
Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3912787A (en) * | 1972-07-26 | 1975-10-14 | Phillips Petroleum Co | Selective partial hydrogenation of aromatics |
US4056489A (en) * | 1973-12-10 | 1977-11-01 | Engelhard Minerals & Chemicals Corporation | High temperature stable catalyst composition and method for its preparation |
US4162235A (en) * | 1976-06-17 | 1979-07-24 | Johnson, Matthey & Co., Limited | Catalysts |
US4197415A (en) * | 1976-10-08 | 1980-04-08 | Toray Industries, Inc. | Process for preparing cyclic olefins by selective partial hydrogenation of aromatic hydrocarbons |
US4235755A (en) * | 1979-02-21 | 1980-11-25 | Uop Inc. | Hydrocarbon dehydrogenation method and nonacidic multimetallic catalytic composite for use therein |
US4665274A (en) * | 1985-09-11 | 1987-05-12 | Sumitomo Chemical Company, Limited | Method for producing cycloolefins |
US4678861A (en) * | 1985-10-23 | 1987-07-07 | Asahi Kasei Kogyo Kabushiki Kaisha | Process for producing a cycloolefin |
US4734536A (en) * | 1985-10-03 | 1988-03-29 | Asahi Kasei Kogyo Kabushiki Kaisha | Process for producing cycloolefins |
Family Cites Families (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3981795A (en) * | 1975-08-08 | 1976-09-21 | Uop Inc. | Hydrocarbon conversion with an acidic multimetallic catalytic composite |
DE3164339D1 (en) * | 1980-12-31 | 1984-07-26 | Stamicarbon | Process for the preparation of a cycloalkene through partial hydrogenation of the corresponding aromatic hydrocarbon |
JPS6059215B2 (ja) * | 1983-02-24 | 1985-12-24 | 工業技術院長 | ベンゼンからのシクロヘキセンの製法 |
DE3569233D1 (en) * | 1984-07-31 | 1989-05-11 | Sumitomo Chemical Co | A method for producing cycloolefins |
JPS6185334A (ja) * | 1984-10-02 | 1986-04-30 | Sumitomo Chem Co Ltd | シクロオレフインの製造法 |
JPS6245544A (ja) * | 1985-08-22 | 1987-02-27 | Asahi Chem Ind Co Ltd | シクロオレフインの製造方法 |
JPH0739353B2 (ja) * | 1985-09-18 | 1995-05-01 | 旭化成工業株式会社 | 触媒の劣化防止方法 |
JPH0639399B2 (ja) * | 1985-10-02 | 1994-05-25 | 旭化成工業株式会社 | 単環芳香族炭化水素の部分水素化法 |
JPS6281332A (ja) * | 1985-10-03 | 1987-04-14 | Asahi Chem Ind Co Ltd | シクロオレフインを製造する方法 |
JPS62108826A (ja) * | 1985-11-05 | 1987-05-20 | Asahi Chem Ind Co Ltd | 単環芳香族炭化水素の部分水素化方法 |
JPS62142126A (ja) * | 1985-12-13 | 1987-06-25 | Sumitomo Chem Co Ltd | シクロオレフインの製造法 |
JPS62205037A (ja) * | 1986-03-03 | 1987-09-09 | Asahi Chem Ind Co Ltd | シクロオレフインの製造方法 |
JPS62255438A (ja) * | 1986-04-26 | 1987-11-07 | Fuji Kagaku Kogyo Kk | 芳香族炭化水素の部分核水素化法 |
JPS62294422A (ja) * | 1986-06-13 | 1987-12-21 | Mitsui Toatsu Chem Inc | 改良された除湿剤 |
JPH07106991B2 (ja) * | 1986-07-14 | 1995-11-15 | 旭化成工業株式会社 | 部分水素化方法 |
JPH0825918B2 (ja) * | 1986-08-19 | 1996-03-13 | 旭化成工業株式会社 | シクロオレフインの製造方法 |
JPH0816073B2 (ja) * | 1986-10-02 | 1996-02-21 | 旭化成工業株式会社 | シクロオレフインを製造する方法 |
JPH0825919B2 (ja) * | 1987-03-30 | 1996-03-13 | 旭化成工業株式会社 | シクロオレフインの製造方法 |
JPS63243039A (ja) * | 1987-03-31 | 1988-10-07 | Asahi Chem Ind Co Ltd | シクロオレフインを製造する方法 |
JP2634828B2 (ja) * | 1987-12-16 | 1997-07-30 | 旭化成工業株式会社 | 芳香族化合物の部分核水素化方法 |
JPH088985B2 (ja) * | 1987-12-29 | 1996-01-31 | 三井石油化学工業株式会社 | 水添用触媒 |
JP2814711B2 (ja) * | 1990-07-13 | 1998-10-27 | 三菱化学株式会社 | シクロオレフィンの製造法 |
US5344790A (en) * | 1993-08-31 | 1994-09-06 | Sgs-Thomson Microelectronics, Inc. | Making integrated circuit transistor having drain junction offset |
-
1992
- 1992-02-26 US US07/843,347 patent/US5414171A/en not_active Expired - Fee Related
-
1993
- 1993-02-26 AU AU37363/93A patent/AU3736393A/en not_active Abandoned
- 1993-02-26 EP EP93906270A patent/EP0628020A4/en not_active Withdrawn
- 1993-02-26 WO PCT/US1993/001828 patent/WO1993016972A1/en not_active Application Discontinuation
- 1993-02-26 CN CN93103687A patent/CN1080273A/zh active Pending
- 1993-02-26 JP JP5515112A patent/JPH07504418A/ja active Pending
- 1993-03-08 TW TW082101745A patent/TW222262B/zh active
Patent Citations (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3912787A (en) * | 1972-07-26 | 1975-10-14 | Phillips Petroleum Co | Selective partial hydrogenation of aromatics |
US4056489A (en) * | 1973-12-10 | 1977-11-01 | Engelhard Minerals & Chemicals Corporation | High temperature stable catalyst composition and method for its preparation |
US4162235A (en) * | 1976-06-17 | 1979-07-24 | Johnson, Matthey & Co., Limited | Catalysts |
US4197415A (en) * | 1976-10-08 | 1980-04-08 | Toray Industries, Inc. | Process for preparing cyclic olefins by selective partial hydrogenation of aromatic hydrocarbons |
US4235755A (en) * | 1979-02-21 | 1980-11-25 | Uop Inc. | Hydrocarbon dehydrogenation method and nonacidic multimetallic catalytic composite for use therein |
US4665274A (en) * | 1985-09-11 | 1987-05-12 | Sumitomo Chemical Company, Limited | Method for producing cycloolefins |
US4734536A (en) * | 1985-10-03 | 1988-03-29 | Asahi Kasei Kogyo Kabushiki Kaisha | Process for producing cycloolefins |
US4678861A (en) * | 1985-10-23 | 1987-07-07 | Asahi Kasei Kogyo Kabushiki Kaisha | Process for producing a cycloolefin |
Non-Patent Citations (1)
Title |
---|
See also references of EP0628020A4 * |
Cited By (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5569803A (en) * | 1993-12-24 | 1996-10-29 | Mitsubishi Chemical Corporation | Method for producing a cycloolefin |
EP0691320A1 (de) | 1994-07-08 | 1996-01-10 | Basf Aktiengesellschaft | Verfahren zur kontinuierlichen Herstellung von Cyclohexen durch partielle Hydrierung von Benzol |
US6344593B1 (en) | 1994-07-08 | 2002-02-05 | Basf Aktiengesellschaft | Continuous preparation of cyclohexene by partial hydrogenation of benzene |
WO2012059387A1 (de) | 2010-11-02 | 2012-05-10 | Basf Se | Verfahren zur herstellung eines phenylcyclohexans |
US8653313B2 (en) | 2010-11-02 | 2014-02-18 | Basf Se | Process for preparing a phenylcyclohexane |
Also Published As
Publication number | Publication date |
---|---|
US5414171A (en) | 1995-05-09 |
AU3736393A (en) | 1993-09-13 |
EP0628020A4 (en) | 1995-01-11 |
CN1080273A (zh) | 1994-01-05 |
EP0628020A1 (en) | 1994-12-14 |
JPH07504418A (ja) | 1995-05-18 |
TW222262B (US06380249-20020430-C00008.png) | 1994-04-11 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US5334790A (en) | Process and catalyst for partially hydrogenating aromatics to produce cycloolefins | |
US5414171A (en) | Process and washed catalyst for partially hydrogenating aromatics to produce cycloolefins | |
WO2017011496A2 (en) | Silver promoted catalysts for oxidative coupling of methane | |
WO2019095405A1 (zh) | 一种由合成气直接制取芳烃并联产低碳烯烃的方法 | |
KR101437072B1 (ko) | 효율적인 이산화탄소 전환 촉매 및 이의 제조 방법 | |
CN109776249B (zh) | 一种由合成气与芳烃直接制取对二甲苯的方法 | |
US6288295B1 (en) | Catalyst for use in organic compound transformation reactions | |
WO2017099161A1 (ja) | アルキル芳香族化合物脱水素化触媒とその製造方法、及びそれを用いた脱水素化方法 | |
WO2019095985A1 (zh) | 一种芳烃合成用催化剂及其制备方法 | |
US7550611B2 (en) | Carbon nanochips as catalyst supports for metals and metal oxides | |
JP4597024B2 (ja) | シクロオレフィン製造触媒およびシクロオレフィン製造方法 | |
JP5296549B2 (ja) | アルキル化芳香族化合物の製造方法およびフェノールの製造方法 | |
US4482758A (en) | Process for the orthomethylation of phenolic compounds | |
CN114433220B (zh) | 一种苯和合成气烷基化催化剂的制备方法 | |
US3692840A (en) | Process for producing aldehydes and ketones | |
US5705723A (en) | Hydrogenation catalyst composition and a hydrogenation process | |
EP0211545B1 (en) | Catalytic reduction process for the production of aromatic amino compounds | |
US4507399A (en) | Cadmium-containing catalyst | |
EP1608610B1 (en) | Process for the hydrogenation of alkylaryl ketones | |
US4453025A (en) | Process for the preparation of 3,5-xylenol | |
JP2019005746A (ja) | クメンを製造するための触媒及びその適用 | |
CN114433217B (zh) | 苯和合成气烷基化催化剂及其制备方法和应用 | |
JPWO2009063763A1 (ja) | アルキル化芳香族化合物の製造方法およびフェノールの製造方法 | |
CA1097311A (en) | Hydroalkylation using multi metallic zeolite catalyst | |
JP2925129B2 (ja) | シクロオレフィンの製造方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AK | Designated states |
Kind code of ref document: A1 Designated state(s): AT AU BB BG BR CA CH DE DK ES FI GB HU JP KP KR LK LU MG MN MW NL NO NZ PL PT RO RU SD SE UA |
|
AL | Designated countries for regional patents |
Kind code of ref document: A1 Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR SN TD TG |
|
DFPE | Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101) | ||
WWE | Wipo information: entry into national phase |
Ref document number: 1993906270 Country of ref document: EP |
|
WWP | Wipo information: published in national office |
Ref document number: 1993906270 Country of ref document: EP |
|
REG | Reference to national code |
Ref country code: DE Ref legal event code: 8642 |
|
NENP | Non-entry into the national phase |
Ref country code: CA |
|
WWW | Wipo information: withdrawn in national office |
Ref document number: 1993906270 Country of ref document: EP |