US20210292875A1 - 6xxx aluminum alloys - Google Patents
6xxx aluminum alloys Download PDFInfo
- Publication number
- US20210292875A1 US20210292875A1 US17/336,859 US202117336859A US2021292875A1 US 20210292875 A1 US20210292875 A1 US 20210292875A1 US 202117336859 A US202117336859 A US 202117336859A US 2021292875 A1 US2021292875 A1 US 2021292875A1
- Authority
- US
- United States
- Prior art keywords
- aluminum alloy
- 6xxx aluminum
- new 6xxx
- product
- alloys
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 229910000838 Al alloy Inorganic materials 0.000 title claims abstract description 163
- 229910052749 magnesium Inorganic materials 0.000 claims abstract description 38
- 229910052710 silicon Inorganic materials 0.000 claims abstract description 37
- 229910052802 copper Inorganic materials 0.000 claims abstract description 23
- 229910052742 iron Inorganic materials 0.000 claims abstract description 17
- 229910052719 titanium Inorganic materials 0.000 claims abstract description 16
- 229910052804 chromium Inorganic materials 0.000 claims abstract description 14
- 229910052748 manganese Inorganic materials 0.000 claims abstract description 13
- 239000012535 impurity Substances 0.000 claims abstract description 10
- 229910052726 zirconium Inorganic materials 0.000 claims abstract description 10
- 229910052725 zinc Inorganic materials 0.000 claims abstract description 9
- 229910052720 vanadium Inorganic materials 0.000 claims abstract description 8
- 229910052782 aluminium Inorganic materials 0.000 claims abstract description 6
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims abstract description 6
- 238000005097 cold rolling Methods 0.000 claims description 18
- 238000005098 hot rolling Methods 0.000 claims description 15
- 238000000034 method Methods 0.000 claims description 10
- 238000010438 heat treatment Methods 0.000 claims description 9
- 229910052751 metal Inorganic materials 0.000 claims description 6
- 239000002184 metal Substances 0.000 claims description 6
- 238000010791 quenching Methods 0.000 claims description 5
- 230000000171 quenching effect Effects 0.000 claims description 5
- 238000005266 casting Methods 0.000 claims description 4
- 229910045601 alloy Inorganic materials 0.000 description 72
- 239000000956 alloy Substances 0.000 description 72
- 239000011777 magnesium Substances 0.000 description 37
- 239000010949 copper Substances 0.000 description 20
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 18
- 239000003973 paint Substances 0.000 description 15
- 239000010936 titanium Substances 0.000 description 14
- 230000032683 aging Effects 0.000 description 12
- 239000011651 chromium Substances 0.000 description 11
- 239000011572 manganese Substances 0.000 description 11
- 239000000243 solution Substances 0.000 description 11
- 238000012545 processing Methods 0.000 description 9
- 238000012360 testing method Methods 0.000 description 9
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 description 7
- 229910001369 Brass Inorganic materials 0.000 description 6
- 239000010951 brass Substances 0.000 description 6
- 238000001887 electron backscatter diffraction Methods 0.000 description 6
- 239000000463 material Substances 0.000 description 6
- 239000011701 zinc Substances 0.000 description 6
- 238000009957 hemming Methods 0.000 description 5
- 239000000203 mixture Substances 0.000 description 5
- 238000009749 continuous casting Methods 0.000 description 4
- 238000005259 measurement Methods 0.000 description 4
- 238000005096 rolling process Methods 0.000 description 4
- 230000008901 benefit Effects 0.000 description 3
- 238000002149 energy-dispersive X-ray emission spectroscopy Methods 0.000 description 3
- 239000010703 silicon Substances 0.000 description 3
- 238000005482 strain hardening Methods 0.000 description 3
- XKRFYHLGVUSROY-UHFFFAOYSA-N Argon Chemical compound [Ar] XKRFYHLGVUSROY-UHFFFAOYSA-N 0.000 description 2
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 description 2
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 2
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 2
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 2
- 230000006978 adaptation Effects 0.000 description 2
- 238000004458 analytical method Methods 0.000 description 2
- 238000005452 bending Methods 0.000 description 2
- 238000005260 corrosion Methods 0.000 description 2
- 230000007797 corrosion Effects 0.000 description 2
- 238000007405 data analysis Methods 0.000 description 2
- 238000001514 detection method Methods 0.000 description 2
- 239000007769 metal material Substances 0.000 description 2
- 238000012986 modification Methods 0.000 description 2
- 230000004048 modification Effects 0.000 description 2
- 238000005498 polishing Methods 0.000 description 2
- 238000001953 recrystallisation Methods 0.000 description 2
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 1
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 description 1
- 229910019752 Mg2Si Inorganic materials 0.000 description 1
- 241000612118 Samolus valerandi Species 0.000 description 1
- 238000000137 annealing Methods 0.000 description 1
- 229910052786 argon Inorganic materials 0.000 description 1
- 229910001423 beryllium ion Inorganic materials 0.000 description 1
- 239000011248 coating agent Substances 0.000 description 1
- 238000000576 coating method Methods 0.000 description 1
- 229910052681 coesite Inorganic materials 0.000 description 1
- 239000008119 colloidal silica Substances 0.000 description 1
- 238000001816 cooling Methods 0.000 description 1
- 238000005336 cracking Methods 0.000 description 1
- 229910052906 cristobalite Inorganic materials 0.000 description 1
- 239000002178 crystalline material Substances 0.000 description 1
- 238000013480 data collection Methods 0.000 description 1
- 230000003247 decreasing effect Effects 0.000 description 1
- 230000000593 degrading effect Effects 0.000 description 1
- 230000010339 dilation Effects 0.000 description 1
- 238000010894 electron beam technology Methods 0.000 description 1
- 238000001125 extrusion Methods 0.000 description 1
- 238000000445 field-emission scanning electron microscopy Methods 0.000 description 1
- 238000005242 forging Methods 0.000 description 1
- 238000000227 grinding Methods 0.000 description 1
- 238000004519 manufacturing process Methods 0.000 description 1
- 238000010422 painting Methods 0.000 description 1
- 238000004663 powder metallurgy Methods 0.000 description 1
- 238000002360 preparation method Methods 0.000 description 1
- 238000011002 quantification Methods 0.000 description 1
- 238000007670 refining Methods 0.000 description 1
- VSZWPYCFIRKVQL-UHFFFAOYSA-N selanylidenegallium;selenium Chemical compound [Se].[Se]=[Ga].[Se]=[Ga] VSZWPYCFIRKVQL-UHFFFAOYSA-N 0.000 description 1
- 239000000377 silicon dioxide Substances 0.000 description 1
- 239000006104 solid solution Substances 0.000 description 1
- 238000000992 sputter etching Methods 0.000 description 1
- 229910052682 stishovite Inorganic materials 0.000 description 1
- 238000005728 strengthening Methods 0.000 description 1
- JBQYATWDVHIOAR-UHFFFAOYSA-N tellanylidenegermanium Chemical compound [Te]=[Ge] JBQYATWDVHIOAR-UHFFFAOYSA-N 0.000 description 1
- 229910052905 tridymite Inorganic materials 0.000 description 1
- LEONUFNNVUYDNQ-UHFFFAOYSA-N vanadium atom Chemical compound [V] LEONUFNNVUYDNQ-UHFFFAOYSA-N 0.000 description 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0236—Cold rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0273—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/02—Alloys based on aluminium with silicon as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/02—Alloys based on aluminium with silicon as the next major constituent
- C22C21/04—Modified aluminium-silicon alloys
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
- C22F1/043—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with silicon as the next major constituent
Definitions
- Aluminum alloys are useful in a variety of applications. However, improving one property of an aluminum alloy without degrading another property often proves elusive. For example, it is difficult to increase the strength of an alloy without decreasing its corrosion resistance. Other properties of interest for aluminum alloys include formability and critical fracture strain, to name two.
- the present disclosure relates to new 6xxx aluminum alloys having an improved combination of properties, such as an improved combination of strength, formability, bending, and/or corrosion resistance, among others.
- the new 6xxx aluminum alloys comprise (and in some instances consist essentially of or consist of) from 0.65 to 0.85 wt. % Si, from 0.40 to 0.59 wt. % Mg wherein the ratio of wt. % Mg to wt. % Si is from 0.47:1 to 0.90:1 (Mg:Si), from 0.05 to 0.35 wt. % Fe, from 0.04 to 0.13 wt. % Mn, from 0 to 0.20 wt. % Cu, from 0 to 0.15 wt. % Cr, from 0 to 0.15 wt. % Zr, from 0 to 0.10 wt. % Ti, from 0 to 0.05 wt. % V, from 0 to 0.05 wt. % Zn, the balance being aluminum and impurities.
- the amount of magnesium (Mg) and silicon (Si) in the new 6xxx aluminum alloys may relate to the improved combination of properties (e.g., strength, formability).
- the new 6xxx aluminum alloy includes from 0.40 to 0.59 wt. % Mg.
- a new 6xxx aluminum alloy includes at least 0.425 wt. % Mg.
- a new 6xxx aluminum alloy includes at least 0.45 wt. % Mg.
- a new 6xxx aluminum alloy includes at least 0.475 wt. % Mg.
- a new 6xxx aluminum alloy includes at least 0.50 wt. % Mg.
- a new 6xxx aluminum alloy includes not greater than 0.57 wt. % Mg.
- a new 6xxx aluminum alloy includes from 0.49 to 0.59 wt. % Mg.
- the new 6xxx aluminum alloy includes from 0.65 to 0.85 wt. % Si. In one embodiment, a new 6xxx aluminum alloy includes at least 0.675 wt. % Si. In another embodiment, a new 6xxx aluminum alloy includes at least 0.70 wt. % Si. In one embodiment, a new 6xxx aluminum alloy includes not greater than 0.825 wt. % Si. In another embodiment, a new 6xxx aluminum alloy includes not greater than 0.80 wt. % Si. In one embodiment, a new 6xxx aluminum alloy includes from 0.70 to 0.80 wt. % Si.
- the new 6xxx aluminum alloy includes silicon and magnesium such that the weight ratio of magnesium-to-silicon of from 0.47:1 to 0.90:1, i.e., the ratio of wt. % Mg to wt. % Si is from 0.47:1 to 0.90:1 (Mg:Si).
- the ratio of wt. % Mg to wt. % Si is at least 0.50:1(Mg:Si).
- the ratio of wt. % Mg to wt. % Si is at least 0.52:1(Mg:Si).
- the ratio of wt. % Mg to wt. % Si is at least 0.54:1(Mg:Si).
- the ratio of wt. % Mg to wt. % Si is at least 0.56:1(Mg:Si). In yet another embodiment, the ratio of wt. % Mg to wt. % Si is at least 0.58:1(Mg:Si). In another embodiment, the ratio of wt. % Mg to wt. % Si is at least 0.60:1(Mg:Si). In one embodiment, the ratio of wt. % Mg to wt. % Si is not greater than 0.88:1(Mg:Si). In another embodiment, the ratio of wt. % Mg to wt. % Si is not greater than 0.86:1(Mg:Si).
- the ratio of wt. % Mg to wt. % Si is not greater than 0.84:1(Mg:Si). In another embodiment, the ratio of wt. % Mg to wt. % Si is not greater than 0.82:1(Mg:Si). In one embodiment, the ratio of wt. % Mg to wt. % Si is from 0.61:1 to 0.84:1 (Mg:Si).
- a new 6xxx aluminum alloy includes at least 0.08 wt. % Fe. In another one embodiment, a new 6xxx aluminum alloy includes at least 0.10 wt. % Fe. In yet another embodiment, a new 6xxx aluminum alloy includes at least 0.12 wt. % Fe. In another embodiment, a new 6xxx aluminum alloy includes at least 0.15 wt. %. In one embodiment, a new 6xxx aluminum alloy includes not greater than 0.32 wt. % Fe. In another embodiment, a new 6xxx aluminum alloy includes not greater than 0.30 wt. % Fe. In yet another embodiment, a new 6xxx aluminum alloy includes not greater than 0.28 wt. % Fe. In one embodiment, a new 6xxx aluminum alloy includes from 0.09 to 0.26 wt. % Fe.
- the amount of manganese (Mn) in the new 6xxx aluminum alloys may relate to the improved combination of properties (e.g., formability).
- the new 6xxx aluminum alloy includes from 0.04 to 0.13 wt. % Mn.
- a new 6xxx aluminum alloy includes at least 0.05 wt. % Mn.
- a new 6xxx aluminum alloy includes at least 0.06 wt. % Mn.
- a new 6xxx aluminum alloy includes not greater than 0.12 wt. % Mn.
- a new 6xxx aluminum alloy includes not greater than 0.11 wt. % Mn.
- a new 6xxx aluminum alloy includes not greater than 0.10 wt. % Mn.
- a new 6xxx aluminum alloy includes from 0.06 to 0.10 wt. % Mn.
- the new 6xxx aluminum alloy may optionally include copper (Cu) and in an amount of up to 0.20 wt. % Cu (e.g., for strengthening purposes).
- a new 6xxx aluminum alloy includes at least 0.02 wt. % Cu.
- a new 6xxx aluminum alloy includes at least 0.04 wt. % Cu.
- a new 6xxx aluminum alloy includes at least 0.06 wt. % Cu.
- a new 6xxx aluminum alloy includes at least 0.07 wt. % Cu.
- a new 6xxx aluminum alloy includes at least 0.08 wt. % Cu.
- a new 6xxx aluminum alloy includes at least 0.09 wt.
- a new 6xxx aluminum alloy includes not greater than 0.19 wt. % Cu. In another embodiment, a new 6xxx aluminum alloy includes not greater than 0.18 wt. % Cu. In yet another embodiment, a new 6xxx aluminum alloy includes not greater than 0.17 wt. % Cu. In one embodiment, a new 6xxx aluminum alloy includes from 0.09 to 0.17 wt. % Cu.
- the new 6xxx aluminum alloy may optionally include chromium (Cr) and in an amount of up to 0.15 wt. % Cr (e.g., for grain structure control).
- a new 6xxx aluminum alloy includes at least 0.01 wt. % Cr.
- a new 6xxx aluminum alloy includes at least 0.02 wt. % Cr.
- a new 6xxx aluminum alloy incudes not greater than 0.10 wt. % Cr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.08 wt. % Cr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.06 wt. % Cr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.05 wt. % Cr.
- a new 6xxx aluminum alloy includes from 0.01 to 0.05 wt. % Cr.
- the new 6xxx aluminum alloy may optionally include zirconium (Zr) and in an amount of up to 0.15 wt. % Zr (e.g., for grain structure control).
- Zr zirconium
- a new 6xxx aluminum alloy incudes not greater than 0.10 wt. % Zr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.05 wt. % Zr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.03 wt. % Zr.
- a new a new 6xxx aluminum alloy incudes not greater than 0.01 wt. % Zr.
- the new 6xxx aluminum alloy may include up to 0.15 wt. % Ti. Titanium (Ti) may optionally be present in the new 6xxx aluminum alloy, such as for grain refining purposes.
- a new 6xxx aluminum alloy includes at least 0.005 wt. % Ti.
- a new 6xxx aluminum alloy includes at least 0.010 wt. % Ti.
- a new 6xxx aluminum alloy includes at least 0.0125 wt. % Ti.
- a new 6xxx aluminum alloy includes not greater than 0.10 wt. % Ti.
- a new 6xxx aluminum alloy includes not greater than 0.08 wt. % Ti.
- a new 6xxx aluminum alloy includes not greater than 0.05 wt. % Ti. In one embodiment, a target amount of titanium in a new 6xxx aluminum alloy is 0.03 wt. % Ti. In one embodiment, a new 6xxx aluminum alloy includes from 0.01 to 0.05 wt. % Ti.
- Zinc (Zn) may optionally be present in the new 6xxx aluminum alloy, and in an amount up to 0.10 wt. % Zn.
- a new alloy includes not greater than 0.05 wt. % Zn.
- a new alloy includes not greater than 0.03 wt. % Zn.
- a new alloy includes not greater than 0.01 wt. % Zn.
- Vanadium (V) may optionally be present in the new 6xxx aluminum alloy, and in an amount of up to 0.05 wt. % V.
- a new 6xxx aluminum alloy includes not greater than 0.03 wt. % V.
- a new 6xxx aluminum alloy includes not greater than 0.01 wt. % V.
- a new 6xxx aluminum alloy includes not greater than 0.15 wt. %, in total, of the impurities, and wherein the 6xxx aluminum alloy includes not greater than 0.05 wt. % of each of the impurities.
- a new 6xxx aluminum alloy includes not greater than 0.10 wt. %, in total, of the impurities, and wherein the 6xxx aluminum alloy includes not greater than 0.03 wt. % of each of the impurities.
- the new 6xxx alloys may be useful in a variety of product forms, including ingot or billet, wrought product forms (sheet, plate, forgings and extrusions), shape castings, additively manufactured products, and powder metallurgy products.
- a new 6xxx aluminum alloy is a rolled product.
- the new 6xxx aluminum alloys may be produced in sheet form.
- a sheet made from the new 6xxx aluminum alloy has a thickness of from 1.5 mm to 4.0 mm.
- the new 6xxx aluminum alloys are produced using ingot casting and hot rolling.
- a method includes the steps of casting an ingot of the new 6xxx aluminum alloy, homogenizing the ingot, rolling the ingot into a rolled product having a final gauge (via hot rolling and/or cold rolling), solution heat treating the rolled product, wherein the solution heat treating comprises heating the rolled product to a temperature and for a time such that some or substantially all of Mg 2 Si of the rolled product is dissolved into solid solution, and after the solution heat treating, quenching the rolled product (e.g., water or air quenching). After the quenching, the rolled product may be artificially aged.
- one or more anneal steps may be completed before or after a rolling step (e.g., hot rolling to a first gauge, annealing, cold rolling to the final gauge).
- the artificially aged product can be painted (e.g., for an automobile part), and may thus be subjected to a paint-bake cycle.
- the rolled aluminum alloy products produced from the new alloy may be incorporated in an automobile.
- the new 6xxx aluminum alloys products are cast via continuous casting. Downstream of the continuous casting, the product can be (a) rolled (hot and/or cold), (b) optionally annealed (e.g., after hot rolling and prior to any cold rolling steps), (c) solution heat treated and quenched, (d) optionally cold worked (post-solution heat treatment), and (e) artificially aged, and all steps (a)-(e) may occur in-line or off-line relative to the continuous casting step.
- Some methods for producing the new 6xxx aluminum alloys products using continuous casting and associated downstream steps are described in, for example, U.S. Pat. No. 7,182,825, U.S. Patent Application Publication No. 2014/0000768, and U.S. Patent Application Publication No. 2014/036998, each of which is incorporated herein by reference in its entirety.
- the artificially aged product can be painted (e.g., for an automobile part), and may thus be subjected to a paint-bake cycle.
- the hot rolling comprises hot rolling to an intermediate gauge product, wherein the intermediate gauge product exits the hot rolling apparatus at a temperature of not greater than 290° C.
- an optional anneal may be completed.
- the intermediate gauge product may be cold rolled to final gauge.
- the hot rolling comprises rolling to an intermediate gauge product, wherein the intermediate gauge product exits the hot rolling apparatus at a temperature of from 400-480° C.
- the intermediate gauge product may then be cold rolled to final gauge, i.e., no anneal is required after the hot rolling and prior to cold rolling in this embodiment.
- the cold rolling When cold rolling is completed, the cold rolling generally comprises reducing the thickness of the intermediate gauge thickness to the final gauge thickness. In one embodiment, the cold rolling comprises cold rolling by at least 50%. In another embodiment, the cold rolling comprises cold rolling by at least 60%. In yet another embodiment, the cold rolling comprises cold rolling by at least 65%. In one embodiment, the cold rolling is not greater than 85%.
- XX CR % is the amount of thickness reduction achieved when the aluminum alloy body is reduced from a first thickness of T 1 to a second thickness of T 2 , where T 1 is the intermediate gauge thickness and wherein T 2 is the thickness.
- XX CR % is equal to:
- XX CR % is 80%.
- the peak metal temperature during solution heat treatment is in the range of from 504° C. to 593° C.
- the peak metal temperature is the highest temperature realized by an alloy product during solution heat treatment.
- the new 6xxx aluminum alloy products are processed to a T4 temper as defined by ANSI H35.1 (2009), i.e., the new 6xxx are solution heat treated and then quenched and then naturally aged to a substantially stable condition.
- the natural aging amount is 30 days and the T4 properties of the new 6xxx aluminum alloy are measured at 30 days of natural aging.
- the new 6xxx aluminum alloys are processed to a T6 temper as defined by ANSI H35.1 (2009), i.e., the new 6xxx are solution heat treated and then quenched and then artificially aged.
- the artificial aging comprises paint baking.
- the artificial aging consist of paint baking.
- paint baking comprises heating the new 6xxx aluminum alloy product to 180° C. and then holding for 20 minutes.
- the new 6xxx aluminum alloys are processed to a T8 temper as defined by ANSI H35.1 (2009), i.e., the new 6xxx are solution heat treated and then quenched and then cold worked (e.g., stretched), and then artificially aged.
- the artificial aging comprises paint baking.
- the artificial aging consist of paint baking.
- paint baking comprises heating the new 6xxx aluminum alloy product to 180° C. and then holding for 20 minutes.
- the processing of the new 6xxx aluminum alloy steps may be accomplished such that a new aluminum alloy body product realizes a predominately recrystallized microstructure.
- a predominately recrystallized microstructure means that the aluminum alloy body contains at least 51% recrystallized grains (by volume fraction).
- the degree of recrystallization of a new 6xxx aluminum alloy product may be determined using appropriate metallographic samples of the material analyzed with EBSD by an appropriate SEM and computer software to determine intergranular misorientation.
- a new 6xxx aluminum alloy product is at least 60% recrystallized.
- a new 6xxx aluminum alloy product is at least 70% recrystallized.
- a new 6xxx aluminum alloy product is at least 80% recrystallized.
- a new 6xxx aluminum alloy product is at least 90% recrystallized. In yet another embodiment, a new 6xxx aluminum alloy product is at least 95% recrystallized. In another embodiment, a new 6xxx aluminum alloy product is at least 98% recrystallized, or more.
- a new 6xxx aluminum alloy product may realize a fine grain size.
- a new 6xxx aluminum alloy product realizes an area weighted average grain size of not greater than 45 micrometers.
- a new 6xxx aluminum alloy product realizes an area weighted average grain size of not greater than 40 micrometers.
- a new 6xxx aluminum alloy product realizes an area weighted average grain size of at least 20 micrometers.
- a new 6xxx aluminum alloy product realizes an area weighted average grain size of at least 25 micrometers.
- a new 6xxx aluminum alloy product realizes an area weighted average grain size of at least 30 micrometers.
- a new 6xxx aluminum alloy product may realize a unique texture.
- Texture means a preferred orientation of at least some of the grains of a crystalline structure.
- matchsticks as an analogy, consider a material composed of matchsticks. That material has a random texture if the matchsticks are included within the material in a completely random manner. However, if the heads of at least some of those matchsticks are aligned in that they point the same direction, like a compass pointing north, then the material would have at least some texture due to the aligned matchsticks.
- the same principles apply with grains of a crystalline material.
- Texture components resulting from production of aluminum alloy products may include one or more of copper, S texture, brass, cube, and Goss texture, to name a few. Each of these texture components is defined in Table 1, below.
- grain size and texture are to be measured and normalized as follows:
- the EBSD acquisition is to be performed using EDAX TSL EBSD Data Collection (OIM)TM software, version 7, or equivalent.
- OFM EDAX TSL EBSD Data Collection
- Ai is the area of each individual grain as measured per above.
- “vi” is the calculated individual grain size assuming the grain is a circle.
- the number average grain size, v-bar_n, is the arithmetic mean of vi.
- the new 6xxx aluminum alloys disclosed herein may realize an improved combination of properties.
- a new 6xxx aluminum alloy realizes a T4 tensile yield strength in the LT (long transverse) direction of from 90 to 110 MPa.
- a new 6xxx aluminum alloy realizes a T4 uniform elongation in the LT (long transverse) direction of at least 21%.
- a new 6xxx aluminum alloy realizes a T4 n value (10-20%) in the LT (long transverse) direction of at least 0.245.
- T4 properties are to be measured after 30 days of natural aging.
- tensile yield strength and uniform elongation are to be measured in accordance with ASTM E8 and B557.
- n value (10-20%) is to be measured in accordance with ASTM E646 using 10-20% strain.
- a new 6xxx aluminum alloy realizes a T6 (0% pre-strain/stretch) tensile yield strength of at least 160 MPa when artificially aged by paint baking at 180° C. for 20 minutes.
- a new 6xxx aluminum alloy realizes a T6, (0% pre-strain/stretch) tensile yield strength of at least 170 MPa when artificially aged by paint baking at 180° C. for 20 minutes.
- a new 6xxx aluminum alloy realizes a T6 (0% pre-strain/stretch) tensile yield strength of at least 180 MPa when artificially aged by paint baking at 180° C. for 20 minutes.
- a new 6xxx aluminum alloy realizes a T8 tensile yield strength of at least 215 MPa when post-SHT stretched 1-3% and then artificially aged by paint baking at 180° C. for 20 minutes.
- a new 6xxx aluminum alloy realizes a Hem rating of 2 or better. Hem rating is defined in the below Examples. In another embodiment, a new 6xxx aluminum alloy realizes a Hem rating of 1.
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 125°.
- VDA testing is to be tested by natural aging the product for 30 days, and then stretching the product 10% in the L (longitudinal) direction, and then conducting the VDA bend test in accordance with the VDA 238-100 bend test specification. (https://www.vda.de/en/services/Publications/vda-238-100-plate-bending-test-for-metallic-materials.html).
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 130°.
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 135°.
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 140°.
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 143°.
- a new 6xxx aluminum alloy is absent of Ludering.
- Ludering is to be tested by naturally aging the product for 8 days, and then stretching the product 10% in the L (longitudinal) direction. If Luder lines are visible to the naked eye, the product is not absent of Ludering. If Luder lines are invisible to the naked eye, the product is absent of Ludering.
- a new 6xxx aluminum alloy realizes a combination of properties shown in the “Preferred Property Box” of FIG. 1 .
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 140°. Others of the above-identified properties may also be realized.
- a new 6xxx aluminum alloy realizes a combination of properties shown in the “Preferred Property Box” of FIG. 2 .
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 140°. Others of the above-identified properties may also be realized.
- a new 6xxx aluminum alloy realizes a combination of properties shown in the “Preferred Property Box” of FIG. 3 .
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 140°. Others of the above-identified properties may also be realized.
- a new 6xxx aluminum alloy realizes a combination of properties shown in the “Preferred Property Box” of FIG. 4 .
- a new 6xxx aluminum alloy realizes a VDA bend angle of at least 140°. Others of the above-identified properties may also be realized.
- the term “or” is an inclusive “or” operator, and is equivalent to the term “and/or,” unless the context clearly dictates otherwise.
- the term “based on” is not exclusive and allows for being based on additional factors not described, unless the context clearly dictates otherwise.
- the meaning of “a,” “an,” and “the” include plural references, unless the context clearly dictates otherwise.
- the meaning of “in” includes “in” and “on”, unless the context clearly dictates otherwise.
- FIG. 1 is an image of the grain structure of alloy A1-1.
- FIG. 2 is an image of the grain structure of alloy A1-10.
- FIG. 3 is an image of the grain structure of alloy A1-19.
- FIG. 4 is an image of the grain structure of alloy A1-22.
- FIG. 5 is a graph illustrating the tensile yield strength (after paint bake, no pre-strain, i.e., T6) versus n value (10-20%) in the as is (T4) temper for various example alloys.
- FIG. 6 is a graph illustrating the tensile yield strength (after paint bake, no pre-strain, i.e., T6) versus uniform elongation in the as is (T4) temper for various example alloys.
- FIG. 7 is a graph illustrating the tensile yield strength (after paint bake, 2% pre-strain, i.e., T8) versus n value (10-20%) in the as is (T4) temper for various example alloys.
- FIG. 8 is a graph illustrating the tensile yield strength (after paint bake, 2% pre-strain, i.e., T8) versus uniform elongation in the as is (T4) temper for various example alloys.
- Example 1 Compositions of Example 1 Alloys (wt. %) Sample Si Fe Cu Mn Mg Cr Ti Zn Bal. Alloy 0.74 0.18 0.13 0.07 0.52 0.03 0.03 0.005 A1 + A1 Imp. (inv.) Alloy 0.76 0.14 0.13 0.07 0.54 0.03 0.03 0.007 A1 + A2 Imp. (inv.) Alloy 0.63 0.21 0.13 0.07 0.60 0.03 0.02 0.004 A1 + B1 Imp. (non- inv.)
- the ingots were then homogenized and then hot rolled to an intermediate gauge with an exit temperature of not greater than 290° C.
- the alloys were then cold rolled to a final gauge of 0.95 or 1.2 mm.
- the cold rolling amounts (reduction from the intermediate gauge to the final gauge) are provided in Table 2, below.
- the final gauge products were then solution heat treated by heating to various peak metal temperatures (shown in Table 2), after which the alloys were immediately air quenched. After quenching, some alloys were then stretched while others were not, as shown in Table 2. All alloys were then naturally aged for 30 days, after which some alloys were then stretched, and after which some alloys (both stretched and non-stretched) were artificially aged by heating to 180° C. and then holding at this temperature for 20 minutes, and then cooling to room temperature. The 2% stretching (pre-strain) was completed in the lab and simulates a typical forming operation.
- the invention alloys achieved higher tensile yield strengths (TYS) and ultimate yield strengths (UTS) than non-invention alloys. Further, the invention alloys showed less strength loss at lower peak metal temperatures. The invention alloys also generally had higher elongation and higher n values over non-invention alloys at most processing conditions, indicating improved formability.
- Example 1 alloys were tested for hemming performance by stretching them 15% in the L direction after which a flat hem test was performed. The stretching was completed on alloys that had been naturally aged for 30 days and without subsequent artificial aging, i.e., the alloys were in a T4 temper prior to the 15% stretching. Four hems were completed for each processing condition. The hem ratings were then evaluated per the below scale.
- Table 4 shows the achieved hem ratings for A1 and A2 alloys.
- A1 alloys have more iron than A2 alloys. Those in industry have associated higher iron content to poorer hemming performance. However, the A1 alloys demonstrated better hemming performance than the A2 alloys. Further, higher iron content improved hemming performance in samples with lower levels of cold working (e.g. alloys A1-22, A1-23 and A1-24 had 65% cold work and demonstrated the same hemming performance as alloys A1-10, A1-11 and A1-12, which were the same gauge but only 81% cold work).
- Example 1 alloys were naturally aged 8 days and then stretched 10% in the LT direction, after which a coating of paint was applied. After painting, the alloys were examined to determine if Luder bands were present. Table 6, below, shows the tensile yield strength and Luder band results for select Example 2 alloys.
- Grain size and texture measurements of select A1 samples from Example 2 were obtained via electron backscattering detection in a scanning electron microscope. The results of the grain size and texture measurements are shown in Table 7, below. Further, grain structure images obtained via SEM are shown in FIGS. 1-4 .
- FIGS. 1-4 show the grain structure images obtained via SEM for alloys A1-1, A1-10, A1-19, and A1-22.
- the weighted average grain sizes obtained from these images for alloys A1-1, A1-10, A1-19, and A1-22 were 32 ⁇ m, 32 ⁇ m, 34 ⁇ m, and 41 ⁇ m, respectively.
- the A1 alloy have finer (smaller) grain structure.
- alloy A1-1 had a coarser grain structure than alloy B1-1.
- the new alloys disclosed herein may have grain size area weighted average of from 20 micrometers to 45 micrometers. In one embodiment, the new alloys have a grain size of from 30 to 40 micrometers.
- the new alloys disclosed herein may be in sheet form and have the following texture characteristics:
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Continuous Casting (AREA)
- Conductive Materials (AREA)
- Laminated Bodies (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US17/336,859 US20210292875A1 (en) | 2018-12-05 | 2021-06-02 | 6xxx aluminum alloys |
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US201862775746P | 2018-12-05 | 2018-12-05 | |
PCT/US2019/064148 WO2020117748A1 (en) | 2018-12-05 | 2019-12-03 | 6xxx aluminum alloys |
US17/336,859 US20210292875A1 (en) | 2018-12-05 | 2021-06-02 | 6xxx aluminum alloys |
Related Parent Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2019/064148 Continuation WO2020117748A1 (en) | 2018-12-05 | 2019-12-03 | 6xxx aluminum alloys |
Publications (1)
Publication Number | Publication Date |
---|---|
US20210292875A1 true US20210292875A1 (en) | 2021-09-23 |
Family
ID=70974866
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US17/336,859 Pending US20210292875A1 (en) | 2018-12-05 | 2021-06-02 | 6xxx aluminum alloys |
Country Status (8)
Country | Link |
---|---|
US (1) | US20210292875A1 (de) |
EP (1) | EP3891315A4 (de) |
JP (1) | JP2022513692A (de) |
KR (1) | KR20210088670A (de) |
CN (1) | CN113166857B (de) |
CA (1) | CA3121042A1 (de) |
MX (1) | MX2021006476A (de) |
WO (1) | WO2020117748A1 (de) |
Families Citing this family (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN111850350A (zh) * | 2020-06-16 | 2020-10-30 | 福建省南平铝业股份有限公司 | 新能源汽车熔断器用铝合金材料及其制备方法 |
CN113073239A (zh) * | 2021-03-24 | 2021-07-06 | 瑞旭实业有限公司 | 一种太阳能光伏边框支架铝合金材料及制造方法 |
Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20190153577A1 (en) * | 2016-07-14 | 2019-05-23 | Constellium Neuf-Brisach | Method of making 6xxx aluminium sheets |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS59685B2 (ja) | 1974-11-13 | 1984-01-07 | トヨタ自動車株式会社 | ナイネンキカンノ ノウコンゴウキキヨウキユウソウチ |
JP3590685B2 (ja) * | 1994-12-27 | 2004-11-17 | 本田技研工業株式会社 | 自動車外板用アルミニウム合金板の製造方法 |
JP2004027253A (ja) | 2002-06-21 | 2004-01-29 | Furukawa Sky Kk | 成形加工用アルミニウム合金板およびその製造方法 |
US6811625B2 (en) * | 2002-10-17 | 2004-11-02 | General Motors Corporation | Method for processing of continuously cast aluminum sheet |
US7182825B2 (en) | 2004-02-19 | 2007-02-27 | Alcoa Inc. | In-line method of making heat-treated and annealed aluminum alloy sheet |
FR2902442B1 (fr) * | 2006-06-16 | 2010-09-03 | Aleris Aluminum Koblenz Gmbh | Alliage de la serie aa6xxx, a grande tolerance aux dommages pour l'industrie aerospatiale |
JP5059423B2 (ja) * | 2007-01-18 | 2012-10-24 | 株式会社神戸製鋼所 | アルミニウム合金板 |
JP2009041045A (ja) * | 2007-08-06 | 2009-02-26 | Nippon Steel Corp | 塗装焼付け硬化性に優れたアルミニウム合金板及びその製造方法 |
CN100554486C (zh) * | 2007-11-16 | 2009-10-28 | 苏州有色金属研究院有限公司 | 改善低Cu含量铝合金汽车板材烘烤硬化性能的方法 |
JP5758676B2 (ja) * | 2011-03-31 | 2015-08-05 | 株式会社神戸製鋼所 | 成形加工用アルミニウム合金板およびその製造方法 |
US9856552B2 (en) | 2012-06-15 | 2018-01-02 | Arconic Inc. | Aluminum alloys and methods for producing the same |
JP5949315B2 (ja) | 2012-08-20 | 2016-07-06 | Jfeスチール株式会社 | 連続鋳造鋳片の製造方法 |
EP2964800B2 (de) * | 2013-03-07 | 2022-06-15 | Aleris Aluminum Duffel BVBA | Verfahren zur herstellung eines walzblechprodukts mit al-mg-si-legierung mit ausgezeichneter formbarkeit |
JP6752146B2 (ja) * | 2014-01-21 | 2020-09-09 | アーコニック テクノロジーズ エルエルシーArconic Technologies Llc | 6000系アルミニウム合金 |
EP2993244B1 (de) * | 2014-09-05 | 2020-05-27 | Constellium Valais SA (AG, Ltd) | Herstellungsverfahren eines Strangpressprofils aus 6xxx Aluminiumlegierung mit ausgezeichneter Crashverhalten |
JP6785772B2 (ja) * | 2015-01-12 | 2020-11-18 | ノベリス・インコーポレイテッドNovelis Inc. | 表面ローピングが低減されたまたは全くない高度に成形可能な自動車用アルミニウムシート及びその製造方法 |
JP6506678B2 (ja) | 2015-11-02 | 2019-04-24 | 株式会社神戸製鋼所 | 自動車構造部材用アルミニウム合金板およびその製造方法 |
US10538834B2 (en) * | 2015-12-18 | 2020-01-21 | Novelis Inc. | High-strength 6XXX aluminum alloys and methods of making the same |
CN105441740A (zh) * | 2016-01-12 | 2016-03-30 | 苏州有色金属研究院有限公司 | 汽车车身用高卷边性能6xxx系合金板材及其制造方法 |
JP2017179468A (ja) * | 2016-03-30 | 2017-10-05 | 株式会社神戸製鋼所 | 高成形性アルミニウム合金板 |
-
2019
- 2019-12-03 JP JP2021531352A patent/JP2022513692A/ja active Pending
- 2019-12-03 CN CN201980080272.8A patent/CN113166857B/zh active Active
- 2019-12-03 MX MX2021006476A patent/MX2021006476A/es unknown
- 2019-12-03 WO PCT/US2019/064148 patent/WO2020117748A1/en unknown
- 2019-12-03 CA CA3121042A patent/CA3121042A1/en active Pending
- 2019-12-03 EP EP19892594.3A patent/EP3891315A4/de active Pending
- 2019-12-03 KR KR1020217017549A patent/KR20210088670A/ko unknown
-
2021
- 2021-06-02 US US17/336,859 patent/US20210292875A1/en active Pending
Patent Citations (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20190153577A1 (en) * | 2016-07-14 | 2019-05-23 | Constellium Neuf-Brisach | Method of making 6xxx aluminium sheets |
Also Published As
Publication number | Publication date |
---|---|
CA3121042A1 (en) | 2020-06-11 |
EP3891315A4 (de) | 2022-10-26 |
WO2020117748A1 (en) | 2020-06-11 |
CN113166857B (zh) | 2022-12-27 |
MX2021006476A (es) | 2021-07-16 |
JP2022513692A (ja) | 2022-02-09 |
CN113166857A (zh) | 2021-07-23 |
KR20210088670A (ko) | 2021-07-14 |
EP3891315A1 (de) | 2021-10-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP3950987B1 (de) | Hochformbares aluminiumblech für die automobilindustrie mit verringertem oder keinem oberflächen-roping und verfahren zur herstellung | |
JP4285916B2 (ja) | 高強度、高耐食性構造用アルミニウム合金板の製造方法 | |
CA2908196C (en) | High strength, high formability, and low cost aluminum-lithium alloys | |
JP6771456B2 (ja) | アルミニウム合金製品及び調製方法 | |
US20210292875A1 (en) | 6xxx aluminum alloys | |
US9222161B2 (en) | Magnesium alloy sheet and method for producing same | |
ES2220902T5 (es) | Elemento de estructura de avión de aleación Al.Cu.Mg | |
US20170283913A1 (en) | Aluminum alloy sheet having high formability | |
Tan | Influence of Heat Treatment on the Mechanical Properties of AA6066 Alloy. | |
EP3395458A1 (de) | Blech aus magnesiumlegierung und verfahren zur herstellung davon | |
CN114450425A (zh) | 铝合金精密板 | |
US20020014290A1 (en) | Al-si-mg aluminum alloy aircraft structural component production method | |
US20190169727A1 (en) | Low Cost, Substantially Zr-Free Aluminum-Lithium Alloy for Thin Sheet Product with High Formability | |
JP7116394B2 (ja) | マグネシウム合金及びマグネシウム合金の製造方法 | |
JP2017210673A (ja) | r値の異方性が小さいプレス成形用アルミニウム合金板およびその製造方法 | |
JP2003171726A (ja) | 曲げ加工性および耐食性に優れたアルミニウム合金板およびその製造方法 | |
US20170349978A1 (en) | Aluminum alloy sheet | |
KR20230090332A (ko) | 개선된 7xxx 알루미늄 합금 | |
EP3643802A1 (de) | Blech aus einer magnesiumlegierung und herstellungsverfahren dafür | |
JP6526404B2 (ja) | アルミニウム合金ブレージングシート | |
JP2019099868A (ja) | ろう付用アルミニウム合金板材及びその製造方法 | |
KR20230137348A (ko) | 신규 6xxx 알루미늄 합금 | |
CN117769606A (zh) | 新型6xxx铝合金 | |
CA3099351A1 (en) | Thin sheets made of aluminium-copper-lithium alloy for aircraft fuselage manufacture | |
Iwamura et al. | Effects of natural aging and cold work on the strength of 2013 aluminum alloy |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: ARCONIC TECHNOLOGIES LLC, PENNSYLVANIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNOR:ARCONIC INC.;REEL/FRAME:056417/0525 Effective date: 20200310 Owner name: ARCONIC INC., PENNSYLVANIA Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HOSCH, TIMOTHY A.;MOOY, DIRK C.;BELL, CYRIL F.;SIGNING DATES FROM 20181207 TO 20181214;REEL/FRAME:056416/0435 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |
|
AS | Assignment |
Owner name: JPMORGAN CHASE BANK, N.A., NEW YORK Free format text: NOTICE OF GRANT OF SECURITY INTEREST (ABL) IN INTELLECTUAL PROPERTY;ASSIGNOR:ARCONIC TECHNOLOGIES LLC;REEL/FRAME:064641/0798 Effective date: 20230818 Owner name: U.S. BANK TRUST COMPANY, NATIONAL ASSOCIATION, NEW YORK Free format text: NOTICE OF GRANT OF SECURITY INTEREST IN INTELLECTUAL PROPERTY (FIRST LIEN);ASSIGNOR:ARCONIC TECHNOLOGIES LLC;REEL/FRAME:064641/0781 Effective date: 20230818 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: NON FINAL ACTION MAILED |