Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F136/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F136/02—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F136/04—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
  • C08F136/06—Butadiene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F136/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F136/02—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F136/04—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B60—VEHICLES IN GENERAL
  • B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
  • B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/04—Monomers containing three or four carbon atoms
  • C08F210/08—Butenes
  • C08F210/10—Isobutene
  • C08F210/12—Isobutene with conjugated diolefins, e.g. butyl rubber
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F36/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F36/02—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F36/04—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/06—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen
  • C08F4/08—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen of alkali metals
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/06—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen
  • C08F4/08—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen of alkali metals
  • C08F4/086—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen of alkali metals an alkali metal bound to nitrogen, e.g. LiN(C2H5)2
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/06—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen
  • C08F4/16—Metallic compounds other than hydrides and other than metallo-organic compounds; Boron halide or aluminium halide complexes with organic compounds containing oxygen of silicon, germanium, tin, lead, titanium, zirconium or hafnium
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/54—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with other compounds thereof
  • C08F4/545—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with other compounds thereof rare earths being present, e.g. triethylaluminium + neodymium octanoate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/607—Catalysts containing a specific non-metal or metal-free compound
  • C08F4/609—Catalysts containing a specific non-metal or metal-free compound organic
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/607—Catalysts containing a specific non-metal or metal-free compound
  • C08F4/609—Catalysts containing a specific non-metal or metal-free compound organic
  • C08F4/6093—Catalysts containing a specific non-metal or metal-free compound organic containing halogen
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/30—Introducing nitrogen atoms or nitrogen-containing groups
  • C08F8/32—Introducing nitrogen atoms or nitrogen-containing groups by reaction with amines
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/42—Introducing metal atoms or metal-containing groups
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/0091—Complexes with metal-heteroatom-bonds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/56—Organo-metallic compounds, i.e. organic compounds containing a metal-to-carbon bond
  • C08K5/57—Organo-tin compounds
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L9/00—Compositions of homopolymers or copolymers of conjugated diene hydrocarbons
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2410/00—Features related to the catalyst preparation, the catalyst use or to the deactivation of the catalyst
  • C08F2410/01—Additive used together with the catalyst, excluding compounds containing Al or B
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2380/00—Tyres

Definitions

• the present invention relates to a catalyst composition for preparing a conjugated diene-based polymer and a conjugated diene-based polymer prepared using the same.
• conjugated diene-based polymer which is a synthetic rubber, specifically, a butadiene-based polymer is increasing as an alternative material to natural rubber of which the produced amount is insufficient.
• linearity and the degree of branching greatly affect the physical properties of the polymer.
• the dissolution rate and viscosity properties of the polymer increase, and as a result, the processability of the polymer is improved.
• the degree of branching of the polymer is excessively large, molecular weight distribution is broadened, and the mechanical properties of the polymer, which influence the abrasion resistance, cracking resistance or repellency of a rubber composition may rather be deteriorated.
• the linearity and the degree of branching of the conjugated diene-based polymer are highly dependent on the amount of cis-1,4 bonds contained in the polymer. If the amount of cis-1,4 bonds contained in the conjugated diene-based polymer increases, the linearity may increase. As a result, the polymer has good mechanical properties, thereby increasing the abrasion resistance, cracking resistance and repellency of a rubber composition.
• a method of preparing a butadiene-based polymer using a compound of a rare earth metal such as neodymium and an alkylating agent in group I to group III, particularly, a polymerization catalyst of a composite metal composed of methyl aluminoxane has been developed.
• a polymer obtainable by the method has an insufficiently high amount of cis-1,4 bonds, and an insufficiently small amount of vinyl, such that the improving effect of physical properties is still insufficient.
• a method of preparing a butadiene-based polymer having a high amount of cis-1,4 bonds using a polymerization catalyst including a rare earth metal compound, an alkylating agent in group I to group III, and an ionic compound composed of non-coordinating anions and cations has been developed.
• Nd(OCOCCl 3 ) 3 is used as the rare earth metal compound, but the polymerization activity of the metal compound is low, and the amount of vinyl bonds of the butadiene polymer is large, such that a rubber composition including the butadiene-based polymer prepared by the method attained an insufficient improvement of physical properties when compared to a rubber composition including the conventional butadiene-based polymer.
• the butadiene-based polymer prepared by the method has a large amount of vinyl bonds and wide molecular weight distribution.
• a method of preparing a butadiene-based polymer having a large amount of cis-1,4 bonds using a polymerization catalyst composed of a rare earth metal salt composed of a halogen atom-containing component and aluminoxane has been developed.
• a specific catalyst such as neodymium bis(trichloroacetate) (versatic acid), etc. is used, such that the polymerization activity of a neodymium salt is low, and industrial applicability is low.
• a first task for solving of the present invention is to provide a catalyst composition has excellent catalytic activity, useful in the preparation of a conjugated diene-based polymer having high linearity and narrow molecular weight distribution.
• a second task for solving of the present invention is to provide a conjugated diene-based polymer prepared using the catalyst composition, and a method for preparing the same.
• a third task for solving of the present invention is to provide a rubber composition including the conjugated diene-based polymer prepared by using the catalyst composition, and a tire part manufactured from the rubber composition.
• a catalyst composition for preparing a conjugated diene-based polymer including a functionalizing agent of the following Formula 1, a rare earth metal compound, an alkylating agent, and a halogen compound, wherein the functionalizing agent is included in 1 equivalent to 20 equivalents based on 1 equivalent of the rare earth metal compound:
• a is an integer of 1 to 3
• X 1 and X 2 are each independently selected from the group consisting of a hydrogen atom, monovalent C 1-20 hydrocarbon, —OR, and a covalent bonding functional group, where at least one of X 1 , and X 2 includes the covalent bonding functional group, where R is selected from the group consisting of a hydrogen atom, C 1-20 alkyl, C 3-20 cycloalkyl, C 6-20 aryl, C 7-20 alkylaryl, C 7-20 arylalkyl, and a covalent bonding functional group, and
• the covalent bonding functional group is a functional group containing a carbon-carbon double bond.
• a conjugated diene-based polymer prepared by using the catalyst composition and having a mooney viscosity of 10 MU to 90 MU at 100° C. and a polydispersity of 3.4 or less.
• a method for preparing a conjugated diene-based polymer including performing a polymerization reaction of conjugated diene-based monomers using the catalyst composition.
• a rubber composition including the conjugated diene-based polymer, and a tire part manufactured by using the rubber composition.
• the catalyst composition for preparing a conjugated diene-based polymer according to the present invention includes a functionalizing agent which is capable of providing a functional group which may make a covalent bond during preparing a conjugated diene-based polymer, high catalytic activity and polymerization reactivity are shown, and a conjugated diene-based polymer having high linearity and excellent processability and physical properties may be prepared when preparing a conjugated diene-based polymer using the catalyst composition.
• preforming means pre-polymerization in a catalyst composition for preparing a conjugated diene-based polymer.
• a catalyst composition for preparing a conjugated diene-based polymer including a rare earth metal compound, an alkylating agent including an aluminum compound, and a halogen compound includes diisobutyl aluminum hydride (hereinafter, DIBAH) as the aluminum compound, a small amount of a monomer such as butadiene is included together to decrease the production possibility of diverse catalytically active species.
• DIBAH diisobutyl aluminum hydride
• the pre-polymerization of butadiene in the catalyst composition for preparing a conjugated diene-based polymer is performed prior to the polymerization reaction for preparing a conjugated diene-based polymer, and this process is referred to as preforming.
• premixing means a homogenously mixed state of each of constituting components without being polymerized in a catalyst composition.
• catalyst composition used in the present disclosure mean a simple mixture of constituting components, diverse composites caused by physical or chemical attraction, or a chemical reaction product of constituting components.
• a functionalizing agent including a covalent bonding functional group such as an allyl group in a molecule is used during preparing a catalyst composition for forming a conjugated diene-based polymer, and the structural stability of a catalytically active species may be improved, the catalytic activity and reactivity of the catalyst composition may be increased, and a conjugated diene-based polymer having high linearity and excellent processability and physical properties may be prepared.
• the catalyst composition for conjugated diene polymerization includes (a) a functionalizing agent, (b) a rare earth metal compound, (c) an alkylating agent, and (d) a halogen compound.
• a functionalizing agent for conjugated diene polymerization
• a rare earth metal compound for conjugated diene polymerization
• a rare earth metal compound for conjugated diene polymerization
• an alkylating agent for conjugated diene polymerization according to an embodiment of the present invention.
• the functionalizing agent in the catalyst composition for conjugated diene polymerization is a silane (Si)-based compound including at least one covalent bonding functional group containing a carbon-carbon double bond.
• the covalent bonding functional group is a functional group containing a carbon-carbon double bond such as vinyl, allyl, methallyl, and (meth)acryl, and may improve catalytic activity by the reaction with a neodymium compound which is activated by an alkylating agent in the catalyst composition, thereby stabilizing a catalytically active species and increasing the reactivity thereof.
• the functionalizing agent includes Si as a central element, the activity of a catalyst composition may be further increased, and as a result, a conjugated diene-based polymer having narrow molecular weight distribution may be prepared during preparing a conjugated diene-based polymer.
• the functionalzing agent may be a compound of the following Formula 1:
• a is an integer of 1 to 3
• X 1 and X 2 are each independently selected from the group consisting of a hydrogen atom, monovalent C 1-20 hydrocarbon, —OR, and a covalent bonding functional group, where at least one of X 1 , and X 2 includes the covalent bonding functional group, where R is selected from the group consisting of a hydrogen atom, C 1-20 alkyl, C 3-20 cycloalkyl, C 6-20 aryl, C 7-20 alkylaryl, C 7-20 arylalkyl, and a covalent bonding functional group, and
• the covalent bonding functional group is a functional group containing a carbon-carbon double bond.
• a relation of a >1 a relation of a >1 is satisfied, a plurality of X 1 may be the same or different. Also, if a relation of 4-a>1 is satisfied in Formula 1, a plurality of X 2 may be the same or different.
• X 1 and X 2 may be each independently selected from the group consisting of a hydrogen atom, monovalent C 1-20 hydrocarbon, —OR (in this case, R is selected from the group consisting of a hydrogen atom, C 1-20 alkyl, C 3-20 cycloalkyl, C 6-20 aryl, C 7-20 alkylaryl, C 7-20 arylalkyl, and a covalent bonding functional group), and a covalent bonding functional group.
• the monovalent hydrocarbon group may be particularly, linear or branched C 1-20 alkyl such as methyl, ethyl and propyl; C 3-20 cycloalkyl such as cyclopropyl, cyclobutyl, and cyclopentyl; C 6-20 aryl such as phenyl; and C 7-20 arylalkyl or C 7-20 alkylaryl as the combination thereof.
• the covalent bonding functional group may be alkenyl or (meth)acryl, and in this case, the alkenyl may be particularly, C 2-20 alkenyl, more particularly, C 2-12 alkenyl, and further more particularly, C 2-6 alkenyl. More particularly, the covalent bonding functional group may be selected from the group consisting of vinyl, allyl, methallyl, butenyl, pentenyl, hexenyl and (meth)acryl, and the covalent bonding functional group may be allyl in consideration of remarkable improving effect of catalytic activity and polymerization reactivity when applied to a catalyst composition. Meanwhile, in the present invention, (meth)acryl means the inclusion of acryl and methacryl.
• X 1 and X 2 may be each independently substituted with at least one substituent selected from the group consisting of linear or branched C 1-20 alkyl, C 3-20 cycloalkyl, and C 6-30 aryl.
• X 1 and X 2 may be each independently selected from the group consisting of a hydrogen atom, alkyl, alkoxy, vinyl, allyl, methallyl, and (meth)acryl, and wherein the alkyl may be linear or branched C 1-20 alkyl, more particularly, linear or branched C 1-6 alkyl, and the alkoxy may be linear or branched C 1-20 alkoxy, more particularly, linear or branched C 1-6 alkoxy.
• at least one of X 1 and X 2 is a covalent bonding functional group containing a double bond in a molecule such as vinyl, allyl, methallyl, and (meth)acryl.
• the functionalizing agent may be selected from the group consisting of the compounds of the following Formulae 2a to 2k:
• Me means methyl
• nBu means n-butyl
• Ph means phenyl
• OEt means ethoxy
• the functionalizing agent may be Formula 1, in which X 1 and X 2 may be each independently selected from the group consisting of linear or branched C 1-6 alkyl, vinyl, allyl, and methallyl, where at least one of X 1 and X 2 may be vinyl, allyl, or methallyl.
• the functionalizing agent of Formula 1 may be used by using a common synthesis reaction.
• the functionalizing agent of Formula 1 may be prepared by the reaction as in the following Reaction 1.
• the following Reaction 1 is only an embodiment for explaining the present invention, and the present invention is not limited thereto.
• the rare earth metal compound is activated by an alkylating agent and then reaction with a reactive group of the functionalizing agent is performed to form a catalytically active species for the polymerization of a conjugated diene.
• the rare earth metal compound any one used for the preparation of a common conjugated diene-based polymer may be used, without specific limitation.
• the rare earth metal compound may be a compound including one or at least two of rare earth metals of atomic numbers of 57 to 71 such as lanthanum, neodymium, cerium, gadolinium and praseodymium, and more particularly, a compound including one or at least two selected from the group consisting of neodymium, lanthanum and gadolinium may be used.
• the rare earth metal compound may be rare earth metal-containing carboxylates (for example, neodymium acetate, neodymium acrylate, neodymium methacrylate, neodymium acetate, neodymium gluconate, neodymium citrate, neodymium fumarate, neodymium lactate, neodymium maleate, neodymium oxalate, neodymium 2-ethylhexanoate, neodymium neodecanoate, etc.), organic phosphates (for example, neodymium dibutyl phosphate, neodymium dipentyl phosphate, neodymium dihexyl phosphate, neodymium diheptyl phosphate, neodymium dioctyl phosphate, neodymium bis(1-methyl h
• the rare earth metal compound may be a neodymium compound of the following Formula 3:
• R 1 to R 3 are each independently a hydrogen atom, or a linear or branched C 1-12 alkyl group.
• the neodymium compound of Formula 3 includes a carboxylate ligand containing an alkyl group having various lengths of at least two carbons at an a position as a substituent
• sterical change may be induced around a neodymium central metal to block the tangle between compounds, and as a result, oligomerization is restrained, and a conversion ratio into an active species is high.
• Such a neodymium compound has a high solubility in a polymerization solvent.
• the rare earth metal compound may be a neodymium compound of Formula 3, in which R 1 is a linear or branched C 6-12 alkyl group, and R 2 and R 3 are each independently a hydrogen atom, or a linear or branched C 2-6 alkyl group, where R 2 and R 3 are not hydrogen atoms at the same time.
• R 8 may be linear or branched C 6-8 alkyl, and R 2 and R 3 may be each independently linear or branched C 2-6 alkyl.
• R 1 is an alkyl group of 6 or more carbon atoms
• R 2 and R 3 are alkyl groups of 2 or more carbon atoms
• the deterioration of conversion efficiency to catalytically active species may be further improved without fear of oligomerization during a polymerization process, and excellent catalytic activity may be shown.
• the neodymium compound may be at least one selected from the group consisting of Nd(2,2-diethyl decanoate) 3 , Nd(2,2-dipropyl decanoate) 3 , Nd(2,2-dibutyl decanoate) 3 , Nd(2,2-dihexyl decanoate) 3 , Nd(2,2-dioctyl decanoate) 3 , Nd(2-ethyl-2-propyl decanoate) 3 , Nd(2-ethyl-2-butyl decanoate) 3 , Nd(2-ethyl-2-hexyl decanoate) 3 , Nd(2-propyl-2-butyl decanoate) 3 , Nd(2-propyl-2-butyl decanoate) 3 , Nd(2-propyl-2-hexyl decanoate) 3 , Nd(2-propyl-2-butyl decanoate)
• the neodymium compound may be at least one selected from the group consisting of Nd(2,2-diethyl decanoate) 3 , Nd(2,2-dipropyl decanoate) 3 , Nd(2,2-dibutyl decanoate) 3 , Nd(2,2-dihexyl decanoate) 3 , and Nd(2,2-dioctyl decanoate) 3 , or a mixture of at least two thereof.
• the neodymium compound may have a solubility of about 4 g or more per 6 g a non-polar solvent at room temperature (23 ⁇ 5° C.).
• the solubility of the neodymium compound means the degree of clear dissolution without generating turbid phenomenon. Through such a high solubility, excellent catalytic activity may be attained.
• the alkylating agent is an organometallic compound which is capable of delivering a hydrocarbyl group to another metal and plays the role of a co-catalyst.
• Any alkylating agents used for the preparation of a common diene-based polymer may be used as the alkylating agent, without specific limitation.
• the alkylating agent is soluble in a non-polar solvent, particularly, a non-polar hydrocarbon-based solvent, and may be an organometallic compound including a bond between a cationic metal such as metals in group 1, 2, or 3 with carbon, or a boron-containing compound. More particularly, the alkylating agent may be at least one selected from the group consisting of an organoaluminum compound, an organomagnesium compound, and an organolithium compound, or a mixture of at least two thereof.
• the organoaluminum compound may be, particularly, a compound of the following Formula 4:
• R is each independently a monovalent organic group which is combined with an aluminum atom via a carbon atom, and may be a hydrocarbyl group such as C 1-20 alkyl, C 3-20 cycloalkyl, C 2-20 alkenyl, C 3-20 cycloalkenyl, C 6-20 aryl, C 7-20 arylalkyl, C 7-20 alkylaryl, allyl, and C 2-32 alkynyl; or a heterohydrocarbyl group containing at least one heteroatom selected from the group consisting of a nitrogen atom, an oxygen atom, a boron atom, a silicon atom, a sulfur atom, and a phosphor atom in place of carbon in a hydrocarbyl structure,
• X is each independently selected from the group consisting of a hydrogen atom, a halogen group, a carboxyl group, an alkoxy group and an aryloxy group,
• z is an integer of 1 to 3.
• the organoaluminum compound may include dihydrocarbylaluminum hydride such as diethylaluminum hydride, di-n-propylaluminum hydride, diisopropylaluminum hydride, di-n-butylaluminum hydride, diisobutylaluminum hydride (DIBAH), di-n-octylaluminum hydride, diphenylaluminum hydride, di-p-tolylaluminum hydride, dibenzylaluminum hydride, phenylethylaluminum hydride, phenyl-n-propylaluminum hydride, phenylisopropylaluminum hydride, phenyl-n-butylaluminum hydride, phenylisobutylaluminum hydride, phenyl-n-octylaluminum hydride, p-tolyleth
• the organoaluminum compound may include aluminoxanes.
• the aluminoxane may be prepared by reacting trihydrocarbyl aluminum-based compounds with water, and may particularly be linear aluminoxanes of the following Formula 5a or circular aluminoxanes of the following Formula 5b:
• R is a monovalent organic group which is combined with an aluminum atom via a carbon atom and is the same as the above-defined R
• x and y are each independently an integer of 1 or more, particularly, 1 to 100, and more particularly, an integer of 2 to 50.
• the aluminoxane may be, methylaluminoxane (MAO), modified methylaluminoxane (MAO), ethylaluminoxane, n-propylaluminoxane, isopropylaluminoxane, butylaluminoxane, isobutylaluminoxane, n-pentylaluminoxane, neopentylaluminoxane, n-hexylaluminoxane, n-octylaluminoxane, 2-ethylhexylaluminoxane, cyclohexylaluminoxane, 1-methylcyclopentylaluminoxane, phenylaluminoxane or 2,6-dimethylphenyl aluminoxane, and any one or a mixture of at least two thereof may be used.
• MAO methylaluminoxane
• MAO modified methylaluminoxane
• the modified methylaluminoxane is obtained by substituting the methyl group of the methylaluminoxane with a modifier (R), particularly, a C 2-20 hydrocarbon group, and particularly, may be a compound of the following Formula 6:
• R is the same as defined above, and each of m and n may be an integer of 2 or more.
• Me means a methyl group.
• R in the above Formula 6 may be linear or branched C 2-20 alkyl, C 3-20 cycloalkyl, C 2-20 alkenyl, C 3-20 cycloalkenyl, C 6-20 aryl, C 7-20 arylalkyl, C 7-20 alkylaryl, allyl, or C 2-20 alkynyl, and more particularly, may be linear or branched C 2-10 alkyl such as ethyl, isobutyl, hexyl and octyl, and even more particularly, may be isobutyl.
• the modified methylaluminoxane may be obtained by substituting about 50 mol % to 90 mol % of the methyl group of the methylaluminoxane with the hydrocarbon group.
• the amount of the hydrocarbon group substituted in the modified methylaluminoxane is in the range, alkylation may be promoted, and catalytic activity may increase.
• Such modified methylaluminoxane may be prepared by a common method, and particularly, may be prepared using trimethylaluminum and an alkylaluminum other than trimethylaluminum.
• the alkylaluminum may be triisobutylaluminum, triethylaluminum, trihexylaluminum, or trioctylaluminum, and any one or a mixture of at least two thereof may be used.
• an organomagnesium compound as the alkylating agent includes at least one magnesium-carbon bond, and may be a magnesium compound dissoluble in a non-polar solvent, specifically, a non-polar hydrocarbon-based solvent.
• the organomagnesium compound may be a compound of the following Formula 7a:
• R is each independently a monovalent organic group and is the same as the above defined R.
• the organomagnesium compound of Formula 7a may be an alkylmagnesium compound such as diethylmagnesium, di-n-propylmagnesium, diisopropylmagnesium, dibutylmagnesium, dihexylmagnesium, diphenylmagnesium, and dibenzylmagnesium.
• organomagnesium compound may be a compound of the following Formula 7b:
• R is a monovalent organic group and is the same as the above defined R, and X is selected from the group consisting of a hydrogen atom, a halogen group, a carboxyl group, an alkoxy group and an aryloxy group.
• the organomagnesium compound of Formula 7b may be a hydrocarbyl magnesium hydride such as methyl magnesium hydride, ethyl magnesium hydride, butyl magnesium hydride, hexyl magnesium hydride, phenyl magnesium hydride, and benzyl magnesium hydride; a hydrocarbyl magnesium halide such as methyl magnesium chloride, ethyl magnesium chloride, butyl magnesium chloride, hexyl magnesium chloride, phenyl magnesium chloride, benzyl magnesium chloride, methyl magnesium bromide, ethyl magnesium bromide, butyl magnesium bromide, hexyl magnesium bromide, phenyl magnesium bromide, and benzyl magnesium bromide; a hydrocarbyl magnesium carboxylate such as methyl magnesium hexanoate, ethyl magnesium hexanoate, butyl magnesium hexanoate, hexyl magnesium hexanoate, methyl magnesium
• an alkyl lithium of R—Li as an organolithium compound (in this case, R is linear or branched C 1-20 alkyl, and more particularly, linear C 1-8 alkyl) may be used. More particularly, methyllithium, ethyllithium, isopropyllithium, n-butyllithium, sec-butyllithium, t-butyllithium, isobutyllithium, pentyllithium, isopentyllithium, etc. may be used, and any one or a mixture of at least two thereof may be used.
• an alkylating agent used in the present invention may be specifically, DIBAH which may play the role of a molecular weight controlling agent during polymerization.
• the alkylating agent may be the modified methylaluminoxane in consideration of improving catalytic activity and reactivity by using aliphatic hydrocarbon-based solvents of a single phase as a solvent system used during preparing a catalyst composition.
• the kind of the halogen compound is not specifically limited, but any halogenating agents used in the preparation of a common diene-based polymer may be used without specific limitation.
• the halogen compound may be a diatomic halogen, an interhalogen compound, a hydrogen halide, an organic halide, a nonmetal halide, a metal halide, or an organometallic halide, etc., and any one or a mixture of at least two thereof may be used.
• the halogen compound may be one selected from the group consisting of an organic halide, a metal halide and an organometallic halide, or a mixture of at least two thereof.
• the diatomic halogen may include fluorine, chlorine, bromine, or iodine.
• the interhalogen compound may particularly include iodine monochloride, iodine monobromide, iodine trichloride, iodine pentafluoride, iodine monofluoride, iodine trifluoride, etc.
• the hydrogen halide may particularly include hydrogen fluoride, hydrogen chloride, hydrogen bromide, or hydrogen iodide.
• the organic halide may particularly include t-butyl chloride (t-BuCl), t-butyl bromide, allyl chloride, allyl bromide, benzyl chloride, benzyl bromide, chloro-di-phenylmethane, bromo-di-phenylmethane, triphenylmethyl chloride, triphenylmethyl bromide, benzylidene chloride, benzylidene bromide, methyltrichlorosilane, phenyltrichlorosilane, dimethyldichlorosilane, diphenyldichlorosilane, trimethylchlorosilane (TMSCl), benzoyl chloride, benzoyl bromide, propionyl chloride, propionyl bromide, methyl chloroformate, methyl bromoformate, iodomethane, diiodomethane, triiodomethane (also t-
• the nonmetal halide may particularly include phosphorus trichloride, phosphorus tribromide, phosphorus pentachloride, phosphorus oxychloride, phosphorus oxybromide, boron trifluoride, boron trichloride, boron tribromide, silicon tetrafluoride, silicon tetrachloride (SiCl 4 ), silicon tetrabromide, arsenic trichloride, arsenic tribromide, selenium tetrachloride, selenium tetrabromide, tellurium tetrachloride, tellurium tetrabromide, silicon tetraiodide, arsenic triiodide, tellurium tetraiodide, boron triiodide, phosphorus triiodide, phosphorus oxyiodide or selenium tetraiodide.
• the metal halide may particularly include tin tetrachloride, tin tetrabromide, aluminum trichloride, aluminum tribromide, antimony trichloride, antimony pentachloride, antimony tribromide, aluminum trifluoride, gallium trichloride, gallium tribromide, gallium trifluoride, indium trichloride, indium tribromide, indium trifluoride, titanium tetrachloride, titanium tetrabromide, zinc dichloride, zinc dibromide, zinc difluoride, aluminum triiodide, gallium triiodide, indium triiodide, titanium tetraiodide, zinc diiodide, germanium tetraiodide, tin tetraiodide, tin diiodide, antimony triiodide or magnesium diiodide.
• the organometallic halide may particularly include dimethylaluminum chloride, diethylaluminum chloride, dimethylaluminum bromide, diethylaluminum bromide, dimethylaluminum fluoride, diethylaluminum fluoride, methylaluminum dichloride, ethylaluminum dichloride, methylaluminum dibromide, ethylaluminum dibromide, methylaluminum difluoride, ethylaluminum difluoride, methylaluminum sesquichloride, ethylaluminum sesquichloride (EASC), isobutylaluminum sesquichloride, methylmagnesium chloride, methylmagnesium bromide, ethylmagnesium chloride, ethylmagnesium bromide, n-butylmagnesium chloride, n-butylmagnesium bromide, pheny
• the catalyst composition for preparing a conjugated diene polymer according to an embodiment of the present invention may include a non-coordinating anion-containing compound or a non-coordinating anion precursor compound together with the halogen compound instead of the halogen compound.
• the non-coordinating anions may be anions not forming a coordination bond with the active center of a catalyst system due to steric hindrance and having a sterically large volume, and may be tetraarylborate anions or tetraarylborate fluoride anions.
• the non-coordinating anion-containing compound may include carbonium cations such as triaryl carbonium cations; ammonium cations such as N,N-dialkyl anilinium cations, or counter cations such as phosphonium cations together with the non-coordinating anions.
• the non-coordinating anion-containing compound may be triphenylcarbonium tetrakis(pentafluorophenyl)borate, N,N-dimethylanilinium tetrakis(pentafluorophenyl)borate, triphenylcarbonium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, N,N-dimethylanilinium tetrakis[3,5-bis(trifluoromethyl)phenyl]borate, or the like.
• a triaryl boron compound (BR 3 , where R is a strongly electron withdrawing aryl group such as a pentafluorophenyl group and a 3,5-bis(trifluoromethyl)phenyl group) may be used as a compound capable of forming non-coordinating anions under reaction conditions.
• the catalyst composition for forming a conjugated diene-based polymer according to an embodiment of the present invention may further include a diene-based monomer in addition to the above-described components.
• the diene-based monomer may be mixed with a catalyst for polymerization and form a premixing type catalyst, or may be polymerized with components in a catalyst for polymerization, specifically an alkylating agent such as DIBAH to form a preforming type catalyst.
• a catalyst for polymerization specifically an alkylating agent such as DIBAH to form a preforming type catalyst.
• catalytic activity may be improved, and a conjugated diene-based polymer thus prepared may be further stabilized.
• diene-based monomer any one used for the preparation of a common conjugated diene-based polymer may be used, without specific limitation.
• the diene-based monomer may be 1,3-butadiene, isoprene, 1,3-pentadiene, 1,3-hexadiene, 2,3-dimethyl-1,3-butadiene, 2-ethyl-1,3-butadiene, 2-methyl-1,3-pentadiene, 3-methyl-1,3-pentadiene, 4-methyl-1,3-pentadiene, 2,4-hexadiene, or the like, and any one or a mixture of at least two thereof may be used.
• the catalyst composition for forming a conjugated diene-based polymer according to an embodiment of the present invention may further include a reaction solvent in addition to the above-described components.
• the reaction solvent may particularly be a non-polar solvent having no reactivity with the components constituting the catalyst.
• linear, branched or circular aliphatic C 5-20 hydrocarbon such as n-pentane, n-hexane, n-heptane, n-octane, n-nonane, n-decane, isohexane, isopentane, isooctane, 2,2-dimethylbutane, cyclopentane, cyclohexane, methylcyclopentane and methylcyclohexane; a mixture solvent of aliphatic C 5-20 hydrocarbon such as petroleum ether, petroleum spirits, and kerosene; or an aromatic hydrocarbon-based solvent such as benzene, toluene, ethylbenzene, and xylene, and any one or a mixture of at least two thereof may be used.
• the non-polar solvent may be linear, branched or circular aliphatic C 5-20 hydrocarbon or a mixture solvent of aliphatic hydrocarbon, and more particularly, n-hexane, cyclohexane, or a mixture thereof may be used.
• reaction solvent may be appropriately selected according to the kind of the materials constituting the catalyst composition, specifically, the alkylating agent.
• an alkylaluminoxane such as methylaluminoxane (MAO) and ethylaluminoxane as the alkylating agent is not easily dissolved in an aliphatic hydrocarbon-based solvent, and an aromatic hydrocarbon-based solvent may be appropriately used.
• MAO methylaluminoxane
• ethylaluminoxane ethylaluminoxane
• an aliphatic hydrocarbon-based solvent may be appropriately used.
• a single solvent system may be attained together with an aliphatic hydrocarbon-based solvent such as hexane, which is mainly used as a polymerization solvent, the polymerization reaction may be more favorable.
• the aliphatic hydrocarbon-based solvent may promote catalytic activity, and reactivity may be further improved due to such catalytic activity.
• the above-described constituting components in the catalyst composition may form a catalytically active species via the interaction therebetween. Accordingly, the catalyst composition according to an embodiment of the present invention may include by optimally combining the amounts of the constituting components so as to show even better catalytic activity and excellent polymerization reactivity.
• the catalyst composition may include 20 equivalents or less of the functionalizing agent based on 1 equivalent of the rare earth metal compound. If the amount of the functionalizing agent is greater than 20 equivalents, unreacted functionalizing agent may remain to induce side reactions. More particularly, the functionalizing agent may be included in an amount of 3 equivalent to 7 equivalents based on 1 equivalent of the rare earth metal compound.
• the catalyst composition may include the alkylating agent in an amount of 5 moles to 200 moles based on 1 mole of the rare earth metal compound. If the amount of the alkylating agent is less than 5 molar ratio, activation effect with respect to the rare earth metal compound may be insignificant, and if the amount is greater than 200 molar ratio, the control of catalyst reaction during preparing a polymer is not easy, and it is apprehended that an excessive amount of the alkylating agent may induce side reactions. More particularly, the catalyst composition may include the alkylating agent in an amount of 5 moles to 20 moles based on 1 mole of the rare earth metal compound, and may include 5 moles to 10 moles in consideration of the remarkable improving effect of processability.
• the catalyst composition may include 1 mole to 20 moles, and may more particularly include 2 moles to 6 moles of the halogen compound based on 1 mole of the rare earth metal compound. If the amount of the halogen compound is less than 1 molar ratio, the generation of a catalytically active species is insufficient, and catalytic activity may be deteriorated. If the amount is greater than 20 molar ratio, the control of catalyst reaction is not easy, and the excessive amount of the halogen compound may induce side reactions.
• the catalyst composition may particularly further include 1 equivalent to 50 equivalents, and more particularly, 20 equivalents to 35 equivalents of the diene-based monomer based on 1 equivalent of the rare earth metal compound.
• the catalyst composition may further include the reaction solvent in an amount of 20 moles to 20,000 moles, and more particularly, 100 moles to 1,000 moles based on 1 mole of the rare earth metal compound.
• the catalyst composition having the above-described constitution may be prepared by mixing the functionalizing agent, the rare earth metal compound, the alkylating agent, the halogen compound, and selectively the conjugated diene monomer and the reaction solvent by a common method.
• a premixing type catalyst composition may be prepared by adding a functionalizing agent, a rare earth metal compound, an alkylating agent, a halogen compound and selectively a conjugated diene monomer to a reaction solvent one by one or simultaneously, and then, mixing.
• a preforming type catalyst composition may be prepared by mixing a functionalizing agent, a rare earth metal compound, an alkylating agent and a halogen compound to a reaction solvent, adding a conjugated diene monomer, and preforming.
• the mixing and polymerizing processes may be conducted in a temperature range of 0° C. to 60° C., and in this case, heat treatment may be conducted simultaneously to fulfill the temperature conditions.
• the catalyst composition may be prepared by mixing a rare earth metal compound, an alkylating agent, a reaction solvent and selectively a conjugated diene monomer, first heat treating at a temperature of 10° C. to 60° C., adding a halogen compound to the mixture thus obtained, and second heat treating in a temperature range of 0° C. to 60° C.
• a catalytically active species is formed by the interaction of constituting components.
• the catalyst composition of the present invention may produce a catalytically active species having better catalytic activity and polymerization reactivity when compared to the conventional composition.
• a conjugated diene-based polymer having even higher linearity and processability may be prepared.
• the catalyst composition having the above-described components may show the degree of a catalytic activity of 10,000 kg [polymer]/mol[Nd].h or more during the polymerization in a temperature range of 20° C. to 90° C. for 5 minutes to 60 minutes.
• the degree of catalytic activity is a value obtained from the injection molar ratio of the rare earth metal compound with respect to the total amount obtained of the conjugated diene-based polymer thus prepared.
• a conjugated diene-based polymer prepared using the catalyst composition and a method of preparing the same are provided.
• the conjugated diene-based polymer according to an embodiment of the present invention may be prepared by the polymerization reaction of a conjugated diene-based monomer according to a typical preparation method of a conjugated diene-based polymer except for using the catalyst composition for conjugated diene polymerization.
• the polymerization reaction may be conducted by a bulk polymerization, a solution polymerization, a suspension polymerization or an emulsion polymerization, and may be also conducted by a batch method, a continuous method and a semi-continuous method. More particularly, a method may be appropriately selected and conducted among the polymerization methods according to the kind of the functionalizing agent used in the catalyst composition.
• the polymerization reaction may be conducted by various methods such as a bulk polymerization, a solution polymerization, a suspension polymerization and an emulsion polymerization, and may be also conducted by a batch method, a continuous method and a semi-continuous method. More particularly, a method may be appropriately selected and conducted among the polymerization methods according to the kind of the functionalizing agent used in the catalyst composition. In an embodiment, in the case where the functionalizing agent included in the catalyst composition is a Si compound, a batch type polymerization method may be used.
• the conjugated diene polymer according to an embodiment of the present invention may be prepared by injecting a diene-based monomer to the catalyst composition for polymerization in a polymerization solvent, and performing reaction.
• the conjugated diene-based monomer any one used for preparing a common conjugated diene-based polymer may be used, without specific limitation.
• the diene-based monomer may particularly be 1,3-butadiene, isoprene, 1,3-pentadiene, 1,3-hexadiene, 2,3-dimethyl-1,3-butadiene, 2-ethyl-1,3-butadiene, 2-methyl-1,3-pentadiene, 3-methyl-1,3-pentadiene, 4-methyl-1,3-pentadiene, 2,4-hexadiene, etc., and any one or a mixture of at least two thereof may be used. More particularly, the conjugated diene-based monomer may be 1,3-butadiene.
• the other monomers may particularly include an aromatic vinyl monomer such as styrene, p-methylstyrene, ⁇ -methylstyrene, 1-vinylnaphthalene, 3-vinyltoluene, ethylvinylbenzene, divinylbenzene, 4-cyclohexylstyrene, and 2,4,6-trimethylstyrene, and any one or a mixture of at least two thereof may be used.
• the other monomers may be used in an amount of 20 wt % or less based on the total amount of the monomers used in the polymerization reaction.
• the diene-based monomer is used not such that the total amount used for the preparation of a diene-based polymer is dissolved in a non-polar solvent, but such that a portion of the total amount is dissolved in a polymerization solvent and polymerized, and then injected in installments according to the polymerization conversion ratio in once or more times, particularly, in twice or more times, and more particularly, in twice to four times.
• the polymerization solvent may be a non-polar solvent, and this solvent is the same as the solvent used in advance for the preparation of a catalyst for polymerization.
• the concentration of a monomer used in the polymerization solvent is not specifically limited, and may be 3 wt % to 80 wt %, and more particularly, 10 wt % to 30 wt %.
• additives may be further used, including a molecular weight controlling agent such as trimethylaluminum, diisobutylaluminum hydride, and trimethylsilane; a reaction terminator such as polyoxyethylene glycol phosphate; and an antioxidant such as 2,6-di-t-butylparacresol.
• a molecular weight controlling agent such as trimethylaluminum, diisobutylaluminum hydride, and trimethylsilane
• reaction terminator such as polyoxyethylene glycol phosphate
• an antioxidant such as 2,6-di-t-butylparacresol.
• additives serving easy solution polymerization particularly, additives such as a chelating agent, a dispersant, a pH controlling agent, a deoxidant, and an oxygen scavenger may be selectively used.
• the polymerization reaction may be conducted at a temperature of 0° C. to 200° C., and more particularly, 20° C. to 100° C.
• the polymerization reaction may be performed in the above temperature range until a conversion ratio of a conjugated diene-based polymer reaches 100%, for 5 minutes to 1 hour, particularly, for 10 minutes to 2 hours.
• the conjugated diene-based polymer may be a rare earth metal catalyzed conjugated diene-based polymer, which contains an active organometallic part which is derived from the catalyst including a rare earth metal compound, more particularly, a rare earth metal catalyzed butadiene-based polymer containing a 1,3-butadiene monomer unit, and more particularly, a neodymium catalyzed butadiene-based polymer containing a 1,3-butadiene monomer unit.
• the conjugated diene-based polymer may be a polybutadiene composed of only 1,3-butadiene monomers.
• the conjugated diene-based polymer produced by the polymerization reaction may be dissolved in a polymerization solvent, or may be obtained in a precipitated state. If the polymer is dissolved in the polymerization solvent, precipitation may be obtained by adding a lower alcohol such as methyl alcohol or ethyl alcohol, or steam.
• the method of preparing a conjugated diene-based polymer according to an embodiment of the present invention may further include precipitation and separation processes with respect to a conjugated diene-based polymer prepared after the polymerization reaction. In this case, filtering, separating and drying processes with respect to the precipitated conjugated diene-based polymer may be conducted by a common method.
• a conjugated diene-based polymer having high linearity and processability may be prepared by using a functionalizing agent during preparing a catalyst composition.
• the conjugated diene-based polymer may include a functional group derived from the functionalzing agent in a molecule.
• the conjugated diene-based polymer may be a rare earth metal catalyzed diene-based polymer which contains an active organometallic part which is derived from the catalyst including a rare earth metal compound, more particularly, a rare earth metal catalyzed butadiene-based polymer containing a 1,3-butadiene monomer unit, and more particularly, a neodymium catalyzed butadiene-based polymer.
• the conjugated diene-based polymer according to an embodiment of the present invention may have narrow distribution of molecular weight, i.e., have a polydispersity (PDI) of 3.4 or less, which is a ratio (Mw/Mn) of a weight average molecular weight (Mw) and a number average molecular weight (Mn).
• PDI polydispersity
• Mw/Mn weight average molecular weight
• Mn number average molecular weight
• the polydispersity of the conjugated diene-based polymer may be 3.2 or less in consideration of remarkable improving effect of the mechanical properties of the polymer according to the control of polydispersity.
• the conjugated diene-based polymer according to an embodiment of the present invention may have a weight average molecular weight (Mw) of 300,000 g/mol to 1,200,000 g/mol, and particularly 400,000 g/mol to 1,000,000 g/mol.
• Mw weight average molecular weight
• the conjugated diene-based polymer according to an embodiment of the present invention may have a number average molecular weight (Mn) of 100,000 g/mol to 700,000 g/mol, and particularly 120,000 g/mol to 500,000 g/mol.
• each of the weight average molecular weight and the number average molecular weight is conversion molecular weight with a polystyrene standard, which is analyzed by gel permeation type chromatography (GPC).
• the conjugated diene-based polymer according to an embodiment of the present invention may preferably satisfy the polydispersity, the weight average molecular weight and the number average molecular weight conditions at the same time.
• the conjugated diene-based polymer has a ratio (Mw/Mn) of a weight average molecular weight (Mw) and a number average molecular weight (Mn) of 3.4 or less, a weight average molecular weight (Mw) of 300,000 g/mol to 1,200,000 g/mol, and a number average molecular weight (Mn) of 100,000 g/mol to 700,000 g/mol, and more particularly, a ratio (Mw/Mn) of a weight average molecular weight (Mw) and a number average molecular weight (Mn) of 3.2 or less, a weight average molecular weight (Mw) of 400,000 g/mol to 1,000,000 g/mol, and a number average molecular weight (Mn) of 120,000 g/mol to 500,000 g/mol.
• the conjugated diene-based polymer shows high linearity due to the use of a functionalizing agent during the preparation process thereof.
• a branching degree may decrease, and a solution viscosity may increase.
• the linearity (SV/MV) of the conjugated diene-based polymer according to an embodiment of the present invention may be 1 to 15, and more particularly 3 to 13.
• the mooney viscosity (ML1+4) of the conjugated diene-based polymer at 100° C. may be 10 MU to 90 MU, and particularly, 20 MU to 80 MU.
• the solution viscosity of the conjugated diene-based polymer may be 100 cP to 600 cP, and particularly, 170 cP to 500 cP.
• the mooney viscosity may be measured, for example, by using MV2000E manufactured by Monsanto Co., Ltd. using Large Rotor at 100° C. at a rotor speed of 2 ⁇ 0.02 rpm.
• a specimen used may be stood at room temperature (23 ⁇ 3° C.) for 30 minutes or more, and 27 ⁇ 3 g of the specimen may be collected and put in a die cavity, and then, the mooney viscosity may be measured by operating Platen.
• the unit of the mooney viscosity is a mooney unit (MU).
• the solution viscosity (SV) was measured by the same method for measuring the mooney viscosity, but the viscosity of a polymer in 5% toluene at 20° C. was measured.
• the conjugated diene-based polymer according to an embodiment of the present invention may have a mooney viscosity (MV) at 100° C. of 20 MU to 80 MU, a solution viscosity (SV) of 100 cP to 600 cP, and a linearity (SV/MV) of 3 to 13.
• MV mooney viscosity
• SV solution viscosity
• SV/MV linearity
• the conjugated diene-based polymer according to an embodiment of the present invention may have the cis content in the conjugated diene-based polymer, when measured by Fourier transform infrared spectroscopy, particularly, the cis-1,4 bond content of 95% or more, and more particularly, 96% or more.
• the vinyl bond content in the conjugated diene-based polymer may be 1% or less.
• the conjugated diene-based polymer according to an embodiment of the present invention has pseudo-living properties. Accordingly, a polymer may be modified via the modification process of the terminal thereof for functionalizing using a functional group such as a group having an interaction with an inorganic filler such as carbon black and silica.
• the method of preparing a conjugated diene-based polymer according to an embodiment of the present invention may further include a modification process using a modifier with respect to the conjugated diene-based polymer prepared as the result of a polymerization reaction.
• the modification process may be conducted by a common modification method except for using the conjugated diene-based polymer according to the present invention.
• a compound which may impart a polymer with the functional group or increase a molecular weight via coupling during the reaction with a conjugated diene-based polymer may be used.
• the terminal modifier may be one selected from the group consisting of alkoxysilane, an imine-containing compound, an ester, an ester-carboxylate metal complex, an alkyl ester carboxylate metal complex, an aldehyde or ketone, an amide, an isocyanate, an isothiocyanate, an imine and an epoxide, or a mixture of at least two thereof.
• the modifier may be (E)-N,N-dimethyl-4-((undecylimino)methyl)benzenamine.
• the terminal modifier during a modification process may be used in an amount of 0.01 equivalents to 200 equivalents, and more particularly, 0.1 equivalents to 150 equivalents based on 1 equivalent of the rare earth metal compound.
• the conjugated diene-based polymer prepared via the modification process includes a modifier derived functional group in the polymer, particularly, at the terminal thereof.
• the modifier derived functional group may be at least one selected from an azacyclopropane group, a ketone group, a carboxyl group, a thiocarboxyl group, a carbonate group, a carboxylic anhydride group, a metal carboxylate, an acid halide, an urea group, a thiourea group, an amide group, a thioamide group, an isocyanate group, a thioisocyanate group, a halo-isocyano group, an epoxy group, a thioepoxy group, an imine group and an M-Z bond (where M is selected from the group consisting of Sn, Si, Ge and P, and Z is a halogen atom).
• a modified and conjugated diene-based polymer is provided.
• a rubber composition including the conjugated diene-based polymer is provided.
• the rubber composition may include 10 wt % to 100 wt % of the conjugated diene-based polymer and less than 90 wt % of a rubber component. If the amount of the conjugated diene-based polymer is less than 10 wt %, the improving effect of the abrasion resistance, crack resistance, and ozone resistance of the rubber composition may be insignificant.
• the rubber component may particularly be natural rubber (NR); or synthetic rubber such as a styrene-butadiene copolymer (SBR), a hydrogenated SBR, a polybutadiene (BR) having a low cis-1,4 bond content, a hydrogenated BR, a polyisoprene (IR), butyl rubber (IIR), ethylene propylene rubber, ethylene propylene diene rubber, polyisobutylene-co-isoprene, neoprene, poly(ethylene-co-propylene), poly(styrene-co-butadiene), poly(styrene-co-isoprene), poly(styrene-co-isoprene-co-butadiene), poly(isoprene-co-butadiene), poly(ethylene-co-propylene-co-diene), polysulfide rubber, acryl rubber, urethane rubber, silicone rubber, and epichloro
• the rubber composition may further include 10 parts by weight or more of a filler based on 100 parts by weight of the rubber component.
• the filler may be carbon black, starch, silica, aluminum hydroxide, magnesium hydroxide, clay (hydrated aluminum silicate), etc., and any one or a mixture of at least two thereof may be used.
• a compounding agent used in a common rubber industry such as a vulcanizing agent, a vulcanization accelerator, an antiaging agent, a scorch preventing agent, a softening agent, a zinc white, stearic acid and a silane coupling agent may be appropriately selected and mixed in addition to the rubber component and filler in a range of not hindering the object of the present invention.
• the rubber composition is prepared by using a catalyst composition including a functionalizing agent, and includes a conjugated diene-based polymer having excellent linearity and processability, thereby exhibiting improved effects of abrasion, viscoelasticity and processability in balance without leaning to one side.
• the rubber composition is useful for the manufacture of various rubber molded articles such as tires for a car, a truck (track) and a bus (for example, a tire tread, a side-wheel, a sub-tread, a bead filler, a breaking member, etc.), elastic parts of a tire stock, an O-ring, a profile, a gasket, a film, a hose, a belt, the sole of shoes, dustproof rubber and a window seal.
• a tire tread for example, a tire tread, a side-wheel, a sub-tread, a bead filler, a breaking member, etc.
• elastic parts of a tire stock for example, a tire tread, a side-wheel, a sub-tread, a bead filler, a breaking member, etc.
• elastic parts of a tire stock for example, a tire tread, a side-wheel, a sub-tread, a bead filler, a breaking member, etc.
• Triallylphenylsilane was prepared by conducting the same method described in Preparation Example 3 except for using PhSnCl 3 instead of MeSiCl 3 in Preparation Example 3.
• DIBAH diisobutylaluminum hydride
• DEAC diethylaluminum chloride
• a butadiene polymer was prepared by conducting the same method described in Example 1 except for using 5 equivalents of the functionalizing agent (ii) (TAS) of a chemical formula which was prepared in Preparation Example 5 as the functionalizing agent in Example 1 based on 1 equivalent of the neodymium compound.
• TAS functionalizing agent
• the functionalizing agent (i) DAS, 1 equivalent based on 1 equivalent of the neodymium compound
• DIBAH diisobutylaluminum hydride
• DEAC diethylaluminum chloride
• a butadiene polymer was prepared by conducting the same method described in Example 1 except for using the catalyst composition thus prepared.
• DIBAH diisobutylaluminum hydride
• DEAC diethylaluminum chloride
• a butadiene polymer was prepared by conducting the same method described in Example 1 except for using the catalyst for polymerization thus prepared.
• a butadiene polymer (BR1208TM, manufactured by LG Chemicals Co., Ltd.) prepared by conducting the same method described in Example 1 except for using nickel octoate instead of a Nd-based catalyst and not using a functionalizing agent in Example 1, was used.
• 89 mg (0.054 mmol) of a neodymium compound of Nd(2,2-diethyl decanoate) 3 , a functionalizing agent described in the following Table 1, diisobutylaluminum hydride (DIBAH) (0.12 ml, 0.675 mmol), and diethylaluminum chloride (DEAC) (0.13 ml, 0.130 mmol) were added one by one to hexane, and mixed to prepare a catalyst composition.
• DIBAH diisobutylaluminum hydride
• DEAC diethylaluminum chloride
• Example 4 (iii) 5 eq 30 min 98% Example 5 (i) 5 eq 30 min 91% Example 6 Example 7 Example 8 (iv) 5 eq 5 eq 5 eq 30 min 60 min 120 min 42.1% 58.4% 70.1% Example 9 Example 10 Example 11 (v) 5 eq 5 eq 5 eq 30 min 60 min 120 min 35.2% 49.3% 68.3% Example 12 (vi) 5 eq 30 min 10% Example 13 (vii) 5 eq 30 min 25%
• the amounts of cis-1,4 bonds, vinyl bonds and trans bonds in the prepared butadiene polymers were respectively measured by using Fourier infrared spectroscopy and nuclear magnetic resonance spectroscopy.
• the weight average molecular weight (Mw), and the number average molecular weight (Mn) of the prepared butadiene polymers were measured by gel permeation chromatography (GPC), and polydispersity (PDI, Mw/Mn) was calculated therefrom.
• each of the butadiene-based polymers thus prepared was dissolved in THF for 30 minutes under 40° C. conditions and loaded on gel permeation chromatography and flowed.
• two columns of PLgel Olexis and one column of PLgel mixed-C manufactured by Polymer Laboratories Co., Ltd. were used in combination as columns.
• all newly replaced columns were mixed bed type columns, and polystyrene (PS) was used as a GPC standard material.
• PS polystyrene
• Mooney viscosity (MV, (ML1+4 @100° C.) (MU): The mooney viscosity (MV) for the butadiene-based polymers was measured by using MV2000E manufactured by Monsanto Co., Ltd. using Large Rotor at 100° C. at a rotor speed of 2 ⁇ 0.02 rpm. In this case, a specimen used was stood at room temperature (23 ⁇ 3° C.) for 30 minutes or more, and 27 ⁇ 3 g of the specimen was collected and put in a die cavity, and then, the mooney viscosity was measured by operating Platen while applying torque.
• ⁇ S/R value was determined from a gradient value on the change of mooney viscosity, which was shown by the release of the torque when measuring the mooney viscosity.
• Solution viscosity was obtained by measuring viscosity of a polymer in 5% toluene at 20° C.
• the butadiene polymers of Examples 1 to 3 which were prepared using a functionalizing agent showed 97% or more of the cis bond content and 0.5% or less of the vinyl bond content in a polymer, and the butadiene polymers of Examples 1 to 3 showed 0.65 or more of a ⁇ S/R value and high linearity.
• the butadiene polymer of Examples 1 to 3, which were prepared using a functionalizing agent showed a low PDI of 3.05 or less, more particularly, 2.78 to 3.05, and was found to show narrow molecular weight distribution.
• the butadiene polymers of Examples 1 to 3, which were prepared using a functionalizing agent had SV/MV in a range of 3.08 to 10.5.
• Example 3 which was prepared using a catalyst composition in which 1,3-butadiene was additionally added as a conjugated diene-based monomer during preparing the catalyst composition, showed markedly lower solution viscosity and SV/MV when compared to those of Examples 1 and 2 using the same functionalizing agent. From the results, the improvement of processability during preparing a rubber composition may be expected.
• the butadiene polymer of Comparative Example 1 which was prepared by the same method as Example 1 except for not using a functionalizing agent, showed broader molecular weight distribution and a lower ⁇ S/R value when compared to those of Examples 1 to 3, which used a functionalizing agent. Accordingly, the butadiene polymer of Comparative Example 1 showed processability deterioration as shown in the following Table 3.
• Rubber specimens were manufactured using the butadiene polymers prepared in Examples 1 to 3, and Comparative Examples 1 and 2, and abrasion properties, viscoelasticity and processability were measured for the rubber specimens thus manufactured by the following methods, and the results are shown in Table 3.
• Loss volume index ARI A (abrasion resistance index, Method A) was measured according to a method specified in the experimental standard of ASTM D5963, and was represented as an index value. The higher the value was, the better the abrasion properties was.
• a dynamic mechanical analyzer of TA Co., Ltd. was used.
• a Tan 5 value was measured by changing deformation with a frequency of 10 Hz at each measurement temperature ( ⁇ 70° C. to 70° C.) with a twist mode.
• Payne effect was illustrated as a difference between a minimum value and a maximum value between the deformation of 0.28% to 40%. If the Payne effect was decreased, dispersibility of a filler such as silica was improved. If the Tan 5 value at a low temperature of 0° C. was increased, wet traction was good, and if the Tan 5 value at a high temperature of 50° C. to 70° C. was decreased, hysteresis loss was decreased, and low rolling resistance of a tire, i.e., a low fuel consumption ratio became good.
• each result was scored as 1-4 by representing near 1 when the surface state of a sheet was good and the edge portion thereof was clean, and 4 when the surface state was rough and the edge was not planar, to evaluate processability.
• the butadiene polymers prepared in Examples 1 to 3 using a catalyst composition including a functionalizing agent showed a higher loss volume index when compared to that of Comparative Examples 1 and 2, and were found to have better abrasion properties.
• the butadiene polymers of Examples 1 to 3 which were prepared using a catalyst composition including a functionalizing agent, showed similar level of a Tan 5 value at a low temperature of 0° C. as those of Comparative Examples 1 and 2, and was found to show equivalent level of wet traction.
• a Tan 5 value at a high temperature of 50° C. to 70° C. was further smaller in general when compared to those of Comparative Examples 1 and 2, and hysteresis loss was small, and low rolling resistance of a tire, i.e., a low fuel consumption ratio was further improved.
• rubber compositions including the butadiene polymer according to the present invention were found to show improved effects of abrasion properties, viscoelasticity, and processability in balance without leaning to one side when compared to the rubber compositions of the comparative examples.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Mechanical Engineering (AREA)
• General Chemical & Material Sciences (AREA)
• Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Polymerization Catalysts (AREA)

Applications Claiming Priority (5)

Publications (1)

Family

ID=57797297

Family Applications (6)

Family Applications Before (3)

Family Applications After (2)

Country Status (5)

Cited By (1)

Families Citing this family (15)

Citations (1)

Family Cites Families (48)

• 2015
  • 2015-12-22 KR KR1020150184238A patent/KR20170000756A/ko unknown
  • 2015-12-22 KR KR1020150184237A patent/KR101899637B1/ko active IP Right Grant
  • 2015-12-22 KR KR1020150184236A patent/KR101899636B1/ko active IP Right Grant
  • 2015-12-22 KR KR1020150184239A patent/KR20170000757A/ko unknown
• 2016
  • 2016-06-24 US US15/554,949 patent/US10538608B2/en active Active
  • 2016-06-24 CN CN201680023661.3A patent/CN107531853B/zh active Active
  • 2016-06-24 EP EP16814759.3A patent/EP3315520B1/en active Active
  • 2016-06-24 US US15/554,935 patent/US10538607B2/en active Active
  • 2016-06-24 EP EP16814756.9A patent/EP3315518B1/en active Active
  • 2016-06-24 CN CN201680022544.5A patent/CN107466299B/zh active Active
  • 2016-06-24 KR KR1020160079544A patent/KR101864014B1/ko active IP Right Grant
  • 2016-06-24 CN CN201680022860.2A patent/CN107531820B/zh active Active
  • 2016-06-24 EP EP16814757.7A patent/EP3315519B1/en active Active
  • 2016-06-24 JP JP2017549217A patent/JP6545278B2/ja active Active
  • 2016-06-24 US US15/554,907 patent/US10556976B2/en active Active
  • 2016-06-24 JP JP2017549213A patent/JP6552632B2/ja active Active
  • 2016-06-24 CN CN201680022490.2A patent/CN107531819B/zh active Active
  • 2016-06-24 JP JP2017549214A patent/JP6467067B2/ja active Active
  • 2016-06-24 US US15/554,894 patent/US20180044452A1/en not_active Abandoned
  • 2016-06-24 EP EP16814755.1A patent/EP3315517B1/en active Active
  • 2016-06-24 JP JP2017549227A patent/JP6467068B2/ja active Active
• 2019
  • 2019-06-27 US US16/454,888 patent/US10995165B2/en active Active
  • 2019-12-19 US US16/720,933 patent/US10836850B2/en active Active