US20160208115A1 - Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same - Google Patents

Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same Download PDF

Info

Publication number
US20160208115A1
US20160208115A1 US14/915,226 US201414915226A US2016208115A1 US 20160208115 A1 US20160208115 A1 US 20160208115A1 US 201414915226 A US201414915226 A US 201414915226A US 2016208115 A1 US2016208115 A1 US 2016208115A1
Authority
US
United States
Prior art keywords
chemical conversion
coating agent
top coating
chromium
trivalent chromium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/915,226
Other languages
English (en)
Inventor
Yasuhiro Kato
Toshiki Inomata
Manabu Inoue
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dipsol Chemicals Co Ltd
Original Assignee
Dipsol Chemicals Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dipsol Chemicals Co Ltd filed Critical Dipsol Chemicals Co Ltd
Assigned to DIPSOL CHEMICALS CO., LTD. reassignment DIPSOL CHEMICALS CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: INOMATA, TOSHIKI, INOUE, MANABU, KATO, YASUHIRO
Publication of US20160208115A1 publication Critical patent/US20160208115A1/en
Priority to US15/348,948 priority Critical patent/US9650521B1/en
Abandoned legal-status Critical Current

Links

Classifications

    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40Additives
    • C09D7/60Additives non-macromolecular
    • C09D7/61Additives non-macromolecular inorganic
    • C09D7/125
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D171/00Coating compositions based on polyethers obtained by reactions forming an ether link in the main chain; Coating compositions based on derivatives of such polymers
    • C09D171/02Polyalkylene oxides
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C09D183/04Polysiloxanes
    • C09D183/06Polysiloxanes containing silicon bound to oxygen-containing groups
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D183/00Coating compositions based on macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon, with or without sulfur, nitrogen, oxygen, or carbon only; Coating compositions based on derivatives of such polymers
    • C09D183/10Block or graft copolymers containing polysiloxane sequences
    • C09D183/12Block or graft copolymers containing polysiloxane sequences containing polyether sequences
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D5/00Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
    • C09D5/08Anti-corrosive paints
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40Additives
    • C09D7/60Additives non-macromolecular
    • C09D7/63Additives non-macromolecular organic
    • CCHEMISTRY; METALLURGY
    • C09DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09DCOATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D7/00Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
    • C09D7/40Additives
    • C09D7/65Additives macromolecular
    • CCHEMISTRY; METALLURGY
    • C23COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23CCOATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C22/00Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
    • C23C22/82After-treatment
    • C23C22/83Chemical after-treatment
    • CCHEMISTRY; METALLURGY
    • C08ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08GMACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
    • C08G77/00Macromolecular compounds obtained by reactions forming a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon in the main chain of the macromolecule
    • C08G77/42Block-or graft-polymers containing polysiloxane sequences
    • C08G77/46Block-or graft-polymers containing polysiloxane sequences containing polyether sequences
    • CCHEMISTRY; METALLURGY
    • C23COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23CCOATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2222/00Aspects relating to chemical surface treatment of metallic material by reaction of the surface with a reactive medium
    • C23C2222/10Use of solutions containing trivalent chromium but free of hexavalent chromium

Definitions

  • the present invention relates to a top coating agent used on a trivalent chromium or chromium-free chemical conversion film for aluminum, magnesium, zinc, and zinc alloys to improve the corrosion resistance and scratch resistance.
  • a chromate treatment using hexavalent chromium has been used to improve the corrosion resistance of aluminum, magnesium, zinc, and zinc alloys.
  • hexavalent chromium has been regulated.
  • a chemical conversion treatment using trivalent chromium has been used as an alternative to the chromate treatment.
  • atop coat may be applied on a chemical conversion film or on a finished surface prepared by subjecting a chemical conversion film to a finishing treatment as described in, for example, Japanese Patent Application Publication No. 2005-23372, WO2012/137680, etc.
  • a polyolefin wax-based friction modifier is generally mixed and dispersed in a top coating agent to adjust the friction coefficient.
  • an acidic water solvent-based top coating agent which is generally used for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film, has such a problem that the dispersed polyolefin wax separates, and hence a stable friction coefficient cannot be obtained.
  • an object of the present invention is to provide a friction modifier for a top coating agent for a trivalent chromium chemical conversion treatment coating film or a chromium-free chemical conversion treatment coating film, the friction modifier making it possible to obtain a stable friction coefficient, and to provide a top coating agent comprising the friction modifier.
  • a polyoxyalkylene fatty acid ester is effective as a friction modifier for a top coating agent in imparting a stable friction coefficient to a topcoat film on a hexavalent chromium-free trivalent chromium chemical conversion film or a chromium-free chemical conversion film formed on a surface of a substrate of a metal such as aluminum, magnesium, zinc, or a zinc alloy. It is also found that the above-described object can be achieved by a treatment using a top coating agent in which a modified organopolysiloxane and a water-soluble glycol ether are contained in a water solvent and to which a polyoxyalkylene fatty acid ester is added as an friction modifier. The present invention has been made based on these findings.
  • the present invention provides a friction modifier for a top coating agent for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film, the friction modifier comprising a polyoxyalkylene fatty acid ester.
  • the present invention also provides a top coating agent for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film, the top coating agent comprising: a polyoxyalkylene fatty acid ester; a modified organopolysiloxane; a water-soluble glycol ether; and water.
  • the present invention makes it possible to impart a stable friction coefficient, a high corrosion resistance, and the like to a surface of a substrate of a metal such as aluminum, magnesium, zinc, or a zinc alloy on which a trivalent chromium chemical conversion film or a chromium-free chemical conversion film is formed.
  • a friction modifier for a top coating agent for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film of the present invention comprises a polyoxyalkylene fatty acid ester.
  • the polyoxyalkylene fatty acid ester is preferably a saturated or unsaturated fatty acid ester of a poly(lower oxyalkylene) such as polyethylene glycol, polypropylene glycol, or polyisobutylene.
  • a poly(lower oxyalkylene) such as polyethylene glycol, polypropylene glycol, or polyisobutylene.
  • Specific examples of the polyoxyalkylene fatty acid ester include polyethylene glycol mono- or di-stearate, polypropylene glycol mono- or di-stearate, polypropylene glycol isostearate, polyethylene glycol mono- or di-oleate, polyethylene glycol mono- or di-laurate, and the like.
  • the HLB of the polyoxyalkylene fatty acid ester is preferably in a range from 8 to 20, and more preferably in a range from 15 to 18.
  • polyoxyalkylene fatty acid esters are readily available as commercial products.
  • One of the above-described polyoxyethylene fatty acid esters can be used alone, or two or more thereof can be used in combination.
  • the friction modifier may further comprise a known friction modifier other than the polyoxyalkylene fatty acid ester in combination, unless an effect of the friction modifier of the present invention is impaired.
  • composition of a top coating agent to which the friction modifier of the present invention used for a top coating agent for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film and comprising the polyoxyalkylene fatty acid ester is added is not particularly limited.
  • the top coating agent is preferably a water-soluble solvent top coating agent comprising a water-soluble resin, a water-soluble organic solvent, water, and the like, and further preferably a water solvent-based top coating agent comprising a water-soluble resin and water.
  • atop coating agent for a trivalent chromium chemical conversion film or a chromium-free chemical conversion film of the present invention comprises: a polyoxyalkylene fatty acid ester; a modified organopolysiloxane; a water-soluble glycol ether; and water.
  • the polyoxyalkylene fatty acid ester is as described above.
  • the concentration of the polyoxyalkylene fatty acid ester in the top coating agent is preferably in a range from 1 to 100 g/L, and more preferably in a range from 20 to 60 g/L.
  • a hydrophilic segment is bonded to a silicon atom at a terminal or in a side chain of an organopolysiloxane segment.
  • the hydrophilic segment may be a polyalkylene glycol, a polyalkylene glycol monoalkyl ether, an N-acylalkyleneimine, acrylic acid, vinyl alcohol, or the like.
  • the hydrophilic segment is preferably a polyalkylene glycol, and particularly preferably propylene glycol. Accordingly, preferred modified organopolysiloxanes are polyoxyalkylene-modified organopolysiloxanes.
  • Polyoxypropylene-modified organopolysiloxanes are particularly preferable. These polysiloxanes are readily available as commercially available polypropylene glycol-modified silicones. One of the modified organopolysiloxanes can be used alone, or two or more thereof can be used in combination.
  • the concentration of the modified organopolysiloxane in the top coating agent is preferably in a range from 50 to 450 g/L, and more preferably in a range from 150 to 350 g/L.
  • the above-described water-soluble glycol ether is preferably an alkylene glycol alkyl ether, and is, for example, a monoalkylene glycol monomonoalkyl ether or a monoalkylene glycol dialkyl ether. More preferred are ethylene glycol monoalkyl ethers (cellosolves).
  • ethylene glycol monomethyl ether (methyl cellosolve), ethylene glycol monoethyl ether (ethyl cellosolve), ethylene glycol monobutyl ether (butyl cellosolve), propylene glycol monomethyl ethers (2-methoxy-1-propanol, 1-methoxy-2-propanol, and the like), butylene glycol monomethyl ethers (2-methoxy-1-butanol, 3-methoxy-1-butanol, 1-methoxy-2-butanol, and the like), diethylene glycol monomethyl ether, triethylene glycol monomethyl ether, ethylene glycol dimethyl ether (dimethyl cello solve), ethylene glycol diethyl ether (diethyl cellosolve), and the like.
  • glycol monoalkyl ethers particularly preferred are ethylene glycol monobutyl ether and butylene glycol monomethyl ethers.
  • ethylene glycol monobutyl ether and butylene glycol monomethyl ethers are particularly preferred.
  • One of the above-described water-soluble glycol ethers can be used alone, or two or more thereof can be used in combination.
  • the concentration of the water-soluble glycol ether in the top coating agent is preferably in a range from 50 to 400 g/L, and more preferably in a range from 100 to 200 g/L.
  • the top coating agent of the present invention may further comprise a colloidal metal oxide.
  • the colloidal metal oxide is preferably silicon oxide, titanium oxide, aluminum oxide, zirconium oxide, zinc oxide, dichromium trioxide (Cr 2 O 3 ), or the like.
  • concentration of the colloidal metal oxide in the top coating agent is preferably 150 g/L or less, more preferably in a range from 10 to 100 g/L, and further preferably in a range from 20 to 50 g/L.
  • the top coating agent of the present invention may further comprise any coloring agent for a coating material, for example, a pigment or dye for coloring.
  • concentration of the pigment or dye for coloring in the top coating agent is generally in a range from 5 to 100 g/L, and more preferably in a range from 7 to 30 g/L.
  • blackening agents for blackening include carbon black pigments, carbon-based black pigments used for coating materials, solvent-soluble black dyes, such as metal complex salt dyes including chromium complex salt azo dyes, used for coating materials and being soluble in a solvent such as an organic solvent or water, and the like.
  • the blackening agent a combination of a carbon black pigment and a black dye is preferable, because a better black is obtained.
  • the ratio of the carbon black pigment and the black dye is preferably such that the ratio of carbon black pigment/black dye is in a range from 90/10 to 10/90.
  • the top coating agent of the present invention may further comprise an ultraviolet absorber.
  • the ultraviolet absorber may be benzophenone, benzotriazole, hydroxyphenylbenzotriazole, hydroxybenzophenone, hydroxyphenyl Striazine, an oxanilide derivative, or the like.
  • One of the above-described ultraviolet absorbers can be used alone, or two or more thereof can be used in combination.
  • the concentration of the ultraviolet absorber in the top coating agent is preferably 150 g/L or less, and more preferably in a range from 5 to 100 g/L.
  • the top coating agent of the present invention may further comprise additives for coating materials, a so-called stain-proofing agent for preventing stain and an anti-mold agent for preventing the development of mold used for metal surface treatment agents and the like, a surfactant and a water-soluble resin for improving the uniformity and gloss of the finished appearance, an anti-tarnish agent, and the like.
  • the balance of the top coating agent of the present invention other than the above-described components is water.
  • the top coating agent can be used after being diluted to a moderate concentration with, for example, water and a water-soluble organic solvent, for example, water and butyl cellosolve, for the purposes of adjustment of the coating workability, the storability, the thickness of the coated film, and the like.
  • concentration of the top coating agent in the diluted top coating agent solution is 30 to 100% by weight, and preferably 50 to 80% by weight.
  • a topcoat film to be formed on a trivalent chromium chemical conversion film or a chromium-free chemical conversion film can be obtained by immersing a workpiece in the above-described top coating agent, or by applying the above-described top coating agent to a workpiece with a spray, then sufficiently draining the top coating agent by centrifugation, and sufficiently drying the film.
  • the centrifugal drainage is preferably performed at 200 to 1000 rpm.
  • the draining time is preferably 2 to 5 minutes.
  • the drying temperature is preferably 100 to 220° C. In addition, the drying time is preferably 10 to 60 minutes. If the drying temperature is below the range, the corrosion resistance decreases. If the drying temperature is too high, the corrosion resistance decreases.
  • a two-stage drying method which includes preliminary drying and subsequent main drying.
  • the preliminary drying is preferably conducted at a drying temperature of 30° C. to 80° C. for a drying time of 3 to 30 minutes.
  • the main drying is preferably conducted at a drying temperature of 100° C. to 220° C. for a drying time of 10 to 60 minutes.
  • the preliminary drying at 80° C. or below is preferable, because it is possible to prevent failures of the film such as breakage and an attachment failure of the film due to the shrinkage of the film during drying at high temperature.
  • the thickness of the above-described topcoat film is generally 0.8 to 5 ⁇ m, and preferably 1 to 3 ⁇ m. When the thickness is within this range, a topcoat film having a high corrosion resistance can be obtained with excellent appearance, and it is also possible to prevent the formation of a pool of the liquid, the generation of a stain, and the decrease in dimensional precision.
  • Metal substrates used in the present invention include substrates of metals and alloys such as various metals including iron, nickel, copper, and aluminum, alloys thereof, and aluminum subjected to a zincate conversion treatment in various shapes such as a plate, a cuboid, a solid cylinder, a hollow cylinder, or a sphere.
  • the above-described metal substrate may be plated with zinc or a zinc alloy in a usual manner.
  • zinc plating it is possible to use any one of acidic or neutral baths such as a sulfuric acid bath, a fluoborate bath, a potassium chloride bath, a sodium chloride bath, and an ammonium chloride eclectic bath, and alkaline baths such as a cyanide bath, a zincate bath, and a pyrophosphate bath.
  • a zincate bath is preferable.
  • the zinc alloy plating may be conducted by using any alkaline bath such as an ammonium chloride bath or an organic chelate bath.
  • the zinc alloy plating may be zinc-iron alloy plating, zinc-nickel alloy plating, zinc-cobalt alloy plating, tin-zinc alloy plating, or the like.
  • the thickness of the zinc or zinc alloy plating may be any, and is preferably 1 ⁇ m or more, and more preferably 5 to 25 ⁇ m.
  • a method for using the top coating agent of the present invention is not particularly limited, as long as the top coating agent of the present invention is used for a top coating on a trivalent chromium chemical conversion film or a chromium-free chemical conversion film formed on the above-described substrate metal or on various films optionally formed on the trivalent chromium chemical conversion film or the chromium-free chemical conversion film.
  • a method for using the top coating agent of the present invention is, for example, as follows. Specifically, the above-described substrate metal as it is or the substrate metal on which zinc or zinc alloy plating has been deposited is optionally subjected to a pretreatment such as washing with water or washing with water and a subsequent activation treatment with nitric acid.
  • a chemical conversion treatment is conducted by, for example, a method based on an immersion treatment or the like by using a treatment solution for forming a trivalent chromium chemical conversion film or a chromium-free chemical conversion film.
  • the chemical conversion film is optionally subjected to a finishing treatment described in, for example, Japanese Patent Application Publication No. 2005-23372 or WO2012/137680.
  • the top coating agent of the present invention is used as an agent for top coating.
  • a trivalent chromium chemical conversion film when a trivalent chromium chemical conversion film is formed on a metal substrate having a zinc or zinc-based alloy plating layer, the metal substrate is generally immersed in a trivalent chromium chemical conversion treatment solution, for example, for 5 to 600 seconds with the liquid temperature being 10 to 80° C.
  • a trivalent chromium chemical conversion film having a thickness of about 0.1 to 0.3 ⁇ m is formed on the zinc or zinc-based alloy plating layer.
  • the workpiece when the metal substrate is plated with zinc, the workpiece is generally immersed in a diluted nitric acid solution before the trivalent chromium chemical conversion treatment to increase the gloss of the trivalent chromium chemical conversion film.
  • This pretreatment may be employed, but does not necessarily have to be employed in the present invention.
  • a layer of a finishing agent is formed on the trivalent chromium chemical conversion film as follows. Specifically, after or without washing the metal substrate having the trivalent chromium chemical conversion film, the trivalent chromium chemical conversion film is brought into contact with the finishing agent in the form of an aqueous solution (preferably, immersed in an aqueous finishing agent solution) to attach the finishing agent. Then, without washing with water, the metal substrate is dehydrated and dried to form the layer of the finishing agent.
  • the contact temperature (preferably, the immersion temperature) is generally 10 to 80° C.
  • the contact time (preferably, immersion time) is 3 to 30 seconds
  • the drying temperature is 50° C. to 200° C.
  • the drying time is 5 minutes to 60 minutes.
  • the thickness of the finished layer may be any, and is preferably about 0.05 to 0.3 ⁇ m.
  • a treatment solution used for forming the trivalent chromium chemical conversion film or the chromium-free chemical conversion film is not particularly limited, and any one of various known chemical conversion treatment solutions for zinc, a zinc alloy, aluminum, an aluminum alloy, or the like can be used.
  • the trivalent chromium chemical conversion treatment liquid it is possible to use any one of various trivalent chromate treatment liquids described in U.S. Pat. No. 5,415,702, Japanese Patent Application Publication Nos. 2003-166074, 2003-166075, 2002-053975, 2005-171296, and 2004-285373, etc.
  • black trivalent chromate treatment solutions described in Japanese Patent Application Publication Nos. 2003-26856 and 2007-100206, WO2007/094496, WO2007/100135, etc. are particularly preferable.
  • examples of the chromium-free chemical conversion treatment solution include chromium-free chemical conversion treatment solutions described in Japanese Patent Application Publication Nos. 2010-031332 and 2009-138132 etc.
  • a trivalent chromium black chemical conversion treatment liquid for zinc or zinc alloy plating is described in further detail.
  • a supply source of trivalent chromium ions any chromium compound containing trivalent chromium ions can be used. It is preferable to use a trivalent chromium salt such as chromium chloride, chromium sulfate, chromium nitrate, chromium phosphate, or chromium acetate.
  • chromium chloride chromium sulfate, chromium nitrate, chromium phosphate, or chromium acetate.
  • chromium salt such as chromium chloride, chromium sulfate, chromium nitrate, chromium phosphate, or chromium acetate.
  • One of the above-described supply sources of trivalent chromium can be used alone, or two or more thereof can be used in combination.
  • the concentration of trivalent chromium in the treatment liquid is not limited in terms of performance, but is preferably made as low as possible from the viewpoint of the wastewater treatment. Accordingly, considering the corrosion resistance performance and the like, the concentration of trivalent chromium ions in the treatment liquid is preferably in a range from 0.5 to 20 g/L, and more preferably in a range from 1 to 10 g/L. A concentration of trivalent chromium ions within this range is advantageous in terms of the wastewater treatment and is also economically advantageous.
  • the above-described trivalent chromium black chemical conversion treatment liquid is a trivalent chromium black chemical conversion treatment liquid for forming a coating generally called a hexavalent chromium-free trivalent chromium black chemical conversion film.
  • the above-described trivalent chromium black chemical conversion treatment liquid does not necessarily have to contain a chelating agent. However, it is preferable to contain a chelating agent, because a more uniform chemical conversion film can be obtained.
  • the chelating agent may be an organic carboxylic acid having a chelate-forming ability, a salt thereof, or the like.
  • organic carboxylic acids preferred are dicarboxylic acids such as oxalic acid, malonic acid, succinic acid, citric acid, and adipic acid, oxycarboxylic acids such as citric acid, tartaric acid, and malic acid, and polycarboxylic acids such as tricarballylic acid.
  • organic carboxylic acids may be in the form of salts (for example, salts with sodium, potassium, ammonium, or the like).
  • concentration of the chelating agent in the treatment liquid is preferably in a range from 1 to 40 g/L, and more preferably in a range from 5 to 35 g/L.
  • the mole ratio of the chelating agent to the trivalent chromium ions is preferably 0.2 to 4, and more preferably 1 to 2.
  • a method for mixing the chelating agent with the trivalent chromium compound is not particularly limited.
  • the formation of the complex may be promoted in advance by mixing under heating at a temperature of 60° C. or above, and then the mixture may be used.
  • the above-described trivalent chromium black chemical conversion treatment liquid may further contain additional metal ions other than trivalent chromium ions.
  • metal ions metal ions selected from the group consisting of Co, V, Ti, W, Zr, Mn, Mo, Ta, Ce, Sr, Fe, and Al ions may be contained.
  • the supply source of the metal ions maybe a chloride, nitrate, sulfate, acetate, oxoacid salt, or the like of the metal ions.
  • One of the above-described metal ion species can be used alone, or two or more thereof can be used in combination.
  • the concentration of the metal ions in the treatment liquid is preferably in a range from 0.1 to 50 g/L, and more preferably in a range from 0.5 to 20 g/L.
  • the concentration in the treatment liquid is preferably 0.1 to 50 g/L, and more preferably 0.5 to 20 g/L.
  • the treatment liquid may further comprise a sulfur compound.
  • the sulfur compound may be an inorganic sulfur compound or an organic sulfur compound. Of these sulfur compounds, the sulfur compound is preferably an organic sulfur compound. Especially, thiourea, thioacetic acid, thioglycolic acid, thiomalic acid, thiomaleic acid, dithioglycolic acid, sodium salts thereof, and ammonium salts thereof are preferable.
  • the concentration of the sulfur compound in the treatment liquid is preferably 0.1 to 10 g/L.
  • the zinc ion concentration in the above-described trivalent chromium black chemical conversion treatment liquid increases with the progress of the chemical conversion treatment.
  • the zinc ion concentration in the treatment bath during the use is 20 g/L or less. It is preferable that the zinc ion concentration be in a range from 0.1 g/L to 20 g/L, and that the zinc ion concentration at the initial stage (at the initial make-up of the bath) be in a range from 0.1 g/L to 10 g/L. Too high a zinc ion concentration in the treatment bath is not preferable, because the corrosion resistance and the degree of blackness decrease.
  • a zinc ion measurement method employed for managing the zinc ion concentration during the chemical conversion treatment is not particularly limited, and the zinc ion concentration can be managed precisely based on a known method such as a titration analysis, ion plasma spectrometry, or atomic absorption spectrometry.
  • the trivalent chromium ion concentration can also be managed using the same method.
  • the above-described trivalent chromium black chemical conversion treatment liquid may further comprise one or more inorganic acid ion species selected from the group of ions of phosphorus oxoacids other than phosphorous acid, phosphinic acid, alkali salts thereof, phosphoric acid alkyl esters, and phosphorous acid alkyl esters, chlorine ions, nitrate ions, sulfate ions, and the like.
  • the supply source of the inorganic acid may be phosphoric acid, phosphinic acid, hydrochloric acid, nitric acid, sulfuric acid, a salt thereof, or the like.
  • One of the above-described inorganic acids can be used alone, or two or more thereof can be used in combination.
  • the total concentration of the inorganic acid ions in the treatment liquid is preferably in a range from 1 to 80 g/L, and more preferably in a range from 2 to 20 g/L.
  • the pH of the above-described trivalent chromium black chemical conversion treatment liquid is preferably 0.5 to 5, and more preferably 1 to 4.
  • the pH may be adjusted by using the above-described inorganic acid or an alkaline agent such as an alkali hydroxide or ammonia water.
  • the balance of the above-described trivalent chromium black chemical conversion treatment liquid other than the above-described components is water.
  • the trivalent chromium black chemical conversion film used as a lower layer is preferably formed by using a hexavalent chromium-free trivalent chromium black chemical conversion treatment liquid having a Zn ion concentration of 20 g/L or less.
  • the amount of chromium ions attached in the trivalent chromium black chemical conversion film is preferably 0.2 to 3.0 mg/dm 2 . When the amount of chromium ions attached is within the range, an excellent black appearance and a high corrosion resistance can be obtained.
  • Atop coating agent 500 mL is placed in a 500 mL plastic bottle, and allowed to stand at room temperature for one week. After that, the separation of the liquid is visually observed.
  • a bolt is cut at the center between two surfaces of the head portion, and the film thickness is measured with an electron microscope.
  • the color of the exterior is visually observed.
  • a salt spray test was conducted according to JIS Z 2371 to evaluate the time to the formation of white rust.
  • the total friction coefficient is measured by the fastening test method according to JIS B 1084.
  • M6 bolts iron plated with zinc by a zincate process (using NZ-110 bath manufactured by DIPSOL CHEMICALS Co., Ltd.) to a thickness of 8 ⁇ m were used.
  • trivalent chromium chemical conversion films were formed by using a trivalent chromium chemical conversion treatment liquid (ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd., ZT-444DSM1: 75 mL/L and ZT-444DST: 1 mL/L, chemical conversion treatment conditions; 35° C. ⁇ 20 seconds).
  • ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd.
  • ZT-444DSM1 75 mL/L
  • ZT-444DST 1 mL/L
  • topcoat films were formed by using a top coating agent shown in Table 1 below to which a friction modifier was added, and the bolts were subjected to a centrifugal dehydrator (700 rpm, 3minutes), and dried (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium black chemical conversion films were formed by using a trivalent chromium black chemical conversion treatment liquid (ZTB-447S123C3 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-44751: 50 mL/L, ZTB-44752: 20 mL/L, and ZTB-44753: 7 mL/L, chemical conversion treatment conditions: 30° C. ⁇ 40 seconds). Subsequently, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes).
  • black topcoat films were formed by using a black top coating agent shown in Table 1 below to which a friction modifier was added, and subjected to a centrifugal dehydrator (700 rpm, 3 minutes), preliminary drying (40° C., 5 minutes), and then main drying (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium black chemical conversion films were formed by using a trivalent chromium black chemical conversion treatment liquid (ZTB-447S123C3 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-44751: 50 mL/L, ZTB-44752: 20 mL/L, and ZTB-44753: 7 mL/L, chemical conversion treatment conditions: 30° C. ⁇ 40 seconds). Further, a finishing treatment was conducted (ZTB-118 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-118: 150 mL/L, 45° C., 10 seconds).
  • the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes). After that, black topcoat films were formed by using a black top coating agent shown in Table 1 below to which a friction modifier was added. Then, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium chemical conversion films were formed by using a trivalent chromium chemical conversion treatment liquid (ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd., ZT-444DSM1: 75 mL/L and ZT-444DST: 1 mL/L, chemical conversion treatment conditions: 35° C. ⁇ 20 seconds). Subsequently, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes). After that, topcoat films were formed by using a top coating agent shown in Table 1 below. Then, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (200° C., 10 minutes).
  • ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd.
  • ZT-444DSM1 75 mL/L
  • ZT-444DST 1 mL/L
  • chemical conversion treatment conditions 35° C. ⁇ 20 seconds
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium black chemical conversion films were formed by using a trivalent chromium black chemical conversion treatment liquid (ZTB-447S123C3 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-44751: 50 mL/L, ZTB-44752: 20 mL/L, and ZTB-44753: 7 mL/L, chemical conversion treatment conditions: 30° C. ⁇ 40 seconds).
  • a centrifugal dehydrator 700 rpm, 3 minutes
  • black topcoat films were formed by using a black top coating agent shown in Table 1 below.
  • the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium chemical conversion films were formed by using a trivalent chromium chemical conversion treatment liquid (ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd.,
  • ZT-444DSM1 75 mL/L and ZT-444DST: 1 mL/L, chemical conversion treatment conditions: 35° C. ⁇ 20 seconds) Subsequently, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium black chemical conversion films were formed by using a trivalent chromium black chemical conversion treatment liquid (ZTB-447S123C3 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-44751: 50 mL/L, ZTB-44752: 20 mL/L, and ZTB-44753: 7 mL/L, chemical conversion treatment conditions: 30° C. ⁇ 40 seconds). Further, a finishing treatment was conducted (ZTB-118 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-118: 150 mL/L, treatment conditions: 45° C. ⁇ 10 seconds). Subsequently, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (80° C. 10 minutes).
  • a centrifugal dehydrator 700 rpm, 3 minutes
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium chemical conversion films were formed by using a trivalent chromium chemical conversion treatment liquid (ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd., ZT-444DSM1: 75 mL/L and ZT-444DST: 1 mL/L, chemical conversion treatment conditions: 35° C. ⁇ 20 seconds). Subsequently, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes). After that, topcoat films were formed by using a top coating agent shown in Table 1 below to which a conventional polyolefin wax friction modifier was added. Then, the bolts were subjected to a centrifugal dehydrator (700 rpm, 3minutes), and dried (200° C., 10 minutes).
  • ZT-444DSMT type manufactured by DIPSOL CHEMICALS Co., Ltd.
  • ZT-444DSM1 75 mL/L
  • ZT-444DST 1 mL/L
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.
  • trivalent chromium black chemical conversion films were formed by using a trivalent chromium black chemical conversion treatment liquid (ZTB-4475123 C3 type manufactured by DIPSOL CHEMICALS Co., Ltd., ZTB-44751: 50 mL/L, ZTB-44752: 20 mL/L, and ZTB-44753: 7 mL/L, chemical conversion treatment conditions: 30° C. ⁇ 40 seconds).
  • a centrifugal dehydrator 700 rpm, 3 minutes
  • black topcoat films were formed by using a black top coating agent shown in Table 1 below to which a conventional polyolefin wax friction modifier was added.
  • the bolts were subjected to a centrifugal dehydrator (700 rpm, 3 minutes), and dried (200° C., 10 minutes).
  • the obtained bolts were measured for the topcoat film thickness, the finished appearance, the corrosion resistance, the scratch resistance, and the total friction coefficient.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Wood Science & Technology (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Inorganic Chemistry (AREA)
  • Chemical Treatment Of Metals (AREA)
  • Paints Or Removers (AREA)
US14/915,226 2013-08-28 2014-08-19 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same Abandoned US20160208115A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US15/348,948 US9650521B1 (en) 2013-08-28 2016-11-10 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2013-176901 2013-08-28
JP2013176901 2013-08-28
PCT/JP2014/071642 WO2015029836A1 (ja) 2013-08-28 2014-08-19 3価クロム化成皮膜又はクロムフリー化成皮膜のトップコート剤用摩擦調整剤及びそれを含むトップコート剤

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2014/071642 A-371-Of-International WO2015029836A1 (ja) 2013-08-28 2014-08-19 3価クロム化成皮膜又はクロムフリー化成皮膜のトップコート剤用摩擦調整剤及びそれを含むトップコート剤

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/348,948 Continuation US9650521B1 (en) 2013-08-28 2016-11-10 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same

Publications (1)

Publication Number Publication Date
US20160208115A1 true US20160208115A1 (en) 2016-07-21

Family

ID=52586399

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/915,226 Abandoned US20160208115A1 (en) 2013-08-28 2014-08-19 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same
US15/348,948 Expired - Fee Related US9650521B1 (en) 2013-08-28 2016-11-10 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/348,948 Expired - Fee Related US9650521B1 (en) 2013-08-28 2016-11-10 Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same

Country Status (6)

Country Link
US (2) US20160208115A1 (zh)
EP (1) EP3040385A4 (zh)
JP (1) JP6074042B2 (zh)
CN (1) CN105518090B (zh)
MX (1) MX2016002495A (zh)
WO (1) WO2015029836A1 (zh)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018144580A1 (en) * 2017-02-01 2018-08-09 Chemeon Surface Technology, Llc Dyed trivalent chromium conversion coatings and methods of using same
US10752996B2 (en) 2015-07-01 2020-08-25 Nihon Parkerizing Co., Ltd Surface treatment agent, surface treatment method, and surface treated metal material
US11248125B2 (en) * 2017-06-01 2022-02-15 The Johns Hopkins University Coating system for aluminum-magnesium alloys

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3656890A4 (en) * 2017-07-19 2021-06-09 Okuno Chemical Industries Co., Ltd. TREATMENT SOLUTION INTENDED FOR FILM FORMATION
US11084942B2 (en) 2018-10-04 2021-08-10 Hamilton Sundstrand Corporation Additive for quality determination of conversion coatings
JP7500014B2 (ja) 2020-04-01 2024-06-17 ディップソール株式会社 トップコート剤及びこのトップコート剤を用いて形成した保護膜を有する銀白色締結部材
EP4269652A1 (en) * 2022-04-29 2023-11-01 Atotech Deutschland GmbH & Co. KG Method for black-passivating a zinc layer, black-passivation composition, and respective use

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5415702A (en) 1993-09-02 1995-05-16 Mcgean-Rohco, Inc. Black chromium-containing conversion coatings on zinc-nickel and zinc-iron alloys
JP3178980B2 (ja) * 1994-12-16 2001-06-25 信越化学工業株式会社 含フッ素シロキサン水中油滴型乳化組成物
JP4865139B2 (ja) 2000-05-31 2012-02-01 ディップソール株式会社 Sn−Zn合金めっき上にクロムフリー耐食性皮膜を形成する方法
JP2003026856A (ja) 2001-07-12 2003-01-29 Tayca Corp 合成樹脂配合用ハイブリッド粉体およびその製造方法
JP3332373B1 (ja) 2001-11-30 2002-10-07 ディップソール株式会社 亜鉛及び亜鉛合金めっき上に六価クロムフリー防錆皮膜を形成するための処理溶液、六価クロムフリー防錆皮膜及びその形成方法。
JP3332374B1 (ja) 2001-11-30 2002-10-07 ディップソール株式会社 亜鉛及び亜鉛合金めっき上に六価クロムフリー防錆皮膜を形成するための処理溶液、六価クロムフリー防錆皮膜及びその形成方法。
JP2004285373A (ja) 2003-03-19 2004-10-14 Dipsol Chem Co Ltd アルミニウム又はアルミニウム合金に高耐食性の6価クロム及びフッ素を含まない化成皮膜を形成する方法及び高耐食性アルミニウム又はアルミニウム合金
JP4625244B2 (ja) 2003-07-02 2011-02-02 ディップソール株式会社 3価クロメート皮膜用仕上げ剤組成物及び3価クロメート皮膜の仕上方法
JP4472965B2 (ja) * 2003-10-27 2010-06-02 ディップソール株式会社 3価クロメート液及びそれを用いた亜鉛ニッケル合金めっき上に6価クロムフリー耐食性皮膜を形成する方法
JP4446230B2 (ja) 2003-12-09 2010-04-07 ディップソール株式会社 アルミニウム又はアルミニウム合金用3価クロメート液及びそれを用いたアルミニウム又はアルミニウム合金表面に耐食性皮膜を形成する方法
US20060180247A1 (en) * 2005-02-15 2006-08-17 United States Of America As Represented By The Secretary Of The Navy Process for preparing chromium conversion coatings for iron and iron alloys
JP5198727B2 (ja) 2005-10-07 2013-05-15 ディップソール株式会社 亜鉛又は亜鉛合金上に黒色の6価クロムフリー化成皮膜を形成するための処理溶液
KR101020920B1 (ko) 2006-02-17 2011-03-09 딥솔 가부시키가이샤 아연 또는 아연 합금 상에 흑색의 3가 크롬 화성 피막을 형성하기 위한 처리 용액 및 아연 또는 아연 합금 상에 흑색의 3가 크롬 화성 피막을 형성하는 방법
JP5155850B2 (ja) 2006-03-03 2013-03-06 ディップソール株式会社 亜鉛又は亜鉛合金上に黒色の3価クロム化成皮膜を形成するための処理水溶液及び黒色3価クロム化成皮膜の形成方法
FR2908989B1 (fr) * 2006-11-23 2012-08-17 Oreal Composition cosmetique comprenant au moins un ester volatil
JP5914949B2 (ja) * 2007-08-03 2016-05-11 ディップソール株式会社 3価クロム耐食性化成皮膜及び3価クロム化成処理溶液
JP5467715B2 (ja) * 2007-09-03 2014-04-09 株式会社Uacj アルミニウム用親水性潤滑塗料、及びそれを用いた被塗物
JP5322000B2 (ja) 2007-12-07 2013-10-23 ディップソール株式会社 亜鉛又は亜鉛合金めっきに耐食性皮膜を形成させるための表面処理水溶液及び処理方法
WO2009145183A1 (ja) * 2008-05-27 2009-12-03 ユケン工業株式会社 仕上げ剤、および仕上げ剤から形成されたオーバーコートを備える部材
JP5593532B2 (ja) * 2008-07-30 2014-09-24 ディップソール株式会社 亜鉛又は亜鉛合金めっき上にクロムフリー化成皮膜を形成するための化成処理水溶液及びそれより得られたクロムフリー化成皮膜
JP5413842B2 (ja) * 2010-01-18 2014-02-12 株式会社Uacj 導電性プレコートアルミニウム合金板
TWI555880B (zh) * 2011-04-01 2016-11-01 迪普索股份有限公司 3價鉻化學轉換被膜用整理加工劑及黑色3價鉻化學轉換被膜之整理加工方法
JP5728766B2 (ja) * 2011-07-25 2015-06-03 日本表面化学株式会社 クロムフリー黒色化成皮膜形成処理液とそれを用いた黒色化成皮膜形成方法
JP6283857B2 (ja) 2013-08-28 2018-02-28 ディップソール株式会社 耐食性及び黒色外観に優れた車両用黒色締結部材

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10752996B2 (en) 2015-07-01 2020-08-25 Nihon Parkerizing Co., Ltd Surface treatment agent, surface treatment method, and surface treated metal material
WO2018144580A1 (en) * 2017-02-01 2018-08-09 Chemeon Surface Technology, Llc Dyed trivalent chromium conversion coatings and methods of using same
US10533254B2 (en) 2017-02-01 2020-01-14 Chemeon Surface Technology, Llc Dyed trivalent chromium conversion coatings and methods of using same
US11248125B2 (en) * 2017-06-01 2022-02-15 The Johns Hopkins University Coating system for aluminum-magnesium alloys

Also Published As

Publication number Publication date
EP3040385A4 (en) 2017-03-29
CN105518090A (zh) 2016-04-20
EP3040385A1 (en) 2016-07-06
JPWO2015029836A1 (ja) 2017-03-02
US20170121540A1 (en) 2017-05-04
US9650521B1 (en) 2017-05-16
WO2015029836A1 (ja) 2015-03-05
CN105518090B (zh) 2018-04-03
JP6074042B2 (ja) 2017-02-01
MX2016002495A (es) 2016-05-31

Similar Documents

Publication Publication Date Title
US9650521B1 (en) Friction modifier for top coating agent for trivalent chromium chemical conversion coating film or chromium-free chemical conversion coating film, and top coating agent including same
KR101212335B1 (ko) 아연 또는 아연 합금 도금에 내식성 피막을 형성시키기 위한 표면 처리 수용액 및 처리 방법
US4263059A (en) Coating solutions of trivalent chromium for coating zinc and cadmium surfaces
ES2912177T3 (es) Hojalata con tratamiento de superficie libre de cromo, método de producción y agente de tratamiento de superficie para la misma
KR910003722B1 (ko) 인산염 코우팅 조성물과 아연-니켈 인산염 코우팅의 적용 방법
JPS6352114B2 (zh)
MX2013010913A (es) Agente de acabado para pelicula de recubrimiento con conversion quimica de cromo trivalente, y metodo para el acabado de pelicula de recubrimiento con conversio quimica de cromo trivalente negra.
US10240237B2 (en) Black coupling member for vehicles, having excellent corrosion resistance and black appearance
WO2016104703A1 (ja) 亜鉛又は亜鉛合金基材用3価クロム化成処理液及び化成皮膜
US4351675A (en) Conversion coatings for zinc and cadmium surfaces
TWI519683B (zh) 含鐵材料之腐蝕保護方法
US9573162B2 (en) Processes and compositions for improving corrosion performance of zirconium oxide pretreated zinc surfaces
KR101322063B1 (ko) Mo계 혼합 조성물 및 이를 이용한 내흑화성과 전기전도성이 우수한 표면처리강판
JP5660751B2 (ja) 亜鉛又は亜鉛合金めっき上にクロムフリー化成皮膜を形成するための化成処理水溶液及びそれより得られたクロムフリー化成皮膜
TWI827811B (zh) 化成處理劑、具有化成皮膜的金屬材料的製造方法以及具有化成皮膜的金屬材料
JP7046317B2 (ja) ヘッドレストステー
KR960007775B1 (ko) 크롬용출이 억제되는 크로메이트용액 및 이 용액을 이용한 크로메이트강판 제조방법
KR100293233B1 (ko) 크로메이트바탕피막제조용전처리용액및이를이용한표면외관및내식성이우수한도포형크로메이트피막제조방법
KR101332477B1 (ko) 표면외관이 우수한 크롬프리 흑화 전기도금강판 제조 방법
JP2004244647A (ja) 耐食性亜鉛系めっき鋼板およびその製造方法
JP2000064062A (ja) 耐食性および耐黒変性に優れたクロメート処理電気亜鉛めっき鋼板の製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: DIPSOL CHEMICALS CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KATO, YASUHIRO;INOMATA, TOSHIKI;INOUE, MANABU;REEL/FRAME:037848/0668

Effective date: 20160209

STCB Information on status: application discontinuation