US20150240056A1 - Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product - Google Patents

Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product Download PDF

Info

Publication number
US20150240056A1
US20150240056A1 US14/431,345 US201314431345A US2015240056A1 US 20150240056 A1 US20150240056 A1 US 20150240056A1 US 201314431345 A US201314431345 A US 201314431345A US 2015240056 A1 US2015240056 A1 US 2015240056A1
Authority
US
United States
Prior art keywords
filler material
mono
succinic anhydride
substituted succinic
calcium carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/431,345
Other languages
English (en)
Inventor
Samuel Rentsch
Matthias Buri
René Vinzenz Blum
Martin Brunner
Patrick A.C. Gane
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Omya International AG
Original Assignee
Omya International AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Omya International AG filed Critical Omya International AG
Priority to US14/431,345 priority Critical patent/US20150240056A1/en
Assigned to OMYA INTERNATIONAL AG reassignment OMYA INTERNATIONAL AG ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BURI, MATTHIAS, Blum, René Vinzenz , GANE, PATRICK A.C., RENTSCH, SAMUEL, BRUNNER, MARTIN
Publication of US20150240056A1 publication Critical patent/US20150240056A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C07—ORGANIC CHEMISTRY
    • C07D—HETEROCYCLIC COMPOUNDS
    • C07D307/00—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom
    • C07D307/02—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings
    • C07D307/34—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members
    • C07D307/56—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom not condensed with other rings having two or three double bonds between ring members or between ring members and non-ring members with hetero atoms or with carbon atoms having three bonds to hetero atoms with at the most one bond to halogen, e.g. ester or nitrile radicals, directly attached to ring carbon atoms
    • C07D307/60—Two oxygen atoms, e.g. succinic anhydride
    • D—TEXTILES; PAPER
    • D01—NATURAL OR MAN-MADE THREADS OR FIBRES; SPINNING
    • D01F—CHEMICAL FEATURES IN THE MANUFACTURE OF ARTIFICIAL FILAMENTS, THREADS, FIBRES, BRISTLES OR RIBBONS; APPARATUS SPECIALLY ADAPTED FOR THE MANUFACTURE OF CARBON FILAMENTS
    • D01F1/00—General methods for the manufacture of artificial filaments or the like
    • D01F1/02—Addition of substances to the spinning solution or to the melt
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/12—Surface area
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K9/00—Use of pretreated ingredients
    • C08K9/04—Ingredients treated with organic substances
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK  ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
    • C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
    • C09C1/02—Compounds of alkaline earth metals or magnesium
    • C09C1/021—Calcium carbonates
    • D—TEXTILES; PAPER
    • D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
    • D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
    • D04H3/00—Non-woven fabrics formed wholly or mainly of yarns or like filamentary material of substantial length
    • D04H3/005—Synthetic yarns or filaments
    • D04H3/007—Addition polymers
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2321/00—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • D10B2321/02—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins
    • D10B2321/022—Fibres made from polymers obtained by reactions only involving carbon-to-carbon unsaturated bonds polyolefins polypropylene
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2501/00—Wearing apparel
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2505/00—Industrial
    • D10B2505/04—Filters
    • D—TEXTILES; PAPER
    • D10—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B—INDEXING SCHEME ASSOCIATED WITH SUBLASSES OF SECTION D, RELATING TO TEXTILES
    • D10B2509/00—Medical; Hygiene
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
    • Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]

Definitions

  • the present invention relates to a process for preparing a surface treated filler material product with succinic anhydride(s), a surface treated filler material product, a polymer composition, a fiber and/or filament and/or film and/or thread comprising the surface treated filler material product and/or the polymer composition, an article comprising the surface treated filler material product and/or the polymer composition and/or the fiber and/or filament and/or film and/or thread as well as the use of a mono-substituted succinic anhydride for decreasing the hydrophilicity of a calcium carbonate-containing filler material surface and the use of a surface-treated filler material product for initiating the crosslinking reaction in epoxide resins.
  • filler materials and especially calcium carbonate-containing filler materials are often used as particulate fillers in thermoplastic polymer products, like fibers, filaments, films and/or threads, usually made of polyethylene (PE), polypropylene (PP), polyurethane (PU), polyvinylchloride (PVC), polyester (PES) and/or polyamide (PA).
  • PE polyethylene
  • PP polypropylene
  • PU polyurethane
  • PVC polyvinylchloride
  • PET polyvinylchloride
  • PA polyamide
  • additives are introduced to provide the filler material with a coating and to improve the dispersability of said mineral filler material in the polymer composition as well as possibly to improve the processability of this polymer composition and/or properties of the final application products such as fibers, filaments, films and/or threads.
  • An elimination of such additives would unacceptably reduce the resulting fiber, filament, film and/or thread quality.
  • such mineral filler materials are generally associated with the presence of volatiles evolving at temperatures
  • volatiles may lead to a reduction in the tensile and tear strength of such a fiber, filament, films and/or threads, and may degrade its visible aspects, in particular of its visible uniformity. Furthermore, volatiles can generate excessive foaming of the mineral filled polymer melt during a step of compounding, causing unwanted product build-up at the vacuum extraction and hence, forcing a reduced output rate.
  • WO 00/20336 relates to an ultrafine natural calcium carbonate, which may optionally be treated with one or several fatty acids or one or several salts or mixtures thereof, and which is used as a theology regulator for polymer compositions.
  • U.S. Pat. No. 4,407,986 relates a precipitated calcium carbonate that is surface-treated with a dispersant that may include higher aliphatic acids and their metal salts in order to limit the addition of lubricant additives when kneading this calcium carbonate with crystalline polypropylene and to avoid the formation of calcium carbonate aggregates that limit the impact strength of the polypropylene.
  • EP 0 998 522 relates to surface treated calcium carbonate filler for breathable films using fatty acids of at least 10 carbon atoms wherein the filler before and after the treatment process has to be mostly free of moisture in the range of below 0.1 wt.-%.
  • Example 7 discloses a mixture of an ammonium salt of 12-hydroxystearic acid in combination with a fatty acid (in a weight ratio of 1:1) used to treat a mineral filler.
  • WO 03/082966 relates to a cross-linkable and/or cross-linkable and/or cross-linked nanofiller composition which, in optional embodiments, may additionally include fillers that may or may not be coated with stearic acid, stearate, silane, siloxane and/or titanate.
  • Such nanofiller compositions are used to increase barrier properties, strength and heat distortion temperatures, making them useful in medical, automotive, electrical, construction and food application.
  • US 2002/0102404 describes dispersible calcium carbonate particles coated on their surface with a combination of saturated and unsaturated aliphatic carboxylic acids and salts thereof along with an organic compound such as a phthalic ester, which are used in adhesive compositions to improve viscosity stability and adhesion properties.
  • US 2002/0102404 requires the implementation of a mixture of saturated and unsaturated aliphatic carboxylic acids/salts.
  • the presence of unsaturated aliphatic carboxylic acids/salts increases the risk or unwanted in situ side reactions with the double bond during processing of any unsaturated aliphatic carboxylic acid/salt-comprising material.
  • the presence of unsaturated aliphatic carboxylic acids/salts may result in discoloration of, or unwanted odour development, and notably rancid odours, in the material in which they are implemented.
  • Claim 11 of WO 92/02587 indicates that a saponified sodium salt solution of at least one high molecular weight unsaturated fatty acid or combination of at least one high molecular weight unsaturated fatty acid and at least one high molecular weight unsaturated fatty acid, may be added to a pre-heated slurry of precipitated calcium carbonate, to ultimately produce a desired level of fatty acid coating on the calcium carbonate before proceeding with further process steps.
  • JP54162746 discloses a composition comprising given relative amounts of rigid vinyl chloride resin, fatty acid treated-colloidal calcium carbonate, and barium stearate used in order to improve the heat stability of the vinyl chloride composition.
  • U.S. Pat. No. 4,520,073 describes mineral filler materials with improved hydrophobic coatings prepared by pressure coating of porous minerals using steam as a carrier for the coating material.
  • Said coating material may be selected, among other options, from long chain aliphatic fatty acids and their salts.
  • WO 01/32787 describes a particulate alkaline earth metal carbonate material product which has on its particles a coating of hydrophobic material comprising a composition formed of (a) a first component which comprises the reaction product of the alkaline earth metal carbonate and at least one given aliphatic carboxylic acid and (b) a second component having a carbonate release temperature substantially higher than the first component comprises a compound of formula CH 3 (CH 2 ) m COOR.
  • WO 2008/077156 A2 relates to spunlaid fibers comprising at least one polymeric resin and at least one filler having an average particle size of less than or equal to about 5 microns and/or having a top cut of less than about 15 microns, wherein the at least one filler is present in an amount of less than about 40% by weight, relative to the total weight of the spunlaid fibers.
  • the coating of the filler is described as being at least one organic material chosen from fatty acids and salts and esters thereof, e.g. stearic acid, stearate, ammonium stearate and calcium stearate.
  • GB 2 336 366 A relates to filled thermoplastic compositions, and, in particular, filled low density polyethylene compositions which are to be formed into products of articles by the process of extrusion.
  • the hydrophobising agent is preferably an organic carboxylic acid or partially or fully neutralised salt thereof which has at least one saturated or unsaturated hydrocarbon chain having from 8 to 28 carbon atoms, if the particulate mineral filler has a neutral to alkaline surface reaction, for example calcium carbonate.
  • a further objective of the present invention to provide a process for preparing a surface treated filler material product having improved surface characteristics, and especially a low hydrophilicity.
  • a still further objective is to provide a process for preparing a surface treated filler material product featuring a limited quantity of total volatiles evolved at temperatures of between 25 and 350° C.
  • a further objective is to provide a process for preparing a surface treated filler material product by using a surface treatment agent which can be easily handled and features a high flash point.
  • a further objective is to provide a process for preparing a surface treated filler material product that can be carried out under cost-efficient and mild conditions, i.e. by avoiding an intensive thermal treatment. Further objects can be gathered from the following description of the invention.
  • a process for preparing a surface treated filler material product with succinic anhydride(s) comprising at least the steps of:
  • filler material in the meaning of the present invention refers to substances of mineral origin added to materials such as paper, plastics, rubber, paints and adhesives, etc. to lower the consumption of more expensive materials such as binders, or to enhance technical properties of the products.
  • filler material refers to substances of mineral origin added to materials such as paper, plastics, rubber, paints and adhesives, etc. to lower the consumption of more expensive materials such as binders, or to enhance technical properties of the products.
  • typical filler materials used in the respective fields.
  • calcium carbonate-containing filler material refers to a material that comprises at least 80 wt.-% calcium carbonate, based on the total dry weight of the calcium carbonate-containing filler material.
  • surface treated filler material product in the meaning of the present invention refers to a calcium carbonate-containing filler material which has been contacted with a surface treatment agent such as to obtain a coating layer on at least a part of the surface of the calcium carbonate-containing filler material.
  • succinic anhydride also called dihydro-2,5-furandione, succinic acid anhydride or succinyl oxide, has the molecular formula C 4 H 4 O 3 and is the acid anhydride of succinic acid.
  • succinic anhydride in the meaning of the present invention refers to a succinic anhydride substituted with one substituent.
  • the term “mono-substituted” succinic acid in the meaning of the present invention refers to a succinic acid substituted with one substituent.
  • dry calcium carbonate-containing filler material is understood to be a filler material having less than 0.3% by weight of water relative to the filler material weight.
  • the % water (equal to residual total moisture content) is determined according to the Coulometric Karl Fischer measurement method, wherein the filler material is heated to 220° C., and the water content released as vapour and isolated using a stream of nitrogen gas (at 100 ml/min) is determined in a Coulometric Karl Fischer unit.
  • salty reaction products in the meaning of the present invention refers to products obtained by contacting a calcium carbonate-containing filler material with one or more mono-substituted succinic anhydride(s). Said salty reaction products are formed between the mono-substituted succinic acid which is formed from the applied mono-substituted succinic anhydride and reactive molecules located at the surface of the calcium carbonate-containing filler material. Alternatively, said salty reaction products are formed between the mono-substituted succinic acid, which may optionally be present with the at least one mono-substituted succinic anhydride, and reactive molecules located at the surface of the calcium carbonate-containing filler material.
  • the term “specific surface area” (in m 2 /g) of the mineral filler in the meaning of the present invention is determined using the BET method with nitrogen as adsorbing gas, which is well known to the skilled man (ISO 9277:1995).
  • the total surface area (in m 2 ) of the mineral filler is then obtained by multiplication of the specific surface area and the mass (in g) of the mineral filler prior to treatment.
  • the “d 50 ” value is determined based on measurements made by using a SedigraphTM 5100 of Micromeritics Instrument Corporation (operating instrument software version 1.04) and is defined as the size at which 50% (the median point) of the particle volume or mass is accounted for by particles having a diameter equal to the specified value.
  • the method and the instrument are known to the skilled person and are commonly used to determine grain size of fillers and pigments.
  • the measurement is carried out in an aqueous solution of 0.1 wt.-% Na 4 P 2 O 7 .
  • the samples are dispersed using a high speed stirrer and supersonics.
  • a surface treated filler material product comprising
  • the molar ratio of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid to the salty reaction product(s) thereof is from 0.1:99.9 to 99.9:01, preferably from 30:70 to 10:90. It is also preferred that the salty reaction product(s) of the at least one mono-substituted succinic anhydride and/or the at least one mono-substituted succinic acid are one or more calcium and/or magnesium salts thereof. It is further preferred that the treatment layer further comprises at least one organic material such as polysiloxanes.
  • the surface treated filler material product comprises the treatment layer in an amount of from 0.1 to 2.5 wt.-%, preferably in an amount of from 0.1 to 2 wt.-%, more preferably in an amount of from 0.1 to 1.5 wt.-%, even more preferably in an amount of from 0.1 to 1 wt.-% and most preferably in an amount of from 0.2 to 0.8 wt.-% based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • a polymer composition comprising at least one polymeric resin and from 1 to 85 wt.-%, based on the total weight of the polymer composition, of the surface treated filler material product.
  • the at least one polymeric resin is at least one thermoplastic polymer, preferably a thermoplastic polymer selected from the group comprising homopolymers and/or copolymers of polyolefins, polyamides halogen-containing polymers and/or polyesters.
  • the polymer composition is a masterbatch, preferably the masterbatch comprises the surface treated filler material product in an amount of from 50 to 85 wt.-%, preferably from 60 to 85 wt.-% and more preferably from 70 to 80 wt.-%, based on the total weight of the masterbatch.
  • a fiber and/or filament and/or film and/or thread comprising the surface treated filler material product and/or the polymer composition.
  • an article comprising the surface treated filler material product and/or a polymer composition and/or a fiber and/or filament and/or film and/or thread is provided, wherein the article is selected from the group comprising hygiene products, medical and healthcare products, filter products, geotextile products, agriculture and horticulture products, clothing, footwear and baggage products, household and industrial products, packaging products, construction products and the like.
  • the use of a mono-substituted succinic anhydride for decreasing the hydrophilicity of a calcium carbonate-containing filler material surface is provided.
  • the use of a surface-treated filler material product for initiating the crosslinking reaction in epoxide resins is provided.
  • the at least one calcium carbonate-containing filler material of step a) is selected from among ground calcium carbonate (GCC), precipitated calcium carbonate (PCC), modified calcium carbonate (MCC) and mixture thereof.
  • the at least one calcium carbonate-containing filler material of step a) comprises at least one ground calcium carbonate (GCC) selected from the group comprising marble, chalk, dolomite limestone and mixtures thereof and/or at least one precipitated calcium carbonate (PCC) selected from the group comprising one or more of the aragonitic, vateritic and calcitic mineralogical crystal forms and/or at least one modified calcium carbonate (MCC).
  • GCC ground calcium carbonate
  • PCC precipitated calcium carbonate
  • MCC modified calcium carbonate
  • the at least one calcium carbonate-containing filler material of step a) has a weight median particle size d 50 from 0.25 ⁇ m to 5 ⁇ m and preferably from 0.7 ⁇ m to 4 ⁇ m.
  • the at least one calcium carbonate-containing filler material of step a) has a top cut (d 98 ) of ⁇ 12.5 ⁇ m, preferably of ⁇ 10 ⁇ m and most preferably of ⁇ 7.5 ⁇ m.
  • the at least one calcium carbonate-containing filler material of step a) has a specific surface area (BET) of from 0.5 to 50 m 2 /g, more preferably of from 0.5 to 35 m 2 /g and most preferably of from 0.5 to 15 m 2 /g as measured by the BET nitrogen method.
  • BET specific surface area
  • the at least one calcium carbonate-containing filler material of step a) has a residual total moisture content of from 0.01 to 0.2 wt.-%, preferably from 0.02 to 0.15 wt.-% and most preferably from 0.04 to 0.15 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the at least one calcium carbonate-containing filler material of step a) is preheated before contacting step c) is carried out, preferably the at least one calcium carbonate-containing filler material of step a) is preheated at a temperature of from 50 to 200° C., more preferably of from 80 to 200° C., even more preferably of from 90 to 150° C. and most preferably of from 100 to 130° C.
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step b) are provided in a total amount of from 0.1 to 2.5 wt.-%, preferably in an amount of from 0.1 to 2 wt.-%, more preferably in an amount of from about 0.1 to 1.5 wt.-%, even more preferably in an amount of from 0.1 to 1 wt.-% and most preferably in an amount of from 0.2 to 0.8 wt.-% based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the at least one mono-substituted succinic anhydride of step b) consists of succinic anhydride mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C25 and most preferably from C4 to C20 in the substituent.
  • the at least one mono-substituted succinic anhydride of step b) is at least one alkyl mono-substituted succinic anhydride, preferably at least one alkyl mono-substituted succinic anhydride selected from the group comprising ethylsuccinic anhydride, propylsuccinic anhydride, butylsuccinic anhydride, triisobutyl succinic anhydride, pentylsuccinic anhydride, hexylsuccinic anhydride, heptylsuccinic anhydride, octylsuccinic anhydride, nonylsuccinic anhydride, decyl succinic anhydride, dodecyl succinic anhydride, hexadecanyl succinic anhydride, octadecanyl succinic anhydride, and mixtures thereof.
  • the at least one mono-substituted succinic anhydride of step b) is at least one alkenyl mono-substituted succinic anhydride, preferably at least one alkenyl mono-substituted succinic anhydride selected from the group comprising ethenylsuccinic anhydride, propenylsuccinic anhydride, butenylsuccinic anhydride, triisobutenyl succinic anhydride, pentenylsuccinic anhydride, hexenylsuccinic anhydride, heptenylsuccinic anhydride, octenylsuccinic anhydride, nonenylsuccinic anhydride, decenyl succinic anhydride, dodecenyl succinic anhydride, hexadecenyl succinic anhydride, octadecenyl succinic
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step b) are added in contacting step c) in a total amount of from 0.1 to 2 wt.-%, preferably of from 0.2 to 1.5 wt.-% and most preferably of from 0.3 to 1 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material of step a).
  • the at least one mono-substituted succinic acid of step b) is present in an amount of ⁇ 10 mol.-%, based on the molar sum of the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid.
  • contacting step c) is carried out at a temperature of from 30 to 200° C., preferably of from 80 to 150° C. and most preferably of from 110 to 130° C.
  • contacting step c) is carried out in a batch or continuous process, preferably for a period of time from 0.1 to 1000 seconds. It is preferred that contacting step c) is a continuous process and comprises one or several contacting steps and the total contacting time is from 0.1 to 20 s, preferably from 0.5 to 15 s and most preferably from 1 to 10 s.
  • the salty reaction product(s) of the mono-substituted succinic acid and/or the at least one mono-substituted succinic acid formed on the surface of said at least one calcium carbonate-containing filler material in step c) are one or more calcium salts and/or magnesium salts thereof.
  • the process further comprises step d) of contacting the at least one calcium carbonate-containing filler material of step a), in one or more steps, with at least one organic material such as polysiloxanes. It is preferred that contacting step d) is carried out during and/or after contacting step c), preferably after contacting step c). It is further preferred that contacting step d) is carried out at a temperature of from 40 to 200° C., preferably of from 50 to 150° C. and most preferably of from 60 to 120° C.
  • the at least one organic material is added in contacting step d) in an amount of from 100 to 1 000 ppm, preferably from 200 to 800 ppm and most preferably from 300 to 700 ppm, based on the total dry weight of the at least one calcium carbonate-containing filler material of step a).
  • the obtained surface treated filler material product has a water pick-up of from 0.1 to 0.8 mg/g, preferably of from 0.2 to 0.7 mg/g and most preferably of from 0.2 to 0.6 mg/g at a temperature of 23° C. ( ⁇ 2° C).
  • the obtained surface treated filler material product has a volatile onset temperature of ⁇ 250° C., preferably of ⁇ 260° C. and most preferably of ⁇ 270° C.
  • the obtained surface treated filler material product has a hydrophilicity of below 8:2 volumetric ratio of water:ethanol measured at +23° C. ( ⁇ 2° C.) with the sedimentation method.
  • the inventive process for preparing a surface treated filler material product with succinic anhydrides comprises at least the process steps of a), b) and c).
  • step a) of the process of the present invention at least one calcium carbonate-containing filler material is provided.
  • the at least one calcium carbonate-containing filler material in the meaning of the present invention refers to a filler material selected from among ground (or natural) calcium carbonate (GCC), a precipitated calcium carbonate (PCC), a modified calcium carbonate (MCC) and mixtures thereof.
  • GCC ground (or natural) calcium carbonate
  • PCC precipitated calcium carbonate
  • MCC modified calcium carbonate
  • GCC is understood to be a naturally occurring form of calcium carbonate, mined from sedimentary rocks such as limestone or chalk, or from metamorphic marble rocks and processed through a treatment such as grinding, screening and/or fractionizing in wet and/or dry form, for example by a cyclone or classifier.
  • the GCC is selected from the group comprising marble, chalk, dolomite, limestone and mixtures thereof.
  • calcium carbonate of the PCC type include synthetic calcium carbonate products obtained by carbonation of a slurry of calcium hydroxide, commonly referred to in the art as a slurry of lime or milk of lime when derived from finely divided calcium oxide particles in water or by precipitation out of an ionic salt solution.
  • PCC may be rhombohedral and/or scalenohedral and/or aragonitic; preferred synthetic calcium carbonate or precipitated calcium carbonate comprising aragonitic, vateritic or calcite mineralogical crystal forms or mixtures thereof.
  • Modified calcium carbonate in the meaning of the present invention may feature a natural ground or precipitated calcium carbonate with an internal structure modification or a surface-reaction product. According to a preferred embodiment of the present invention, the modified calcium carbonate is a surface-reacted calcium carbonate.
  • the at least one calcium carbonate-containing filler material is marble.
  • the amount of calcium carbonate in the at least one calcium carbonate-containing filler material is at least 80 wt.-%, e.g. at least 95 wt.-%, preferably between 97 and 100 wt.-%, preferably between 98.5 and 99.95 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the at least one calcium carbonate-containing filler material is preferably in the form of a particulate material, and may have a particle size distribution as conventionally employed for the material(s) involved in the type of product to be produced. In general, it is one specific requirement of the present invention that the at least one calcium carbonate-containing filler material has a weight median particle size d 50 value in the range from 0.1 to 7 ⁇ m. For example, the at least one calcium carbonate-containing filler material has a weight median particle size d 50 from 0.25 ⁇ m to 5 ⁇ m and preferably from 0.7 ⁇ m to 4 ⁇ m.
  • the at least one calcium carbonate-containing filler material has a top cut (d 98 ) of ⁇ 15 ⁇ m.
  • the at least one calcium carbonate-containing filler material has a top cut (d 98 ) of ⁇ 12.5 ⁇ m, preferably of ⁇ 10 ⁇ m and most preferably of ⁇ 7.5 ⁇ m.
  • the at least one calcium carbonate-containing filler material has a BET specific surface area of from 0.5 and 150 m 2 /g as measured by the BET nitrogen method according to ISO 9277.
  • the at least one calcium carbonate-containing filler material has a specific surface area (BET) of from 0.5 to 50 m 2 /g, more preferably of from 0.5 to 35 m 2 /g and most preferably of from 0.5 to 15 m 2 /g as measured by the BET nitrogen method according to ISO 9277.
  • the at least one calcium carbonate-containing filler material is preferably a marble having a median particle size diameter d 50 value from 0.1 ⁇ m to 7 ⁇ m, preferably from 0.25 ⁇ m to 5 ⁇ m and most preferably from 0.7 ⁇ m to 4 ⁇ m.
  • the at least one calcium carbonate-containing filler material exhibits a BET specific surface area of from 0.5 to 150 m 2 /g, preferably of from 0.5 to 50 m 2 g, more preferably of from 0.5 to 35 m 2 /g and most preferably of from 0.5 to 15 m 2 /g, measured using nitrogen and the BET method according to ISO 9277.
  • the at least one calcium carbonate-containing filler material is a dry ground material, a material being wet ground and dried or a mixture of the foregoing materials.
  • the grinding step can be carried out with any conventional grinding device, for example, under conditions such that refinement predominantly results from impacts with a secondary body, i.e. in one or more of: a ball mill, a rod mill, a vibrating mill, a roll crusher, a centrifugal impact mill, a vertical bead mill an attrition mill, a pin mill, a hammer mill, a pulveriser, a shredder, a de-clumper, a knife cutter, or other such equipment known to the skilled man.
  • the grinding step may be performed under conditions such that autogenous grinding takes place and/or by horizontal ball milling, and/or other such processes known to the skilled man.
  • the wet processed ground calcium carbonate-containing filler material thus obtained may be washed and dewatered by well known processes, e.g. by flocculation, filtration or forced evaporation prior to drying.
  • the subsequent step of drying may be carried out in a single step such as spray drying, or in at least two steps, e.g.
  • the residual total moisture content of the filler can be measured by the Karl Fischer coulometric titration method, desorbing the moisture in an oven at 195° C. and passing it continuously into the KF coulometer (Mettler Toledo coulometric KF Titrator C30, combined with Mettler oven DO 0337) using dry N 2 at 100 ml/min for 10 min.
  • the residual total moisture content can be determined with a calibration curve and also a blind of 10 min gas flow without a sample can be taken into account.
  • the residual total moisture content may be further reduced by applying a second heating step to the at least one calcium carbonate-containing filler material.
  • the first step may be carried out by heating in a hot current of air, while the second and further drying steps are preferably carried out by an indirect heating in which the atmosphere in the corresponding vessel comprises a surface treatment agent.
  • the at least one calcium carbonate-containing filler material is subjected to a beneficiation step (such as a flotation, bleaching or magnetic separation step) to remove impurities.
  • the at least one calcium carbonate-containing filler material comprises a dry ground calcium carbonate-containing filler material.
  • the at least one calcium carbonate-containing filler material is a material being set ground in a horizontal ball mill, and subsequently dried by using the well known process of spray drying.
  • the at least one calcium carbonate-containing filler material has a residual total moisture content of from 0.01 to 1 wt.-%, preferably from 0.01 to 0.2 wt.-%, more preferably from 0.02 to 0.15 wt.-% and most preferably from 0.04 to 0.15 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the residual total moisture content of the at least one calcium carbonate-containing filler material is preferably of from 0.01 to 0.1 wt.-%, more preferably from 0.02 to 0.08 wt.-% and most preferably from 0.04 to 0.07 wt.-% based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the residual total moisture content of the at least one calcium carbonate-containing filler material is preferably of from 0.01 to 0.2 wt.-%, more preferably from 0.05 to 0.17 wt.-% and most preferably from 0.05 to 0.10 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • step b) of the process of the present invention at least one mono-substituted succinic anhydride and optionally at least one mono-substituted succinic acid are provided.
  • At least one mono-substituted succinic anhydride means that one or more kinds of mono-substituted succinic anhydride may be provided in the process of the present invention.
  • the at least one mono-substituted succinic anhydride may be one kind of mono-substituted succinic anhydride.
  • the at least one mono-substituted succinic anhydride may be a mixture of two or more kinds of mono-substituted succinic anhydride.
  • the at least one mono-substituted succinic anhydride may be a mixture of two or three kinds of mono-substituted succinic anhydride, like two kinds of mono-substituted succinic anhydride.
  • the at least one mono-substituted succinic anhydride is one kind of mono-substituted succinic anhydride.
  • the at least one mono-substituted succinic anhydride represents a surface treatment agent and consists of succinic anhydride mono-substituted with a group selected from any linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C3 to C20 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a linear and aliphatic group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent. Additionally or alternatively, the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a branched and aliphatic group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a linear or branched, alkyl group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a linear alkyl group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a branched alkyl group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • alkyl in the meaning of the present invention refers to a linear or branched, saturated organic compound composed of carbon and hydrogen.
  • alkyl mono-substituted succinic anhydrides are composed of linear or branched, saturated hydrocarbon chains containing a pendant succinic anhydride group.
  • the at least one mono-substituted succinic anhydride is at least one linear or branched alkyl mono-substituted succinic anhydride.
  • the at least one alkyl mono-substituted succinic anhydride is selected from the group comprising ethylsuccinic anhydride, propylsuccinic anhydride, butylsuccinic anhydride, triisobutyl succinic anhydride, pentylsuccinic anhydride, hexylsuccinic anhydride, heptylsuccinic anhydride, octylsuccinic anhydride, nonylsuccinic anhydride, decyl succinic anhydride, dodecyl succinic anhydride, hexadecanyl succinic anhydride, octadecanyl succinic anhydride, and mixtures thereof.
  • butylsuccinic anhydride comprises linear and branched butylsuccinic anhydride(s).
  • linear butylsuccinic anhydride(s) is n-butylsuccinic anhydride.
  • branched butylsuccinic anhydride(s) are iso-butylsuccinic anhydride, sec-butylsuccinic anhydride and/or tert-butylsuccinic anhydride.
  • hexadecanyl succinic anhydride comprises linear and branched hexadecanyl succinic anhydride(s).
  • linear hexadecanyl succinic anhydride(s) is n-hexadecanyl succinic anhydride.
  • branched hexadecanyl succinic anhydride(s) are 14-methylpentadecanyl succinic anhydride, 13-methylpentadecanyl succinic anhydride, 12-methylpentadecanyl succinic anhydride, 11-methylpentadecanyl succinic anhydride, 10-methylpentadecanyl succinic anhydride, 9-methylpentadecanyl succinic anhydride, 8-methylpentadecanyl succinic anhydride, 7-methylpentadecanyl succinic anhydride, 6-methylpentadecanyl succinic anhydride, 5-methylpentadecanyl succinic anhydride, 4-methylpentadecanyl succinic anhydride, 3-methylpentadecanyl succinic anhydride, 2-methylpentadecanyl succinic anhydride, 1-methylpentadecanyl succinic anhydride, 13
  • octadecanyl succinic anhydride comprises linear and branched octadecanyl succinic anhydride(s).
  • linear octadecanyl succinic anhydride(s) is n-octadecanyl succinic anhydride.
  • branched hexadecanyl succinic anhydride(s) are 16-methylheptadecanyl succinic anhydride, 15-methylheptadecanyl succinic anhydride, 14-methylheptadecanyl succinic anhydride, 13-methylheptadecanyl succinic anhydride, 12-methylheptadecanyl succinic anhydride, 11-methylheptadecanyl succinic anhydride, 10-methylheptadecanyl succinic anhydride, 9-methylheptadecanyl succinic anhydride, 8-methylheptadecanyl succinic anhydride, 7-methylheptadecanyl succinic anhydride, 6-methylheptadecanyl succinic anhydride, 5-methylheptadecanyl succinic anhydride, 4-methylheptadecanyl succinic anhydride, 3-methylheptadecanyl succinic anhydride
  • the at least one alkyl mono-substituted succinic anhydride is selected from the group comprising butylsuccinic anhydride, hexylsuccinic anhydride, heptylsuccinic anhydride, octylsuccinic anhydride, hexadecanyl succinic anhydride, octadecanyl succinic anhydride, and mixtures thereof.
  • the at least one mono-substituted succinic anhydride is one kind of alkyl mono-substituted succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is butylsuccinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is hexylsuccinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is heptylsuccinic anhydride or octylsuccinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is hexadecanyl succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is linear hexadecanyl succinic anhydride such as n-hexadecanyl succinic anhydride or branched hexadecanyl succinic anhydride such as 1-hexyl-2-decanyl succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is octadecanyl succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is linear octadecanyl succinic anhydride such as n-octadecanyl succinic anhydride or branched octadecanyl succinic anhydride such as iso-octadecanyl succinic anhydride or 1-octyl-2-decanyl succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is butylsuccinic anhydride such as n-butylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkyl mono-substituted succinic anhydrides.
  • the at least one mono-substituted succinic anhydride is a mixture of two or three kinds of alkyl mono-substituted succinic anhydrides.
  • the at least one mono-substituted succinic anhydride consists of succinic anhydride mono-substituted with one group being a linear or branched alkenyl group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • alkenyl in the meaning of the present invention refers to a linear or branched, unsaturated organic compound composed of carbon and hydrogen. Said organic compound further contains at least one double bond in the substituent, preferably one double bond.
  • alkenyl mono-substituted succinic anhydrides are composed of linear or branched, unsaturated hydrocarbon chains containing a pendant succinic anhydride group. It is appreciated that the term “alkenyl” in the meaning of the present invention includes the cis and trans isomers.
  • the at least one mono-substituted succinic anhydride is at least one linear or branched alkenyl mono-substituted succinic anhydride.
  • the at least one alkenyl mono-substituted succinic anhydride is selected from the group comprising ethenylsuccinic anhydride, propenylsuccinic anhydride, butenylsuccinic anhydride, triisobutenyl succinic anhydride, pentenylsuccinic anhydride, hexenylsuccinic anhydride, heptenylsuccinic anhydride, octenylsuccinic anhydride, nonenylsuccinic anhydride, decenyl succinic anhydride, dodecenyl succinic anhydride, hexadecenyl succinic anhydride, octadecenyl succinic
  • hexadecenyl succinic anhydride comprises linear and branched hexadecenyl succinic anhydride(s).
  • linear hexadecenyl succinic anhydride(s) is n-hexadecenyl succinic anhydride such as 14-hexadecenyl succinic anhydride, 13-hexadecenyl succinic anhydride, 12-hexadecenyl succinic anhydride, 11-hexadecenyl succinic anhydride, 10-hexadecenyl succinic anhydride, 9-hexadecenyl succinic anhydride, 8-hexadecenyl succinic anhydride, 7-hexadecenyl succinic anhydride, 6-hexadecenyl succinic anhydride, 5-hexadeceny
  • branched hexadecenyl succinic anhydride(s) are 14-methyl-9-pentadecenyl succinic anhydride, 14-methyl-2-pentadecenyl succinic anhydride, 1-hexyl-2-decenyl succinic anhydride and/or iso-hexadecenyl succinic anhydride.
  • octadecenyl succinic anhydride comprises linear and branched octadecenyl succinic anhydride(s).
  • linear octadecenyl succinic anhydride(s) is n-octadecenyl succinic anhydride such as 16-octadecenyl succinic anhydride, 15-octadecenyl succinic anhydride, 14-octadecenyl succinic anhydride, 13-octadecenyl succinic anhydride, 12-octadecenyl succinic anhydride, 11-octadecenyl succinic anhydride, 10-octadecenyl succinic anhydride, 9-octadecenyl succinic anhydride, 8-octadecenyl succinic anhydride
  • branched octadecenyl succinic anhydride(s) are 16-methyl-9-heptadecenyl succinic anhydride, 16-methyl-7-heptadecenyl succinic anhydride, 1-octyl-2-decenyl succinic anhydride and/or iso-octadecenyl succinic anhydride.
  • the at least one alkenyl mono-substituted succinic anhydride is selected from the group comprising hexenylsuccinic anhydride, octenylsuccinic anhydride, hexadecenyl succinic anhydride, octadecenyl succinic anhydride, and mixtures thereof.
  • the at least one mono-substituted succinic anhydride is one alkenyl mono-substituted succinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is hexenylsuccinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is octenylsuccinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is hexadecenyl succinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is linear hexadecenyl succinic anhydride such as n-hexadecenyl succinic anhydride or branched hexadecenyl succinic anhydride such as 1-hexyl-2-decenyl succinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is octadecenyl succinic anhydride.
  • the one alkyl mono-substituted succinic anhydride is linear octadecenyl succinic anhydride such as n-octadecenyl succinic anhydride or branched octadencenyl succinic anhydride such iso-octadecenyl succinic anhydride, or 1-octyl-2-decenyl succinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is linear octadecenyl succinic anhydride such as n-octadecenyl succinic anhydride.
  • the one alkenyl mono-substituted succinic anhydride is linear octensylsuccinic anhydride such as n-octenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is one alkenyl mono-substituted succinic anhydride
  • the one alkenyl mono-substituted succinic anhydride is present in an amount of ⁇ 95 wt.-% and preferably of ⁇ 96.5 wt.-%, based on the total weight of the at least one mono-substituted succinic anhydride provided in step b).
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides.
  • the at least one mono-substituted succinic anhydride is a mixture of two or three kinds of alkenyl mono-substituted succinic anhydrides.
  • one alkenyl mono-substituted succinic anhydride is linear or branched octadecenyl succinic anhydride, while each further alkenyl mono-substituted succinic anhydride is selected from ethenylsuccinic anhydride, propenylsuccinic anhydride, butenylsuccinic anhydride, pentenylsuccinic anhydride, hexenylsuccinic anhydride, heptenylsuccinic anhydride, nonenylsuccinic anhydride, hexadecenyl succinic anhydride and mixtures thereof.
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides, wherein one alkenyl mono-substituted succinic anhydride is linear octadecenyl succinic anhydride and each further alkenyl mono-substituted succinic anhydride is selected from ethenylsuccinic anhydride, propenylsuccinic anhydride, butenylsuccinic anhydride, pentenylsuccinic anhydride, hexenylsuccinic anhydride, heptenylsuccinic anhydride, nonenylsuccinic anhydride, hexadecenyl succinic anhydride and mixtures thereof.
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides, wherein one alkenyl mono-substituted succinic anhydride is branched octadecenyl succinic anhydride and each further alkenyl mono-substituted succinic anhydride is selected from ethyenylsuccinic anhydride, propenylsuccinic anhydride, butenylsuccinic anhydride, pentenylsuccinic anhydride, hexenylsuccinic anhydride, heptenylsuccinic anhydride, nonenylsuccinic anhydride, hexadecenyl succinic anhydride and mixtures thereof.
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides comprising one or more hexadecenyl succinic anhydride, like linear or branched hexadecenyl succinic anhydride(s), and one or more octadecenyl succinic anhydride, like linear or branched octadecenyl succinic anhydride(s).
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides comprising linear hexadecenyl succinic anhydride(s) and linear octadecenyl succinic anhydride(s).
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides comprising branched hexadecenyl succinic anhydride(s) and branched octadecenyl succinic anhydride(s).
  • the one or more hexadecenyl succinic anhydride is linear hexadecenyl succinic anhydride like n-hexadecenyl succinic anhydride and/or branched hexadecenyl succinic anhydride like 1-hexyl-2-decenyl succinic anhydride.
  • the one or more octadecenyl succinic anhydride is linear octadecenyl succinic anhydride like n-octadecenyl succinic anhydride and/or branched octadecenyl succinic anhydride like iso-octadecenyl succinic anhydride and/or 1-octyl-2-decenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides, it is appreciated that one alkenyl mono-substituted succinic anhydride is present in an amount of from 20 to 60 wt.-% and preferably of from 30 to 50 wt.-%, based on the total weight of the at least one mono-substituted succinic anhydride provided in step b).
  • the at least one mono-substituted succinic anhydride is a mixture of two or more kinds of alkenyl mono-substituted succinic anhydrides comprising one or more hexadecenyl succinic anhydride(s), like linear or branched hexadecenyl succinic anhydride(s), and one or more octadecenyl succinic anhydride(s), like linear or branched hexadecenyl succinic anhydride(s), it is preferred that the one or more octadecenyl succinic anhydride(s) is present in an amount of from 20 to 60 wt.-% and preferably of from 30 to 50 wt.-%, based on the total weight of the at least one mono-substituted succinic anhydride provided in step b).
  • the at least one mono-substituted succinic anhydride may be a mixture of at least one alkyl mono-substituted succinic anhydrides and at least one alkenyl mono-substituted succinic anhydrides.
  • the at least one mono-substituted succinic anhydride is a mixture of at least one alkyl mono-substituted succinic anhydrides and at least one alkenyl mono-substituted succinic anhydrides
  • the alkyl substituent of the at least one alkenyl mono-substituted succinic anhydrides and the alkenyl substituent of the of at least one alkenyl mono-substituted succinic anhydrides are preferably the same.
  • the at least one mono-substituted succinic anhydrides is a mixture of ethylsuccinic anhydride and ethylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of propylsuccinic anhydride and propenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of butylsuccinic anhydride and butenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of triisobutyl succinic anhydride and triisobutenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of pentylsuccinic anhydride and pentenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of hexylsuccinic anhydride and hexenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of heptylsuccinic anhydride and heptenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of octylsuccinic anhydride and octensylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of nonylsuccinic anhydride and nonenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of decyl succinic anhydride and decenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of dodecyl succinic anhydride and dodecenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of hexadecanyl succinic anhydride and hexadecenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of linear hexadecanyl succinic anhydride and linear hexadecenyl succinic anhydride or a mixture of branched hexadecanyl succinic anhydride and branched hexadecenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of octadecanyl succinic anhydride and octadecenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of linear octadecanyl succinic anhydride and linear octadecenyl succinic anhydride or a mixture of branched octadecanyl succinic anhydride and branched octadecenyl succinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of nonylsuccinic anhydride and nonenylsuccinic anhydride.
  • the at least one mono-substituted succinic anhydride is a mixture of at least one alkyl mono-substituted succinic anhydrides and at least one alkenyl mono-substituted succinic anhydride and the at least one alkenyl mono-substituted succinic anhydride is between 90:10 and 10:90 (wt.-%/wt.-%).
  • the weight ratio between the at least one alkyl mono-substituted succinic anhydride and the at least one alkenyl mono-substituted succinic anhydride is between 70:30 and 30:70 (wt.-%/wt.-%) or between 60:40 and 40:60.
  • At least one mono-substituted succinic acid is provided according to step b) of the inventive process.
  • At least one mono-substituted succinic acid means that one or more kinds of mono-substituted succinic acid may be provided in the process of the present invention.
  • the at least one mono-substituted succinic acid may be one kind of mono-substituted succinic acid.
  • the at least one mono-substituted succinic acid may be a mixture of two or more kinds of mono-substituted succinic acid.
  • the at least one mono-substituted succinic acid may be a mixture of two or three kinds of mono-substituted succinic acid, like two kinds of mono-substituted succinic acid.
  • the at least one mono-substituted succinic acid is one kind of mono-substituted succinic acid.
  • the at least one mono-substituted succinic acid represents a surface treatment agent and consists of succinic acid mono-substituted with a group selected from any linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30 in the substituent.
  • the at least one mono-substituted succinic acid consists of succinic acid mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C3 to C20 in the substituent.
  • the at least one mono-substituted succinic acid consists of succinic acid mono-substituted with a group selected from a linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid may comprise the same or different substituent.
  • the succinic acid molecule of the at least one mono-substituted succinic acid and the succinic anhydride molecule of the at least one mono-substituted succinic anhydride are mono-substituted with the same group selected from any linear, branched, aliphatic and cyclic group having a total amount of carbon atoms from C2 to C30, preferably from C3 to C20 and most preferably from C4 to C18 in the substituent.
  • the at least one mono-substituted succinic anhydride is provided in combination with at least one mono-substituted succinic acid, the at least one mono-substituted succinic acid is present in an amount of ⁇ 10 mol.-%, based on the molar sum of the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid.
  • the at least one mono-substituted succinic acid is present in an amount of ⁇ 5 mo.-%, preferably of ⁇ 2.5 mol.-% and most preferably of ⁇ 1 mol.-%, based on the molar sum of the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid.
  • At least one mono-substituted succinic anhydride and at least one mono-substituted succinic acid are provided in method step b).
  • At least one mono-substituted succinic anhydride and at least one mono-substituted succinic acid are provided in method step b), the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid are preferably provided as a blend.
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid are provided in a total amount of from 0.1 to 3 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid are provided in an amount of from 0.1 to 2.5 wt.-%, preferably in an amount of from 0.1 to 2 wt.-%, more preferably in an amount of from 0.1 to 1.5 wt.-%, even more preferably in an amount of from 0.1 to 1 wt.-% and most preferably in an amount of from 0.2 to 0.8 wt.-% based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of the present invention are preferably provided in a quantity such that the total weight of said at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid on the surface of the at least one calcium carbonate-containing filler material is less than 5 mg/m 2 of the at least one calcium carbonate-containing filler material provided in step (a).
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of the present invention are preferably provided in a quantity such that the total weight of said at least one mono-substituted succinic anhydride and mono-substituted succinic acid and/or salty reaction product(s) thereof on the surface of the at least one calcium carbonate-containing filler material is less than 4.5 mg/m 2 and most preferably less than 4.0 mg/m 2 of the at least one calcium carbonate-containing filler material provided in step (a).
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of the present invention are preferably provided in a quantity such that the total weight of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid on the surface of the surface treated filler material product is from 0.1 to 5 mg/m 2 , more preferably from 0.2 to 4 mg/m 2 and most preferably from 1 to 4 mg/m 2 of the at least one calcium carbonate-containing filler material provided in step a).
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b) of the inventive process are provided as a liquid at room temperature, i.e. said at least one mono-substituted succinic anhydride features a viscosity of less than 5 000, preferably of less than 2 500, more preferably of less than 1,000 mPa ⁇ s and most preferably of less than 500 mPa ⁇ s at +20° C. ( ⁇ 2° C.), when measured with the appropriate equipment e.g.
  • Physica MCR 300 rheometer (Paar Physica) equipped with the measuring cell TEZ 150 P-C and the CC 28.7 measuring system at a shear rate of 5 s ⁇ 1 and at +20° C. ( ⁇ 2° C.).
  • step c) of the inventive process the at least one calcium carbonate-containing filler material of step a) is contacted under mixing, in one or more steps, with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step b).
  • Step c) of contacting the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid takes place under mixing conditions.
  • the skilled man will adapt these mixing conditions (such as the configuration of mixing pallets and mixing speed) according to his process equipment.
  • the inventive process may be a continuous process.
  • the at least one calcium carbonate-containing filler material is contacted with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b) in one step, wherein said at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid is preferably added in one portion.
  • the inventive process may be a batch process, i.e. the at least one calcium carbonate-containing filler material is contacted with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid in more than one steps, wherein said at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid is preferably added in about equal portions.
  • contacting step (c) is carried out in a batch or continuous process for a period of time from 0.1 to 1000 s.
  • contacting step (c) is a continuous process and comprises one or several contacting steps and the total contacting time is from 0.1 to 20 s, preferably from 0.5 to 15 s and most preferably from 1 to 10 s.
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step b) When implementing the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step b), it features a workable viscosity at about room temperature, i.e. the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid is in a liquid state. Therefore, the contacting of the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid may be carried out at lower treatment temperatures than that used in processes implementing fatty acids and/or fatty acid salts having at least 10 chain carbon atoms. It is thus one requirement of the present invention that the temperature is adjusted during contacting step c) such that
  • a “molten” or “liquid” state in the meaning of the present invention is defined as the state in which a material is entirely liquid, in other words is entirely melted.
  • a substance is qualified as being molten as of the moment following melting when the temperature begins to rise, as observed on a curve plotting temperature versus energy input obtained by Dynamic Scanning Calorimetry, DSC, (DIN 51005: 1983-11).
  • the temperature before and/or during contacting step c) is adjusted such that the temperature is at least 2° C. above the melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the temperature before contacting step c) is adjusted such that the temperature is at least 2° C. above the melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the temperature before and during contacting step c) is adjusted such that the temperature is at least 2° C. above the melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid refers to the melting point of the at least one mono-substituted succinic anhydride or, if the at least one mono-substituted succinic acid is present, to the blend comprising the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid.
  • the temperature before and/or during contacting step c) is adjusted such that the temperature is at least 5° C., preferably, at least 8° C. and most preferably at least 10° C. above the melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the temperature before and/or during contacting step c) is adjusted such that the temperature is from 2 to 50° C., preferably from 5 to 40° C., more preferably from 8 to 30° C. and most preferably from 10 to 20° C. above the melting point of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the contacting of the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid is thus carried out at a treatment temperature of below 200° C.
  • the contacting of at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the operational at least one mono-substituted succinic acid is carried out at a treatment temperature of from 30 to 200° C., preferably of from 80 to 150° C. and most preferably of from about 110 to 130° C.
  • the treatment time for carrying out the contacting of the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b) is carried out for a period of 1 000 s or less, preferably for a period of 500 s or less, more preferably for a period of 250 s or less and most preferably from 0.1 to 1 000 s.
  • contacting step (c) is carried out for a period of time from 0.1 to 20 s, preferably from 0.5 to 15 s and most preferably from 1 to 10 s.
  • the length of contacting the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b) is determined by the treatment temperature applied during said contacting.
  • the treatment temperature applied during said contacting For example, where a treatment temperature of about 200° C. is applied, the treatment time is as short as, for example, about 0.1. If a treatment temperature of about 90° C. is applied, the treatment time can be as long as, for example, about 1 000 s.
  • At least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid are added in contacting step c) in an amount of from 0.1 to 2 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material of step a).
  • the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid is added in contacting step c) in an amount of from 0.2 to 1.5 wt.-% or of from 0.3 to 1 wt.-%, based on the total dry weight of the at least one calcium carbonate-containing filler material of step a).
  • the at least one calcium carbonate-containing filler material is preheated, i.e. activated, before contacting step c) is carried out. That is to say, the at least one calcium carbonate-containing filler material is treated at a temperature of from 50 to 200° C., preferably of from about 80 to 200° C., more preferably of from 90 to 150° C. and most preferably of from 100 to 130° C. before contacting step c) is carried out.
  • the treatment time for carrying out the preheating of the at least one calcium carbonate-containing filler material is carried out for a period of 30 min or less, preferably for a period of 20 min or less and more preferably for a period of 15 min or less.
  • the preheating of the at least one calcium carbonate-containing filler material is carried out at a temperature that is of about equal to the temperature implemented during contacting step c).
  • equal temperature in the meaning of the present invention refers to a preheating temperature that is at most 20° C., preferably at most 15° C., more preferably 10° C. and most preferably at most 5° C. below or above the temperature implemented during contacting step c).
  • the process further comprises step (d) of contacting the at least one calcium carbonate-containing filler material of step (a), in one or more steps, with at least one organic material such as polysiloxanes.
  • the inventive process further comprises contacting step (d), such contacting of the at least one calcium carbonate-containing filler material with the at least one organic material may be carried out during and/or after the contacting of the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b).
  • such contacting with the at least one organic material is carried out after the contacting of the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid of step (b).
  • contacting step d) is preferably carried out at temperatures of from 40 to 200° C.
  • contacting step d) is carried out at temperature of from 50 to 150° C. or from 60 to 120° C.
  • the at least one organic material such as polysiloxane is added in contacting step d) in an amount of from 100 to 1 000 ppm, preferably from 200 to 800 ppm and most preferably from 300 to 700 ppm, based on the total dry weight of the at least one calcium carbonate-containing filler material of step a)
  • the at least one organic material such as polysiloxane is preferably added such that the amount of the at least one organic material on the surface of the surface treated filler material product, i.e. in the treatment layer, is less than 0.1 mg, more preferably less than 0.08 mg and most preferably less than 0.07 mg of the total weight of the at least organic material/m 2 of the at least one calcium carbonate-containing filler material provided in step a).
  • the treatment time for carrying out the contacting of the at least one calcium carbonate-containing filler material with the at least one organic material is carried out for a period of 0.00166 to 166.66 min.
  • the contacting of the at least one calcium carbonate-containing filler material with the at least one organic material is carried out for a contacting time from 0.0166 to 20 min, preferably from 0.0833 to 15 min and most preferably from 0.166 to 10 min.
  • the length of contacting step d) is determined by the treatment temperature applied during said contacting.
  • the treatment time is as short as, for example from about 0.166 to 1 min.
  • the treatment layer formed on the surface of the at least one calcium carbonate-containing filler material comprises the at least one mono-substituted succinic anhydride provided in step b) and the optional at least one mono-substituted succinic acid, optionally provided in step b) and/or obtained as reaction product from contacting the calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride(s), and/or salty reaction product(s) thereof obtained from contacting the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the treatment layer of the surface treated filler material product preferably comprises salty reaction product(s) of the mono-substituted succinic acid and/or the at least one mono-substituted succinic anhydride formed on the surface of said at least one calcium carbonate-containing filler material in step c).
  • salty reaction product(s) such as one or more calcium salts and/or magnesium salts of the at least one mono-substituted succinic acid and/or the at least one mono-substituted succinic anhydride.
  • the treatment layer of the surface treated filler material product further comprises at least one organic material such as polysiloxane.
  • the at least one calcium carbonate-containing filler material product obtained in process step c) and optionally after step d), i.e. the surface treated filler material product comprises, preferably consists of, at least one calcium carbonate-containing filler material and a treatment layer comprising at least one mono-substituted succinic anhydride and at least one mono-substituted succinic acid and/or salty reaction product(s) thereof.
  • the treatment layer is formed on the surface of said at least one calcium carbonate-containing filler material of step a).
  • the treatment layer on the surface of the at least one calcium carbonate-containing filler material comprises at least one mono-substituted succinic acid
  • the at least one mono-substituted succinic acid is formed from the applied at least one mono-substituted succinic anhydride. That is to say, the substituent of the at least one mono-substituted succinic acid and the substituent of the at least one mono-substituted succinic anhydride are the same.
  • the at least one mono-substituted succinic acid is provided in a blend together with the at least one mono-substituted succinic anhydride.
  • the treatment layer formed on the surface of the at least one calcium carbonate-containing filler material comprises the at least one mono-substituted succinic anhydride provided in step b) and at least one mono-substituted succinic acid or salty reaction product(s) thereof obtained from contacting the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the treatment layer formed on the surface of the at least one calcium carbonate-containing filler material comprises the at least one mono-substituted succinic anhydride provided in step b) and at least one mono-substituted succinic acid and salty reaction product(s) thereof obtained from contacting the at least one calcium carbonate-containing filler material with the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the treatment layer is preferably characterized in that the total weight of the at least one mono-substituted succinic anhydride and at least one mono-substituted succinic acid and/or salty reaction product(s) thereof on the surface of the surface treated filler material product is from 0.1 to 5 mg/m 2 , more preferably from 0.2 to 4 mg/m 2 and most preferably from 1 to 4 mg/m 2 of the at least one calcium carbonate-containing filler material provided in step a).
  • the treatment layer is preferably characterized in that the total weight of the at least one mono-substituted succinic anhydride and at least one mono-substituted succinic acid and/or salty reaction product(s) thereof on the surface of the surface treated filler material product is from 0.05 to 1 wt.-%/m 2 , more preferably from 0.1 to 0.5 wt.-%/m 2 and most preferably from 0.15 to 0.25 wt.-%/m 2 of the at least one calcium carbonate-containing filler material provided in step a)
  • the treatment layer is characterized in that the total weight of the at least one mono-substituted succinic anhydride and mono-substituted succinic acid and/or salty reaction product(s) thereof and the optional at least one organic material on the surface of the surface treated filler material product is from 0.1 to 5 mg/m 2 , more preferably from 0.25 to 4.5 mg/m 2 and most preferably from 1.0 to 4.0 mg/m 2 of the at least one calcium carbonate-containing material provided in step a).
  • the treatment layer of the surface treated filler material product comprises the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid and/or salty reaction product(s) thereof in a specific molar ratio.
  • the molar ratio of the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid to the salt reaction product(s) thereof is from 99.9:0.1 to 0.1:99.9, preferably from 70:30 to 90:10.
  • the wording “molar ratio of the at least one mono-substituted succinic anhydride and the at least one mono-substituted succinic acid to the salty reaction product(s) thereof” in the meaning of the present invention refers to the sum of the molecular weight of the at least one mono-substituted succinic anhydride and the sum of the molecular weight of the at least one mono-substituted succinic acid to the sum of the molecular weight of the mono-substituted succinic anhydride molecules in the salty reaction products thereof and the sum of the molecular weight of the mono-substituted succinic acid molecules in the salt reaction products thereof.
  • the obtained surface treated filler material product comprises the treatment layer in an amount of from 0.1 to 2.5 wt.-%, preferably in an amount of from 0.1 to 2 wt.-%, more preferably in an amount of from 0.1 to 1.5 wt.-%, even more preferably in an amount of from 0.1 to 1 wt.-% and most preferably in an amount of from 0.2 to 0.8 wt.-% based on the total dry weight of the at least one calcium carbonate-containing filler material.
  • the resulting surface treated filler material product obtained according to the present invention has excellent surface characteristics in comparison to mineral fillers treated with fatty acids and/or fatty acid salts having at least 10 chain carbon atoms, i.e. without the implementation of the at least one mono-substituted succinic anhydride and the optional at least one mono-substituted succinic acid.
  • the surface treated filler material product obtained by the inventive process features a volatile onset temperature of ⁇ 250° C.
  • the surface treated filler material product obtained by the inventive process features a volatile onset temperature of ⁇ 260° C. or of ⁇ 270° C.
  • the surface treated filler material product obtained by the inventive process features a total volatiles between 25 and 350° C. of less than 0.25%, and preferably of less than 0.23% by mass, e.g. of from 0.04 to 0.21% by mass, preferably from 0.08 to 0.15% by mass, more preferably from 0.1 to 0.12% by mass.
  • the surface treated filler material product obtained by the inventive process features a low moisture pick up susceptibility. It is preferred that the moisture pick up susceptibility of the surface treated filler material product obtained by the inventive process is such that its total surface moisture level is less than 0.8 mg/g of dry calcium carbonate-containing filler material, at a temperature of about +23° C. ( ⁇ 2° C.).
  • the surface treated filler material product obtained by the inventive process has a moisture pick up susceptibility of from 0.1 to 0.8 mg/g, more preferably of from 0.2 to 0.7 mg/g and most preferably of from 0.2 to 0.6 mg/g of dry calcium carbonate-containing material after at a temperature of +23 C. ( ⁇ 2° C.).
  • the surface treated filler material product obtained by the inventive process has a hydrophilicity of below 8:2 volumetric ratio of water:ethanol measured at +23° C. ( ⁇ 2° C.) with the sedimentation method.
  • the surface treated filler material product has a hydrophilicity of below 7:3 volumetric ratio of water:ethanol measured at +23° C. ( ⁇ 2° C.) with the sedimentation method.
  • one aspect of the present invention relates to the surface treated filler material product comprising
  • the surface treated filler material product is obtainable by the process of the present invention.
  • the at least one calcium carbonate-containing filler material the at least one mono-substituted succinic anhydride, the at least one mono-substituted succinic acid, the salty reaction product(s) thereof, the surface treated filler material product, and preferred embodiments thereof, reference is made to the comments provided above when discussing process steps a), b) and c), and optional step d).
  • the surface treated filler material product is thus obtained is advantageously implemented in polymer composition comprising at least one polymeric resin and from 1 to 85 wt.-% of the surface treated filler material product.
  • the polymer composition comprises at least one polymeric resin.
  • the polymer resin represents the backbone of the composition and provides strength, flexibility, toughness and durability to the final fiber and/or filament and/or film and/or thread.
  • the at least one polymeric resin according to the present invention is not restricted to a specific resin material as long as the polymer composition is suitable for the preparation of fibers and/or filaments and/or films and/or thread.
  • the at least one polymeric resin is at least one thermoplastic polymer.
  • the at least one polymeric resin is a thermoplastic polymer selected from the group comprising homopolymers and/or copolymers of polyolefins, polyamides, halogen-containing polymers and/or polyesters.
  • the at least one polymeric resin is a polyamide
  • the at least one polymeric resin is preferably nylon.
  • the at least one polymeric resin is a homopolymer and/or copolymer of a polyolefin.
  • the at least one polymeric resin is a homopolymer and a copolymer of a polyolefin.
  • the at least one polymeric resin is a homopolymer or a copolymer of a polyolefin.
  • the at least one polymeric resin is preferably a homopolymer of a polyolefin.
  • the polyolefin can be polyethylene and/or polypropylene and/or polybutylene. Accordingly, if the polyolefin is polyethylene, the polyolefin is selected from the group comprising homopolymers and/or copolymers of polyethylene like high-density polyethylene (HDPE), medium-density polyethylene (MDPE), low-density polyethylene (LDPE), very low-density polyethylene (VLDPE), linear low-density polyethylene (LLDPE).
  • HDPE high-density polyethylene
  • MDPE medium-density polyethylene
  • LDPE low-density polyethylene
  • VLDPE very low-density polyethylene
  • LLDPE linear low-density polyethylene
  • the polyolefin is a homopolymer and/or copolymer of polyethylene.
  • the expression homopolymer of polyethylene used in the present invention relates to polyethylene comprising a polyethylene that consists substantially, i.e. of more than 99.7 wt.-%, still more preferably of at least 99.8 wt.-%, based on the total weight of the polyethylene, of ethylene units. For example, only ethylene units in the homopolymer of polyethylene are detectable.
  • the at least one polymeric resin of the polymer composition comprises a copolymer of polyethylene
  • the polyethylene contains units derivable from ethylene as major components.
  • the copolymer of polyethylene comprises at least 55 wt.-% units derivable from ethylene, more preferably at least 60 wt-% of units derived from ethylene, based on the total weight of the polyethylene.
  • the copolymer of polyethylene comprises 60 to 99.5 wt.-%, more preferably 90 to 99 wt.-%, units derivable from ethylene, based on the total weight of the polyethylene.
  • the comonomers present in such copolymer of polyethylene are C 3 to C 10 ⁇ -olefins, preferably 1-butene, 1-hexene and 1-octene, the latter especially preferred.
  • the polyolefin is a homopolymer and/or copolymer of polypropylene.
  • homopolymer of polypropylene as used throughout the instant invention relates to a polypropylene that consists substantially, i.e. of more than 99 wt.%, still more preferably of at least 99.5 wt.-%, like of at least 99.8 wt.-%, based on the total weight of the polypropylene, of propylene units. In a preferred embodiment only propylene units are detectable in the homopolymer of polypropylene.
  • the polypropylene preferably contains units derivable from propylene as major components.
  • the copolymer of polypropylene preferably comprises, preferably consists of, units derived from propylene and C 2 and/or at least one C 4 to C 10 ⁇ -olefin.
  • the copolymer of polypropylene comprises, preferably consists of, units derived from propylene and at least one ⁇ -olefin selected from the group consisting of ethylene, 1-butene, 1-pentene, 1-hexene and 1-octene.
  • the copolymer of polypropylene comprises, preferably consists of, units derived from propylene and ethylene.
  • the units derivable from propylene constitutes the main part of the polypropylene, i.e. at least 60 wt.-%, preferably of at least 70 wt.-%, more preferably of from 80 wt.-%, still more preferably of from 60 to 99 wt.-%, yet more preferably of from 70 to 99 wt.-% and most preferably of from 80 to 99 wt.-%, based on the total weight of the polypropylene.
  • the amount of units derived from C 2 and/or at least one C 4 to C 10 ⁇ -olefin in the copolymer of polypropylene is in the range of 1 to 40 wt.-%, more preferably in the range of 1 to 30 wt.-% and most preferably in the range of 1 to 20 wt.-%, based on the total weight of the copolymer of polypropylene.
  • the amount of ethylene is preferably in the range of 1 to 20 wt.-%, preferably in the range of 1 to 15 wt.-% and most preferably in the range of 1 to 10 wt.-%, based on the total weight of the copolymer of polypropylene.
  • the amount of propylene is preferably in the range of 80 to 99 wt.-%, preferably in the range of 85 to 99 wt.-% and most preferably in the range of 90 to 99 wt.-%, based on the total weight of the copolymer of polypropylene.
  • the polyolefin is a homopolymer and/or copolymer of polybutylene.
  • homopolymer of polybutylene as used throughout the instant invention relates to a polybutylene that consists substantially, i.e. or more than 99 wt.-%, still more preferably of at least 99.5 wt.-%, like of at least 99.8 wt.-%, based on the total weight of the polybutylene, of butylene units. In a preferred embodiment only butylene units are detectable in the homopolymer of polybutylene.
  • the polybutylene preferably contains units derivable from butylene as major components.
  • the copolymer of polybutylene preferably comprises, preferably consists of, units derived from butylene and C 2 and/or C 3 and/or at least one C 5 to C 10 ⁇ -olefin.
  • the copolymer of polybutylene comprises, preferably consists of, units derived from butylene and at least one ⁇ -olefin selected from the group consisting of ethylene, 1-propene, 1-pentene, 1-hexene and 1-octene.
  • the copolymer of polybutylene comprises, preferably consists of, units derived from butylene and ethylene.
  • the units derivable from butylene constitutes the main part of the polybutylene, i.e. at least 60 wt.-%, preferably of at least 70 wt.-%, more preferably of at least 80 wt.-%, still more preferably of from 60 to 99 wt.-%, yet more preferably of from 70 to 99 wt.-% and most preferably of from 80 to 99 wt.-%, based on the total weight of the polybutylene.
  • the amount of units derived from C 2 and/or C 3 and/or at least one C 5 to C 10 ⁇ -olefin in the copolymer of polybutylene is in the range of 1 to 40 wt.-%, more preferably in the range of 1 to 30 wt.-% and most preferably in the range of 1 to 20 wt.-%, based on the total weight of the copolymer of polybutylene.
  • the at least one polymeric resin is a homopolymer and/or copolymer of a halogen-containing polymer
  • the at least one polymeric resin is preferably selected from polyvinylchloride (PVC), polyvinylidene chloride (PVDC), polyvinylidene fluoride (PVDF) and polytetrafluoroethylene (PTFE).
  • the at least one polymeric resin is a homopolymer and/or copolymer of polyester
  • the at least one polymeric resin is preferably selected from polyethylene terephthalate (PET), polytrimetethylene terephthalate (PTT), polybutylene terephthalate (PBT), polyethylene aphthalate (PEN), but also degradable polyesters, such as polylactic acid (polylactide, PLA).
  • the at least one polymeric resin is a homopolymer of polyethylene and/or polypropylene and/or polybutylene.
  • the at least one polymeric resin is a homopolymer of polyethylene and polypropylene.
  • the at least one polymeric resin is a homopolymer of polyethylene or polypropylene.
  • the at least one polymeric resin is a homopolymer of polypropylene.
  • At least one polymeric resin means that one or more kinds of polymeric resin may be present in the inventive polymer composition.
  • Full or partially based bio-based polymers are derived from renewable biomass sources, such as vegetable fats and oils, corn starch, pea starch or microbiota, aliphatic biopolyesters such as polyhydroxyalkanoates (PHA), polyhydroxybutyrate (PHB), polyhydroxyvalerate (PHV), polyhydroxyhexanoate (PHH), or polyesters such as polyethylene terephthalate (PET).
  • renewable biomass sources such as vegetable fats and oils, corn starch, pea starch or microbiota
  • aliphatic biopolyesters such as polyhydroxyalkanoates (PHA), polyhydroxybutyrate (PHB), polyhydroxyvalerate (PHV), polyhydroxyhexanoate (PHH), or polyesters such as polyethylene terephthalate (PET).
  • Blends, Mixtures, Alloys and combinations of two or more of the above mentioned polymers can be used as well in the present invention.
  • the at least one polymeric resin may be a mixture of two or more kinds of polymeric resins.
  • one polymeric resin is a homopolymer or copolymer of polypropylene
  • the second or further polymeric resin is selected from the group comprising homopolymers and/or copolymers of polyethylene, polybutylene, polyamides, polyesters, halogen-containing polymers and mixtures thereof, wherein the polymers can be fully or partially based biopolymers.
  • the at least one polymeric resin is one kind of polymeric resin.
  • the at least one polymeric resin is a homopolymer of polyethylene or polypropylene.
  • the at least one polymeric resin has a melting temperature Tm of above 100° C., more preferably of above 150° C., like of above 200° C.
  • Tm melting temperature
  • the melting temperature of the at least one polymeric resin ranges from 100 to 350° C., more preferably ranges from 150 to 325° C. and most preferably ranges from 200 to 300° C.
  • the at least one polymeric resin may be selected from polymeric resins having a broad spectrum of melt flow rate.
  • the at least one polymeric resin has a melt flow rate MFR (190° C.) of from 0.1 to 3 000 g/10 min, more preferably of from 0.2 to 2 500 g/10 min.
  • the at least one polymeric resin has a melt flow rate MFR (190° C.) of from 0.3 to 2 000 g/10 min or from 0.3 to 1 600 g/10 min.
  • the at least one polymeric resin has a melt flow rate MFR (230° C.) of from 0.1 to 3 000 g/10 min, more preferably of from 0.2 to 2 500 g/10 min.
  • the at least one polymeric resin has a melt flow rate MFR (230° C.) of from 0.3 to 2 000 g/10 min or from 0.3 to 1 600 g/10 min.
  • the at least one polymeric resin is a polyolefin being a homopolymer and/or copolymer of polypropylene
  • the at least one polymeric resin has a melt flow rate MFR (190° C., 2.16 kg) of from 1 to 3 000 g/10 min, more preferably of from 3 to 2 500 g/10 min.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polypropylene has a melt flow rate MFR (190° C.) of from 5 to 2 000 g/10 min or from 10 to 1 600 g/10 min.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polypropylene has a melt flow rate MFR (230° C.) of from 1 to 3 000 g/10 min, more preferably of from 3 to 2 500 g/10 min.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polypropylene has a melt flow rate MFR (230° C.) of from 5 to 2 000 g/10 min or from 10 to 1 600 g/10 min.
  • the at least one polymeric resin is a polyolefin being a homopolymer and/or copolymer of polyethylene
  • the at least one polymeric resin has a rather low melt flow rate.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polyethylene has a melt flow rate MFR (190° C.) of from 0.5 to 20 g/10 min, more preferably of from 0.7 to 15 g/10 min.
  • the at least one polymeric resin has a melt flow rate MFR (190° C.) of from 0.9 to 10 g/10 min or from 0.9 to 5 g/10 min.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polyethylene has a melt flow rate MFR (230° C.) of from 0.1 to 3 000 g/10 min, more preferably of from 0.2 to 2 500 g/10 min.
  • the at least one polymeric resin which is a homopolymer and/or copolymer of polyethylene has a melt flow rate MFR (230° C.) of from 0.3 to 2 000 g/10 min or from 0.3 to 1 600 g/10 min.
  • a further essential component of the present polymer composition is the surface treated filler material product.
  • the surface treated filler material product and preferred embodiments thereof, reference is made to the comments provided above when discussing process steps a), b) and c).
  • the polymer composition comprises the surface treated filler material product in an amount of 1 to 85 wt.-%, based on the total weight of the polymer composition.
  • the polymer composition comprises the surface treated filler material product in an amount of from 5 to 85 wt.-% and preferably from 10 to 85 wt.-%, based on the total weight of the polymer composition.
  • the polymer composition comprises the surface treated filler material product in an amount of from 15 to 80 wt.-%, based on the total weight of the polymer composition.
  • the polymer composition is a masterbatch.
  • masterbatch refers to a composition having a concentration of the surface treated filler material product that is higher than the concentration of the polymer composition used for preparing the final application product such as a fiber and/or filament and/or film. That is to say, the masterbatch is further diluted such as to obtain a polymer composition which is suitable for preparing the final application product such as a fiber and/or filament and/or film and/or thread.
  • the masterbatch comprises the surface treated filler material product in an amount of from 50 to 85 wt.-%, preferably from 60 to 85 wt.-% and more preferably from 70 to 80 wt.-%, based on the total weight of the masterbatch.
  • the masterbatch is used to produce fibers and/or filaments and/or films and/or threads.
  • the polymer masterbatch obtainable by the inventive process may be used in the manufacture of polymer products, wherein said polymer products preferably comprise polyolefin articles, such as woven fibers, non-woven fibers, profiles, cables, films, or molded products.
  • polyolefin articles such as woven fibers, non-woven fibers, profiles, cables, films, or molded products.
  • the products comprising the polymer masterbatch according to the present invention may be manufactured by any process known to the skilled person.
  • melt processing techniques for example, profile extrusion (for pipes, sheets and hollow sheets), cable extrusion, film extrusion (for cast films and blow films), molding (e.g., injection molding, rotomolding, blow molding and thermoforming), fiber spinning (e.g., melt spinning, wet spinning, dry spinning and structural fibers), co-kneading and pultrusion.
  • the final articles may provide mono-layer or multi-layer structures.
  • the polymer masterbatch obtainable by the inventive process can advantageously be used for the preparation of various shaped articles for plastics applications.
  • Examples include flexible packaging for industrial and consumer applications, including roll stocks, bags, pouches, labels, wraps, lidding, shrink sleeves and stretch films; rigid packaging for industrial and consumer applications including plastic bottles, cups and containers; building and construction materials, including pipes and conduits, cladding and profiles, insulation, seals and gaskets, geotextiles; agriculture and horticulture materials including greenhouse material, mulch films, tunnel, silage, bale wraps, boxes and crates; transportation and automotive applications including interior parts, such as instrument and door panels, consoles, pillars and seating; exterior parts, such as bumper fascia, fenders, tailgates as well as under the hood applications including air ducts, air intake manifolds, radiators and cooling hoses; electrical and electronic applications including CD players, DVD systems, personal computers and TV sets, notebooks, tablets, smartphones, cookers, refrigerators and freezers, washing machines, dishwasher
  • the polymer composition used for preparing the final application product such as a fiber and/or filament and/or film and/or thread comprises the surface treated filler material product in an amount of from 1 to 50 wt.-%, preferably of from 5 to 45 wt.-% and most preferably from 10 to 40 wt.-%, based on the total weight of the polymer composition.
  • the polymer composition used for preparing the final application product such as a fiber and/or filament and/or film comprises the surface treated filler material product in an amount of from 15 to 25 wt.-%, based on the total weight of the polymer composition.
  • the polymer composition used for preparing the final application product such as a fiber and/or filament and/or film and/or thread comprises the at least one calcium carbonate-containing material in an amount of from 1 and 10 wt.-%, based on the total weight of the polymer composition. It is appreciated that the polymer composition preferably comprises this amount when it is used as packaging material for acidic food like citrus fruits or containers and/or bottles for fruit juice.
  • the masterbatch is diluted such as to obtain a polymer composition suitable for preparing the final application product such as a fiber and/or filament and/or film and/or thread. That is to say, the masterbatch is diluted such as to comprises the surface treated filler material product in an amount of from 1 to 50 wt.-%, preferably of from 5 to 45 wt.-% and most preferably from 10 to 40 wt.-%, based on the total weight of the polymer composition.
  • a filter pressure test was performed in order to determine the filter pressure value FPV of a LLDPE masterbatch as described above and compared to the FPV a masterbatch comprising a mineral material of the prior art.
  • the filter pressure test as herein described provides for the Filter Pressure Value, in the present case, of dispersed mineral material in LLDPE.
  • the Filter Pressure Value FPV is defined as the increase of pressure per gram filler. This test is performed to determine the dispersion quality and/or presence of excessively coarse particles or agglomerates of mineral materials in a masterbatch.
  • Low Filter Pressure Values refers to a good dispersion and fine material, wherein high Filter Pressure Values refer to bad dispersion and coarse or agglomerated material.
  • the Filter Pressure test was performed on a commercially available Collin Pressure Filter Test, Teach-Line FT-E20T-IS, according to the standard EN 13900-5. Filter type used was 14 ⁇ m and 25 ⁇ m, extrusion was carried out at 200° C.
  • the polymer composition is a fibre and/or filament and/or film and/or thread.
  • the fiber and/or filament and/or film and/or thread comprises the surface treated filler material product in an amount of from 1 to 50 wt.-%, preferably from 5 to 45 wt.-%, more preferably from 10 to 40 wt.-% and most preferably from 15 to 25 wt.-%, based on the total weight of the fiber and/or filament and/or film and/or thread.
  • the surface treated filler material product according to the present invention imparts excellent mechanical properties to final application products such as fibers and/or filaments and/or films and/or threads.
  • the surface treated filler material product imparts excellent mechanical properties to final application products such as fibers and/or filaments and/or films and/or threads, when the surface treated filler material product is provided in form of the polymer composition of the present invention.
  • the present invention refers in a further aspect to a fibre and/or filament and/or film and/or threads comprising the polymer composition as defined above and/or the surface treated filler material product as defined above.
  • the present invention refers in another aspect to a method for preparing a fibre and/or filament and/or film and/or thread, the method comprising at least the steps of:
  • the polymer composition of the present invention may advantageously be implemented in a process of mixing and/or extruding and/or compounding and/or blow moulding for preparing fibers and/or filaments and/or films and/or threads, wherein the at least one polymeric resin is preferably a thermoplastic polymer selected from the group comprising homopolymers and/or copolymers of polyolefins, polyamides and/or polyesters.
  • the at least one polymeric resin is preferably a thermoplastic polymer selected from the group comprising homopolymers and/or copolymers of polyolefins, polyamides and/or polyesters.
  • fiber in the meaning of the present invention refers to a linear structure forming textile fabrics such as nonwovens which typically consist of fiber webs bonded together by e.g. mechanical methods. Accordingly, the term “fiber” is understood to refer to a finite structure.
  • the term “thread” in the meaning of the present invention refers to a linear structure forming textile fabrics such as nonwovens which typically consist of thread webs bonded together by e.g. mechanical methods. Accordingly, the term “thread” is understood to refer to a finite structure.
  • the thread may be constructed as mono-, bi- or multi-thread. If a bi- or multi-thread is present, the composition of the single thread may be substantially the same. That is to say, the compositions of the single threads comprise substantially the same components, i.e. the at least one polymeric resin and surface treated filler material product, in the same amounts. Alternatively, the composition of the single threads may be different. That is to say, the compositions of the single threads may comprise the same components, i.e.
  • the at least one polymeric resin and surface treated filler material product in varying amounts or the compositions of the single threads may comprise different components, i.e. the at least one polymeric resin and/or surface treated filler material product may be different, in the same amounts or the composition of the single threads may comprise different components, i.e. the at least one polymeric resin and/surface treated filler material product may be different may be different, in varying amounts.
  • filament in the meaning of the present invention refers to a structure that differs from fibers by its structure length. Accordingly, the term “filament” is understood to refer to endless fibers. It is further appreciated that the filament may be constructed as mono-, bi- or multi-filament. If a bi- or multi-filament is present, the composition of the single filaments may be substantially the same. That is to say, the compositions of the single filaments comprise substantially the same components, i.e. the at least one polymeric resin and surface treated filler material product, in the same amounts. Alternatively, the composition of the single filaments may be different. That is to say, the compositions of the single filaments may comprise the same components, i.e.
  • the at least one polymeric resin and surface treated filler material product in varying amounts or the compositions of the single filaments may comprise different components, i.e. the at least one polymeric resin and/or surface treated filler material product may be different, in the same amounts or the composition of the single filaments may comprise different components, i.e. the at least one polymeric resin and/or surface treated filler material product may be different may be different, in varying amounts.
  • the cross-section of the filaments and/or fibers and/or threads may have a great variety of shapes. It is preferred that the cross-sectional shape of the filaments and/or fibers and/or threads may be round, oval or n-gonal, wherein n is ⁇ 3, e.g. n is 3. For example, the cross-sectional shape of the filaments and/or fibers and/or threads is round or trilobal, like round. Additionally or alternatively, the cross-sectional shape of the filaments and/or fibers and/or threads is hollow.
  • the filaments and/or fibers and/or threads may be prepared by all techniques known in the art used for preparing such filaments and/or fibers and/or threads.
  • the filaments and/or fibers and/or threads of the present invention can be prepared by the well known melt-blown process, spunbonded process or staple fibre production.
  • said filled PP masterbatches were used by melt extrusion processes to form fiber and filaments and continuous filament nonwoven fabrics by means known to the skilled person.
  • the fibers and filaments are formed by extrusion of the molten polymer through small orifices.
  • the fibers or filaments thus formed are then drawn or elongated to induce molecular orientation and affect crystallinity, resulting in a reduction in diameter and an improvement in physical properties.
  • Spunmelt is a generic term describing the manufacturing of nonwoven webs (fabrics) directly from thermoplastic polymers. It encompasses 2 processes (spunlaid and meltblown) and the combination of both.
  • polymer granules are melted and molten polymer is extruded through in a spinneret assembly which creates a plurality of continuous polymeric filaments.
  • the filaments are then quenched and drawn, and collected to form a nonwoven web. Some remaining temperature can cause filaments to adhere to one another, but this cannot be regarded as the principal method of bonding.
  • a bonding step includes, but is not be limited to calendaring, hydroentangling, needling and/or bonding by means of chemicals or adhesives.
  • the spunlaid process (also known as spunbonded) has the advantage of giving nonwovens greater strength. Co-extrusion of second components is used in several spunlaid processes, usually to provide extra properties or bonding capabilities.
  • meltblown web formation low viscosity polymers are extruded into a high velocity airstream on leaving the spinneret. This scatters the melt, solidifies it and breaks it up into a fibrous web.
  • Processes are well known in the art, and are commercially available, for producing spunbond fabric of polypropylene polymeric resin.
  • the two typical processes are known as the Lurgi process and the Reinfen Reifen process.
  • the Lurgi process is based on the extrusion of molten polymer through spinneret orifices followed by the newly formed extruded filaments being quenched with air and drawn by suction through Venturi tubes. Subsequent to formation, the filaments are disbursed on a conveyor belt to form a nonwoven web.
  • the Reifen Reifen Reifen Reifenberger process differs from the Lurgi process in that the quenching area for the filaments is sealed, and the quenched air stream is accelerated, thus inducing more effective entrainment of the filaments into the air stream.
  • nonwoven fabrics are generally produced using polypropylene resins having a melt flow index of about 25 to 40 grams/10 minutes.
  • a Lurgi line was used to produce polypropylene nonwovens.
  • Extruder temperatures are between 230° and 250° C.
  • the four spin beams are equipped with melt pumps and spinnerets which contain 600 orifices each with a diameter of 0.8 millimeters.
  • the extruded filaments are formed to a nonwoven web.
  • the conveyor belt speed was adjusted to 20 meters/minute and hydroentangling was used to bond the nonwoven web.
  • Hydroentangling also known as spunlacing, is a process which employs high pressure water jets to entangle fibers in a loose web thereby creating a fabric held together by frictional forces between the said fibers.
  • the final bonded nonwoven web with a width of 100 cm has a fabric weight of 385 g/m2.
  • Samples of the said nonwoven fabrics comprising the CaCO3 according to the present invention and samples of nonwoven fabrics comprising the prior art CaCO3 are compared hereafter in tables 5 and 6.
  • Different amounts of the filled masterbatches were mixed with further polypropylene (PP HF420FB, a homo-polypropylene with MFR 19 g/10 min. (230° C., 2.16 kg, ISO 1133) from Borealis) and nonwoven fabrics were made from these mixtures.
  • PP HF420FB polypropylene
  • MFR 19 g/10 min. 230° C., 2.16 kg, ISO 1133
  • film in the meaning of the present invention refers to a structure that differs from filaments and/or fibers by its dimensional structure. Accordingly, the term “film” is understood to refer to a sheet.
  • the films may be prepared by all techniques known in the art used for preparing such films.
  • the films of the present invention can be prepared by the well known techniques used for preparing stretched/oriented films, and preferably extrusion coating films, blown films, technical blown films, monotapes, cast films and the like.
  • fibers and/or filaments and/or films and/or threads according to the present invention are characterized in that they contain said polymer composition and/or surface treated filler material product and in that they have improved material properties such as improved mechanical properties.
  • fibers and/or filaments and/or films and/or threads according to the present invention cause lower pressure decreases during film extrusion.
  • the fibers and/or filaments and/or films and/or threads according to the present invention further show good mechanical properties such as tensile modulus, tensile test at yield and at break, elongation at break and tear resistance.
  • a further aspect of the present invention is directed to the use of the mono-substituted succinic anhydride for decreasing the hydrophilicity of a calcium carbonate-containing filler material surface.
  • the at least one mono-substituted succinic anhydride as defined above can be used to decrease the hydrophilicity of the calcium carbonate-containing filler material surface such that the surface treated filler material product is suitable for use in fibers and/or filaments and/or films and/or threads.
  • a still further aspect of the present invention is directed to the use of the surface treated filler material product, as defined above, for initiating the crosslinking reaction in epoxide resins.
  • Another aspect of the present invention is directed to an article comprising the polymer composition as defined above and/or the surface treated filler material product as defined above and/or the fibre and/or filament and/or film and/or thread as defined above.
  • the article is preferably selected from the group comprising hygiene products, medical and healthcare products, filter products, geotextile products, agriculture and horticulture products, clothing, footwear and baggage products, household and industrial products, packaging products, construction products and the like.
  • the hygiene products are selected from the group comprising absorbent hygiene products such as baby diapers or nappies, feminine hygiene, adult incontinence products, depilatory strips, bandages and wound dressings, disposable bath and face towels, disposable slippers and footwear, top sheets or coverstocks, consumer face masks, leg cuffs, acquisition/distribution layers, core wraps, back sheets, stretch ears, landing zones, dusting layers and fastening systems; and wipes such as wet wipes, skin care wipes, baby wipes, facial wipes, cleansing wipes, hand and body wipes, moist towelettes, personal hygiene wipes, feminine hygiene wipes, antibacterial wipes and medicated wipes.
  • absorbent hygiene products such as baby diapers or nappies, feminine hygiene, adult incontinence products, depilatory strips, bandages and wound dressings, disposable bath and face towels, disposable slippers and footwear, top sheets or coverstocks, consumer face masks, leg cuffs, acquisition/distribution layers, core wraps, back sheets, stretch ears, landing zones, dust
  • the medical and healthcare products are selected from the group comprising medical products which can be sterilized, medical packaging, caps like surgical disposable caps, protective clothing, surgical gowns, surgical masks and face masks, surgical scrub suits, surgical covers, surgical drapes, wraps, packs, sponges, dressings, wipes, bed linen, contamination control gowns, examination gowns, lab coats, isolation gowns, transdermal drug delivery, shrouds, underpads, procedure packs, heat packs, ostomy bag liners, fixation tapes, incubator mattress, sterilisation wraps (CSR wrap), wound care, cold/heat packs, drug delivery systems like patches.
  • medical packaging caps like surgical disposable caps, protective clothing, surgical gowns, surgical masks and face masks, surgical scrub suits, surgical covers, surgical drapes, wraps, packs, sponges, dressings, wipes, bed linen, contamination control gowns, examination gowns, lab coats, isolation gowns, transdermal drug delivery, shrouds, underpads, procedure packs, heat packs, ostomy bag liners, fixation
  • the filter products are selected from the group comprising gasoline filters, oil filters, air filters, water filters, coffee filters, tea bags, pharmaceutical industry filters, mineral processing filters, liquid cartridge and bag filters, vacuum bags, allergen membranes and laminates with nonwoven layers.
  • the geotextile products are selected from the group comprising soil stabilizers and roadway underlayment, foundation stabilizers, erosion control, canals construction, drainage systems, geomembrane protection, frost protection, agriculture mulch, pond and canal water barriers, said infiltration barrier for drainage tile and landfill liners.
  • the agriculture and horticulture products are selected from the group comprising crop covers, plant protection, seed blankets, weed control fabrics, greenhouse shading, root control bags, biodegradable plant pots, capillary matting, and landscape fabric.
  • the clothing, footwear and baggage products are selected from the group comprising interlinings like fronts of overcoats, collars, facings, waistbands, lapels etc., disposable underwear, shoe components like shoelace eyelet reinforcement, athletic shoe and sandal reinforcement and inner sole lining etc., bag components, bonding agents, composition and (wash) care labels.
  • the packaging products are selected from the group comprising interlinings like desiccant packaging, sorbents packaging, gift boxes, file boxes, nonwoven bags, book covers, mailing envelopes. Express envelopes, courier bags and the like.
  • the household and industrial products are selected from the group comprising abrasives, bed linen like pocket cloth for pocket springs, separation layer, spring cover, top cover, quilt backing, duvet coverings, pillow cases etc. blinds/curtains, carpet/carpet backings like scatter rugs, carpet tiles, bath mats etc., covering and separation material, detergent pouches, fabric softener sheets, flooring, furniture/upholstery like inside lining, reverse fabric for cushions, dust cover, spring covering, pull strips etc., mops, table linen, tea and coffee bags, vacuum cleaning bags, wall-covering, wipes like household care wipes, floor care wipes, cleaning wipes, pet care wipes etc., automotive building, cable wrapping, civil engineering, filtration packaging, protection clothing, primary and secondary carpet backing, composites, marine sail laminates, tablecover laminates, chopped strand mats, backing/stabilizer for machine embroidery, packaging where porosity is needed, insulation like fiberglass batting, pillows, cushions, padding like upholstery padding, batting in quilts or comforters, consumer and medical
  • the construction products are selected from the group comprising house wrap, asphalt overlap, road and railroad beds, golf and tennis courts, wallcovering backings, acoustical wall coverings, roofing materials and tile underlayment, soil stabilizers and roadway underlayment, foundation stabilizers, erosion control, canals construction, drainage systems, geomembrane protection, frost protection, agriculture mulch, pond and canal water barriers, and sand infiltration barriers for drainage tile.
  • the following examples may additionally illustrate the invention but are not meant to restrict the invention to the exemplified embodiments.
  • the examples below show the reduced total volatiles, the reduced moisture pick up susceptibility and the decreased hydrophilicity of the surface treated filler material product and the good mechanical properties of the fiber and/or filament and/or film and/or thread prepared from the polymer composition according to the present invention.
  • the “total volatiles” associated with mineral fillers and evolved over a temperature range of 25 to 350° C. is characterized according to % mass loss of the mineral filler sample over a temperature range as read on a thermogravimetric (TGA) curve.
  • TGA thermogravimetric
  • thermogravimetric analysis is performed using a Mettler Toledo TGA 851 based on a sample of 500+/ ⁇ 50 mg and scanning temperatures from 25 to 350° C. at a rate of 20° C./minute under an air flow of 70 ml/min.
  • the skilled man will be able to determine the “volatile onset temperature” by analysis of the TGA curve as follows: the first derivative of the TGA curve is obtained and the inflection points thereon between 150 and 350° C. are identified. Of the inflection points having a tangential slope value of greater than 45° relative to a horizontal line, the one having the lowest associated temperature above 200° C. is identified. The temperature value associated with this lowest temperature inflection point of the first derivative curve is the “volatile onset temperature”.
  • the “total volatiles” evolved on the TGA curve is determined using Star e SW 9.01 software. Using this software, the curve is first normalised relative to the original sample weight in order to obtain mass losses in % values relative to the original sample. Thereafter, the temperature range of 25 to 350° C. is selected and the step horizontal (in German: “Stufe horizontal”) option selected in order to obtain the % mass loss over the selected temperature range.
  • the “d 50 ” value is determined based on measurements made by using a SedigraphTM 5100 of Micromeritics Instrument Corporation and is defined as the size at which 50% (the median point) of the particle volume or mass is accounted for by particles having a diameter equal to the specified value.
  • the method and the instrument are known to the skilled person and are commonly used to determine grain size of fillers and pigments.
  • the measurement is carried out in an aqueous solution of 0.1 wt.-% Na 4 P 2 O 2 .
  • the samples are dispersed using a high speed stirrer and supersonics.
  • the specific surface area (in m 2 /g) of the mineral filler is determined using the BET method (using nitrogen as absorbing gas), which is well known to the skilled man (ISO 9277:1995).
  • the total surface area (in m 2 ) of the mineral filler is then obtained by multiplication of the specific surface area and the mass (in g) of the mineral filler prior to treatment.
  • moisture pick-up susceptibility in the meaning of the present invention refers to the amount of moisture absorbed on the surface of the mineral filler and is determined in mg moisture/g of the dry treated mineral filler product after exposure to an atmosphere of 10 and 85% of relative humidity, resp., for 2.5 hours at a temperature of +23° C. ( ⁇ 2° C.).
  • the treated mineral filler product is first held at an atmosphere of 10% of relative humidity for 2.5 hours, then the atmosphere is changed to 85% of relative humidity, where the sample is held for another 2.5 hours.
  • the weight increase between 10% and 85% relative humidity is then used to calculate the moisture pick-up in mg moisture/g of dry treated mineral filler product.
  • the “hydrophilicity” of a mineral filler product is evaluated at +23° C. by determining the minimum water to ethanol ratio in a volume/volume based water/ethanol-mixture needed for the settling of the majority of said mineral filler product, where said mineral filler product is deposited on the surface of said water/ethanol-mixture by passage through a house hold tea sieve.
  • the volume/volume base is related to the volumes of both separate liquids before blending them together and do not include the volume contraction of the blend.
  • the evaluation at +23° C. refers to a temperature of +23° C. ⁇ 1° C.
  • a 8:2 volumetric ratio of a water/ethanol-mixture has typically a surface tension of 41 mN/m and a 6:4 volumetric ratio of a water/ethanol-mixture has typically a surface tension of 26 mN/m measured at +23° C. as described in the “Handbook of Chemistry and Physics”, 84 th edition, David R. Lid, 2003 (first edition 1913).
  • the dart drop test is measured according to ASTM D 1709/A.
  • the residual total moisture content of the filler is measured according to the Karl Fischer coulometric titration method, desorbing the moisture in an oven at 220° C. and passing it continuously into the KF coulometer (Mettler Toledo coulometric KF Titrator C30, combined with Mettler oven DO 0337) using dry N 2 at 100 ml/min for 10 min. A calibration curve using water has to be made and a blind of 10 min gas flow without a sample has to be taken in account.
  • Titer or Linear Density [dtex] may be measured according to EN ISO 2062 and corresponds to the weight in grams of 10'000 m yarn. A sample of 25 or 100 meters is wound up on a standard reel under a pretension of 0.5 cN/tex and weighted on an analytical scale. The grams per 10'000 m yarn length are then calculated.
  • Tenacity is calculated from the breaking force and the linear density, and expressed in centinewton per tex [cN/tex]. the test is carried out on a dynamometer with a constant stretching speed, applicable standards for this test are EN ISO 5079 and ASTM D 3822.
  • Breaking force and elongation at break The breaking force is the force needed to be applied on a yarn to make it break. It is expressed in Newton [N].
  • the elongation at break is the increase of the length produced by stretching a yarn to its breaking point. It is expressed as a percentage [%] of its initial length.
  • Tensile index is the product of tenancy [cN/tex] and the square root of the elongation at break [%].
  • Fabric weight or mass per unit are [g/m 2 ] is measured according to EN ISO 9864.
  • Tensile properties of geotextiles are measured according to EN ISO 10319 using a wide-width strip with 200 mm width and 100 mm length on a tensile testing machine.
  • Tensile strength [kN/m] and the elongation at maximum load [%] are measured in machine direction (MD) and in cross machine direction (CD).
  • the energy value according to EN ISO 10319 is calculated by the tensile strength (MD+CD)/2.
  • CBR test Static puncture resistance in [kN] is measured according to EN ISO 12236. This method specifies the determination of the puncture resistance by measuring the force required to push a flat-ended plunger through geosynthetics.
  • Ash content in [%] of the fibers and the masterbatches is determined by incineration of a sample in an incineration crucible which is put into an incineration furnace at 570° C. for 2 hours. The ash content is measured as the total amount of remaining inorganic residues.
  • This example relates to the preparation of a surface treated filler material product in accordance with the process of the present invention.
  • the obtained calcium carbonate-containing filler material features a d 50 of approximately 1.7 microns, a top cut (d 98 ) of 5 ⁇ m and a specific surfaced area of 4.1 m 2 /g and a residual moisture content of 0.06 wt.-%.
  • the obtained spray dried calcium carbonate-containing filler material was further treated as outlined in the following tests:
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately. The results are presented in table 2.
  • the surface treated filler material product prepared in accordance with the present invention shows excellent properties.
  • the surface treated filler material product prepared in accordance with the present invention has a moisture pick up susceptibility of less than 0.8 mg/g, a volatile onset temperature of ⁇ 250° C., and a hydrophilicity of below 8:2 volumetric ratio of water:ethanol.
  • This example relates to the preparation of a blown film comprising the surface treated filler material product prepared in accordance with the present invention and at least one polymeric resin.
  • the polymer compositions used for preparing the blown film were afterward diluted to 20 wt.-% calcium carbonate-containing material, based on the total weight of the obtained film.
  • Treated carbonate A is a stearic acid treated dry ground calcium carbonate (marble from Italy) with a medium diameter (d 50 ) of 1.7 ⁇ m and a top cut (d 98 ) of 6.8 ⁇ m, 57 wt.-% of the particles have a diameter of below 2 ⁇ m.
  • This treated filler material is used as an internal reference.
  • Polymer resin relates to a linear low density polyethylene resin (LLDPE) which is commercially available as Dowlex NG 5056G from Down Chemical Company, Dow Europe GmbH, Horgen, Switzerland.
  • LLDPE linear low density polyethylene resin
  • Polymer composition F0 contains only the pure polymer resin, no surface treated filler material product is included.
  • the blown film was prepared on a Collin blown film line with a film grammage of 37.5 g/m 2 and a film thickness of 40 ⁇ m.
  • the fiber and/or filament and/or film and/or thread comprising the inventive surface treated filler material product prepared in accordance with the present invention show excellent mechanical properties such as shown in FIG. 1 .
  • FIG. 1 demonstrates clearly that fibers and/or filaments and/or films and/or threads comprising the inventive surface treated filler material product prepared in accordance with the present invention show increased values in dart drop.
  • the values determined for the dart drop of the fibers and/or filaments and/or films and/or threads comprising the inventive surface treated filler material product prepared in accordance with the present invention are significantly higher than the values determined for the sample consisting only of the polymeric resin as well as for the reference sample.
  • the polymer composition comprising the inventive surface treated filler material product prepared in accordance with the present invention and which is used for preparing the fiber and/or filament and/or film and/or thread also shows an excellent filter pressure value (FPV) as can be gathered from Table 4.
  • FV filter pressure value
  • This example relates to the preparation of a nonwoven fabric comprising the surface treated filler material product prepared in accordance with the present invention and at least one polymeric resin.
  • Samples of the said nonwoven fabrics comprising the CaCO 3 according to the present invention and samples of nonwoven fabrics comprising the prior art CaCO 3 are compared hereafter in tables 5 and 6.
  • Different amounts of the filled masterbatches were mixed with further polypropylene (PP HF420FB, a homo-polypropylene with MFR 19 g/10 min. (230° C., 2.16 kg, ISO 1133) from Borealis) and nonwoven fabrics were made from these mixtures.
  • PP HF420FB polypropylene
  • MFR 19 g/10 min. 230° C., 2.16 kg, ISO 1133
  • 70% MB Invention 1 refers to 70 wt % of a masterbatch of 28 wt % PP HH450 FB homo-polypropylene with MFR 37 g/10 min. (230° C., 2.16 kg, ISO 1133) from Borealis and 2 wt % Irgastab FS 301, processing and thermal stabilizer from BASF and 70 wt % of CaCO 3 according to the present invention, wherein the treated CaCO 3 has a median particles size diameter d50 of 1.7 ⁇ m, a top cut of d98 of 6 ⁇ m.
  • Hydrores AS 1000 (KEMIRA; CAS number 68784-12-3): 500 g of the spray dried calcium carbonate-containing filler material was added to an MTI Mixer and the sample was activated for 10 minutes at 120° C. and 3000 rpm. Thereafter, Hydrores AS 1000 (Kemira) was introduced to the mixer in a quantity of 0.5 wt %. The contents of the mixer were mixed at 120° C. under a stirring speed of 3000 rpm for a period of 10 minutes.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately.
  • T onset 289° C.; Water-pick-up: 0.7 mg/g
  • 70% MG Invention 2 refers to 70 wt % of a masterbatch of 28 wt % PP HH450 FB homo-polypropylene with MFR 37 g/10 min. (230° C., 2.16 kg, ISO 1133) from Borealis and 2 wt % Irgastab FS 301, processing and thermal stabilizer from BASF and 70 wt % of CaCO 3 according to the present invention, wherein the treated CaCO 3 has a median particles size diameter d50 of 1.7 ⁇ m, a top cut of d98 of 6 ⁇ m.
  • the obtained surface treated filler material product was stored in a closed plastic bag.
  • the sample was taken out of the closed plastic bag and analyzed immediately.
  • T onset 300° C.; Water-pick-up: 0.8 mg/g
  • 70% of MA PA1 refers to 70 wt % of a masterbatch of 28 wt % PP HH450 FB homo-polypropylene with MFR 37 g/10 min. (230° C., 2.16 kg, ISO 1133) from Borealis and 2 wt % Irgastab FS 301, processing and thermal stabilizer from BASF and 70 wt % of a wet ground surface treated CaCO 3 of the prior art, and the CaCO 3 has a median particle size diameter d50 of 1.7 ⁇ m and a top cut of d98 of 6 ⁇ m.
  • samples of polypropylene nonwoven fabrics comprises the CaCO 3 according to the present invention and as seen in example 4 from tables 5 and 6, samples of nonwoven fabrics comprising the prior art CaCO 3 can be produced in good quality with slightly reduced mechanical properties compared to Example 1 being the unfilled polypropylene PP HF420FB.
  • polypropylenes mentioned are not the only one and that other PP polymers or PE polymers or a mix of PP and PE polymers are suitable as well to be used for producing a masterbatch comprising the CaCO 3 of the present invention.
  • This example relates to the preparation of multifilament fibers comprising the surface treated filler material product prepared in accordance with the present invention and at least one polymeric resin.
  • Samples of the said multifilament fibers comprising the CaCO 3 according to the present invention and samples of multifilament fibers comprising the prior art CaCO 3 are summarized hereafter in table 8 to 14.
  • Different amounts of the filled masterbatches were mixed with further polypropylene (Moplen HP 561R, a homo-polypropylene with MFR 25 g/10 min. (230° C., 2.16 kg, ISO 1133) from LyondellBasell) and multifilament fibers were made from these mixtures using a Collin Multifilament Lab Line CMF 100 (produced by Dr.
  • Condition 1 Condition 2 Condition 3 Roll 1 80° C. 100° C. 110° C. Roll 2 85° C. 105° C. 115° C. Roll 3 90° C. 105° C. 115° C. Roll 4 90° C. 110° C. 120° C.
  • 70% MG Invention 3 refers to 70 wt % of a masterbatch produced on industrial scale wherein the treated CaCO 3 has a median particles size diameter d50 of 1.7 ⁇ m, a top cut of d98 of 6 ⁇ m.
  • Treatment of the CaCO 3 0.5 wt % of Hydrores AS 1000 (KEMIRA; CAS number 68784-12-3).
  • KEMIRA CAS number 68784-12-3
  • the precise filler content of the masterbatch was determined by the ash content: 72.2 wt % and the melt flow rate (MFR, 230° C., 2.16 kg, ISO 1133) of the masterbatch is 9.13 g/10 min.
  • 70% of MB PA2 refers to a masterbatch produced on industrial scale wherein 70 wt % of a wet ground surface treated CaCO 3 of the prior art is used and the CaCO 3 has a median particle size diameter d50 of 1.7 ⁇ m and a top cut of d98 of 6 ⁇ m.
  • the precise filler content of the masterbatch was determined by the ash content: 72.2 wt % and the melt flow rate (MFR, 230° C., 2.16 kg, ISO 1133) of the masterbatch is 9.04 g/10 min.
  • samples of polypropylene multifilament fibers comprises the CaCO 3 according to the present invention and as seen in tables 11 to 13, samples of polypropylene multifilament fibers comprising the prior art CaCO 3 can be produced in good quality under various processing conditions by varying the amount of CaCO 3 addition, the draw ratio and the draw temperatures.
  • Table 14 shows the results of polypropylene multifilament fibers comprising no CaCO 3 .
US14/431,345 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product Abandoned US20150240056A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US14/431,345 US20150240056A1 (en) 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Applications Claiming Priority (5)

Application Number Priority Date Filing Date Title
EP12188739.2 2012-10-16
EP12188739.2A EP2722368B1 (en) 2012-10-16 2012-10-16 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
US201261717135P 2012-10-23 2012-10-23
PCT/EP2013/071185 WO2014060286A1 (en) 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
US14/431,345 US20150240056A1 (en) 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2013/071185 A-371-Of-International WO2014060286A1 (en) 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/862,483 Continuation US11530313B2 (en) 2012-10-16 2020-04-29 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Publications (1)

Publication Number Publication Date
US20150240056A1 true US20150240056A1 (en) 2015-08-27

Family

ID=47022577

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/431,345 Abandoned US20150240056A1 (en) 2012-10-16 2013-10-10 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
US16/862,483 Active US11530313B2 (en) 2012-10-16 2020-04-29 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Family Applications After (1)

Application Number Title Priority Date Filing Date
US16/862,483 Active US11530313B2 (en) 2012-10-16 2020-04-29 Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product

Country Status (26)

Country Link
US (2) US20150240056A1 (ru)
EP (2) EP2722368B1 (ru)
JP (2) JP6272883B2 (ru)
KR (1) KR101725698B1 (ru)
CN (1) CN104736646B (ru)
AR (1) AR093016A1 (ru)
AU (1) AU2013331867B2 (ru)
BR (1) BR112015008494B1 (ru)
CA (1) CA2886812C (ru)
DK (1) DK2722368T3 (ru)
ES (1) ES2597970T3 (ru)
HR (1) HRP20161294T1 (ru)
HU (1) HUE031169T2 (ru)
IL (1) IL238020A0 (ru)
MX (1) MX358406B (ru)
MY (1) MY169926A (ru)
PH (1) PH12015500697A1 (ru)
PL (1) PL2722368T3 (ru)
PT (1) PT2722368T (ru)
RU (1) RU2623258C2 (ru)
SG (1) SG11201502541UA (ru)
SI (1) SI2722368T1 (ru)
TW (1) TWI510566B (ru)
UA (1) UA114208C2 (ru)
WO (1) WO2014060286A1 (ru)
ZA (1) ZA201503395B (ru)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170218148A1 (en) * 2014-08-14 2017-08-03 Omya International Ag Surface-treated fillers for breathable films
US20170355104A1 (en) * 2014-12-02 2017-12-14 Omya International Ag Surface-treated compacted material
US9951228B2 (en) * 2014-04-16 2018-04-24 Omya International Ag Reduced moisture pickup in polyol-containing mineral filler products
JP2019534355A (ja) * 2016-11-07 2019-11-28 オムヤ インターナショナル アーゲー 一置換コハク酸無水物の使用
EP3590892A4 (en) * 2017-02-28 2021-01-06 Shiraishi Kogyo Kaisha, Ltd. CALCIUM CARBONATE AND MANUFACTURING PROCESS FOR IT
CN113366049A (zh) * 2019-02-11 2021-09-07 欧米亚国际集团 为聚合物制品提供改善的uv稳定性的表面处理的填料材料产品
WO2022073934A1 (en) * 2020-10-05 2022-04-14 Omya International Ag Kit comprising surface-treated calcium carbonate and a peroxide agent for improving the mechanical properties of polyethylene/polypropylene compositions
US11530313B2 (en) 2012-10-16 2022-12-20 Omya International Ag Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
US11708478B2 (en) * 2016-07-19 2023-07-25 Omya International Ag Use of mono-substituted succinic anhydride

Families Citing this family (52)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SI2949707T1 (sl) * 2014-05-26 2017-07-31 Omya International Ag Postopek za pripravo drobcev, ki vsebujejo kalcijev karbonat
PT2963162T (pt) * 2014-07-01 2018-10-19 Omya Int Ag Fibras multifilamento de poliéster
ES2701827T3 (es) * 2014-07-11 2019-02-26 Omya Int Ag Proceso de secado
EP3012223A1 (en) 2014-10-24 2016-04-27 Omya International AG PCC with reduced portlandite content
SI3018174T1 (en) 2014-11-07 2018-07-31 Omya International Ag METHOD FOR THE PRODUCTION OF SUSPENSION CONTAINING MATERIAL CONTAINING CALCIUM CARBONATE
EP3025786A1 (en) 2014-11-28 2016-06-01 Omya International AG Apparatus for simultaneous grinding and froth flotation
EP3042878B1 (en) 2015-01-07 2019-03-06 Omya International AG Process to obtain an ultrafine GCC with high light scattering properties and high solid content
EP3072687A1 (en) 2015-03-24 2016-09-28 Omya International AG Easy to disperse calcium carbonate to improve hot tack strength
EP3088475A1 (en) 2015-04-27 2016-11-02 Omya International AG Modified mineral-based filler comprising copper salts
EP3098202A1 (en) 2015-05-28 2016-11-30 Omya International AG Process for increasing opacity of precipitated calcium carbonate
TR201810471T4 (tr) * 2015-06-23 2018-08-27 Omya Int Ag Poliolefinlerin alfa nükleasyonu için yüzey işlemi görmüş dolgu malzemesi ürünü.
PT3118161T (pt) 2015-07-17 2018-10-08 Omya Int Ag Pcc com alto teor de sólidos com celulose carboxilada despolimerizada
EP3124436A1 (en) 2015-07-31 2017-02-01 Omya International AG Precipitated calcium carbonate with improved resistance to structural breakdown
EP3133127B1 (en) 2015-08-21 2018-08-08 Omya International AG Process for the preparation of a mineral filler product
EP3156369B1 (en) 2015-10-16 2018-07-11 Omya International AG High solids pcc with copolymeric additive
EP3176204A1 (en) * 2015-12-02 2017-06-07 Omya International AG Surface-treated fillers for ultrathin breathable films
EP3184644A1 (en) 2015-12-22 2017-06-28 Omya International AG Microbial cell viability assay for detection of or determining slurry contamination
EP3192839B1 (en) 2016-01-14 2023-03-08 Omya International AG Alkoxysilane treatment of a calcium carbonate-comprising material
ES2702459T3 (es) 2016-01-14 2019-03-01 Omya Int Ag Uso de un carbonato de calcio tratado en superficie como secuestrante de oxígeno
EP3192837B1 (en) * 2016-01-14 2020-03-04 Omya International AG Wet surface treatment of surface-modified calcium carbonate
EP3192838A1 (en) 2016-01-14 2017-07-19 Omya International AG Treatment of surface-reacted calcium carbonate
JP2019511441A (ja) 2016-02-01 2019-04-25 イメリーズ ミネラルズ リミテッド ポリマーフィルムにおいて使用するのに適した無機微粒子状物質
JP2017210597A (ja) * 2016-05-18 2017-11-30 地方独立行政法人 大阪市立工業研究所 無機充填剤の表面処理方法
EP3272524A1 (en) 2016-07-21 2018-01-24 Omya International AG Calcium carbonate as cavitation agent for biaxially oriented polypropylene films
EP3275946A1 (en) 2016-07-25 2018-01-31 Omya International AG Post treatment of surface-reacted calcium carbonate with different functional cations
EP3275838A1 (en) 2016-07-25 2018-01-31 Omya International AG Production of amorphous calcium carbonate
EP3293322A1 (en) 2016-09-13 2018-03-14 Omya International AG Slip resistant product
WO2018095515A1 (en) * 2016-11-22 2018-05-31 Omya International Ag Surface-treated fillers for biaxially oriented polyester films
EP3339355B1 (en) * 2016-12-21 2019-10-23 Omya International AG Surface-treated fillers for polyester films
EP3415570A1 (en) 2017-06-14 2018-12-19 Omya International AG Process for preparing a surface treated filler material product with mono-substituted succinic anhydride(s) and a mixture of aliphatic linear or branched carboxylic acids comprising stearic acid
EP3418064A1 (en) 2017-06-22 2018-12-26 Omya International AG Tamper-proof medium for thermal printing
EP3467050A1 (en) 2017-10-04 2019-04-10 Omya International AG Coating compositions comprising ground natural calcium carbonate (gcc)
EP3572456A1 (en) 2018-05-23 2019-11-27 Omya International AG Surface-treated fillers for polyester films
RU2687231C1 (ru) * 2018-08-03 2019-05-08 Сергей Борисович Врублевский Способ получения пигментов
EP3623428A1 (en) 2018-09-17 2020-03-18 Omya International AG Compacted polymer-based filler material for plastic rotomoulding
EP3628705A1 (en) * 2018-09-28 2020-04-01 Omya International AG Process for preparing a coarse surface treated filler material product
EP3693339A1 (en) 2019-02-01 2020-08-12 Omya International AG Production of surface-reacted calcium salts by grinding induced conversion
EP3725851A1 (en) 2019-04-16 2020-10-21 Omya International AG Process for preparing surface-reacted calcium carbonate
EP3750950A1 (en) 2019-06-12 2020-12-16 Omya International AG Chemical foaming of pvc with surface-reacted calcium carbonate (mcc) and/or hydromagnesite
EP3753980A1 (en) 2019-06-17 2020-12-23 Omya International AG Caco3 coated with maleic anhydride grafted polyethylene and/or maleic anhydride grafted polypropylene and at least one hydrophobizing agent
WO2021005182A1 (en) 2019-07-11 2021-01-14 Omya International Ag Nonwoven fabric and process for the production thereof
KR20220128631A (ko) * 2020-01-29 2022-09-21 옴야 인터내셔널 아게 폴리락트산 및 표면-처리된 탄산칼슘을 포함하는 부직 직물
EP4130137A4 (en) * 2020-03-24 2024-04-03 New Japan Chem Co Ltd MODIFIER FOR POLYOLEFIN RESINS AND POLYOLEFIN RESIN COMPOSITIONS CONTAINING THIS MODIFIER
EP4175998A1 (en) * 2020-07-03 2023-05-10 Omya International AG Low noise biodegradable breathable films
IL299785A (en) 2020-07-16 2023-03-01 Omya Int Ag Alkali trace metal minerals as carriers for surfactants in drilling fluids
AR123009A1 (es) 2020-07-20 2022-10-19 Omya Int Ag Agente estabilizante para composición probiótica
CN112159494B (zh) * 2020-08-28 2021-04-23 江苏康爱特环境工程集团有限公司 一种水性道路标线涂料乳液及其制备方法
US20230383097A1 (en) * 2020-10-05 2023-11-30 Omya International Ag Surface-treated ultrafine calcium carbonate for improving the mechanical properties of polyethylene/polypropylene compositions
WO2022112434A1 (en) 2020-11-25 2022-06-02 Omya International Ag Ultrafine surface-treated fillers for thin breathable films
WO2023118351A1 (en) * 2021-12-22 2023-06-29 Omya International Ag Calcium carbonate-comprising material with high bio-based carbon content for polymer formulations
WO2023118361A1 (en) * 2021-12-22 2023-06-29 Omya International Ag Precipitated calcium carbonate with high bio-based carbon content for polymer formulations
CN117603522B (zh) * 2024-01-23 2024-03-29 四川腾达峰橡塑科技有限公司 一种全生物降解塑料母粒及制备方法和应用

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4328041A (en) * 1980-06-09 1982-05-04 Milliken Research Corporation Comminuted inorganic materials
US4876152A (en) * 1988-03-28 1989-10-24 Ppg Industries, Inc. Water-proofing composition
US20090324979A1 (en) * 2005-12-29 2009-12-31 Omya Development Ag Calcium carbonate barrier films and uses thereof
WO2011124564A1 (en) * 2010-04-09 2011-10-13 Omya Development Ag Use of surface modified calcium carbonate in adhesives, sealants and/or caulks

Family Cites Families (55)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE792985A (fr) 1971-12-20 1973-04-16 Asahi Chemical Ind Compositions de matieres thermoplastiques
JPS54162746A (en) 1978-06-14 1979-12-24 Matsushita Electric Works Ltd Vinyl chloride resin composition
JPS56120742A (en) 1980-02-29 1981-09-22 Idemitsu Petrochem Co Ltd Polypropylene composition
US4482655A (en) * 1980-06-09 1984-11-13 Milliken Research Corporation Comminuted inorganic materials
US4359556A (en) 1981-06-05 1982-11-16 Gulf Oil Corporation Thermoplastic polyamide hot melt adhesive composition
US4520073A (en) 1983-12-23 1985-05-28 Usg Corporation Pressure coating of mineral fillers
US5135967A (en) 1988-01-21 1992-08-04 Deutsche Solvay-Werke Gmbh Underseal composition, and process for the production thereof
DE3801649C2 (de) 1988-01-21 1996-09-19 Solvay Werke Gmbh Unterbodenschutzmasse, Verfahren zu deren Herstellung sowie Verwendung eines gegebenenfalls synthetischen Calciumcarbonats zur Rheologiesteuerung von Unterbodenschutzmassen
WO1992002587A1 (en) 1990-08-06 1992-02-20 Pfizer Inc. Calcium carbonate treated with fatty acids, manufacture and use
JPH06234896A (ja) * 1993-02-09 1994-08-23 Showa Denko Kk 強化ポリアミド樹脂組成物
JPH09508424A (ja) 1994-01-28 1997-08-26 ザ、プロクター、エンド、ギャンブル、カンパニー 生分解性コポリマー及び３−ヒドロキシヘキサノエートの生分解性コポリマーを含んでなるプラスチック物品
JPH11511804A (ja) 1996-06-13 1999-10-12 リージェンツ・オブ・ザ・ユニバーシティ・オブ・ミネソタ 生分解性プラスティックを製造するために、合成ポリマーに官能基をグラフトさせる方法
JPH1160928A (ja) 1997-08-27 1999-03-05 Nishikawa Rubber Co Ltd ポリヒドロキシカルボン酸樹脂組成物およびその製造方法
GB2336366A (en) 1998-04-14 1999-10-20 Ecc Int Ltd Filled polyethylene compositions
AU3938399A (en) 1998-05-22 1999-12-13 Imerys Minerals Limited Particulate carbonates and their preparation and use in thermoplastic film compositions
FR2784371B1 (fr) * 1998-10-07 2000-12-15 Pluss Stauffer Ag Nouveaux carbonates de calcium naturels broyes, eventuellement traites avec un acide gras ou son sel, leur application comme regulateur de rheologie dans des compositions polymeriques
KR100623906B1 (ko) * 1999-04-09 2006-09-13 마루오 칼슘 가부시키가이샤 표면-처리 탄산칼슘 충전재, 그것의 제조 방법, 및충전재를 함유하는 수지 조성물
GB9925927D0 (en) 1999-11-03 1999-12-29 Ecc Int Ltd Treating particulate alkaline earth metal carbonates
US6686044B2 (en) 2000-12-04 2004-02-03 Shiraishi Kogyo Kaisha, Ltd. Surface-coated calcium carbonate particles, method for manufacturing same, and adhesive
TWI283235B (en) 2001-11-16 2007-07-01 Maruo Calcium Surface-treated calcium carbonate, production method thereof, and resin composition containing the calcium carbonate
AUPS146402A0 (en) 2002-03-28 2002-05-09 Compco Pty Ltd Nanofiller compositions
PT102888B (pt) 2002-12-23 2005-04-29 Filipe Manuel Rodrigues Aguiar Processo industrial de producao de acido polilactico (pla) obtido por esterificacao e polimerizacao de acido lactico purificado, sendo o referido acido produzido atraves de um processo fermentativo
NZ547789A (en) * 2003-12-22 2010-03-26 Eka Chemicals Ab Filler for papermaking process comprising a calcium salt and a cellulose derivative
US7507561B2 (en) 2004-05-20 2009-03-24 Reliance Life Sciences Pvt. Ltd. Process for the production of polylactic acid (PLA) from renewable feedstocks
US20060020056A1 (en) 2004-07-23 2006-01-26 Specialty Minerals (Michigan) Inc. Method for improved melt flow rate fo filled polymeric resin
US20070213434A1 (en) 2006-03-11 2007-09-13 Lima Avelino F Process for the preparation of mineral filled polyamide and polyester compositions exhibiting increased melt flow and articles formed therefrom
GB0605885D0 (en) 2006-03-24 2006-05-03 Smith & Nephew Composite Material
CN1887716A (zh) * 2006-07-31 2007-01-03 南京大学 单分散微米级球状球霰石型碳酸钙及其制备方法
ES2391042T3 (es) * 2006-10-24 2012-11-20 Lubrizol Limited Agentes de acoplamiento poliméricos
FI20070093A0 (fi) * 2007-02-02 2007-02-02 Kemira Oyj Kipsituote ja menetelmä sen valmistamiseksi
CN101434754A (zh) * 2007-05-01 2009-05-20 迪乐公司 厚固体表面层合制品及其制造方法
EP2397293A1 (en) 2007-06-03 2011-12-21 Imerys Pigments, Inc. Spunlaid fibers comprising coated calcium carbonate, processes for their production, and nonwoven products
US8188185B2 (en) 2008-06-30 2012-05-29 Kimberly-Clark Worldwide, Inc. Biodegradable packaging film
CA2729498A1 (en) * 2008-07-03 2010-01-07 Basf Se Aqueous suspensions of fine-particulate fillers, method for the manufacture thereof and use thereof for the manufacture of fluid-containing papers
KR101022786B1 (ko) 2009-03-30 2011-03-17 대상 주식회사 폴리락트산-함유 생분해성 수지 조성물
BRPI1016046A2 (pt) * 2009-04-06 2016-05-10 Metabolix Inc método para aperfeiçoar o processamento de filmes e a moldagem por injeção de polímeros de polihidroxialcanoato
JP5566157B2 (ja) 2010-03-30 2014-08-06 ユニ・チャーム株式会社 透湿性及び防水性を有するフィルム、並びにその製造方法
PL2371766T3 (pl) 2010-04-01 2013-07-31 Omya Int Ag Sposób wytwarzania wytrąconego węglanu wapnia
DK2390280T3 (en) * 2010-05-28 2015-06-01 Omya Int Ag Treated mineral filler products, process for their preparation, and uses of the same
CN101914311B (zh) * 2010-07-30 2012-12-26 浙江常山金雄有限公司 一种碳酸钙表面改性的方法
WO2012018327A1 (en) 2010-08-04 2012-02-09 Frederic Scheer High heat resistant polymer compositions having poly(lactic acid)
BRPI1004962A2 (pt) 2010-08-20 2012-05-29 Companhia Refinadora Da Amazonia processo de produção de poli (ácido lático ) e reatores para utilização no referido processo
PL2447213T3 (pl) 2010-10-26 2015-10-30 Omya Int Ag Wytwarzanie strącanego węglanu wapnia o dużej czystości
WO2012094758A1 (en) 2011-01-14 2012-07-19 Cerestech, Inc. Poly (lactic-acid) resin compositions
US8686080B2 (en) 2011-05-10 2014-04-01 Basf Se Biodegradable polyester film
ES2549029T3 (es) 2011-05-16 2015-10-22 Omya International Ag Método para la producción de carbonato de calcio precipitado a partir de desecho de la molienda de pulpa
KR101271655B1 (ko) 2011-08-24 2013-06-05 주식회사 대한아이엠 생분해성 수지조성물과 이로부터 제조된 드레인 보드의 코어재 및 드레인 보드
CN102557099B (zh) * 2011-12-16 2014-11-05 杭州师范大学 一种方解石相和/或球霰石相碳酸钙的制备方法
US9428398B2 (en) 2012-03-23 2016-08-30 Omya International Ag Process for preparing scalenohedral precipitated calcium carbonate
ES2674120T3 (es) 2012-05-07 2018-06-27 Aktec Development Limited Plásticos biodegradables, método de producción y uso de los mismos
GB201210800D0 (en) 2012-06-18 2012-08-01 Imerys Minerals Ltd Compositions
EP2722368B1 (en) 2012-10-16 2016-07-13 Omya International AG Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
DK2840065T3 (da) 2013-08-20 2017-02-20 Omya Int Ag Fremgangsmåde til fremstilling af præcipiteret calciumcarbonat
EP2952543B1 (en) 2014-06-05 2017-11-01 Omya International AG Polymer composition filled with an inorganic filler material mixture
ES2660425T3 (es) 2014-12-02 2018-03-22 Omya International Ag Proceso para la producción de un material compactado, material así producido y uso del mismo

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4328041A (en) * 1980-06-09 1982-05-04 Milliken Research Corporation Comminuted inorganic materials
US4876152A (en) * 1988-03-28 1989-10-24 Ppg Industries, Inc. Water-proofing composition
US20090324979A1 (en) * 2005-12-29 2009-12-31 Omya Development Ag Calcium carbonate barrier films and uses thereof
WO2011124564A1 (en) * 2010-04-09 2011-10-13 Omya Development Ag Use of surface modified calcium carbonate in adhesives, sealants and/or caulks
US9012554B2 (en) * 2010-04-09 2015-04-21 Omya International Ag Use of surface modified calcium carbonate in adhesives, sealants and/or caulks

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
"Octadecenylsuccinic anhydride" from www.BuyersGuideChem.com. (Year: 2019) *

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11530313B2 (en) 2012-10-16 2022-12-20 Omya International Ag Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
US9951228B2 (en) * 2014-04-16 2018-04-24 Omya International Ag Reduced moisture pickup in polyol-containing mineral filler products
US10619050B2 (en) * 2014-04-16 2020-04-14 Omya International Ag Reduced moisture pickup in polyol-containing mineral filler products
US10287407B2 (en) * 2014-08-14 2019-05-14 Omya International Ag Surface-treated fillers for breathable films
US20170218148A1 (en) * 2014-08-14 2017-08-03 Omya International Ag Surface-treated fillers for breathable films
US20170355104A1 (en) * 2014-12-02 2017-12-14 Omya International Ag Surface-treated compacted material
US11708478B2 (en) * 2016-07-19 2023-07-25 Omya International Ag Use of mono-substituted succinic anhydride
US11505678B2 (en) 2016-11-07 2022-11-22 Omya International Ag Use of mono-substituted succinic anhydride
JP2019534355A (ja) * 2016-11-07 2019-11-28 オムヤ インターナショナル アーゲー 一置換コハク酸無水物の使用
EP3590892A4 (en) * 2017-02-28 2021-01-06 Shiraishi Kogyo Kaisha, Ltd. CALCIUM CARBONATE AND MANUFACTURING PROCESS FOR IT
US11167998B2 (en) 2017-02-28 2021-11-09 Shiraishi Kogyo Kaisha, Ltd. Calcium carbonate and production method therefor
CN113366049A (zh) * 2019-02-11 2021-09-07 欧米亚国际集团 为聚合物制品提供改善的uv稳定性的表面处理的填料材料产品
WO2022073934A1 (en) * 2020-10-05 2022-04-14 Omya International Ag Kit comprising surface-treated calcium carbonate and a peroxide agent for improving the mechanical properties of polyethylene/polypropylene compositions

Also Published As

Publication number Publication date
CN104736646A (zh) 2015-06-24
MX2015004204A (es) 2015-09-16
US20210079196A1 (en) 2021-03-18
TWI510566B (zh) 2015-12-01
RU2015118318A (ru) 2016-12-10
US11530313B2 (en) 2022-12-20
SI2722368T1 (sl) 2016-10-28
AR093016A1 (es) 2015-05-13
BR112015008494A2 (pt) 2017-07-04
JP6539305B2 (ja) 2019-07-03
PT2722368T (pt) 2016-10-25
UA114208C2 (uk) 2017-05-10
EP2722368B1 (en) 2016-07-13
EP2909275A1 (en) 2015-08-26
IL238020A0 (en) 2015-05-31
JP6272883B2 (ja) 2018-01-31
HUE031169T2 (en) 2017-06-28
DK2722368T3 (en) 2016-10-24
CA2886812A1 (en) 2014-04-24
AU2013331867B2 (en) 2015-09-03
PL2722368T3 (pl) 2017-08-31
JP2018008868A (ja) 2018-01-18
ZA201503395B (en) 2016-08-31
CA2886812C (en) 2017-08-15
BR112015008494B1 (pt) 2022-05-17
KR20150068424A (ko) 2015-06-19
SG11201502541UA (en) 2015-04-29
ES2597970T3 (es) 2017-01-24
EP2722368A1 (en) 2014-04-23
AU2013331867A1 (en) 2015-04-16
MY169926A (en) 2019-06-17
TW201434999A (zh) 2014-09-16
JP2016503373A (ja) 2016-02-04
WO2014060286A1 (en) 2014-04-24
KR101725698B1 (ko) 2017-04-10
PH12015500697A1 (en) 2015-05-25
CN104736646B (zh) 2017-03-15
RU2623258C2 (ru) 2017-06-23
MX358406B (es) 2018-08-01
HRP20161294T1 (hr) 2016-11-18

Similar Documents

Publication Publication Date Title
US11530313B2 (en) Process of controlled chemical reaction of a solid filler material surface and additives to produce a surface treated filler material product
CA2899282C (en) New surface treatment of white mineral materials for application in plastics
US11441037B2 (en) Process for preparing a surface treated filler material product with mono-substituted succinic anhydride(s) and a mixture of aliphatic linear or branched carboxylic acids comprising stearic acid
US9783682B2 (en) Earth alkali carbonate, surface modified by at least one polyhydrogensiloxane
EA041327B1 (ru) Способ приготовления продукта материала наполнителя, поверхностно-обработанного монозамещенным янтарным ангидридом (ангидридами) и смесью алифатических линейных или разветвленных карбоновых кислот, содержащей стеариновую кислоту

Legal Events

Date Code Title Description
AS Assignment

Owner name: OMYA INTERNATIONAL AG, SWITZERLAND

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:RENTSCH, SAMUEL;BURI, MATTHIAS;BLUM, RENE VINZENZ;AND OTHERS;SIGNING DATES FROM 20150427 TO 20150511;REEL/FRAME:035822/0714

STPP Information on status: patent application and granting procedure in general

Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION

STPP Information on status: patent application and granting procedure in general

Free format text: NON FINAL ACTION MAILED

STPP Information on status: patent application and granting procedure in general

Free format text: RESPONSE TO NON-FINAL OFFICE ACTION ENTERED AND FORWARDED TO EXAMINER

STPP Information on status: patent application and granting procedure in general

Free format text: FINAL REJECTION MAILED

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION