US20150203686A1 - Alumina slurry, method for producing same, and coating liquid - Google Patents

Alumina slurry, method for producing same, and coating liquid Download PDF

Info

Publication number
US20150203686A1
US20150203686A1 US14/416,901 US201314416901A US2015203686A1 US 20150203686 A1 US20150203686 A1 US 20150203686A1 US 201314416901 A US201314416901 A US 201314416901A US 2015203686 A1 US2015203686 A1 US 2015203686A1
Authority
US
United States
Prior art keywords
alumina
particle diameter
weight
less
particles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/416,901
Other languages
English (en)
Inventor
Hirotaka Ozaki
Noriaki Fujita
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sumitomo Chemical Co Ltd
Original Assignee
Sumitomo Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sumitomo Chemical Co Ltd filed Critical Sumitomo Chemical Co Ltd
Assigned to SUMITOMO CHEMICAL COMPANY, LIMITED reassignment SUMITOMO CHEMICAL COMPANY, LIMITED ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FUJITA, NORIAKI, OZAKI, HIROTAKA
Publication of US20150203686A1 publication Critical patent/US20150203686A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
    • C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
    • C09D1/00—Coating compositions, e.g. paints, varnishes or lacquers, based on inorganic substances
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/431—Inorganic material
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
    • C01F7/00—Compounds of aluminium
    • C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
    • C01F7/021—After-treatment of oxides or hydroxides
    • C01F7/023—Grinding, deagglomeration or disintegration
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
    • C01F7/00—Compounds of aluminium
    • C01F7/02—Aluminium oxide; Aluminium hydroxide; Aluminates
    • C01F7/021—After-treatment of oxides or hydroxides
    • C01F7/026—Making or stabilising dispersions
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/052—Li-accumulators
    • H01M10/0525—Rocking-chair batteries, i.e. batteries with lithium insertion or intercalation in both electrodes; Lithium-ion batteries
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M10/00—Secondary cells; Manufacture thereof
    • H01M10/05—Accumulators with non-aqueous electrolyte
    • H01M10/058—Construction or manufacture
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/403—Manufacturing processes of separators, membranes or diaphragms
    • H01M50/406—Moulding; Embossing; Cutting
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/411—Organic material
    • H01M50/414—Synthetic resins, e.g. thermoplastics or thermosetting resins
    • H01M50/417—Polyolefins
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/443—Particulate material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/446—Composite material consisting of a mixture of organic and inorganic materials
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/409—Separators, membranes or diaphragms characterised by the material
    • H01M50/449—Separators, membranes or diaphragms characterised by the material having a layered structure
    • H01M50/451—Separators, membranes or diaphragms characterised by the material having a layered structure comprising layers of only organic material and layers containing inorganic material
    • H—ELECTRICITY
    • H01—ELECTRIC ELEMENTS
    • H01M—PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
    • H01M50/00—Constructional details or processes of manufacture of the non-active parts of electrochemical cells other than fuel cells, e.g. hybrid cells
    • H01M50/40—Separators; Membranes; Diaphragms; Spacing elements inside cells
    • H01M50/489—Separators, membranes, diaphragms or spacing elements inside the cells, characterised by their physical properties, e.g. swelling degree, hydrophilicity or shut down properties
    • H01M50/491—Porosity
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/51—Particles with a specific particle size distribution
    • C01P2004/53—Particles with a specific particle size distribution bimodal size distribution
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2004/00—Particle morphology
    • C01P2004/60—Particles characterised by their size
    • C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/12—Surface area
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/22—Rheological behaviour as dispersion, e.g. viscosity, sedimentation stability
    • C—CHEMISTRY; METALLURGY
    • C01—INORGANIC CHEMISTRY
    • C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
    • C01P2006/00—Physical properties of inorganic compounds
    • C01P2006/80—Compositional purity
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K3/00—Use of inorganic substances as compounding ingredients
    • C08K3/18—Oxygen-containing compounds, e.g. metal carbonyls
    • C08K3/20—Oxides; Hydroxides
    • C08K3/22—Oxides; Hydroxides of metals
    • C08K2003/2227—Oxides; Hydroxides of metals of aluminium
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02E—REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
    • Y02E60/00—Enabling technologies; Technologies with a potential or indirect contribution to GHG emissions mitigation
    • Y02E60/10—Energy storage using batteries
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P70/00—Climate change mitigation technologies in the production process for final industrial or consumer products
    • Y02P70/50—Manufacturing or production processes characterised by the final manufactured product

Definitions

  • the present invention relates to an alumina slurry and a method for producing the same, and a coating liquid. More particularly, the present invention relates to an alumina slurry as a raw material of a coating liquid which is suited for formation of a heat-resistant layer in a laminated porous film including the heat-resistant layer and a polyolefin porous film laminated to each other, and a method for producing the same.
  • a nonaqueous electrolyte secondary battery especially a lithium ion secondary battery, has widely been used as a battery which is used in personal computers, mobile phones, mobile information terminals, and the like, because of its high energy density.
  • the nonaqueous electrolyte secondary battery typified by a lithium ion secondary battery has high energy density, and a large current flows to intensely generate heat when inner short circuit and outer short circuit occur due to breakage of the battery or accidents such as breakage of devices using the battery. Therefore, there is a need for the nonaqueous electrolyte secondary battery to secure high safety by preventing excess heat generation.
  • Examples of such a method include a method in which a porous film made of a material, which melts at abnormal heat generation, is used as a separator.
  • the separator for example, a porous film containing polyolefin as a main component is used.
  • the separator composed of a polyolefin porous film melts at about 80 to 180° C. and changes into a non-porous separator at abnormal heat generation of the battery, thereby to shutdown permeation of ions, thus suppressing further heat generation.
  • the separator composed of the polyolefin porous film may undergo shrinkage or film rupture, leading to direct contact between positive and negative electrodes, thus causing short circuit.
  • the separator composed of the polyolefin porous film sometimes failed to suppress abnormal heat generation due to short circuit because of insufficient shape stability.
  • a separator composed of a laminated porous film including a porous film made mainly of polyolefin as a base material (hereinafter sometimes referred to as a “base material porous film”) and a heat-resistant layer containing an alumina filler in the form of a fine powder laminated to each other (see, for example, Patent Document 1).
  • base material porous film a porous film made mainly of polyolefin as a base material
  • the separator composed of the laminated porous film including the heat-resistant layer sometimes causes falling-off of the filler from the heat-resistant layer on a surface thereof, so-called “powder falling”. If powder falling occurs from the separator, expected physical properties of the separator do not appear, and also process defects such as contamination of devices with a powder fallen in the case of assembling into a battery. Therefore, there is a need to develop an alumina slurry capable of obtaining a heat-resistant layer which enables suppression of “powder falling”.
  • Patent Document 1 JP 2004-227972 A
  • an object of the present invention is to provide an alumina slurry serving as a raw material of a coating liquid suited for formation of a heat-resistant layer, which suppresses powder falling in a separator for nonaqueous electrolyte secondary battery and also has chemical stability and shape stability at a high temperature, in an easy and stable manner.
  • Another object of the present invention is to provide a method for producing the alumina slurry.
  • the present invention includes the following inventions.
  • An alumina slurry substantially including alpha-alumina particles and water, wherein
  • the alpha-alumina particles satisfy all particle diameter distribution conditions (a) to (d) mentioned below,
  • the alpha-alumina particles have an alumina purity of 90% by weight or more
  • the content of alumina in the slurry is 20% by weight or more and 50% by weight or less
  • the slurry has a viscosity of 0.5 Pa ⁇ s or more and 15 Pa's or less:
  • D1 denotes a maximum particle diameter of a frequency maximum showing the smallest maximum particle diameter among frequency maximums which appear in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m in the condition (d), and M1 denotes a maximum value; and D2 denotes a maximum particle diameter of a frequency maximum showing the largest maximum particle diameter among frequency maximums which appear in a particle diameter range of 1 ⁇ m or more in the condition (f), and M2 denotes a maximum value.
  • ⁇ 3> The alumina slurry according to the above ⁇ 1> or ⁇ 2>, wherein the amount of coarse particles having a particle diameter of 10 ⁇ m or more is 10 ppm or less in the alpha-alumina particles.
  • ⁇ 4> The alumina slurry according to any one of the above ⁇ 1> to ⁇ 3>, wherein the content of Zr in the alumina solid component is 300 ppm or more calculated on a weight basis.
  • ⁇ 6> The method for producing the alumina slurry according to the above ⁇ 5>, wherein the wet grinding is performed in the absence of a dispersing agent.
  • ⁇ 7> The method for producing the alumina slurry according to the above ⁇ 5> or ⁇ 6>, wherein the wet grinding is wet grinding by dispersion media and the dispersion media are ZrO 2 beads having a diameter of 0.65 mm to 1.5 mm.
  • a coating liquid comprising a binder, alpha-alumina particles, and a solvent, which is used for formation of a heat-resistant layer in a separator for nonaqueous electrolyte secondary battery, including the heat-resistant layer containing alpha-alumina particles and a binder, and polyolefin porous film laminated to each other, wherein
  • the coating liquid is prepared by mixing the alumina slurry according to any one of the above ⁇ 1> to ⁇ 4> with a binder, and contains the alpha-alumina particles in the amount of 100 to 10,000 parts by weight based on 100 parts by weight of the binder.
  • an alumina slurry serving as a raw material of a coating liquid capable of producing a separator for nonaqueous electrolyte secondary battery, including a heat-resistant layer which suppresses powder falling and also has excellent shape stability, in a stable manner; and a coating liquid containing the alumina slurry.
  • FIG. 1 shows particle diameter distribution of alumina particles in alumina slurries 1 to 4 (Examples 1 and 2, and Comparative Examples 1 and 2).
  • the alumina slurry of the present invention is used as a raw slurry of a coating liquid which is used for formation of a layer B in a separator composed of a laminated porous film including a polyolefin base material porous film (hereinafter sometimes referred to as a “layer A”) and a heat-resistant layer containing a binder and a filler composed of alumina particles (hereinafter sometimes referred to as a “layer B”) laminated to each other.
  • a layer A a polyolefin base material porous film
  • layer B heat-resistant layer containing a binder and a filler composed of alumina particles
  • a coating liquid prepared by dissolving and dispersing the alumina slurry of the present invention in an appropriate solvent together with a binder is applied to one or both surfaces of a layer A and the solvent is removed, thereby to laminate the layer B on one or both surfaces of the layer A, thus forming the laminated porous film.
  • the layer A melts and changes into a non-porous layer at abnormal heat generation when accidents of a battery occur, thus imparting the shutdown function to the laminated porous film.
  • the layer B has heat resistance at a high temperature at which shutdown occurs, thus imparting the shape stability function to the laminated porous film.
  • the alumina slurry of the present invention is an alumina slurry substantially comprising alpha-alumina particles and water, and may include alpha-alumina particles and components other than water as long as the object of the present invention can be achieved.
  • components other than water examples include alcohols such as methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, and t-butanol, known dispersing agents, and the like.
  • the alumina slurry of the present invention can be obtained without using solvents other than water or a dispersing agent.
  • the alpha-alumina particles included in the alumina slurry of the present invention satisfy all particle diameter distribution conditions (a) to (d) mentioned below.
  • Particle diameter distribution can be obtained by a laser diffraction method. Specific mention will be made below in Examples.
  • the average particle diameter means a particle diameter equivalent to 50% cumulative percentage (D 50 ) on a mass basis.
  • the average particle diameter is 1 ⁇ m or less, and preferably 0.4 ⁇ m or more and 0.7 ⁇ m or less
  • particles having a particle diameter of more than 1.5 ⁇ m account for 15% by weight or less, and preferably 10% by weight or less
  • the alpha-alumina particles further satisfy all particle diameter distribution conditions (e) to (g) mentioned below.
  • D1 denotes a maximum particle diameter of a frequency maximum showing the smallest maximum particle diameter among frequency maximums which appear in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m in the condition (d), and M1 denotes a maximum value; and D2 denotes a maximum particle diameter of a frequency maximum showing the largest maximum particle diameter among frequency maximums which appear in a particle diameter range of 1 ⁇ m or more in the condition (f), and M2 denotes a maximum value.
  • the alumina particles included in the alumina slurry of the present invention are alpha-alumina particles which are thermally and chemically excellent in stability. Therefore, the heat-resistant layer formed from the alumina slurry of the present invention is thermally and chemically excellent in stability.
  • Alumina includes, in addition to alpha-alumina, beta-alumina, gamma-alumina, theta-alumina, and the like, which are easy to obtain a particulate material as compared with alpha-alumina.
  • these alumina(s) other than alpha-alumina are thermally and chemically inferior in stability as compared with alpha-alumina and are therefore unsuited for formation of a heat-resistant layer.
  • the alpha-alumina particles according to the present invention has an alumina purity of 90% by weight or more, preferably 99% by weight or more, more preferably 99.9% by weight or more, and most preferably 99.99% by weight or more. It is not preferred that the alumina purity of the alpha-alumina particles is less than 90% by weight since the contents of impurities such as Si, Na, and Fe included in the alpha-alumina powder increase, thus failing to obtain satisfactory electrical insulation properties, and increasing amount of metallic foreign substances which cause short circuit.
  • the alumina purity can be determined by a solid-state emission spectrometry. Specific mention will be made below in Examples.
  • the content of alumina in the alumina slurry of the present invention is 20% by weight or more and 50% by weight or less, and preferably 20% by weight or more 40% by weight or less. If the content of alumina is less than 20% by weight, the concentration of alumina of the coating liquid decreases, and thus drying after coating requires energy. If the concentration is more than 50% by weight, the viscosity of the slurry excessively increases, leading to deterioration of grinding efficiency such as a decrease in liquid feed speed of the slurry.
  • the alumina slurry of the present invention preferably has a viscosity within a range of 0.5 Pa ⁇ s or more 15 Pa ⁇ s or less, and more preferably 1.0 Pa ⁇ s or more 4.0 Pa ⁇ s or less.
  • the viscosity of the slurry is the value determined by a B-type viscometer. Specific mention will be made below in Examples.
  • the amount of coarse particles having a particle diameter of 10 ⁇ m or more is preferably 10 ppm or less, and more preferably 3 ppm or less.
  • coarse particles having a particle diameter of 10 ⁇ m or more is included in the amount of more than 10 ppm, defects such as streaks or coarse voids due to aggregation particles are sometimes partially generated.
  • the amount of coarse particles can be determined by a wet sieving method disclosed in the below-mentioned Examples.
  • the content of Zr in the alumina solid component is preferably 300 ppm or more, and more preferably 500 ppm or more, calculated on a weight basis.
  • the upper limit of the content of Zr is preferably 1,500 ppm or less calculated on a weight basis.
  • the content of Zr in the alumina solid component can be measured by ICP atomic emission spectroscopy disclosed in the below-mentioned Examples.
  • alumina slurry of the present invention has physical properties mentioned above.
  • an alpha-alumina powder satisfying the alumina purity and the particle size distribution is preferably dispersed in a predetermined amount of water and the adjustment is made so as to satisfy the slurry viscosity.
  • alumina particles included in the alumina slurry of the present invention sometimes aggregate during storage to form an aggregate.
  • the slurry contains large aggregate, film defects are generated in the layer B due to deterioration of coatability, thus resulting in deterioration of film properties such as shutdown properties of a separator and ion permeability (air permeability). Therefore, fine alumina particles are hardly dispersed in water, thus substantially requiring a dispersing agent, in addition to water.
  • the alumina slurry of the present invention satisfying the above particle diameter distribution can be obtained without using the dispersing agent, using only water as a solvent.
  • the method for producing an alumina slurry of the present invention includes adding raw alpha-alumina particles having an alumina purity of 90% by weight or more, a BET specific surface area of 15 m 2 /g or less, and an average particle diameter of 1 ⁇ m or more and 30 ⁇ m or less to water, which is a solvent, so that the content of alumina becomes 20% by weight or more and 50% by weight or less, thereby allowing the raw alpha-alumina particles to undergo wet grinding.
  • the production method of the present invention has such an advantage that since alpha-alumina can be directly dispersed in a water solvent by wet grinding of comparatively coarse raw alpha-alumina particles mentioned above in the water solvent, the alumina slurry of the present invention exhibiting the above physical properties can be obtained even if wet grinding is performed in the absence of a dispersing agent.
  • raw alpha-alumina particles serving as a raw material (hereinafter referred to as “raw alpha-alumina particles”) in the production method of the present invention.
  • the raw alpha-alumina particles have an alumina purity of 90% by weight or more, preferably 99% by weight or more, more preferably 99.9% by weight or more, and most preferably 99.99% by weight or more.
  • the alumina purity can be determined by solid-state emission spectrometry.
  • the raw alpha-alumina particles have a BET specific surface area of 15 m 2 /g or less, and preferably 10 m 2 /g or less.
  • the average particle diameter of raw alpha-alumina particles is 1 ⁇ m or more and 30 ⁇ m or less, and preferably 1 ⁇ m or more 20 ⁇ m or less.
  • the average particle diameter of raw alpha-alumina particles can be determined by a laser diffraction method.
  • the above raw alpha-alumina particles are added to water which is a solvent, thereby allowing the raw alpha-alumina particles to undergo wet grinding.
  • the amount of raw alpha-alumina particles to be added is decided so that the viscosity of the slurry after wet grinding becomes 0.5 Pa ⁇ s or more and 15 Pa ⁇ s or less, and the content of alumina is 20% by weight or more and 50% by weight or less when the total of the raw alpha-alumina particles and the water solvent is 100% by weight.
  • a media-type dispenser is preferable, and specific examples thereof include a tower mill, a pearl mill, a sand mill, a dyno-mill, an ultra visco mill, an atriter, an annular mill, and the like.
  • alumina beads and zirconia (ZrO 2 ) beads are used, and ZrO 2 beads having a diameter of 0.65 mm to 1.5 mm are preferable in view of large specific gravity, and excellent abrasion resistance and grindability.
  • wet grinding conditions are not primarily determined by devices, dispersion media, and the like to be used, and appropriate grinding conditions may be decided by performing a preliminary test. Specifically, the amount of dispersion media accounts for 30% by volume to 90% by volume of a grinder capacity, and the retention time is usually within a range of about 2 to 10 minutes under the conditions that the content of alumina is 20% by weight or more and 50% by weight or less.
  • the alumina slurry of the present invention is used as a coating liquid containing a binder, alpha-alumina particles, and a solvent, which is used for formation of a heat-resistant layer in a separator for nonaqueous electrolyte secondary battery, including the heat-resistant layer containing a filler composed of alpha-alumina particles (hereinafter sometimes simply referred to as a “filler”) and a binder, and a polyolefin base material porous film laminated to each other, by mixing it with a binder and a solvent.
  • a filler composed of alpha-alumina particles (hereinafter sometimes simply referred to as a “filler”) and a binder
  • a polyolefin base material porous film laminated to each other by mixing it with a binder and a solvent.
  • the coating liquid can be obtained by mixing and dispersing the alumina slurry of the present invention with the binder and the solvent until the mixture becomes uniform, and used for formation of a heat-resistant layer (layer B) of a laminated porous film.
  • alumina slurry there is no particular limitation on the method for mixing an alumina slurry, a binder, and a solvent, and it is possible to use conventionally known dispersers, for example, a stirring-type emulsifying device, a three-one motor, a homogenizer, a media-type dispenser, a pressure-type dispenser, and the like.
  • dispersers for example, a stirring-type emulsifying device, a three-one motor, a homogenizer, a media-type dispenser, a pressure-type dispenser, and the like.
  • an organic solvent such as methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, t-butanol, acetone, ethyl methyl ketone, N-methylpyrrolidone, dimethyl sulfoxide, or N,N-dimethylformamide, or a mixed solvent of water and an organic solvent.
  • the binder to be selected is a binder which has a property capable of binding a filler composed of alumina particles and bonding with a layer A, and is also dissolved or dispersed in the solvent.
  • a water-soluble polymer is preferably used since an aqueous coating liquid can be prepared.
  • the water-soluble polymer preferably has a hydrophilic functional group. It is possible to preferably use, as the material having the hydrophilic functional group, carboxymethyl cellulose, alkyl cellulose, hydroxyalkyl cellulose, starch, polyvinyl alcohol, and sodium alginate because of high adhesion to the layer A. Salts thereof may also be used.
  • the amount of the alumina slurry (calculated in terms of the solid component) is within a range of 100 to 10,000 parts by weight, and preferably 1,000 to 5,000 parts by weight, based on 100 parts by weight of the binder. Too small amount of the filler leads to insufficient ion permeability, while too large amount of the filler leads to an increase in the amount of powder falling.
  • the concentration of the filler is preferably within a range of 6 to 50% by weight, and more preferably 10 to 40% by weight.
  • the concentration of the binder is preferably 0.30% by weight or more and 2.0% by weight or less, and more preferably 0.40% by weight or more and 1.5% by weight or less, based on the weights of the binder and the solvent. It is preferred to use a binder whose molecular weight is appropriately selected so as to obtain the viscosity suited for coating.
  • the coating liquid of the present invention obtained by the above method is applied to one or both surfaces of a base material porous film (layer A) and the solvent is removed, thus enabling formation of a heat-resistant layer containing a filler and a binder.
  • the layer A is a porous film of polyolefin, and is not dissolved in an electrolytic solution in a nonaqueous secondary battery.
  • the layer preferably contains a high molecular weight component having a weight average molecular weight of 5 ⁇ 10 5 to 15 ⁇ 10 6 .
  • the polyolefin include high molecular weight homopolymers or copolymers obtained by polymerizing ethylene, propylene, 1-butene, 4-methyl-1-pentene, 1-hexene, and the like. Of these, a high molecular weight polyethylene composed mainly of ethylene is preferable.
  • the porosity of the layer A is preferably within a range of 20 to 80% by volume, and more preferably 30 to 70% by volume.
  • the porosity of less than 20% by volume may lead to a decrease in electrolytic solution holding amount.
  • the porosity of more than 80% by volume may lead to insufficient change into a non-porous layer at a high temperature at which shutdown arises, in other words, it may become impossible to cut off a current when a batter generates heat due to accidents.
  • the thickness of the layer A is usually within a range of 4 to 50 ⁇ m, and preferably 5 to 30 ⁇ m.
  • the thickness of less than 4 ⁇ m may leads to insufficient shutdown, while the thickness of more than 50 ⁇ m may lead to an increase in thickness of a laminated porous film, thus resulting in reduction of a capacitance of a battery.
  • the pore diameter of the layer A is preferably 3 ⁇ m or less, and more preferably 1 ⁇ m or less.
  • the layer A is a structure including connected pores therein, and enables a gas or a liquid to permeate from one face to the other face.
  • the light transmittance (air permeability) is usually represented by the Gurley value.
  • the Gurley value of the laminated porous film of the present invention is preferably within a range of 30 to 400 seconds/100 cc, and more preferably 50 to 300 seconds/100 cc.
  • the method for producing a layer A includes a method as disclosed in JP 7-29563 A in which a plasticizer is added to a thermoplastic resin and a film is formed, and then the plasticizer is removed by an appropriate solvent, and a method as disclosed in JP 7-304110 A in which, using a film made of a thermoplastic resin produced by a known method, the structurally weak amorphous portion of the film is selectively stretched to form micropores.
  • the layer A is formed from a polyolefin resin including an ultra-high molecular weight polyethylene and a low molecular weight polyolefin having a weight average molecular weight 10,000 or less
  • the layer is preferably produced by the method mentioned below from the viewpoint of production costs.
  • the method is a method including the steps of:
  • the method for applying the coating liquid of the present invention to a layer A is a method capable of performing uniform wet coating, and a conventionally known method can be employed. It is possible to employ, for example, a capillary coating method, a spin coating method, a slit die coating method, a spray coating method, a dip coating method, a roll coating method, a screen printing method, a flexographic printing method, a bar coater method, a gravure coater method, a die coater method, and the like.
  • the thickness of the layer B can be controlled by adjusting the thickness of a coating film, the concentration of a binder in a coating liquid, and the ratio of a filler to a binder.
  • the method for removing a solvent is commonly a method by drying.
  • the drying temperature of the solvent is preferably the temperature which does not cause deterioration of air permeability of the layer A.
  • a heat-resistant layer (layer B) is formed on the layer A.
  • the thickness of the layer B is usually within a range of 0.1 ⁇ m or more and 20 ⁇ m or less, and preferably 1 ⁇ m or more and 15 ⁇ m or less. Too thick layer B may lead to an increase in thickness of a laminated porous film including the layer A, thus resulting in reduction of a capacitance of a battery. Too thin layer B may lead to shrinkage of a laminated porous film since it is impossible to resist heat shrinkage of a porous film (layer A) of polyolefin when a batter generates heat due to accidents.
  • the thickness of the layer B is the total thickness of both surfaces.
  • the layer B is a porous film in which fillers are connected by a binder, and pores formed in the space between fillers are connected to each other, thus enabling a gas or a liquid to permeate from one face to the other face.
  • the pore diameter of the pore is preferably 3 ⁇ m or less, and more preferably 1 ⁇ m or less, in terms of an average of a diameter of a sphere in the case of approximating the pore by a spherical shape.
  • the size of an average of the pore diameter of more than 3 ⁇ m may cause a problem that short circuit is likely to occur when carbon powders or small pieces thereof, which are main components of positive and negative electrodes, fall off.
  • the porosity of the layer B is preferably within a range of 30 to 65% by volume, and more preferably 40 to 60% by volume.
  • the powder falling ratio of the layer B is preferably 30% or less, and more preferably 25% or less.
  • the laminated porous film of the present invention includes a layer A and a layer B formed on the layer B by the above-mentioned method. Namely, the coating liquid of the present invention is applied to one or both surfaces of a base material porous film (layer A) and then a solvent is removed to obtain a laminated porous film of the present invention in which a heat-resistant layer (layer B) containing alpha-alumina particles and a binder is formed on one or both surfaces of the base material porous film (layer A).
  • the laminated porous film of the present invention can be used as a separator for nonaqueous electrolyte secondary battery.
  • the total thickness of the laminated porous film of the present invention i.e. total thickness of the layer A and the layer B, is usually within a range of 5 to 80 ⁇ m, preferably 5 to 50 ⁇ m, and particularly preferably 6 to 35 ⁇ m.
  • the total thickness of the laminated porous film is less than 5 ⁇ m, film rupture is likely to occur. Meanwhile, the total thickness of more than 80 ⁇ m may lead to an increase in thickness of the laminated porous film, thus resulting in reduction of a capacitance of a battery.
  • the total porosity of the laminated porous film of the present invention is usually within a range of 30 to 85%, and preferably 40 to 80%.
  • air permeability of the laminated porous film is preferably within a range of 50 to 2,000 seconds/100 cc, more preferably 50 to 1,000 seconds/100 cc, and still more preferably 50 to 300 seconds/100 cc.
  • the air permeability of 2,000 seconds/100 cc or more may lead to deterioration of ion permeability of the laminated porous film and load characteristics of the battery.
  • the size retention rate of the laminated porous film at a high temperature at which shutdown arises smaller value of those in MD direction or TD direction of the layer A is 85% or more, preferably 90% or more, and more preferably 95% or more.
  • the MD direction means a longitudinal direction during film forming
  • the TD direction means a width direction during film forming.
  • the size retention rate of less than 85% may cause short circuit between positive and negative electrodes due to heat shrinkage of the laminated porous film at a high temperature at which shutdown arises, thus resulting in insufficient shutdown function.
  • High temperature, at which shutdown arises is the temperature within a range of 80 to 180° C. and is usually within a range of about 130 to 160° C.
  • the laminated porous film of the present invention may include films other than the layer A and the layer B, for example, porous films such as an adhesive film and a protective film, as long as the object of the present invention is not impaired.
  • the nonaqueous electrolyte secondary battery When a nonagueous electrolyte secondary battery is produced using a laminated porous film of the present invention as a separator, the nonaqueous electrolyte secondary battery has high load characteristics, and also the separator exerts the shutdown function even if the battery intensely generates heat due to accidents, leading to avoidance of contact between positive and negative electrodes due to shrinkage of the separator, and thus a high-safety nonaqueous electrolyte secondary battery is obtained.
  • Alumina purity used was determined by subtracting the sum total (%) of the weights of SiO 2 , Na 2 O, MgO, CuO, and Fe 2 O 3 included in an oxide (alpha-alumina) serving as a standard from 100.
  • the calculation equation is as follows. The content of each of Si, Na, Mg, Cu, and Fe was measured by solid-state emission spectrometry.
  • Alumina purity (% by weight) 100 ⁇ sum total (% by weight) of weights of impurities
  • BET specific surface area of alumina particles was determined by a nitrogen adsorption method in accordance with the method defined in JIS-Z-8830. “FlowSorb II 2300” manufactured by Shimadzu Corporation was used as a specific surface area analyzer.
  • particle diameter distribution on a mass standard of alumina particles was determined by a laser diffraction method. A particle diameter equivalent to 50% cumulative percentage by mass was regarded as an average particle diameter. The measurement was made by ultrasonic dispersion of a sample in an aqueous 0.2% by weight sodium hexametaphosphate solution.
  • the content of Zr in the alumina solid component was determined by evaporating an alumina slurry to dryness at 200° C., followed by measurement using ICP emission spectroscopy.
  • alumina slurry 100 g was dispersed in 4 L of pure water containing 0.2% sodium hexametaphosphate as a dispersing agent by irradiation with ultrasonic wave, and the slurry was passed through a sieve with 10 ⁇ m mesh size. The alumina powder remaining on the sieve and then the content was measured.
  • a rotor No. 3 was rotated at 6 rpm to measure a viscosity of an alumina slurry.
  • the thickness of the separator was measured by a high-accuracy micrometer manufactured by Mitutoyo Corporation.
  • the separator was cut into a tetragon having a side length of 8 cm and then the weight W (g) was measured.
  • the Basis weight was measured by the following equation:
  • Basis weight (g/m 2 ) W/(0.08 ⁇ 0.08).
  • the basis weight of a layer B was calculated by subtracting a basis weight of a porous base material (layer A) from a basis weight of a laminated porous film.
  • a film was cut into a tetragon having a side length of 8 cm, and the weight W (g) and the thickness D (cm) were measured.
  • the weight of each of materials in a sample was determined by calculation and the weight Wi (g) of each material was divided by a true specific gravity to calculate the volume of each material, and then the porosity (% by volume) was determined by the following equation.
  • the basis weight of each material was calculated by the amount used in film formation and the proportion
  • air permeability was measured by a digital timer-type Gurley densometer manufactured by Toyo Seiki Seisaku-Sho, Ltd.
  • a film was cut into pieces measuring 8 cm ⁇ 8 cm and each film piece, on which a tetragon measuring 6 cm ⁇ 6 cm was drawn, was interposed between papers, followed by putting in an oven heated at 150° C. After one hour, the film was taken out from the oven and the size of the side of the tetragon drawn on the film was measured, and then a heat shape retention ratio was calculated.
  • the calculation method is as follows.
  • Powder falling ratio (%) amount of powder falling (g/m 2 )/basis weight (g/m 2 ) ⁇ 100
  • Alumina particles having a BET specific surface area of 4.1 m 2 /g and an average particle diameter of 6.2 ⁇ m were added to water so that the concentration of alumina became 30% by weight while stirring the alumina particles to obtain an alumina-water suspension.
  • Dyno-Mill KDL-PILOT A model manufactured by AG MASCHINENFABRIK BASEL, dispersion was performed under wet grinding conditions (circumferential speed: 10 m/second, material of beads: ZrO 2 , diameter of beads; 1.0 mm, filling ratio of beads: 85% by volume, flow rate: 0.5 L/minute, and retention time: 4.4 minutes) in a path system to obtain an alumina slurry 1.
  • a viscosity was 2.75 Pa ⁇ s
  • alumina particles included had an average particle diameter of 0.57 ⁇ m
  • the amount of coarse particles of 10 ⁇ m or more was 3 ppm or less.
  • the alumina slurry 1 was evaporated to dryness. As a result, the thus measured content of Zr in solid alumina was 1,010 ppm calculated on a weight basis.
  • alumina particles in the alumina slurry 1 were alumina particles, wherein
  • particles having a particle diameter of less than 0.2 ⁇ m accounts for 4.6% by weight
  • particles having a particle diameter of more than 1.5 ⁇ m accounts for 8.3% by weight
  • one frequency maximum exists in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m
  • particles having a particle diameter of 0.5 ⁇ m or more and less than 1 ⁇ m accounts for 29.2% by weight
  • one frequency maximum appears in a particle diameter range of 1 ⁇ m or more
  • D1 is 0.34 ⁇ m
  • D2 is 1.06 ⁇ m
  • M1 is 4.30
  • M2 is 4.19
  • a ratio of M1 to M2 (M1/M2) is 1.03.
  • An alumina slurry 1 and physical properties of alumina particles in the alumina slurry 1 are collectively shown in Table 1.
  • a separator for evaluation composed of a laminated porous film including a base material porous film (layer A) and a heat-resistant layer (layer B) laminated to each other was produced by the following method as the separator for evaluation.
  • the layer A was formed by the following method.
  • the obtained powder mixture was melt-kneaded by a twin-screw extruder to obtain a polyolefin resin composition.
  • the polyolefin resin composition was rolled by a pair of rolls at a surface temperature of 150° C. to form a sheet.
  • This sheet was immersed in an aqueous hydrochloric acid solution (hydrochloric acid of 4 mol/L, nonionic surfactant of 0.5% by weight) to dissolve calcium carbonate, followed by removal calcium carbonate. Subsequently, the sheet was stretched six times at 105° C. to obtain a base material porous film A1 (film thickness: 16.1 ⁇ m, basis weight: 7.0 g/m 2 , air permeability: 129 seconds/100 cc).
  • alumina slurry 1 of Example 1 mixing was performed in accordance with such formulation that the amount of carboxymethyl cellulose (CMC, Dai-ichi Kogyo Seiyaku Co., Ltd. SORGEN 3H) became 2.9 parts by weight, the amount of pure water became 312 parts by weight, and the amount of ethanol became 156 parts by weight based on 100 parts by weight of alumina, (alumina solid component: 17.5% by weight).
  • CMC carboxymethyl cellulose
  • SORGEN 3H carboxymethyl cellulose
  • the coating liquid 1 was applied on a layer A and dried.
  • the coating liquid 1 was applied on the other surface of the layer A in the same manner and dried, and then a layer B was laminated on both surfaces of the layer A to produce a separator 1 of Example 1.
  • the thickness of the layer B is the total thickness of the layer B provided on both surfaces.
  • the layer B formed in the separator 1 exhibited a porosity of 49% by volume, an air permeability of 189 seconds/100 cc, an MD heat shape retention ratio of 98%, an MD heat shape retention ratio of 98%, sufficient porosity and air permeability to permeation of lithium ions, and also had low powder falling rate and high heat resistance.
  • Example 2 Using the same operation as in Example 1, except that wet grinding conditions were changed as follows: circumferential speed: 10 m/second, material of beads: ZrO 2 , diameter of beads: 1.0 mm, filling ratio of beads: 85% by volume, flow rate: 0.5 L/minute, and retention time: 5.8 minutes, an alumina slurry 2 of Example 2 was produced.
  • a viscosity was 3.04 Pa ⁇ s
  • alumina particles included had an average particle diameter of 0.52 ⁇ m
  • the amount of coarse particles of 10 ⁇ m or more was 3 ppm or less.
  • the alumina slurry was evaporated to dryness. As a result, the thus measured content of Zr in solid alumina was 1,270 ppm calculated on a weight basis.
  • alumina particles in the alumina slurry 2 were alumina particles, wherein
  • particles having a particle diameter of less than 0.2 ⁇ m accounts for 4.6% by weight
  • particles having a particle diameter of more than 1.5 ⁇ m accounts for 4.7% by weight
  • one frequency maximum exists in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m
  • particles having a particle diameter of 0.5 ⁇ m or more and less than 1 ⁇ m accounts for 31.8% by weight
  • one frequency maximum appears in a particle diameter range of 1 ⁇ m or more
  • D1 is 0.34
  • D2 is 0.97
  • M1 is 4.75
  • M2 is 4.07
  • a ratio of M1 to M2 (M1/M2) is 1.17.
  • Example 2 Using the same operation as in Example 1, except that the alumina slurry 2 was used in place of the alumina slurry 1, a coating liquid 2 and a separator 2 of Example 2 were obtained. In the same manner as in Example 1, a base material porous film A1 was used as the layer A.
  • the layer B formed in the separator 2 exhibited a porosity of 40% by volume, an air permeability of 202 seconds/100 cc, an MD heat shape retention ratio of 98%, an MD heat shape retention ratio of 98%, sufficient porosity and air permeability to permeation of lithium ions, and also had low powder falling rate and high heat resistance.
  • alumina slurry 3 of Comparative Example 1 was produced.
  • a viscosity was 1.74 Pa ⁇ s
  • alumina particles included had an average particle diameter of 1.30 ⁇ m
  • the amount of coarse particles of 10 ⁇ m or more was 3,531 ppm or less
  • the content of coarse particles in the slurry was large.
  • the alumina slurry 3 was evaporated to dryness. As a result, the thus measured content of Zr in solid alumina was 340 ppm calculated on a weight basis.
  • alumina particles in the alumina slurry 3 were alumina particles, wherein
  • particles having a particle diameter of less than 0.2 ⁇ m accounts for 4.1% by weight
  • particles having a particle diameter of more than 1.5 ⁇ m accounts for 43.7% by weight
  • one frequency maximum exists in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m
  • particles having a particle diameter of 0.5 ⁇ m or more and less than 1 ⁇ m accounts for 13.6% by weight
  • one frequency maximum appears in a particle diameter range of 1 ⁇ m or more
  • D1 is 0.29 ⁇ m
  • D2 is 1.64 ⁇ m
  • M1 is 2.54, and M2 is 3.97
  • a ratio of M1 to M2 (M1/M2) is 0.64.
  • Example 2 Using the same operation as in Example 2, except that the alumina slurry 3 was used, a coating liquid 3 and a separator 3 of Comparative Example 1 were obtained. In the same manner as in Example 1, a base material porous film A1 was used as the layer A.
  • the layer B formed in the separator 3 exhibited a porosity of 68% by volume, an air permeability of 189 seconds/100 cc, an MD heat shape retention ratio of 97%, an MD heat shape retention ratio of 96%.
  • Physical properties of the obtained separator 3 are collectively shown in Table 2. Since the proportion of coarse particles in the alumina slurry was large, porosity excessively increased. As a result of SEM image observation, surface unevenness was large, and also the powder falling rate was 31% and the coating film strength was low.
  • alumina slurry 4 of Comparative Example 2 was produced.
  • a viscosity was 4.60 Pa ⁇ s
  • alumina particles included had an average particle diameter of 0.37 ⁇ m
  • the amount of coarse particles of 10 ⁇ m or more was 3 ppm or less.
  • the alumina slurry 4 was evaporated to dryness. As a result, the thus measured content of Zr in solid alumina was 2,000 ppm calculated on a weight basis.
  • alumina particles in the alumina slurry 4 were alumina particles, wherein
  • particles having a particle diameter of less than 0.2 ⁇ m accounts for 8.0% by weight
  • particles having a particle diameter of more than 1.5 ⁇ m accounts for 0% by weight
  • one frequency maximum exists in a particle diameter range of 0.1 ⁇ m or more and less than 0.5 ⁇ m
  • particles having a particle diameter of 0.5 ⁇ m or more and less than 1 ⁇ m accounts for 24.3% by weight. However, a frequency maximum was not recognized in a particle diameter range of 1 ⁇ m or more.
  • Example 2 Using the same operation as in Example 2, except that the alumina slurry 4 was used, a coating liquid 4 and a separator 4 of Comparative Example 2 were obtained. In the same manner as in Example 1, a base material porous film A1 was used as the layer A.
  • the layer B formed in the separator 4 exhibited a porosity of 29% by volume, an air permeability of 190 seconds/100 cc, an MD heat shape retention ratio of 99%, an MD heat shape retention ratio of 99%. Regardless of having high heat resistance, sufficient porosity to permeation of lithium ions was not obtained.
  • a separator for nonaqueous secondary battery having excellent shutdown properties and ion permeability can be obtained by using the alumina slurry of the present invention. Since a nonaqueous electrolyte secondary battery using the separator prevents the separator from directly contacting with positive and negative electrodes even if the battery intensely generates heat, and also becomes a high-safety nonaqueous electrolyte secondary battery by maintaining insulation properties due to quick changing of a polyolefin porous film into a non-porous material, the present invention is significantly useful in industry.

Landscapes

  • Chemical & Material Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Electrochemistry (AREA)
  • General Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Organic Chemistry (AREA)
  • Inorganic Chemistry (AREA)
  • Manufacturing & Machinery (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Materials Engineering (AREA)
  • Geology (AREA)
  • Dispersion Chemistry (AREA)
  • Composite Materials (AREA)
  • Wood Science & Technology (AREA)
  • Health & Medical Sciences (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Cell Separators (AREA)
  • Secondary Cells (AREA)
  • Laminated Bodies (AREA)
US14/416,901 2012-07-27 2013-07-24 Alumina slurry, method for producing same, and coating liquid Abandoned US20150203686A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2012-167011 2012-07-27
JP2012167011 2012-07-27
PCT/JP2013/070674 WO2014017662A1 (ja) 2012-07-27 2013-07-24 アルミナスラリーおよびその製造方法並びに塗工液

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/070674 A-371-Of-International WO2014017662A1 (ja) 2012-07-27 2013-07-24 アルミナスラリーおよびその製造方法並びに塗工液

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US15/826,811 Continuation US10836913B2 (en) 2012-07-27 2017-11-30 Alumina slurry, method for producing same, and coating liquid

Publications (1)

Publication Number Publication Date
US20150203686A1 true US20150203686A1 (en) 2015-07-23

Family

ID=49997464

Family Applications (2)

Application Number Title Priority Date Filing Date
US14/416,901 Abandoned US20150203686A1 (en) 2012-07-27 2013-07-24 Alumina slurry, method for producing same, and coating liquid
US15/826,811 Active 2034-03-27 US10836913B2 (en) 2012-07-27 2017-11-30 Alumina slurry, method for producing same, and coating liquid

Family Applications After (1)

Application Number Title Priority Date Filing Date
US15/826,811 Active 2034-03-27 US10836913B2 (en) 2012-07-27 2017-11-30 Alumina slurry, method for producing same, and coating liquid

Country Status (7)

Country Link
US (2) US20150203686A1 (ko)
EP (1) EP2879205B1 (ko)
JP (1) JP6067016B2 (ko)
KR (1) KR101739211B1 (ko)
CN (1) CN104488109B (ko)
TW (1) TW201410799A (ko)
WO (1) WO2014017662A1 (ko)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170155114A1 (en) * 2015-11-30 2017-06-01 Sumitomo Chemical Company, Limited Nonaqueous electrolyte secondary battery separator
US20180114966A1 (en) * 2015-03-30 2018-04-26 Zeon Corporation Composition for secondary battery porous membrane, porous membrane for secondary battery and secondary battery
CN110819138A (zh) * 2019-09-29 2020-02-21 浙江安力能源有限公司 一种钠镍电池陶瓷管表面涂层的制作方法
US10662071B2 (en) 2016-11-14 2020-05-26 Sumitomo Chemical Company, Limited Alumina and slurry containing the same, and alumina porous film using the same, laminated separator, nonaqueous electrolyte secondary battery and method for manufacturing nonaqueous electrolyte secondary battery
US20220077541A1 (en) * 2018-12-26 2022-03-10 Sumitomo Chemical Company, Limited alpha-ALUMINA, SLURRY, POROUS MEMBRANE, LAMINATED SEPARATOR, AND NONAQUEOUS ELECTROLYTE SECONDARY BATTERY AND METHOD FOR PRODUCING SAME
US20230411794A1 (en) * 2021-05-07 2023-12-21 Lg Energy Solution, Ltd. Porous substrate for separator and separator for electrochemical device comprising same

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6413676B2 (ja) * 2014-11-13 2018-10-31 三菱ケミカル株式会社 積層多孔フィルムの製造方法
JP6394346B2 (ja) * 2014-12-10 2018-09-26 三菱ケミカル株式会社 アルミナスラリーの製造方法
JP6415312B2 (ja) * 2014-12-26 2018-10-31 積水化学工業株式会社 セパレータ及び電気化学デバイス
KR101981079B1 (ko) * 2016-07-25 2019-05-22 도레이 카부시키가이샤 전지용 세퍼레이터
JP6634133B2 (ja) * 2018-09-26 2020-01-22 積水化学工業株式会社 セパレータ及び電気化学デバイス
CN109516782A (zh) * 2018-10-25 2019-03-26 建德华明高纳新材料有限公司 锂电池陶瓷隔膜用易分散氧化铝及其制备方法
CN112194915A (zh) * 2020-10-08 2021-01-08 潍坊中凯新能源有限公司 一种氧化铝预分散剂的制备方法
WO2022210259A1 (ja) * 2021-03-30 2022-10-06 デンカ株式会社 無機質粉末、無機質組成物、及び樹脂組成物
TW202332655A (zh) * 2021-11-26 2023-08-16 日商住友化學股份有限公司 氧化鋁粉末及包含其之氧化鋁漿料
WO2024085058A1 (ja) * 2022-10-17 2024-04-25 東レ株式会社 積層多孔質膜および積層多孔質膜を含む電池用セパレータ

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070122716A1 (en) * 2005-11-28 2007-05-31 Le Chem, Ltd. Organic/inorganic composite porous membrane and electrochemical device using the same
US20090181300A1 (en) * 2008-01-11 2009-07-16 Samsung Sdi Co., Ltd. Electrode assembly and secondary battery having the same

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6521203B1 (en) 1992-06-02 2003-02-18 Sumitomo Chemical Co., Ltd. Process for producing α-alumina
CZ284790B6 (cs) 1992-06-02 1999-03-17 Sumitomo Chemical Company, Limited Způsob výroby alfa-oxidu hlinitého
JP3050021B2 (ja) 1993-05-11 2000-06-05 三菱化学株式会社 バッテリーセパレーター及びそれを用いたリチウム電池
JP3003830B2 (ja) 1994-05-12 2000-01-31 宇部興産株式会社 積層多孔質フイルム及びその製法
JP4792688B2 (ja) 2003-01-24 2011-10-12 住友化学株式会社 非水電解液二次電池用セパレータの製造方法
WO2005104270A1 (ja) 2004-04-19 2005-11-03 Matsushita Electric Industrial Co., Ltd. リチウムイオン二次電池およびその製造法
JP4763253B2 (ja) 2004-05-17 2011-08-31 パナソニック株式会社 リチウムイオン二次電池
JP2008156146A (ja) * 2006-12-22 2008-07-10 Sumitomo Chemical Co Ltd αアルミナスラリー
EP2517880B1 (en) * 2007-06-06 2014-03-26 Asahi Kasei E-materials Corporation Multilayer porous film
JP2012004103A (ja) 2010-02-25 2012-01-05 Sumitomo Chemical Co Ltd 無機酸化物粉末および無機酸化物含有スラリーならびに該スラリーを使用したリチウムイオン二次電池およびその製造方法
JP5636312B2 (ja) * 2010-03-09 2014-12-03 住友化学株式会社 サファイア単結晶製造用αアルミナおよびその製造方法
JP2011216257A (ja) * 2010-03-31 2011-10-27 Teijin Ltd 非水系二次電池用セパレータ
JP5362132B2 (ja) 2012-01-20 2013-12-11 住友化学株式会社 無機酸化物粉末および無機酸化物含有スラリーならびに該スラリーを使用したリチウムイオン二次電池およびその製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070122716A1 (en) * 2005-11-28 2007-05-31 Le Chem, Ltd. Organic/inorganic composite porous membrane and electrochemical device using the same
US20090181300A1 (en) * 2008-01-11 2009-07-16 Samsung Sdi Co., Ltd. Electrode assembly and secondary battery having the same

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20180114966A1 (en) * 2015-03-30 2018-04-26 Zeon Corporation Composition for secondary battery porous membrane, porous membrane for secondary battery and secondary battery
US10381624B2 (en) * 2015-03-30 2019-08-13 Zeon Corporation Composition for secondary battery porous membrane, porous membrane for secondary battery and secondary battery
US20170155114A1 (en) * 2015-11-30 2017-06-01 Sumitomo Chemical Company, Limited Nonaqueous electrolyte secondary battery separator
US10662071B2 (en) 2016-11-14 2020-05-26 Sumitomo Chemical Company, Limited Alumina and slurry containing the same, and alumina porous film using the same, laminated separator, nonaqueous electrolyte secondary battery and method for manufacturing nonaqueous electrolyte secondary battery
US20220077541A1 (en) * 2018-12-26 2022-03-10 Sumitomo Chemical Company, Limited alpha-ALUMINA, SLURRY, POROUS MEMBRANE, LAMINATED SEPARATOR, AND NONAQUEOUS ELECTROLYTE SECONDARY BATTERY AND METHOD FOR PRODUCING SAME
US11990640B2 (en) * 2018-12-26 2024-05-21 Sumitomo Chemical Company, Limited α-alumina, slurry, porous membrane, laminated separator, and nonaqueous electrolyte secondary battery and method for producing same
CN110819138A (zh) * 2019-09-29 2020-02-21 浙江安力能源有限公司 一种钠镍电池陶瓷管表面涂层的制作方法
US20230411794A1 (en) * 2021-05-07 2023-12-21 Lg Energy Solution, Ltd. Porous substrate for separator and separator for electrochemical device comprising same

Also Published As

Publication number Publication date
US20180079910A1 (en) 2018-03-22
WO2014017662A1 (ja) 2014-01-30
JPWO2014017662A1 (ja) 2016-07-11
EP2879205B1 (en) 2019-02-06
US10836913B2 (en) 2020-11-17
KR20150039749A (ko) 2015-04-13
EP2879205A4 (en) 2016-04-06
CN104488109A (zh) 2015-04-01
KR101739211B1 (ko) 2017-05-23
JP6067016B2 (ja) 2017-01-25
CN104488109B (zh) 2017-02-22
TW201410799A (zh) 2014-03-16
EP2879205A1 (en) 2015-06-03

Similar Documents

Publication Publication Date Title
US10836913B2 (en) Alumina slurry, method for producing same, and coating liquid
JP6498712B2 (ja) 非水電解液二次電池用セパレータ
US10217982B2 (en) Method for producing laminated porous film
JP6466544B2 (ja) 積層多孔質フィルム
KR102022822B1 (ko) 적층 다공질 필름 및 비수 전해액 이차 전지
JP6017446B2 (ja) 積層多孔質フィルムの製造方法及び積層電極シートの製造方法
JP5743032B1 (ja) 塗工液及び積層多孔質フィルム
TW201308723A (zh) 層合多孔質薄膜及非水電解液蓄電池
WO2012043501A1 (ja) スラリー及び該スラリーを使用したセパレータの製造方法
JP2013014017A (ja) 積層多孔質フィルム
JP6354650B2 (ja) 塗工液及び積層多孔質フィルム
JP2013133418A (ja) 塗工液、積層多孔質フィルム及び積層多孔質フィルムの製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: SUMITOMO CHEMICAL COMPANY, LIMITED, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:OZAKI, HIROTAKA;FUJITA, NORIAKI;REEL/FRAME:034802/0319

Effective date: 20141224

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION