US20140202677A1 - Original plate material for heat-exchanging plate and heat-exchanging plate using the same - Google Patents

Original plate material for heat-exchanging plate and heat-exchanging plate using the same Download PDF

Info

Publication number
US20140202677A1
US20140202677A1 US14/232,549 US201214232549A US2014202677A1 US 20140202677 A1 US20140202677 A1 US 20140202677A1 US 201214232549 A US201214232549 A US 201214232549A US 2014202677 A1 US2014202677 A1 US 2014202677A1
Authority
US
United States
Prior art keywords
heat
projecting parts
plate material
plate
exchanging
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US14/232,549
Other languages
English (en)
Inventor
Yasuyuki Fujii
Akio Okamoto
Yoshio Itsumi
Akihisa Fujita
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Kobe Steel Ltd
Original Assignee
Kobe Steel Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2011246574A external-priority patent/JP5208260B2/ja
Priority claimed from JP2011284605A external-priority patent/JP5208264B2/ja
Application filed by Kobe Steel Ltd filed Critical Kobe Steel Ltd
Assigned to KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) reassignment KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.) ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: FUJII, YASUYUKI, FUJITA, AKIHISA, ITSUMI, YOSHIO, OKAMOTO, AKIO
Publication of US20140202677A1 publication Critical patent/US20140202677A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
    • F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
    • F28F3/04—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
    • F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
    • F28F3/025—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being corrugated, plate-like elements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21C—MANUFACTURE OF METAL SHEETS, WIRE, RODS, TUBES OR PROFILES, OTHERWISE THAN BY ROLLING; AUXILIARY OPERATIONS USED IN CONNECTION WITH METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL
    • B21C37/00—Manufacture of metal sheets, bars, wire, tubes or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape
    • B21C37/02—Manufacture of metal sheets, bars, wire, tubes or like semi-manufactured products, not otherwise provided for; Manufacture of tubes of special shape of sheets
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B21—MECHANICAL METAL-WORKING WITHOUT ESSENTIALLY REMOVING MATERIAL; PUNCHING METAL
    • B21K—MAKING FORGED OR PRESSED METAL PRODUCTS, e.g. HORSE-SHOES, RIVETS, BOLTS OR WHEELS
    • B21K23/00—Making other articles
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F13/00—Arrangements for modifying heat-transfer, e.g. increasing, decreasing
    • F28F13/02—Arrangements for modifying heat-transfer, e.g. increasing, decreasing by influencing fluid boundary
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F13/00—Arrangements for modifying heat-transfer, e.g. increasing, decreasing
    • F28F13/06—Arrangements for modifying heat-transfer, e.g. increasing, decreasing by affecting the pattern of flow of the heat-exchange media
    • F28F13/12—Arrangements for modifying heat-transfer, e.g. increasing, decreasing by affecting the pattern of flow of the heat-exchange media by creating turbulence, e.g. by stirring, by increasing the force of circulation
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
    • F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F21/00—Constructions of heat-exchange apparatus characterised by the selection of particular materials
    • F28F21/08—Constructions of heat-exchange apparatus characterised by the selection of particular materials of metal
    • F28F21/081—Heat exchange elements made from metals or metal alloys
    • F28F21/086—Heat exchange elements made from metals or metal alloys from titanium or titanium alloys
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
    • F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
    • F28F3/04—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element
    • F28F3/042—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element
    • F28F3/044—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element the deformations being pontual, e.g. dimples
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F28—HEAT EXCHANGE IN GENERAL
    • F28F—DETAILS OF HEAT-EXCHANGE AND HEAT-TRANSFER APPARATUS, OF GENERAL APPLICATION
    • F28F3/00—Plate-like or laminated elements; Assemblies of plate-like or laminated elements
    • F28F3/02—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations
    • F28F3/04—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element
    • F28F3/042—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element
    • F28F3/046—Elements or assemblies thereof with means for increasing heat-transfer area, e.g. with fins, with recesses, with corrugations the means being integral with the element in the form of local deformations of the element the deformations being linear, e.g. corrugations

Definitions

  • the present invention relates to an original plate material for a heat-exchanging plate and a heat-exchanging plate using the original plate material.
  • Patent Literature 1 A good heat transfer characteristics are required for a heat-exchanging plate incorporated in a plate-type heat exchanger or the like described in, for example, Patent Literature 1.
  • An object of the present invention is to provide an original plate material for a heat exchanger.
  • the original plate material has a significantly good heat conductivity and a significantly good workability in press forming to be performed in a downstream process, and can be easily formed into a heat-exchanging plate.
  • An original plate material for a heat-exchanging plate according to the present invention is made by forming a fine recess and fine projections on a surface of a metal flat plate material and is subjected to press working performed as a downstream process so as to be used as a heat-exchanging plate.
  • the recess and the projections are set on a surface of the original plate material such that a shape parameter G1 defined as a height of a projecting part in ⁇ m ⁇ [a width of a recessed part in ⁇ m/a pitch between the adjacent projecting parts in ⁇ m] is equal to or smaller than 85 ⁇ m.
  • Another original plate material for a heat-exchanging plate according to the present invention is made by forming a fine recess and fine projections on a surface of a metal flat plate material and is subjected to press working performed as a downstream process so as to be used as a heat-exchanging plate.
  • the recess and the projections are set on a surface of the original plate material such that a shape parameter G2 defined as a height of a projecting part in ⁇ m ⁇ [a width of a recessed part in ⁇ m/a pitch between the adjacent projecting parts in ⁇ m/an angle of the projecting part in deg] is equal to or smaller than 0.94 ⁇ m/deg.
  • a heat-exchanging plate can be fabricated without the occurrence of breakage or the like in press working.
  • the heat-exchanging plate fabricated with the technology of the present invention has a significantly good heat conductivity.
  • FIG. 1 illustrates a method for fabricating a heat-exchanging plate.
  • FIG. 2 illustrates arrangement of projecting parts formed on a surface of an original plate material.
  • FIG. 3 illustrates different arrangement of the projecting parts formed on the surface of the original plate material.
  • FIG. 4 illustrates the relationship between L ⁇ Rz/P and the ratio of concentration of stress.
  • FIG. 6 illustrates the relationship between heat transfer efficiency and the dimensions and shapes of the recessed and projecting shapes formed on the surface of the original plate material, and the relationship between the desirability of the press formability and the dimensions and shapes of the recessed and projecting shapes formed on the surface of the original plate material.
  • FIG. 7 illustrates an outline of a device that forms the recessed and projecting shapes on the surface of the original plate material.
  • FIG. 8 is an explanatory diagram illustrating the shape of the projecting part.
  • FIG. 9 illustrates the relationship between the angle ⁇ of the projecting parts and flows of a fluid.
  • FIG. 10 illustrates the relationship between a shape parameter G2 and the ratio of improvement in heat conductivity.
  • FIG. 11 illustrates the relationships among the shape parameter G2, the ratio of improvement in heat conductivity, and the press formability.
  • FIG. 12 illustrates the relationships among the shape parameter G2, the ratio of improvement in heat conductivity, and the press formability.
  • Titanium is a material having anisotropy.
  • the anisotropy of a material affects its deformation behavior such as a decrease in thickness or strain gradient in a portion where stress is concentrated. For this reason, titanium has significantly poor press formability and the like compared to other materials not having anisotropy.
  • titanium easily causes seizure, the titanium material tends to break or become scratched due to contact with a die for pressing or a tool when lubricant film breakdown occurs while being pressed, and accordingly, titanium is not easily processed.
  • the following successful example with a titanium material can be applied to other metal materials such as stainless steel and aluminum.
  • FIG. 1 is a conceptual view illustrating a method for fabricating a heat-exchanging plate according to a first embodiment.
  • the flat plate material 1 serving as a raw material is formed to have a specified size. Then, the flat plate material 1 is subjected to press working so as to have fine recessed and projecting shapes on a surface 1 a of the flat plate material 1 , thereby producing a plate raw sheet (original plate material) having fine recessed and projecting shapes as illustrated in FIG. 1 ( b ). Next, as illustrated in FIG. 1 ( a ), the flat plate material 1 serving as a raw material is formed to have a specified size. Then, the flat plate material 1 is subjected to press working so as to have fine recessed and projecting shapes on a surface 1 a of the flat plate material 1 , thereby producing a plate raw sheet (original plate material) having fine recessed and projecting shapes as illustrated in FIG. 1 ( b ). Next, as illustrated in FIG.
  • the plate raw sheet 2 original plate material
  • the plate raw sheet 2 original plate material having the fine recessed and projecting shapes on a surface 2 a
  • herringbone which is a plurality of chevron-shaped grooves having a height of less than 10 mm to less than 10 cm by press-forming.
  • a heat-exchanging plate 4 is fabricated.
  • the flat plate material 1 illustrated in FIG. 1 ( a ) is made of titanium, and the dimensions and thickness thereof are determined with consideration of dimensions and thickness desired for the heat-exchanging plate 4 as a finished product.
  • the plate raw sheet 2 is fabricated by forming the fine recessed and projecting shapes (made of a plurality of projecting parts 5 and a recessed part 6 interposed therebetween) using a process device 10 , which will be described later, on the surface 1 a of the flat plate material 1 .
  • the plate raw sheet 2 having the recessed and projecting shapes formed thereon has a significantly good heat conductivity (a significantly high heat transfer coefficient).
  • the plate raw sheet 2 according to the present invention is made of titanium, the characteristics of which such as corrosion resistance and strength are good and the weight of which is light compared to other metal materials.
  • the plate raw sheet 2 is preferably used in products for which corrosion resistance and strength are required such as a plate for a plate-type heat exchanger.
  • a herringbone 3 formed in the plate raw sheet 2 includes a plurality of chevron-shaped grooves, which appear like a skeleton shape, and the size of the grooves is from less than 10 mm to less than 10 cm in height.
  • the raw sheet 2 is incorporated in a heat exchanger. Even when a flow of a working fluid in the heat exchanger is not uniform, recesses and projections of inclined grid-like shapes, typical examples of which include the herringbone 3 , can serve as walls perpendicular to the working fluid flowing from any direction, and accordingly, contribute to improvement of heat conductivity due to turbulence.
  • the projecting parts 5 formed on a surface 2 a of the plate raw sheet 2 each have a substantially circular shape in plan view and a diameter D of equal to or greater than 400 ⁇ m.
  • the projecting parts 5 are arranged in a staggered manner in plan view.
  • arrangement in a staggered manner means that the centers of the projecting parts 5 adjacent to each other in a vertical and horizontal direction are non-collinear with each other.
  • the projecting parts 5 adjacent to each other in the vertical direction may be shifted to each other by a half pitch in the horizontal direction in the plate raw sheet 2 .
  • the projecting parts 5 may be arranged such that a line (dotted-chain line) A connecting the centers of the adjacent projecting parts 5 to one another in the horizontal direction forms an angle ⁇ of 60° with a line (dotted-chain line) B connecting the centers of the adjacent projecting parts 5 to one another in the vertical direction (Y-direction).
  • the recess and projections can serve as walls perpendicular to the working fluid flowing from any direction, and accordingly, contribute to improvement of heat conductivity due to turbulence. Also, concentration of stress due to anisotropy of titanium or other materials having anisotropy can be addressed.
  • the distance L between the projecting parts 5 (width L of the recessed part 6 ) adjacent to each other in the vertical or horizontal direction is equal to or greater than 200 ⁇ m.
  • the pitch P between the adjacent projecting parts 5 means the distance between the centers of the projecting parts 5 most closely adjacent to each other in the horizontal or vertical direction (distance between the centers of the projecting parts 5 spaced apart from each other by the shortest distance).
  • the width L of the recessed part 6 illustrated in FIG. 2 ( a ) is the same in the vertical and horizontal directions. That is, the distance between the projecting parts 5 adjacent to each other in the vertical direction and the distance between the projecting parts 5 adjacent to each other in the horizontal direction are the same.
  • the pitch P (distance between the centers of the projecting parts 5 ) of the adjacent projecting parts 5 is equal to or greater than 600 ⁇ m.
  • the projecting parts 5 formed on the surface of the plate raw sheet 2 each have a substantially trapezoidal shape in sectional view having a side wall 7 that extend upward and a front wall 8 that closes an upper edge of the side wall 7 in a direction parallel to the surface 2 a .
  • the projecting parts 5 have a flat portion at its top.
  • the height Rz of the projecting parts 5 (side wall 7 ) expressed as ten-point average roughness (may also be referred to as height Rz hereafter) is equal to or greater than 5 ⁇ m, and equal to or smaller than 1/10 (one tenth) of the thickness t of the plate raw sheet 2 .
  • the above-described range of the height Rz of the projecting parts 5 is determined since, when the recessed and projecting shapes are excessively large relative to the thickness, during roll transfer using the process device 10 , which will be described later, flatness (shape) cannot be ensured, and accordingly, stability in rolling cannot be obtained. Furthermore, when a plate is press-formed in a downstream process, if the flatness of the plate is not ensured, stress distribution occurs, and accordingly, the plate breaks in portions of the plate where stress is higher. That is, the projecting parts 5 having an excessively large height Rz cause (become the starting points of) breaks in press working and cause scratches. In contrast, when the height Rz is excessively small (equal to or smaller than 5 ⁇ m), the heat transfer efficiency cannot be improved.
  • the shape of the projecting part 5 in plan view includes not only a perfect circle but also an ellipse, with a flattening of up to about 0.2.
  • the projecting part 5 having a polygonal shape or another shape in plan view also seems possible, the projecting part 5 preferably has a substantially circular shape in plan view from the viewpoint of avoiding concentration of stress in press working to be performed in a downstream process.
  • the staggered arrangement of the projecting parts 5 is not limited to that illustrated in FIG. 2 .
  • the projecting parts 5 may be arranged such that a line (dotted-chain line) A′ connecting the centers of the adjacent projecting parts 5 to one another in the horizontal direction forms an angle ⁇ of 45° with a line (dotted-chain line) B′ connecting the centers of the adjacent projecting parts 5 to one another in the vertical direction.
  • the angle ⁇ may be other than 45°.
  • the recessed and projecting shapes of the plate raw sheet 2 as described above are based on the findings as follows.
  • the inventors In fabricating the plate raw sheet 2 , in order for the height Rz of the projecting parts 5 , the number of the projecting parts 5 (the width L of the recessed part 6 ), and the pitch P between the adjacent projecting parts formed on the surface of the plate raw sheet 2 to satisfy desirable requirements (such as heat transfer characteristics), the inventors have found the following shape parameter G1 of the recessed and projecting shapes including the above-described dimensions and the like: “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)”.
  • the height Rz of the projecting parts 5 or the width L of the recessed part 6 is not excessively large and the pitch P between the projecting parts is not excessively small.
  • the shape parameter G1 that represents these is thought to have an upper limit.
  • the inventors have clarified the relationships between the shape parameter G1 defined as “[height Rz of projecting parts 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts])” and press formability for the plate raw sheet 2 formed of titanium and having a variety of the recessed and projecting shapes through experiments and the like.
  • the herringbone (grooves) 3 is initially formed in the original plate raw sheet 2 so as to form the heat-exchanging plate 4 .
  • a piece of die for formation is initially prepared in accordance with the working conditions of the heat exchanger.
  • the herringbone 3 is formed in the plate raw sheet 2 by using the die.
  • a plurality of the heat-exchanging plates 4 are fabricated.
  • the plurality of heat-exchanging plates 4 are fabricated such that the heat-exchanging plates 4 having a formation height that is incremented by 0.1 mm from one plate to another.
  • a formation limit height of the die with which no necking occurs is evaluated as an indentation amount.
  • FIG. 6 illustrates a press formability score, which is the above-described indentation amount having been normalized. The inventors have confirmed that, when the press formability score is equal to or greater than 1, press-forming can be reliably performed while the occurrence of necking is prevented.
  • the press formability score decreases.
  • the press formability score can be equal to or greater than 1.
  • the occurrence of necking can be prevented. That is, when the shape parameter G1 is equal to or smaller than 85 ⁇ m, the occurrence of necking can be prevented, and accordingly, a decrease in press formability can be avoided.
  • the shape parameter G1 is equal to or smaller than 65 ⁇ m, seizure or an increase in local bearing pressure occurring due to non-uniform distribution of a lubricating state caused by an increase in the height of the recess and projection can be further prevented. Because of this, it has been confirmed by the inventors through an experiment and the like that the heat-exchanging plate 4 can be reliably fabricated without troubles with press working.
  • the plate raw sheet 2 according to the present invention is a material of a plate that is part the heat exchanger, specifically, a material processed to form a bulkhead for exchanging heat.
  • the plate raw sheet 2 according to the present invention is also required to have a large heat transfer coefficient (large heat transfer efficiency).
  • heat transfer efficiency of a plate having recessed or projecting shapes compared to heat transfer efficiency of “a flat plate without recessed and projecting shapes”
  • the heat transfer efficiency of the heat-exchanging plate needs to be greater than 1.00.
  • the relationship between the heat transfer efficiency and the shape parameter G1 is discussed.
  • the shape parameter G1 gradually decreases from 85 ⁇ m.
  • the heat transfer efficiency also gradually decreases as illustrated in FIG. 6 . This makes the heat transfer efficiency become closer to that of the flat plate without the recessed or projecting parts formed thereon.
  • the shape parameter G1 is equal to or greater than 4 ⁇ m, the heat transfer efficiency required for the actual heat exchanger (equal to or greater than 1.05) can be ensured.
  • the shape parameter G1 be equal to or greater than 4 ⁇ m when fabricating the plate raw sheet 2 . It is more preferable that the shape parameter G1 be greater than 12 ⁇ m, and specifically, the shape parameter G1 be greater than 12 ⁇ m and equal to or smaller than 85 ⁇ m.
  • the shape parameter G1 decreases.
  • the recessed part 6 having an excessively small width L causes heat conductivity to be decreased.
  • the width L of the recessed part 6 of a certain degree of size be ensured. That is, it is thought to be necessary that the shape parameter G1 also be of a certain degree of magnitude.
  • the shape parameter G1 of a certain degree of magnitude needs to be ensured while the shape parameter G1 is equal to or smaller than 85 ⁇ m. Specifically, as described above, it is thought that the shape parameter needs to be equal to or greater than 4 ⁇ m.
  • the shape parameter G1 By setting the shape parameter G1 to a value in a range from 4 ⁇ m to 85 ⁇ m, and as described above, setting the height Rz of the projecting parts 5 expressed as ten-point average roughness Rz to equal to or greater than 5 ⁇ m and to (thickness of flat plate material ⁇ 0.1) ⁇ m, the width L of the recessed part 6 (or the pitch P between the projecting parts 5 ) is automatically determined (found).
  • the ratio S of pressure contact areas in the plate raw sheet 2 satisfy an expression (1) for the recessed and projecting shapes illustrated in FIG. 2 ( a ):
  • S1 is an area of a plane in FIG. 2 (area of a triangle surrounded by the line A and the lines B in FIG. 2 ).
  • S2 is the area of the projecting parts 5 in FIG. 2 (area of the projecting parts existing within the above-described triangle).
  • the heat-exchanging plate 4 which is part of the heat exchanger, can be fabricated without the occurrence of breakage or the like during press working.
  • the heat-exchanging plate 4 fabricated as described above has a heat exchanger effectiveness of equal to or greater than 1.05 and exhibits a significantly good heat conductivity.
  • a heat exchanger in which this heat-exchanging plate 4 is incorporated has a significantly high heat exchanger efficiency.
  • the above-described plate raw sheet 2 can be formed using the process device 10 as illustrated in FIG. 7 .
  • the process device 10 includes transport rollers 11 , a process roller 12 , and a support roller 13 .
  • the transport rollers 11 transport the flat plate material 1 and are disposed on the upstream side and the downstream side of the process roller 12 .
  • the process roller 12 forms a recess and projections in the order of micrometers (smaller than 10 ⁇ m to smaller than one mm) on the surface of the flat plate material 1 being transported. Specifically, the process roller 12 forms the recessed and projecting parts 5 and 6 on the surface 1 a of the flat plate material 1 such that the shape parameter G1 of the plate raw sheet 2 after processing is within a range from 4 ⁇ m to 85 ⁇ m. That is, the height Rz of the projecting parts 5 , the width L of the recessed part 6 , and the pitch P between the adjacent projecting parts 5 are set in the process roller 12 in order to form the recessed and projecting parts 5 and 6 so as to satisfy the shape parameter G1 in the range from 4 to 85 ⁇ m.
  • Process portions 14 each having a projecting shape are formed over a whole area of an outer peripheral surface of the process roller 12 by etching or electro-discharge texturing.
  • the height of the process portions 14 is set such that the height Rz of the projecting parts 5 in the plate raw sheet 2 after processing is equal to or greater than 5 ⁇ m and equal to or smaller than (thickness t of flat plate material ⁇ 0.1) ⁇ m. It is desirable that a surface layer of the process roller 12 be Cr-plated or tungsten-carbide coated from the viewpoint of load bearing characteristics and wear resistance.
  • the process device 10 presses the process portions 14 provided on the process roller 12 against the surface of the flat plate material 1 while the process roller 12 is being rotated.
  • the recessed part 6 and projecting parts 5 which are complementarily shaped with respect to the process portions 14 , is formed on the surface of the flat plate material 1 . That is, by using the process device 10 , the plate raw sheet 2 having the recessed and projecting shapes can be formed, the shape parameter G1 of which is from 4 ⁇ m to 85 ⁇ m and the height Rz of which is equal to or greater than 5 ⁇ m and equal to or smaller than 10% of the plate thickness t.
  • the method of forming the projecting parts 5 is not limited to machining using the above-described process device or the like.
  • the projecting parts 5 may be formed by chemical processing such as etching.
  • the heat-exchanging plate 4 is fabricated in press working performed on the plate raw sheet 2 according to the present invention.
  • This press working performed on the plate raw sheet 2 may be any press working and not limited to the foregoing press working that forms the herringbone.
  • the range from 4 ⁇ m to 85 ⁇ m of the shape parameter G1 be satisfied in at least part of the plate raw sheet 2 , and it is preferable that this range of the shape parameter G1 be satisfied over the entirety of the plate raw sheet 2 .
  • a second embodiment is described below. Description common to the above-described first embodiment and the second embodiment is omitted as appropriate.
  • the projecting parts 5 formed on the surface 2 a of the plate raw sheet 2 each have the side wall 7 and the front wall 8 .
  • the side wall 7 stands erect in the thickness direction (thickness direction of the plate raw sheet 2 ).
  • the front wall 8 closes the upper end (upper edge) of the side wall 7 .
  • the projecting parts 5 have a flat portion at its top.
  • the projecting parts 5 have a cylindrical shape or a conical shape
  • the projecting parts 5 have a single side wall 7 .
  • the projecting parts 5 have a square rod shape or a pyramid shape
  • the projecting parts 5 have a plurality of side walls 7 .
  • the projecting parts 5 formed on the surface 2 a of the plate raw sheet 2 each have a substantially circular shape in plan view and a diameter D of equal to or greater than 400 ⁇ m. It is preferable that the projecting parts 5 be arranged in a staggered manner in plan view as is the case with the first embodiment, and the pitch P between the adjacent projecting parts 5 (the distance between the centers of the projecting parts 5 , that is, the distance between the centers of the front walls 8 ), be equal to or greater than 600 ⁇ m.
  • the projecting parts 5 formed on the surface of the plate raw sheet 2 have a substantially trapezoidal shape as illustrated in FIG. 2 ( b ).
  • the height (height Rz) of the projecting parts 5 (side wall 7 ) expressed as ten-point average roughness Rz is equal to or greater than 5 ⁇ m, and equal to or smaller than 1/10 (one tenth) of the thickness t of the plate raw sheet 2 .
  • Rz of the projecting parts 5 of the plate raw sheet 2 is, for example, about 25 ⁇ m (about 10 ⁇ m when expressed as Ra).
  • the recessed and projecting shapes of the plate raw sheet 2 according to the second embodiment are based on the findings as follows.
  • the inventors In fabricating the plate raw sheet 2 , in order to optimize the height Rz of the projecting parts 5 , the number of the projecting parts 5 (the width L of the recessed part 6 ), the pitch P between the adjacent projecting parts, and the angle ⁇ of the projecting parts formed on the surface of the plate raw sheet 2 , the inventors have focused on the following shape parameter G2 of the recessed and projecting shapes including the above-described values: “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts])/angle ⁇ of projecting part”.
  • the height Rz of the projecting parts 5 or the width L of the recessed part 6 is not excessively large and the pitch P between the projecting parts is not excessively small, and a parameter that expresses these values has an upper limit.
  • FIG. 6 summarizes the relationship between the press formability and the heat transfer efficiency when the parameter defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)”, which does not include the above-described rising angle ⁇ of the projecting parts, is changed.
  • the press formability score illustrated in FIG. 6 represents the normalized indentation amount described below.
  • an evaluation test for evaluating the formability in press working is the same as that of the first embodiment and description thereof is omitted.
  • the press formability score decreases.
  • the press formability score can be equal to or greater than 1.
  • the plate raw sheet 2 according to the present invention is a material of a plate that is part the heat exchanger, specifically, a material processed to form a bulkhead for exchanging heat.
  • the heat transfer efficiency be equal to or greater than 1.05.
  • the relationship between the heat transfer efficiency and the parameter is discussed.
  • the parameter gradually decreases from 85 ⁇ m.
  • the heat transfer efficiency also gradually decreases as illustrated in FIG. 6 . This makes the heat transfer efficiency become closer to that of the flat plate without the recessed or projecting parts formed thereon.
  • the parameter is equal to or greater than 4 ⁇ m, the heat transfer efficiency required for the actual heat exchanger (equal to or greater than 1.05) can be ensured.
  • the parameter defined as “height Rz of projecting part 5 ⁇ width L of recessed part 6 /pitch P between adjacent projecting parts” be from 4 ⁇ m to 85 ⁇ m.
  • the plate raw sheet 2 having a good press formability and a good heat conductivity can be fabricated.
  • a fluid, the temperature of which is high is caused to flow on a rear side (one side); and a fluid, the temperature of which is low (low-temperature fluid), is caused to flow on a front side (the other side and a side on which the recessed and projecting surface is formed).
  • the low-temperature fluid may be changed from a gas to a liquid (condensed) or remain in a liquid state. In either case, in order to increase the heat transfer efficiency of the heat-exchanging plate 4 , it is important to cause turbulence or forced convection on the low-temperature fluid (liquid) side.
  • the inventors have also examined the shape of the projecting part 5 , with which turbulence or forced convection is easily caused, by considering not only the height Rz of the projecting parts 5 , the width L of the recessed part 6 , and the pitch P between the projecting parts 5 , but also the angle ⁇ of the projecting parts 5 (rising angle ⁇ of the side walls 7 ).
  • FIG. 9 ( a ) schematically illustrates a flow of the fluid when the angle ⁇ of the projecting parts 5 is large.
  • FIG. 9 ( b ) schematically illustrates a flow of the fluid when the angle ⁇ of the projecting parts 5 is smaller than that illustrated in FIG. 9 ( a ).
  • the inventors have studied the more suitable shape parameter G2 that includes the angle ⁇ of the projecting parts 5 , which affects heat conductivity, in addition to the height Rz of the projecting parts 5 , the width L of the recessed part 6 , and the pitch P between the projecting parts 5 .
  • the shape parameter G2 defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)/angle ⁇ (deg) of projecting part 5 ” is obtained by dividing the above-described parameter defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)” by the angle ⁇ of the projecting parts 5 .
  • FIG. 10 summarizes the relationship between the shape parameter G2 and the ratio of improvement in heat conductivity.
  • the tendency of the heat transfer efficiency in condensation when the shape parameter G2 is increased and decreased is similar to the tendency of the heat transfer efficiency in forced convection. From this, it can be said that the above-described shape parameter G2 is most suitable for representing heat transfer characteristics in condensation and forced convection.
  • FIG. 11 summarizes the relationship between the press formability and the heat transfer efficiency when the shape parameter G2 defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)/angle ⁇ (deg) of projecting part”, which includes the rising angle ⁇ of the projecting parts, is changed.
  • the press formability score decreases.
  • the shape parameter G2 is equal to or smaller than 0.94 ⁇ m/deg
  • the press formability score can be equal to or greater than 1.
  • press-forming can be reliably performed while the occurrence of necking is prevented. That is, when the shape parameter for also considering condensation and forced convection is equal to or smaller than 0.94 ⁇ m/deg, the occurrence of necking can be prevented and a reduction in press formability can be avoided.
  • the shape parameter G2 which is obtained by multiplying the parameter defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)” by the angle ⁇ of the projecting parts 5 , is equal to or smaller than 0.94 ⁇ m/deg, the plate raw sheet 2 having a significantly good heat conductivity and suitable for press-forming can be fabricated.
  • the shape parameter G2 needs to be equal to or greater than 0.14 ⁇ m/deg.
  • the shape parameter G2 is equal to or greater than 0.16 ⁇ m/deg, and more preferably, the shape parameter G2 is equal to or greater than 0.2 ⁇ m/deg.
  • the ratio S of pressure contact areas in the plate raw sheet 2 satisfy the expression (1) for the recessed and projecting shapes illustrated in FIG. 2 ( a ).
  • S1 is an area of a plane in FIG. 2 (area of the triangle surrounded by the line A and the lines B in FIG. 2 ).
  • S2 is the area of the projecting parts 5 in FIG. 2 (area of the projecting parts existing within the above-described triangle).
  • the heat-exchanging plate 4 which is part of the heat exchanger, can be fabricated without the occurrence of breakage or the like during press working.
  • the heat-exchanging plate 4 fabricated as above has a significantly good heat conductivity and can be used as a gas-liquid heat-exchanging plate and a liquid-liquid heat-exchanging plate.
  • the above-described plate raw sheet 2 can be formed using the process device 10 as illustrated in FIG. 7 similarly to the first embodiment.
  • the height Rz of the projecting parts 5 , the width L of the recessed part 6 , the pitch P between the adjacent projecting parts 5 , and the angle ⁇ of the projecting parts are set in the process roller 12 in order to form the recessed and projecting parts 5 and 6 so as to satisfy the shape parameter G2 in the range from 0.14 to 0.94 ⁇ m/deg.
  • the shape parameter G2 including the rising angle ⁇ of the projecting parts 5 is 0.14 to 0.94 ⁇ m/deg.
  • the shape parameter G2 is further examined through an experience and the like. Description of the same structures as those of the second embodiment is omitted.
  • FIG. 12 summarizes the relationship between the press formability and the heat transfer efficiency when the shape parameter G2 defined as “height Rz of projecting part 5 ⁇ (width L of recessed part 6 /pitch P between adjacent projecting parts)/angle ⁇ (deg) of projecting part”, which includes the rising angle ⁇ of the projecting parts, is changed.
  • the press formability score decreases.
  • the press formability score can be equal to or greater than 1.
  • the shape parameter G2 for also considering condensation and forced convection is equal to or smaller than 0.94 ⁇ m/deg
  • the occurrence of necking can be prevented and a reduction in press formability can be avoided.
  • the upper limit of the shape parameter G2 needs to be equal to or smaller than 0.94 ⁇ m/deg.
  • the heat transfer efficiency needs to be equal to or greater than 1.05.
  • the heat-exchanging plate 4 is also used as, for example, a gas-liquid or liquid-liquid heat-exchanging plate, it is sufficient that the heat transfer efficiency of equal to or greater than 1.03 be ensured.
  • the shape parameter G2 is equal to or greater than 0.028 ⁇ m/deg
  • the heat transfer efficiency can be equal to or greater than 1.03.
  • the lower limit of the shape parameter G2 be 0.028 ⁇ m/deg.
  • the filled circles representing forced convection are superposed with the hollow circles representing condensation, and values in forced convection are substantially the same as values in condensation.
  • the recess and projections are formed by using the process device 10 (process roller 12 ) such that the shape parameter G2 is 0.028 to 0.94 ⁇ m/deg.
  • the details of the fabricating method are the same as the above-described embodiments and description thereof is omitted.
  • the range from 0.14 to 0.94 ⁇ m/deg of the shape parameter G2 be satisfied in at least part of the plate raw sheet 2 , and it is preferable that this range of the shape parameter G2 be satisfied over the entirety of the plate raw sheet 2 .
  • the original plate material for a heat-exchanging plate according to the present invention and the heat-exchanging plate using the original plate material is preferable as the original plate for a plate of a heat exchanger used for electric generation by temperature difference and the like and a heat-exchanging plate using the original plate.

Landscapes

  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • General Engineering & Computer Science (AREA)
  • Shaping Metal By Deep-Drawing, Or The Like (AREA)
  • Heat-Exchange Devices With Radiators And Conduit Assemblies (AREA)
US14/232,549 2011-09-16 2012-09-14 Original plate material for heat-exchanging plate and heat-exchanging plate using the same Abandoned US20140202677A1 (en)

Applications Claiming Priority (9)

Application Number Priority Date Filing Date Title
JP2011-203423 2011-09-16
JP2011-203422 2011-09-16
JP2011203423 2011-09-16
JP2011203422 2011-09-16
JP2011-246574 2011-11-10
JP2011246574A JP5208260B2 (ja) 2011-09-16 2011-11-10 熱交換用プレートの元板材、及び熱交換用プレートの元板材の製造方法
JP2011284605A JP5208264B2 (ja) 2011-09-16 2011-12-27 熱交換用プレートの元板材、及び熱交換用プレートの元板材の製造方法
JP2011-284605 2011-12-27
PCT/JP2012/073661 WO2013039214A1 (ja) 2011-09-16 2012-09-14 熱交換用プレートの元板材、及びこれを用いた熱交換用プレート

Publications (1)

Publication Number Publication Date
US20140202677A1 true US20140202677A1 (en) 2014-07-24

Family

ID=50573002

Family Applications (1)

Application Number Title Priority Date Filing Date
US14/232,549 Abandoned US20140202677A1 (en) 2011-09-16 2012-09-14 Original plate material for heat-exchanging plate and heat-exchanging plate using the same

Country Status (7)

Country Link
US (1) US20140202677A1 (ko)
EP (1) EP2757341B1 (ko)
KR (1) KR101563830B1 (ko)
CN (1) CN103782125B (ko)
DK (1) DK2757341T3 (ko)
PL (1) PL2757341T3 (ko)
WO (1) WO2013039214A1 (ko)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3382315A1 (en) * 2017-03-31 2018-10-03 BSH Hausgeräte GmbH Household appliance comprising at least one metal component
CN108691178A (zh) * 2017-03-31 2018-10-23 Bsh家用电器有限公司 包括至少一个金属的部件的家用器具
US20220299244A1 (en) * 2021-03-19 2022-09-22 Daikin Industries, Ltd. Shell and plate heat exchanger for water-cooled chiller and water-cooled chiller including the same

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6219199B2 (ja) * 2014-02-27 2017-10-25 株式会社神戸製鋼所 熱交換用プレートとなる元板材、及びその元板材の製造方法
JP2015175507A (ja) * 2014-03-18 2015-10-05 株式会社神戸製鋼所 チタン溶接管、及びチタン溶接管の製造方法
JP2015193922A (ja) * 2014-03-24 2015-11-05 三菱重工業株式会社 撥液化する表面微細構造並びにその製造方法、熱交換器、および空気調和機の構成要素
CN104279905A (zh) * 2014-10-14 2015-01-14 上海板换机械设备有限公司 用于蒸发或冷凝过程的强化传热元件
EP3023727B1 (en) * 2014-11-24 2020-01-08 Taiwan SRP Heat Exchanger Inc. Fluid guide plate and associated plate heat exchanger
KR101839245B1 (ko) * 2016-12-14 2018-03-15 주식회사 포스코 압연롤 및 이에 의해 제조된 도금강판

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040231393A1 (en) * 2001-06-07 2004-11-25 Tetsuya Mega High tensile hot-rolled steel sheet excellent in resistance to scuff on mold and in fatigue characteristics
US20100127125A1 (en) * 2008-08-05 2010-05-27 Ming Li Metal sheets and plates having friction-reducing textured surfaces and methods of manufacturing same
US20120052241A1 (en) * 2009-02-17 2012-03-01 The Board Of Trustees Of The University Of Illinoi S Flexible Microstructured Superhydrophobic Materials

Family Cites Families (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2290623A1 (fr) * 1974-11-06 1976-06-04 Lorraine Laminage Tole pour emboutissage profond ou extraprofond et procede d'obtention d'une telle tole
CA1155107A (en) * 1981-02-11 1983-10-11 Theodore C. Carnavos Heat transfer boiling surface
JP2995950B2 (ja) * 1991-10-04 1999-12-27 住友金属工業株式会社 冷間圧延用ロールおよび金属板の圧延方法
CA2126458A1 (en) * 1991-12-25 1993-07-08 Tetsuya Nishiura Steel sheet excellent in coating sharpness, defect-formation resistance and workability
WO1995007774A1 (en) * 1993-09-17 1995-03-23 Sidmar N.V. Method and device for manufacturing cold rolled metal sheets or strips, and metal sheets or strips obtained
DE9408904U1 (de) * 1994-05-31 1994-08-11 Hans Güntner GmbH, 82256 Fürstenfeldbruck Plattenwärmeaustauscher
KR100407377B1 (ko) * 2001-10-30 2003-11-28 전자부품연구원 마이크로 소자의 제조 방법 및 그를 성형하기 위한 금형의제조 방법
DE10159860C2 (de) * 2001-12-06 2003-12-04 Sdk Technik Gmbh Wärmeübertragungsfläche mit einer aufgalvanisierten Mikrostruktur von Vorsprüngen
JP2009192140A (ja) 2008-02-14 2009-08-27 Atago Seisakusho:Kk プレート式熱交換器
CN201827175U (zh) * 2009-04-17 2011-05-11 美铝公司 运输器
JP4638951B2 (ja) * 2009-06-08 2011-02-23 株式会社神戸製鋼所 熱交換用の金属プレート及び熱交換用の金属プレートの製造方法
AU2010341861B2 (en) * 2010-01-15 2015-04-23 Rigidized Metals Corporation Methods of forming enhanced-surface walls for use in apparatae

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20040231393A1 (en) * 2001-06-07 2004-11-25 Tetsuya Mega High tensile hot-rolled steel sheet excellent in resistance to scuff on mold and in fatigue characteristics
US20100127125A1 (en) * 2008-08-05 2010-05-27 Ming Li Metal sheets and plates having friction-reducing textured surfaces and methods of manufacturing same
US20120052241A1 (en) * 2009-02-17 2012-03-01 The Board Of Trustees Of The University Of Illinoi S Flexible Microstructured Superhydrophobic Materials

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3382315A1 (en) * 2017-03-31 2018-10-03 BSH Hausgeräte GmbH Household appliance comprising at least one metal component
CN108691178A (zh) * 2017-03-31 2018-10-23 Bsh家用电器有限公司 包括至少一个金属的部件的家用器具
US20220299244A1 (en) * 2021-03-19 2022-09-22 Daikin Industries, Ltd. Shell and plate heat exchanger for water-cooled chiller and water-cooled chiller including the same
US11976856B2 (en) * 2021-03-19 2024-05-07 Daikin Industries, Ltd. Shell and plate heat exchanger for water-cooled chiller and water-cooled chiller including the same

Also Published As

Publication number Publication date
DK2757341T3 (da) 2020-07-27
EP2757341A1 (en) 2014-07-23
WO2013039214A1 (ja) 2013-03-21
KR101563830B1 (ko) 2015-10-27
EP2757341B1 (en) 2020-05-13
KR20140049595A (ko) 2014-04-25
CN103782125B (zh) 2016-06-22
EP2757341A4 (en) 2015-10-21
CN103782125A (zh) 2014-05-07
PL2757341T3 (pl) 2020-09-21

Similar Documents

Publication Publication Date Title
US20140202677A1 (en) Original plate material for heat-exchanging plate and heat-exchanging plate using the same
US9656313B2 (en) Original plate material for heat-exchanging plate, and method for fabricating original plate material for heat-exchanging plate
EP2442059B1 (en) Metal plate used for heat exchange and method for manufacturing metal plate used for heat exchange
CN110303079B (zh) 一种双金属复合板的交叉波纹轧制方法
EP3133683A1 (en) Fine mold for molding fuel cell separator, method for manufacturing fuel cell separator, and fuel cell separator
US20160363395A1 (en) Plate for use as heat exchange plate and method for manufacturing such base plate
JP5208260B2 (ja) 熱交換用プレートの元板材、及び熱交換用プレートの元板材の製造方法
JP5631287B2 (ja) 熱交換用プレートの元板材、及び熱交換用プレートの元板材の製造方法
JP5208264B2 (ja) 熱交換用プレートの元板材、及び熱交換用プレートの元板材の製造方法
JP6805925B2 (ja) 差厚板材の製造方法、及び差厚板材
JP5872389B2 (ja) チタン板の製造方法及びチタン板
JP5839945B2 (ja) 熱交換用プレートの元板材
JP6153584B2 (ja) 金属プレートの製造方法、及び該製造方法により製造された金属プレートのプレート式熱交換器への使用
CN105327936A (zh) 板材加工方法及板材
CN109926458A (zh) 一种表面油膜稳定的薄带钢及其生产方法
CN214694310U (zh) 一种承载冷轧钢带卷的对流板
JP5911752B2 (ja) 熱交換用プレートとなる元板材の製造方法
CN206738376U (zh) 一种汽车用高硬度耐磨转轴
CN108131979A (zh) 一种外曲线翅片管
JP2013226609A (ja) 構造部材表面の加工方法及び構造部材

Legal Events

Date Code Title Description
AS Assignment

Owner name: KABUSHIKI KAISHA KOBE SEIKO SHO (KOBE STEEL, LTD.)

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:FUJII, YASUYUKI;OKAMOTO, AKIO;ITSUMI, YOSHIO;AND OTHERS;REEL/FRAME:031954/0722

Effective date: 20130201

STCB Information on status: application discontinuation

Free format text: ABANDONED -- AFTER EXAMINER'S ANSWER OR BOARD OF APPEALS DECISION