Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L75/00—Compositions of polyureas or polyurethanes; Compositions of derivatives of such polymers
  • C08L75/04—Polyurethanes
  • C08L75/08—Polyurethanes from polyethers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/30—Low-molecular-weight compounds
  • C08G18/32—Polyhydroxy compounds; Polyamines; Hydroxyamines
  • C08G18/3203—Polyhydroxy compounds
  • C08G18/3206—Polyhydroxy compounds aliphatic
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L75/00—Compositions of polyureas or polyurethanes; Compositions of derivatives of such polymers
  • C08L75/04—Polyurethanes
• • B—PERFORMING OPERATIONS; TRANSPORTING
  • B29—WORKING OF PLASTICS; WORKING OF SUBSTANCES IN A PLASTIC STATE IN GENERAL
  • B29C—SHAPING OR JOINING OF PLASTICS; SHAPING OF MATERIAL IN A PLASTIC STATE, NOT OTHERWISE PROVIDED FOR; AFTER-TREATMENT OF THE SHAPED PRODUCTS, e.g. REPAIRING
  • B29C33/00—Moulds or cores; Details thereof or accessories therefor
  • B29C33/38—Moulds or cores; Details thereof or accessories therefor characterised by the material or the manufacturing process
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/30—Low-molecular-weight compounds
  • C08G18/32—Polyhydroxy compounds; Polyamines; Hydroxyamines
  • C08G18/3225—Polyamines
  • C08G18/3234—Polyamines cycloaliphatic
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/40—High-molecular-weight compounds
  • C08G18/48—Polyethers
  • C08G18/4866—Polyethers having a low unsaturation value
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/28—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the compounds used containing active hydrogen
  • C08G18/65—Low-molecular-weight compounds having active hydrogen with high-molecular-weight compounds having active hydrogen
  • C08G18/66—Compounds of groups C08G18/42, C08G18/48, or C08G18/52
  • C08G18/6666—Compounds of group C08G18/48 or C08G18/52
  • C08G18/667—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38
  • C08G18/6674—Compounds of group C08G18/48 or C08G18/52 with compounds of group C08G18/32 or polyamines of C08G18/38 with compounds of group C08G18/3203
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
  • C08G18/75—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G18/00—Polymeric products of isocyanates or isothiocyanates
  • C08G18/06—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen
  • C08G18/70—Polymeric products of isocyanates or isothiocyanates with compounds having active hydrogen characterised by the isocyanates or isothiocyanates used
  • C08G18/72—Polyisocyanates or polyisothiocyanates
  • C08G18/74—Polyisocyanates or polyisothiocyanates cyclic
  • C08G18/75—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic
  • C08G18/758—Polyisocyanates or polyisothiocyanates cyclic cycloaliphatic containing two or more cycloaliphatic rings
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L53/00—Compositions of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L75/00—Compositions of polyureas or polyurethanes; Compositions of derivatives of such polymers
  • C08L75/02—Polyureas
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G2140/00—Compositions for moulding powders
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L2205/00—Polymer mixtures characterised by other features
  • C08L2205/03—Polymer mixtures characterised by other features containing three or more polymers in a blend
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
  • C08L23/16—Elastomeric ethene-propene or ethene-propene-diene copolymers, e.g. EPR and EPDM rubbers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
  • C08L23/26—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
  • C08L33/02—Homopolymers or copolymers of acids; Metal or ammonium salts thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L33/00—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
  • C08L33/04—Homopolymers or copolymers of esters
  • C08L33/06—Homopolymers or copolymers of esters of esters containing only carbon, hydrogen and oxygen, which oxygen atoms are present only as part of the carboxyl radical
  • C08L33/062—Copolymers with monomers not covered by C08L33/06
  • C08L33/064—Copolymers with monomers not covered by C08L33/06 containing anhydride, COOH or COOM groups, with M being metal or onium-cation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
  • C08L75/00—Compositions of polyureas or polyurethanes; Compositions of derivatives of such polymers
  • C08L75/04—Polyurethanes
  • C08L75/14—Polyurethanes having carbon-to-carbon unsaturated bonds
  • C08L75/16—Polyurethanes having carbon-to-carbon unsaturated bonds having terminal carbon-to-carbon unsaturated bonds
• • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
  • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
  • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
  • Y10T428/00—Stock material or miscellaneous articles
  • Y10T428/31504—Composite [nonstructural laminate]
  • Y10T428/31551—Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
  • Y10T428/31554—Next to second layer of polyamidoester

Definitions

• thermoplastic urethane/urea compositions and to compositions which are blends of a thermoplastic polyurethane/urea and (b) at least one copolymer and/or alloy. These compositions and blends are suitable for molding, particularly suitable for slush molding to form a shell having improved feel. The shell also maintains good weathering and air bag deployment properties.
• thermoplastic elastomers made from double metal cyanide catalysts in combination with chain extenders in the preparation of thermoplastic elastomers. Compositions made with such polyols are disclosed, for example, in U.S. Pat. Nos. 5,096,993 and 5,185,420.
• the thermoplastic polyurethane elastomers produced with polyoxyalkylene polyols had poor physical properties, such as being too hard, due to high levels of terminal unsaturation in the polyols used in their production.
• the thermoplastic polyurethane elastomers disclosed in U.S. Pat. Nos. 5,096,993 and 5,185,420 are thermoplastic elastomers made with polyols having less than 0.04 meq/g of end group unsaturation. These thermoplastic elastomers are taught to have enhanced softness.
• U.S. Pat. No. 4,883,837 discloses one technique for producing compatible blends of polyolefins with thermoplastic polyurethanes.
• a modified polyolefin is also included in the blended composition.
• the blends taught in U.S. Pat. No. 4,883,837 are made up of from 15 to 60 wt. % of polyolefin, from 30 to 70 wt. % thermoplastic polyurethane and from 10 to 35 wt. % modified polyolefin. It is the modified polyolefin which acts a compatibilizing agent for the polyolefin and thermoplastic polyurethane.
• U.S. Pat. No. 5,109,050 discloses a composition made up of from 80-99 parts by weight of a thermoplastic polyurethane resin and from 1 to 20 parts by weight of a modified polyolefin resin. Any of the known thermoplastic polyurethane resins may be used in the compositions of U.S. Pat. No. 5,109,050. Any of the known modified polyolefin resins may be used in the compositions of U.S. Pat. No. 5,109,050.
• the compositions described in U.S. Pat. No. 5,109,050 are taught to be flexible, smooth to the touch and stretchable. It is these properties which are said to make these compositions particularly useful for producing diapers.
• U.S. Pat. No. 5,852,118 discloses block copolymers of chemically modified polyolefins with thermoplastic polyurethanes, copolyesters or copolyamides and a coupling agent.
• the coupling agent is a diisocyanate with blocked or unblocked polyisocyanates.
• This diisocyanate coupling agent may be used in combination with a co-coupling agent selected from primary amines, secondary amines, diols, diepoxides, amino/hydroxy and amino/epoxy compounds.
• These block copolymers are useful as compatibilizing blends of polar and non-polar thermoplastic elastomers and for promoting adhesion of thermoplastic elastomers onto various polar engineering resins.
• U.S. Pat. No. 5,605,961 discloses homogeneous thermoplastic compositions which include (1) a polyolefin selected from isotactic polypropylene, syndiotactic polypropylene and a blend of isotactic polypropylene and thermoplastic polyurethane and (2) a mixture of from 1 to 99% thermoplastic polyurethane and from 1 to 99% of the reaction product of a modified polyolefin and a polyamide resin.
• U.S. Pat. No. 5,623,019 discloses a compatibilized thermoplastic molding composition made up of from 30 to 90% thermoplastic polyurethane, 10 to 70% of a polyolefin having a number average molecular weight of at least 10,000 and a compatibilizing agent which is a copolymer having a number average molecular weight of from 25,000 to 350,000 and containing blocks of monoalkylene arene and either hydrogenated conjugated diene or non-hydrogenated conjugated diene.
• U.S. Pat. No. 6,054,533 discloses compatibilized blends of a thermoplastic elastomer and a polyolefin in which the compatibilizing agent is a thermoplastic polyurethane.
• This thermoplastic polyurethane compatibilizing agent is the reaction product of a substantially hydrocarbon intermediate, a diisocyanate and an amine or diol chain extender.
• the thermoplastic polyurethane compatibilizing agent is included in an amount of from 0.25 to 15 parts by weight for every 100 parts by weight of thermoplastic elastomer plus polyolefin.
• U.S. Pat. No. 6,174,959 discloses compatible blends of from 50 to 99% of an aliphatic thermoplastic polyurethane with from 1 to 50% of a copolymer composed of units derived from ethylene and propylene with 25-35% by weight of the copolymer being derived from propylene units.
• the polyether polyols used to produce the thermoplastic polyurethanes required in U.S. Pat. No. 6,174,959 may have functionalities no greater than 6 and molecular weights of from 400 up to 20,000. There is no teaching in this disclosure with respect to the unsaturation level of the polyether polyols used to produce the thermoplastic polyurethanes used in these blends.
• U.S. Pat. No. 6,235,830 discloses a polyurethane resin for slush molding composed of a thermoplastic polyurethane elastomer, a plasticizer and a compound containing a radical polymerizable unsaturated group.
• the plasticizer is included in an amount of from 5 to 50 parts by weight per 100 parts by weight of polyurethane elastomer.
• the compound containing a radical polymerizable unsaturated group is included in an amount of from 0.1 to 10 parts by weight per 100 parts by weight of polyurethane elastomer.
• thermoplastic polyurethane resins which form compatible blends with polyolefins.
• the compatibility described therein is taught to be attributable to production of the thermoplastic polyurethane from a reaction mixture which includes a reactive polyolefin containing at least one hydroxyl, amine or carboxylic acid functional group.
• U.S. Pat. No. 6,469,099 and EP 1,235,879 B1 each disclose compatibilized resin blends which include a thermoplastic polyurethane, a succinimide-based compatibilizing agent containing pendant isocyanate-reactive groups or polyoxyalkylene groups corresponding to a specified structure.
• the compatibilizing agent is used in amounts ranging from 0.5 wt. % to 20 wt. %, depending upon the particular application for which the product resin will be used.
• thermoplastic urethane/ureas and blends of these urethane/ureas produced with an olefin-containing block copolymer and/or alloy are characterized by an ability to maintain low temperature resistance (ductility to about ⁇ 30° C.) and also weatherability (DE ⁇ 3.0 after 1993 kilojoules/m 2 ).
• thermoplastic urethane/urea alloy compositions within the scope of the present invention are capable of meeting automotive weathering requirements, for instance, exposure to 1993 kiloJoules/m 2 of Xenon arc artificial weathering with a delta E (color change) less than or equal to 3.
• Instrument panel skins molded from these thermoplastic urethane/urea alloy compositions are expected to be capable of withstanding successful air bag deployments at ⁇ 30° C. and 107° C. and after heat aging for 400 hours at 107° C.
• the present invention provides a skin, cover or shell, particularly for automotive trim panels, and more particularly for air bag door and instrument panel applications, which are produced from the melt-blended composition of a light stable polyether polyol-based aliphatic thermoplastic urethane/urea elastomer alone or in combination with an olefin-containing block copolymer and/or alloy.
• Aliphatic thermoplastic urethane/urea elastomers which are suitable for use in the compositions of the present invention may be produced from an isocyanate-reactive component that includes at least one low end group unsaturation, low molecular weight polyol and at least one aliphatic or cycloaliphatic diamine which is reacted with an aliphatic diisocyanate and stabilized with one or more ultraviolet stabilizing agents, an antioxidant and pigments.
• substitution of about 5-10% of the olefin-containing block copolymer and/or alloy with an ionomer has been found to provide improved weathering and less surface porosity, particularly when higher amounts of modifier are present.
• the alloy compositions of the present invention may be prepared by melt blending the aliphatic urethane/urea elastomer with the olefin-containing block copolymer and/or alloy (with or without ionomer) using a twin screw extruder. Pellets may then be formed and cryogenically ground to form a slush castable powder. The output of the extruder may also be formed into minibeads or microspheres according to the teachings of U.S. Pat. Nos.
• thermoplastic urethane/urea of the present invention may be the reaction product of one or more low unsaturation (i.e., unsaturation level of less than 0.04 meq/g, preferably less than 0.02 meq/g) polyether polyol, one or more aliphatic or cycloaliphatic diamines, one or more chain extenders and an aliphatic organic diisocyanate.
• low unsaturation i.e., unsaturation level of less than 0.04 meq/g, preferably less than 0.02 meq/g
• polyether polyol one or more aliphatic or cycloaliphatic diamines, one or more chain extenders and an aliphatic organic diisocyanate.
• an aliphatic diisocyanate is a diisocyanate that contains only hydrocarbon functionality such as hexamethylene diisocyanate or (HMDI).
• the overall level of aliphatic functionality of a diisocyanate may therefore be greater than 75% (wt.) and fall within the range of 75-100% (wt).
• a completely (100% wt.) aliphatic urethane/urea is a urethane/urea produced from one or more aliphatic diisocyanates, one or more aliphatic polyols (e.g., aliphatic polyether or polyester), one or more aliphatic or cycloaliphatic diamines, and one or more aliphatic chain extenders.
• the aliphatic urethane/urea so prepared may also be prepared in the presence of a urethane catalyst.
• the weight percent ratio of thermoplastic urethane/urea used in an alloy composition of the present invention may be from 5-95% by weight (based on total weight of thermoplastic urethane/urea plus polyolefin-based modifier) and the weight percent of the polyolefin-based modifier may be from 5 to 95% by weight (based on total weight of thermoplastic urethane/urea plus olefin), including all values and increments therein.
• the thermoplastic urethane/urea may be present in an amount of 50% by weight (based on total weight of thermoplastic urethane/urea plus olefin modifier) and the polyolefin modifier may also be present at about 50% by weight (based on total weight of thermoplastic urethane/urea plus olefin modifier). In a particularly preferred embodiment of the present invention, 45-90% by weight thermoplastic urethane/urea and 5-45% by weight olefin-based modifier are present.
• a terpolymer is a polymer having three different repeating units which may be present in block, random or even alternating configuration. These repeating units may be polyalkylene type repeating units (e.g., —CH 2 —) which may be substituted with additional hydrocarbon functionality.
• the olefin-containing block copolymer may be a vulcanized terpolymer of ethylene/propylene/diene dispersed in polypropylene or polyethylene, such as that which is commercially available under the trademark SantopreneTM 819155B from Advanced Elastomer Systems.
• These vulcanized terpolymers generally have a specific gravity of about 1.04, a tensile strength at break (ASTM D412) of about 590 psi, an elongation at break (ASTM D412) of about 600%, and a compression set (257° F., 70.0 hr) of about 55% (ASTM D395).
• Suitable thermoplastic vulcanizates are those that have relatively low levels of crosslinking and/or an elongation at break of between 100-1000%, including all values and increments therein.
• the block copolymer for blending with the light-stable TPU may be any of the styrenic block copolymers with a hydrogenated midblock of styrene-ethylene/butylene-styrene (SEBS) or styrene ethylene/propylene-styrene (SEPS).
• SEBS styrene-ethylene/butylene-styrene
• SEPS styrene ethylene/propylene-styrene
• Such styrenic block copolymers include that which is commercially available under the designation Kraton G from Kraton Polymers Group.
• Olefin-containing block copolymers composed of a linear triblock copolymer based on styrene and ethylene/butylenes, such as those which are commercially available under the designations MD 6945M and G1643M, from the Kraton Polymers Group are also suitable modifiers for the compositions of the present invention.
• Block copolymers of SBS (styrene butadiene-styrene) and SIS (styrene-isoprene-styrene) may also be used to produce the alloy compositions of the present invention.
• the olefin-containing block copolymers used in the practice of the present invention may also be one or more of thermoplastic elastomers (TPE), such as that which is commercially available under the designation Tekron® from Teknor Apex.
• Thermoplastic vulcanizates such as those which are available from Teknor Apex Company under the trademarks Uniprene®; Telecar® (thermoplastic rubbers (TPR)), Monprene® (TPO/saturated styrene block copolymers), and Elexar® SEBS are also suitable for use in the present invention.
• Olefin-containing block copolymers such as those composed of a block copolymer thermoplastic elastomer which are available from Teknor Apex under the designations TK-1448A and TK-1468D are also suitable for use in the present invention.
• the olefin containing block copolymer which is an ethylene-octene copolymer that is commercially available under the name EngageTM8400 Polyolefin Elastomer from Dow Plastics is also suitable for use in the present invention.
• thermoplastic urethane/ureas and olefin-containing copolymer compositions of the present invention may also contain fillers, pigments or other additives which may function to improve processing and/or product performance. Such additives may be present at levels which may be up to about 15% by weight in total.
• Surlyn® 9970 is an advanced ethylene/methacrylic acid copolymer in which the methacrylic acid groups have been partially neutralized with zinc ions which is commercially available from DuPont.
• the melt blend of thermoplastic urethane/urea and olefin-containing block copolymer and/or alloy may also include a color concentrate as a source of color.
• Suitable color concentrates are known to those skilled in the art.
• One example of a suitable color concentrate is that which is commercially available under the name Clariant 374A Pebble from Clariant Corporation.
• This product may include about 30% by weight pigment(s), about 5-10% of an antioxidant (e.g., Tinuvin 213 from Ciba-Geigy) and about 60-65% of an aliphatic thermoplastic urethane/urea suitable for use in the composition of the present invention.
• the color concentrate may be present in an amount of from about 5 to about 10% by weight of the thermoplastic urethane/urea alloy.
• thermoplastic urethane/ureas of the present invention may be used without an olefin based modifier, it is preferred that such a modifier be included.
• Typical compositions containing both the thermoplastic urethane/urea and olefin based modifier which may be melt blended to form the slush castable elastomers of the present invention include:
• ionomer preferably, Surlyn® 9970 or 9975 ionomer
• the slush castable elastomers formed from the melt blending of the above ingredients will generally have a melt flow index (MFI) of about 38 (grams/10 minutes, 160° C./10 kilograms).
• MFI melt flow index
• the compatible blends of the present invention will generally have MFI's of between 20-150, including all values and increments herein.
• thermoplastic urethane/urea(s) employed to produce the compatible blends of the present invention may be made by a “one-shot” reaction process.
• the “one-shot” technique involves mixing, in a suitable container, polyol, diamine, chain extender, organic diisocyanate, any ultraviolet stabilizing agent(s), any antioxidant, any pigment(s) or color concentrate, and urethane catalyst and, then, agitating the mixture for approximately 20 to 30 seconds.
• thermoplastic urethane/ureas can also be made by pre-blending a portion of the polyol, aliphatic or cycloaliphatic diamine, any antioxidant, catalyst and any UV/heat stabilizers.
• the polyol blend may be added to an agitated, heated tank of a urethane casting machine; isocyanate is placed into a separate agitated, heated tank; chain extender/crosslinker is placed into a third tank; and pigment masterbatch with the additional polyol is added at the mixhead.
• the components are metered individually using gear pumps or other pumps with the required metering accuracy, with suitable flow control devices, to a low pressure mixhead for blending. This mixture may be cast onto a temperature and speed controlled belt for completion of the reaction. Various temperatures could be maintained in different areas of the chamber.
• the mixture from the mixing head of the urethane/urea casting machine may also be used as the feed for a twin screw extruder.
• Various screw sections can be set up to convey the liquid to continue polymerization, melt and blend the elastomer, and the final unpigmented elastomer could be fed to a strand die for pelletizing.
• the extruder output could also be used to make beads of the desired size for dry casting.
• the extrusion operation could also be used to melt blend dry pigment for coloring/pigmenting the elastomer.
• the dry blended pigment would be fed into the extruder using a side feeder which would meter the proper amount into a clear melt mixture.
• the output of the side feeder would be synchronized with the output of the extruder.
• the ingredients may also be fed directly into the throat of the twin screw extruder which would perform the blending, polymerization, melting, and pigmentation operations.
• the polyether polyol, aliphatic or cycloaliphatic diamine, diisocyanate, chain extender, and other components are typically reacted under conditions of elevated temperature.
• a preferred method of forming the desired thermoplastic elastomers is by continuous processing utilizing an extruder.
• An alternative method involves mixing in a “one shot” batch process, the polyol, diamine, chain extender, organic diisocyanate, ultra violet stabilizing agent, antioxidant, pigment, and urethane catalyst in a vessel to produce the elastomer of the present invention.
• This aliphatic thermoplastic urethane/urea elastomer may then be combined with a polyolefin-based modifier in the appropriate amount by any of the techniques known to those skilled in the art.
• the aliphatic thermoplastic polyurethane and any polyolefin-based modifier is/are then placed into a suitable container where it is heated and, then chopped or ground into a powder using either a non-cryogenic or a cryogenic methods such as liquid nitrogen to facilitate and expedite the granularization or pelletizing of the slush molding composition.
• spherical particles having a diameter between 0.007 and 0.040 inches are formed by melt extruding the mixture of thermoplastic polyurethane and any other additives, particularly, a pigment and then directing the molten material through orifices with openings of the desired size into a liquid bath.
• the molten material passing into the liquid bath is cut into pieces to cause that molten material to be shaped into microspheres.
• This same process is suitable for the aliphatic thermoplastic polyurethane plus polyolefin-based modifier mixture from which the slush molding compositions of the present invention are formed.
• the powder or beads obtained are suitable for use as a castable powder. That is, the powder can be placed in a molding tool and heated to form an article of manufacture.
• Non-cryogenic grinding is made possible by changing the index of the aliphatic thermoplastic polyurethane elastomer.
• the index is the ratio of reactive equivalents of NCO containing components/reactive equivalents of OH and NH containing components. This change reduces the molecular weight of the elastomer and its inherent toughness allowing the polymer to be ground at ambient temperatures.
• the polymer may be prepared at an NCO/OH+NH equivalent ratio of from 0.90 to 0.99 with a preferred range of 0.94 to 0.98.
• the mixing of the polyurethane-forming reactants can be carried out at ambient temperature (approximately 25° C.) and the resulting mixture is then heated to a temperature of the order of about 40 to about 130° C., preferably to a temperature of about 90 to 120° C.
• diisocyanates which are particularly useful include: isophorone diisocyanate, hexamethylene diisocyanate, methylene bis(cyclohexyl isocyanate), its isomers and mixtures thereof, isomers and isomeric mixtures of cyclohexylene diisocyanate, 1-methyl-2,5-cyclohexylene diisocyanate, 1-methyl-2,4-cyclohexylene diisocyanate, 1-methyl-2,6-cyclohexylene diisocyanate, 4,4′-isopropylidene bis(cyclohexyl isocyanate) and mixtures and derivatives thereof.
• the organic diisocyanates can be present in amounts ranging from 20% to 50% but are preferably present in amounts in the range of approximately 25% to 40%.
• Preferred polyol reactants for producing the aliphatic thermoplastic polyurethanes used in the present invention are polyether polyols and combinations thereof.
• Suitable polyols include at least one ether structural unit and have a number average molecular weight of from 1000 to 10,000 Da, preferably, at least 1250 and most preferably, at least 2,000 but less than 10,000 Da, preferably, less than 8,000 Da.
• the functionality of the polyol is preferably from 2 to 4.
• Suitable polyether polyols include polyoxyethylene glycols, polyoxypropylene glycols, copolymers of ethylene oxide and propylene oxide, polytetramethylene glycols, and copolymers of tetrahydrofuran and ethylene oxide and/or propylene oxide.
• polyether polyols in combination with other known polyols (e.g., polyester polyols) but such other types of polyols should not be used in an amount greater than 50%.
• the polyether polyol is of the type produced using an organometallic catalyst which results in a polyol having a level of terminal unsaturation of less than 0.04 meq/g, and preferably less than 0.02 meq/g.
• a representative example of such a polyol is Acclaim 4220N (sold by Bayer MaterialScience LLC).
• Acclaim 4220N polyol is an ethylene oxide capped poly(propylene oxide) polyol with an approximate molecular weight of 4000 and a hydroxyl number of 28.
• the polyol component can be present in amounts ranging from approximately 40% to 70%.
• the preferred concentration of polyol present in the reaction ranges between 40% and 60% and is adjusted in this range to vary the hardness of the elastomer produced.
• any of the known aliphatic and/or cycloaliphatic diamines having a molecular weight of up to 4000 Da, preferably from 100 to 1000 Da, most preferably from about 200 to about 500 Da may be used to produce the thermoplastic polyurethane/urea for the molding compositions of the present invention.
• Primary or secondary amines are suitable.
• particularly preferred diamines are Jefflink® 754 (a cycloaliphatic secondary amine having a molecular weight of 254) which is commercially available from Huntsman and Clearlink® 1000 (aliphatic diamine having a molecular weight of 322) which is commercially available from UOP.
• the diamine is generally included in an amount of up to 10%, preferably, up to about 5%, most preferably up to about 2%.
• Chain extending agents which may be employed in the preparation of the urethane/urea thermoplastic elastomer used in the present invention include diols and aromatic secondary diamines all of which are well known in the art.
• Preferred diol chain extenders include ethylene glycol, diethylene glycol, propylene glycol, pentane diol, 3-methylpentane-1,5-diol, 1,6-hexane diol, HQEE [hydroquinone bis(2-hydroxyethyl)ether], CHDM (1,4-cyclohexanedimethanol), HBPA (hydrogenated bisphenol A), 1,4-butane diol, neopentyl glycol, and dipropylene glycol can also be used.
• the chain extender is 1,4-butanediol.
• the chain extender such as 1,4-butanediol, can be present in concentrations varying from 4% to 15%, but preferably ranges from 7% to approximately 13%.
• the ultraviolet stabilizing agents include a combination of a hindered amine light stabilizers (HALS) such as bis(1,2,2,6,6-pentamethyl-1-4-piperidinyl) sebacate (Chemical Abstract Number 41556-26-7, also known as Tinuvin 292 or 765 Ciba-Geigy Corp., Hawthorne, N.Y.) and a hydroxyphenyl benzotriazole such as a benzotriazole mixture of poly(oxy-1,2-ethanediyl), alpha-[3-[3-(2H-benzotriazol-2-yl)-5-(1,1-dimethylethyl)-4-hydroxyphenyl]-1-oxopropyl]-omega-hydroxy- and poly(oxy-1,2-ethanediyl), alpha-[3-[3-(2H-benzotriazol-2-yl)-5-(1,1-dimethylethyl)-4-hydroxyphenyl]-1
• any suitable pigmenting agent or mixture of pigmenting agents may be used to produce the compositions of the present invention.
• the agent or agents must have long-term ultraviolet light resistance for Arizona exposure; heat resistance up to 260° C. (500° F.) to survive the dry casting process, and the extrusion compounding process; and must not promote any degradation of the urethane elastomer.
• pigments include carbon black (Columbian Chemicals Corporation); titanium dioxide (DuPont Company, Chemicals Department); Chomophthal Red BPP (Ciba-Geigy, Pigments Division); Phthalocyanine Blue Red Shade (Ciba-Geigy, Pigments Divisions); Yellow Iron Oxide (Miles Incorporated, Organic Products Division); and Quinacridone Violet (Hoechst Celanese Corporation, Specialty Products Group-Pigments).
• the pigmenting agent being present at a total concentration in the range of approximately 0.90% to 2.0% and preferably in a range wherein the total concentration is approximately 1.0% to 1.94%.
• the urethane catalysts which are useful in the present invention may be any suitable urethane catalyst, or mixture of urethane catalyst, may be used in the elastomer forming process of the present invention.
• Representative samples include (a) tertiary amines such as ZF-20 [bis 2-(N,N-dimethylamino)ether] from Huntsman Chemical; N-methylmorpholine from Huntsman Chemical; N-ethylmorpholine from Huntsman Chemical; DMEA N,N-dimethylethanolamine from Union Carbide; Dabco 1,4-diazbicyclo[2,2,2]octane from Air Products and the like; (b) salts of organic acids with a variety of metals such as alkali metals, alkaline earth metals, Al, Sn, Pb, Mn, Co., Ni, and Cu, including, for example, sodium acetate, potassium laurate, calcium hexanoate, stannous acetate, and stannous
• Useful organotin compounds include dialkyltin salts of carboxylic acids, e.g., dibutyltin diacetate, dibutyltin dilaurate, dibutyltin maleate, dilauryltin diacetate, dioctyltin diacetate and the like.
• Preferred catalysts are BiCat 8, BiCat 12, BiCat V and Coscat 83.
• the BiCat materials are products of Shepherd Chemical.
• Coscat 83 is a product of CasChem Corporation.
• BiCats 8 and 12 are mixtures of bismuth and zinc carboxylates.
• BiCat V and Coscat 83 are bismuth neodecanoates. These catalysts are present at a total concentration in the range of approximately of 0.1% to 0.3% by weight, and preferably in the range of approximately 0.15% to 0.25%.
• thermoplastic urethane/urea elastomer is then combined with the polyolefin-based modifier in the appropriate amount by any of the techniques known to those skilled in the art.
• the mixture of aliphatic thermoplastic urethane/urea and polyolefin-based modifier may, for example, be placed into a suitable container and then chopped or ground into a powder using either a non-cryogenic or a cryogenic methods such as liquid nitrogen to facilitate and expedite the granularization or pelletizing of the slush molding composition.
• spherical particles having a diameter between 0.007 and 0.040 inches are formed by melt extruding the mixture of thermoplastic urethane/urea and any other additives, particularly, a pigment and then directing the molten material through orifices with openings of the desired size into a liquid bath.
• the molten material passing into the liquid bath is cut into pieces to cause that molten material to be shaped into microspheres.
• This process is suitable for processing the aliphatic thermoplastic urethane/urea plus polyolefin-based modifier mixture from which the slush molding compositions of the present invention are formed.
• the resulting powder or beads are then suitable for use as a castable powder. This powder can be placed in a molding tool and heated to form an article of manufacture.
• Automobile interior trim components having increased ultraviolet light stability and resistance to artificial weathering can be produced by continuous processing utilizing an extruder wherein the virgin elastomer is extruded and molded into automotive interior trim components as is well known in the art.
• the castable powder elastomer, described above may be added to a mold and heated to produce an automotive trim component.
• the slush molding composition of the present invention in the form of a powder or microspheres may be used to produce articles by roto-casting.
• a predetermined charge of materials is placed within a hollow mold that is supported on an arm of a centrifuge.
• the centrifuge has a motor that will drive the arm to cause the charge of material to flow evenly across the inner surface of the mold.
• the mold is heated to cause the slush molding composition to melt as it flows evenly across the inner surface of the mold to build-up a uniform thickness shell on the mold.
• the mold and shell are cooled and the mold is opened to remove the shell as a finished part or a near net shape part for final finishing.
• the slush molding composition of the present invention in the form of a powder or microspheres (particularly, microspheres in the size range of 0.007′′ to 0.040′′) is suitable for use in slush molding.
• an excess charge of the slush molding composition is placed in a charge or powder box.
• the box is connected to a mold having a cavity formed in part by a casting surface heated or cooled by a suitable heater or air cooling system. Once the box is connected to the mold, the box and mold are inverted so that the excess charge of materials is dumped into the mold cavity.
• Typical slush molding apparatus are described in U.S. Pat. Nos.
• the apparatus described in these patents maintain a static head of material over the layer of material that is dumped onto the casting surface of the mold cavity.
• the heating system provides heated air (other suitable heaters are suitable for use with the invention such as the hot oil heater of U.S. Pat. No. 4,389,177 or electrical heaters as shown in U.S. Pat. No. 4,979,888).
• the casting surface is heated to cause the thermoplastic melt extruded microspheres to melt as they are flowed evenly across the casting surface and compacted thereon by the static head of the overlying material. It has been found that this enables a wider range of microsphere sizes to be used for build-up of a uniform thickness shell on the casting surface having low porosity that is below a visual threshold for holes in the skin.
• the mold cavity is cooled by suitable air cooling or liquid cooling systems as shown in U.S. Pat. Nos. 4,621,994; 4,623,503 and 5,106,285.
• the shell is concurrently cooled and the powder box and mold cavity are separated so that the mold is opened to remove the shell as a finished part or a near net shape part for final finishing.
• the slush molding compositions of the present invention can be used to cast shells.
• Minibeads and spheroidal particles made by extruding the mixture of aliphatic thermoplastic urethane/urea, any polyolefin-based modifier being used and any other additives and pelletizing this mixture with an underwater pelletizing system have been successfully cast into shells using the same equipment as used for powder.
• the low-melt viscosity of the composition of the present invention contributes greatly to the success in using this material to cast shells. The benefits seen are improved flow into areas with small radii and return edges, easier clean up and loading, and increased bulk density of the particle.
• Pigmented slush molding compositions can be produced from the aliphatic thermoplastic urethane/urea elastomer and any polyolefin-based modifier to be included by using a single or twin screw extruder. Twin screw extruders can also be used to make thermoplastic urethane elastomers which are non-pigmented. These materials are then pigmented in a second operation by using color concentrates for injection molding or dry/wet pigments in a second extruder or other high-intensity mixers for other applications.
• the dry (heat and UV stable automotive grade) pigments and other additives could be metered into the melt stream of the reactor to produce the desired color and then the melt could be fed to the pelletizing unit to produce pellets that can be further dried for use.
• This process reduces the handling operations currently used to pigment elastomers.
• a thin shell having a thickness between about 0.5 and 1.5 mm, may be formed by first providing a mold with a mold surface configured to complement the desired shape of the shell to be molded.
• the mold surface may then be heated (via suitable heaters such as a hot oil heater, or an electrical heater, or hot air or infrared heating).
• suitable heaters such as a hot oil heater, or an electrical heater, or hot air or infrared heating.
• the heated casting surface may then cause the melt extruded microspheres (particles, pellets, etc.) of the inventive composition to melt as they are flowed evenly across the casting surface and compacted thereon by the static head of the overlying material. It has been found that this enables a wider range of particle sizes to be used for build-up of a shell having a uniform thickness on the casting surface and low porosity that may be below a visual threshold for holes in the skin.
• compositions of the present invention may also comprise the outer layer of a dual layer cast shell in which the composition of the present invention is applied as an outer layer, and a second layer which may comprise a different material, e.g., an aromatic based polyurethane composition.
• the layers may be of about equal thickness. That is, the inner layer of the skin or shell of the dual layer cast shell may be primarily aromatic based.
• An aromatic polyurethane type inner layer should be understood herein to be a polyurethane produced from an aromatic diisocyanate and/or the use of an aromatic diisocyanate along with an aromatic extender.
• aromatic polyurethane may utilize a polyol, including an aliphatic polyol (e.g., aliphatic polyether or aliphatic polyester). Accordingly, it can be appreciated that the use of an aromatic diisocyanate or even an aromatic extender may serve to increase a physical property such as heat resistance.
• the aromatic based inner layer may therefore be one that has a DE>3.0 after 2450 kJ of Xenon arc exposure.
• the aromatic polyurethane so prepared may also be prepared in the presence of a urethane catalyst.
• the aromatic urethane composition also preferably in the form of a dry particulate, such as powder or microspheres, may be cast on the inner surface of the outer layer formed of the first aliphatic urethane material.
• the aromatic urethane material may be allowed to melt and form an inner layer at least partially, and preferably completely, covering the inner surface of the outer layer. Sufficient heat may be transferred from the heated mold surface through the outer layer to melt the inner layer.
• the mold surface may then be cooled or allowed to cool which may allow the inner and outer layers to harden and bond together. Finally, the shell is removed from the mold.
• the inner layer of the dual layer cast shell may comprise regrind or recycled plastic.
• the inner layer may comprise a polymer material, a portion of which comprised a formed article prior to its use as the polymer material for the inner layer.
• formed article it is meant to include polymer material that has, e.g., experienced a prior plastics manufacturing operation, such as slush molding or injection molding, wherein the plastic material has been converted, by heat, or by heat and pressure, into some desired shape, but which may not have survived a quality control measure, and may have been rejected by the manufacturer for commercial release. This would also include materials recovered in manufacture such as trim scrap and faulty parts (regrind or recycle), and materials recovered from discarded post-consumer products (reclaim). Having thus described the invention, the following Examples are given as being illustrative thereof.
• thermoplastic polyurethane (Comparative Example 1) and two thermoplastic urethane/ureas within the scope of the present invention were prepared from the materials listed in TABLE 1 in the amounts listed in TABLE 1.
• Example 1 (Comparative) 2 3 Elongation, 450% 730% 440% original Elongation, heat 300% 470% 570% aged 500 hrs. @110° C. Elongation, heat — 310% 400% aged 1000 hrs. @ 110° C. Elongation, heat — 170% 250% aged 1000 hrs. @ 120° C. Elongation, heat 200% 410% 420% aged 500 hrs. @ 120° C. Xenon Arc Exposure, DE 1240 kJ 1.13 0.292 0.769 2000 kJ — 0.159 1.254 2450 kJ 1.43 0.551 1.170 Air bag ⁇ 30° C. ⁇ 40° C. — deployment after heat aging for 400 hrs. @ 107° C., No fragmentation
• Panels produced from the elastomer of Example 2 were able to produce acceptable air bag deployment with no skin fragmentation results at ⁇ 40° C., after heat aging for 400 hours at 107° C.
• the elastomer produced in comparative Example 1 produced acceptable results only to ⁇ 30° C.
• thermoplastic composition produced in Example 2 was slush cast by melt blending either MODIFIER A or MODIFIER B (in the amount indicated in TABLE 3).
• compositions described in TABLE 3 had a melt flow index within the range between 20-150.
• inventive compositions disclosed herein may be formed into the skins or shells of the present invention by any of the known processes for making such articles, including cast molding, slush molding, injection molding, blow molding, transfer molding, rotational molding, and injection-compression molding.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Engineering & Computer Science (AREA)
• Manufacturing & Machinery (AREA)
• Mechanical Engineering (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Polyurethanes Or Polyureas (AREA)
• Moulding By Coating Moulds (AREA)
• Processing And Handling Of Plastics And Other Materials For Molding In General (AREA)
• Inorganic Chemistry (AREA)
• Instrument Panels (AREA)
• Manufacture Of Macromolecular Shaped Articles (AREA)

Priority Applications (1)

Applications Claiming Priority (7)

Related Parent Applications (1)

Related Child Applications (1)

Publications (1)

Family

ID=40351349

Family Applications (4)

Family Applications Before (2)

Family Applications After (1)

Country Status (9)

Cited By (1)

Families Citing this family (16)

Citations (6)

Family Cites Families (28)

• 2008
  • 2008-08-08 KR KR1020107002954A patent/KR101556025B1/ko active IP Right Grant
  • 2008-08-08 JP JP2010520996A patent/JP5325218B2/ja not_active Expired - Fee Related
  • 2008-08-08 MX MX2010001389A patent/MX2010001389A/es active IP Right Grant
  • 2008-08-08 EP EP08795136A patent/EP2178979A4/en not_active Withdrawn
  • 2008-08-08 WO PCT/US2008/009541 patent/WO2009023138A2/en active Application Filing
  • 2008-08-08 US US12/672,174 patent/US9708438B2/en active Active
  • 2008-08-08 JP JP2010520994A patent/JP5366949B2/ja not_active Expired - Fee Related
  • 2008-08-08 CN CN200880102080A patent/CN101772549A/zh active Pending
  • 2008-08-08 JP JP2010520993A patent/JP5281087B2/ja not_active Expired - Fee Related
  • 2008-08-08 WO PCT/US2008/009518 patent/WO2009023130A2/en active Application Filing
  • 2008-08-08 CN CN201410225557.5A patent/CN103980696A/zh active Pending
  • 2008-08-08 KR KR1020107002901A patent/KR101516450B1/ko active IP Right Grant
  • 2008-08-08 EP EP08795154A patent/EP2188338A4/en not_active Withdrawn
  • 2008-08-08 CN CN2008801020626A patent/CN101784609B/zh not_active Expired - Fee Related
  • 2008-08-08 CN CN2008801020490A patent/CN102216389A/zh active Pending
  • 2008-08-08 CA CA2695567A patent/CA2695567C/en not_active Expired - Fee Related
  • 2008-08-08 US US12/672,148 patent/US9796807B2/en active Active
  • 2008-08-08 WO PCT/US2008/009519 patent/WO2009023131A2/en active Application Filing
  • 2008-08-08 EP EP08795137A patent/EP2178980A4/en not_active Withdrawn
  • 2008-08-08 US US12/733,059 patent/US20110105673A1/en not_active Abandoned
  • 2008-08-08 KR KR1020107002902A patent/KR101519679B1/ko active IP Right Grant
  • 2008-08-08 MX MX2010001391A patent/MX2010001391A/es active IP Right Grant
  • 2008-08-08 CA CA2695537A patent/CA2695537C/en not_active Expired - Fee Related
  • 2008-08-08 MX MX2010001386A patent/MX2010001386A/es active IP Right Grant
  • 2008-08-08 CA CA2695534A patent/CA2695534C/en not_active Expired - Fee Related
  • 2008-08-11 TW TW097130554A patent/TW200938559A/zh unknown
  • 2008-08-11 TW TW097130547A patent/TW200938558A/zh unknown
  • 2008-08-11 TW TW097130545A patent/TWI445763B/zh not_active IP Right Cessation
• 2017
  • 2017-05-08 US US15/588,763 patent/US10683417B2/en not_active Expired - Fee Related

Patent Citations (7)

Non-Patent Citations (4)

Also Published As

Similar Documents

Legal Events