US20100234500A1 - Thermoplastic elastomer composition - Google Patents

Thermoplastic elastomer composition Download PDF

Info

Publication number
US20100234500A1
US20100234500A1 US12/721,955 US72195510A US2010234500A1 US 20100234500 A1 US20100234500 A1 US 20100234500A1 US 72195510 A US72195510 A US 72195510A US 2010234500 A1 US2010234500 A1 US 2010234500A1
Authority
US
United States
Prior art keywords
polyamide resin
thermoplastic elastomer
elastomer composition
para
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US12/721,955
Other languages
English (en)
Inventor
Yuichi Hara
Naoyuki Morooka
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yokohama Rubber Co Ltd
Original Assignee
Yokohama Rubber Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yokohama Rubber Co Ltd filed Critical Yokohama Rubber Co Ltd
Assigned to THE YOKOHAMA RUBBER CO., LTD. reassignment THE YOKOHAMA RUBBER CO., LTD. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HARA, YUICHI, MOROOKA, NAOYUKI
Publication of US20100234500A1 publication Critical patent/US20100234500A1/en
Priority to US13/107,268 priority Critical patent/US8129453B2/en
Priority to US13/368,539 priority patent/US8288461B2/en
Abandoned legal-status Critical Current

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60C—VEHICLE TYRES; TYRE INFLATION; TYRE CHANGING; CONNECTING VALVES TO INFLATABLE ELASTIC BODIES IN GENERAL; DEVICES OR ARRANGEMENTS RELATED TO TYRES
    • B60C1/00—Tyres characterised by the chemical composition or the physical arrangement or mixture of the composition
    • B60C1/0008—Compositions of the inner liner
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/26—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment
    • C08L23/28—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment by reaction with halogens or compounds containing halogen
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
    • C08L23/26—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment
    • C08L23/28—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers modified by chemical after-treatment by reaction with halogens or compounds containing halogen
    • C08L23/283—Halogenated homo- or copolymers of iso-olefins
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/0008—Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59
    • C08K5/0016—Plasticisers
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
    • C08K5/00—Use of organic ingredients
    • C08K5/36—Sulfur-, selenium-, or tellurium-containing compounds
    • C08K5/43—Compounds containing sulfur bound to nitrogen
    • C08K5/435—Sulfonamides
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2207/00—Properties characterising the ingredient of the composition
    • C08L2207/04—Thermoplastic elastomer
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L2312/00—Crosslinking
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L77/00—Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Compositions of derivatives of such polymers
    • C08L77/02—Polyamides derived from omega-amino carboxylic acids or from lactams thereof
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L77/00—Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Compositions of derivatives of such polymers
    • C08L77/06—Polyamides derived from polyamines and polycarboxylic acids
    • C—CHEMISTRY; METALLURGY
    • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
    • C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
    • C08L77/00—Compositions of polyamides obtained by reactions forming a carboxylic amide link in the main chain; Compositions of derivatives of such polymers
    • C08L77/10—Polyamides derived from aromatically bound amino and carboxyl groups of amino-carboxylic acids or of polyamines and polycarboxylic acids

Definitions

  • the present invention relates to a thermoplastic elastomer composition including a polyamide resin and a halogenated isoolefin/para-alkylstyrene copolymer rubber. More particularly, the present invention relates to a thermoplastic elastomer composition, in which a halogenated isoolefin/para-alkylstyrene copolymer rubber is dispersed in a polyamide resin, which is a matrix, in order to improve the cold temperature durability (cyclic fatigue endurance) of the polyamide resin. The present invention further relates to a pneumatic tire using the thermoplastic elastomer composition in an inner liner.
  • thermoplastic elastomer composition superior in balance between air barrier property and flexibility comprising a specific thermoplastic resin matrix in which a specific rubber elastomer ingredient is dispersed as a discontinuous phase. See Japanese Unexamined Patent Publication No. 8-259741.
  • thermoplastic resin ingredient a melt viscosity ( ⁇ m ) of a thermoplastic resin ingredient and a melt viscosity ( ⁇ d ) of a rubber elastomer ingredient in the thermoplastic elastomer composition and a difference in the solubility parameters of the elastomer ingredient and thermoplastic resin ingredient ( ⁇ SP) satisfy a specific relationship, a high elastomer ingredient ratio is achieved and thereby a thermoplastic elastomer composition much richer in flexibility and superior in gas barrier property is obtained and further a pneumatic tire using the same as a gas barrier layer. See Japanese Unexamined Patent Publication No. 10-25375.
  • thermoplastic elastomer composition comprising a thermoplastic elastomer having a thermoplastic resin as a matrix and a rubber composition as a dispersed phase in which a barrier resin composition having a phase structure dispersed in a flat shape is introduced so that the gas barrier property is greatly improved and flexibility, oil resistance, cold resistance, and heat resistance are given. See Japanese Unexamined Patent Publication No. 10-114840.
  • thermoplastic elastomer composition comprising an aliphatic polyamide resin modified by a layered silicate into which an acid anhydride modified ethylene-based modifying polymer is blended. See Japanese Unexamined Patent Publication No. 2000-160024.
  • thermoplastic elastomer composition including a polyamide resin and a halogenated isoolefin/para-alkylstyrene copolymer rubber
  • a dynamically cross-linked thermoplastic elastomer composition including a polyamide resin and a halogenated isoolefin/para-alkylstyrene copolymer rubber
  • the more finely the halogenated isoolefin/para-alkylstyrene copolymer rubber is dispersed the better the durability becomes, and that the higher volume fraction the halogenated isoolefin/para-alkylstyrene copolymer rubber is loaded to, the better the durability becomes.
  • halogenated isoolefin/para-alkylstyrene copolymer rubber reacts directly with polyamide resin, the more finely the halogenated isoolefin/para-alkylstyrene copolymer rubber is dispersed, the more reaction with the polyamide resin takes place, and the higher volume fraction the halogenated isoolefin/para-alkylstyrene copolymer rubber is loaded to, the more reaction with the polyamide resin takes place, which decreases flowability of the polyamide resin in a molten state which results in a significantly poorer film forming property.
  • An object of the present invention is to provide a thermoplastic elastomer composition, which includes a halogenated isoolefin/para-alkylstyrene copolymer rubber dispersed in a polyamide resin which is a matrix, and which maintains high flowability allowing good film formation, even if a halogenated isoolefin/para-alkylstyrene copolymer rubber is finely dispersed and mixed at a high rate.
  • An aspect of the present invention is a thermoplastic elastomer composition
  • a thermoplastic elastomer composition comprising a continuous phase composed of a modified polyamide resin (A) and a dispersed phase composed of a halogenated isoolefin/para-alkylstyrene copolymer rubber (B), wherein the modified polyamide resin (A) is a resin obtained by melt-kneading 100 parts by weight of a polyamide resin (C) with not less than 0.05 part by weight and less than 3 parts by weight of a compound (D) capable of binding to a terminal amino group of the polyamide resin at a temperature of not lower than the melting point of the polyamide resin (C).
  • the compound (D) capable of binding to a terminal amino group of the polyamide resin is preferably a monofunctional epoxy compound.
  • the polyamide resin (C) is preferably at least one selected from the group consisting of nylon 11, nylon 12, nylon 6, nylon 66, nylon 6/66, nylon 6/12, nylon 6/10, nylon 4/6, nylon 6/66/12 and aromatic nylons.
  • the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is preferably a brominated isobutylene/para-methylstyrene copolymer rubber.
  • the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is preferably dynamically cross-linked.
  • the amount of the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is preferably 57 to 70 parts by weight based on 100 parts by weight of the total of the polyamide resin (C) and the halogenated isoolefin/para-alkylstyrene copolymer rubber (B).
  • thermoplastic elastomer composition preferably further comprises a plasticizer (E) in an amount of 5 to 20 parts by weight based on 100 parts by weight of the total of the polyamide resin (C) and the plasticizer (E).
  • a plasticizer (E) in an amount of 5 to 20 parts by weight based on 100 parts by weight of the total of the polyamide resin (C) and the plasticizer (E).
  • the plasticizer (E) is preferably butylbenzenesulfonamide.
  • the cross-linking agent used for the dynamic cross-linking is preferably zinc oxide.
  • the cross-linking agent used for the dynamic cross-linking is preferably a secondary amine.
  • Another aspect of the present invention is a pneumatic tire having an inner liner comprising the thermoplastic elastomer composition.
  • thermoplastic elastomer composition which can maintain high flowability allowing good film formation, even if a halogenated isoolefin/para-alkylstyrene copolymer rubber is finely dispersed and mixed at a high rate, can be provided by using a modified polyamide resin obtained by melt-kneading in advance 100 parts by weight of a polyamide resin with not less than 0.05 part by weight and less than 3 parts by weight of a compound capable of binding to a terminal amino group of the polyamide resin.
  • thermoplastic elastomer composition according to the present invention in an inner liner is superior in low temperature fatigue durability.
  • thermoplastic elastomer composition according to the present invention comprises a modified polyamide resin (A) and a halogenated isoolefin/para-alkylstyrene copolymer rubber (B).
  • the modified polyamide resin (A) to be used according to the present invention is a resin obtained by melt-kneading 100 parts by weight of a polyamide resin (C) with not less than 0.05 part by weight and less than 3 parts by weight of a compound (D) capable of binding to a terminal amino group of a polyamide resin at a temperature of not lower than the melting point of the polyamide resin (C).
  • nylon 11 nylon 12
  • nylon 6 nylon 66
  • nylon 6/66 nylon 6/12
  • nylon 6/10 nylon 4/6, nylon 6/66/12
  • aromatic nylons can be used, without limitation thereto, singly or in combination.
  • nylon 6 and nylon 6/66 are preferable in view of fatigue resistance and a gas barrier property.
  • Examples of a compound (D) capable of binding to a terminal amino group of a polyamide resin include a monofunctional epoxy compound, a compound having an isocyanate group, a compound having an anhydride group, and a compound having a halogenated alkyl group.
  • a monofunctional epoxy compound is preferable from a viewpoint of the reactivity with a terminal amino group of a polyamide resin.
  • Examples of a monofunctional epoxy compound include ethylene oxide, epoxypropane, 1,2-epoxybutane, 2,3-epoxybutane, 3-methyl-1,2-epoxybutane, 1,2-epoxypentane, 4-methyl-1,2-epoxypentane, 2,3-epoxypentane, 3-methyl-1,2-epoxypentane, 4-methyl-1,2-epoxypentane, 4-methyl-2,3-epoxypentane, 3-ethyl-1,2-epoxypentane, 1,2-epoxyhexane, 2,3-epoxyhexane, 3,4-epoxyhexane, 5-methyl-1,2-epoxyhexane, 4-methyl-1,2-epoxyhexane, 5-methyl-1,2-epoxyhexane, 3-ethyl-1,2-epoxyhexane, 3-propyl-1,2-epoxyhexane, 4-ethyl-1,2-epoxyhex
  • the polyamide resin (C) and the compound (D) capable of binding to a terminal amino group of the polyamide resin may be, for example, charged into a twin screw kneader and melt-kneaded at a temperature not lower than the melting point of the polyamide resin (C), preferably higher than the melting point by at least 20° C., e.g. between 220 and 250° C.
  • the melt-kneading time is, for example, between 1 and 10 minutes, and preferably between 2 and 5 minutes.
  • a monofunctional epoxy compound is melt-kneaded as a compound (D) capable of binding to a terminal amino group of the polyamide resin
  • terminal amino group changes as follows.
  • the amount of the compound (D) capable of binding to a terminal amino group of a polyamide resin to be used for modifying the polyamide resin (C) is not less than 0.05 part by weight and less than 3 parts by weight based on 100 parts by weight of the polyamide resin (C), and preferably between 0.1 part by weight and 1 part by weight. If the amount of the compound (D), capable of binding to a terminal amino group of a polyamide resin, is too low, flowability is undesirably low, when a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is mixed at a high rate. Reversely, if the amount is too high, the low temperature durability (cyclic fatigue resistance) of the polyamide resin is deteriorated, which is also undesirable.
  • a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) to be used according to the present invention can be produced by halogenating a copolymer of an isoolefin and a para-alkylstyrene.
  • a copolymer of an isoolefin and a para-alkylstyrene There are no particular restrictions on the mixture ratio, degree of polymerization, average molecular weight, polymerization mode (a block-copolymer, a random copolymer, etc.), viscosity, type of a halogen atom, etc., of a halogenated isoolefin and the para-alkylstyrene, which can be selected freely in accordance with required physical properties for a thermoplastic elastomer composition.
  • Examples of an isoolefin constituting the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) include isobutylene, isopentene and isohexene. Isobutylene is preferable.
  • Examples of a para-alkylstyrene constituting the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) include para-methylstyrene, para-ethylstyrene, para-propylstyrene and para-butylstyrene. Para-methylstyrene is preferable.
  • halogenated isoolefin/para-alkylstyrene copolymer rubber (B) examples include fluorine, chlorine, bromine and iodine. Bromine is preferable.
  • An especially preferable halogenated isoolefin/para-alkylstyrene copolymer rubber is para-methylstyrene polyisobutylene copolymer rubber.
  • a brominated isobutylene para-methylstyrene copolymer rubber is yielded by brominating an isobutylene para-methylstyrene copolymer rubber having the recurring units represented by the formula (3):
  • a brominated isobutylene para-methylstyrene copolymer rubber is available from ExxonMobil Chemical Company under the trade name of Exxpro®.
  • the amount of a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) in a thermoplastic elastomer composition is preferably 57 to 70 parts by weight based on 100 parts by weight of the total of the polyamide resin (C) and the halogenated isoolefin/para-alkylstyrene copolymer rubber (B), and more preferably 57 to 68 parts by weight.
  • halogenated isoolefin/para-alkylstyrene copolymer rubber (B) If the content of a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is too low, the low temperature durability becomes poor, and reversely, if it is too high, the flowability in a molten state decreases and significantly deteriorates the film formation property.
  • a modified polyamide resin (A) forms a continuous phase and a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) forms a dispersed phase.
  • phase structure can be obtained by selecting appropriately the contents and the viscosities of the modified polyamide resin (A) and the halogenated isoolefin/para-alkylstyrene copolymer rubber (B). Theoretically, with a higher content of the modified polyamide resin (A), and a lower viscosity thereof, the modified polyamide resin (A) can form a continuous phase more easily.
  • thermoplastic elastomer composition according to the present invention preferably further comprises a plasticizer (E).
  • a plasticizer imparts plasticity to a rubber and a resin to assist mixture and dispersion of another ingredient, to facilitate processing such as extrusion, and to increase the tackiness of green rubber facilitating processing.
  • Examples of a usable plasticizer include dibutyl phthalate, dioctyl phthalate, dioctyl adipate, dibutylglycol adipate, dibutylcarbitol adipate, dioctyl sebacate, tricresyl phosphate, cresyl diphenyl phosphate, tributyl phosphate, trioctyl phosphate, tributoxydiethyl phosphate, and butylbenzenesulfonamide; and butylbenzenesulfonamide is preferable among them.
  • the amount of the plasticizer (E) is preferably 5 to 20 parts by weight based on 100 parts by weight of the total of the polyamide resin (C) and the plasticizer (E), and more preferably 5 to 15 parts by weight. If the amount of the plasticizer is too low, the advantage of the use of the plasticizer cannot be obtained; and reversely, in case it is too high, such adverse effects can take place as deterioration in the gas barrier property of the polyamide resin (C) and decrease in the durability caused by coarser dispersion of the rubber due to lowered viscosity.
  • the halogenated isoolefin/para-alkylstyrene copolymer rubber should preferably be dynamically cross-linked. Through the dynamic cross-linking, the continuous phase and the dispersed phase of a thermoplastic elastomer composition can be stabilized together.
  • the dynamic cross-linking can be performed by melt-kneading the halogenated isoolefin/para-alkylstyrene copolymer rubber together with a cross-linking agent.
  • Examples of a cross-linking agent to be used for the dynamic cross-linking include zinc oxide, stearic acid, zinc stearate, magnesium oxide, m-phenylene bismaleimide, an alkylphenol resin or a halogenated resin thereof, and a secondary amine.
  • Examples of the secondary amine to be used as a cross-linking agent include N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine and polymerized 2,2,4-trimethyl-1,2-dihydroquinoline.
  • zinc oxide, stearic acid, zinc stearate and N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine are used preferably as a cross-linking agent for the dynamic cross-linking.
  • the amount of the cross-linking agent is preferably 4 to 12 parts by weight based on 100 parts by weight of the halogenated isoolefin/para-alkylstyrene copolymer rubber (B), and more preferably 6 to 9 parts by weight.
  • the amount of the cross-linking agent is too low, the dynamic cross-linking becomes insufficient and fine dispersion of the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) cannot be stabilized leading to decrease in the durability.
  • the amount of the cross-linking agent is too high, scorching may occur during kneading or processing, or foreign matter may be generated in the film.
  • thermoplastic elastomer composition according to the present invention can be produced by melt-kneading a modified polyamide resin (A) and a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) at a temperature not lower than the melting point of the modified polyamide resin (A).
  • the temperature for melt-kneading may be a temperature not lower than the melting point of the modified polyamide resin, it should be preferably higher than the melting point of the modified polyamide resin by 20° C., for example, between 180 and 300° C.
  • the melt-kneading time is usually 1 to 10 minutes, and preferably 1 to 5 minutes.
  • a mixture of a plasticizer (E) and a compound (D) capable of binding to a terminal amino group of a polyamide resin is kneaded with a polyamide resin (C) in a twin screw kneader for 1 to 10 minutes at a preset temperature between 220 and 250° C. to produce a modified polyamide resin (A); then a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) and the modified polyamide resin (A) are charged into a twin screw kneader at a preset temperature between 220 and 250° C.
  • halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is dispersed; and then a cross-linking agent is added to cross-link dynamically the halogenated isoolefin/para-alkylstyrene copolymer rubber (B). Finally other ingredients are added to yield a thermoplastic elastomer composition.
  • a mixture of a plasticizer (E) and a compound (D) capable of binding to a terminal amino group of a polyamide resin is kneaded with a polyamide resin (C) in a twin screw kneader for 1 to 10 minutes at a preset temperature between 220 and 250° C. to produce a modified polyamide resin (A); and the produced modified polyamide resin (A), a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) and other ingredients are kneaded in a twin screw kneader for 1 to 10 minutes at a preset temperature between 220 and 250° C. to yield a thermoplastic elastomer composition.
  • a plasticizer (E) and a compound (D) capable of binding to a terminal amino group of a polyamide resin is kneaded with a polyamide resin (C) in a twin screw kneader for 1 to 10 minutes at a preset temperature between 220 and
  • a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is pelletized by a rubber pelletizer, and separately a mixture of a polyamide resin (A) and a plasticizer (F) is prepared by kneading a polyamide resin (A) and a plasticizer (F) in a twin screw kneader for 1 to 10 minutes at a preset temperature between 220 and 250° C.
  • the pellet of the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) and the mixture of the polyamide resin (A) and the plasticizer (F) are charged into a twin screw kneader at a preset temperature between 220 and 250° C.; and, when the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is dispersed, a cross-linking agent (E) is added to cross-link dynamically the halogenated isoolefin/para-alkylstyrene copolymer rubber (B).
  • a compound (D) capable of binding to a terminal amino group of a polyamide resin is added to be reacted with the polyamide, and finally an antioxidant is added to yield a thermoplastic elastomer composition.
  • a polyamide resin (C) is charged and molten in a twin screw kneader; then a plasticizer (E) is added; and then a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) is added.
  • a cross-linking agent is added to cross-link dynamically the halogenated isoolefin/para-alkylstyrene copolymer rubber (B); and then a compound (D) capable of binding to a terminal amino group of a polyamide resin is added; followed by additional melt-kneading to yield a thermoplastic elastomer composition.
  • thermoplastic elastomer composition according to the present invention may comprise, in addition to the afore-described ingredients, such various conventional additives used for resin or rubber compositions, as reinforcing materials (fillers), e.g. carbon black or silica, vulcanizing or cross-linking agents, vulcanizing or cross-linking accelerators, plasticizers, various types of oils, and antioxidants.
  • fillers e.g. carbon black or silica
  • vulcanizing or cross-linking agents e.g. carbon black or silica
  • vulcanizing or cross-linking agents e.g. carbon black or silica
  • vulcanizing or cross-linking accelerators e.g. carbon black or silica
  • plasticizers e.g. carbon black or silica
  • various types of oils, and antioxidants e.g. carbon black or silica
  • the contents of such additives may be identical to conventionally applicable contents, insofar as the additives should not conflict with the purpose of
  • thermoplastic elastomer composition according to the present invention can be converted to a film by a T-die extruder or a blown film machine. Since the film has a superior gas barrier property, heat resistance, and fatigue durability, it can be utilized as an inner layer for a pneumatic tire.
  • a film of the thermoplastic elastomer composition according to the present invention can be laminated to a laminate with a sheet of a rubber composition containing a diene component.
  • a rubber constituting a rubber composition containing a diene component to be used for the laminate of the film of the thermoplastic elastomer composition according to the present invention and a sheet of a rubber composition containing a diene component include a natural rubber, an emulsion polymerization styrene-butadiene rubber, a solution polymerization styrene-butadiene rubber, a high-cis butadiene rubber, a low-cis butadiene rubber, an isoprene rubber, an acrylonitrile-butadiene rubber, a hydrogenated nitrile rubber, a butyl rubber, a halogenated butyl rubber, and a chloroprene rubber; and a halogenated butyl rubber is preferable among them, because it can
  • the content of a halogenated butyl rubber in polymer components of the rubber composition is preferably 30 to 100% by weight. If the content of a halogenated butyl rubber is low, it cannot be directly bonded by heat to a film of the thermoplastic elastomer composition yielded according to the present invention, and therefore should be bonded cumbersomely using an adhesive.
  • a rubber composition containing a diene component may comprise, in addition to the afore-described ingredients, such various conventional additives used for resin or rubber compositions, as reinforcing materials (fillers), e.g. carbon black or silica, vulcanizing or cross-linking agents, vulcanizing or cross-linking accelerators, plasticizers, various types of oils, and antioxidants.
  • fillers e.g. carbon black or silica
  • vulcanizing or cross-linking agents e.g. carbon black or silica
  • vulcanizing or cross-linking agents e.g. carbon black or silica
  • vulcanizing or cross-linking accelerators e.g. carbon black or silica
  • plasticizers e.g., vulcanizing or cross-linking accelerators
  • plasticizers e.g., various types of oils, and antioxidants.
  • antioxidants e.g. carbon black or silica
  • the contents of such additives may be identical to conventionally
  • the pneumatic tire according to the present invention is a pneumatic tire using a thermoplastic elastomer composition produced according to the afore-described production process in an inner liner thereof. More particularly, it is a pneumatic tire having an inner liner using the thermoplastic elastomer composition film or the laminate.
  • the tire may be produced by a conventional process.
  • a thermoplastic elastomer composition according to the present invention is extruded to a film having pre-determined width and thickness, which is then placed cylindrically onto a tire building drum as an inner liner.
  • thermoplastic elastomer composition according to the present invention can also be used for producing a hose.
  • a conventional process can be applied for producing a hose using a thermoplastic elastomer composition according to the present invention.
  • a hose can be produced as follows: using pellets of a thermoplastic elastomer composition according to the present invention, the thermoplastic elastomer composition is extruded by a resin extruder with a cross-head extrusion system onto a mandrel to form an inner hose, on which an outer layer of the inner hose may be additionally formed by extruding another thermoplastic elastomer composition according to the present invention or a conventional thermoplastic rubber composition.
  • an adhesive is coated or sprayed over the inner hose. Further, reinforcing fibers or reinforcing steel wires are braided on the inner hose by a wire braider. If required, an adhesive is coated on a reinforcing layer for bonding to an outer hose, then a thermoplastic elastomer composition according to the present invention or a conventional thermoplastic rubber composition is similarly extruded thereon by a cross-head resin extruder to form an outer hose. Finally, the mandrel is pulled out to yield a hose.
  • Examples of an adhesive to be coated on an inner hose or a reinforcing layer include an isocyanate type, a urethane type, a phenol resin type, a resorcinol resin type, a chlorinated rubber type and an HRH type; and especially preferable are an isocyanate type and a urethane type.
  • B halogenated isoolefin/para-alkylstyrene copolymer rubber
  • Br-IPMS brominated isobutylene para-methylstyrene copolymer rubber
  • polyamide resin (C) As a polyamide resin (C) were used the following 3 types:
  • nylon 6/66 UBE Nylon 5033B (by Ube Industries, Ltd.);
  • nylon 6 UBE Nylon 1030B (by Ube Industries, Ltd.);
  • nylon 11 Rilsan BESNOTL (by Arkema).
  • glycidol Epiol® OH (by NOF Corp.);
  • BPGE p-sec-butylphenyl glycidyl ether
  • EHGE 2-ethylhexyl glycidyl ether
  • plasticizer (E) As a plasticizer (E) was used the following:
  • BBSA n-butylbenzenesulfonamide
  • cross-linking agent As a cross-linking agent were used the following 3 types:
  • zinc oxide zinc oxide of JIS 3 grade (by Seido Chemical Industry Co., Ltd.);
  • stearic acid stearic acid beads (by NOF Corp.);
  • zinc stearate zinc stearate (by Seido Chemical Industry Co., Ltd.).
  • the following antioxidant N-(1,3-dimethylbutyl)-N′-phenyl-p-phenylenediamine: Santoflex 6PPD (by Flexsys; hereinafter abbreviated as “6PPD”) was used.
  • the 6PPD functions also as a cross-linking agent, and is an antioxidant, as well as a cross-linking agent.
  • a halogenated isoolefin/para-alkylstyrene copolymer rubber (B) was pelletized by a rubber pelletizer (by Moriyama Company Ltd.).
  • a plasticizer (E) was mixed with a compound (D) capable of binding to a terminal amino group of the polyamide resin, and the mixture and a polyamide resin (C) were kneaded by a twin screw kneader (by Japan Steel Works, Ltd.) at a preset temperature of 230° C. for 3 minutes to produce a modified polyamide resin (A).
  • the produced pellets of the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) and modified polyamide resin (A) as well as other ingredients were kneaded by a twin screw kneader (by Japan Steel Works, Ltd.) at a preset temperature of 230° C. for 3 minutes to produce pellets of a thermoplastic elastomer composition.
  • the respective contents were selected as shown in Table 1 and Table 2.
  • the produced pellets were molded by a T-die extruder to 1 mm- and 0.1 mm-thick sheets for measuring physical properties.
  • thermoplastic elastomer composition For the produced thermoplastic elastomer composition, scorch time, fatigue durability and gas permeability were measured according to the following methods.
  • a capillary rheometer (by Toyo Seiki Seisaku-sho, Ltd.) was filled with a sample, maintained at 230° C. for pre-determined time periods, then extruded at a shear rate of 300 sec ⁇ 1 , and the extrudant appearance was monitored. The time until a nonsmooth surface appears was determined as the scorch time. Measurements were conducted at intervals of 5 minutes up to 30 minutes. The scorch time is an index of heat resistance, and a longer time is preferable.
  • thermoplastic elastomer compositions according to the present invention (Examples 1 to 10) exhibited sufficient scorch time, comfortable film formability and excellent fatigue durability and gas barrier property.
  • Comparative Example 1 since the content of a compound (D) capable of binding to a terminal amino group of a polyamide resin was low, the reaction between a polyamide resin (C) and the halogenated isoolefin/para-alkylstyrene copolymer rubber (B) continued to proceed, so that the polyamide resin lost flowability causing phase inversion and the cross-linked halogenated isoolefin/para-alkylstyrene copolymer rubber formed a continuous phase, by which processing required for measurements of physical properties became impossible.
  • Comparative Example 2 since the content of a compound (D) capable of binding to a terminal amino group of a polyamide resin was too high, the scorch time was long, but the fatigue durability was poor.
  • Comparative Example 3 in which an unmodified polyamide resin was used, since the content of the plasticizer is high, processing required for measurements of physical properties was possible, but the scorch time was short.
  • thermoplastic elastomer composition according to the present invention can be favorably used as an inner liner of a pneumatic tire. Further, the thermoplastic elastomer composition according to the present invention can be utilized for, in addition to a pneumatic tire, a barrier material in such rubber laminates requiring gas barrier property, as a hose, a fender, a rubber bag, and a fuel tank.

Landscapes

  • Chemical & Material Sciences (AREA)
  • General Chemical & Material Sciences (AREA)
  • Health & Medical Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Medicinal Chemistry (AREA)
  • Polymers & Plastics (AREA)
  • Organic Chemistry (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Compositions Of Macromolecular Compounds (AREA)
  • Tires In General (AREA)
  • Polyamides (AREA)
US12/721,955 2009-03-13 2010-03-11 Thermoplastic elastomer composition Abandoned US20100234500A1 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US13/107,268 US8129453B2 (en) 2009-03-13 2011-05-13 Method for preparing thermoplastic elastomer composition
US13/368,539 US8288461B2 (en) 2009-03-13 2012-02-08 Thermoplastic elastomer composition

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2009-061879 2009-03-13
JP2009061879A JP4821868B2 (ja) 2009-03-13 2009-03-13 熱可塑性エラストマー組成物

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US13/107,268 Division US8129453B2 (en) 2009-03-13 2011-05-13 Method for preparing thermoplastic elastomer composition

Publications (1)

Publication Number Publication Date
US20100234500A1 true US20100234500A1 (en) 2010-09-16

Family

ID=42664258

Family Applications (3)

Application Number Title Priority Date Filing Date
US12/721,955 Abandoned US20100234500A1 (en) 2009-03-13 2010-03-11 Thermoplastic elastomer composition
US13/107,268 Expired - Fee Related US8129453B2 (en) 2009-03-13 2011-05-13 Method for preparing thermoplastic elastomer composition
US13/368,539 Active US8288461B2 (en) 2009-03-13 2012-02-08 Thermoplastic elastomer composition

Family Applications After (2)

Application Number Title Priority Date Filing Date
US13/107,268 Expired - Fee Related US8129453B2 (en) 2009-03-13 2011-05-13 Method for preparing thermoplastic elastomer composition
US13/368,539 Active US8288461B2 (en) 2009-03-13 2012-02-08 Thermoplastic elastomer composition

Country Status (4)

Country Link
US (3) US20100234500A1 (ja)
JP (1) JP4821868B2 (ja)
CN (2) CN104448451A (ja)
DE (1) DE102010010345A1 (ja)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130030124A1 (en) * 2010-06-25 2013-01-31 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and manufacturing method therefor
EP2826819A4 (en) * 2012-03-13 2015-12-16 Yokohama Rubber Co Ltd Thermoplastic Elastomer Composition
US20180286537A1 (en) * 2015-10-30 2018-10-04 Yazaki Corporation Heat-resistant flexible electric cable and wire harness using the same

Families Citing this family (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5990967B2 (ja) * 2012-03-23 2016-09-14 横浜ゴム株式会社 熱可塑性エラストマー組成物の製造方法
EP2861662B1 (en) * 2012-06-19 2019-09-25 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and process to produce same
FR2999587B1 (fr) * 2012-12-17 2014-12-26 Michelin & Cie Pneumatique comportant une composition de caoutchouc comprenant un elastomere epoxyde reticule par un poly-acide carboxylique
US9546266B2 (en) 2013-03-13 2017-01-17 Basf Se Inner liner for a pneumatic tire assembly
JP5668876B2 (ja) * 2014-02-07 2015-02-12 横浜ゴム株式会社 熱可塑性エラストマー組成物の製造方法
US20180179372A1 (en) * 2015-07-28 2018-06-28 Exxonmobil Chemical Patents Inc. Elastomeric Compositions and Their Use in Articles
DE102016209098A1 (de) * 2016-05-25 2017-11-30 Leibniz-Institut Für Polymerforschung Dresden E.V. Kautschuk- oder elastomerzusammensetzungen und verfahren zu deren herstellung
JP6437509B2 (ja) * 2016-12-16 2018-12-12 横浜ゴム株式会社 動的架橋アロイの溶融粘度を低減する方法
CN113943461A (zh) * 2021-11-05 2022-01-18 道恩高材(北京)科技有限公司 一种用于轮胎内衬层耐温高气体阻隔动态硫化合金
CN115139615B (zh) * 2022-08-25 2023-06-06 河北泰达包装材料有限公司 一种软包装改性cpp薄膜及其生产方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5910544A (en) * 1995-11-02 1999-06-08 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and process for production thereof and low permeability hose using the same
US6079465A (en) * 1995-01-23 2000-06-27 The Yokohama Rubber Co., Ltd. Polymer composition for tire and pneumatic tire using same
US20090038729A1 (en) * 2006-01-10 2009-02-12 The Yokohama Rubber Co., Ltd Laminate or thermoplastic polymer composition having low air permeability and pneumatic tire using same as inner liner

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS6425375A (en) 1987-07-22 1989-01-27 Omron Tateisi Electronics Co Magnetic card
JPH0192223A (ja) * 1987-10-02 1989-04-11 Nisso Yuka Kogyo Kk ポリアミドのβ−ヒドロキシアルキル化方法
US5003003A (en) * 1988-04-22 1991-03-26 Copolymer Rubber & Chemical Corporation Polyamide thermoplastic elastomer obtained by blending
ZA899629B (en) * 1988-12-22 1990-09-26 Ferro Corp Toughened compositions of polyamide and functionalized rubber block or graft copolymers
JPH03265662A (ja) * 1990-03-15 1991-11-26 Japan Synthetic Rubber Co Ltd 熱可塑性エラストマー組成物
JP2715330B2 (ja) * 1990-03-30 1998-02-18 宇部興産株式会社 アルキレンオキサイドグラフトポリアミド組成物
JPH03281570A (ja) * 1990-03-30 1991-12-12 Ube Ind Ltd アルキレンオキサイドグラフトポリアミド組成物
JPH06192517A (ja) * 1992-04-23 1994-07-12 Sumitomo Dow Ltd 熱可塑性樹脂組成物
JP3217239B2 (ja) 1995-01-23 2001-10-09 横浜ゴム株式会社 タイヤ用ポリマー組成物およびそれを使用した空気入りタイヤ
JP3620882B2 (ja) 1995-02-16 2005-02-16 横浜ゴム株式会社 空気入りタイヤ及びその製造方法
CA2157260A1 (en) * 1995-08-30 1997-03-01 Shinji Yamamoto Fine fiber-reinforced thermoplastic elastomer composition and process for producing same
JPH1025375A (ja) * 1996-07-12 1998-01-27 Yokohama Rubber Co Ltd:The 熱可塑性エラストマー組成物及びこれを使用した空気入りタイヤ、ホース
JPH09239905A (ja) * 1996-03-12 1997-09-16 Yokohama Rubber Co Ltd:The ゴム／ポリアミド系樹脂積層体
JP3159941B2 (ja) 1996-07-23 2001-04-23 横浜ゴム株式会社 低気体透過性熱可塑性エラストマー組成物及びその製造方法
DE29621008U1 (de) 1996-12-03 1997-01-30 Textilma Ag Vorrichtung zur Steuerung der Querbewegung mindestens eines Fadens einer Textilmaschine
JP3236257B2 (ja) * 1998-01-13 2001-12-10 横浜ゴム株式会社 熱可塑性エラストマー組成物およびそれを使用した空気入りタイヤ
US6274697B1 (en) * 1998-10-02 2001-08-14 E. I. Du Pont De Nemours And Company Process and product for making polyamides
JP4197784B2 (ja) * 1998-11-24 2008-12-17 横浜ゴム株式会社 ガスバリヤー性に優れた熱可塑性エラストマー組成物およびそれを使用した積層体
US20060241244A1 (en) * 2003-03-06 2006-10-26 Yoshihiro Soeda Oriented thermoplastic elastomer film and process for producing the same
JP4600015B2 (ja) * 2003-12-02 2010-12-15 東レ株式会社 樹脂組成物およびその製造方法
CN101296997B (zh) * 2005-10-27 2011-12-07 埃克森美孚化学专利公司 低渗透性热塑性弹性体组合物
US7954528B2 (en) * 2005-10-27 2011-06-07 Exxonmobil Chemical Patents Inc. Thermoplastic elastomer composition and process for producing same
WO2007111584A1 (en) * 2006-03-24 2007-10-04 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition having excellent low temperature property

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6079465A (en) * 1995-01-23 2000-06-27 The Yokohama Rubber Co., Ltd. Polymer composition for tire and pneumatic tire using same
US5910544A (en) * 1995-11-02 1999-06-08 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and process for production thereof and low permeability hose using the same
US20090038729A1 (en) * 2006-01-10 2009-02-12 The Yokohama Rubber Co., Ltd Laminate or thermoplastic polymer composition having low air permeability and pneumatic tire using same as inner liner

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130030124A1 (en) * 2010-06-25 2013-01-31 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and manufacturing method therefor
US8933172B2 (en) * 2010-06-25 2015-01-13 The Yokohama Rubber Co., Ltd. Thermoplastic elastomer composition and manufacturing method therefor
EP2586829A4 (en) * 2010-06-25 2015-08-12 Yokohama Rubber Co Ltd THERMOPLASTIC ELASTOMER COMPOSITION AND MANUFACTURING METHOD THEREFOR
EP2826819A4 (en) * 2012-03-13 2015-12-16 Yokohama Rubber Co Ltd Thermoplastic Elastomer Composition
US20180286537A1 (en) * 2015-10-30 2018-10-04 Yazaki Corporation Heat-resistant flexible electric cable and wire harness using the same
US10381133B2 (en) * 2015-10-30 2019-08-13 Yazaki Corporation Heat-resistant flexible electric cable and wire harness using the same

Also Published As

Publication number Publication date
CN101831094A (zh) 2010-09-15
US20120136100A1 (en) 2012-05-31
US20110218281A1 (en) 2011-09-08
US8288461B2 (en) 2012-10-16
JP2010215727A (ja) 2010-09-30
JP4821868B2 (ja) 2011-11-24
US8129453B2 (en) 2012-03-06
CN104448451A (zh) 2015-03-25
DE102010010345A1 (de) 2010-09-30

Similar Documents

Publication Publication Date Title
US8129453B2 (en) Method for preparing thermoplastic elastomer composition
EP2184323B1 (en) Tire manufactured using a thermoplastic resin composition
JP4004518B2 (ja) ゴム積層体を用いた空気入りタイヤ
EP2610311B1 (en) Thermoplastic resin composition and tire using same
US9540504B2 (en) Thermoplastic resin composition
EP2474570B1 (en) Manufacturing method for thermoplastic resin composition
US20120214943A1 (en) Process for producing thermoplastic elastomer composition
US9127147B2 (en) Method for producing thermoplastic resin compositions
US9512313B2 (en) Thermoplastic elastomer composition
JP5668876B2 (ja) 熱可塑性エラストマー組成物の製造方法
JP5521363B2 (ja) 熱可塑性エラストマー組成物の製造方法
US10889709B2 (en) Thermoplastic resin composition, inner liner and pneumatic tire
US8933172B2 (en) Thermoplastic elastomer composition and manufacturing method therefor
US8921483B2 (en) Thermoplastic elastomer composition
JP5487656B2 (ja) 熱可塑性エラストマー組成物の製造方法

Legal Events

Date Code Title Description
AS Assignment

Owner name: THE YOKOHAMA RUBBER CO., LTD., JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:HARA, YUICHI;MOROOKA, NAOYUKI;REEL/FRAME:024067/0096

Effective date: 20100219

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION