US20090206708A1 - Fluid dynamic bearing apparatus and motor comprising the same - Google Patents

Fluid dynamic bearing apparatus and motor comprising the same Download PDF

Info

Publication number
US20090206708A1
US20090206708A1 US11/915,490 US91549006A US2009206708A1 US 20090206708 A1 US20090206708 A1 US 20090206708A1 US 91549006 A US91549006 A US 91549006A US 2009206708 A1 US2009206708 A1 US 2009206708A1
Authority
US
United States
Prior art keywords
fluid dynamic
housing
dynamic bearing
bracket
bearing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US11/915,490
Other languages
English (en)
Inventor
Kazutoyo Murakami
Masaki Egami
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NTN Corp
Original Assignee
NTN Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NTN Corp filed Critical NTN Corp
Assigned to NTN CORPORATION reassignment NTN CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: EGAMI, MASAKI, MURAKAMI, KAZUTOYO
Publication of US20090206708A1 publication Critical patent/US20090206708A1/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/14—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by the properties of the layers
    • B32B37/144—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by the properties of the layers using layers with different mechanical or chemical conditions or properties, e.g. layers with different thermal shrinkage, layers under tension during bonding
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/12—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C17/00—Sliding-contact bearings for exclusively rotary movement
    • F16C17/10—Sliding-contact bearings for exclusively rotary movement for both radial and axial load
    • F16C17/102—Sliding-contact bearings for exclusively rotary movement for both radial and axial load with grooves in the bearing surface to generate hydrodynamic pressure
    • F16C17/107—Sliding-contact bearings for exclusively rotary movement for both radial and axial load with grooves in the bearing surface to generate hydrodynamic pressure with at least one surface for radial load and at least one surface for axial load
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/02—Parts of sliding-contact bearings
    • F16C33/04—Brasses; Bushes; Linings
    • F16C33/06—Sliding surface mainly made of metal
    • F16C33/10—Construction relative to lubrication
    • F16C33/1025—Construction relative to lubrication with liquid, e.g. oil, as lubricant
    • F16C33/106—Details of distribution or circulation inside the bearings, e.g. details of the bearing surfaces to affect flow or pressure of the liquid
    • F16C33/107—Grooves for generating pressure
    • H—ELECTRICITY
    • H02—GENERATION; CONVERSION OR DISTRIBUTION OF ELECTRIC POWER
    • H02K—DYNAMO-ELECTRIC MACHINES
    • H02K7/00—Arrangements for handling mechanical energy structurally associated with dynamo-electric machines, e.g. structural association with mechanical driving motors or auxiliary dynamo-electric machines
    • H02K7/08—Structural association with bearings
    • H02K7/085—Structural association with bearings radially supporting the rotary shaft at only one end of the rotor
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B37/00—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding
    • B32B37/12—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives
    • B32B2037/1253—Methods or apparatus for laminating, e.g. by curing or by ultrasonic bonding characterised by using adhesives curable adhesive
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2311/00—Metals, their alloys or their compounds
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2386/00—Specific polymers obtained by polycondensation or polyaddition not provided for in a single one of index codes B32B2363/00 - B32B2383/00
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2457/00—Electrical equipment

Definitions

  • the present invention relates to a fluid dynamic bearing apparatus which supports a rotational member by a fluid membrane formed in a bearing gap and a motor comprising the same.
  • Bearing apparatuses of this type can be suitably used for information appliances, for example, in spindle motors for magnetic disk drive units such as HDD, optical disk drive units such as CD-ROM, CD-R/RW, DVD-ROM/RAM, magneto-optic disk drive units such as MD and MO, polygon scanner motors of laser beam printers (LBP), collar wheels of projectors, or electrical machinery and apparatuses, for example, small motors such as axial fans.
  • spindle motors for magnetic disk drive units such as HDD, optical disk drive units such as CD-ROM, CD-R/RW, DVD-ROM/RAM, magneto-optic disk drive units such as MD and MO, polygon scanner motors of laser beam printers (LBP), collar wheels of projectors, or electrical machinery and apparatuses, for example, small motors such as axial fans.
  • LBP laser
  • Fluid dynamic bearings of this type are roughly classified into: hydrodynamic bearings comprising a hydrodynamic pressure producing part for producing hydrodynamic pressure in a lubricating fluid within a bearing gap; and so-called cylindrical bearings (bearings having a bearing cross section in a perfect circle shape) without a hydrodynamic pressure producing part.
  • a radial bearing portion which supports a shaft member in the radial direction and a thrust bearing portion which supports the shaft member in the thrust direction are both sometimes constituted by hydrodynamic bearings.
  • hydrodynamic bearing apparatuses An example of known radial bearing portions in fluid dynamic bearing apparatuses (hydrodynamic bearing apparatuses) of this type is such that hydrodynamic grooves are formed as a hydrodynamic pressure producing part on either the inner circumferential surface of a bearing member (when the bearing member comprises a housing and a bearing sleeve, the inner circumferential surface of the bearing sleeve) or the outer circumferential surface of a shaft member opposing this and a radial bearing gap is formed between both faces.
  • hydrodynamic grooves are formed as a hydrodynamic pressure producing part on either the inner circumferential surface of a bearing member (when the bearing member comprises a housing and a bearing sleeve, the inner circumferential surface of the bearing sleeve) or the outer circumferential surface of a shaft member opposing this and a radial bearing gap is formed between both faces.
  • a fluid dynamic bearing apparatus having the constitution described above is used by being integrated into, for example, a spindle motor for magnetic disk apparatuses such as HDD
  • mounting of the fluid dynamic bearing apparatus onto a motor is normally carried out by adhesively fixing the outer circumferential surface of the housing on the inner periphery face of a bracket having a portion for mounting a stator coil.
  • Adhesives used in adhesive fixing of this type are often anaerobic adhesives and epoxy-based adhesives from the standpoint of workability, outgassing characteristics and the like. Normally, curing of these adhesives involves a heating process after application. Therefore, a diametrical gap (adhesion gap) between the housing and bracket where the adhesives are provided changes because of the thermal expansion of the two components during the curing step.
  • the adhesion gap of this type is desirably set to have a predetermined width depending on the necessity, but when the adhesives are cured with heating, they are cured in a state that the adhesion gap between the two components changes during heating. Therefore, adhesion is carried out with the width of the adhesion gap different from that before the heating. Such a situation may prevent obtaining sufficient adhesive strength between the two components even if the width of the above adhesion gap is appropriately set in advance.
  • An object of the present invention is to provide a fluid dynamic bearing apparatus with an increased adhesive strength between a component having an adhesion fixing face and a bracket by appropriately controlling an adhesion gap.
  • the present invention provides a fluid dynamic bearing apparatus comprising a shaft member, a bracket, a radial bearing portion which rotatably supports the shaft member in the radial direction by a fluid membrane formed in a radial bearing gap, and an adhesion fixing face which is adhesively fixed to the inner circumferential surface of the bracket, wherein the value obtained by dividing the linear expansion coefficient of the component having the adhesion fixing face by the linear expansion coefficient of the bracket is not lower than 0.5 but not higher than 2.0.
  • the present invention is made by focusing on the variation in the adhesion gap associated with the thermal expansion of the component having the adhesion fixing face and the bracket, and is characterized in that the value obtained by dividing the linear expansion coefficient of the component having the adhesion fixing face by the linear expansion coefficient of the bracket is not lower than 0.5 but not higher than 2.0.
  • Such a constitution achieves the adhesive fixing between the component having the adhesion fixing face and the bracket in a state that a variation in the adhesion gap associated with heating is minimized to such a degree that the curing of adhesives is not adversely affected. Therefore, even when an adhesive which is cured with heating is used, high adhesive strength can be obtained between the component having the adhesion fixing face and the bracket, and the demand for increased disk capacities of the disk apparatuses can be met.
  • the reason why the ratio of the linear expansion coefficients of the two components ⁇ (the linear expansion coefficient of the component having the adhesion fixing face)/(the linear expansion coefficient of the bracket) ⁇ is defined to fall within the above range is as follows: when the above ratio of linear expansion coefficients is higher than 2.0, the adhesion gap becomes to narrow during heating of the adhesive, and in some cases it becomes a negative gap, whereby uncured adhesive may be squeezed out from the adhesion gap and the adhesive may fall short. Moreover, if the above ratio of the linear expansion coefficients is lower than 0.5 and the adhesion gap thereby becomes too wide, the adhesive strength may be lowered.
  • anaerobic adhesives As adhesives used for adhesively fixing the component having the adhesion fixing face and the bracket, anaerobic adhesives, ultraviolet curable adhesive, and epoxy-based adhesives are suitable in terms of workability, in particular curing speed and outgassing characteristics.
  • either or both of the components having the adhesion fixing face and the bracket can be formed from a metallic material.
  • either or both of the two components can be also formed from a resin composition.
  • examples of base resins constituting the resin composition include polyphenylene sulfide (PPS) which has excellent characteristics required for the component having the adhesion fixing face, for example, oil resistance, moldability (fluidity during molding), outgassing characteristics and other properties.
  • PPS polyphenylene sulfide
  • carbon fiber and an inorganic compound can be added to the resin composition as a filler, whereby the linear expansion coefficient of the resin composition can be controlled.
  • the amount of Na contained in the resin composition having the above constitution is preferably 2000 ppm or lower. This can accordingly reduce the amount of Na ion elution into the lubricating oil, and the cleanliness of the inside and outside of the bearing can be maintained at a high level.
  • polyphenylene sulfides PPS
  • linear polyphenylene sulfide PPS having the smallest number of side chains is preferable in that the number of molecular terminal groups per unit volume is less and the amount of Na contained is less.
  • carbon fiber those having a tensile strength of 3000 MPa or higher are preferred.
  • examples of those having high conductivity as well as high strength include PAN-based (polyacrylonitrile-based) carbon fibers.
  • the strengthening effect, dimension stabilizing effect, electrostatic removal effect and other effects produced by the addition of these carbon fibers to the resin composition can be demonstrated more noticeably by considering the aspect ratio of the carbon fibers. That is, the more the fiber length of the carbon fibers, the higher the strengthening effect and electrostatic removal effect, and the smaller the fiber diameter, the higher the wear resistance, in particular, the less the damage of the sliding contacting material. From these perspectives, the aspect ratio of the carbon fibers is preferably 6.5 or higher specifically.
  • the amount of the carbon fibers contained in the resin composition is preferably 10 to 35 vol. % so that the additional effects (strengthening effect, improved conductivity, improved dimensional stability) produced by adding the above carbon fibers can be demonstrated sufficiently and at the same time the fluidity (low melt viscosity) as a resin composition can be ensured.
  • inorganic compounds with a small amount of ion elution can be suitably used.
  • Inorganic compounds of this type can suppress the ion elution into the lubricating oil, which can be hazardous, to a low level, and therefore the degeneration, deterioration and a decrease in the viscosity of the lubricating oil can be avoided, maintaining the bearing performance at a high level.
  • the situation that the aforementioned ions are deposited on the bearing apparatus and its surroundings can be avoided and the cleanliness of the inside of the bearing or around the bearing apparatus can be ensured.
  • Another possible fluid dynamic bearing apparatus having the constitution described above is such that further comprises, in addition to the shaft member and bracket, a bearing sleeve whose inner circumferential surface forms a radial bearing gap between itself and the outer circumferential surface of the shaft member, and a housing in which the bearing sleeve is fixed on its inner periphery and an adhesion fixing face is formed on its outer periphery.
  • the above component having the adhesion fixing face corresponds to the housing.
  • another possible bearing apparatus is such that further comprises, in addition to the shaft member and bracket, a bearing member whose inner circumferential surface forms a radial bearing gap between itself and the outer circumferential surface of the shaft member and in which an adhesion fixing face is formed on its outer circumferential surface.
  • the above component having the adhesion fixing face corresponds to the bearing member.
  • the fluid dynamic bearing apparatus having the constitution described above can be suitably provided as a motor comprising this fluid dynamic bearing apparatus, a stator coil, and a rotor magnet which generates excitation between itself and the stator coil.
  • a fluid dynamic bearing apparatus with an increased adhesive strength between a component having an adhesion fixing face and a bracket can be provided by appropriately controlling the adhesion gap.
  • FIGS. 1 to 4 A first embodiment of the present invention will be described below with reference to FIGS. 1 to 4 .
  • FIG. 1 conceptionally shows a constitutional example of a spindle motor for information appliances which integrates a fluid dynamic bearing apparatus 1 according to the first embodiment of the present invention.
  • This spindle motor is for use in disk drive units such as HDD, and comprises the fluid dynamic bearing apparatus (hydrodynamic bearing apparatus) 1 which rotatably supports a rotational member 3 comprising a shaft 2 in a non-contact manner, stator coils 4 opposing each other, for example, across a gap in the radial direction, and a rotor magnet.
  • the stator coils 4 are attached to coil mounting portions 6 b of a bracket 6 described later, and the rotor magnet 5 is attached to the outer periphery of the rotational member 3 .
  • a housing 7 of the fluid dynamic bearing apparatus 1 is fixed to the inner periphery of the bracket 6 .
  • one or more disk-shaped information recording media (hereinafter simply referred to as disks.) such as magnetic disks are retained on the rotational member 3 .
  • disks. disk-shaped information recording media
  • the rotor magnet 5 is rotated by the excitation generated between the stator coils 4 and rotor magnet 5 , whereby the rotational member 3 and the disks retained on the rotational member 3 rotate with the shaft 2 .
  • FIG. 2 shows the fluid dynamic bearing apparatus 1 .
  • This fluid dynamic bearing apparatus 1 mainly comprises the bracket 6 , the housing 7 fixed to the inner periphery of the bracket 6 , a bearing sleeve 8 fixed on the housing 7 , and the rotational member 3 which rotates relative to the housing 7 and bearing sleeve 8 .
  • the rotational member 3 corresponds to the shaft member.
  • the side sealed with the lid member 10 is referred to as the lower side, while the side opposite to the sealed side is referred as the topside in the description below.
  • the rotational member 3 comprises, for example, a hub portion 9 disposed on the opening side of the housing 7 and the shaft 2 inserted at the inner periphery of the bearing sleeve 8 .
  • the hub portion 9 is formed from a metal or a resin, and is constituted of a disk portion 9 a covering the opening side of the housing 7 (topside), a cylindrical portion 9 b extending downwardly from the outer circumference of the disk portion 9 a in the axial direction, and a disk loading face 9 c and brim 9 d which are provided on the outer periphery of the cylindrical portion 9 b .
  • the disks (not shown) are fitted onto the outer periphery of the disk portion 9 a , and are mounted on the disk loading face 9 c .
  • the disks are retained on the hub portion 9 by an appropriate retaining means (ex., clamper), which is not illustrated.
  • the shaft 2 is formed integrally with the hub portion 9 in this embodiment, and comprises a flange portion 2 b separately as slip-off prevention (preventive) at its lower end.
  • the flange portion 2 b is made of a metal, and is fixed to the shaft 2 , for example, by a means such as screw connection.
  • the bearing sleeve 8 can be formed from, for example, a metal including a copper alloy such as brass and aluminum alloy, and can be also formed from a porous body comprising a sintered metal. In this embodiment, it is cylindrically formed from a porous body of a sintered metal comprising copper as a main ingredient.
  • a region in which a plurality of hydrodynamic grooves are arranged is formed on the entire or a part of the cylindrical region of the inner circumferential surface 8 a of the bearing sleeve 8 as a radial hydrodynamic pressure producing part.
  • two regions in which a plurality of hydrodynamic grooves 8 a 1 , 8 a 2 are arranged in a herringbone shape are formed separately in the axial direction.
  • a region in which a plurality of hydrodynamic grooves are arranged in a spiral shape is formed as a thrust hydrodynamic pressure producing part, although not illustrated in the Fig.
  • This region in which hydrodynamic grooves are formed opposes the upper end face 2 b 1 of the flange portion 2 b as a thrust bearing face, and forms a thrust bearing gap of a second thrust bearing portion T 2 between itself and the upper end face 2 b 1 during rotation of the shaft 2 (rotational member 3 ) (refer to FIG. 2 ).
  • the housing is cylindrically formed from a resin.
  • the housing 7 has such a configuration that both of its axial ends are open, and the other axial end side is sealed with a lid member 10 .
  • a thrust bearing face 7 a is provided on the entire or a part of the annular region of the end face (upper end face) of one end side.
  • a region in which a plurality of hydrodynamic grooves 7 a 1 are arranged in a spiral shape is formed on the thrust bearing face 7 a as a thrust hydrodynamic pressure producing part.
  • This thrust bearing face 7 a (region in which hydrodynamic grooves 7 a 1 are formed) opposes a lower end face 9 a 1 of the disk portion 9 a of the hub portion 9 , and while the rotational member 3 is in rotation, it forms a thrust bearing gap of the first thrust bearing portion T 1 described later between itself and the lower end face 9 a 1 (refer to FIG. 2 ).
  • the lid member 10 sealing the other end side of the housing 7 is formed from a metal or a resin, and is fixed to a shoulder 7 b provided on the inner periphery side at the other end of the housing 7 .
  • the fixing means is particularly limited, and, for example, means such as adhesion (including loose adhesion, press fitting adhesion), press fitting, deposition (for example, ultrasonic deposition), welding (for example, laser welding) can be suitably selected depending on the combination of materials, required mounting strength, sealing performance and other conditions.
  • the outer circumferential surface 8 b of the bearing sleeve 8 is fixed by a suitable means such as, for example, adhesion (including loose adhesion and press fitting adhesion), press fitting, deposition and the like.
  • a tapered sealing face 7 d whose diameter gradually increases toward the top is formed on the outer periphery of the housing 7 .
  • This tapered sealing face 7 d forms an annular sealing space S whose radial dimension gradually decreases from the sealed side (the bottom) of the housing 7 toward the opening side (the top) between itself and the inner circumferential surface 9 b 1 of the cylindrical portion 9 b .
  • This sealing space S is in communication with the outer diameter side of the thrust bearing gap of the first thrust bearing portion T 1 while the shaft 2 and the hub portion 9 are in rotation.
  • An adhesion fixing face 7 e is formed at the lower end of the outer periphery of the housing 7 .
  • the adhesion fixing face 7 e has a cylindrical shape with a constant diameter in this embodiment, and is fixed to the inner circumferential surface 6 a of the bracket 6 with an adhesive (refer to FIG. 2 ).
  • ultraviolet curable adhesives for example, ultraviolet curable adhesives, anaerobic adhesives or epoxy-based adhesives are used in term of workability, in particular curing speed and outgassing characteristics.
  • ultraviolet curable adhesives include 3000 series manufactured by Three Bond Co., Ltd.
  • anaerobic adhesives include 1300 series also manufactured by Three Bond Co., Ltd.
  • epoxy-based adhesives include 2200 series also manufactured by Three Bond Co., Ltd.
  • materials for forming the housing 7 and bracket 6 are selected so that the value obtained by dividing the linear expansion coefficient of the housing 7 by the linear expansion coefficient of the bracket 6 is not lower than 0.5 but not higher than 2.0.
  • the value of the adhesion gap between the two components 6 , 7 before heating is generally 10 ⁇ m to 100 ⁇ m in the diametrical gap.
  • the above adhesion gap is suitably 20 ⁇ m to 40 ⁇ m in the diametrical gap.
  • the materials of the bracket 6 and the housing 7 can be optionally selected, and, it is possible to form, for example, the bracket 6 of a metal such as stainless steel, and the housing 7 of a resin composition comprising a crystalline resin such as LCP, PPS and PEEK as a base resin.
  • high oil resistance low oil absorbing property
  • ester-based lubricating oil during use is required for materials of the housing 7 . It is also necessary to suppress the amount of outgas generated and the amount of water absorbed during use. Moreover, considering a change in temperature in the used atmosphere, high heat resistance is also required.
  • the housing 7 which is excellent in all of the oil resistance, outgassing property, water absorbing property and heat resistance mentioned above can be formed.
  • the base resins crystalline resins such as LCP, PPS, PEEK
  • the housing 7 which is excellent in all of the oil resistance, outgassing property, water absorbing property and heat resistance mentioned above can be formed.
  • polyphenylene sulfide (PPS) is available at less cost compared to other resins and is excellent in fluidity during molding (melt viscosity). Therefore, it is especially suitable as a base resin for the housing 7 of this type.
  • Polyphenylene sulfide is generally produced by the polycondensation reaction of sodium sulfide and paradichlorobenzene, and simultaneously contains a by-product, sodium chloride. Accordingly, it is necessary to use an appropriate solvent to clean polyphenylene sulfide (PPS). Any solvent may be used for cleaning as long as it has a relative dielectric constant of 10 or higher, preferably 20 or higher, and more preferably 50 or higher. Taking environmental aspects into consideration, for example, water (relative dielectric constant: about 80) is preferable, and in particular ultrapure water is preferable. Na in the terminal groups in polyphenylene sulfide (PPS) is mainly removed by conducing cleaning with such a solvent.
  • the amount of Na contained in polyphenylene sulfide (PPS) can be reduced (for example, 2000 ppm or lower), which renders polyphenylene sulfide (PPS) usable as a resin material for forming the housing 7 .
  • removing Na in the terminal groups is also advantageous in that the crystallization speed is increased.
  • Polyphenylene sulfide is roughly categorized into three groups: crosslinked polyphenylene sulfide (PPS); semilinear polyphenylene sulfide (PPS) with fewer side chains; and linear polyphenylene sulfide (PPS) with fewer side chains.
  • PPS polyphenylene sulfide
  • linear polyphenylene sulfide (PPS) with fewer side chains is preferred in that it has fewer molecular terminal groups per molecule and therefore the amount of Na contained is less.
  • linear polyphenylene sulfide (PPS) is also preferable in that it is easy to clean than other types of polyphenylene sulfide (PPS) or it is almost unnecessary to reduce the amount of Na contained by cleaning.
  • those having the amount of Na contained of 2000 ppm or lower, more preferably 1000 ppm, and even more preferably 500 ppm or lower correspond to linear polyphenylene sulfide (PPS). According to this, the amount of Na ion elution into the lubricating oil can be suppressed and Na deposition on the disks retained on the fluid dynamic bearing apparatus 1 and the rotational member 3 or the surface of a disk head (not shown) can be prevented.
  • PPS linear polyphenylene sulfide
  • One or both of carbon fiber and an inorganic compound can be added to the above base resin as fillers.
  • the filler functions to adjust the linear expansion coefficient of the formed housing 7 with these base resins and resin compositions containing fillers by changing the amount to be added to the base resin.
  • the addition of carbon fiber as a filler can greatly strengthen the housing 7 and suppress the dimensional change associated with a change in temperature of the housing 7 so that high dimensional stability can be obtained.
  • This enables forming the hydrodynamic groove 7 a 1 of the thrust bearing face 7 a highly accurately, and controlling the thrust bearing gap of the first thrust bearing portion T 1 during use highly accurately.
  • high conductivity is demonstrated of the carbon fiber by adding carbon fiber to the base resin, and therefore sufficient conductivity (for example, volume resistivity: 1.0 ⁇ 10 6 ⁇ cm or lower) can be imparted to the housing 7 . Accordingly, the static electricity which has accumulated in the disks during use can be dissipated to ground side members (bracket 6 , etc.) through the rotational member 3 and housing 7 (further through the bearing sleeve 8 in some cases).
  • the carbon fiber for example, PAN-based, pitch-based and various other carbon fibers are usable. From the perspective of the strengthening effect and impact absorbing ability, those having relatively high tensile strength (preferably 3000 MPa or higher) are preferable, and PAN-based carbon fibers are preferable as those also having especially high conductively.
  • the carbon fibers added to the resin are preferably rather long fibers in anticipation of breakage of the fibers during molding, and specifically carbon fibers having an average fiber length of 100 ⁇ m or more, and more preferably 1 mm or more are desirably used.
  • the resin cured within the mold is sometimes withdrawn, fused again, and is kneaded with a virgin resin composition to be reused (recycled).
  • the fibers since part of the fibers are repeatedly recycled, when the initial fiber length is too long, the fibers become significantly shorter than their initial fiber lengths because of the cutting associated with the recycling, and changes in the characteristics of the resin composition (lowered melt viscosity, etc.) become noticeable. To minimize such changes in the characteristics, the shorter the fiber length, the better. More specifically, it is desirable to set the average fiber length to 500 ⁇ m or less (preferably 300 ⁇ m or less).
  • the selection of the fiber length of the carbon fibers mentioned above can be determined by the kind of history of the resin composition used in the actual injection molding step. For example, when only the virgin resin composition is used, or when a mixture of the virgin resin composition and recycled resin compositions are used and the ratio of the virgin resin composition is large, from the perspective of inhibiting decreases in the strength, conductively and other properties, it is preferable to use carbon fibers within the dimension range mentioned in the above (1). Contrarily, when the ratio of the recycled resin compositions is large, from the perspective of inhibiting changes in the characteristics of the resin composition associated with the recycling, it is desirable to use carbon fibers within the dimension range mentioned in the above (2).
  • the higher its aspect ratio the higher the strengthening effect due to the fiber reinforcement. Therefore, the higher the aspect ratio of the carbon fibers, the better. More specifically, an aspect ratio of 6.5 or higher is preferred.
  • its average fiber diameter is suitably 5 to 20 ⁇ m.
  • the amount of the carbon fibers added to the base resin is desirably 10 to 35 vol. %, and more preferably 15 to 25 vol. %. This is because if the amount of the carbon fibers added is less than 10 vol. %, the strengthening effect and electrostatic removal effect produced by the carbon fibers are not sufficiently demonstrated and the wear resistance of the portion of the housing 7 which is slid against the hub portion 9 , in particular the wear resistance of the hub portion 9 against which the housing 7 is slid, is not ensured. On the other hand, if the amount added is more than 35 vol. %, the moldability of the housing 7 is lowered, and high dimensional accuracy becomes difficult to obtain.
  • the inorganic compounds Various substances are usable as the inorganic compounds. Among these, inorganic compounds with a small amount of ion elution are especially preferred. As long as the inorganic compounds used are of this type, ion elution which can be a hazardous substance into the lubricating oil can be suppressed and the bearing performance can be maintained at a high level. Alternatively, the situation that the ions stated above are deposited on the bearing apparatus and its surroundings can be avoided so that the cleanliness inside the bearing or around the bearing apparatus can be ensured.
  • inorganic compounds which meet the above conditions include aluminum borate compounds, titanium oxides, zinc oxides and the like.
  • aluminum borate compounds can be especially preferably used.
  • Some of these inorganic compounds are fibrous or powdery. Among these, fibrous one, in particular whiskered ones, are preferable considering the strengthening effect on the housing, while powdery ones are preferred considering the moldability (resin filling capability) of the housing.
  • the melt viscosity of the resin composition containing filters such as carbon fibers and inorganic compounds added to the above base resin is preferably suppressed to 500 Pa ⁇ s or lower at a temperature of 310° C. and a shear rate of 1000 s ⁇ 1 to highly accurately fill the inside of the cavity with the molten resin. Therefore, the melt viscosity of the base resin (PPS) is preferably 100 Pa ⁇ s or lower at a temperature of 310° C. and a shear rate of 1000 s ⁇ 1 to compensate an increase in the viscosity of the resin composition.
  • the housing 7 having high adhesive strength with the bracket 6 , high oil resistance, low outgassing property, high fluidity during molding, low water absorbing property and high heat resistance can be obtained. Therefore, the durability and reliability of the fluid dynamic bearing apparatus 1 and the disk drive unit integrating this bearing apparatus can be increased.
  • the inside of the fluid dynamic bearing apparatus 1 having the constitution described above is filled with the lubricating oil, and the oil level of the lubricating oil is always maintained within the sealing space S.
  • Various substances can be used as the lubricating oil. Low evaporation rate and low viscosity are required especially for the lubricating oil provided to fluid dynamic bearing apparatuses for disk drive units such as HDD.
  • DOS dioctyl sebacate
  • DOZ dioctyl azelate
  • like ester-based lubricating oils are suitable.
  • an oil film of the lubricating oil is formed by the hydrodynamic effect of the hydrodynamic grooves in the thrust bearing gap between the thrust bearing face 7 a of the housing 7 (region in which hydrodynamic grooves 7 a 1 are formed) and the lower end face 9 a 1 of the hub portion 9 (disk portion 9 a ) opposing this, and the thrust bearing gap between the lower end face 8 c of the bearing sleeve 8 (region in which hydrodynamic grooves are formed) and the upper end face 2 b 1 of the flange portion 2 h opposing this, respectively.
  • the first thrust bearing portion T 1 and second thrust bearing portion T 2 which support the rotational member 3 in the thrust direction in a non-contact manner are constituted by the pressure of these oil films.
  • first thrust bearing portion T 1 a thrust bearing face 7 a in which a plurality of hydrodynamic grooves 7 a 1 are arranged on the upper end face of the housing 7 is provided
  • second thrust bearing portion T 2 a thrust bearing face in which a plurality of hydrodynamic grooves are arranged on the lower end face 8 c of the bearing sleeve 8 is provided
  • first thrust bearing portion T 1 a thrust bearing face in which a plurality of hydrodynamic grooves are arranged on the lower end face 8 c of the bearing sleeve 8 is provided
  • second thrust bearing portion T 2 a thrust bearing face in which a plurality of hydrodynamic grooves are arranged on the lower end face 8 c of the bearing sleeve 8 is provided
  • the present invention can be also applied to a fluid dynamic bearing apparatus provided only with the first thrust bearing portion T 1 .
  • the shaft 2 has a straight configuration which does not have the flange portion 2 b .
  • the housing 7 can be formed to have a bottomed cylindrical shape by using a lid member 10 as the bottom integrally from a resin material.
  • the shaft 2 and the hub portion 9 can be formed from a metal or a resin by integrally molding, or the shaft 2 can be formed separately from the hub portion 9 .
  • the shaft 2 can be made of a metal
  • the rotational member 3 can be formed from a resin integrally with the hub portion 9 by using this shaft 2 made of a metal as an insert piece.
  • FIG. 5 shows a fluid dynamic bearing apparatus 11 according to a second embodiment of the present invention.
  • the shaft member 12 comprises a flange portion 12 b provided integrally or separately at its lower end.
  • the housing 17 comprises a cylindrical side portion 17 a , and a bottom 17 b having a structure separate from the side portion 17 a and positioned at the lower end portion of the side portion 17 a .
  • a sealing portion 13 protruding toward the inner periphery side is formed integrally with the housing 17 at the upper end portion of the side portion 17 a of the housing 17 .
  • a first thrust bearing portion T 11 is formed between the lower end face 8 c of the bearing sleeve 8 and the upper end face 12 b 1 of the flange portion 12 b of the shaft member 12
  • a second thrust bearing portion T 12 is formed between the upper end face 17 b 1 of the bottom 17 b of the housing 17 and a lower end face 12 b 2 of the flange portion 12 b.
  • the outer circumferential surface 17 c of the housing 17 serves as an adhesion fixing face which is adhesively fixed to the inner circumferential surface of the bracket (not illustrated). Therefore, if materials such that the ratio of their linear expansion coefficients is not lower than 0.5 but not higher than 2.0 are selected as the materials for forming this housing 17 and the bracket as in the above first embodiment, the housing 17 excellent in the adhesive strength with the bracket, oil resistance, wear resistance, cleanliness, moldability and other properties can be obtained.
  • FIG. 6 shows a fluid dynamic bearing apparatus 21 according to a third embodiment of the present invention.
  • a sealing portion 23 is formed separately from a side portion 27 a of the housing 27 , and is fixed to the inner periphery of the upper end portion of the housing 27 by adhesion, press fitting, deposition or other means.
  • a bottom 27 b of the housing 27 is formed integrally with the side portion 27 a of the housing 27 , and is in the shape of a bottomed cylinder. Since the other constitutions than those mentioned above are similar to the second embodiment, their explanation is omitted.
  • the outer circumferential surface 27 c of the housing 27 serves as an adhesion fixing face which is adhesively fixed to the inner circumferential surface of the bracket (also not illustrated). Therefore, combinations of materials which meet the ratio of their linear expansion coefficients as in the above first embodiment are selected as the materials for forming the housing 27 and the bracket, whereby the housing 27 excellent in the adhesive strength with the bracket, oil resistance, wear resistance, cleanliness, moldability and other properties can be obtained.
  • FIG. 7 shows a fluid dynamic bearing apparatus 31 according to the fourth embodiment of the present invention, and the apparatus has a constitution different from the fluid dynamic bearing apparatuses according to the above first to third embodiments in that it comprises a bearing member 37 as an integral article.
  • the bearing member 37 forms a radial bearing gap between its inner circumferential surface 37 a and the outer circumferential surface 2 a of the shaft 2 , and has an adhesion fixing face 37 e with the bracket 6 on its outer periphery. Furthermore, on the inner circumferential surface 37 a which faces the radial bearing gap, for example, as shown in FIG. 3 , a region (radial bearing face) in which the hydrodynamic grooves 8 a 1 , 8 a 2 are formed is formed. Similarly, the end faces 37 b , 37 c of the bearing member 37 have the configurations corresponding to the thrust bearing faces 7 a , 8 c , respectively, shown in the first embodiment. Since the other constitutions than those mentioned above are similar to the first embodiment, their explanation is omitted.
  • the present invention can be applied not only to the form described above, but also to other components as long as they have the adhesion fixing face 7 e with the bracket 6 .
  • the present invention can be applied to the bracket 6 as long as it has a component having the adhesion fixing face 7 e such as the housing 7 which is adhesively fixed to its inner periphery and is a component for fixing the fluid dynamic bearing apparatus 1 to a motor.
  • the bracket 6 does not necessarily have the portion 6 b for mounting the stator coil 4 , and the present invention can be also applied, for example, by producing the bracket 6 separately from the base component of the motor and adhesively fixing this to the adhesion fixing face 7 e when the fluid dynamic bearing apparatus 1 is fixed to the motor.
  • the housing 7 when the housing 7 is formed from a resin composition, the case where fillers such as carbon fibers and inorganic compounds are added to a single kind of a base resin (polyphenylene sulfide) is described.
  • a base resin polyphenylene sulfide
  • other crystalline resins and noncrystalline resins, rubber components and like organic substances may be added unless they lower the effect of the present. Invention.
  • metal fibers, glass fibers, whiskers and like inorganic substances may be added.
  • PTFE polytetrafluoroethylene
  • carbon black can be added as a conductive agent.
  • the housing 7 is formed from a resin composition and the bracket 6 is formed from a metal is mainly described above, but, as mentioned above, other combinations are also possible as long as the ratio of their linear expansion coefficients falls within the above range (not lower than 0.5 but not higher than 2.0) (also applies to the combination of the bearing member 37 and the bracket 6 .).
  • the housing 7 and the bracket 6 can be both formed from resin compositions, and the two components 6 and 7 can be both formed from a metal.
  • examples of usable metallic materials include SUS420, SUJ2SUS304 and like stainless steel, so-called gunmetal and like copper alloys (bronze, brass, etc.) and aluminium materials (A5056, etc.).
  • the constitution in which the hydrodynamic effect of the lubricating fluid is produced by the hydrodynamic grooves in a herringbone shape and a spiral shape is shown as examples of as the radial bearing portions R 1 , R 2 and thrust bearing portions T 1 , T 2 , but the present invention is not limited to this.
  • a so-called stepped hydrodynamic pressure producing part in which grooves in the axial direction are formed in a plurality of portions in the circumferential direction, or a so-called multilobe bearing in which a plurality of arcuate faces are arranged in the circumferential direction and a wedge-shaped radial gap (bearing gap) is formed between the arcuate faces and the outer circumferential surface 2 a of the opposing shaft 2 (or the shaft member 12 ) may be employed.
  • a so-called circular bearing can be constituted by rendering the inner circumferential surface 8 a of the bearing sleeve 8 which serves as the radial bearing face an inner circumferential surface in the shape of a perfect circle with no hydrodynamic grooves as the hydrodynamic pressure producing part or arcuate faces provided and using this inner circumferential surface and the opposing outer circumferential surface 2 a of the shaft 2 in a perfect circle.
  • One or both of the thrust bearing portions T 1 , T 2 can be also constituted of a so-called step bearing in which a plurality of hydrodynamic grooves in the form of radial grooves are provided at predetermined intervals in the circumferential direction in the region which serves as the thrust bearing face, a wave bearing (in which steps are waves) or other bearings.
  • bearing faces on which the hydrodynamic pressure producing parts are formed are not limited to the components on the fixed side.
  • they can be provided on the side of the shaft 2 , flange portion 2 b and hub portion 9 opposing these (rotation side).
  • housing simulating test pieces and bracket simulating test pieces were prepared from a plurality of materials having different linear expansion coefficients, and the evaluation of the characteristics required for the housing for fluid dynamic bearing apparatuses, including the adhesive strength between the housing and bracket, was carried out.
  • Five types of metallic materials and three types of resin compositions were used as the materials of the above test pieces.
  • Linear polyphenylene sulfide (PPS) was used as a base resin of all the resin compositions.
  • a carbon fiber and an inorganic compound were used as fillers. The constitutional ratio and compounding ratio of the above materials are as shown in FIG. 8 .
  • carbon fiber PAN-based
  • Alborex grade: Y, main constituent: aluminum borate, average diameter: 0.5 to 1.0 ⁇ m, average fiber length: 10 to 30 ⁇ m, form: whisker
  • carbon black was added as an additive in this Example. More specifically, carbon black (grade: #3350B, average particle diameter: 24 nm) manufactured by Mitsubishi Chemical Corporation was used.
  • the molten strand was withdrawn through the holes of a die each having a diameter of 4 mm and cooled, thereby giving rice-sized pellets of the resin composition.
  • the above blend was provided from the side feed portion of the biaxial extruder at a predetermined speed.
  • the evaluation items are the following six: (0) the ratio of the linear expansion coefficients, (1) insolubility of ions of the housing simulating test pieces, (2) volume resistivity [ ⁇ cm], (3) ring abrasion depth [ ⁇ m], (4) abrasion depth of the sliding contacting material [ ⁇ m], and (5) adhesive strength [N].
  • the evaluation test of (0) the ratio of the linear expansion coefficients and (5) adhesive strength were conducted on both the housing simulating test pieces and the bracket simulating test pieces, while the evaluation tests of (1) insolubility of ions to (4) abrasion depth of the sliding contacting material were conducted on the housing simulating test pieces.
  • the evaluation method of each evaluation item (the method of measuring the value of the evaluation item) and the criteria for judging whether it is acceptable or not are as shown below.
  • the linear expansion coefficients of the materials of the ratios of constituents shown in FIG. 8 were determined by using a TMA (thermomechanical analyzer). A specific procedure is shown below.
  • (a) Cup-shaped test pieces in the form of a bottomed cylinder ( ⁇ 10 mm ⁇ > ⁇ 8 mm ⁇ 15 mm, thickness of the bottom: 2 mm) were prepared by using from materials having the ratios of constituents shown in FIG. 8 .
  • the test pieces having the above configuration were formed from a round bar by a lathe turning process.
  • a pin gate was disposed on the outer surface side of the base plate portion to prepare test pieces having the above configuration by injection-molding.
  • the cup-shaped test pieces were set in the TMA.
  • the test pieces which were difficult to set were used with both of their axial ends cut to have the shape of a ring.
  • the measurement direction of a measurement probe is made to coincide with the radial direction of the test pieces.
  • the amount of thermal expansion in the radial direction was determined under the following conditions: measurement load: 0.05 N, measurement temperature range: 23° C. to 100° C., programming rate: 5° C./min, and the atmosphere gas: nitrogen. It should be noted that the upper limit value of the measurement temperature range was set by taking the heat-curing condition (90° C. ⁇ 1 h) of the adhesive described later into consideration.
  • Ratio of linear expansion coefficients [dimensionless] (linear expansion coefficient of housing simulating test piece)/(linear expansion coefficient of bracket simulating test piece)
  • a beaker into which no test piece is placed and only pure water is poured is similarly set in a constant temperature oven heated to 80° C. for one hour, and is used as a blank.
  • the amount of ions contained in ultrapure water into which the test piece obtained in the above is placed is determined by the ion chromatography (measurement value A).
  • the amount of ions contained in the blank is determined in a similar manner separately (measurement value B).
  • the measurement value B is subtracted from the measurement value A to confirm the presence or absence of ion elution.
  • the ions which can be analyzed with the column commonly used in the ion chromatography were used as detectable ions (refer to Table 1 below). A test piece was judged acceptable if the ion described in the table was not detected (Good), while it was judged unacceptable if it such ion was detected (Poor).
  • Measurement was carried out by the four probe method according to JIS K 7194 using the test pieces formed from materials having the ratios of constituents shown in FIG. 8 .
  • criteria for judging whether it is acceptable or not a value of 1.0 ⁇ 10 6 ⁇ cm or lower was judged acceptable (Good), while a value higher than 1.0 ⁇ 10 6 ⁇ cm was judged unacceptable (Poor).
  • Measurement was carried out by the ring-on-disk test in which the disk sides of the ring-shaped test pieces formed from materials having the ratios of constituents shown in FIG. 8 were rotated in a state that the test pieces were pushed against a disk-shaped sliding contacting material in the lubricating oil with a predetermined load.
  • ring-shaped test pieces sizing ⁇ 21 mm (outer diameter) ⁇ 17 mm (inside diameter) ⁇ 3 mm (thickness) were used.
  • a disk material manufactured by SUS420 having the surface roughness Ra of 0.04 ⁇ m and the size of ⁇ 30 mm (diameter) ⁇ 5 mm (thickness) was used as the sliding contacting material.
  • the lubricating oil used as diester oil was di(2-ethylhexyl)azelate.
  • the dynamic viscosity of this lubricating oil at 40° C. is 10.7 mm 2 /s.
  • the contact pressure of the sliding contacting material against the test pieces was 0.25 MPa
  • the rotation speed (peripheral speed) was 1.4 m/min
  • the test time was 14 hours
  • the oil temperature was 80° C.
  • the criteria for judging whether it is acceptable or not were as follows: As for the ring abrasion depth, a value of 3 ⁇ m or lower is judged acceptable (Good), while a value higher than 3 ⁇ m was judged unacceptable (Poor). As for the abrasion depth of the sliding contacting material, a value of 2 ⁇ m or lower was judged acceptable (Good), while a value higher than 2 ⁇ m was judged unacceptable (Poor).
  • Cup-shaped test pieces ⁇ 1> simulating the housing were prepared by using the materials having the ratios of constituents shown in FIG. 8 .
  • the configuration and dimension are the same as the cup-shaped test pieces prepared for the test of (0) the ratio of the linear expansion coefficients.
  • Bushes made of gunmetal were press-fitted onto the inner peripheries of the housing simulating test pieces ⁇ 1> to prevent the deformation of the test pieces ⁇ 1> when they were withdrawn, which will be described below.
  • bracket simulating test pieces ⁇ 2> sizing ⁇ 20 mm ⁇ 10 mm ⁇ 10 mm were prepared from the materials shown in FIG.
  • test pieces ⁇ 1> and ⁇ 2> were sufficiently degreased.
  • a primer was applied on their adhesion faces (the outer circumferential surfaces of the test pieces ⁇ 1>).
  • an anaerobic adhesive was applied on the adhesion faces of all the test pieces ⁇ 2> (the surfaces of the test pieces ⁇ 2> which face the test pieces ⁇ 1> when the test pieces ⁇ 1> were inserted into the test pieces ⁇ 2>).
  • the test pieces ⁇ 1> were then inserted into the test pieces ⁇ 2>, and were cured with heating at 90° C. for one hour.
  • “TB1359D” manufactured by Three Bond Co., Ltd. was used as the anaerobic adhesive
  • “TB1390F” manufactured by Three Bond Co., Ltd. was used as the primer.
  • the amount of the anaerobic adhesive applied was about 10 mg, and the amount of the primer applied was about 1 mg (determined as an increase in the weight of the molded product after a solvent component has been evaporated).
  • the test pieces ⁇ 1> were then withdrawn from the test pieces ⁇ 2>, the maximum load in withdrawing was considered as the adhesive strength.
  • a test piece having an adhesive strength higher than 1000 N was judged acceptable (Good), while that having an adhesive strength of 1000 N or lower was judged unacceptable (Poor).
  • FIGS. 9 and 10 the evaluation results relating to the evaluation items (0) to (5) of each example product and comparative product are shown. If the ratio of the linear expansion coefficient of the linear expansion coefficient of the housing simulated of the test piece to the bracket simulating test piece is too low (lower than 0.5) as comparative products 1 and 2, sufficient adhesive strength cannot be obtained. Moreover, if the above ratio of the linear expansion coefficients is too high as comparative products 3 and 4 (higher than 2.0), sufficient adhesive strength cannot be obtained either.
  • example products 1 to 8 according to the present invention showed excellent results in all the aspects including the adhesive strength, wear resistance (abrasion depth of the ring and contacting material), cleanliness (insolubility of ions) and the electrostatic removability (volume resistivity).
  • FIG. 1 is a cross-sectional view of a spindle motor integrating the fluid dynamic bearing apparatus according to the first embodiment of the present invention.
  • FIG. 2 is a cross-sectional view of the fluid dynamic bearing apparatus according to the first embodiment.
  • FIG. 3 is a cross-sectional view of the bearing sleeve.
  • FIG. 4 shows the upper end face of the housing.
  • FIG. 5 is a cross-sectional view of the fluid dynamic bearing apparatus according to the second embodiment of the present invention.
  • FIG. 6 is a cross-sectional view of the fluid dynamic bearing apparatus according to the third embodiment of the present invention.
  • FIG. 7 is a cross-sectional view of the fluid dynamic bearing apparatus according to the fourth embodiment of the present invention.
  • FIG. 8 is a table showing the ratios of constituents of the materials used for example products and comparative products.
  • FIG. 9 is a table showing the test results of example products.
  • FIG. 10 is a table showing the test results of the comparative products.

Landscapes

  • Engineering & Computer Science (AREA)
  • General Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Fluid Mechanics (AREA)
  • Chemical & Material Sciences (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Power Engineering (AREA)
  • Sliding-Contact Bearings (AREA)
  • Connection Of Motors, Electrical Generators, Mechanical Devices, And The Like (AREA)
  • Mounting Of Bearings Or Others (AREA)
US11/915,490 2005-05-24 2006-04-11 Fluid dynamic bearing apparatus and motor comprising the same Abandoned US20090206708A1 (en)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2005151617 2005-05-24
JP2005151617A JP4794907B2 (ja) 2005-05-24 2005-05-24 流体軸受装置およびこれを備えたモータ
PCT/JP2006/307652 WO2006126337A1 (ja) 2005-05-24 2006-04-11 流体軸受装置およびこれを備えたモータ

Related Parent Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2006/307652 A-371-Of-International WO2006126337A1 (ja) 2005-05-24 2006-04-11 流体軸受装置およびこれを備えたモータ

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/495,538 Continuation US9694567B2 (en) 2005-05-24 2014-09-24 Fluid dynamic bearing apparatus and motor comprising the same

Publications (1)

Publication Number Publication Date
US20090206708A1 true US20090206708A1 (en) 2009-08-20

Family

ID=37451769

Family Applications (2)

Application Number Title Priority Date Filing Date
US11/915,490 Abandoned US20090206708A1 (en) 2005-05-24 2006-04-11 Fluid dynamic bearing apparatus and motor comprising the same
US14/495,538 Active US9694567B2 (en) 2005-05-24 2014-09-24 Fluid dynamic bearing apparatus and motor comprising the same

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/495,538 Active US9694567B2 (en) 2005-05-24 2014-09-24 Fluid dynamic bearing apparatus and motor comprising the same

Country Status (5)

Country Link
US (2) US20090206708A1 (de)
JP (1) JP4794907B2 (de)
CN (1) CN101184928B (de)
DE (1) DE112006001324T5 (de)
WO (1) WO2006126337A1 (de)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120066701A1 (en) * 2010-09-15 2012-03-15 Lg Innotek Co., Ltd. Spindle motor

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2014141655A1 (ja) * 2013-03-15 2014-09-18 パナソニック株式会社 回転位置検出装置
DE102018129709A1 (de) * 2018-11-26 2020-05-28 Minebea Mitsumi Inc. Spindelmotor
DE102019103550A1 (de) * 2019-02-13 2020-08-13 Minebea Mitsumi Inc. Fluiddynamisches Lagersystem
DE102019117013A1 (de) * 2019-06-25 2020-12-31 Minebea Mitsumi Inc. Fluiddynamisches Lagersystem

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4713703A (en) * 1985-08-31 1987-12-15 Alps Electric Co., Ltd. Information recording and reproducing apparatus
US4908402A (en) * 1985-08-23 1990-03-13 Mitsubishi Rayon Co., Ltd. Reinforced resin composition
US5945752A (en) * 1996-12-27 1999-08-31 Sankyo Seiki Mfg. Co., Ltd. Shaft-fixed-type motor
US6390681B1 (en) * 1999-04-05 2002-05-21 Ntn Corporation Dynamic pressure bearing-unit
US6431757B1 (en) * 1999-10-28 2002-08-13 Ntn Corporation Hydrodynamic type bearing unit
US6513979B2 (en) * 2000-08-22 2003-02-04 Ntn Corporation Hydrodynamic oil-impregnated sintered bearing unit
US20040264817A1 (en) * 2003-05-13 2004-12-30 Fuminori Satoji Fluid bearing device
US20050127782A1 (en) * 2001-12-21 2005-06-16 Morinobu Endo Ultrasonic motor, and electronic timepiece having ultrasonic motor
US20060045395A1 (en) * 2004-09-01 2006-03-02 Eiichiro Shimazu Shaft member for hydrodynamic bearing device
US7147376B2 (en) * 2003-06-10 2006-12-12 Ntn Corporation Dynamic bearing device
US7431505B2 (en) * 2005-01-17 2008-10-07 Ntn Corporation Fluid lubrication bearing apparatus
US7625124B2 (en) * 2003-09-18 2009-12-01 Ntn Corporation Fluid bearing device
US7650697B2 (en) * 2004-06-01 2010-01-26 Nidec Corporation Methods of manufacturing fluid-dynamic-pressure bearing and spindle motor incorporating the bearing, and spindle motor and recording-disk drive incorporating the bearing
US7690845B2 (en) * 2003-07-23 2010-04-06 Ntn Corporation Fluid bearing device
US7798721B2 (en) * 2004-03-30 2010-09-21 Ntn Corporation Fluid dynamic bearing device

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE3689772T2 (de) 1985-12-28 1994-10-06 Nissha Printing Übertragungsmaterial für gedruckte leiterplatte, sowie vorbereitete gedruckte leiterplatte zur verwendung dieses übertragungsmaterials und verfahren zur herstellung.
JPH06104773B2 (ja) * 1987-09-08 1994-12-21 東レ株式会社 ポリフェニレンスルフィド樹脂組成物
JPH10243605A (ja) * 1996-12-27 1998-09-11 Sankyo Seiki Mfg Co Ltd 軸固定型モータ
JPH11191234A (ja) * 1997-10-23 1999-07-13 Ntn Corp 光学式ピックアップのレンズホルダおよびそのアクチュエータ
JP3774080B2 (ja) * 1999-04-05 2006-05-10 Ｎｔｎ株式会社 動圧型軸受ユニット
JP4738578B2 (ja) 2000-09-12 2011-08-03 キヤノン株式会社 情報端末、情報端末の制御方法、及び記録媒体
US7027545B2 (en) 2001-05-09 2006-04-11 Tropian, Inc. Data sampler for digital frequency/phase determination
JP2003214432A (ja) * 2002-01-24 2003-07-30 Matsushita Electric Ind Co Ltd 軸受装置およびそのシール方法
JP4216509B2 (ja) 2002-02-20 2009-01-28 Ｎｔｎ株式会社 動圧軸受装置の製造方法
JP4330961B2 (ja) * 2003-09-16 2009-09-16 Ｎｔｎ株式会社 動圧軸受装置
JP4754794B2 (ja) * 2003-09-12 2011-08-24 ミネベア株式会社 流体軸受ユニットおよび該流体軸受ユニットを備えたスピンドルモータ、記録ディスク駆動装置
JP2005114164A (ja) * 2003-09-18 2005-04-28 Ntn Corp 動圧軸受装置
JP2006029565A (ja) 2004-07-21 2006-02-02 Matsushita Electric Ind Co Ltd 流体軸受装置、その流体軸受装置を有するスピンドルモータ及びハードディスク駆動装置

Patent Citations (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4908402A (en) * 1985-08-23 1990-03-13 Mitsubishi Rayon Co., Ltd. Reinforced resin composition
US4713703A (en) * 1985-08-31 1987-12-15 Alps Electric Co., Ltd. Information recording and reproducing apparatus
US5945752A (en) * 1996-12-27 1999-08-31 Sankyo Seiki Mfg. Co., Ltd. Shaft-fixed-type motor
US6390681B1 (en) * 1999-04-05 2002-05-21 Ntn Corporation Dynamic pressure bearing-unit
US6431757B1 (en) * 1999-10-28 2002-08-13 Ntn Corporation Hydrodynamic type bearing unit
US6513979B2 (en) * 2000-08-22 2003-02-04 Ntn Corporation Hydrodynamic oil-impregnated sintered bearing unit
US20050127782A1 (en) * 2001-12-21 2005-06-16 Morinobu Endo Ultrasonic motor, and electronic timepiece having ultrasonic motor
US20040264817A1 (en) * 2003-05-13 2004-12-30 Fuminori Satoji Fluid bearing device
US7267484B2 (en) * 2003-05-13 2007-09-11 Ntn Corporation Fluid bearing device
US7147376B2 (en) * 2003-06-10 2006-12-12 Ntn Corporation Dynamic bearing device
US7690845B2 (en) * 2003-07-23 2010-04-06 Ntn Corporation Fluid bearing device
US7625124B2 (en) * 2003-09-18 2009-12-01 Ntn Corporation Fluid bearing device
US7798721B2 (en) * 2004-03-30 2010-09-21 Ntn Corporation Fluid dynamic bearing device
US7650697B2 (en) * 2004-06-01 2010-01-26 Nidec Corporation Methods of manufacturing fluid-dynamic-pressure bearing and spindle motor incorporating the bearing, and spindle motor and recording-disk drive incorporating the bearing
US20060045395A1 (en) * 2004-09-01 2006-03-02 Eiichiro Shimazu Shaft member for hydrodynamic bearing device
US7431505B2 (en) * 2005-01-17 2008-10-07 Ntn Corporation Fluid lubrication bearing apparatus

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120066701A1 (en) * 2010-09-15 2012-03-15 Lg Innotek Co., Ltd. Spindle motor
US8607256B2 (en) * 2010-09-15 2013-12-10 Lg Innotek Co., Ltd. Spindle motor

Also Published As

Publication number Publication date
WO2006126337A1 (ja) 2006-11-30
CN101184928A (zh) 2008-05-21
CN101184928B (zh) 2010-08-11
US20150007937A1 (en) 2015-01-08
JP2006329275A (ja) 2006-12-07
DE112006001324T5 (de) 2008-04-17
US9694567B2 (en) 2017-07-04
JP4794907B2 (ja) 2011-10-19

Similar Documents

Publication Publication Date Title
KR101237845B1 (ko) 동압 베어링 장치
US9694567B2 (en) Fluid dynamic bearing apparatus and motor comprising the same
US20060045395A1 (en) Shaft member for hydrodynamic bearing device
WO2007032299A1 (ja) 流体軸受装置およびその製造方法、並びにディスク駆動装置
JP5095115B2 (ja) 動圧軸受装置
US8267587B2 (en) Housing for fluid lubrication bearing apparatuses
KR20070059047A (ko) 동압 베어링 장치
US20090297076A1 (en) Fluid dynamic bearing device
JP5085025B2 (ja) 流体軸受装置
JP4628720B2 (ja) 動圧軸受装置用ハウジング及びこれを備えた動圧軸受装置、並びにこの動圧軸受装置を有するモータ
JP2006046431A (ja) 動圧軸受装置
JP4907106B2 (ja) 流体軸受装置用ハウジング、及び流体軸受装置用ハウジングと軸受スリーブとの一体化部材
US8778242B2 (en) Housing for fluid dynamic bearing device
JP4907105B2 (ja) 流体軸受装置用ハウジング、及び流体軸受装置用ハウジングと軸受スリーブとの一体化部材
JP2007082267A (ja) 流体軸受装置
JP2004011721A (ja) 流体軸受装置
JP5031863B2 (ja) 流体軸受装置
JP2008131832A5 (de)

Legal Events

Date Code Title Description
AS Assignment

Owner name: NTN CORPORATION, JAPAN

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MURAKAMI, KAZUTOYO;EGAMI, MASAKI;REEL/FRAME:022287/0451

Effective date: 20071228

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION