US20060234592A1 - Flame-retardant fiber composite and fabric produced therefrom - Google Patents
Flame-retardant fiber composite and fabric produced therefrom Download PDFInfo
- Publication number
- US20060234592A1 US20060234592A1 US10/554,488 US55448805A US2006234592A1 US 20060234592 A1 US20060234592 A1 US 20060234592A1 US 55448805 A US55448805 A US 55448805A US 2006234592 A1 US2006234592 A1 US 2006234592A1
- Authority
- US
- United States
- Prior art keywords
- fiber
- weight
- flame resistant
- fibers
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Links
Classifications
-
- D—TEXTILES; PAPER
- D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
- D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
- D02G3/00—Yarns or threads, e.g. fancy yarns; Processes or apparatus for the production thereof, not otherwise provided for
- D02G3/44—Yarns or threads characterised by the purpose for which they are designed
- D02G3/443—Heat-resistant, fireproof or flame-retardant yarns or threads
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4282—Addition polymers
-
- D—TEXTILES; PAPER
- D02—YARNS; MECHANICAL FINISHING OF YARNS OR ROPES; WARPING OR BEAMING
- D02G—CRIMPING OR CURLING FIBRES, FILAMENTS, THREADS, OR YARNS; YARNS OR THREADS
- D02G3/00—Yarns or threads, e.g. fancy yarns; Processes or apparatus for the production thereof, not otherwise provided for
- D02G3/02—Yarns or threads characterised by the material or by the materials from which they are made
- D02G3/04—Blended or other yarns or threads containing components made from different materials
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/425—Cellulose series
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4266—Natural fibres not provided for in group D04H1/425
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4282—Addition polymers
- D04H1/43—Acrylonitrile series
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4326—Condensation or reaction polymers
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4326—Condensation or reaction polymers
- D04H1/4334—Polyamides
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4326—Condensation or reaction polymers
- D04H1/4334—Polyamides
- D04H1/4342—Aromatic polyamides
-
- D—TEXTILES; PAPER
- D04—BRAIDING; LACE-MAKING; KNITTING; TRIMMINGS; NON-WOVEN FABRICS
- D04H—MAKING TEXTILE FABRICS, e.g. FROM FIBRES OR FILAMENTARY MATERIAL; FABRICS MADE BY SUCH PROCESSES OR APPARATUS, e.g. FELTS, NON-WOVEN FABRICS; COTTON-WOOL; WADDING ; NON-WOVEN FABRICS FROM STAPLE FIBRES, FILAMENTS OR YARNS, BONDED WITH AT LEAST ONE WEB-LIKE MATERIAL DURING THEIR CONSOLIDATION
- D04H1/00—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres
- D04H1/40—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties
- D04H1/42—Non-woven fabrics formed wholly or mainly of staple fibres or like relatively short fibres from fleeces or layers composed of fibres without existing or potential cohesive properties characterised by the use of certain kinds of fibres insofar as this use has no preponderant influence on the consolidation of the fleece
- D04H1/4382—Stretched reticular film fibres; Composite fibres; Mixed fibres; Ultrafine fibres; Fibres for artificial leather
- D04H1/43835—Mixed fibres, e.g. at least two chemically different fibres or fibre blends
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
- Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
- Y10T442/696—Including strand or fiber material which is stated to have specific attributes [e.g., heat or fire resistance, chemical or solvent resistance, high absorption for aqueous compositions, water solubility, heat shrinkability, etc.]
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
- Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
- Y10T442/697—Containing at least two chemically different strand or fiber materials
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T442/00—Fabric [woven, knitted, or nonwoven textile or cloth, etc.]
- Y10T442/60—Nonwoven fabric [i.e., nonwoven strand or fiber material]
- Y10T442/697—Containing at least two chemically different strand or fiber materials
- Y10T442/698—Containing polymeric and natural strand or fiber materials
Definitions
- the technique can provide an advanced flame resistant fiber composite having outstanding touch and outstanding moisture absorptivity, and advanced flame resistance by means of mixing of a small amount of a heat-resistant fiber, that is, of mixing of halogen atom and Sb compounds containing fiber that can be used for work uniform usage, and cotton, etc.
- the present invention relates to a flame resistant fiber composite obtained by compounding so as to give 100% by weight of a total amount of (A) to (D): 20 to 85% by weight of a fiber (A) containing 0.5 to 50 parts by weight of an Sb compound to 100 parts by weight of a polymer containing halogen atom of not less than 17% by weight; 5 to 80% by weight of a heat-resistant fiber (B); 0 to 40% by weight of a cellulosic fiber (C); and 0 to 40% by weight of an inflammable fiber (D), such as chemical fiber.
- copolymerizable vinyl monomer examples include, for example: acrylic acid, and esters thereof; methacrylic acid, and esters thereof; acrylamide; methacryl amide; vinyl acetate; vinyl sulfonic acid, and salts thereof; methallyl sulfonic acid, and salts thereof; styrene sulfonic acid, and salts thereof; 2-acrylamide-2-methylsulfonic acid, and salts thereof. These may be used independently or two kinds or more may be used in combination.
- Examples of a copolymer containing units originated from the halogen containing vinyl based monomer and acrylonitrile include, for example, a copolymer consisting of 50 parts of vinyl chloride, 49 parts of acrylonitrile, and 1 part of sodium styrene sulfonate; a copolymer consisting of 43.5 parts of vinylidene chloride, 55 parts of acrylonitrile, and 1.5 parts of sodium styrene sulfonate; a copolymer consisting of 41 parts of vinylidene chloride, 56 parts of acrylonitrile, and 3 parts of sodium 2-acrylamide-2-methylsulfonate etc.
- the heat-resistant fiber (B) (hereinafter referred to as fiber (B)) used for the present invention is a component is for formation of a backbone structure for maintenance of a shape of the flame resistant fiber composite in burning of the inflammable component in the flame resistant fiber composite.
- fiber (B) has a melting point
- the melting point is not less than 350 degrees C.
- the heat-resistant fiber (B) is a fiber having heat-resisting property with a decomposition temperature of not less than 300 degrees C.
- the fiber (B) include, for example, the fibers obtained from aromatic polyamides, melamine, polyamidoimides, poly benzimidazoles, etc., silicic acid containing fibers, phenolic fibers, carbon fibers, etc. and the fiber (B) may be used independently and two or more kinds may be used in combination.
- the component fibers are compounded so as to give 100% by weight of a sum total of: 85 to 20% by weight of the fiber (A), and preferably 75 to 25% by weight; 15 to 80% by weight of the silicic acid containing cellulose fiber, and preferably 20 to 70% by weight; and 0 to 40% by weight of the fiber (D), and preferably 5 to 35% by weight.
- an amount of the fiber (B) of less than 10% by weight cannot give sufficient fire-resistant effect having durability to flame for a long time.
- an amount exceeding 50% by weight gives the flame resistant fiber composite with only unsatisfactory touch and sensuousness as a disadvantage of usual heat-resistant fibers.
- an amount of the fiber containing 0.5 to 5.5 parts by weight of the Sb compound to a polymer containing chlorine of not less than 25% by weight as the fiber (A) is smaller than that of the fiber (C) in the flame resistant fiber composite, inadequate amount of formation of carbonized materials occurs, leading to decrease in fire-resistant effect with durability to flaming for a long time.
- the fabrics When a fabric is manufactured using the flame resistant fiber composite of the present invention, the fabrics has characteristics, such as outstanding flame resistance, touch, feeling, moisture absorptivity, sensuousness, etc. originated in the flame resistant fiber composite of the present invention.
- the above-described “fabric” comprises textiles, knittings, nonwoven fabrics, and strings, and the “fabric” may be advantageously used not only in garments, such as fire-resistant work uniforms, but in interior designed products, such as curtains and carpets, beddings, such as sheets, blankets, bed mats, and bed pads etc. and moreover in applications that need general fiber characteristics and advanced flame resistance and also that need excellent touch, moisture absorptivity, feeling, and sensuousness.
- Dyeing was performed under following conditions: cationic dyestuffs (Maxilon Yellow 2RL 0.55% omf, Maxilon Red GRL 0.25% omf, Maxilon Blue GRL 0.30% omf: all manufactured by Ciba-Geigy), acetic acid, sodium acetate, and anionic dispersant 2% omf (LevenolWX: manufactured by Kao Corp.) as an auxiliary agent, an accelerating agent 0.4% omf (sodium lauryl sulfate), liquor ratio 1:2.5, and boiled at normal pressure for 1-hour. After dyeing, the sample was dehydrated by a centrifugal dehydrator, and dried at ordinary temperature to obtain a nonwoven fabric having dark brown hue.
- cationic dyestuffs Maxilon Yellow 2RL 0.55% omf, Maxilon Red GRL 0.25% omf, Maxilon Blue GRL 0.30% omf: all manufactured by Ciba-Gei
- the antimony trioxide had a particle diameter uniformly adjusted to not more than 2 micrometers, and was beforehand adjusted so that it might disperse uniformly in a diluting resin solution.
Landscapes
- Engineering & Computer Science (AREA)
- Textile Engineering (AREA)
- Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Mechanical Engineering (AREA)
- Artificial Filaments (AREA)
- Woven Fabrics (AREA)
- Yarns And Mechanical Finishing Of Yarns Or Ropes (AREA)
- Treatments For Attaching Organic Compounds To Fibrous Goods (AREA)
- Absorbent Articles And Supports Therefor (AREA)
Applications Claiming Priority (7)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2003-123269 | 2003-04-28 | ||
JP2003123269 | 2003-04-28 | ||
JP2003125162 | 2003-04-30 | ||
JP2003-125162 | 2003-04-30 | ||
JP2003125161 | 2003-04-30 | ||
JP2003-125161 | 2003-04-30 | ||
PCT/JP2004/005583 WO2004097088A1 (ja) | 2003-04-28 | 2004-04-19 | 難燃繊維複合体およびそれを用いて製造した布帛 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20060234592A1 true US20060234592A1 (en) | 2006-10-19 |
Family
ID=33424782
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US10/554,488 Abandoned US20060234592A1 (en) | 2003-04-28 | 2004-04-19 | Flame-retardant fiber composite and fabric produced therefrom |
Country Status (11)
Country | Link |
---|---|
US (1) | US20060234592A1 (zh) |
EP (1) | EP1619278B1 (zh) |
JP (1) | JP4308820B2 (zh) |
KR (1) | KR20060007032A (zh) |
CN (1) | CN1806071B (zh) |
AT (1) | ATE433509T1 (zh) |
CA (1) | CA2523378A1 (zh) |
DE (1) | DE602004021484D1 (zh) |
ES (1) | ES2326170T3 (zh) |
MX (1) | MXPA05011334A (zh) |
WO (1) | WO2004097088A1 (zh) |
Cited By (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060090272A1 (en) * | 2004-10-22 | 2006-05-04 | Kaneka Corporation | Flame-retardant mattress |
US20090139016A1 (en) * | 2005-12-16 | 2009-06-04 | E.I. Du Pont De Nemours And Company | Thermal Performance Garments Comprising an Outer Shell Fabric of PIPD and Aramid Fibers |
US20100021723A1 (en) * | 2008-07-24 | 2010-01-28 | Nat Style Limited | "Layered product with high thermal insulation and self-extinguishing capacity" |
US7816287B1 (en) * | 2009-07-10 | 2010-10-19 | Polymer Group, Inc. | Flame retardant nonwoven fabric and bedding articles |
US20110212658A1 (en) * | 2010-03-01 | 2011-09-01 | Bekaert Textiles Usa, Inc. | Fire retardant fabric |
US9091000B2 (en) | 2011-09-26 | 2015-07-28 | Kaneka Corporation | Flameproof spun yarn, fabric, clothes and flameproof work clothes |
US9175147B2 (en) | 2011-07-06 | 2015-11-03 | National Research Council Of Canada | Fire-resistant cellulosic material |
US20230019403A1 (en) * | 2020-03-10 | 2023-01-19 | Kaneka Corporation | Cloth for mattress and method for manufacturing the same |
Families Citing this family (23)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP4757543B2 (ja) * | 2005-06-14 | 2011-08-24 | 株式会社カネカ | 難燃性不織布およびそれを用いた難燃性マットレス |
JP2007105403A (ja) * | 2005-10-17 | 2007-04-26 | Kaneka Corp | 難燃性不織布およびそれを用いた難燃性マットレス |
KR100756557B1 (ko) * | 2006-04-27 | 2007-09-11 | (주)리디아 | 난연처리된 레이온 단사를 이용한 방염 부직포 및 원단 및그 제조방법 |
ITFI20070003A1 (it) * | 2007-01-10 | 2008-07-11 | Marco Cavallaro | Un materiale termomodellabile, e suo procedimento di realizzazione. |
US7786031B2 (en) | 2007-01-26 | 2010-08-31 | Milliken & Company | Flame resistant textile |
CN101787599B (zh) * | 2010-04-02 | 2012-05-23 | 绍兴文理学院 | 一种t/r/h多元功能纤维混纤高质感纱线的生产工艺 |
BR112013014071A2 (pt) * | 2010-12-09 | 2016-09-13 | Kaneka Corp | roupas de trabalho de proteção de arco contendo fibras modacrílicas |
US20130029151A1 (en) * | 2011-03-18 | 2013-01-31 | E. I. Du Pont De Nemours And Company | Flame-resistant finish for inherently flame resistant polymer yarns and process for making same |
KR101280553B1 (ko) * | 2012-01-03 | 2013-07-01 | 남택욱 | 레이온 단섬유와 탄소섬유를 포함하는 준 불연 방적사 및 이를 사용한 원단 |
US20140187113A1 (en) * | 2012-04-04 | 2014-07-03 | Drifire, Llc | Fiber blends for dual hazard and comfort properties |
CN102677290A (zh) * | 2012-05-29 | 2012-09-19 | 蔡紫林 | 一种面料 |
WO2013183755A1 (ja) * | 2012-06-08 | 2013-12-12 | 株式会社カネカ | 防護服用布帛、及び耐アーク防護服 |
KR101442720B1 (ko) * | 2013-03-22 | 2014-09-19 | 한국니트산업연구원 | 방염성 원사 및 그 제조방법 |
CN105495750B (zh) * | 2014-09-22 | 2018-06-05 | 株式会社钟化 | 阻燃性布帛和含有该布帛的防护服 |
CN108882763B (zh) * | 2016-03-25 | 2021-07-27 | 株式会社钟化 | 人工毛发用丙烯酸系纤维、其制造方法及包含其的头饰制品 |
JP6714074B2 (ja) * | 2016-04-05 | 2020-06-24 | 帝人株式会社 | 布帛および多層構造布帛および繊維製品 |
EP3579727B1 (en) * | 2017-02-09 | 2024-04-03 | Tuft & Needle, LLC | Flame retardant cover |
CN107313168A (zh) * | 2017-08-31 | 2017-11-03 | 苏州英得福机电科技有限公司 | 一种环保复合型阻燃面料 |
CN110067037A (zh) * | 2019-04-26 | 2019-07-30 | 中科国联劳动防护技术研究院(北京)有限公司 | 一种再生纤维素纤维 |
CN110079889A (zh) * | 2019-04-26 | 2019-08-02 | 中科国联劳动防护技术研究院(北京)有限公司 | 一种灭火型再生纤维素纤维共混物 |
CN110042565A (zh) * | 2019-04-26 | 2019-07-23 | 中科国联劳动防护技术研究院(北京)有限公司 | 一种基于灭火型阻燃再生纤维素纤维的阻燃防电弧共混物 |
KR102654523B1 (ko) * | 2019-09-10 | 2024-04-05 | 가부시키가이샤 가네카 | 난연성 섬유 복합체 및 난연성 작업복 |
WO2023171288A1 (ja) * | 2022-03-09 | 2023-09-14 | 株式会社カネカ | 難燃性アクリル系繊維、その製造方法、並びにそれを含む難燃性繊維集合体及び難燃性作業服 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4863797A (en) * | 1984-10-05 | 1989-09-05 | Kanegafuchi Kagaku Kogyo Kabushiki Kaisha | Flame-retarded composite fiber |
US4865906A (en) * | 1988-01-22 | 1989-09-12 | Smith Novis W Jr | Flame retardant yard blend |
US5417752A (en) * | 1991-12-31 | 1995-05-23 | Kemira Fibres Oy | Product containing silicon dioxide and a method for its preparation |
US5981407A (en) * | 1996-05-13 | 1999-11-09 | Kaneka Corporation | Thermal resistance-improved flame retardant cloth |
US6162747A (en) * | 1996-05-13 | 2000-12-19 | Keneka Corporation | Flame retardant cloth |
US20040226100A1 (en) * | 2003-05-05 | 2004-11-18 | Small James Douglas | Heat and flame-resistant materials and upholstered articles incorporating same |
US7259117B2 (en) * | 2001-09-12 | 2007-08-21 | Mater Dennis L | Nonwoven highloft flame barrier |
Family Cites Families (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6189339A (ja) * | 1984-10-05 | 1986-05-07 | 鐘淵化学工業株式会社 | 複合難燃繊維 |
JP2693129B2 (ja) * | 1995-02-16 | 1997-12-24 | 鐘淵化学工業株式会社 | 難燃繊維複合体およびそれを用いて製造した布帛 |
JP4420554B2 (ja) * | 2000-11-22 | 2010-02-24 | 株式会社カネカ | 難燃性不織布 |
-
2004
- 2004-04-19 CA CA002523378A patent/CA2523378A1/en not_active Abandoned
- 2004-04-19 KR KR1020057020164A patent/KR20060007032A/ko not_active Application Discontinuation
- 2004-04-19 CN CN2004800163501A patent/CN1806071B/zh not_active Expired - Fee Related
- 2004-04-19 WO PCT/JP2004/005583 patent/WO2004097088A1/ja active Application Filing
- 2004-04-19 DE DE200460021484 patent/DE602004021484D1/de not_active Expired - Lifetime
- 2004-04-19 AT AT04728234T patent/ATE433509T1/de not_active IP Right Cessation
- 2004-04-19 ES ES04728234T patent/ES2326170T3/es not_active Expired - Lifetime
- 2004-04-19 JP JP2005505844A patent/JP4308820B2/ja not_active Expired - Fee Related
- 2004-04-19 US US10/554,488 patent/US20060234592A1/en not_active Abandoned
- 2004-04-19 EP EP04728234A patent/EP1619278B1/en not_active Expired - Lifetime
- 2004-04-19 MX MXPA05011334A patent/MXPA05011334A/es unknown
Patent Citations (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4863797A (en) * | 1984-10-05 | 1989-09-05 | Kanegafuchi Kagaku Kogyo Kabushiki Kaisha | Flame-retarded composite fiber |
US5348796A (en) * | 1984-10-05 | 1994-09-20 | Kanegafuchi Kogaku Kogyo Kabushiki Kaisha | Flame-retarded composite fiber |
US5503916A (en) * | 1984-10-05 | 1996-04-02 | Kanegafuchi Kagaku Kogyo Kabushiki Kaisha | Flame-retarded clothing |
US5503915A (en) * | 1984-10-05 | 1996-04-02 | Kanegafuchi Kagaku Kogyo Kabushiki Kaisha | Flame retarded interior good |
US5506042A (en) * | 1984-10-05 | 1996-04-09 | Kanegafuchi Kagaku Kogyo Kabushiki Kaisha | Flame-retarded bedding product |
US4865906A (en) * | 1988-01-22 | 1989-09-12 | Smith Novis W Jr | Flame retardant yard blend |
US5417752A (en) * | 1991-12-31 | 1995-05-23 | Kemira Fibres Oy | Product containing silicon dioxide and a method for its preparation |
US5981407A (en) * | 1996-05-13 | 1999-11-09 | Kaneka Corporation | Thermal resistance-improved flame retardant cloth |
US6162747A (en) * | 1996-05-13 | 2000-12-19 | Keneka Corporation | Flame retardant cloth |
US7259117B2 (en) * | 2001-09-12 | 2007-08-21 | Mater Dennis L | Nonwoven highloft flame barrier |
US20040226100A1 (en) * | 2003-05-05 | 2004-11-18 | Small James Douglas | Heat and flame-resistant materials and upholstered articles incorporating same |
Cited By (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20060090272A1 (en) * | 2004-10-22 | 2006-05-04 | Kaneka Corporation | Flame-retardant mattress |
US7858542B2 (en) * | 2004-10-22 | 2010-12-28 | Kaneka Corporation | Flame-retardant mattress |
US20090139016A1 (en) * | 2005-12-16 | 2009-06-04 | E.I. Du Pont De Nemours And Company | Thermal Performance Garments Comprising an Outer Shell Fabric of PIPD and Aramid Fibers |
US20100021723A1 (en) * | 2008-07-24 | 2010-01-28 | Nat Style Limited | "Layered product with high thermal insulation and self-extinguishing capacity" |
US7816287B1 (en) * | 2009-07-10 | 2010-10-19 | Polymer Group, Inc. | Flame retardant nonwoven fabric and bedding articles |
US20110212658A1 (en) * | 2010-03-01 | 2011-09-01 | Bekaert Textiles Usa, Inc. | Fire retardant fabric |
US9175147B2 (en) | 2011-07-06 | 2015-11-03 | National Research Council Of Canada | Fire-resistant cellulosic material |
US9091000B2 (en) | 2011-09-26 | 2015-07-28 | Kaneka Corporation | Flameproof spun yarn, fabric, clothes and flameproof work clothes |
US20230019403A1 (en) * | 2020-03-10 | 2023-01-19 | Kaneka Corporation | Cloth for mattress and method for manufacturing the same |
US12037723B2 (en) * | 2020-03-10 | 2024-07-16 | Kaneka Corporation | Cloth for mattress and method for manufacturing the same |
Also Published As
Publication number | Publication date |
---|---|
MXPA05011334A (es) | 2006-01-30 |
WO2004097088A1 (ja) | 2004-11-11 |
EP1619278A1 (en) | 2006-01-25 |
KR20060007032A (ko) | 2006-01-23 |
ES2326170T3 (es) | 2009-10-02 |
CN1806071A (zh) | 2006-07-19 |
EP1619278A4 (en) | 2006-09-20 |
ATE433509T1 (de) | 2009-06-15 |
CN1806071B (zh) | 2011-08-31 |
DE602004021484D1 (de) | 2009-07-23 |
EP1619278B1 (en) | 2009-06-10 |
JP4308820B2 (ja) | 2009-08-05 |
CA2523378A1 (en) | 2004-11-11 |
JPWO2004097088A1 (ja) | 2006-07-13 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1619278B1 (en) | Flame-retardant fiber composite and fabric produced therefrom | |
TWI408266B (zh) | 難燃性合成纖維與難燃纖維集合體及該等之製造方法、與纖維製品 | |
JP2593985B2 (ja) | 寝具用繊維製品 | |
WO2005103346A1 (ja) | 難燃性合成繊維およびそれを用いた難燃繊維製品 | |
US20220167700A1 (en) | Flame-retardant fiber composite and flame-retardant working clothes | |
EP1798318B1 (en) | Flame-retardant synthetic fiber, flame-retardant fiber composite, and upholstered furniture product made with the same | |
JP2693129B2 (ja) | 難燃繊維複合体およびそれを用いて製造した布帛 | |
JP2007270410A (ja) | カバー用難燃性布帛 | |
US20070237953A1 (en) | Flame resistant synthetic fiber, flame resistant fiber composite and upholstered furniture products using the same | |
JP3004107B2 (ja) | 難燃繊維複合体 | |
JP2593989B2 (ja) | インテリア繊維製品 | |
JP4346566B2 (ja) | 難燃性合成繊維および該難燃性合成繊維を用いた難燃性繊維複合体および該難燃性繊維複合体を用いた布張り家具製品 | |
JP2593988B2 (ja) | 衣料用繊維製品 | |
WO2022181337A1 (ja) | 難燃性アクリル系繊維、難燃性繊維複合体、及び難燃性マットレス | |
JPH111842A (ja) | カバー用難燃性布帛 | |
JP4777892B2 (ja) | 難燃性合成繊維、難燃繊維複合体およびそれを用いた布張り家具製品 | |
WO2010010639A1 (ja) | 難燃性合成繊維とその製造方法、難燃繊維複合体及び繊維製品 | |
JP2007270411A (ja) | 難燃性合成繊維、難燃繊維複合体およびそれを用いた布張り家具製品 | |
JP2812672B2 (ja) | 難燃繊維複合体の製法 | |
JPWO2006008958A1 (ja) | 難燃性合成繊維、難燃繊維複合体および難燃繊維複合体を用いた布張り家具製品 | |
JP2007308849A (ja) | 難燃性合成繊維、難燃繊維複合体およびそれを用いた布張り家具製品 | |
JP2007169794A (ja) | 難燃性合成繊維、難燃繊維複合体及びそれを用いた布張り家具製品 | |
JP2007154338A (ja) | カバー用難燃性布帛 | |
JPH05239728A (ja) | 複合難燃繊維の製法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: KANEKA CORPORATION, JAPAN Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:MIO, WATARU;IWADE, SUSUMU;MARUYAMA, SHIGERU;AND OTHERS;REEL/FRAME:017903/0071;SIGNING DATES FROM 20051014 TO 20051018 |
|
STCB | Information on status: application discontinuation |
Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION |