TWI818583B - 顯示器保護器 - Google Patents
顯示器保護器 Download PDFInfo
- Publication number
- TWI818583B TWI818583B TW111121538A TW111121538A TWI818583B TW I818583 B TWI818583 B TW I818583B TW 111121538 A TW111121538 A TW 111121538A TW 111121538 A TW111121538 A TW 111121538A TW I818583 B TWI818583 B TW I818583B
- Authority
- TW
- Taiwan
- Prior art keywords
- edge
- adhesive layer
- stress
- layer
- glass
- Prior art date
Abstract
提供一種顯示器保護器，其包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及超薄玻璃（UTG：ultra-thin glass）層，其位於所述第一應力緩和粘著層上，其中，所述第一應力緩和粘著層的儲能模量在-10℃下為約0.03 MPa至約0.2 MPa。
Description
本發明涉及一種顯示器保護器，更具體地，涉及一種顯示器保護器，其不僅應對可折疊終端或可卷曲終端，而且具有優良的折疊可靠性，因此即使在可折疊終端或可卷曲終端上長時間使用也不會剝落，並且在需要時可相對容易地拆卸。
隨著可折疊終端和可卷曲終端的逐漸實用化，對能夠保護可折疊終端和可卷曲終端的顯示區域的顯示器保護器的需求也越來越大。特别是，可折疊終端和可卷曲終端上使用的顯示器保護器必須經受長時間的多次折疊和滾動。因此，需要對這樣的折疊和滾動具有高可靠性的顯示器保護器。
本發明要解决的第一個技術問題是提供一種顯示器保護器，其不僅兼容可折疊終端或可卷曲終端，而且具有優良的折疊可靠性，因此即使在可折疊終端或可卷曲終端上長時間使用也不會剝落，並且在需要時可相對容易地拆卸。
本發明要解决的第二個技術問題是提供一種顯示器保護器附接配套元件，其可用於容易地將具有優異折疊可靠性的顯示器保護器附接於可折疊終端或可卷曲終端上，所述顯示器保護器即使在長時間使用時也不會剝落，並且在需要時可相對容易地拆卸。
為了解决上述的技術問題，本發明提供一種顯示器保護器，其包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及超薄玻璃（UTG：ultra-thin glass）層，其位於所述第一應力緩和粘著層上，其中，所述第一應力緩和粘著層的儲能模量在-20℃下為約0.1 MPa至約0.5 MPa。
在一些實施例中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個可具有約600 gf/in至約1,500 gf/in的粘著力。在一些實施例中，所述第一應力緩和粘著層的儲能模量在+40℃下可為約0.02 MPa至約0.2 MPa。在一些實施例中，所述第二應力緩和粘著層的儲能模量在-10℃下可為約0.03 MPa至約0.2 MPa。在一些實施例中，所述第二應力緩和粘著層的儲能模量在+40℃下可為約0.02 MPa至約0.2 MPa。
在一些實施例中，所述顯示器保護器可進一步包括防散射塗層，其位於所述UTG層上。
在一些實施例中，所述UTG層可具有約30微米（μm）至約70 μm的厚度，並且為經過強化的玻璃，以在折疊為1.0 mm的曲率半徑時不會損壞。在一些實施例中，所述第一應力緩和粘著層的儲能模量可小於或基本等於所述第二應力緩和粘著層的儲能模量。
本發明的另一方面提供一種顯示器保護器，其包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及UTG層；其位於所述第一應力緩和粘著層上，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個相對於所述透明基材層以及對於可折疊或可卷曲顯示器具有約600 gf/in至約1,500 gf/in的粘著力。
在一些實施例中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在-10℃下可為約0.03 MPa至約0.18 MPa。在一些實施例中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在-10℃下可為約0.06 MPa至約0.14 MPa。在一些實施例中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在+40℃下可為約0.02 MPa至約0.18 MPa。在一些實施例中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在+40℃下可為約0.04 MPa至約0.14 MPa。
在一些實施例中，所述UTG層的角部可包括曲率半徑為約0.5 mm至約3 mm的曲線。在一些實施例中，所述超薄玻璃層的厚度可為約30 μm至約70 μm。
本發明的另一方面提供一種顯示器保護器，其包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及UTG層，其位於所述第一應力緩和粘著層上。其中，所述UTG層包括：第一玻璃邊緣和第二玻璃邊緣，其各自在第一方向上延伸並且彼此相對；以及第三玻璃邊緣和第四玻璃邊緣，其各自在垂直於第一方向的第二方向上延伸並且彼此相對。並且，所述透明基材層、所述第一應力緩和粘著層和所述第二應力緩和粘著層包括共同的外邊緣，其中，所述共同的外邊緣包括：第一薄膜邊緣和第二薄膜邊緣，其分别平行於所述第一玻璃邊緣和所述第二玻璃邊緣延伸；以及第三薄膜邊緣和第四薄膜邊緣，其分别對應於所述第三玻璃邊緣和所述第四玻璃邊緣。此外，所述第一薄膜邊緣和所述第二薄膜邊緣分别比所述第一玻璃邊緣和所述第二玻璃邊緣向内偏移（offset）。
根據一些實施例，所述顯示器保護器可被配置為可相對於平行於所述第一玻璃邊緣和所述第二玻璃邊緣的折疊軸折疊。所述第三薄膜邊緣比所述第三玻璃邊緣可至少部分地向外偏移；所述第四薄膜邊緣比所述第四玻璃邊緣可至少部分地向外偏移；或者所述第三薄膜邊緣和所述第四薄膜邊緣分别比所述第三玻璃邊緣和所述第四玻璃邊緣可至少部分地向外偏移。
在一些實施例中，所述第三薄膜邊緣可包括：第一薄膜子邊緣部，其與所述折疊軸相交並比所述第三玻璃邊緣向外偏移；第一角邊緣部，其形成所述第三薄膜邊緣的末端部並與所述第一薄膜邊緣相接；以及第二薄膜子邊緣部，其連接所述第一薄膜子邊緣部與所述第一角邊緣部。此時，所述第一角邊緣部可比所述UTG層的對應角邊緣向内偏移。並且，所述第二薄膜子邊緣部包括比所述第三玻璃邊緣向外偏移的部分，並且所述第二薄膜子邊緣部向外偏移的尺寸可隨著與所述第一角邊緣部的距離减小而逐漸减小。
在一些實施例中，所述第一薄膜子邊緣部可比所述第三玻璃邊緣向外偏移至少20微米（μm），並且所述第二薄膜子邊緣部相對於其80％或更多的長度可比所述第三玻璃邊緣的對應部分向内偏移。
在一些實施例中，所述第一薄膜子邊緣部可在所述折疊軸上比所第三玻璃邊緣向外偏移的尺寸為約50 μm至約400 μm。
為了實現上述第一個技術問題，本發明提供一種顯示器保護器附接配套元件，其包括：所述顯示器保護器；以及粘著溶液，其可提供到所述顯示器保護器的邊緣。此時，所述透明基材層、所述第一應力緩和粘著層和所述第二應力緩和粘著層具有共同的外邊緣，並且所述共同的外邊緣比所述UTG層的邊緣向内偏移。
在一些實施例中，所述粘著溶液的粘度在約20℃至約25℃的溫度下可為約10 cp至約50 cp。
在下文中，將參照附圖詳細描述本發明概念的優選實施例。然而，可以以各種其他形式修改本發明概念的實施例，並且本發明概念的範圍不應被解釋為由以下描述的實施例限制。優選地將本發明概念的實施例解釋為是為了向本領域普通技術人員更完整地解釋本發明概念而提供的。相同的符號不時指代相同的元件。此外，附圖中的各個元件和區域是概略性繪製的。因此，本發明概念不受附圖中所繪出的相對尺寸或間距的限制。
可以使用諸如第一、第二等術语來描述各種組件，但是這些組件不受這些術语的限制。上述術语僅用於將一個組件與另一個組件區分開來。例如，在不脱離本發明概念的範圍的情况下，第一組件可以被稱為第二組件，相反地，第二組件可以被稱為第一組件。
本申請中所使用的術语僅用於描述特定實施例，並不用於限制本發明概念。除非上下文另有明確規定，否則單數表述包括復數表述。在本申請中，諸如“包括”或“具有”等表述旨在表示存在說明書中描述的特徵、數量、步驟、操作、組件、部分或其組合，但應當理解，這並不排除添加或存在一個或多個其他特徵或數量、操作、組件、部分或其組合的可能性。
除非另有定義，本文使用的所有術语具有與本發明概念所屬領域的普通技術人員通常理解的相同的含義，包括技術和科學術语。此外，字典中定義的通常使用的術语應理解為具有與其在相關技術上下文中的含義一致的含義，除非在此明確定義，將理解的是，不應將術语解釋為過於正式的意義。
在某些實施例以其他方式可行的情况下，可以執行與所描述的順序不同的特定工藝順序。例如，連續描述的兩個工藝可以基本上同時執行，或者可以以與描述的順序相反的順序執行。
在附圖中，例如取决於製造技術和/或公差，可以預期所示形狀的變化。因此，本發明的實施例不應被解釋為限於本說明書中所示的區域的特定形狀，而應包括例如由製造過程引起的形狀變化。如本文所用的所有術语“和/或”包括一個或多個所述組件的每一個組合。此外，如在本說明書中使用的術语“基材”可以指基材本身或包括基材和形成在其表面上的預定層或膜的層壓結構。此外，在本說明書中，術语“基材的表面”可以指基材本身所露出的表面，或形成在基材上的預定層或膜的外表面。
第1A圖為概略地示出根據本發明一實施例的顯示器保護器100的層壓結構的示意圖。
參照第1A圖，所述顯示器保護器100包括透明基材層110、分别設置在所述透明基材層110的兩個主表面，即第一表面110a和第二表面11b上的第一應力緩和粘著層120a和第二應力緩和粘著層120b，以及在所述第一應力緩和粘著層120a上的超薄玻璃（UTG：ultra-thin glass）層130。
透明基材層
所述透明基材層110具有第一表面110a和第二表面110b，其為彼此面對的兩個主表面。
所述透明基材層110可包括例如聚氨酯樹脂、聚酯樹脂和/或（甲基）丙烯酸樹脂。
在一些實施例中，所述聚氨酯樹脂可具有約100,000至約3,000,000的重均分子量。
在一些實施例中，所述聚氨酯樹脂可為具有兩個或多個異氰酸酯基(-N＝C＝O)的多官能異氰酸酯化合物與多元醇化合物的聚合產物。
所述多官能異氰酸酯化合物可以是脂肪族、芳香族、脂環族（alicyclic）或芳香脂肪族異氰酸酯化合物。
在所述多官能異氰酸酯化合物中，所述脂肪族異氰酸酯化合物可選自，例如，乙烯二異氰酸酯、三亞甲基二異氰酸酯、四亞甲基二異氰酸酯、六亞甲基二異氰酸酯（HMDI）、亞辛基二異氰酸酯、亞壬基二異氰酸酯、十二亞甲基二異氰酸酯、2,2-二甲基戊烷二異氰酸酯、2,2,4-三甲基六亞甲基二異氰酸酯、十亞甲基二異氰酸酯、丁烯二異氰酸酯、1,3-丁二烯-1,4-二異氰酸酯、2,4,4-三甲基六亞甲基二異氰酸酯、1,6,11-十一烷三異氰酸酯、2,2,4-三甲基六亞甲基二異氰酸酯、賴氨酸二異氰酸酯、2,6-二異氰酸酯正己酸甲酯、雙(2-異氰酸乙酯)富馬酸酯、雙(2-異氰酸乙酯)碳酸鹽、2-異氰酸乙酯-2,6-二異氰酸酯己酸鹽、1,3,5-六亞甲基三異氰酸酯、1,8-二異氰酸酯-4-異氰酸酯、雙（異氰酸酯乙基）醚、1,4-丁二醇二丙醚-ω,ω'-二異氰酸酯、賴氨酸二異氰酸酯甲酯、賴氨酸三異氰酸酯、2-異氰酸酯乙基-2,6-二異氰酸酯乙基-2,6-二異氰酸酯己酸鹽、2-異氰酸酯丙基-2,6-二異氰酸酯己酸鹽、2,6-二（異氰酸酯甲基）呋喃、1,3-雙（6-異氰酸酯己基）尿丁啶-2,4-二酮和1,3,5-三（6-異氰酸酯己基）異氰脲酸酯中的至少一種，但本發明不限於此。
在所述多官能異氰酸酯化合物中，所述芳香族異氰酸酯化合物可為，例如，亞苯基1,4-二異氰酸酯、甲苯基2,4-和/或2,6-二異氰酸酯（TDI）、亞萘基1,5-二異氰酸酯、二苯基甲烷2,2'-和/或2,4'-和/或4,4'-二異氰酸酯（MDI）和/或高级同系物（pMDI），但本發明不限於此。
在所述多官能異氰酸酯化合物中，脂環族異氰酸酯化合物可選自，例如，異佛爾酮二異氰酸酯（IPDI）、4,4'-二環己甲烷二異氰酸酯、環己基二異氰酸酯、甲基亞環己基二異氰酸酯、雙（2-二異氰酸酯）-4-環己烯-1,2-二甲酸、2,5-降冰片烷二異氰酸酯、2,6-降冰片烷二異氰酸酯、2,2-二甲基二環己甲烷二異氰酸酯、雙（4-異氰酸酯-n-亞丁基）季戊四醇、二聚酸二異氰酸酯、2-異氰酸酯甲基-3-（3-異氰酸酯丙基）)-5-異氰酸酯甲基-雙環[2.2.1]-庚烷、2-異氰酸酯甲基-3-(3-異氰酸酯丙基)-6-異氰酸酯甲基-雙環[2.2.1]-庚烷、2-異氰酸酯甲基-2-(3-異氰酸酯丙基)-5-異氰酸酯甲基-雙環[2.2.1]-庚烷、2-異氰酸酯甲基-2-(3-異氰酸酯丙基)-6-異氰酸酯甲基-雙環[2.2.1]-庚烷、2-異氰酸酯甲基-3-(3-異氰酸酯丙基)-6-(2-異氰酸酯乙基)-雙環[2.2.1]-庚烷、2-異氰酸酯甲基-3-(3-異氰酸酯丙基)-6-(2-異氰酸酯乙基)-雙環[2.1.1]-庚烷、2-異氰酸酯甲基-2-(3-異氰酸酯丙基)-5-異氰酸酯乙基)-雙環[2.1.1]-庚烷、2-異氰酸酯甲基-2-(3-異氰酸酯丙基)-6-(2-異氰酸酯乙基)-雙環[2.2.1]-庚烷和降冰片烷雙（異氰酸酯甲基）中的至少一種，但本發明不限於此。
在所述多官能異氰酸酯化合物中，所述芳香脂肪族異氰酸酯化合物可為，例如，1,3-雙（異氰酸酯甲基）苯（m-二甲苯酯二異氰酸酯，m-XDI）、1,4-雙（異氰酸酯甲基）苯（p-二甲苯酯二異氰酸酯，p-XDI）、1,3-雙（2-異氰酸酯丙-2-基）苯（m-四甲基二甲苯酯二異氰酸酯，m-TMXDI）、1,3-雙（異氰酸酯甲基）-4-甲苯、1,3-雙（異氰酸酯甲基）-4-乙苯、1,3-雙（異氰酸酯甲基）-5-甲苯、1,3-雙（異氰酸酯甲基）-4,5-二甲苯、1,4-雙（異氰酸酯甲基）-2,5-二甲苯、1,4-雙（異氰酸酯甲基）-2,3,5,6-四甲基苯、1,3-雙（異氰酸酯甲基）-5-叔-丁基苯、1,3-雙（異氰酸酯甲基）-4-氯苯、1,3-雙（異氰酸酯甲基）-4,5-二氯苯、1,3-雙（異氰酸酯甲基）-2,4,5,6-四氯苯、1,4-雙（異氰酸酯甲基）-2,3,5,6-四氯苯、1,4-雙（異氰酸酯甲基）-2,3,5,6-四溴苯、1,4-雙（2-異氰酸酯甲基）苯、1,4-雙（異氰酸酯甲基）萘、苯二甲基二異氰酸酯、雙（二異氰酸酯）苯、雙（二異氰酸酯丙基）苯、α,α,α',α'-四甲基苯二甲基二異氰酸酯、雙（二異氰酸酯丁基）苯、雙（二異氰酸酯丙基）萘、雙（二異氰酸酯甲基）二苯醚和雙（二異氰酸酯乙基）鄰苯二甲酸酯，但本發明不限於此。
所述多元醇化合物可為，例如，乙二朜、二甘醇、1,2-丙二醇、1,3-丁二醇、1,4-丁二醇、1,5-戊二醇、1,6-己二醇、1,9-壬二醇、1,10-癸二醇、2,2-二甲基-1,3-丙二醇、1,3-丙二醇、2-甲基-1,3-丙二醇、2,2-二甲基-1,3-丙二醇、3-甲基-1,5-戊二醇、新戊二醇、2-甲基-1,8-辛二醇、二丙二醇等，但本發明不限於此。
在一些實施例中，所述聚酯樹脂可具有約100,000至約3,000,000的重均分子量。
所述聚酯樹脂是具有酯鍵的聚合物，主要是多元羧酸與多元醇的縮聚物。對於所使用的多元羧酸，主要使用二價二羧酸，例如，包括間苯二甲酸、對苯二甲酸、對苯二甲酸二甲酯、萘二甲酸二甲酯等。另外，對於所使用的多元醇，主要使用二元醇，上面已經對其進行了說明，在此不再贅述。
所述聚酯樹脂的具體實例可包括聚對苯二甲酸乙二醇酯、聚對苯二甲酸丁二醇酯、聚萘二甲酸乙二酯、聚萘二甲酸丁二醇酯、聚對苯二甲酸丙二醇酯、聚萘二甲酸丙二醇酯、聚環己烷二甲酯和聚環己烷萘甲酸酯等。也可以優選使用上述實例的共混樹脂或共聚物。
在一些實施例中，所述(甲基)丙烯酸樹脂可具有約100,000至約3,000,000的重均分子量。
所述(甲基)丙烯酸樹脂可以是(甲基)丙烯酸酯單體和/或(甲基)丙烯酸酯低聚物的聚合產物。
所述(甲基)丙烯酸酯單體可以是例如多官能(甲基)丙烯酸酯化合物。術语“多官能（甲基）丙烯酸酯化合物”可表示具有兩個或更多個聚合性官能團的（甲基）丙烯酸酯化合物。
具體地，所述多官能（甲基）丙烯酸酯可為雙官能丙烯酸酯化合物，例如乙二醇二（甲基）丙烯酸酯、二乙二醇二（甲基）丙烯酸酯、丁二醇（甲基）丙烯酸酯、己二醇二（甲基）丙烯酸、壬二醇二（甲基）丙烯酸、乙氧基化己二醇二（甲基）丙烯酸酯、丙氧基化己二醇二（甲基）丙烯酸酯、二（甲基）丙烯酸酯、二乙二醇二（甲基）丙烯酸酯、聚乙二醇二（甲基）丙烯酸酯、三丙二醇二（甲基）丙烯酸酯，聚丙二醇二（甲基）丙烯酸酯，丙烯酸新戊二醇二（甲基）丙烯酸酯、環氧化新戊二醇二（甲基）丙烯酸酯、三丙二醇二（甲基）丙烯酸酯、聚丙二醇二（甲基）丙烯酸酯、新戊二醇二（甲基）丙烯酸酯、乙氧基化新戊二醇二（甲基）丙烯酸酯、三丙二醇二（甲基）丙烯酸酯、羥基新戊酸新戊二醇二（甲基）丙烯酸酯等，可為三官能丙烯酸酯化合物，例如三羥甲基丙烷三（甲基）丙烯酸酯、乙氧基化三羥甲基丙烷三（甲基）丙烯酸酯、丙氧基化三羥甲基丙烷三（甲基）丙烯酸酯、三2-羥乙基異氰脲酸酯三（甲基）丙烯酸酯或甘油三（甲基）丙烯酸酯、季戊四醇三（甲基）丙烯酸酯、二季戊四醇三（甲基）丙烯酸酯或雙三羥甲基丙烷三（甲基）丙烯酸酯等，或可為多於三官能的多官能丙烯酸酯化合物，例如季戊四醇四（甲基）丙烯酸酯、雙三羥甲基丙烷四（甲基）丙烯酸酯、二季戊四醇四（甲基）丙烯酸酯、二季戊四醇五（甲基）丙烯酸酯、雙三羥甲基丙烷五（甲基）丙烯酸酯、二季戊四醇六（甲基）丙烯酸酯或雙三羥甲基丙烷六（甲基）丙烯酸酯等，但本發明不限於此。
所述（甲基）丙烯酸酯低聚物可以是，例如，環氧（甲基）丙烯酸酯、氨基甲酸酯（甲基）丙烯酸酯、聚酯（甲基）丙烯酸酯、聚丁二烯（甲基）丙烯酸酯、有機矽（甲基）丙烯酸酯或(甲基)丙烯酸烷基酯等，但本發明不限於此。在一些實施例中，作為所述（甲基）丙烯酸酯低聚物，可使用氨基甲酸酯丙烯酸酯作為主材料來製造所述（甲基）丙烯酸酯樹脂。
在一些實施例中，作為所述透明基材層110，可選择並使用由Jaewon產业（Jaewon Industry）市售的JWR-6、JWR-AEF-01和JWR-AEF-02膜產品中的一種。
所述透明基材層110可具有約10 μm至約40 μm、約12 μm至約35 μm、約14 μm至約30 μm、約15 μm至約25 μm或這些值之間的任何範圍的厚度。所述顯示器保護器100可在所述透明基材層110具有約15 μm至約25 μm的厚度時獲得更好的可折疊性。
當所述透明基材層110的厚度脱離上述範圍並且太薄時，機械強度可能不足，並且當UTG層損壞時，防止玻璃飛散的效果可能不足。相反，所述透明基材層110的厚度脱離上述範圍並且過厚時，在折疊所述顯示器保護器100時，剪切應力可能過度集中在折疊部分，並且當重復折疊和展開時，容易出現翹起的現象。
在一些實施例中，所述透明基材層110在-20℃下可具有約2 GPa至約6 GPa的儲能彈性模量。在一些實施例中，所述透明基材層110在-20℃下可具有約2 GPa至約6 Gpa、約2.2 GPa至約5.8 Gpa、約2.4 GPa至約5.6 Gpa、約2.6 GPa至約5.4 GPa、約2.8 GPa至約5.2 GPa、約3 GPa至約5 Gpa，或這些值之間的任何範圍的儲能彈性模量。在下文中，“儲能彈性模量（storage elastic modulus）”和“儲能模量”具有相同的含義並且與儲能彈性率具有相同的含義。
當所述透明基材層110的儲能彈性模量在上述範圍之外且太小，則所述顯示器保護器100的恢復力可能不足，並且當所述透明基材層110的儲能彈性模量在上述範圍之外且太大，則所述顯示器保護器100的折疊特性可能會變差。
在一些實施例中，所述透明基材層110可具有約30%至約250%的延伸率（elongation）。在一些實施例中，所述透明基材層110可具有約30%至約250%、約40%至約230%、約50%至約200%、約60%至約190%、約70%至約180%、約80%至約170%、約90%至約160%、約100%至約150%，或這些值之間的任何範圍的延伸率。當所述透明基材層110的延伸率過低，則所述顯示器保護器100的恢復力可能不足，並且當所述透明基材層110的延伸率過高，則所述顯示器保護器100的折疊特性可能會變差。
第一應力緩和粘著層和第二應力緩和粘著層
所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地包括丙烯酸聚合物或聚矽氧烷化合物。
所述丙烯酸聚合物可以是例如（甲基）烯酸單體的聚合產物。
具體地，所述（甲基）烯酸單體可為單功能單體，例如正丁基（甲基）丙烯酸酯、2-丁基（甲基）丙烯酸酯、叔丁基（甲基）丙烯酸酯、異丁基（甲基）丙烯酸酯、己基（甲基）丙烯酸酯、環己基（甲基）丙烯酸酯、N-乙烯基吡咯烷酮、2-乙基己基（甲基）丙烯酸酯、乙基（甲基）丙烯酸酯、甲基（甲基）丙烯酸酯、正丙基（甲基）丙烯酸酯、異丙基（甲基）丙烯酸酯、戊基（甲基）丙烯酸酯、正辛基（甲基）丙烯酸酯、異辛基（甲基）丙烯酸酯、2-甲基丁基（甲基）丙烯酸酯、正壬基（甲基）丙烯酸酯、異壬基（甲基）丙烯酸酯、異戊基（甲基）丙烯酸酯、正癸基（甲基）丙烯酸酯、異癸基（甲基）丙烯酸酯、亞冰片基（甲基）丙烯酸酯、4-甲基-2-戊基（甲基）丙烯酸酯、十二烷基（甲基）丙烯酸酯、2-十二烷基硫代乙基（甲基）丙烯酸酯、月桂基（甲基）丙烯酸酯、2-乙氧基乙基（甲基）丙烯酸酯、2-甲氧基乙基（甲基）丙烯酸酯、羥乙基丙基（甲基）丙烯酸酯、羥丁基（甲基）丙烯酸酯、烯丙基（甲基）丙烯酸酯、十八烷基（甲基）丙烯酸酯、苯氧基乙酯（甲基）丙烯酸酯、四糠基（甲基）丙烯酸酯、四氫糠基（甲基）丙烯酸酯和丙烯酰嗎啉等；雙官能單體，例如1,3-丁二醇二（甲基）丙烯酸酯、1,4-丁二醇二（甲基）丙烯酸酯、1,6-己二醇二（甲基）丙烯酸酯、2-丁基-2-乙基-1,3-丙二醇二乙酸酯、1,9-壬二醇二丙烯酸酯、乙二醇二（甲基）丙烯酸酯、雙酚A-乙二醇二丙烯酸酯、二甘醇二（甲基）丙烯酸酯、三乙二醇二（甲基）丙烯酸酯、四乙二醇二（甲基）丙烯酸酯、丙二醇二（甲基）丙烯酸酯、二丙二醇二（甲基）丙烯酸酯、三丙二醇二（甲基）丙烯酸酯、新戊二醇二（甲基）丙烯酸酯、二環戊基二（甲基）丙烯酸酯、己内酯改性的二環戊烯基（甲基）丙烯酸酯、環氧乙烷改性的磷酸二（甲基）丙烯酸酯、雙（2-羥乙基）異氰脲酸酯二（甲基）丙烯酸酯、二(丙烯酰氧基乙基)異氰脲酸酯、烯丙基化環己基二（甲基）丙烯酸酯、二羥甲基二環戊烷二丙烯酸酯、環氧乙烷改性的六氫鄰苯二甲酸二丙烯酸酯、三環癸烷二甲醇丙烯酸酯、新戊二醇改性的三羥甲基丙烷二丙烯酸酯和金刚烷二丙烯酸酯等；三官能單體，例如三羥甲基丙烷三（甲基）丙烯酸酯、季戊四醇三（甲基）丙烯酸酯、二季戊四醇三（甲基）丙烯酸酯、丙酸改性的三羥甲基丙烷三（甲基）丙烯酸酯、環氧丙烷改性的三羥甲基丙烷三（甲基）丙烯酸酯、三（2-羥乙基）異氰脲酸酯三（甲基）丙烯酸酯、三（丙烯酰氧基乙基）異氰脲酸酯和甘油三（甲基）丙烯酸酯等；四官能單體，例如雙甘油四（甲基）丙烯酸酯、季戊四醇四（甲基）丙烯酸酯、雙三羥甲基丙烷四（甲基）丙烯酸酯和四羥甲基丙烷四(甲基)丙烯酸酯等；五官能單體，例如二季戊四醇五（甲基）丙烯酸酯和丙酸改性的二季戊四醇五（甲基）丙烯酸酯等；六官能單體，例如二季戊四醇六（甲基）丙烯酸酯和己内酯改性的二季戊四醇六(甲基)丙烯酸酯等，但本發明不限於此。
所述（甲基）丙烯酸單體可以與共聚單體一起聚合。在一些實施例中，所述共聚單體可包括烷基（甲基）丙烯酸酯單體、具有環氧乙烷的單體、具有環氧丙烷的單體、具有胺基的單體、具有酰胺基的單體、具有烷氧基的單體、具有磷酸基的單體、具有磺酸基的單體、具有苯基的單體和具有矽烷基的單體中的至少一種，但不限於此。
在一些實施例中，所述（甲基）丙烯酸酯單體可包括例如具有1至20個碳原子的未取代的線性或支化烷基（甲基）丙烯酸酯。例如，所述（甲基）丙烯酸酯單體可包括甲基（甲基）丙烯酸酯、乙基（甲基）丙烯酸酯、丙基（甲基）丙烯酸酯、正丁基（甲基）丙烯酸酯、叔丁基（甲基）丙烯酸酯、異丁基（甲基）丙烯酸酯、戊基（甲基）丙烯酸酯、己基（甲基）丙烯酸酯、庚基（甲基）丙烯酸酯、乙基己基（甲基）丙烯酸酯、辛基（甲基）丙烯酸酯、異辛基（甲基）丙烯酸酯、壬基（甲基）丙烯酸酯、癸基（甲基）丙烯酸酯、月桂基（甲基）丙烯酸酯和異冰片基（甲基）丙烯酸酯中的至少一種。具體地，通過使用具有4至8個碳原子的烷基（甲基）丙烯酸酯單體作為共聚單體，可以進一步具有提高初始粘著力的效果。
在一些實施例中，所述具有環氧乙烷的單體可包括例如一種或多種含有環氧乙烷基團(-CH2CH2O-)的（甲基）丙烯酸酯單體。例如，所述具有環氧乙烷的單體可以是聚環氧乙烷烷基醚（甲基）丙烯酸酯，例如聚環氧乙烷單甲醚（甲基）丙烯酸酯、聚環氧乙烷單乙醚（甲基）丙烯酸酯、聚環氧乙烷單丙醚（甲基）丙烯酸酯、聚環氧乙烷單丁醚（甲基）丙烯酸酯、聚環氧乙烷單戊醚（甲基）丙烯酸酯、聚環氧乙烷二甲醚（甲基）丙烯酸酯、聚環氧乙烷二乙醚（甲基）丙烯酸酯、聚環氧乙烷單異丙醚（甲基）丙烯酸酯、聚環氧乙烷單異丁醚（甲基）丙烯酸酯、聚環氧乙烷單叔丁基醚（甲基）丙烯酸酯等，但不限於此。
在一些實施例中，所述具有環氧丙烷的單體可以是例如聚環氧丙烷烷基醚（甲基）丙烯酸酯，例如聚環氧丙烷單甲醚（甲基）丙烯酸酯、聚環氧丙烷單乙醚（甲基）丙烯酸酯、聚環氧丙烷單丙醚（甲基）丙烯酸酯、聚環氧丙烷單丁醚（甲基）丙烯酸酯、聚環氧丙烷單戊醚（甲基）丙烯酸酯、聚環氧丙烷二甲醚（甲基）丙烯酸酯、聚環氧丙烷二乙醚（甲基）丙烯酸酯、聚環氧丙烷單異丙醚（甲基）丙烯酸酯、聚環氧丙烷單異丁基醚（甲基）丙烯酸酯和聚環氧丙烷單叔丁基醚（甲基）丙烯酸酯等，但不限於此。
在一些實施例中，所述具有氨基的單體可以是例如含有氨基的（甲基）丙烯酸單體，例如單甲氨基乙基（甲基）丙烯酸酯、單乙氨基乙基（甲基）丙烯酸酯、單甲氨基丙基（甲基）丙烯酸酯、單乙氨基丙基（甲基）丙烯酸酯、二甲氨基乙基（甲基）丙烯酸酯、二乙氨基乙基（甲基）丙烯酸酯、N-叔丁基氨基乙基（甲基）丙烯酸酯和甲基丙烯酰氧乙基三甲基氯化銨（甲基）丙烯酸酯等，但不限於此。
在一些實施例中，具有酰胺基單體可以是例如含有酰胺基的（甲基）丙烯酸單體，例如（甲基）丙烯酰胺、N-甲基丙烯酰胺、N-甲氧基甲基(甲基)丙烯酰胺、N,N-亞甲基雙(甲基)丙烯酰胺和2-羥乙基丙烯酰胺等，但不限於此。
在一些實施例中，所述具有烷氧基的單體可以是例如2-甲氧基乙基（甲基）丙烯酸酯,、2-甲氧基丙基（甲基）丙烯酸酯、2-乙氧基丙基（甲基）丙烯酸酯、2-丁氧基丙基（甲基）丙烯酸酯2-甲氧基戊基（甲基）丙烯酸酯、2-乙氧基戊基（甲基）丙烯酸酯、2-丁氧基己基（甲基）丙烯酸酯、3-甲氧基戊基（甲基）丙烯酸酯、3-乙氧基戊基（甲基）丙烯酸酯、3-丁氧基己基（甲基）丙烯酸酯，但不限於此。
在一些實施例中，所述具有磷酸基單體可以是例如具有磷酸基丙烯酸單體，例如2-甲基丙烯酰氧基乙基二苯基磷酸酯（甲基）丙烯酸酯、三甲基丙烯酰氧基乙基磷酸酯（甲基）丙烯酸酯和三丙烯酰羥乙基磷酸酯（甲基）丙烯酸酯等，但不限於此。
在一些實施例中，所述具有磺酸基的單體可以是例如具有磺酸基的丙烯酸單體，例如磺丙基(甲基)丙烯酸鈉、2-磺乙基(甲基)丙烯酸鈉、和2-丙烯酰胺基-2-甲基丙烷磺酸鈉等，但不限於此。
在一些實施例中，所述具有苯基的單體可以是例如具有苯基的丙烯酸乙烯基單體，例如對叔丁基苯基（甲基）丙烯酸酯和鄰聯苯基（甲基）丙烯酸酯等，但不限於此。
在一些實施例中，所述具有矽烷基的單體可以是例如具有矽烷基的乙烯基單體，例如2-乙酰乙酸（甲基）丙烯酸酯乙二醇酯、乙烯基三甲氧基矽烷、乙烯基三乙氧基矽烷、乙烯基三（β-甲氧基乙基）矽烷、乙烯基三乙酰基矽烷和甲基丙烯酰氧基丙基三甲氧基矽烷等，但不限於此。
所述共聚單體可以按單體混合物的重量計包括約60%至約95%，例如約70%至約90%。在上述範圍内，所述第一應力緩和粘著層120a和第二應力緩和粘著層120b可以獲得優異的粘著力和應力分散效果。
所述丙烯酸聚合物可具有約100,000至約3,000,000的重均分子量。
所述聚矽氧烷化合物可以是例如下式1的聚矽氧烷化合物。
＜化學式1＞
（其中，n為100至10,000的整數，R1至R8各自獨立地為氫、鹵素、腈基、硝基、羥基、氨基、具有1至10個碳原子的取代或未取代的烷基、具有1至10個碳原子的取代或未取代的烷氧基、具有2至10個碳原子的取代或未取代的烯基，具有2至10個碳原子的取代或未取代的炔基，具有2至10個碳原子的取代或未取代的亞烷基，具有3至15個碳原子的取代或未取代的環烷基、具有6至15個碳原子的取代或未取代的芳基、具有6至15個碳原子的取代或未取代的芳氧基、具有7至15個碳原子的取代或未取代的芳烷基，或具有7至15個碳原子的取代或未取代的烷芳基。）
這裡，“取代”是指與化合物或官能團的碳原子鍵合的氫原子變成另一個取代基，被取代的位置是氫原子被取代的位置，並且没有特别限制，只要它是可被取代基取代的位置即可。此外，當兩個或多個取代基被取代時，兩個或多個取代基可以彼此相同或不同。
在此，“取代或未取代”是指被選自氘；鹵素；腈基（-CN）；硝基；羥基；氨基；甲矽烷基；硼基；烷氧基；芳氧基；烷基；環烷基；芳基；和杂環基中的一個或兩個或多個取代基取代、被其中上述取代基中的兩個或多個取代基相連的取代基取代、或不具有任何取代基。例如，“其中兩個或多個取代基相連的取代基”可以是聯苯基。即，聯苯基可以是芳基或可以解釋為其中兩個苯基連接的取代基。
所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地具有約10 μm至約40 μm、約11 μm至約38 μm、約12 μm至約36 μm、約13 μm至約34 μm、約14 μm至約32 μm、約15 μm至約30 μm，或這些值之間的任何範圍的厚度。所述顯示器保護器100可在所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b具有約15 μm 的厚度時獲得最佳的可折疊性。
當所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的厚度脱離上述範圍並且太薄時，緩和應力的效果可能不充分，並且可能發生剝離（翹起）。相反，當所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的厚度脱離上述範圍並且太厚時，可以承受折疊的應力，但是在應力緩和粘著層的兩個表面上產生的應力變得過度不平衡，並且可能發生折疊部分的剝離（翹起）。
在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地在-20℃下具有約0.1 MPa至約0.5 MPa的儲能模量。在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地在-20℃下具有約0.1 MPa至約0.5 MPa、約0.12 MPa至約0.48 MPa、約0.14 MPa至約0.46 MPa、約0.16 MPa至約0.44 MPa、約0.18 MPa至約0.42 MPa、約0.2 MPa至約0.4 MPa、約0.25 MPa至約0.35 MPa，或這些值之間的任何範圍的儲能模量。
所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地在-10℃下具有約0.03 MPa至約0.2 MPa的儲能彈性模量。在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立在-10℃下具有約0.03 MPa至約0.20 MPa、約0.04 MPa至約0.18 MPa、約0.05 MPa至約0.16 MPa、約0.06 MPa至約0.14 MPa、約0.07 MPa至約0.12 MPa、約0.08 MPa至約0.11 MPa、約0.08 MPa至約0.10 Mpa、約0.08 MPa至約0.15 MPa、約0.1 MPa至約0.15 MPa，或這些值之間的任何範圍的儲能彈性模量。
而且，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立在+40℃下具有約0.02 MPa至約0.2 MPa的儲能模量。在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立在+40℃下具有約0.02 MPa至約0.20 MPa、約0.03 MPa至約0.18 MPa、約0.04 MPa至約0.16 MPa、約0.05 MPa至約0.14 MPa、約0.06 MPa至約0.13 MPa、約0.07 MPa至約0.12 MPa、約0.08 MPa至約0.11 MPa、約0.09 MPa 至約0.10 Mpa、約0.05 MPa至約0.15 MPa、更優選地約0.05 MPa至約0.10 MPa，或這些值之間的任何範圍的儲能模量。
當所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的儲能模量脱離上述範圍並且太小時，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b的物理特性可能過於柔軟，使其難以製造，並且在折疊過程中可能由於粘著力的降低而發生剝離（翹起）。
相反，當所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的儲能模量脱離上述範圍並且太大時，相對於顯示器保護器100的變形，緩和所述顯示器保護器100中產生的剪切應力的效果不充分。
在一些實施例中，所述第一應力緩和粘著層120a的儲能模量可小於或基本等於所述第二應力緩和粘著層120b的儲能模量。在此，“基本等於”是指基於兩個值中較大的一個值，兩個值之間的差異在+/-10%以内。在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可具有基本相同的儲能彈性模量。
在另一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可具有彼此不同的儲能彈性模量。
在實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地在約20℃至約25℃的溫度下具有約600 gf/in至約1,500 gf/in的粘著力。在一些實施例中，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b可各自獨立地具有約600 gf/in至約1,500 gf/in、約650 gf/in至約1,450 gf/in、約700 gf/in至約1,400 gf/in、約750 gf/in 至約1,350 gf/in，約800 gf/in至約1,300 gf/in，約850 gf/in至約1,250 gf/in，約900 gf/in至約1,200 gf/in，約950 gf/in至約1,150 gf/in、約1,000 gf/in至約1,110 gf/in或這些值之間的任何範圍的粘著力。
當所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的粘著力脱離上述範圍並且太小時，粘合力強度不足，難以保持與所述顯示器保護器的附接。
相反，所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b中的每一個的粘著力脱離上述範圍並且太大時，當需要更换顯示器保護器100時，難以從附接的電子設備上剝離，並且在剝離過程中存在損壞電子設備顯示器的風險。
UTG層
所述UTG層可以是由具有約25微米(μm)至約70 μm的厚度的強化玻璃材料形成的層。在一些實施例中，所述UTG層130可具有約25 μm 至約70 μm、約30 μm至約70 μm、約32 μm至約70 μm、約34 μm至約65 μm、約36 μm至約60 μm、約38 μm至約55 μm、約40 μm至約50 μm、約25 μm至約65 μm、約25 μm至約60 μm、約25 μm至約55 μm、約25 μm至約50 μm，或這些值之間的任何範圍的厚度。
當所述UTG層130的厚度脱離上述範圍並且太薄時，抗衝擊性可能不足。當所述UTG層130的厚度脱離上述範圍並且厚時，所述UTG層130容易被反復折疊（folding）或滾動（rolling）損壞，並且在折疊時排斥力變強。特别地，在一些情况下，但所述UTG層130的厚度超過50 μm 時，可過度地產生排斥力。
所述UTG層130可包括例如鋁矽酸鹽、碱鋁矽酸鹽、硼矽酸鹽、碱硼矽酸鹽、铝硼矽酸鹽、碱铝硼矽酸鹽、鈉钙或其他合適的玻璃，但不限於此。在一些實施例中，所述UTG層130可從由NEG公司、Corning公司（Corning Inc.）和Schott公司等市售的母玻璃（mother glass）中獲得。
通過應用减薄（Slimming）工藝、單元形切割工藝、玻璃強化工藝、防指紋（Anti-fingerprint：AF）工藝等將所述母玻璃形成為UTG層130。此外，還可以應用防碎塗層工藝。
第1B圖為概略地示出根據本發明另一實施例的顯示器保護器100a的層壓結構的示意圖。所述顯示器保護器100a與參照第1A圖描述的顯示器保護器100基本相同，除了進一步包括防散射塗層140之外。因此，下面將主要描述其不同之處，其餘的不再詳細描述。
參照第1B圖，所述顯示器保護器100a還包括位於UTG層130上的防散射塗層140。盡管在第1B圖中示出了在所述UTG層130的上表面上提供防散射塗層140的示例，但所述防散射塗層140也可以被提供於所述UTG層130的下表面上。在另一實施例中，所述防散射塗層140可提供於所述UTG層130的上表面和下表面上。
所述防散射塗層140是紫外線（UV：ultraviolet）固化樹脂，並且可具有約5 μm至約30 μm的厚度。
所述UV固化樹脂包括通過由光引發劑引發的單體和/或低聚物的聚合而生成的產物。所述光引發劑可用於通過UV照射引發所述單體和/或低聚物的聚合。
作為所述單體，例如，可以使用環氧單體、乙烯基醚、環狀醚、丙烯酸單體等。所述低聚物可以是（甲基）丙烯酸酯低聚物、聚酯（甲基）丙烯酸酯低聚物、丙烯酸（甲基）丙烯酸酯低聚物、聚氨酯（甲基）丙烯酸酯低聚物、環氧丙烯酸酯低聚物和有機矽丙烯酸酯低聚物等，但不限於此。
作為所述光引發劑，可以使用，例如安息香基、羥基酮基、氨基酮基或氧化膦基的光引發劑。具體地，所述光引發劑可包括安息香、安息香甲醚、安息香乙醚、安息香異丙醚、安息香正丁醚、安息香異丁醚、苯乙酮、二甲氨基苯乙酮、2,2-二甲氧基-2-苯基苯乙酮、2,2-二乙氧基-2-苯基苯乙酮、2-羥基-2-甲基-1-苯基丙-1-酮、1-羥基環己基苯基酮、2-甲基-1-[4-(甲硫基)苯基]-2-嗎啉-丙-1-酮、4-(2-羥基乙氧基)苯基-2-(羥基-2-丙基)酮、二苯甲酮、對苯基二苯甲酮、4,4-非環二乙氨基二苯甲酮、二氯二苯甲酮、2-甲基蒽醌、2-乙基蒽醌、2-叔丁基蒽醌、2-氨基蒽醌、2-甲基噻吨酮（thioxanthone）、2-乙基噻吨酮、2-氯噻吨酮、2,4-二甲基噻吨酮、2,4-二乙基噻吨酮、苄基二甲基縮酮、苯乙酮二甲基縮酮、對二甲氨基苯甲酸酯、低聚[2-羥基-2-甲基-1-[4-(1-甲基乙烯基)苯基]丙酮和2,4,6-三甲基苯甲酰基-二苯基-氧化膦等。在本申請中，可以使用上述中的一種或多種，但不限於此。
所述UV固化樹脂可以是在約20℃至約25℃的溫度下具有約100 cps至約8,000 cps的粘度的流體，並且可以通過例如旋塗或刮刀等方法塗覆。此後，可以通過照射UV固化來形成所述防散射塗層140。
第2A圖為示出根據本發明一實施例的顯示器保護器100附接到可折疊顯示裝置1的狀態的透視圖。
參照第2A圖,可折疊顯示裝置1可以包括顯示面板10和下蓋90。下蓋90可包括支撑顯示面板10的第一部分90_1和第二部分90_2。下蓋90可以以第一部分90_1和第二部分90_2之間的折疊軸FAX作中心來折疊。在一實施例中，在第一部分90_1和第二部分90_2之間可包括鉸鏈部90H。此外，在一實施例中，第二部分90_2可包括透光物質。
所述顯示器保護器100可設置為覆蓋顯示面板10的至少一部分。
當所述可折疊顯示裝置1以折疊軸FAX作中心來折疊時，所述顯示器保護器100也一起被折疊。此時，所述顯示器保護器100的折疊部分具有約0.5 mm至約1.3 mm的曲率半徑。因此，所述顯示器保護器100的UTG層130（參照第1A圖）可以是經強化的玻璃，從而即使曲率半徑為0.5 mm、0.6 mm、0.7 mm、0.8 mm、0.9 mm、1.0 mm、1.2 mm和1.3 mm也不會損壞。
在一些實施例中，可進一步在所述UTG層130（參照第1A圖）的表面上提供AF塗層。
第2B圖為示出根據本發明一實施例的顯示器保護器100附接到可卷曲顯示裝置2的狀態的透視圖。
參照第2B圖，可卷曲顯示裝置2可包括顯示面板10、滾輪單元20、外殼部30、模塊部BP和間距調節單元L。
顯示面板10可以是柔性的並且可以容易地彎曲、折疊或卷曲的柔性（flexible）顯示面板。具體地，顯示面板10可以是可卷起或展開的可卷曲（rollable）顯示面板。
顯示面板10可以被滾輪單元20卷起或展開。例如，當顯示面板10在滾輪單元20上滾動時，顯示面板10可以在顯示面板10的第一方向（例如，+x方向或-x方向）上被外殼部30暴露第一間距。當顯示面板10在滾輪單元20上展開時，顯示面板10可以在顯示面板10的第一方向例如，+x方向或-x方向）上被外殼部30暴露大於所述第一間距的第二間距。因此，通過被外殼部30暴露可以改變用户認知的顯示面板10的尺寸。
滾輪單元20可滾動（roll）顯示面板10。或者，滾輪單元20可展開（unroll）顯示面板10。在一些實施例中，滾輪單元20可連接到驅動單元。此時，驅動單元可包括馬達等，並且可旋转滾輪單元20。或者，滾輪單元20可手動卷起或展開顯示面板10。
在一實施例中，滾輪單元20可包括第一滾輪單元20A和第二滾輪單元20B。第一滾輪單元20A和第二滾輪單元20B可設置為在第一方向（例如，+x方向或-x方向）上彼此間隔開。在一些實施例中，可省略第一滾輪單元20A和第二滾輪單元20B中的一個。
外殼部30可容納滾輪單元20。因此，顯示面板10中的一部分可容納在外殼部30中。顯示面板10中的一部分可被帶入外殼部30中，或可從外殼部30中取出。外殼部30可包括彎曲部。因此，用户可容易地抓握外殼部30。
在一施例中，外殼部30可包括第一外殼部30A和第二外殼部30B。第一外殼部30A和第二外殼部30B可設置為在第一方向（例如，+x方向或-x方向）上彼此間隔開。在一些實施例中，可省略第一外殼部30A和第二外殼部30B中的一個。第一外殼部30A可容納第一滾輪單元20A。第二外殼部30B可容納第二滾輪單元20B。
所述顯示器保護器100可設置為覆蓋顯示面板10的至少一部分。特别地，當所述顯示面板10被卷起時，所述顯示器保護器100可以與所述顯示面板10一起被卷起。
當所述可卷曲顯示裝置2以折疊軸FAX作中心來折疊時，所述顯示器保護器100也一起被折疊。此時，所述 顯示器保護器100的折疊部分具有約0.5 mm至約1.3 mm的曲率半徑。因此，所述顯示器保護器100的UTG層130（參照第1A圖）可以是經強化的玻璃，從而即使曲率半徑為0.5 mm、0.6 mm、0.7 mm、0.8 mm、0.9 mm、1.0 mm、1.2 mm和1.3 mm也不會損壞。
在一些實施例中，還可以在所述顯示器保護器100的表面上，具體地，在所述UTG層130（參照第1A圖）的表面上提供AF塗層。
以下將結合具體實施例和比較例對本發明的構成和效果進行更詳細的描述，但這些實施例僅用於清楚地理解本發明，並不用於限制本發明的範圍。
＜折疊可靠性測試＞
在將根據每個配方製造的顯示器保護器附接到可折疊終端之後，執行在室溫（約20℃至約25℃）下重復折疊和展開的測試。
根據下表1中所示的程序進行所述測試。即，第一輪到第四輪依次進行，每一輪從步驟A到步驟D依次進行。表1中的每個數字都是重復折疊和展開的次數，“OUT狀態”表示展開狀態，“IN狀態”表示折疊狀態。
在進行了所有第一輪到第四輪之後，完全没有翹起的情况用◎表示，翹起的尺寸小於10 mm的情况用○表示，翹起的尺寸等於或大於10 mm的情况用X表示。
＜表1＞
| A步驟 | B步驟 | C步驟 | D步驟 | |
| 第1輪 | 粘附後立即350次 | 粘附後以OUT狀態放置5分鐘後30次 | 粘附後以IN狀態放置5分鐘後30次 | 粘附後以IN狀態在0℃下放置5分鐘後30次 |
| 第2輪 | 粘附後立即300次 | 粘附後以OUT狀態放置10分鐘後60次 | 粘附後以IN狀態放置10分鐘後60次 | 粘附後以IN狀態在-5℃下放置10分鐘後60次 |
| 第3輪 | 粘附後立即600次 | 粘附後以OUT狀態放置10分鐘後300次 | 粘附後以IN狀態放置10分鐘後300次 | 粘附後以IN狀態在-10℃下放置X分鐘後300次 |
| 第4輪 | 粘附後立即8000次 |
＜應力緩和粘著層測試＞
通過使用具有12 μm厚度的聚氨酯薄膜作為基材並改變第一和第二應力緩和粘著層中的每一個的厚度和粘著力來進行所述折疊可靠性測試。結果，獲得了下表2中所示的結果。
＜表2＞
| 粘著力（g f/in） | 應力緩和粘著層的厚度（㎛） | 評估結果 | |
| 比較例1 | 400 | 25 | X |
| 比較例2 | 35 | X | |
| 比較例3 | 50 | X | |
| 實施例1 | 600 | 25 | ◎ |
| 實施例2 | 35 | ◎ | |
| 比較例4 | 50 | X | |
| 實施例3 | 1200 | 25 | ◎ |
| 實施例4 | 35 | ◎ | |
| 實施例5 | 50 | O | |
| 實施例6 | 1500 | 25 | ◎ |
| 實施例7 | 35 | ◎ | |
| 實施例8 | 50 | ◎ | |
| 比較例5 | 1700 | 25 | X |
| 比較例6 | 35 | X |
如所述表2所示，當第一和第二應力緩和粘著層中的每一個的粘著力小於600 gf/in時（比較例1至比較例3），作為折疊可靠性測試的結果，出現翹起（參見第3圖）。此外，當第一和第二應力緩和粘著層中的每一個的粘著力超過1,500 gf/in時（比較例5和比較例6），顯示器保護器非常難以從可折疊終端拆卸，並且可折疊終端的表面部分損壞。
當第一和第二應力緩和粘著層中的每一個的厚度為50 ㎛時，折疊可靠性測試結果一般良好，但是當第一和第二應力緩和粘著層中的每一個的粘著力為600 gf/in時（比較例4），確認出現翹起（參照第3B圖）。
然而，當第一和第二應力緩和粘著層中的每一個的粘著力為600 gf/in至1,500 gf/in的範圍内，並且第一和第二應力緩和粘著層中的每一個的厚度分别為25 μm和35 μm時，在没有出現翹起的情况下獲得優異的折疊可靠性測試結果（參照第3C圖）。
＜透明基材層測試＞
通過形成厚度為25 μm的丙烯酸光學透明粘合劑（OCA：optically clear adhesive）層作為第一和第二應力緩和粘著層，並且改變聚氨酯透明基材層的厚度來進行折疊可靠性測試。結果，獲得表3中所示的結果。
＜表3＞
| 粘著力（g f/in） | 透明基材層的厚度（㎛） | 評估結果 | |
| 比較例7 | 400 | 12 | X |
| 比較例8 | 19 | X | |
| 比較例9 | 25 | X | |
| 實施例9 | 600 | 12 | ◎ |
| 比較例10 | 19 | X | |
| 實施例10 | 25 | O | |
| 實施例11 | 1200 | 12 | ◎ |
| 實施例12 | 19 | ◎ | |
| 實施例13 | 25 | ◎ | |
| 實施例14 | 1500 | 12 | ◎ |
| 實施例15 | 19 | ◎ | |
| 實施例16 | 25 | ◎ |
如所述表3所示，即使改變透明基材層的厚度，當第一和第二應力緩和粘著層中的每一個的粘著力小於600 gf/in時（比較例7至比較例9），作為折疊可靠性測試的結果，出現翹起（參照第4圖）。
＜UTG層測試＞
通過使用具有25 μm的厚度和600 gf/in的粘合力的丙烯酸OCA層作為第一和第二應力緩和粘著層中的每一個，使用具有12 μm的厚度的聚氨酯透明基材層作為透明基材層，並在其上形成各種厚度（30 μm、50 μm和75 μm）的UTG層來製造顯示器保護器，從而進行所述折疊可靠性測試。結果，當使用厚度為30 μm和50 μm的UTG層時，UTG層没有翹起或損壞，但當使用厚度為75 μm的UTG層時，觀察到UTG層的翹起和損壞，並且難以將可折疊終端保持在L形。
＜應力緩和粘著層的組合＞
通過使用厚度為12 μm的聚氨酯透明基材層作為透明基材層，並在其兩個表面上提供彼此相同或不同的第一和第二應力緩和粘著層，從而進行了折疊可靠性測試並觀察了翹起。UTG層的厚度為30 μm，並且測試結果總結在下表4中。
＜表4＞
| 比較例11 | 比較例12 | 比較例17 | 比較例18 | |
| UTG層 | 30 μm | |||
| 第一應力緩和粘著層 | FOCA A | FOCA B | FOCA A | FOCA B |
| 透明基材層 | 12 μm | |||
| 第二應力緩和粘著層 | FOCA B | FOCA A | FOCA A | FOCA B |
| 評估結果 | X | O | ◎ | ◎ |
在表4中，FOCA A是在25℃下具有0.1 MPa儲能模量的丙烯酸OCA，並且FOCA B是在25℃下具有0.05 MPa儲能模量的丙烯酸OCA。
如表4所示，當第一應力緩和粘著層的儲能模量大於第二應力緩和粘著層的儲能模量時（比較例11），發生翹起（參照第5A圖）。相反，當第一應力緩和粘著層的儲能模量小於第二應力緩和粘著層的儲能模量時（比較例12），證實了發生翹起的程度减輕。並且，當第一應力緩和粘著層的儲能模量與第二應力緩和粘著層的儲能模量基本相同時（實施例17和實施例18），確認對翹起最有效（參照第5B圖）。
＜應力緩和粘著層的儲能模量＞
在40℃下改變第一和第二應力緩和粘著層中的每一個的儲能模量的同時進行所述折疊可靠性測試，並觀察到翹起。測試結果總結在下表5中。
＜表5＞
| 儲能模量（MPa） | 評估結果 | |
| 實施例1 | 0.02 | ◎ |
| 實施例20 | 0.05 | ◎ |
| 實施例21 | 0.10 | ◎ |
| 實施例22 | 0.15 | ◎ |
| 實施例23 | 0.20 | ◎ |
| 比較例13 | 0.25 | X |
| 比較例14 | 0.30 | X |
| 比較例15 | 0.35 | X |
如表5所示，當第一和第二應力緩和粘著層中的每一個的儲能模量為0.2 MPa或更小時，顯示出優異的折疊可靠性，但是當第一和第二應力緩和粘著層中的每一個的儲能模量為0.25 MPa或更高時，觀察到翹起現象（參照第6圖）。
第7圖為概略地示出根據本發明一實施例的顯示器保護器100b的示意圖。第8A圖和第8B圖為分别示出沿第7圖的A-A'線和B-B'線截取的截面圖。
參照第7圖、第8A圖和第8B圖，所述顯示器保護器100b包括透明基材層110、在所述透明基材層110的第一表面上的第一應力緩和粘著層120a、在所述透明基材層110的第二表面上的第二應力緩和粘著層120b和在所述第一應力緩和粘著層120a上的UTG層130。
特别地，所述UTG層130包括第一玻璃邊緣130E1和第二玻璃邊緣130E2，其都在第一方向（即，X方向）上延伸並且彼此相對。此外，所述UTG層130包括第三玻璃邊緣130E3和第四玻璃邊緣130E4，其都在垂直於所述第一方向的第二方向（即，Y方向）上延伸並且彼此相對。
並且，所述透明基材層110、所述第一應力緩和粘著層120a和所述第二應力緩和粘著層120b具有共同的外邊緣，並且所述共同的外邊緣具有分别對應於所述第一玻璃邊緣130E1和所述第二玻璃邊緣130E2並在第一方向（即，X方向）上延伸的第一薄膜邊緣110E1和第二薄膜邊緣110E2。此外，所述外邊緣具有分别對應於所述第三玻璃邊緣130E3和所述第四玻璃邊緣130E4的第三薄膜邊緣110E3和第四薄膜邊緣110E4。
如第7圖和第8A圖所示，所述第一薄膜邊緣110E1和所述第二薄膜邊緣110E2可以分别比所述第一玻璃邊緣130E1和所述第二玻璃邊緣130E2向内偏移（offset）第一尺寸d1。如上所述，薄膜邊緣比玻璃邊緣向内的偏移可稱為“負偏移”。此外，術语“向内”是指從所述外邊緣或每個邊緣朝向所述UTG層130的中心的方向。
並且，參照第7圖和第8B圖，所述第三薄膜邊緣110E3和/或所述第四薄膜邊緣110E4可分别比所述第三玻璃邊緣130E3和/或所述第四玻璃邊緣130E4向外偏移第二尺寸d2。即，在一些實施例中，所述第三薄膜邊緣110E3可比所述第三玻璃邊緣130E3向外偏移第二尺寸d2。在一些實施例中，所述第四薄膜邊緣110E4可比所述第四玻璃邊緣130E4向外偏移第二尺寸d2。在一些實施例中，所述第三薄膜邊緣110E3和所述第四薄膜邊緣110E4可分别比所述第三玻璃邊緣130E3和所述第四玻璃邊緣130E4向外偏移第二尺寸d2。如上所述，薄膜邊緣比玻璃邊緣向外的偏移可稱為“正偏移”。在此，術语“向外”是指與術语“向内”相反的方向。
所述第一尺寸d1可以是約20 μm至約200 μm。在一些實施例中，所述第一尺寸d1可為約20 μm至約200 μm、約25 μm至約180 μm、約30 μm至約160 μm、約35 μm至約150 μm、約40 μm至約140 μm、約45 μm至約130 μm、約50 μm至約120 μm、約55 μm至約110 μm、約60 μm至約100 μm或這些值之間的任何範圍。
所述第二尺寸d2可以是約50 μm至約400 μm。在一些實施例中，所述第二尺寸d2可為約50 μm至約400 μm、約60 μm至約380 μm、約70 μm至約360 μm、約80 μm至約340 μm、約90 μm至約320 μm、約100 μm至約300 μm、約120 μm 至約280 μm、約140 μm至約260 μm或這些值之間的任何範圍。當所述第二尺寸d2太小時，折疊可靠性可能不足。當所述第二尺寸d2太大時，可能會過多地附著異物。
這裡，所述第二尺寸d2可以是從下面將描述的折疊軸FAX的偏移尺寸。所述顯示器保護器100b可設置成能夠相對於平行於所述第一玻璃邊緣130E1和所述第二玻璃邊緣130E2的折疊軸FAX折疊，這已經參考第1A圖至第2A圖進行了描述，因此這裡省略對其的詳細描述。
這樣，通過在折疊部分相對於折疊軸FAX形成正偏移，當重復折疊和展開時，折疊部分的可靠性可以大大提高。换句话說，當折疊部分相對於折疊軸FAX負偏移時，折疊部分可以隨著折疊和展開的重復而被容易地翹起。然而，本發明的發明人已經發現，當折疊部分相對於折疊軸FAX正偏移時，即使在重復折疊和展開時也可以顯著减少折疊部分的翹起。
第9圖為放大其中第7圖的第一玻璃邊緣110E1和第三玻璃邊緣110E3相接的部分和折疊軸FAX的附近的局部放大圖。
參照第7圖至第9圖，所述第三薄膜邊緣110E3包括第一薄膜子邊緣部110E31，其在與所述折疊軸FAX相交的同時比所述第三玻璃邊緣130E3向外偏移。所述第一薄膜子邊緣部110E31可包括在與第一方向垂直的第二方向（即，Y方向）上延伸的部分。
而且，所述第三薄膜邊緣110E3還可包括與所述第一薄膜邊緣110E1相接的第一角邊緣部110E3c。所述第一角邊緣部110E3c可比UTG層130的對應角部分的邊緣向内負偏移。
所述第三薄膜邊緣110E3還可在所述第一角邊緣部110E3c和所述第一薄膜子邊緣部110E31之間包括第二薄膜子邊緣部110E32。在一些實施例中，所述第二薄膜子邊緣部110E32可以將所述第一角邊緣部110E3c連接到所述第一薄膜子邊緣部110E31。如第9圖所示，所述第二薄膜子邊緣部110E32可在其大部分長度上比所述第三玻璃邊緣130E3向外偏移。在一些實施例中，所述第二薄膜子邊緣部110E32可相對於其80%或更大的長度比所述第三玻璃邊緣130E3向外偏移。在一些實施例中，所述第二薄膜子邊緣部110E32向外偏移的尺寸可以隨著與所述第一角邊緣部10E3c的距離减小而逐漸减小。此外，所述第二薄膜子邊緣部110E32可以在越來越靠近所述第一角邊緣部110E3c的同時與所述第三玻璃邊緣130E3相交。並且，所述第二薄膜子邊緣部110E32可在與所述第一角邊緣部110E3c相接的區域的附近比所述第三玻璃邊緣130E3向内偏移。
雖然第9圖中描述了第一薄膜邊緣110E1和第三薄膜邊緣110E3相接的部分，但本領域普通技術人員可以理解，上述描述同樣應用於第二薄膜邊緣110E2和第三薄膜邊緣110E3相接的部分、第一薄膜邊緣110E1和第四薄膜邊緣110E4相接的部分，以及第二薄膜邊緣110E2和第四薄膜邊緣110E4相接的部分。
第10圖為概略地示出根據本發明另一實施例的顯示器保護器100c的示意圖。
參照第10圖，所述第三薄膜邊緣110E3可包括第一薄膜子邊緣部110E31、第二薄膜子邊緣部110E32和第一角邊緣部110E3c。
如第10圖所示，本實施例的第二薄膜邊緣部110E32可相對於其總長度的80％或更大比所述第三玻璃邊緣130E3的相應部分向内偏移第三尺寸d3。特别地，所述第二薄膜邊緣部110E32可包括在平行於第三玻璃邊緣130E3的第二方向（即，Y方向）上延伸的部分。
所述第三尺寸d3可以是約20 μm至約200 μm。在一些實施例中，所述第三尺寸d3可為約20 μm至約200 μm、約25 μm至約180 μm、約30 μm至約160 μm、約35 μm至約150 μm、約40 μm至約140 μm、約45 μm至約130 μm、約50 μm至約120 μm、約55 μm至約110 μm、約60 μm至約100 μm或這些值之間的任何範圍。
並且，第一薄膜子邊緣部110E31可包括在與折疊軸FAX相交的同時在第二方向（即，Y方向）上延伸的部分。所述第一薄膜子邊緣部110E31可具有正偏移部分，並且所述正偏移部分可在所述第二方向上具有約3 mm至約15 mm的寬度。在一些實施例中，所述寬度可為約4 mm至約13 mm、約5 mm至約11 mm、約6 mm至約10 mm、約7 mm至約9 mm或這些值之間的任何範圍。
並且，所述第一薄膜子邊緣部分110E31可比所述第三玻璃邊緣130E3向外偏移至少20 μm。在一些實施例中，所述第一薄膜子邊緣部110E31可在折疊軸FAX中比所述第三玻璃邊緣130E3向外偏移約20 μm至約400 μm。在一些實施例中，所述第一薄膜子邊緣部110E31可在折疊軸FAX中比所述第三玻璃邊緣130E3向外偏移約20 μm至約400 μm、約30 μm至約380 μm、約40 μm至約360 μm、約50 μm至約340 μm、約60 μm至約320 μm、約70 μm至約300 μm、約80 μm至約280 μm、約90 μm至約260 μm、約100 μm至約240 μm、約110 μm至約220 μm、約120 μm至約200 μm，或這些值之間的任何範圍。由於第10圖所示的顯示器保護器100c還具有相對於折疊軸FAX在折疊部分中形成的正偏移，所以當重復折疊和展開時，折疊部分的可靠性可以大大提高。
第11圖為概略地示出根據本發明另一實施例的顯示器保護器100d的示意圖。第12圖為示出沿第11圖的A-A'線截取的截面圖。
參照第11圖和第12圖，第一至第四薄膜邊緣110E1、110E2、110E3和110E4可分别從第一至第四玻璃邊緣130E1、130E2、130E3和130E4向内偏移第一尺寸d1。即，第一至第四薄膜邊緣110E、110E2、110E3和110E4的偏移均可以是負偏移。
如上所述，因為在相對於折疊軸FAX的折疊部分中形成負偏移，除非采取其他措施，否則折疊部分的可靠性大大降低。然而，如第12圖所示，粘著劑150提供於負偏移部分處。所述粘著劑150可沿著負偏移部分延伸。即，發現由於所述粘著劑150從所述第三薄膜邊緣110E3的側表面横跨折疊軸FAX延伸，因此即使在重復折疊和展開時，折疊部分中的翹起也可以顯著减少。
所述粘著劑150可以在粘著溶液中固化，並且所述粘著溶液可以是具有相對低粘度的粘著溶液，使得可通過毛細管現象在具有第一尺寸d1的窄寬度的空間中很好地滲透。
考慮到基礎聚合物例如丙烯酸樹脂、苯乙烯樹脂或有機矽樹脂與交聯劑例如異氰酸酯化合物、環氧化合物或氮丙啶化合物以及與玻璃之間的粘合性，所述粘著溶液可包括例如添加了諸如矽烷偶聯劑的添加劑的組合物。但本發明不限於此。
在一些實施例中，所述粘著溶液的粘度在約20℃至約25℃的溫度下可為約10 cp至約50 cp。當所述粘著溶液的粘度太低時，粘著性能會降低並且洩漏的可能性會增加。另一方面，當所述粘著溶液的粘度太高時，由於毛細現象導致的滲透性可能降低，因此所述粘著溶液可能無法均匀滲透。
本發明一實施例提供了一種顯示器保護器附接配套元件，其包括顯示器保護器和粘著溶液。
所述顯示器保護器附接配套元件可包括顯示器保護器，其中透明基材層具有相對於UTG層的任意負偏移，以及粘著溶液，其在填充由所述負偏移定義的空間的同時對顯示器表面具有粘著力。所述粘著溶液在填充由所述負偏移定義的空間後可以被UV固化以用作粘著劑。
在一些實施例中，所述顯示器保護器可以是參照第1A圖、第1B圖、第7圖、第10圖和第11圖描述的顯示器保護器中的任何一個。
＜實施例24＞
在分别將粘著力為1,200 gf/in的第一和第二應力緩和粘著層粘附到厚度為12 μm的聚對苯二甲酸乙二醇酯（PET：Polyethylene terephthalate）透明基材層的兩側表面後，厚度為30 μm的UTG層粘附在第一應力緩和粘著層上。所述PET透明基材層與第一和第二應力緩和粘著層的層壓體在折疊軸中被切割成相對於所述UTG層具有-100 μm、+50 μm、+150 μm和+250 μm的偏移，並且對於每種情况，粘附到裝置1和裝置2中的每一個上以進行折疊測試，其結果總結在表6中。另外，當存在-100 μm的偏移時，分别對形成粘著劑的情况和未形成粘著劑的情况進行折疊測試。
＜表6＞
| 偏移 | 裝置1 | 裝置2 |
| -100 | 190 | 300 |
| +50 | 10,000+ | 2030 |
| +150 | 11000+ | 17481+ |
| +250 | 30000+ | 10000+ |
| -100（+粘著劑） | 10000+ | 6000+ |
參照表6，當所述PET透明基材層與第一和第二應力緩和粘著層的層壓體在折疊軸中相對於UTG層負偏移時，在190次和300次折疊和展開後發生翹起。
然而，當折疊軸中包括正偏移時，即使在數千或數万次折疊和展開之後也没有發生翹起。在表6中，在數字後加上“+”意味著即使在該數字中也没有發生翹起。
此外，已經證實，即使具有負偏移，也可以通過在由負偏移限定義的空間中形成粘著劑來確保與正偏移相當的折疊穩定性。
本發明的顯示器保護器不僅可應對可折疊終端或可卷曲終端，而且具有優良的折疊可靠性，因此即使在可折疊終端或可卷曲終端上長時間使用也不會剝落，並且在需要時可相對容易地拆卸。
雖然已在此描述了某些示例性實施例和實施方式，但是根據該描述，其他實施例和修改將是明顯的。因此，本發明構思不限於這些實施例，而是限於所附發明申請專利範圍的更寬範圍，並且對於本領域普通技術人員來說，各種顯而易見的修改和等同佈置將是明顯的。
100, 100a:顯示器保護器
110:透明基材層
120a:第一應力緩和粘著層
120b:第二應力緩和粘著層
130:超薄玻璃(ultra-thin glass, UTG)層
140:防散射塗層
被包括以提供對本發明的進一步理解並且被並入且構成本說明書的一部分的附圖例示本發明的示例性實施例，並且與說明書一起用於解釋本發明構思。
第1A圖為概略地示出根據本發明一實施例的顯示器保護器的層壓結構的示意圖。
第1B圖為概略地示出根據本發明另一實施例的顯示器保護器的層壓結構的示意圖。
第2A圖為示出根據本發明一實施例的顯示器保護器附接到可折疊顯示裝置的狀態的透視圖。
第2B圖為示出根據本發明一實施例的顯示器保護器附接到可卷曲顯示裝置的狀態的透視圖。
第3A圖至第6圖為示出根據本發明實施例的和比較例的折疊可靠性測試結果的圖像。
第7圖為概略地示出根據本發明一實施例的顯示器保護器的示意圖。
第8A圖和第8B圖為分别示出沿第7圖的A-A'線和B-B'線截取的截面圖。
第9圖為放大其中第7圖的第一玻璃邊緣和第三玻璃邊緣相接的部分和折疊軸的附近的局部放大圖。
第10圖為概略地示出根據本發明另一實施例的顯示器保護器的示意圖。
第11圖為概略地示出根據本發明另一實施例的顯示器保護器的示意圖。
第12圖為示出沿第11圖的A-A'線截取的截面圖。
100:顯示器保護器
110:透明基材層
110a:第一表面
110b:第二表面
120a:第一應力緩和粘著層
120b:第二應力緩和粘著層
130:超薄玻璃層
Claims (23)
- 一種顯示器保護器，包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及超薄玻璃層；其位於所述第一應力緩和粘著層上，其中，所述第一應力緩和粘著層的儲能模量在-10℃下為約0.03MPa至約0.2MPa，其中，所述超薄玻璃層具有約30微米(μm)至約70μm的厚度，並且為經過強化的玻璃，以在折疊為1.0mm的曲率半徑時不會損壞。
- 根據請求項1所述的顯示器保護器，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個具有約600gf/in至約1,500gf/in的粘著力。
- 根據請求項1所述的顯示器保護器，其中，所述第一應力緩和粘著層的儲能模量在+40℃下為約0.02MPa至約0.2MPa。
- 根據請求項1所述的顯示器保護器，其中，所述第二應力緩和粘著層的儲能模量在-10℃下為約0.03MPa至約0.2MPa。
- 根據請求項1所述的顯示器保護器，其中， 所述第二應力緩和粘著層的儲能模量在+40℃下為約0.02MPa至約0.2MPa。
- 根據請求項1所述的顯示器保護器，其進一步包括：防散射塗層，其位於所述超薄玻璃層上。
- 根據請求項1所述的顯示器保護器，其中，所述第一應力緩和粘著層的儲能模量小於或基本等於所述第二應力緩和粘著層的儲能模量。
- 一種顯示器保護器，包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及超薄玻璃層；其位於所述第一應力緩和粘著層上，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個相對於所述透明基材層以及對於其上黏附有所述第一應力緩和粘著層和所述第二應力緩和粘著層的可折疊或可卷曲顯示器具有約600gf/in至約1,500gf/in的粘著力，其中，所述超薄玻璃層的厚度為約30μm至約70μm。
- 根據請求項8所述的顯示器保護器，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在-10℃下為約0.03MPa至約0.18MPa。
- 根據請求項9所述的顯示器保護器，其中， 所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在-10℃下為約0.06MPa至約0.14MPa。
- 根據請求項8所述的顯示器保護器，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在+40℃下為約0.02MPa至約0.18MPa。
- 根據請求項11所述的顯示器保護器，其中，所述第一應力緩和粘著層和所述第二應力緩和粘著層中的每一個的儲能模量在+40℃下為約0.04MPa至約0.14MPa。
- 根據請求項8所述的顯示器保護器，其進一步包括：防散射塗層，其位於所述超薄玻璃層上。
- 一種顯示器保護器，包括：透明基材層，其具有第一表面和與所述第一表面相對的第二表面；第一應力緩和粘著層，其位於所述透明基材層的所述第一表面上；第二應力緩和粘著層，其位於所述透明基材層的所述第二表面上；以及超薄玻璃層；其位於所述第一應力緩和粘著層上，其中，所述超薄玻璃層包括：第一玻璃邊緣和第二玻璃邊緣，其各自在第一方向上延伸並且彼此相對；以及第三玻璃邊緣和第四玻璃邊緣，其各自在垂直於第一方向的第二方向上延伸並且彼此相對， 其中，所述超薄玻璃層的厚度為約30μm至約70μm，其中，所述透明基材層、所述第一應力緩和粘著層和所述第二應力緩和粘著層包括共同的外邊緣，其中，所述共同的外邊緣包括：第一薄膜邊緣和第二薄膜邊緣，其分別平行於所述第一玻璃邊緣和所述第二玻璃邊緣延伸；以及第三薄膜邊緣和第四薄膜邊緣，其分別對應於所述第三玻璃邊緣和所述第四玻璃邊緣，其中，所述第一薄膜邊緣和所述第二薄膜邊緣分別比所述第一玻璃邊緣和所述第二玻璃邊緣向內偏移。
- 根據請求項14所述的顯示器保護器，其中，所述顯示器保護器被配置為可相對於平行於所述第一玻璃邊緣和所述第二玻璃邊緣的折疊軸折疊。
- 根據請求項15所述的顯示器保護器，其中，所述第三薄膜邊緣比所述第三玻璃邊緣至少部分地向外偏移；所述第四薄膜邊緣比所述第四玻璃邊緣至少部分地向外偏移；或者所述第三薄膜邊緣和所述第四薄膜邊緣分別比所述第三玻璃邊緣和所述第四玻璃邊緣至少部分地向外偏移。
- 根據請求項16所述的顯示器保護器，其中，所述第三薄膜邊緣和所述第四薄膜邊緣分別比所述第三玻璃邊緣和所述第四玻璃邊緣至少部分地向外偏移。
- 根據請求項16所述的顯示器保護器，其中，所述第三薄膜邊緣包括： 第一薄膜子邊緣部，其與所述折疊軸相交並比所述第三玻璃邊緣向外偏移；第一角邊緣部，其形成所述第三薄膜邊緣的末端部並與所述第一薄膜邊緣相接；以及第二薄膜子邊緣部，其連接所述第一薄膜子邊緣部與所述第一角邊緣部，所述第一角邊緣部比所述超薄玻璃層的對應角邊緣向內偏移。
- 根據請求項18所述的顯示器保護器，其中，所述第二薄膜子邊緣部包括比所述第三玻璃邊緣向外偏移的部分，並且所述第二薄膜子邊緣部向外偏移的尺寸隨著與所述第一角邊緣部的距離減小而逐漸減小。
- 根據請求項18所述的顯示器保護器，其中，所述第一薄膜子邊緣部比所述第三玻璃邊緣向外偏移至少20微米(μm)，所述第二薄膜子邊緣部相對於其80%或更多的長度比所述第三玻璃邊緣的對應部分向內偏移。
- 根據請求項18所述的顯示器保護器，其中，所述第一薄膜子邊緣部在所述折疊軸上比所第三玻璃邊緣向外偏移的尺寸為約50μm至約400μm。
- 一種顯示器保護器附接配套元件，包括：根據請求項1至13中任一項所述的顯示器保護器；以及粘著溶液，其可提供到所述顯示器保護器的邊緣， 其中，所述透明基材層、所述第一應力緩和粘著層和所述第二應力緩和粘著層具有共同的外邊緣，並且所述共同的外邊緣比所述超薄玻璃層的邊緣向內偏移。
- 根據請求項22所述的顯示器保護器附接配套元件，其中，所述粘著溶液的粘度在約20℃至約25℃的溫度下為約10cp至約50cp。