TWI806197B - 具有高損傷抗性之鋯石相容離子交換玻璃 - Google Patents
具有高損傷抗性之鋯石相容離子交換玻璃 Download PDFInfo
- Publication number
- TWI806197B TWI806197B TW110138653A TW110138653A TWI806197B TW I806197 B TWI806197 B TW I806197B TW 110138653 A TW110138653 A TW 110138653A TW 110138653 A TW110138653 A TW 110138653A TW I806197 B TWI806197 B TW I806197B
- Authority
- TW
- Taiwan
- Prior art keywords
- glass
- mol
- ion
- exchanged
- mole
- Prior art date
Links
- 239000011521 glass Substances 0.000 title claims abstract description 168
- 150000002500 ions Chemical class 0.000 title claims abstract description 16
- 229910052845 zircon Inorganic materials 0.000 title claims description 33
- GFQYVLUOOAAOGM-UHFFFAOYSA-N zirconium(iv) silicate Chemical compound [Zr+4].[O-][Si]([O-])([O-])[O-] GFQYVLUOOAAOGM-UHFFFAOYSA-N 0.000 title claims description 33
- 230000000977 initiatory effect Effects 0.000 claims abstract description 13
- 229910000272 alkali metal oxide Inorganic materials 0.000 claims abstract description 10
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims description 37
- 229910004298 SiO 2 Inorganic materials 0.000 claims description 17
- FUJCRWPEOMXPAD-UHFFFAOYSA-N Li2O Inorganic materials [Li+].[Li+].[O-2] FUJCRWPEOMXPAD-UHFFFAOYSA-N 0.000 claims description 4
- 229910018068 Li 2 O Inorganic materials 0.000 claims description 3
- 229910052708 sodium Inorganic materials 0.000 claims description 3
- KKCBUQHMOMHUOY-UHFFFAOYSA-N Na2O Inorganic materials [O-2].[Na+].[Na+] KKCBUQHMOMHUOY-UHFFFAOYSA-N 0.000 claims description 2
- XUCJHNOBJLKZNU-UHFFFAOYSA-M dilithium;hydroxide Chemical compound [Li+].[Li+].[OH-] XUCJHNOBJLKZNU-UHFFFAOYSA-M 0.000 claims 1
- 229910052796 boron Inorganic materials 0.000 abstract description 26
- 238000007373 indentation Methods 0.000 abstract description 18
- -1 boron cations Chemical class 0.000 abstract description 9
- JKWMSGQKBLHBQQ-UHFFFAOYSA-N diboron trioxide Chemical compound O=BOB=O JKWMSGQKBLHBQQ-UHFFFAOYSA-N 0.000 abstract description 6
- 238000005299 abrasion Methods 0.000 abstract description 4
- 229910011255 B2O3 Inorganic materials 0.000 abstract description 3
- PNEYBMLMFCGWSK-UHFFFAOYSA-N aluminium oxide Inorganic materials [O-2].[O-2].[O-2].[Al+3].[Al+3] PNEYBMLMFCGWSK-UHFFFAOYSA-N 0.000 abstract description 3
- 238000006748 scratching Methods 0.000 abstract description 3
- 230000002393 scratching effect Effects 0.000 abstract description 3
- CPLXHLVBOLITMK-UHFFFAOYSA-N Magnesium oxide Chemical compound [Mg]=O CPLXHLVBOLITMK-UHFFFAOYSA-N 0.000 description 30
- 238000000137 annealing Methods 0.000 description 24
- MCMNRKCIXSYSNV-UHFFFAOYSA-N Zirconium dioxide Chemical compound O=[Zr]=O MCMNRKCIXSYSNV-UHFFFAOYSA-N 0.000 description 22
- ZOXJGFHDIHLPTG-UHFFFAOYSA-N Boron Chemical compound [B] ZOXJGFHDIHLPTG-UHFFFAOYSA-N 0.000 description 19
- 150000001768 cations Chemical class 0.000 description 18
- 238000005342 ion exchange Methods 0.000 description 16
- 239000000395 magnesium oxide Substances 0.000 description 15
- 239000000203 mixture Substances 0.000 description 14
- 239000011734 sodium Substances 0.000 description 14
- 229910052782 aluminium Inorganic materials 0.000 description 12
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 12
- 239000010410 layer Substances 0.000 description 12
- 238000007670 refining Methods 0.000 description 12
- 229910052656 albite Inorganic materials 0.000 description 11
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 description 10
- XOLBLPGZBRYERU-UHFFFAOYSA-N tin dioxide Chemical compound O=[Sn]=O XOLBLPGZBRYERU-UHFFFAOYSA-N 0.000 description 10
- 238000005259 measurement Methods 0.000 description 9
- 229910052760 oxygen Inorganic materials 0.000 description 8
- 229910052783 alkali metal Inorganic materials 0.000 description 7
- 239000007788 liquid Substances 0.000 description 7
- 238000000034 method Methods 0.000 description 7
- QVGXLLKOCUKJST-UHFFFAOYSA-N atomic oxygen Chemical compound [O] QVGXLLKOCUKJST-UHFFFAOYSA-N 0.000 description 6
- 239000001301 oxygen Substances 0.000 description 6
- 239000003513 alkali Substances 0.000 description 5
- 150000001340 alkali metals Chemical class 0.000 description 5
- 238000004458 analytical method Methods 0.000 description 5
- JEIPFZHSYJVQDO-UHFFFAOYSA-N iron(III) oxide Inorganic materials O=[Fe]O[Fe]=O JEIPFZHSYJVQDO-UHFFFAOYSA-N 0.000 description 5
- 239000000377 silicon dioxide Substances 0.000 description 5
- 238000005481 NMR spectroscopy Methods 0.000 description 4
- 239000005407 aluminoborosilicate glass Substances 0.000 description 4
- 230000004927 fusion Effects 0.000 description 4
- 239000003607 modifier Substances 0.000 description 4
- 239000002245 particle Substances 0.000 description 4
- FYYHWMGAXLPEAU-UHFFFAOYSA-N Magnesium Chemical compound [Mg] FYYHWMGAXLPEAU-UHFFFAOYSA-N 0.000 description 3
- BPQQTUXANYXVAA-UHFFFAOYSA-N Orthosilicate Chemical compound [O-][Si]([O-])([O-])[O-] BPQQTUXANYXVAA-UHFFFAOYSA-N 0.000 description 3
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical group [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 3
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 3
- 229910052788 barium Inorganic materials 0.000 description 3
- 238000001816 cooling Methods 0.000 description 3
- 230000007547 defect Effects 0.000 description 3
- 230000000694 effects Effects 0.000 description 3
- 229910001947 lithium oxide Inorganic materials 0.000 description 3
- 229910052749 magnesium Inorganic materials 0.000 description 3
- 239000011777 magnesium Substances 0.000 description 3
- 238000004519 manufacturing process Methods 0.000 description 3
- 230000008569 process Effects 0.000 description 3
- 229910052710 silicon Inorganic materials 0.000 description 3
- 229910052712 strontium Inorganic materials 0.000 description 3
- 229910052725 zinc Inorganic materials 0.000 description 3
- 239000011701 zinc Substances 0.000 description 3
- WHXSMMKQMYFTQS-UHFFFAOYSA-N Lithium Chemical compound [Li] WHXSMMKQMYFTQS-UHFFFAOYSA-N 0.000 description 2
- AFCARXCZXQIEQB-UHFFFAOYSA-N N-[3-oxo-3-(2,4,6,7-tetrahydrotriazolo[4,5-c]pyridin-5-yl)propyl]-2-[[3-(trifluoromethoxy)phenyl]methylamino]pyrimidine-5-carboxamide Chemical compound O=C(CCNC(=O)C=1C=NC(=NC=1)NCC1=CC(=CC=C1)OC(F)(F)F)N1CC2=C(CC1)NN=N2 AFCARXCZXQIEQB-UHFFFAOYSA-N 0.000 description 2
- ZLMJMSJWJFRBEC-UHFFFAOYSA-N Potassium Chemical compound [K] ZLMJMSJWJFRBEC-UHFFFAOYSA-N 0.000 description 2
- 229910006404 SnO 2 Inorganic materials 0.000 description 2
- 230000008901 benefit Effects 0.000 description 2
- HYFJXBYGHMZZPQ-UHFFFAOYSA-N boron(1+) Chemical compound [B+] HYFJXBYGHMZZPQ-UHFFFAOYSA-N 0.000 description 2
- 239000005388 borosilicate glass Substances 0.000 description 2
- 229910052791 calcium Inorganic materials 0.000 description 2
- 239000011575 calcium Substances 0.000 description 2
- 230000015556 catabolic process Effects 0.000 description 2
- 239000003153 chemical reaction reagent Substances 0.000 description 2
- 238000009792 diffusion process Methods 0.000 description 2
- 239000002241 glass-ceramic Substances 0.000 description 2
- 239000012535 impurity Substances 0.000 description 2
- 229910052744 lithium Inorganic materials 0.000 description 2
- 238000012986 modification Methods 0.000 description 2
- 230000004048 modification Effects 0.000 description 2
- TWNQGVIAIRXVLR-UHFFFAOYSA-N oxo(oxoalumanyloxy)alumane Chemical compound O=[Al]O[Al]=O TWNQGVIAIRXVLR-UHFFFAOYSA-N 0.000 description 2
- 229910052700 potassium Inorganic materials 0.000 description 2
- 239000011591 potassium Substances 0.000 description 2
- 238000012545 processing Methods 0.000 description 2
- 239000011819 refractory material Substances 0.000 description 2
- 239000012798 spherical particle Substances 0.000 description 2
- 238000007655 standard test method Methods 0.000 description 2
- 238000003860 storage Methods 0.000 description 2
- 238000005728 strengthening Methods 0.000 description 2
- 229910000314 transition metal oxide Inorganic materials 0.000 description 2
- OYPRJOBELJOOCE-UHFFFAOYSA-N Calcium Chemical compound [Ca] OYPRJOBELJOOCE-UHFFFAOYSA-N 0.000 description 1
- 229910020599 Co 3 O 4 Inorganic materials 0.000 description 1
- 101001062093 Homo sapiens RNA-binding protein 15 Proteins 0.000 description 1
- DGAQECJNVWCQMB-PUAWFVPOSA-M Ilexoside XXIX Chemical compound C[C@@H]1CC[C@@]2(CC[C@@]3(C(=CC[C@H]4[C@]3(CC[C@@H]5[C@@]4(CC[C@@H](C5(C)C)OS(=O)(=O)[O-])C)C)[C@@H]2[C@]1(C)O)C)C(=O)O[C@H]6[C@@H]([C@H]([C@@H]([C@H](O6)CO)O)O)O.[Na+] DGAQECJNVWCQMB-PUAWFVPOSA-M 0.000 description 1
- 102100029244 RNA-binding protein 15 Human genes 0.000 description 1
- 229910010413 TiO 2 Inorganic materials 0.000 description 1
- 238000007545 Vickers hardness test Methods 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 229910052784 alkaline earth metal Inorganic materials 0.000 description 1
- 150000001342 alkaline earth metals Chemical class 0.000 description 1
- 150000001450 anions Chemical class 0.000 description 1
- 239000002585 base Substances 0.000 description 1
- 230000009286 beneficial effect Effects 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 229910052794 bromium Inorganic materials 0.000 description 1
- 229910052792 caesium Inorganic materials 0.000 description 1
- KOPBYBDAPCDYFK-UHFFFAOYSA-N caesium oxide Chemical compound [O-2].[Cs+].[Cs+] KOPBYBDAPCDYFK-UHFFFAOYSA-N 0.000 description 1
- 229910001942 caesium oxide Inorganic materials 0.000 description 1
- 229910052801 chlorine Inorganic materials 0.000 description 1
- 150000001875 compounds Chemical class 0.000 description 1
- 230000006835 compression Effects 0.000 description 1
- 238000007906 compression Methods 0.000 description 1
- 239000000356 contaminant Substances 0.000 description 1
- 238000010924 continuous production Methods 0.000 description 1
- 229910052593 corundum Inorganic materials 0.000 description 1
- 238000003280 down draw process Methods 0.000 description 1
- 239000000835 fiber Substances 0.000 description 1
- 239000006025 fining agent Substances 0.000 description 1
- 229910052731 fluorine Inorganic materials 0.000 description 1
- 238000003286 fusion draw glass process Methods 0.000 description 1
- 150000004820 halides Chemical class 0.000 description 1
- 229910052736 halogen Inorganic materials 0.000 description 1
- 150000002367 halogens Chemical class 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 229910052740 iodine Inorganic materials 0.000 description 1
- 238000002955 isolation Methods 0.000 description 1
- 239000000463 material Substances 0.000 description 1
- 238000002844 melting Methods 0.000 description 1
- 230000008018 melting Effects 0.000 description 1
- 229910044991 metal oxide Inorganic materials 0.000 description 1
- 150000004706 metal oxides Chemical class 0.000 description 1
- 229910052664 nepheline Inorganic materials 0.000 description 1
- 239000010434 nepheline Substances 0.000 description 1
- 238000000655 nuclear magnetic resonance spectrum Methods 0.000 description 1
- 238000000399 optical microscopy Methods 0.000 description 1
- 230000003647 oxidation Effects 0.000 description 1
- 238000007254 oxidation reaction Methods 0.000 description 1
- 125000004430 oxygen atom Chemical group O* 0.000 description 1
- 230000000704 physical effect Effects 0.000 description 1
- 238000013001 point bending Methods 0.000 description 1
- 239000002574 poison Substances 0.000 description 1
- 231100000614 poison Toxicity 0.000 description 1
- FGIUAXJPYTZDNR-UHFFFAOYSA-N potassium nitrate Chemical compound [K+].[O-][N+]([O-])=O FGIUAXJPYTZDNR-UHFFFAOYSA-N 0.000 description 1
- 229910052701 rubidium Inorganic materials 0.000 description 1
- 229910001952 rubidium oxide Inorganic materials 0.000 description 1
- CWBWCLMMHLCMAM-UHFFFAOYSA-M rubidium(1+);hydroxide Chemical compound [OH-].[Rb+].[Rb+] CWBWCLMMHLCMAM-UHFFFAOYSA-M 0.000 description 1
- 150000003839 salts Chemical class 0.000 description 1
- 235000012239 silicon dioxide Nutrition 0.000 description 1
- 238000003283 slot draw process Methods 0.000 description 1
- 238000001228 spectrum Methods 0.000 description 1
- 230000000087 stabilizing effect Effects 0.000 description 1
- 239000006058 strengthened glass Substances 0.000 description 1
- 239000000126 substance Substances 0.000 description 1
- 239000002344 surface layer Substances 0.000 description 1
- 229910001845 yogo sapphire Inorganic materials 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
- C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
- C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
- C03C3/093—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium containing zinc or zirconium
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
- C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
- C03C21/002—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to perform ion-exchange between alkali ions
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C21/00—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface
- C03C21/001—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions
- C03C21/005—Treatment of glass, not in the form of fibres or filaments, by diffusing ions or metals in the surface in liquid phase, e.g. molten salts, solutions to introduce in the glass such metals or metallic ions as Ag, Cu
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
- C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
- C03C3/085—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal
- C03C3/087—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound containing an oxide of a divalent metal containing calcium oxide, e.g. common sheet or container glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C4/00—Compositions for glass with special properties
- C03C4/18—Compositions for glass with special properties for ion-sensitive glass
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C2204/00—Glasses, glazes or enamels with special properties
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31—Surface property or characteristic of web, sheet or block
- Y10T428/315—Surface modified glass [e.g., tempered, strengthened, etc.]
Landscapes
- Chemical & Material Sciences (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Chemical Kinetics & Catalysis (AREA)
- General Chemical & Material Sciences (AREA)
- Geochemistry & Mineralogy (AREA)
- Materials Engineering (AREA)
- Organic Chemistry (AREA)
- Glass Compositions (AREA)
- Surface Treatment Of Glass (AREA)
- Compositions Of Oxide Ceramics (AREA)
- Devices For Indicating Variable Information By Combining Individual Elements (AREA)
Applications Claiming Priority (4)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US201261653489P | 2012-05-31 | 2012-05-31 | |
| US61/653,489 | 2012-05-31 | ||
| US201361748981P | 2013-01-04 | 2013-01-04 | |
| US61/748,981 | 2013-01-04 |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| TW202206395A TW202206395A (zh) | 2022-02-16 |
| TWI806197B true TWI806197B (zh) | 2023-06-21 |
Family
ID=48577935
Family Applications (7)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| TW110138653A TWI806197B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW102119385A TWI599549B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW105137024A TWI613175B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW108100044A TWI694977B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW109114430A TWI815009B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW106144083A TWI650297B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW110138662A TWI815197B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
Family Applications After (6)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| TW102119385A TWI599549B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW105137024A TWI613175B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW108100044A TWI694977B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW109114430A TWI815009B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW106144083A TWI650297B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
| TW110138662A TWI815197B (zh) | 2012-05-31 | 2013-05-31 | 具有高損傷抗性之鋯石相容離子交換玻璃 |
Country Status (8)
| Country | Link |
|---|---|
| US (7) | US8951927B2 (enExample) |
| EP (4) | EP3919454B1 (enExample) |
| JP (6) | JP6305992B2 (enExample) |
| KR (5) | KR102651562B1 (enExample) |
| CN (2) | CN106904827A (enExample) |
| DE (2) | DE202013012920U1 (enExample) |
| TW (7) | TWI806197B (enExample) |
| WO (1) | WO2013181134A1 (enExample) |
Families Citing this family (67)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US8901544B2 (en) | 2011-12-06 | 2014-12-02 | Corning Incorporated | Organic thin film transistor with ion exchanged glass substrate |
| US9359251B2 (en) | 2012-02-29 | 2016-06-07 | Corning Incorporated | Ion exchanged glasses via non-error function compressive stress profiles |
| US9517967B2 (en) | 2012-05-31 | 2016-12-13 | Corning Incorporated | Ion exchangeable glass with high damage resistance |
| EP3919454B1 (en) | 2012-05-31 | 2023-11-01 | Corning Incorporated | Zircon compatible, ion exchangeable glass with high damage resistance |
| KR20150029685A (ko) | 2012-06-08 | 2015-03-18 | 코닝 인코포레이티드 | 강화 유리 제품 및 이의 제조방법 |
| EP2956419A2 (en) * | 2013-01-31 | 2015-12-23 | Corning Incorporated | Transition metal-containing, ion exchangeable colored glasses |
| WO2014120628A2 (en) * | 2013-01-31 | 2014-08-07 | Corning Incorporated | Fictivated glass and method of making |
| US9714192B2 (en) | 2013-02-08 | 2017-07-25 | Corning Incorporated | Ion exchangeable glass with advantaged stress profile |
| US11079309B2 (en) | 2013-07-26 | 2021-08-03 | Corning Incorporated | Strengthened glass articles having improved survivability |
| WO2015057552A2 (en) | 2013-10-14 | 2015-04-23 | Corning Incorporated | Ion exchange process and chemically strengthened glass substrates resulting therefrom |
| CN114230176A (zh) * | 2013-11-26 | 2022-03-25 | 康宁股份有限公司 | 具有高压痕阈值的可快速离子交换玻璃 |
| US9517968B2 (en) | 2014-02-24 | 2016-12-13 | Corning Incorporated | Strengthened glass with deep depth of compression |
| JP6630287B2 (ja) | 2014-03-27 | 2020-01-15 | コーニング インコーポレイテッド | ガラス物品 |
| EP3140116B1 (en) | 2014-05-07 | 2022-02-23 | Corning Incorporated | Laminated glass article and method for forming the same |
| WO2015186486A1 (ja) * | 2014-06-04 | 2015-12-10 | 旭硝子株式会社 | 導光板用のガラス板 |
| TWI697403B (zh) | 2014-06-19 | 2020-07-01 | 美商康寧公司 | 無易碎應力分布曲線的玻璃 |
| US11097974B2 (en) | 2014-07-31 | 2021-08-24 | Corning Incorporated | Thermally strengthened consumer electronic glass and related systems and methods |
| JP6701168B2 (ja) | 2014-07-31 | 2020-05-27 | コーニング インコーポレイテッド | 熱強化ガラス、ならびにガラスの熱強化のための方法および装置 |
| US10611664B2 (en) | 2014-07-31 | 2020-04-07 | Corning Incorporated | Thermally strengthened architectural glass and related systems and methods |
| KR20190090090A (ko) | 2014-10-08 | 2019-07-31 | 코닝 인코포레이티드 | 금속 산화물 농도 구배를 포함한 유리 및 유리 세라믹 |
| US10150698B2 (en) | 2014-10-31 | 2018-12-11 | Corning Incorporated | Strengthened glass with ultra deep depth of compression |
| CN115572078A (zh) | 2014-11-04 | 2023-01-06 | 康宁股份有限公司 | 深层非易碎应力曲线及其制造方法 |
| US10407339B2 (en) * | 2015-02-26 | 2019-09-10 | Corning Incorporated | Ion exchangeable soft glasses for three-dimensional shapes |
| US9761817B2 (en) | 2015-03-13 | 2017-09-12 | Corning Incorporated | Photo-patternable gate dielectrics for OFET |
| WO2016176096A1 (en) | 2015-04-30 | 2016-11-03 | Corning Incorporated | Electrically conductive articles with discrete metallic silver layers and methods for making same |
| US10579106B2 (en) | 2015-07-21 | 2020-03-03 | Corning Incorporated | Glass articles exhibiting improved fracture performance |
| US11613103B2 (en) | 2015-07-21 | 2023-03-28 | Corning Incorporated | Glass articles exhibiting improved fracture performance |
| US12338159B2 (en) | 2015-07-30 | 2025-06-24 | Corning Incorporated | Thermally strengthened consumer electronic glass and related systems and methods |
| TWI758263B (zh) | 2015-11-19 | 2022-03-21 | 美商康寧公司 | 顯示螢幕保護器 |
| WO2017091482A1 (en) | 2015-11-23 | 2017-06-01 | Corning Incorporated | Removal of inorganic coatings from glass substrates |
| WO2017100646A1 (en) | 2015-12-11 | 2017-06-15 | Corning Incorporated | Fusion-formable glass-based articles including a metal oxide concentration gradient |
| KR101952085B1 (ko) | 2016-01-12 | 2019-05-21 | 코닝 인코포레이티드 | 얇은, 열적 및 화학적으로 강화된 유리-계 제품 |
| US11286203B2 (en) * | 2016-01-13 | 2022-03-29 | Corning Incorporated | Ultra-thin, non-frangible glass and methods of making |
| KR20190104435A (ko) | 2016-04-08 | 2019-09-09 | 코닝 인코포레이티드 | 금속 산화물 농도 구배를 포함하는 유리-계 제품 |
| KR20200091500A (ko) * | 2016-04-08 | 2020-07-30 | 코닝 인코포레이티드 | 두 영역을 포함하는 응력 프로파일을 포함하는 유리-계 물품, 및 제조 방법 |
| CN115028356B (zh) * | 2016-04-29 | 2024-07-12 | 肖特玻璃科技(苏州)有限公司 | 高强度超薄玻璃以及其制造方法 |
| US10858280B2 (en) * | 2016-11-22 | 2020-12-08 | Corning Incorporated | Automotive and architectural glass articles and laminates |
| US20190030861A1 (en) | 2017-07-27 | 2019-01-31 | Corning Incorporated | Composite laminate with high depth of compression |
| US11523527B2 (en) | 2017-10-03 | 2022-12-06 | Corning Incorporated | Glass-based articles having crack resistant stress profiles |
| US11214515B2 (en) | 2017-11-30 | 2022-01-04 | Corning Incorporated | Glass-based articles having stress profiles with high stored energy and methods of manufacture |
| TWI785156B (zh) | 2017-11-30 | 2022-12-01 | 美商康寧公司 | 具有高熱膨脹係數及對於熱回火之優先破裂行為的非離子交換玻璃 |
| CN108147657B (zh) * | 2017-12-29 | 2020-11-03 | 重庆鑫景特种玻璃有限公司 | 一种素玻璃、强化玻璃及制备方法 |
| JP2019123658A (ja) * | 2018-01-19 | 2019-07-25 | Ａｇｃ株式会社 | 化学強化ガラスの製造方法および化学強化ガラス |
| DE102018116460A1 (de) | 2018-07-06 | 2020-01-09 | Schott Ag | Hoch beständige und chemisch vorspannbare Gläser |
| DE102018116483A1 (de) * | 2018-07-06 | 2020-01-09 | Schott Ag | Chemisch vorspannbare Gläser mit hoher chemischer Resistenz und Rißbeständigkeit |
| DE102019117498B4 (de) | 2018-07-06 | 2024-03-28 | Schott Ag | Gläser mit verbesserter Ionenaustauschbarkeit |
| DE102018116464A1 (de) | 2018-07-06 | 2020-01-09 | Schott Ag | Chemisch vorspannbare, korrosionsstabile Gläser |
| US10829412B2 (en) | 2018-07-13 | 2020-11-10 | Corning Incorporated | Carriers for microelectronics fabrication |
| WO2020076604A1 (en) | 2018-10-09 | 2020-04-16 | Corning Incorporated | Compositions and methods for preventing baggy warp defect |
| US12037282B2 (en) | 2018-11-01 | 2024-07-16 | Corning Incorporated | Strengthened glass articles with reduced delayed breakage and methods of making the same |
| KR20210154825A (ko) | 2019-04-23 | 2021-12-21 | 코닝 인코포레이티드 | 확정 응력 프로파일을 갖는 유리 라미네이트 및 그 제조방법 |
| KR102812568B1 (ko) | 2019-08-05 | 2025-05-23 | 쇼오트 아게 | 시트형의 화학적으로 강화되거나 화학적으로 강화 가능한 유리 물품, 및 이의 제조 방법 |
| DE102019121146A1 (de) | 2019-08-05 | 2021-02-11 | Schott Ag | Heißgeformter chemisch vorspannbarer Glasartikel mit geringem Kristallanteil, insbesondere scheibenförmiger chemisch vorspannbarer Glasartikel, sowie Verfahren und Vorrichtung zu seiner Herstellung |
| DE102019121147A1 (de) | 2019-08-05 | 2021-02-11 | Schott Ag | Scheibenförmiger, chemisch vorgespannter Glasartikel und Verfahren zu dessen Herstellung |
| CN114514115B (zh) | 2019-08-06 | 2023-09-01 | 康宁股份有限公司 | 具有用于阻止裂纹的埋入式应力尖峰的玻璃层压体及其制造方法 |
| JP6791327B2 (ja) * | 2019-09-04 | 2020-11-25 | Ｊｆｅスチール株式会社 | 焼鈍分離剤用粉末の製造方法 |
| CN110642514B (zh) * | 2019-10-10 | 2021-04-13 | 清远南玻节能新材料有限公司 | 铝硅酸盐玻璃、强化玻璃及其制备方法、盖板、背板及装置 |
| CN112897888A (zh) | 2019-12-04 | 2021-06-04 | 康宁股份有限公司 | 具有纹理化表面的玻璃基材的制造方法 |
| DE202021103861U1 (de) | 2021-07-20 | 2021-10-04 | Schott Ag | Scheibenförmiger, chemisch vorgespannter oder chemisch vorspannbarer Glasartikel |
| US12441655B2 (en) | 2021-08-25 | 2025-10-14 | Corning Incorporated | Textured glass-based articles |
| WO2023027972A1 (en) | 2021-08-25 | 2023-03-02 | Corning Incorporated | Methods for etching glass-based substrates |
| WO2023027932A1 (en) | 2021-08-25 | 2023-03-02 | Corning Incorporated | Textured glass-based articles |
| CN113916148B (zh) * | 2021-11-09 | 2023-05-16 | 浙江师范大学 | 一种硅酸盐玻璃压痕裂纹深度的检测方法 |
| WO2024118373A1 (en) | 2022-11-30 | 2024-06-06 | Corning Incorporated | Textured articles and methods for making the same |
| WO2024242899A1 (en) | 2023-05-24 | 2024-11-28 | Corning Incorporated | Textured articles and methods for making the same |
| WO2025058797A1 (en) | 2023-09-14 | 2025-03-20 | Corning Incorporated | Durable cover articles with optical band-pass filtering for sensors |
| WO2025221587A1 (en) * | 2024-04-19 | 2025-10-23 | Corning Incorporated | Ion exchangeable glass articles having improved mechanical durability |
Citations (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20090215607A1 (en) * | 2008-02-26 | 2009-08-27 | Matthew John Dejneka | Fining agents for silicate glasses |
Family Cites Families (42)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US2434139A (en) | 1945-10-11 | 1948-01-06 | Corning Glass Works | Blue glass |
| DE1696063B2 (de) * | 1968-02-01 | 1972-07-20 | Jenaer Glaswerk Schott & Gen, 6500 Mainz | Anwendung eines austauschverfahrens von alkaliionen zur mechanischen festigkeitsverbesserung auf ein boroaluminiumsilikatglas mit einem relativ niedrigen waermeausdehnungskoeffizienten unter 60.10 hoch -7/grad c |
| US4192688A (en) | 1972-07-07 | 1980-03-11 | Owens-Illinois, Inc. | Product and process for forming same |
| JPH01226789A (ja) | 1988-03-07 | 1989-09-11 | Kyushu Electron Metal Co Ltd | Ｃｚ法による結晶引上げ方法及びその装置 |
| JPH01226749A (ja) * | 1988-03-08 | 1989-09-11 | Ngk Insulators Ltd | セラミック接合ガラス組成物 |
| US5674790A (en) * | 1995-12-15 | 1997-10-07 | Corning Incorporated | Strengthening glass by ion exchange |
| JPH11310430A (ja) * | 1998-04-27 | 1999-11-09 | Asahi Glass Co Ltd | 基板として用いるためのガラス組成物 |
| US6296686B1 (en) | 1998-06-03 | 2001-10-02 | Praxair Technology, Inc. | Ceramic membrane for endothermic reactions |
| JP3995902B2 (ja) | 2001-05-31 | 2007-10-24 | Ｈｏｙａ株式会社 | 情報記録媒体用ガラス基板及びそれを用いた磁気情報記録媒体 |
| US20030129329A1 (en) | 2001-12-21 | 2003-07-10 | Grossman David G. | Protective coating on metal |
| US7538050B2 (en) | 2002-02-05 | 2009-05-26 | Nippon Electric Glass Co., Ltd. | Glass composition |
| JP4530618B2 (ja) | 2002-09-27 | 2010-08-25 | コニカミノルタオプト株式会社 | ガラス組成物及びガラス基板 |
| WO2004031088A1 (ja) | 2002-10-07 | 2004-04-15 | Nippon Sheet Glass Co., Ltd. | 封着用ガラスフリット |
| CN101454252A (zh) | 2006-05-25 | 2009-06-10 | 日本电气硝子株式会社 | 强化玻璃及其制造方法 |
| EP3178794A1 (en) | 2006-06-08 | 2017-06-14 | Hoya Corporation | Glass for use in substrate for information recording medium, substrate for information recording medium and information recording medium, and their manufacturing method |
| KR20090027259A (ko) | 2006-10-10 | 2009-03-16 | 니폰 덴키 가라스 가부시키가이샤 | 강화 유리 기판 |
| WO2008108332A1 (ja) | 2007-03-02 | 2008-09-12 | Nippon Electric Glass Co., Ltd. | 強化板ガラスとその製造方法 |
| US7666511B2 (en) | 2007-05-18 | 2010-02-23 | Corning Incorporated | Down-drawable, chemically strengthened glass for cover plate |
| US7694420B2 (en) * | 2007-07-19 | 2010-04-13 | John Mezzalingua Associates, Inc. | Coaxial cable preparation tool and method of use thereof |
| JP5467490B2 (ja) | 2007-08-03 | 2014-04-09 | 日本電気硝子株式会社 | 強化ガラス基板の製造方法及び強化ガラス基板 |
| JP5743125B2 (ja) | 2007-09-27 | 2015-07-01 | 日本電気硝子株式会社 | 強化ガラス及び強化ガラス基板 |
| CN101910079A (zh) * | 2007-11-29 | 2010-12-08 | 康宁股份有限公司 | 具有改进的韧性和抗刮性的玻璃 |
| JP2011510904A (ja) | 2008-02-05 | 2011-04-07 | コーニング インコーポレイテッド | 電子装置のカバープレートとして使用するための耐損傷性ガラス物品 |
| JP2011510903A (ja) | 2008-02-08 | 2011-04-07 | コーニング インコーポレイテッド | 損傷耐性の化学強化された保護カバーガラス |
| KR20180015272A (ko) | 2008-08-08 | 2018-02-12 | 코닝 인코포레이티드 | 강화 유리 제품 및 제조방법 |
| JP2012500177A (ja) | 2008-08-21 | 2012-01-05 | コーニング インコーポレイテッド | 電子装置のための耐久性ガラスハウジング／エンクロージャ |
| JP5622069B2 (ja) | 2009-01-21 | 2014-11-12 | 日本電気硝子株式会社 | 強化ガラス、強化用ガラス及び強化ガラスの製造方法 |
| US8341976B2 (en) * | 2009-02-19 | 2013-01-01 | Corning Incorporated | Method of separating strengthened glass |
| US8802581B2 (en) * | 2009-08-21 | 2014-08-12 | Corning Incorporated | Zircon compatible glasses for down draw |
| CN102092940A (zh) | 2009-12-11 | 2011-06-15 | 肖特公开股份有限公司 | 用于触摸屏的铝硅酸盐玻璃 |
| CN102167509A (zh) * | 2010-02-26 | 2011-08-31 | 肖特玻璃科技(苏州)有限公司 | 能进行后续切割的化学钢化玻璃 |
| JP5683971B2 (ja) * | 2010-03-19 | 2015-03-11 | 石塚硝子株式会社 | 化学強化用ガラス組成物及び化学強化ガラス材 |
| US8778820B2 (en) * | 2010-05-27 | 2014-07-15 | Corning Incorporated | Glasses having low softening temperatures and high toughness |
| US8759238B2 (en) * | 2010-05-27 | 2014-06-24 | Corning Incorporated | Ion exchangeable glasses |
| US9434644B2 (en) | 2010-09-30 | 2016-09-06 | Avanstrate Inc. | Cover glass and method for producing cover glass |
| US8796165B2 (en) | 2010-11-30 | 2014-08-05 | Corning Incorporated | Alkaline earth alumino-borosilicate crack resistant glass |
| JP5834793B2 (ja) | 2010-12-24 | 2015-12-24 | 旭硝子株式会社 | 化学強化ガラスの製造方法 |
| US8889575B2 (en) | 2011-05-31 | 2014-11-18 | Corning Incorporated | Ion exchangeable alkali aluminosilicate glass articles |
| TWI591039B (zh) | 2011-07-01 | 2017-07-11 | 康寧公司 | 具高壓縮應力的離子可交換玻璃 |
| CN102351420B (zh) * | 2011-07-05 | 2013-09-18 | 中国洛阳浮法玻璃集团有限责任公司 | 一种高强度超薄浮法玻璃 |
| EP3919454B1 (en) * | 2012-05-31 | 2023-11-01 | Corning Incorporated | Zircon compatible, ion exchangeable glass with high damage resistance |
| US9517967B2 (en) * | 2012-05-31 | 2016-12-13 | Corning Incorporated | Ion exchangeable glass with high damage resistance |
-
2013
- 2013-05-28 EP EP21168413.9A patent/EP3919454B1/en active Active
- 2013-05-28 EP EP13727766.1A patent/EP2855382B1/en active Active
- 2013-05-28 KR KR1020227041360A patent/KR102651562B1/ko active Active
- 2013-05-28 US US13/903,433 patent/US8951927B2/en active Active
- 2013-05-28 KR KR1020147037052A patent/KR102282976B1/ko active Active
- 2013-05-28 EP EP21203621.4A patent/EP4008694A1/en active Pending
- 2013-05-28 JP JP2015515110A patent/JP6305992B2/ja not_active Expired - Fee Related
- 2013-05-28 KR KR1020217023220A patent/KR102462318B1/ko active Active
- 2013-05-28 WO PCT/US2013/042840 patent/WO2013181134A1/en not_active Ceased
- 2013-05-28 EP EP21203622.2A patent/EP3992161A3/en active Pending
- 2013-05-28 CN CN201710217164.3A patent/CN106904827A/zh active Pending
- 2013-05-28 CN CN201380027920.6A patent/CN104718167B/zh active Active
- 2013-05-28 KR KR1020217033448A patent/KR102472180B1/ko active Active
- 2013-05-28 KR KR1020217033447A patent/KR102472676B1/ko active Active
- 2013-05-28 DE DE202013012920.4U patent/DE202013012920U1/de not_active Expired - Lifetime
- 2013-05-28 DE DE202013012919.0U patent/DE202013012919U1/de not_active Expired - Lifetime
- 2013-05-31 TW TW110138653A patent/TWI806197B/zh active
- 2013-05-31 TW TW102119385A patent/TWI599549B/zh active
- 2013-05-31 TW TW105137024A patent/TWI613175B/zh active
- 2013-05-31 TW TW108100044A patent/TWI694977B/zh active
- 2013-05-31 TW TW109114430A patent/TWI815009B/zh active
- 2013-05-31 TW TW106144083A patent/TWI650297B/zh not_active IP Right Cessation
- 2013-05-31 TW TW110138662A patent/TWI815197B/zh active
-
2014
- 2014-03-05 US US14/197,658 patent/US8946103B2/en active Active
-
2015
- 2015-01-07 US US14/591,361 patent/US9822032B2/en active Active
-
2017
- 2017-04-03 JP JP2017073523A patent/JP6533551B2/ja active Active
- 2017-10-27 US US15/795,844 patent/US10570053B2/en active Active
-
2019
- 2019-05-24 JP JP2019097818A patent/JP6906563B2/ja active Active
-
2020
- 2020-02-24 US US16/799,451 patent/US11767253B2/en active Active
-
2021
- 2021-06-29 JP JP2021107349A patent/JP7089095B2/ja active Active
- 2021-09-23 US US17/483,276 patent/US11447415B2/en active Active
-
2022
- 2022-01-21 JP JP2022007769A patent/JP2022040392A/ja active Pending
- 2022-01-21 JP JP2022007765A patent/JP7399198B2/ja active Active
-
2023
- 2023-08-11 US US18/232,968 patent/US12227449B2/en active Active
Patent Citations (1)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US20090215607A1 (en) * | 2008-02-26 | 2009-08-27 | Matthew John Dejneka | Fining agents for silicate glasses |
Also Published As
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| TWI806197B (zh) | 具有高損傷抗性之鋯石相容離子交換玻璃 | |
| JP7184737B2 (ja) | 耐スクラッチアルミノホウケイ酸ガラス | |
| US9517967B2 (en) | Ion exchangeable glass with high damage resistance |