TWI725867B - 反應器組件及其用途、塗覆方法及塗覆物品 - Google Patents

反應器組件及其用途、塗覆方法及塗覆物品 Download PDF

Info

Publication number
TWI725867B
TWI725867B TW109118878A TW109118878A TWI725867B TW I725867 B TWI725867 B TW I725867B TW 109118878 A TW109118878 A TW 109118878A TW 109118878 A TW109118878 A TW 109118878A TW I725867 B TWI725867 B TW I725867B
Authority
TW
Taiwan
Prior art keywords
fluid
substrate
reaction chamber
flow
inert
Prior art date
Application number
TW109118878A
Other languages
English (en)
Other versions
TW202100796A (zh
Inventor
馬可 普達斯
Original Assignee
芬蘭商皮寇桑公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 芬蘭商皮寇桑公司 filed Critical 芬蘭商皮寇桑公司
Publication of TW202100796A publication Critical patent/TW202100796A/zh
Application granted granted Critical
Publication of TWI725867B publication Critical patent/TWI725867B/zh

Abstract

本發明提供了一種化學沉積反應器組件(100)，配置成用於通過化學沉積在諸如多孔材料等的流體可滲透材料的表面上形成塗層，所述反應器組件包括反應室(101)，配置成至少部分地接收具有待塗覆的目標表面(10A)的流體可滲透基板(10)；至少一個反應性流體吸入管線(21)，配置成將反應性流體(12)流傳遞入所述反應室，以及具有至少一個封閉部分(31)的惰性流體遞送器具，所述封閉部分配置成將惰性流體(11)流通過所述基板(10)朝向所述基板(10)的目標表面傳遞，使得所述惰性流體(11)流在所述表面處遇到所述反應性流體(12)流，從而在所述流體可滲透基板的目標表面處形成塗層(121)。

Description

反應器組件及其用途、塗覆方法及塗覆物品
本發明總體上涉及薄層沉積方法和相關設備。特別地，本發明涉及一種反應器組件以及用於使用化學沉積技術在流體可滲透材料，諸如多孔材料，的表面上形成塗層的相關方法。
化學沉積方法，諸如化學氣相沉積(CVD，Chemical Vapor Deposition)和原子層沉積(ALD，Atomic Layer Deposition)，在本領域中被廣泛描述。通常被認為是CVD工藝的子類的ALD技術已證明是用於在三維基板結構上製造高品質保形塗層的有效工具。
ALD基於交替的自飽和表面反應，其中在非反應性(惰性)氣體載體中作為化學化合物或元素提供的不同反應物(前體)依次脈衝進入容納基板的反應空間中。反應物沉積後通過惰性氣體沖洗基板。習知ALD循環以兩個半反應(脈衝第一前體–沖洗；脈衝第二前體–沖洗)進行，從而以自限(自飽和)方式形成材料層，通常厚為0.05-0.2 nm。為了獲得具有預定厚度的膜，循環根據需要重複多次。針對每種前體的典型基板暴露時間為0.01-1秒。常見的前體包括金屬氧化物、單質金屬、金屬氮化物和金屬硫化物。
當一種或多種前體氣體流動通過多孔基板並完全塗覆在孔隙內部時，就方法在浸漬有多種化學物的基本上多孔結構上生成塗層得能力而言，ALD提供了顯著的益處。
然而，當應用於在基本上多孔材料的表面上形成塗層時，相同的功能構成了顯著缺陷。在習知ALD工藝中，前體氣體可以在1秒內吸收到某些多孔基板中約1 mm的深度。在希望形成奈米級厚膜的情況下，需要從所述多孔基板上去除過量的反應物化學物(滲透至約1 mm的深度)。後者是通過用惰性氣體清洗(沖洗)基板相對長的時間，諸如每次脈衝後1分鐘或更長，來實現。考慮到(前體)脈衝持續時間通常為0.1 s，且每次脈衝後的沖洗持續時間通常為1-10 s(例如，對於非多孔基板)，每次脈衝清洗1分鐘或更長的時間顯著阻礙了該程序。此外，在大多數實例中，不可能控制在多孔基板上形成的塗層的均勻性。另一方面，縮短一個或多個脈衝持續時間不會提高對反應物化學物滲透進入多孔基板的深度的可控性。因此，由缺乏均勻性、差的膜厚度控制以及因此方法的再現性水準不足，阻礙了通過習知ALD方法在多孔基板的表面形成薄膜。
在這方面，鑒於解決與在製造表面塗覆的多孔材料中應用ALD相關的挑戰，仍然希望原子層沉積技術的更新。
本發明的目的是解決或至少緩解由相關技術的侷限和缺點引起的每個問題。該目的是通過反應器組件、相關方法及其用途的各種實施方式來實現的，所述反應器組件被配置成用於通過化學沉積在基本上流體可滲透基板的表面上形成塗層。因此，在本發明的一個方面中，根據獨立請求項1所限定的，提供了一種反應器組件。
在較佳的實施方式中，提供了反應器組件，包括：反應室，其被配置成至少部分地接收具有待塗覆的目標表面的流體可滲透基板；至少一個反應性流體吸入管線，其被配置成將反應性流體流傳遞入所述反應室，以及具有至少一個封閉部分的惰性流體遞送器具，至少一個封閉部分被配置成將惰性流體流通過所述流體可滲透基板朝向流體可滲透基板的目標表面傳遞，使得所述惰性流體流在所述表面處遇到所述反應性流體流，從而在所述基板的目標表面處形成塗層。
在所述反應器組件中，所述流體可滲透基板以僅使所述基板的目標表面暴露於所述反應性流體流的方式被接收到所述反應室中。
在實施方式中，所述封閉部分被配置成聯接所述反應室，使得所述封閉部分與所述反應室之間的流體流動僅經由所述流體可滲透基板發生。
在實施方式中，所述流體可滲透基板至少部分地被接收在所述封閉部分內部。
在實施方式中，所述惰性流體遞送器具更包括至少一個惰性流體吸入管線。
在實施方式中，所述封閉部分基本上設置在所述反應室的外部。在實施方式中，封閉部設置在反應器蓋子中。
在其他實施方式中，所述封閉部分基本上設置在所述反應室內部。在實施方式中，所述封閉部分被配置成用於所述流體可滲透基板的基板固持器。
在實施方式中，所述反應器組件更包括至少一個加熱元件，所述加熱元件聯接或集成至所述封閉部分及/或所述一個或多個惰性流體吸入管線。
在實施方式中，所述反應器組件更包括至少一個惰性流體流調節裝置，其被配置成在預定時間點改變所述惰性流體流並調節在所述目標表面處反應性流體滲透進入所述流體可滲透基板的深度。
在實施方式中，所述反應器組件更包括至少一個反應性流體流調節裝置，其被配置成控制所述至少一個反應性流體吸入管線中的反應性流體流。
在一些實施方式中，所述反應器組件被配置成原子層沉積(ALD)裝置。在一些實施方式中，所述反應器組件被配置成光輔助ALD裝置。在另外的實施方式中，所述反應器組件被配置成電漿增強原子層沉積(PEALD)裝置。
在另一方面，根據獨立請求項15所限定的，提供了一種用於通過化學沉積來塗覆流體可滲透基板的表面的方法。
在實施方式中，所述方法包括：獲得具有反應室的化學沉積反應器，所述反應室被配置成至少部分地接收具有待塗覆的目標表面的流體可滲透基板，引導反應性流體進入所述反應室，以及朝向所述目標表面引導惰性流體通過所述流體可滲透基板，使得惰性流體流在所述表面處遇到反應性流體流，從而在所述流體可滲透基板的目標表面處形成塗層。
在所述方法中，經由惰性流體遞送器具引導惰性流體通過所述流體可滲透基板，所述惰性流體遞送器具具有至少一個封閉部分，所述封閉部分與所述反應室分開佈置，使得所述封閉部分與所述反應室之間的流體流動僅經由所述流體可滲透基板發生。
在實施方式中，朝向所述目標表面引導惰性流體通過所述流體可滲透基板，使得阻止反應性流體在所述基板內部的滲透。
在實施方式中，通過在預定時間點改變所述惰性流體流來調節反應性流體滲透進入所述流體可滲透基板中的深度。
在一些實施例中，當反應性流體到達所述基板的目標表面時，通過中斷所述惰性流體流來調節反應性流體滲透進入所述流體可滲透基板中的深度。
在一些額外的實施方式中，在反應性流體到達所述流體可滲透基板的目標表面的時間點，所述惰性流體流被中斷和反向，從而允許反應性流體滲透到所述基板中。
在實施方式中，被遞送到所述反應室中的反應性流體包含預定前體化合物。
在實施方式中，將若干預定前體按依次順序遞送到所述反應室中。在實施方式中，在遞送每種前體之後清洗所述反應室，其中清洗是通過經由所述至少一個反應性流體吸入管線及/或經由所述至少一個封閉部分將惰性流體引導進入所述反應室來進行的。
在替代性實施方式中，所述塗層由單一前體化合物形成。
在實施方式中，所述流體可滲透基板是多孔基板或顆粒基板。
在實施方式中，所述流體可滲透基板選自由多孔金屬、多孔陶瓷和多孔聚合物組成的群組。
在實施方式中，在所述流體可滲透基板的目標表面處形成的塗層包括催化化合物。
在另一方面，根據獨立請求項23所限定的，提供了一種具有表面的流體可滲透材料的塗覆物品，所述表面包括通過根據前一方面的方法形成的塗層。
在實施方式中，所述塗覆物品包括由顆粒材料建立的流體可滲透材料。在實施方式中，所述塗覆物品包括由選自由多孔金屬、多孔陶瓷和多孔聚合物組成的群組的多孔材料建立的流體可滲透材料。在實施方式中，在所述塗覆物品的表面處形成的塗層包括催化化合物。
在實施方式中，所述塗覆物品被配置成由多孔材料製成的本體，所述本體在其中包括至少一個開口或通路。
在仍另一方面，根據獨立請求項27所限定的，提供了根據一些先前方面的反應器組件用於塗覆感測器裝置，特別是氣體感測器裝置的用途。
在仍另一方面，根據獨立請求項28所限定的，提供了根據一些先前方面的反應器組件用於製造固態多孔催化劑的用途。
取決於本發明的每個特定實施方式，本發明的實用性由多種原因而產生。本發明提供了以薄膜形式在具有不同孔隙率程度(例如1-99%)的多孔材料的表面以相對快速且容易的方式沉積塗層。事實上，本發明允許在多孔基板的表面上以與在非多孔基板上的沉積的相同或至少相當的速度進行化學沉積反應。加快的製造速率允許提高整個生產鏈的成本效益。
因此，本發明允許在時間上顯著減少通過將前體脈衝到所述反應空間內之間的惰性流體清洗反應空間的步驟。
本發明還提供了微調指示允許前體滲透進入多孔基板的程度的量度，從而可以高精度地控制深度解析度(指示塗層的厚度)。這對於需要在亞微米(submicron)解析度的多孔基板上進行層沉積的應用尤其重要，諸如微米和奈米電子學及/或醫學應用，例如植入物。
此外，本文所公開的反應器裝備在容納各種形狀和尺寸的基板方面是極其靈活的。因此，反應器可被配置成容納相對簡單形狀的單個或多個基板，諸如片材、平板、盤等，或具有基本複雜的3D形狀的一種或多種基板。在大多數情況下，塗覆物品建立用於各種應用的即用物品，諸如提供固態催化劑載體及/或提供傳感裝置。
在本公開中，層厚度小於1微米(μm)的材料被稱為「薄膜」。
在本公開中，表述「反應性流體」指示在惰性載體中包括至少一種化學化合物(下文中，前體)的流體流。該表述還適用於被配置成按依次順序輸送至少兩種不同前體的流體流，從而將每種前體一次引入一個反應室中。
在本公開的上下文中，術語ALD包括所有適用的基於ALD的技術以及任何等效或緊密相關的技術，諸如例如以下ALD子類型：電漿輔助ALD(plasma-assisted ALD)、PEALD(Plasma Enhanced Atomic Layer Deposition，電漿增強原子層沉積)和光子增強原子層沉積(也稱為光ALD，photo-ALD，或瞬時增強ALD，flash enhanced ALD)。
在本公開中，表述「若干(a number of)」指的是從一(1)開始的任何正整數，例如到一、二或三。表述「複數個(a plurality of)」在本文中指的是從二(2)開始的任何正整數，例如，到二、三或四。
圖1、圖2、圖4和圖7在100處示出了根據各種實施方式的反應器組件(在下文，「反應器」)。在所有配置中，反應器100被實施成使得允許通過化學沉積在基本上流體可滲透基板的表面上形成塗層。基本上流體可滲透基板較佳是由多孔材料製成的基板(圖1、圖2、圖4)，或者，可替代地是由顆粒材料製成的基板(圖7)。
反應器較佳地被配置成利用基於氣相沉積的技術的原理。就總體實施而言，反應器100可基於例如美國專利第8211235號(Lindfors)中描述的ALD裝備，或基於從芬蘭Picosun Oy可獲得的商標為Picosun R-200 Advanced ALD系統的裝備。然而，本發明構思的基礎特徵可以結合到任何其他實施為例如ALD，MLD(分子層沉積，Molecular Layer Deposition)或CVD裝置的化學沉積反應器中。
參考圖1A，其示出了根據一種實施方式的反應器100。反應器100包括反應室101。反應空間(沉積空間)由所述反應室101的內部建立。
在一些實例中，反應室101可被配置成用蓋子102密封的敞開頂部的容器(圖1至圖3、圖6)。圖1至圖3和圖6所示的反應室因此具有淋噴頭(showerhead)類型流。當從上方觀察時，反應器100具有基本上圓形的佈局。
在一些實例中，反應室可被配置成可從側面或從底部裝載的容器(未示出)。在這種的配置中，蓋子被配置成在反應器容器的側面(在側壁內)或底部設置的艙口。這種類型的反應室可具有例如從側面吹出的交叉流。
反應器100還包括若干器具，其被配置成將反應性流體12流傳遞入反應室101。所提及的器具提供為若干吸入管線(下文中，進料管線)21以及相關的開關及/或調節裝置23，諸如閥，如下面進一步揭示的。
圖1A是本實施方式的說明，其中前體流體12藉助於至少一個進料管線21經由相應的入口22被遞送到反應室101內部。
在一些實例中，較佳的是，反應器包括兩個、三個或更多個進料管線21和相應數量的入口22(未示出)。通過這種佈置，相應地，可以經由分開的進料管線和入口將許多不同的前體引導進入反應室。反應器100可包括儘量多的進料管線和相關的入口，只要就沉積工藝和裝置設計而言被認為是可行的。
反應器還可被配置成不具有進料管線21(即，使進料管線21完全省略)。在這種情況下，閥23被集成到形成反應室101的容器的側壁中或蓋子102中。
在一些配置中，反應器可包括歧管進料管線，其具有一個公共入口22或若干公共入口以及可連接至各種前體源和一個或多個惰性氣體供應(未示出)的分配管道。
一種或多種前體以流體形式被遞送到進料管線21中。流動通過進料管線21的反應性流體12較佳是包含由惰性載體11A攜帶的預定前體化學物12-X的氣態物質。一種或多種前體從被配置為例如容器、盒或管道系統的一個或多個供應源24供應到進料管線21。每個源24較佳地含有作為化學化合物或元素提供的預定前體12-X。每個源24配備有例如作為手動關閉閥提供的至少一個閥25。一種或多種沉積反應，諸如一種或多種ALD反應，所需的多種前體化學物可經由單個進料管線21引導進入反應空間。
在一些實例中，一種或多種前體12-X以氣態形式提供，諸如氨氣(NH3 )。在一些其他實例中，一種或多種前體以液體或固體形式提供，並在與惰性載體混合之前被氣化。
惰性載體11A是流體，較佳為氣體，諸如氮氣(N2 )、氬氣(Ar)或對前體(反應物)和反應產物具有基本零反應性的任何其他合適氣態介質。惰性載體氣體11A由單獨源或多個源(未示出)供應。
舉例來說，在產生微機電系統(MEMS，Microelectromechanical systems)中廣泛的利用三甲基鋁(第一前體)和水(第二前體)沉積氧化鋁的ALD工藝使用兩種化學物，所述兩種化學物從兩個源24經由同一進料管線21或兩個不同的進料管線順序供應到反應室中。
製造複雜的多層結構(所謂的堆疊體)，其中每一層在單獨ALD循環中產生及/或其中所述層在組成方面彼此不同，可相應地採用三種或更多種不同的前體和供應源。
在一些實例中，化合物的混合物，諸如溶劑中的預定前體，例如，可以從同一源24供應。
從不同源供應的一種或多種前體12-X和惰性載體11A經由多口閥23進入進料管線21。閥23被配置成三口閥，例如，具有自動控制系統以及可選地手動備份控制。在較佳的配置中，閥23是三通ALD閥。ALD閥被配置成維持惰性載體流體11A穩定流進入反應室中，並在預定時間點將一種或多種流體前體12-X引入所述載體中。ALD閥可被配置成將前體12-X注入(連續地)流動的載體中。附加地或替代地，可在所述閥23的上游設置其他控制器件，例如諸如一個或多個品質流量控制器(未示出)，以在將前體12-X注入進料管線21的一段時間內中斷載體流體11A流。在任一種情況下，前體的注入以簡短脈衝(0.01-100 s，通常為0.1 s)進行。
在當反應器包括多於一個進料管線21的配置中，較佳的使每個所述進料管線都配備有ALD閥23。
一個或多個進料管線21和相關的一個或多個閥23一起構成反應性流體遞送器具。所述器具可還包括若干輔助部件，諸如設置在閥23上游的前體和惰性載體吸入管線，附加的流體流調節器具，諸如例如一個或多個閥25，以及控制裝置(未示出)。
在一些配置(未示出)中，可以佈置進料管線21以使得將反應性流體12經由蓋子102引導進入反應室101。蓋子102可任選地包括沿其邊緣及/或圍繞其邊緣的一個或多個凸緣。
反應器100還包括用於將諸如多餘載體、前體和反應產物等廢氣流13排出反應室101的排空管線103。排空管線103構成用於排空泵單元104的前管線，並且在一些配置中，它可以包括關閉閥105，較佳地在泵單元104的上游。較佳的是，以不間斷的方式從反應室進行抽取流體物質，由此泵單元104，較佳地被配置為真空泵，在整個沉積工藝期間連續地從反應室中去除流體物質。
較佳的是在操作、裝載和卸載期間將反應室101保持在真空下，因此反應室中的壓力通常保持在100 Pa(1 mbar)或較佳為更低的水準。在另外一些配置中，反應室中的壓力設置為與環境壓力相同的水準。
在圖1B所示的配置中，反應器100附加地包括外部殼體110，其中容納有反應室101。在一些實例中，由所述外部殼體110的內部建立的中間空間保持在真空下，並且稱為真空室。較佳的是，將所述中間空間中的壓力保持在至少1 kPa(10 mbar)的水準，以在反應室101的內部(通常小於100 Pa)與外部殼體110的內部之間建立壓力差。
所述中間空間還可容納若干加熱元件313、313A。若干加熱元件313可放置成與反應室101聯接。附加地或替代地，若干加熱元件可以集成到形成反應室101的一個或多個容器壁中。在另外的附加的或替代性配置中，反應空間的加熱可通過將諸如氣體等的預熱流體經由進料管線21引導進入其中來進行。在這種情況下，可以佈置若干加熱元件，以使其聯接或包圍所述進料管線21，或者併入到形成所述進料管線的管(未示出)中。
外部殼體110還可以以與圖1B所示相同的方式被包括在圖2、圖4A、圖4B和圖7所示的配置中。
參考圖1A，被配置為多孔材料並具有旨在用於在其上沉積塗層的目標表面10A的流體可滲透基板10，其全部或至少部分被進一步接收到反應室101中。為了本發明的目的，較佳的是以如下方式將基板10接收到反應室中：除了目標表面10A之外，所述基板的一個或多個其他表面沒有暴露於反應性流體流。因此，基板10在反應器組件中的位置使得僅所述多孔材料的目標表面10A暴露於反應性流體12流。
表述「目標表面」在此表示待塗覆的多孔材料的外表面。參考圖1至圖6，「多孔材料」是指由所述多孔材料組成或包括所述多孔材料的有限個物品。在後一種情況下，多孔材料可以被配置成在其上包括多孔材料層或被封裝在所述多孔材料中的物品。在實施方式中，多孔材料10提供作為用於一個或多個化學沉積反應的一個或多個基本上固體多孔基板。
多種多孔材料可以用作一種或多種多孔基板，包括但不限於金屬、陶瓷、聚合物、複合材料和半導體材料(例如矽)。還可以利用蜂窩狀固體，諸如金屬泡沫和陶瓷泡沫。
參考圖7，流體可滲透基板還可由基本上可流動的顆粒基板，包括但不限於粉末基板及/或纖維基板，建立。事實上，所述顆粒基板可被視為多孔基板的修改，其具有由顆粒、纖維或任何其他相關顆粒物質之間建立的空氣間隙形成的孔隙。
本發明對諸如多孔基板或顆粒基板等流體可滲透基板的性質沒有設置限制；然而，對於本領域技術人員而言，顯然，基板的選擇取決於潛在的基板材料經受諸如溫度和壓力等反應條件的能力，以及預定前體化學物與所述基板材料以及彼此的相容性，以形成預先設計的塗層。
如本文提及的，在習知化學沉積系統，諸如ALD系統，中，一種或多種前體化學物以0.001-1000 mm/s範圍內的可能速率，例如諸如以約1 mm/s的速率，擴散進入放置在反應室中的一些多孔基板中，並沉積到孔隙的內部上。
反應器100被配置成有效地阻止與反應性流體12一起到達到流體可滲透基板10上的一種或多種前體化學物擴散進入所述基板內部。一種或多種前體不滲透到基板10內部，而是駐留在暴露於反應性流體流的所述基板的表面(即目標表面10A)上，由此在所述目標表面處形成塗層。
在通過在反應室101的方向上引導惰性流體11通過流體可滲透基板10來建立及/或調整逆流流動時形成塗層。當含有前體12-X的反應性流體12經由反應室101到達目標表面10A時，惰性流體11流通過流體可滲透材料10到達所述目標表面10A。在表面10A處，惰性流體11流遇到反應性流體12流，並阻止一種或多種前體滲透進入基板。這導致形成塗層121，並在下文中參考圖5和圖6更詳細地描述。
由惰性流體遞送器具將惰性流體11流傳遞入反應室101。所述器具包括基本中空的封閉空間，下文中為具有預定體積(V )的封閉部分31。封閉部分31基本上與反應室101分開，使得部分31和反應室101之間的流體連通(流體流動)僅經由流體可滲透材料10發生。允許惰性流體11以不受阻礙的方式流過封閉部分31的內部。
較佳的是，流體可滲透基板10至少部分地被接受在封閉部分31內部。
在一些配置中，惰性流體遞送器具還包括至少一個惰性流體吸入管線311。
在一些配置中，惰性流體遞送器具包括由所述至少一個惰性流體吸入管線311建立的封閉部分31。這種類型的示例性配置如圖3A所示。
流體通過基本上固體(多孔)或顆粒材料的傳播伴隨著所述流體的流體動力學特性的變化，諸如速度、流動幾何特性、邊界條件等。因此，流體動力學的變化在惰性流體11從(基本中空的)體積，諸如經由封閉部分31的內部，流過多孔材料10的傳播時發生。流體傳播特性的變化允許提供流體吸入體積，其被配置成在一端具有多孔「入口」10的基本上管狀的構件(圖3A)。
為了確保均勻流速下特別是通過基本上大塊(例如，待塗覆的表面超過1 cm2 )的流體可滲透材料，特別是多孔材料的足夠的流量，有利的是，封閉部分或空間31被配置成聯接反應室101。在這種實例中，封閉部分31可視為惰性流體吸入管線311的延伸。部分31因此被配置成聯接反應室101，使得所述部分31與反應室101之間的流體流動僅經由多孔材料10發生，並且惰性流體的不受阻礙的流動能夠貫穿整個封閉空間31。
一個或多個惰性流體吸入管線311可以以與一個或多個進料管線21相同的方式實施，即，提供作為可較佳地可經由一個或多個適當的分配裝置，諸如一個或多個閥(如下文所述)與相關流體源連接的管或管網。
在一些實施方式中，封閉部分31基本上設置在反應室101的外部(圖1A、圖1B、圖2)。
圖1A示出了反應器佈局，其中封閉空間31基本上經由形成所述反應室的容器的側壁聯接反應室。在所述側壁中，孔佈置成容納多孔基板10(未示出)。孔可以任選地可調整。例如，孔可包括以兩層旋轉式葉片虹膜光圈(two-layer rotary bladed iris diaphragm)(未示出)的方式配置的機動化的圓周調整系統。多孔基板10由此形成用於惰性流體11從由封閉部分31限定的體積流到反應空間的流體可滲透入口。
在一些配置中，封閉部分31還可提供作為細長的、基本為管狀的構件，其包括若干惰性流體吸入管線311。這種佈置允許將兩個或更多個反應器連接到共同的惰性流體吸入源(未示出)。
在一些實例中，由附圖標記11、11A表示的惰性流體可以從同一源或多個互連的源(未示出)供應。
圖2示出了反應器100的另一實施方式，其中封閉部分31設置在蓋子102中。流體可滲透入口由多孔基板10建立，以允許惰性流體11從封閉空間31(設置在蓋子102中)經由吸入管線311流動到反應空間。其他配置包括以吸入管線311的形式提供封閉空間31(以圖3A所示的方式)或提供包括若干吸入管線311的空間31。
以類似的方式，封閉空間31可以設置在被配置為反應器的側壁或底部中艙口的蓋子中(未示出)。
在上述實施方式中，多孔基板10至少部分地合併在封閉空間31內，前提是使所述基板的待塗覆的表面10A暴露於從反應室101到達所述表面的反應性流體12。
圖3B和圖3C示出了圖1A、圖1B和圖2所示的配置的替代配置。以此，流體可滲透基板10如附著於反應容器(圖3B)或蓋子(圖3C)的內表面，而整體設置在反應室101中。若干保持器或連接器，包括但不限於銷、釘子、螺釘連接器、黏合劑及/或支撐材料，諸如網格或網(後者設置在反應室的側面)，可適於將基板10保持在位置上。
圖1A、圖1B和圖2所示的配置可包括任選的惰性流體逸出管線312，所述逸出管線312被配置成從由封閉空間31限定的容積中抽取惰性流體11。惰性流體逸出管線312還可以經由一個或多個分開的路徑(未示出)連接到泵104或附加泵或被配置成用於排空廢氣流的任何其他適當的器具。因此，如圖1A、圖1B和圖2所示的封閉空間31被配置成藉助於附加的惰性流體逸出管線312來將惰性流體11傳遞流通過所述封閉空間。無論是否省略提供排空管線312(圖4A，圖4B)，經由流體可滲透基板10進入反應室101的惰性流體11經由中心排空管線103從反應空間中排出。可替代地，例如，可以採用作為吸入管線311提供的單流體連接在兩個方向上轉移流體，如由適當的調節器具(例如，下面進一步描述的器具33)控制的。
參考圖4A和圖4B，其示出了根據進一步實施方式的反應器100。圖4A、圖4B所示的反應器包括基本上在反應室101內部的封閉部分31。圖4A示出了用於塗覆單獨的基板10的佈局，而圖4B示出了用於塗覆複數個單獨的基板的佈局。
圖4A、圖4B所示的惰性流體吸入器具包括封閉部分31和相關的惰性流體吸入管線311。封閉部分31以此被配置為用於由流體可滲透材料製成的一個或多個基板的基板固持器。可以一次將單個基板或多個(至少兩個)基板定位在反應室101中。惰性流體11經由吸入管線311被接收到被配置成基板固持器的封閉部分31中，由此惰性流體11進一步被引導通過一個或多個由多孔材料製成的基板10進入反應室。一個或多個基板10可以被放置及/或固定在基板固持器上(圖4A，圖4B)。替代地，一個或多個基板10可至少部分地併入所述基板固持器中(圖4A)。圖4A描述的配置允許容納單個基板，其最終尺寸測量僅受反應室的尺寸限制。圖4A的反應器有利地提供對形狀為片材、平板、盤等的單個基板的塗覆；所述基板具有基本上平滑或圖案化的表面。
圖4B描述了封閉部分31的示例性配置，所述封閉部分31被配置成基板固持器並且包括用由多孔材料製成的基本上呈杯狀(從內部凹的)的基板10蓋住的若干突出部。在有蓋端，突出部是開放的，以允許惰性流體流不受限制地通過多孔材料。一種或多種前體沿著暴露於反應空間中的反應性流體12流的多孔基板的整個表面沉積。因此，圖4B描述的配置允許塗覆任何形狀的不同的(彼此分開的)多孔基板，包括複雜的三維結構。所提及的結構可以藉助於上述突出部或通過任何其他合適的保持器具固定在基板固持器31上，前提是允許惰性流體11流不受阻礙地通過多孔部分。
如圖4B描述的，每個基板還可以提供作為本體，其由多孔材料製成並在其中包括至少一個開口或通路(鈍端或貫穿通路，path-through)。因此，圖4B所示的配置允許在由多孔材料製成的基本為管狀的構件的諸如內表面和外表面上施加沉積塗層。因此，在一些實例中，多孔基板10因此提供作為至少一個基本上管狀的構件或管狀結構(流通或鈍端)，其橫切選自各種幾何形狀(圓、半圓、橢圓、矩形、五邊形等)。沉積塗層可以至少部分地施加到所述結構的外表面上，並且，附加地或替代地，施加到所述結構的內表面上。
圖4B所示的配置允許在由多孔材料製成的傳感/檢測裝置諸如多種氣體感測器(例如杯形氣體感測器)的表面上施加沉積塗層。
圖4B所示的配置允許在各種醫療裝置及/或其部分的表面上施加沉積塗層。在一些配置中，醫療裝置提供作為由流體可滲透材料製成的基本上管狀的構件。在一些特定配置中，醫療裝置提供作為導管、支架或內視鏡裝置。
本文公開的反應器組件通過以下使能夠將沉積塗層以高的精度施加至以上提及的基板上，諸如醫療裝置或其部分：通過限制反應性化學物流動進入基板材料的距離(深度解析度)，將一種或多種化學反應靶向到所述裝置的表面上，至所需/希望的深度。
圖3D所示的配置使所述裝置或其部分部分地暴露於反應性流體流，由此沉積塗層的提供可以限於所述裝置的預定區域，諸如尖端(例如內視鏡頭)。通過藉助於適當的基板保持器314，諸如穿通式基板保持器，將基板10或其部分放置到反應室中，可以獲得部分暴露。圖3D所示的配置允許將基板至少部分保留在反應空間101典型的高溫範圍之外。可以例如通過調節裝置33經由惰性流體11的逆向流動來控制允許反應性化學物流入基本管狀的基板10內部(遠離反應空間101)的距離量度。
圖4A和圖4B描述的基板固持器可以被配置成可從一個或多個吸入管線311拆卸並且是可更換的。
還可結合封閉部分31提供若干加熱元件313A(例如，在中間空間110中及/或併入到形成部分31的封閉部的一個或多個壁中)。圖1B、圖3B和圖4A以非限制的方式示出了反應器內加熱元件313A的佈置。
附加地或可替代地，諸如氣體的預熱流體可以經由所述封閉部分31及/或一個或多個吸入管線311被引導進入反應室101。在實施方式中，至少一個加熱元件313A(圖1B、圖4A)聯接、包圍或集成到吸入管線311的一個或多個壁，因此，經由所述管線311和封閉部分31被引導進入反應室中的惰性流體11與在反應室101中的一種或多種流體相比具有更高的溫度。
在較佳的實施方式中，反應器組件100還包括裝置33，所述至少一個裝置被配置成在預定時間點改變惰性流體11流。裝置33可以被配置成連接到相關的控制模組(未示出)的受控開關閥。
強調的是，器具21、23和器具31、311、33被配置成以高度協調的方式將反應性流體和惰性流體獨立地介導(mediate)遞送進入反應室。因此，可以建立若干功能模組，其仲介導流體遞送功能的器具取決於實施方式根據不同的佈局進行佈置。為了清楚之目的，僅參考特定附圖(1B，3A至3D)給出一些特徵和相關實施方式的圖形指示。基於圖1B、圖3A至圖3D的教導和相關描述，假設熟練的讀者也應能夠理解用於圖1A、圖2、圖4A、圖4B和圖7的上述配置。
封閉部分或空間31允許將若干反應器100連接到惰性流體11的公共源(未示出)。在這樣的配置中，可以實現經由一個或多個裝置33對惰性流體供應進行集中調節。
反應器100(圖1、圖2、圖4、圖7)較佳被配置為ALD裝置。另外的配置有利地包括一個或多個光輔助ALD裝置和一個或多個電漿增強原子層沉積(PEALD)裝置。反應器100還可以調整以用於其他化學沉積工藝，諸如MLD、CVD及其修改。
圖5A和圖5B示出了本文揭示的反應器組件100的操作方法基礎的構思。
圖5A示出了在根據圖1至圖3和圖4A描述的任何一種實施方式實施的反應器100中由基本固體、流體可滲透材料製成的單個多孔基板10的目標表面10A上形成塗層121，其中塗層121沿著所述基板的整個目標表面10A建立。
圖5B示出了在具有目標表面10A的複數個單個的流體可滲透基板10(參見描述為未塗覆的最左邊基板)上形成塗層121。杯狀基板10位於佈置在被配置成基板固持器的封閉部分31處的開口端突出部上。
反應性流體12被引導進入反應室，所述反應室至少部分地容納基板10。在其上待沉積塗層的基板(目標)表面10A是暴露於反應性流體12流的基板表面。
在該方法中，被遞送到反應室中的反應性流體12包括預定前體化合物。
朝向目標表面10A引導惰性流體11進而通過多孔材料(基板)10，以使惰性流體11流在所述表面處遇到反應性流體12流，從而阻止反應性流體12滲透到多孔基板10內部。因此，反應性流體12以塗層121的形式僅沉積到目標表面10A上。
在一些實例中，惰性流體11可以連續、不間斷地方式被引導進入反應空間。應用於典型的ALD沉積工藝，惰性流體11通過多孔材料10經由封閉部分31的間斷流動可在整個ALD循環中實現。通過連續引導惰性流體11朝向目標表面10A通過多孔材料，維持或阻止反應性流體12，特別是所述反應性流體中包含的一種或多種前體在多孔材料10內部的滲透。在這種情況下，有利的是徹底調整惰性流體的流速，以允許前體分子接觸目標表面10A。因此，在基板10的最上面的表面層上形成塗層121。當希望形成例如0.1-100 nm的薄塗層時，所述程序是有利的。
在一些實例中，較佳的是，允許反應性流體12中包含的前體流入多孔基板至預定深度(深度解析度)。反應性流體12滲透到多孔材料10中的深度可以通過藉助於惰性流體流調節裝置33在預定時間點改變惰性流體11流來調節(圖1至圖4)。
應用於示例性ALD沉積工藝，在一些較佳的配置中，裝置33可被設置成在示例性時間點1改變(例如中斷)惰性流體11流，在所述時間點，認為如反應性流體12中攜帶的前體12-X應到達目標表面10A。在這種情況下，裝置33及/或相關的控制模組(未示出)登記一個時間點0，在所述時間點，前體經由閥23注入到載體流體11A中(圖1、圖2、圖4)，並在預定時間段0-1到期時啟動時間點1，在此期間，認為如反應性流體12中攜帶的所述前體將通過進料管線21和反應室101到達目標表面10A。計算時間段0-1的持續時間，以允許前體接觸目標表面。惰性流體11流動通過基板材料10在時間點2處重新開始，其中時間段1-2的持續時間是基於前體到多孔基板10的滲透深度的所需/希望的量度來確定的。
實際上，每個時間段0-1、1-2的持續時間可以在0.001 s-100 s的範圍內變化。在一些配置中，每個所述時間段的持續時間構成0.1 s。
所提及的時間段是調整的物件，取決於反應器設計、基板材料、前體化學物、流體流速、所需/希望的深度解析度和其他參數。
上述動作(在時間點1中斷惰性流體流)還可以與啟動惰性流體反向流相關聯。在這種情況下，在認為前體到達目標表面10A的時間點1，惰性流體11流被中斷並反向，從而迫使反應性流體12吸收到多孔材料10中。在預定時間段1-2期間保持惰性流體的反向流(背離目標表面10A)。在時間點2，惰性流體11流恢復回到朝向目標表面10A的方向。
在一些替代性配置中，裝置33可被設置為根據本文公開的在時間點0暫停惰性流體流，並且在示例性時間點1重新開始所述惰性流體11流，在所述時間點1，認為如反應性流體12中攜帶的所述前體應到達目標表面10A。計算時間段0-1的持續時間，以允許前體分子接觸目標表面10A。
較佳的是，以獨立、高度協調的方式實現對裝置33和23的操作功能(分別調節惰性流體11流和調節一種或多種前體12-X注入惰性載體11A；圖1、圖3、圖4)的控制。因此，較佳的是，反應器100還包括中心控制模組(未示出)和相關聯的軟體，所述中心控制模組提供作為具有使用者介面的集成或獨立CPU解決方案。軟體管理功能較佳地包括實現一個或多個本地及/或遠端控制、一次監測若干反應器組件、一個或多個緊急電源控制等。
在實施方式中，塗層121是在單個ALD循環中在目標表面10A上建立的薄膜、層或片材。
參考圖6說明根據一些實施方式的塗覆方法。圖6描述的方法利用了原子層沉積的原理，並提供將至少兩種不同的前體12-1、12-2順序、暫時分離地遞送至反應空間。前體12-1、12-2較佳地是選擇不同的化學物，以在多孔基板的表面上形成預選化合物或組合物121(本文，塗層)。沉積半反應(half-reactions)用羅馬數字(i)和(ii)表示。
惰性流體11以受控的方式被引導進入反應室，由此惰性流體流可通過裝置33以上述方式調節。
在該方法中，將包含第一預定前體12-1的反應性流體12遞送(步驟i；左側)進入反應室，並通過調節惰性流體11朝向所述目標表面逆流流動通過多孔基板，以允許前體分子12-1接觸所述表面10A，來將前體子層(sublayer)沉積在目標表面10A處。第一前體12-1通常通過化學吸附進入與基板10的一個或多個化學反應，以形成子層(步驟i；右側)。此後，用惰性載體11A沖洗反應室，隨即以廢氣流(13)將過量的前體和反應產物排空(圖1、圖2、圖4)。在沖洗期間，惰性載體流體11A(不包含前體)經由閥23被引導進入反應室(圖1、圖2、圖4)。沖洗步驟可伴隨在反應室的方向上引導惰性流體11流通過多孔基板和子層12-1。
方法在ii處繼續(圖6)，隨後將包含第二預定前體12-2的反應性流體12遞送到反應室中。第二前體12-2經受與作為相關子層提供的第一前體12-1的一個或多個化學反應(步驟ii；左側)。調整惰性流體11朝向目標表面10A和反應空間的逆流流動，以允許前體分子12-2接觸在步驟i形成的子層。
在第二前體12-2的沉積期間，前體化合物12-1和12-2彼此反應以形成與12-1和12-2中的任一種不同的化合物121(ii，右)。
如關於步驟i提及的，步驟ii之後，用惰性載體11A沖洗反應室。所述沖洗步驟可伴隨在反應室的方向上引導惰性流體11流通過多孔基板和已建立的塗層121。
通過多孔材料10傳播到反應室101中的惰性流體11和用作一種或多種前體12-X、12-1、12-2的載體的惰性流體11A較佳地是相同的介質，例如，氣態氮氣(N2 )或氬氣。在一些實例中，不排除使用不同的非反應性介質11、11A。
在實施方式中，可以調整通過基板10的惰性流體11流，使得可通過僅使用惰性流體11(即，在不存在(惰性)載體流體11A的情況下)執行至少一個沖洗步驟。因此，在沖洗期間，進入反應空間的惰性流體11流(通過基板10)可以經由進料管線21代替載體流體11A流。在ALD循環內至少一個半反應之後，可以實現用惰性流體11流代替「沖洗流」11A。
一旦建立塗層121，可以進行若干額外的ALD循環n 次，任選地，在不存在經由多孔基板10的惰性逆流流動11的情況下，在目標表面上建立若干額外的塗層121n，從而可以產生多層(堆疊體)結構。
可以通過由排空泵104和若干調節裝置，例如諸如25、33，導致的跨所述材料10產生的壓差來控制通過流體可滲透材料10的流體流。後者可以被配置為配備有一個或多個質量流量控制器及/或一個或多個氣體流量計的開關閥。其他控制器件包括習知器具，諸如氣體感測器和壓力感測器。反應器組件100有利地包括(自動)控制系統，其被實現為例如電腦單元，並且包括至少一個處理器和具有適當的電腦程式或軟體的記憶體。
下文呈現了若干基於ALD技術的非限制性實施例。
實施例1. 由用作前體12-1的三甲基鋁(TMA，Al(CH3 )3 )和用作前體12-2的水，在多孔基板(諸如石墨烯、氧化矽等)上形成氧化鋁(Al2 O3 )塗層121。
實施例2. 如由乙醯丙酮鉑(II)(Pt(acac)2 ；前體12-1)和臭氧(O3 ；前體12-2)在多孔基板(諸如矽基板)上沉積鉑(Pt)塗層121。
實施例3. 如使用作為前體12-1的氯化鋁(AlCl3 )或TMA和作為前體12-2的氨(NH3 )，在多孔基板(諸如矽基板)上沉積氮化鋁(AlN)塗層121。
實施例4. 如使用作為前體12-1的鉻醯氯(CrO2 Cl2 )蒸氣和作為前體12-1的水或過氧化氫H2 O2 ，在多孔基板(諸如陶瓷基板)上沉積厚度為0.3-0.4 nm的氧化鉻(IV)塗層121。
實施例5. 如使用作為前體12-1的四氯化鈦(TiCl4 )蒸氣和作為前體12-1的水在多孔基板(諸如陶瓷基板)上沉積厚度為約0.1 nm的氧化鈦塗層121。
實施例6.如使用作為前體12-1的H2 Si[N(C2 H5 )2 ]2 (由Air Liquide以產品名稱SAM.24商業供應)蒸氣和作為前體12-1的臭氧(O3 )，在多孔基板(諸如陶瓷基板)上沉積厚度為約0.1 nm的氧化矽塗層121。
上述每個示例性反應通常每個沉積循環產生一個0.03-0.4 nm厚的層(取決於沉積條件)，其中典型的(前體)脈衝持續時間為0.1-1 s每一化學物，每個脈衝與約10 s的沖洗交替進行。每個脈衝導致一子層的沉積；而塗層121在包含若干脈衝-沖洗順序的沉積循環中沉積。為了沉積厚度為10-100 nm的層，沉積程序可在約10分鐘至約20小時的時間範圍內完成，這取決於所需的循環次數和每個循環的持續時間。以類似的方式，塗層121可由三種或更多種前體建立。
上述方法特別有利於用在多孔載體上製備固態催化劑。在這種情況下，根據本文所述，塗層121提供作為在順序反應i、ii過程中建立的催化化合物。因此，由催化化合物建立的層121支撐在多孔材料10的表面10A上。
可提供包括支撐在多孔材料表面上的催化塗層的多種固態催化劑，用於輔助包括但不限於轉化、加成和縮合的過程。特別地，可以提供用於碳數為2-12的烯屬烴(烯烴)聚合的固態催化劑。特別地，可以提供用於例如諸如乙烯和丙烯的低級烯烴(C2-C4)聚合的固態催化劑。非限制性實施例包括基於鉑族金屬，諸如鉑、鈀和釕的催化劑，及/或改性Phillips型催化劑。
在一些實例中，塗層121可由單個前體化合物建立。所述程序有利地利用了光輔助原子層沉積(此處為光ALD)的原理，其中，經由使目標表面10A暴露在預定波長範圍內的至少一個波長的電磁輻射中，由遞送到所述目標表面的光子觸發表面膜沉積反應。可使用紫外線輻射(100-40 nm)、可見光(400-800 nm)或紅外線輻射(大於800 nm)。在所描述的配置中，反應器100還可包括至少一個輻射源32(圖4A、圖4B所示；電磁能由E 表示)，其被配置成發射預定波長範圍內的至少一個波長的輻射。附加地或替代地，輻射源32可設置在反應室的外部(未示出)。在這種情況下，反應器組件還包括向目標表面10A和隨後形成的膜121遞送電磁能(E )，諸如電磁輻射，的一個或多個器具。這樣的一個或多個器具例如可以是視窗(例如在蓋子中)或天線裝置。由於在反應室中的高溫，例如諸如300℃在釕(Ru)沉積的情況下，輻射源相對於反應室的外部佈置是較佳的。應該理解，在圖1至圖3和圖7中描述的配置可包括一個或多個電磁源32，如本文所討論的。
圖7示出了反應器組件100的示例性實施方式，所述反應器組件被提出用於在被配置為顆粒基板，例如諸如粉末基板及/或纖維基板，的流體可滲透基板10上形成塗層。
反應器包括封閉部分31，其被配置成至少部分地接收所述顆粒基板10。在圖7所示的配置中，封閉部分31被配置成可裝載於所述基板的基本上管狀的構件。封閉部分較佳地被配置成通過反應室101(反應空間)。在反應空間101中，使基板10暴露在限定為封閉部分31內的至少一個孔31A的預定區域內的反應性流體12流。一個或多個目標表面10A由一個或多個這些暴露區域建立。至少一個孔31A可以是開口，其任選地被例如諸如網格、網或多孔過濾器或膜的支撐材料覆蓋，以阻止顆粒基板10逸出封閉部分31。
類似於圖3A所公開的，封閉部分可以由配置成向目標表面10A輸送惰性流體11的流體吸入管線建立。在圖7的實施方式中，惰性流體的吸入伴隨著通過輸送裝置34經由封閉空間輸送顆粒物質10。
反應器組件還包括第一輔助封閉部分31-1和第二輔助封閉部分31-2，每個所述部分分別包括裝載或卸載裝置。部分31-1、31-2設置在封閉空間31的兩側處。
例如，被配置為習知筒倉(silo)的示例性裝載裝置35可設置在第一輔助封閉部分31-1中。經由裝載裝置35裝載到反應器組件100中的顆粒物質10藉助於輸送裝置34經由管狀的封閉空間31輸送到反應室101中。所述輸送裝置可以在封閉空間31的整個長度上延伸，或者，替代地，輸送裝置可以設置在輔助部分31-1內。
經由第一輔助封閉部分31-1將惰性流體11吸入封閉部分31中，較佳地經由單獨的器具(未示出)來實現。所述惰性流體吸入器具還可被配置成使反向流成為可能(虛線箭頭，封閉部31-1)。
可在第二輔助封閉部分31-2中設置配置為收集塗覆顆粒材料10的容器的示例性卸載裝置36。以與31-1描述的類似方式，經由第二輔助部分31-2將惰性流體11吸入封閉部分31中是經由單獨的器具(未示出)來實現的；所述器具還配置為使反向流成為可能(虛線箭頭，封閉部31-2)。從輔助封閉部分31-1和31-2進入管狀封閉部分31的惰性流體11流至少在流速、時間和流體壓力方面可以同步。通過這樣的器具，可以控制反應性流體12在管狀封閉部分31內的傳播。
輸送裝置34可被配置為輸送帶、帶活塞的壓縮輸送機、螺旋輸送機或配備有振動器件的輸送機。輸送裝置可以任選地傾斜以利用重力流。
輔助封閉部分31-1、31-2較佳地被配置成具有可調節的體積。除本文所述的惰性流體流調節裝置33外，還可在部分31-1、31-2內設置若干輔助控制裝置，包括但不限於質量流量計及/或壓力感測器。總之，所提及的調節器具例如通過致動時間控制的反向流，對顆粒物質10和惰性流體11流通過封閉空間31向一個或兩個輔助封閉部分31-1、31-2提供高精度控制。
結果，沉積到顆粒基板10的目標表面10A上的塗層121可以跨通過孔31A的顆粒體積延伸至任何希望的深度解析度。
可以藉助於產生振動(例如搖動)運動並將該運動轉移到基板10上的一個或多個振動器具來進一步增強通顆粒基板10(圖7)的流體流動。振動器具可以配置為機械振動源、超音波產生源、被配置成經由無線感應引起振動的源等。本發明人在國際申請公開WO 2018/050954中描述了相關的振動器件。
反應器還包括容器36，所述容器用於收集顆粒材料並將顆粒材料從反應空間輸送出。
如本文所公開的，反應器100和相關的沉積方法有利地提供由基本上流體可滲透材料製成並且具有在其上形成塗層121的至少一個表面10A的塗覆物品的製造。反應器100允許一次製造單個塗覆物品或一次製造一批塗覆物品，其中所述一批包括至少兩個待塗覆的基板。
可以提供塗覆物品，其中多孔材料10為多孔金屬、多孔陶瓷或多孔聚合物。在一些實例中，一種或多種塗覆物品中提供的多孔材料可由顆粒基板，諸如粉末基板或纖維基板，建立。另外，多孔複合材料和半導體材料(例如矽)可以被塗覆。
本領域技術人員應當理解，本公開中闡述的實施方式可以根據需要進行調整和組合。因此，本公開旨在涵蓋在所附請求項的範圍內的本技術領域中的普通技術人員可識別的裝置和沉積方法的任何可能的修改。
10:基板 10A:目標表面 11:惰性流體 11A:惰性載體 12:反應性流體 12-X:前體 12-1:前體 12-2:前體 13:廢氣流 21:吸入管線、進料管線 22:入口 23:調節裝置、閥 24:源 25:調節裝置、閥 31:封閉部分 31A:孔 31-1:第1輔助封閉部分 31-2:第2輔助封閉部分 32:輻射源、電磁源 33:調節裝置、閥 34:輸送裝置 35:裝載裝置 36:卸載裝置 100:反應器組件、反應器 101:反應室 102:蓋子 103:排空管線 104:泵、泵單元 105:關閉閥 110:外部殼體、中間空間 121:塗層 311:吸入管線 312:逸出管線 313:加熱元件 313A:加熱元件 314:保持器E:電磁能
圖1A、圖1B、圖2、圖4A和圖4B示意性地示出了根據本發明的一方面的化學沉積反應器組件的各種實施方式。 圖3A至圖3D示意性地示出了根據實施方式在反應器組件內提供的某些元件。 圖5A和圖5B示意性地示出了根據實施方式的反應器組件的操作方法的基礎構思。 圖6示意性地示出了根據實施方式的塗覆方法。 圖7示意性地示出了根據實施方式的化學沉積反應器組件。
本文參考附圖揭示了本發明的詳細實施方式。在所有圖式中，相同的元件符號用於指代相同的構件。
10:基板
10A:目標表面
11:惰性流體
11A:惰性載體
12:反應性流體
12-X:前體
13:廢氣流
21:吸入管線、進料管線
22:入口
23:調節裝置、閥
24:源
25:調節裝置、閥
31:封閉部分
101:反應室
102:蓋子
103:排空管線
104:泵、泵單元
105:關閉閥
110:外部殼體、中間空間
312:逸出管線
313:加熱元件
313A:加熱元件

Claims (28)

  1. 一種反應器組件，配置成用於通過化學沉積在流體可滲透基板的表面上形成塗層，所述反應器組件包括：反應室(101)，配置成至少部分地接收具有待塗覆的目標表面(10A)的流體可滲透基板(10)；至少一個反應性流體吸入管線(21)，配置成將反應性流體(12)流傳遞入所述反應室，以及具有至少一個封閉部分(31)的惰性流體遞送器具，被配置成將惰性流體(11)流通過所述流體可滲透基板(10)朝向其目標表面傳遞，使得所述惰性流體(11)流在所述表面處遇到所述反應性流體(12)流，從而在所述基板的目標表面(10A)處形成塗層(121)。
  2. 如請求項1之反應器組件，其中，所述流體可滲透基板(10)以僅使所述基板的目標表面(10A)暴露於所述反應性流體(12)流的方式被接收到所述反應室(101)中。
  3. 如請求項1或2之反應器組件，其中，所述封閉部分(31)與所述反應室(101)分開佈置，並且其中，所述封閉部分與所述反應室之間的流體流動僅經由所述流體可滲透基板(10)發生。
  4. 如請求項1或2之反應器組件，其中，所述封閉部分(31)被配置成聯接所述反應室(101)，使得在所述封閉部分(31)與所述反應室(101)之間的流體流動僅經由所述流體可滲透基板(10)發生。
  5. 如請求項1或2之反應器組件，其中，所述流體可滲透基板(10)至少部分地接收在所述封閉部分(31)內部。
  6. 如請求項1或2之反應器組件，其中，所述惰性流體遞送器具更包括至少一個惰性流體吸入管線(311)。
  7. 如請求項1或2之反應器組件，其中，所述封閉部分(31)基本上設置在所述反應室(101)的外部。
  8. 如請求項1或2之反應器組件，其中，所述封閉部分(31)設置在蓋子(102)中。
  9. 如請求項1或2之反應器組件，其中，所述封閉部分(31)基本上設置在所述反應室(101)的內部。
  10. 如請求項9之反應器組件，其中，所述封閉部分(31)被配置成用於所述流體可滲透基板(10)的基板固持器。
  11. 如請求項1或2之反應器組件，更包括至少一個加熱元件(313，313A)，所述至少一個加熱元件聯接或集成至所述封閉部分(31)及/或所述一個或多個惰性流體吸入管線(311)。
  12. 如請求項1或2之反應器組件，更包括至少一個惰性流體流調節裝置(33)，所述至少一個惰性流體流調節裝置(33)配置成在預定時間點改變所述惰性流體(11)流並調節反應性流體(12)在所述目標表面(10A)處滲透進入所述流體可滲透基板(10)的深度。
  13. 如請求項1或2之反應器組件，更包括至少一個反應性流體流調節裝置(23)，所述至少一個反應性流體流調節裝置(23)配置成控制所述至少一個反應性流體吸入管線(21)中的所述反應性流體(12)流。
  14. 如請求項1或2之反應器組件，配置成原子層沉積 (ALD)裝置，可選地，配置成光輔助ALD裝置。
  15. 一種用於通過化學沉積對流體可滲透基板的表面進行塗覆的方法，包括：獲得具有反應室(101)的化學沉積反應器(100)，所述反應室(101)配置成至少部分地接收具有待塗覆的目標表面(10A)的流體可滲透基板(10)，引導反應性流體(12)進入所述反應室，以及朝向所述目標表面(10A)引導惰性流體(11)通過所述流體可滲透基板(10)，使得惰性流體(11)流在所述表面處遇到反應性流體(12)流，從而在所述流體可滲透基板的目標表面(10A)處形成塗層(121)。
  16. 如請求項15之方法，其中，經由具有與所述反應室(101)分開佈置的至少一個封閉部分(31)的惰性流體遞送器具引導惰性流體(11)通過所述流體可滲透基板，使得所述封閉部分(31)與所述反應室(101)之間的流體流動僅經由所述流體可滲透基板(10)發生。
  17. 如請求項15或16之方法，其中，朝向所述目標表面(10A)引導惰性流體(11)通過所述流體可滲透基板，使得阻止反應性流體(12)滲透到所述基板(10)內部。
  18. 如請求項15或16之方法，其中，通過在預定時間點改變所述惰性流體(11)流來調節反應性流體(12)滲透進入所述流體可滲透基板(10)中的深度。
  19. 如請求項15或16之方法，其中，通過在反應性流體(12)到達所述基板(10)的目標表面(10A)時的時間點，中斷所述惰性流 體(11)流來調節反應性流體(12)滲透進入所述流體可滲透基板(10)中的深度。
  20. 如請求項15或16之方法，其中，在反應性流體(12)到達所述流體可滲透基板(10)的目標表面(10A)時的時間點，使所述惰性流體(11)流中斷和反向，從而允許反應性流體(12)滲透進入所述基板(10)。
  21. 如請求項15或16之方法，其中，遞送到所述反應室中的反應性流體(12)包括預定前體化合物(12-1，12-2)。
  22. 如請求項21之方法，其中，將若干預定前體(12-1，12-2)按依次順序遞送到所述反應室中，並且其中在遞送每種前體之後，清洗所述反應室(101)，所述清洗是通過經由所述至少一個反應性流體吸入管線(21)及/或經由所述至少一個封閉部分(31)將惰性流體引導到所述反應室中來進行的。
  23. 一種具有表面的流體可滲透材料之塗覆物品，所述表面包括通過請求項15之方法形成的塗層(121)。
  24. 如請求項23之塗覆物品，其中，所述流體可滲透材料(10)為選自由多孔金屬、多孔陶瓷和多孔聚合物組成的群組的顆粒材料或多孔材料。
  25. 如請求項23或24之塗覆物品，其中，所述塗層(121)包括催化化合物。
  26. 如請求項23或24之塗覆物品，其配置成由多孔材料製成的本體，並且所述本體在其中包括至少一個開口或通路。
  27. 一種將請求項1至14中任一項之反應器組件用於塗覆感測器裝置之用途，特別是用於氣體感測器裝置。
  28. 一種將請求項1至14中任一項之反應器組件用於製造固態多孔催化劑之用途。
TW109118878A 2019-06-06 2020-06-05 反應器組件及其用途、塗覆方法及塗覆物品 TWI725867B (zh)